JPS6096622A - Coloring composition for synthetic resin - Google Patents
Coloring composition for synthetic resinInfo
- Publication number
- JPS6096622A JPS6096622A JP20280583A JP20280583A JPS6096622A JP S6096622 A JPS6096622 A JP S6096622A JP 20280583 A JP20280583 A JP 20280583A JP 20280583 A JP20280583 A JP 20280583A JP S6096622 A JPS6096622 A JP S6096622A
- Authority
- JP
- Japan
- Prior art keywords
- pigment
- dye
- dispersant
- coloring composition
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
本発明は合成樹脂の着色剤に関し、更に詳しく云えばポ
リエチレンやポリプロピレン等のポリオレフィン系樹脂
およびその他の合成樹脂の着色に使用する着色剤組成物
の提供を目的とする。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a coloring agent for synthetic resins, and more specifically, an object of the present invention is to provide a coloring agent composition for use in coloring polyolefin resins such as polyethylene and polypropylene, and other synthetic resins.
従来、ポリエチレンやポリプロピレン等のポリオレフィ
ン樹脂およびその他の合成樹脂の着色剤として、染顔料
を低分子量ポリエチレンや脂肪酸金属石けん叫の分散剤
で分散処理した着色剤、あるいはこれらの分散剤を用い
て染顔料をポリエチレンその他の担体樹脂中に高濃度に
分散させたマスターバッチ等が使用されている。Traditionally, dyes and pigments have been dispersed with dispersants such as low molecular weight polyethylene and fatty acid metal soaps as colorants for polyolefin resins such as polyethylene and polypropylene, and other synthetic resins, or dyes and pigments using these dispersants have been used. A masterbatch or the like is used, in which the compound is dispersed at a high concentration in polyethylene or other carrier resin.
しかしながら、従来の粉末状着色剤やマスターバッチで
は染顔料濃度をあまり高くすることができず、また近年
ポリオレフィン系その他の合成樹脂の着色は高稀釈倍率
、高速着色の傾向にあり、従来の粉末状着色剤やマスタ
ーバッチでは十分な対応が困難になりつつあシ、特に薄
肉大型の射出成形品においては粉末状着色剤またはマス
ターバッチの被着色樹脂中への染顔料分散速朋が不十分
でらシ、そのために成形品の色むら等の外観不良の問題
が避けられない。However, with conventional powder colorants and masterbatches, the concentration of dyes and pigments cannot be made very high, and in recent years, the coloring of polyolefin-based and other synthetic resins has tended toward high dilution ratios and high-speed coloring. It is becoming increasingly difficult to provide sufficient support with colorants and masterbatches, especially in the case of thin-walled, large-sized injection molded products. Therefore, the problem of poor appearance such as color unevenness of the molded product is unavoidable.
本発明者は上述の如き従来技術の欠点を解決すべく鋭意
研究の結果、粉末状着色剤あるいはマスターバンチの分
散剤として特定の材料を選択することによって、粉末状
着色剤またはマスターバッチの染顔料含有量を高くして
も、粉末状着色剤またはマスターバッチ中の染顔料が被
着色樹脂中に高速分散し、上述の如き従来技術の欠点が
十分に解決できることを知見して本発明を完成した。As a result of intensive research in order to solve the above-mentioned drawbacks of the prior art, the present inventors have discovered that by selecting a specific material as a dispersant for a powder colorant or a masterbatch, the dye and pigment of a powder colorant or a masterbatch can be improved. The present invention was completed based on the finding that even if the content is high, the dye and pigment in the powdered colorant or masterbatch can be dispersed at high speed in the resin to be colored, and the above-mentioned drawbacks of the conventional technology can be sufficiently solved. .
す力わち、本発明は、染顔料および分散剤および必要に
応じて担体樹脂から成シ、上記分散剤が分子量約500
〜約10,000の直鎖状低密度ポリエチレン(L−L
DPE)ワックスであり、染顔料の含有量が約10〜約
90重量%である合成樹脂着色用組成物である。Specifically, the present invention comprises a dye/pigment, a dispersant, and optionally a carrier resin, and the dispersant has a molecular weight of about 500.
~10,000 linear low density polyethylene (L-L
DPE) wax, and is a synthetic resin coloring composition having a dye and pigment content of about 10 to about 90% by weight.
本発明の詳細な説明すると、本発明で使用し、主として
本発明を傷(i”i、づける分散剤は、従来公知でちシ
、密度が約0.90〜0.94の直錫状低密鹿ポリエチ
レン(L−LDPE)を適当な条件下で熱分解し、その
分子量を約500〜約10,000に減成して調製する
か、あるいはエチレンを適当な条件で分枝を有しないよ
うにして分子量約500〜約10,000のポリエチレ
ンに重合したワックス状ポリエチレンである。これらの
ポリエチレンワックスのうち本発明で最も好ましいもの
は分子量が約1,000〜約s、oooQものである。To explain the present invention in detail, the dispersant used in the present invention and mainly imparting the present invention is a conventionally known dispersant having a density of about 0.90 to 0.94. It is prepared by thermally decomposing L-LDPE under appropriate conditions to reduce its molecular weight to about 500 to about 10,000, or by preparing ethylene under appropriate conditions so that it has no branches. It is a waxy polyethylene polymerized to polyethylene having a molecular weight of about 500 to about 10,000. Among these polyethylene waxes, the most preferred in the present invention are those having a molecular weight of about 1,000 to about s and oooQ.
本発明者はこのような特定範囲のL−LDPEワックス
が、従来公知の分散剤である分校ポリエチレンワックス
や脂肪酸金属石けん等に比して著しくすぐれた染顔料の
高速分散性を有することを知見したものである。このよ
うなL−LDPEワックスは本発明において染顔料io
o重景部あたシ約40〜250重量部の割合で使用する
のが好ましい。The present inventor has discovered that such a specific range of L-LDPE wax has significantly superior high-speed dispersibility of dyes and pigments compared to conventionally known dispersants such as branched polyethylene wax and fatty acid metal soap. It is something. Such L-LDPE wax is used as dye and pigment io in the present invention.
It is preferable to use it in a ratio of about 40 to 250 parts by weight per weight area.
本発明において使用する染顔料とは従来ポリオレフィン
や他の合成樹脂の着色用として使用されている染顔料で
あシ、特に制限されるものではなく、代表的なものとし
ては実施例に示した如きポリアゾ顔料、フタロシアニン
順相、ペリノン・ペリレン染料、酸化チタン、弁柄等が
あげられる。The dyes and pigments used in the present invention are dyes and pigments that have been conventionally used for coloring polyolefins and other synthetic resins, and are not particularly limited. Examples include polyazo pigments, phthalocyanine normal phase, perinone/perylene dyes, titanium oxide, and Bengara.
これらの顔料は本発明の組成物において約30〜70重
量%の量で使用するのが好ましい。These pigments are preferably used in the compositions of the present invention in amounts of about 30-70% by weight.
本発明の着色用組成物の心頭成分は上述の通シであるが
その他、従来公知の低分子上(のポリエチレン等のワッ
クス類、ステアリン醒カルシウム、ステアリン酸亜鉛、
ステアリン酸マグネシウム、ステアリン酸アルミニウム
等の金属石けん類、その他必要な成分を自由に併用する
ことができる。The main components of the coloring composition of the present invention are as mentioned above, but in addition, conventionally known low molecular weight waxes such as polyethylene, calcium stearate, zinc stearate,
Metal soaps such as magnesium stearate and aluminum stearate, and other necessary ingredients can be freely used in combination.
更に本発明の着色用組成物はマスターバッチの形状でも
よく、このよう力場合は、染顔料100重量部あたシ約
60〜3.ooovit部の従来公知の担体樹脂、例え
ば低密度ポリエチレン、高密度ポリエチレン、ポリプロ
ピレン、エチレン−酢酸ビニルコポリマー、ポリスチレ
ン、ポリブテン、ポリ塩化ビニル、ポリアミド、ポリエ
ステル等従来公知の相体樹脂を目的物の着色目的に従っ
て選択して使用することができる。Further, the coloring composition of the present invention may be in the form of a masterbatch, and in such a case, the coloring composition of the present invention may be about 60-3. A conventionally known carrier resin for the ooovit part, such as low density polyethylene, high density polyethylene, polypropylene, ethylene-vinyl acetate copolymer, polystyrene, polybutene, polyvinyl chloride, polyamide, polyester, etc., is used for the purpose of coloring the target object. It can be selected and used according to the following.
上記の如き成分から成る本発明の着色用組成物の製造方
法自体は従来公知の方法がそのまま使用することができ
る。例えば、単軸押出機、二軸押出機、パンバリーミキ
ザー、ニーダ−13本ロール等の通常の混線機により上
記必要成分を加熱下溶融混練し、ベレット、粉末、フレ
ーク等の各種の形状に賦型することにより本発明の着色
用組成物を得ることができる。Conventionally known methods can be used as they are for producing the coloring composition of the present invention comprising the above-mentioned components. For example, the above-mentioned necessary ingredients are melted and kneaded under heat using a normal mixer such as a single-screw extruder, twin-screw extruder, Panbury mixer, or kneader with 13 rolls, and are formed into various shapes such as pellets, powder, and flakes. The coloring composition of the present invention can be obtained by shaping.
以上の如くして得られた本発明の着色用組成物は、ポリ
エチレン、ポリプロピレン、ポリブテン−1等のポリオ
レフィン系樹脂、ポリスチレン、ABS、ポリ塩化ビニ
ル、ポリアミド、ポリエステル、ポリカーボネート等の
着色剤として有用であり、特に顔料の高速均一分散が要
求される射出成形分野において有用であシ、従来の着色
剤に比して著しくすぐれた均一着色成形品を提供するこ
とができる。The coloring composition of the present invention obtained as described above is useful as a coloring agent for polyolefin resins such as polyethylene, polypropylene, polybutene-1, etc., polystyrene, ABS, polyvinyl chloride, polyamide, polyester, polycarbonate, etc. It is particularly useful in the field of injection molding, where high-speed uniform dispersion of pigments is required, and can provide uniformly colored molded products that are significantly superior to conventional colorants.
なお、文中の部または裂は特に断りのない限り重量基準
でおる。Note that parts and parts in the text are based on weight unless otherwise specified.
実施例1
酸化チタン(クイベークR−820、石業産業)60部
、ポリアゾ顔料(クロセフタールエロー301チバ・ガ
イギー)10部およびL−LDPE(分子量約1,00
0)30部を加圧ニーダ−中で加熱下十分に混線した後
取出し、冷却後粉砕し、赤色の粉末状の本発明の着色用
組成物(Ilを得た。Example 1 60 parts of titanium oxide (Kuibake R-820, Stone Industry), 10 parts of polyazo pigment (Croceftal Yellow 301 Ciba Geigy) and L-LDPE (molecular weight approx. 1,000)
0) 30 parts were stirred sufficiently under heating in a pressure kneader, taken out, cooled and pulverized to obtain a red powder coloring composition (Il) of the present invention.
実施例2
実施例1で得られた功末状着色用組成物707?3およ
び低密度ポリエチレン(スミカセン0806、住友化学
)30部を高速混合機中で十分に混合後、該混合物を単
軸押出機にて溶融混練し、ペレット状に押出成形し、本
発明のマスターバッチ状赤色着色用組成物曲を得た。Example 2 After thoroughly mixing the composition 707?3 for coloring powder obtained in Example 1 and 30 parts of low-density polyethylene (Sumikasen 0806, Sumitomo Chemical) in a high-speed mixer, the mixture was uniaxially extruded. The mixture was melt-kneaded in a machine and extruded into pellets to obtain a masterbatch-shaped red coloring composition of the present invention.
実施例3
酸化チタン(タイベークR−680、石原産業)30
部% Mフタロシアニンブルー(クロモファインブルー
4920、大日精化工業)10部、ステアリンn?l3
C−1、三菱油化)30部を高速混合機で十分混合しf
c後、得られたm合物を2軸押用機にて渭練し、ペレッ
ト状に成形して本発明の青色のマスターバッチ状着色用
組成物C1,)を行た。Example 3 Titanium oxide (Tie Bake R-680, Ishihara Sangyo) 30
Part % M Phthalocyanine Blue (Chromofine Blue 4920, Dainichiseika Industries) 10 parts, Stearin n? l3
Thoroughly mix 30 parts of C-1 (Mitsubishi Yuka) with a high-speed mixer.
After c, the obtained compound m was kneaded in a twin-screw extruder and formed into pellets to obtain a blue masterbatch-like coloring composition C1 of the present invention.
実Tltス例4
酸化チタン(タイオキサイドR−FC5、BTP)50
部、ペリノン糸虻料(カヤセットレッドAG、日化学)
30 部をバンバリーミキサ−で十分混練した後、混
線物な2本ロールミル、ペレタイザーでベレット状に賦
型して本発明の赤色着色用組成物(IV)を得た。Actual Tlt example 4 Titanium oxide (Tyoxide R-FC5, BTP) 50
Department, Perinone thread feed (Kayaset Red AG, Nikkagaku)
After fully kneading 30 parts in a Banbury mixer, the mixture was shaped into pellets using a two-roll mill and a pelletizer to obtain a red coloring composition (IV) of the present invention.
比較例1
実施例1におけるl、−LDPEワックスに代えて同量
の通常の分枝低布度ポリエチレンワックス(ハイワック
ス110P、三井石油化学、分子穿、約1,000 )
を使用し、他は実施例1と同様にして比較用の赤色着色
用組成物(I′)を得た0
比較例2
実施例2で使用した粉末状着色用組成物(nの代わりに
同量の比較例1の着色用組成物(工1)を使用し、他は
実施例と同様にして比較用の赤色マスターバッチ(■1
)を得た〇
比較例3
実施例3におけるL−LDPEワックスに代えて同量の
低分子量ポリエチレンワックス(AC−6、アライドケ
ミカル約2,000)を使用し、他は実施例3と同様に
して比較用の青色着色用組成物(■1)を得た。Comparative Example 1 In place of l,-LDPE wax in Example 1, the same amount of ordinary low-branched polyethylene wax (Hiwax 110P, Mitsui Petrochemical, Molecule Polymer, about 1,000) was used.
Comparative Example 2 A red coloring composition (I') for comparison was obtained in the same manner as in Example 1. The amount of the coloring composition (Part 1) of Comparative Example 1 was used, and a red masterbatch for comparison (Part 1) was prepared in the same manner as in Example.
) was obtained. Comparative Example 3 The same amount of low molecular weight polyethylene wax (AC-6, Allied Chemical approx. 2,000) was used in place of the L-LDPE wax in Example 3, and the other conditions were the same as in Example 3. A comparative blue coloring composition (1) was obtained.
比較例4
実施例4のL−LDPEワックスに代えて、同′5+t
″の低分子量ポリエチレンワックス(サンワックス13
1−P三洋化成、分子量約3,500)を使用し、他は
実施例4と同様にして比較用の赤色着色組成物(N’)
を得た。Comparative Example 4 In place of the L-LDPE wax of Example 4, the same '5+t
” low molecular weight polyethylene wax (Sunwax 13
A comparative red colored composition (N') was prepared in the same manner as in Example 4 except that 1-P Sanyo Chemical, molecular weight approximately 3,500) was used.
I got it.
使用例および比較使用例
実施例1〜4および比較例1〜4で得られたそれぞれの
着色用組成物2部を三種の被着色樹脂ioo部に配合し
、タンブラ−で混合後、射出成形温度220℃、背圧1
0 Kg / Cr+1で成形し、いろいろな色に着色
された成形板(ダイレクトゲート、縦200朋、横15
0闘、Hさ3 mm、 ) を得た。更にこの成形板の
ゲート部約100 vqm角を熱プレスして厚さ0、5
mの約200雁角のフィルムを作成し、透過光にて着
色組成物の顔料拡散性能(色むらの発生を訓1べたとこ
ろ、下記第1表の通シであった0なお第1表中の評価数
値は肉眼観察で評価したものであり、5が全く色むらの
発生が無く均一に着色されている状態を示し、1が著し
い色むらの発生を示し、2.3および4は1〜5の中間
を示している。Usage Examples and Comparative Usage Examples 2 parts of each of the coloring compositions obtained in Examples 1 to 4 and Comparative Examples 1 to 4 were blended with 10 parts of three types of resins to be colored, and after mixing in a tumbler, the injection molding temperature was 220℃, back pressure 1
0 Kg / Molded plate made of Cr+1 and colored in various colors (direct gate, length 200 mm, width 15 mm)
0 fighting, height 3 mm, ) was obtained. Furthermore, the gate part of this molded plate was heat-pressed to a thickness of 0.5 mm by approximately 100 vqm square.
A film of approximately 200 wild goose angles was prepared, and when the pigment diffusion performance of the colored composition was examined under transmitted light (for the occurrence of color unevenness), the results were as shown in Table 1 below. The evaluation values are evaluated by visual observation, and 5 indicates uniform coloring with no uneven coloring, 1 indicates significant uneven coloring, and 2.3 and 4 are 1 to 4. It shows the middle of 5.
第 1 表 ・1Table 1 ・1
Claims (1)
脂から成シ、上記分散剤が分子量約500〜約10,0
00の直鎖状低密度ポリエチレンワックスであり、染顔
料の含有量が約10〜約90重量係である合成樹脂着色
用組成物。(1) Comprised of a dye and pigment, a dispersant, and optionally a carrier resin, the dispersant having a molecular weight of about 500 to about 10.0
A synthetic resin coloring composition which is a linear low-density polyethylene wax of No. 00 and has a dye and pigment content of about 10 to about 90% by weight.