JPS6110415A - Decorative sheet - Google Patents

Abstract

PURPOSE:To eliminate the inferior appearance of a decorative sheet due to fish eyes by forming fine unevenness directly on the rear surface of a synthetic resin sheet which is the outermost layer of the decorative sheet. CONSTITUTION:Fine unevenness 12 is formed on the rear surface of a synthetic resin sheet 11, and a metallic thin film layer 13 is formed on the fine unevenness 12. Further the resin for injection molding and a thermal adhesive synthetic resin layer 14 are laminated on said metallic thin film layer 13. The fine unevenness 12 formed on the rear surface of the synthetic resin sheet 11 is hair line, matte finish or other shape, and the height difference between the crest and trough of said unevenness is preferably 0.5-6mu. Aluminium is preferably used for the material of metallic thin film layer, and it is formed on the surface with fine unevenness 12 of the synthetic resin sheet 11 by vapor deposition or spattering, etc.

Description

【発明の詳細な説明】 産業上の利用分野 本発明は、インジェクション成形の際に予め金型内に載
置してお（ことにより成形体と一体化し、成形体の表面
に微小凹凸状の金属反射面と、前記反射面Ｉ−に印刷可
能な保護層とを形成することが可能な化粧シーＩ・に関
するイ、のである。DETAILED DESCRIPTION OF THE INVENTION Field of Industrial Application The present invention provides a method for forming metal particles that are placed in a mold in advance during injection molding (thereby being integrated with the molded body, and having minute irregularities formed on the surface of the molded body). The second aspect relates to a decorative sheet I- which is capable of forming a reflective surface and a printable protective layer on the reflective surface I-.

従来の技術 従来、この神の化粧ノートと【７ては例えば、第２図に
示すように、ポリエステル等のプラスチックフィルム、
２／に、に面をヘアーライン加工した厚み６〜．３０１
ｔｍ程度のアルミニウノ、箔等の金属箔２２を接着剤２
３を用いて貼り合わせ、更にポリスチレンフィルム等の
インジェクション用樹脂と接着しうるフィルム２ｑを貼
り合わせたものが試みられた。Conventional Technology Conventionally, this divine makeup notebook [7] For example, as shown in Figure 2, plastic films such as polyester, etc.
2/, thickness 6~. with hairline processing on the side. 301
Metal foil 22 such as aluminum Uno or foil of about tm is glued with adhesive 2
Attempts have been made to attach a film 2q that can be bonded to an injection resin such as a polystyrene film.

しかし、この従来の化粧シートにおいては次のような点
が欠点となる。However, this conventional decorative sheet has the following drawbacks.

（イ）最下層のポリスチレンフィルムＳには原料樹脂中
のゲル状物質に起因するフィッシュアイが、フィルム表
面に凸状に存在するので、この凸状形状が金属箔を通し
て表向側（図では−に側）から見えるためにヘアーライ
ンの外観が部分的に損なわれ、商品価値を低下させる。(a) In the polystyrene film S of the bottom layer, fish eyes caused by gel-like substances in the raw resin exist in a convex shape on the film surface, so these convex shapes are passed through the metal foil to the front side (in the figure - The appearance of the hairline is partially damaged because it is visible from the side), reducing the product value.

（ロ）中層に金属箔を有するため、上下のプラスチック
層と金属箔の熱による膨張・収縮の割合が異なるので、
加熱や冷却のやり方によっては化粧シートにカールを生
じ、取り扱いに（い。(b) Since the middle layer has metal foil, the rate of expansion and contraction due to heat is different between the upper and lower plastic layers and the metal foil.
Depending on the heating and cooling methods, the decorative sheet may curl and become difficult to handle.

従って本発明においてはへアーライン等の微小凹凸状の
金属反射面を有しつつ、下層の欠点による外観−ヒの欠
陥を解消し、かつ、取り扱いに際してもカールの生じに
くい化粧シートを提供することを目的としてｔ・る。Therefore, it is an object of the present invention to provide a decorative sheet that has a metallic reflective surface with minute irregularities such as hair lines, eliminates the appearance defects caused by defects in the lower layer, and is less likely to curl when handled. As a purpose.

問題点を解決するための手段 上記の問題点を解決するため、本発明においては最」二
層となる合成樹脂シートの裏面に直接にヘアーライン加
工等の微小凹凸加工を施こし、微小凹凸を施した面に金
属薄膜を形成し、更に金属薄膜に接してインジェクショ
ン成形用樹脂と熱接着可能な合成樹脂層を積層すること
により化粧シートを構成するものである。Means for Solving the Problems In order to solve the above problems, in the present invention, micro-irregularities such as hairline processing are directly applied to the back surface of the synthetic resin sheet, which is the second layer, to create micro-irregularities. A decorative sheet is constructed by forming a metal thin film on the surface, and further laminating a synthetic resin layer that can be thermally bonded to an injection molding resin in contact with the metal thin film.

第１図は本発明の化粧シートの典型例を示す断面図であ
り、合成樹脂シート／／の裏面に微小凹凸１２が形成さ
れており、微小凹凸／２には金属薄膜層／３が形成され
ており、更に金属薄膜層／３にインジェクション成形用
樹脂と熱接着可能な合成樹脂層／ｑが積層されている状
態を示す。FIG. 1 is a cross-sectional view showing a typical example of the decorative sheet of the present invention, in which fine irregularities 12 are formed on the back surface of the synthetic resin sheet //, and a metal thin film layer /3 is formed on the fine irregularities /2. The figure shows a state in which a synthetic resin layer /q that can be thermally bonded to an injection molding resin is further laminated on the metal thin film layer /3.

上記における各層及び凹凸について説明すると、合成樹
脂シート／／は下層の微小凹凸及び金属薄膜層を保護す
るものであり、インジェクション成形により成形体と一
体化した後には最表層となるものであるから、用途に応
じた表面の物理的及び化学的性状を有するものである。To explain each layer and unevenness in the above, the synthetic resin sheet // protects the microscopic unevenness and metal thin film layer of the lower layer, and becomes the outermost layer after being integrated with the molded body by injection molding. It has surface physical and chemical properties depending on the intended use.

合成樹脂シート／／の一例としてはポリエチレンテレフ
タレートフィルム、ポリ塩化ビニルフィルム、ポリカー
ボネートフィルム、アクリル樹脂フィルム、ボリスチレ
／フィルム、ポリアミドフィルム等の透明合成樹脂フィ
ルムを挙げることができる。これらのうちポリエチレン
テレフタレートフィルムを用いると、耐熱性や透明性が
良好となり、又、ポリ塩化ビニルフィルムを用〜・ると
、着色性や成形加工性が良（、又、最表面の印刷加工等
の化粧適性も良好となる。Examples of the synthetic resin sheet include transparent synthetic resin films such as polyethylene terephthalate film, polyvinyl chloride film, polycarbonate film, acrylic resin film, polyethylene film, and polyamide film. Among these, when polyethylene terephthalate film is used, it has good heat resistance and transparency, and when polyvinyl chloride film is used, it has good colorability and moldability (also, the printing process on the outermost surface, etc.). The suitability for makeup also improves.

合成樹脂シート／／の厚みは取り扱い上、コ０μｍ以−
にであることが好ましく、上限は特にないが通常／１１
１１程度である。The thickness of the synthetic resin sheet // should not exceed 0 μm for handling reasons.
It is preferable that the upper limit is /11, although there is no particular upper limit.
It is about 11.

合成樹脂シート／ｌの裏面に形成されている微小凹凸１
２は、ヘアーライン、梨地、艶消しもしくはその他の形
状のものであって、凹凸の高低差は特に限定されないが
通常０．！ｉ〜６μｍ程度のもので々）る。これらの微
小凹凸はへアーライン加工、エンボス加工、サンドブラ
スト加工等の方法により形成することができる。Microscopic irregularities formed on the back side of synthetic resin sheet/l 1
2 has a hairline, satin finish, matte finish, or other shape, and the difference in height of the unevenness is not particularly limited, but is usually 0. ! The diameter is approximately 6 μm). These minute irregularities can be formed by methods such as hairline processing, embossing, and sandblasting.

金属薄膜層１３は化粧シート／θに金属光沢を与え、金
属薄膜層１３の上面は微小凹凸／２に接しているので、
上方からの光を反射して、見る人に微小凹凸／２の形状
に基づいた外観を与えるものである。金属薄膜層の材質
は希望する外観により様々なものでありうるが、通常は
アルミニウムを用いることが多い。アルミニウムを用い
るときはいわゆる「銀色」の金属光沢が得られ、このと
き上層の合成樹脂シートもしくは、合成樹脂シートと金
属薄膜層の間に透明な黄色の着色を施しておけばいわゆ
る「金色」の金属光沢が得られ、勿論、他の色の着色も
可能である。金属薄膜層の材質としてはアルミニウム以
外にも金、銀、銅、錫、クロム、ステンレス鋼等も使用
可能であり、これらの材質からなる金属薄膜層は、蒸着
やスパッタリング等の方法や、めっき法により合成樹脂
シー）／／の微小凹凸／コを有する側に形成する。金属
薄膜層／３の厚みは上記のような方法により形成される
常識的な範囲であればよいが、過度に厚（すると経済的
でない一ヒに、他の層との熱による膨張・伸縮の差違を
生じるので通常１０Ａ〜／μｍ程度である。The metal thin film layer 13 gives metallic luster to the decorative sheet /θ, and the upper surface of the metal thin film layer 13 is in contact with the minute irregularities /2.
It reflects light from above and gives the viewer an appearance based on the shape of the minute irregularities/2. The material of the metal thin film layer can vary depending on the desired appearance, but aluminum is usually used. When aluminum is used, a so-called "silver" metallic luster can be obtained, and if a transparent yellow coloring is applied between the upper synthetic resin sheet or between the synthetic resin sheet and the metal thin film layer, a so-called "golden" luster can be obtained. A metallic luster is obtained, and of course other colors are also possible. In addition to aluminum, gold, silver, copper, tin, chromium, stainless steel, etc. can also be used as the material for the metal thin film layer, and metal thin film layers made of these materials can be formed by methods such as vapor deposition, sputtering, or plating. The synthetic resin sheet is formed on the side with minute irregularities. The thickness of the metal thin film layer/3 may be within a common sense range when formed by the method described above, but if it is too thick (it is not economical, it may not expand or contract due to heat with other layers). Since it causes a difference, it is usually about 10 A/μm.

合成樹脂層／グは、化粧シートＩＯをインジェクション
成形の際に金型内に置いて成形するときに、インジェク
ション成形用樹脂と化粧シート／θとを接着する役割を
果たすものであり、接着性の観点からはインジェクショ
ン成形用樹脂と同じ材質か、或いは似通った材質を用い
ることが多（、例えば、ポリスチレン、アクリルニトリ
ル−スチレン共重合体、アクリルニトリル−ブタジェン
−スチレン共重合体、ポリ塩化ビニル等の樹脂のフィル
ムを用いることができ、これらは必要に応じて接着剤（
図示せず）を介して金属薄膜層に接して積層されるか、
或いはこれらの樹脂の溶剤溶液を塗布することにより積
層されろ。The synthetic resin layer /g plays the role of adhering the injection molding resin and the decorative sheet /θ when the decorative sheet IO is placed in a mold during injection molding, and has adhesive properties. From this point of view, materials that are the same as or similar to those for injection molding are often used (e.g., polystyrene, acrylonitrile-styrene copolymer, acrylonitrile-butadiene-styrene copolymer, polyvinyl chloride, etc.). Resin films can be used, and these can be bonded with adhesive (
(not shown) in contact with the metal thin film layer, or
Alternatively, they may be laminated by applying a solvent solution of these resins.

合成樹脂層／ｌｌは、インジェクション成形の際に層／
グ自身が伸ばされて破断したり、他の障害がない限り薄
くてもよ（、又、それ自体が感熱接着剤からなる層であ
ってもよい。ここで使用しうる感熱接着剤としてはホッ
トメルト系接着剤、塩ビ／酢ビ共重合樹脂系接着剤等が
挙げられろ。The synthetic resin layer /ll is formed during injection molding.
The adhesive may be thin (and may itself be a layer of heat-sensitive adhesive) as long as it does not break when stretched or has other problems. Examples include melt adhesives and vinyl chloride/vinyl acetate copolymer resin adhesives.

又、合成樹脂層ＩＱの厚みとしては２μｍ以上とするこ
とが好ましく、上限は特にないが、通常ｌ龍程度である
。Further, the thickness of the synthetic resin layer IQ is preferably 2 μm or more, and although there is no particular upper limit, it is usually about 1 μm.

以」二、本発明の基本的な構成を述べたが、各層間の接
着強度向上のために、合成樹脂シートに微小凹凸を形成
した後にコロナ処理を施したり、プライマー処理を施し
てもよく、更に金属薄膜層形成後にプライマー処理を施
す等、公知の手段の付加を行なうことは差支えない。又
、化粧シートの最懺面に更に別の印刷等の化粧を施した
り、化粧のためのプライマー処理を施すことも差支えな
い。又、化粧シートは必要に応じ、成形、打抜を施して
あってもよい。The basic structure of the present invention has been described below, but in order to improve the adhesive strength between each layer, corona treatment or primer treatment may be applied after forming minute irregularities on the synthetic resin sheet. Further, known means may be added, such as applying a primer treatment after forming the metal thin film layer. Further, it is also possible to apply other decoration such as printing on the most visible surface of the decorative sheet, or to apply a primer treatment for makeup. Further, the decorative sheet may be formed or punched as necessary.

作用 本発明においては、微小凹凸を化粧シートの最表層であ
る合成樹脂シートの裏面に直接形成するので、万一、微
小凹凸形成前にフィッシュアイの存在するような材料を
用いたとしても、微小凹凸形成の際に切削もしくはエン
ボスされて実質上加工面の凸状形状としては現れない。Function In the present invention, since the minute irregularities are directly formed on the back surface of the synthetic resin sheet, which is the outermost layer of the decorative sheet, even if a material with fish eyes is used before forming the minute irregularities, the minute irregularities will be When forming the unevenness, it is cut or embossed so that it does not substantially appear as a convex shape on the processed surface.

又、本発明に：ｔ６いては金属箔を使用せず、合成樹脂
シー）／／と一体化したご（薄い金属層を使用している
ので、熱による膨張・伸縮の差は実質上止じない。In addition, in the present invention: T6 does not use metal foil, but uses a thin metal layer integrated with synthetic resin sheet, so differences in expansion and contraction due to heat are virtually stopped. do not have.

効果 従って本発明においては従来解消できなかった化粧シー
トのフィッシュアイに基づく外観の不良、及び、化粧シ
ートの取り扱いの際のカールがいずれも解消される。Effects Therefore, in the present invention, both the poor appearance of the decorative sheet due to fish eyes and the curling caused when handling the decorative sheet, which could not be solved in the past, can be eliminated.

なお、従来の化粧シートではコ回のラミネート工程を要
したが、本発明の化粧シートでは層／３と層／４’の積
層の際にのみラミネート工程を行なうので、工程的に簡
略化でき、ラミネート時のごみの混入の確率も低下する
利点がある。In addition, conventional decorative sheets required multiple lamination processes, but the decorative sheet of the present invention performs the lamination process only when layer /3 and layer /4' are laminated, so the process can be simplified. This has the advantage of reducing the probability of contamination with dust during lamination.

実施例／ 厚み３ｇμｍのポリエチレンテレフタレートフィルムの
片面にヘアーライン加工を施した後、ヘアーライン加工
面にアルミニウムを厚みが／θｏｏｈになるよう蒸着し
、蒸着面に不飽和ポリエステル樹脂を塗布して厚み７０
μｍの感熱接着剤層とした。Example: After applying hairline processing to one side of a polyethylene terephthalate film with a thickness of 3 g μm, aluminum was vapor-deposited on the hairline-processed surface to a thickness of /θooh, and unsaturated polyester resin was applied to the vapor-deposited surface to obtain a thickness of 70 mm.
It was made into a heat-sensitive adhesive layer of μm.

得られた化粧シートはヘアーライン加工面にフィッシュ
アイによる欠点がな（、又、取り扱いに支障となるよう
なカールは生じなかった。The obtained decorative sheet had no defects due to fish eyes on the hairline-processed surface (and no curling that would impede handling occurred).

実施例コ 実施例／と同様にポリエチレンテレフタレートフィルム
にヘアーライン加工及びアルミニウム蒸着を行なった後
、アルミニウム蒸着面にポリスチレンフィルム（厚み１
３０μｍ）をウレタン系樹脂からなる接着剤を用いて貼
り合わせて化粧シートとしたところ、実施例／で得られ
たのと同様な効果が得られた。EXAMPLE After hairline processing and aluminum deposition were performed on a polyethylene terephthalate film in the same manner as in Example, a polystyrene film (thickness 1
30 μm) were bonded together using an adhesive made of urethane resin to form a decorative sheet, and the same effect as that obtained in Example 1 was obtained.

【図面の簡単な説明】[Brief explanation of the drawing]

第１図は本発明の化粧シートの断面図、第２図は従来の
化粧シートの断面図である。FIG. 1 is a sectional view of the decorative sheet of the present invention, and FIG. 2 is a sectional view of a conventional decorative sheet.

Claims (3)

【特許請求の範囲】[Claims] （１）合成樹脂シートの裏面に微小凹凸が形成されてお
り、前記微小凹凸形成面には金属薄膜層が形成されてお
り、更に前記金属薄膜層にはインジェクション成形用樹
脂と熱接着可能な合成樹脂層が積層されていることを特
徴とする化粧シート。(1) Fine irregularities are formed on the back surface of the synthetic resin sheet, a metal thin film layer is formed on the fine irregularity forming surface, and the metal thin film layer is made of a synthetic resin that can be thermally bonded to injection molding resin. A decorative sheet characterized by laminated resin layers. （２）合成樹脂層が感熱接着剤層であることを特徴とす
る特許請求の範囲第１項記載の化粧シート。(2) The decorative sheet according to claim 1, wherein the synthetic resin layer is a heat-sensitive adhesive layer. （３）微小凹凸がヘアーラインであることを特徴とする
特許請求の範囲第１項又は第２項いずれか記載の化粧シ
ート。(3) The decorative sheet according to claim 1 or 2, wherein the minute irregularities are hair lines.