JPS6092071A - Belt for brazing furnace - Google Patents

Abstract

PURPOSE:To prevent erosion owing to sticking of molten solder and to eliminate the need for a stage for coating antisticking agent by using a specifically composed alloy to constitute a belt for a belt conveyor type brazing furnace and forming an oxide layer on the surface thereof. CONSTITUTION:A belt for brazing furnace is formed of an alloy consisting, by weight, of 10-35% Cr, 2-10% Al, <=2% >=1 kind among Ti, Zr, Hf, Y, Ce and La and the balance Fe. An oxide layer is formed on the surface of at least the part of the solder where the molten solder contacts. The oxide layer can be formed by heating the belt in an oxidative atmosphere. The belt has good resistance to melt sticking to the molten solder and has poor wettability with various brazing filler metals under brazing conditions and therefore the molten solder does not stick to said belt.

Description

【発明の詳細な説明】 〔発明の技術分野〕 本発明はベルトコンベア型ろう付は炉に用いるベルトに
関する〇 〔発明の技術的背景とその問題点〕 自動車部品、電気部品などの部品を組立てるために多量
生産でろう付けを行なう場合には、量産性の点から、被
ろう付は部品とろう材とを組込み水素ガスや不完全燃焼
ガスなどの還元性の雰囲気をもったろう付は炉内に連続
的に送入して、加熱してろう付けする炉中ろう付けが行
なわれている。[Detailed Description of the Invention] [Technical Field of the Invention] The present invention relates to a belt conveyor type brazing belt used in a furnace.[Technical background of the invention and its problems] For assembling parts such as automobile parts and electrical parts. When performing brazing in mass production, from the viewpoint of mass production, over-brazing should be done by assembling the parts and brazing material, and brazing in a reducing atmosphere such as hydrogen gas or incompletely combusted gas should be carried out in a furnace. Furnace brazing is carried out in which the material is continuously fed, heated, and brazed.

そして、炉中ろう付けには、メツシュベルトコンベア型
ろう付は炉が多く使用されている。For in-furnace brazing, a furnace is often used for mesh belt conveyor type brazing.

このろう付は炉は、第１図で示すように被ろう付は品を
搬送するために無端状のメツシュベルト１を設けたもの
で、このメツシュベルト１を駆動装置２により回転させ
、メツシュベルト１に載せた被ろう付は品を還元性葵囲
気の加啓部３に搬入してろう伺けを行なった１外に冷却
都４を通して冷却し、ろう付は作業を行なうものである
。メツシュベルト１は金属線材５を例えば第２図で示す
ように網状に編んだものを用いている。As shown in Fig. 1, this brazing furnace is equipped with an endless mesh belt 1 for conveying the item. Brazing is carried out by transporting the product into a heating section 3 with reducing air and cooling it through a cooling chamber 4 outside of the brazing section. The mesh belt 1 is made of a metal wire 5 knitted into a net shape as shown in FIG. 2, for example.

しかして、従来メツシュベルＩ−１は、耐熱性を考慮し
てステンレスｍ　（８ＵＳ　３１０など）からなる線材
を用いて形成していた。しかしながら、この場合メツシ
ュベルト１がろう付は炉の加熱部３を通過する時に、メ
ツシュベルト１の線材５に溶融ろうが付着して線材の溶
損を生じ易い欠点がある。このため、メツシュベルト１
に付着防止剤（Ａ４Ｏｓ　Ｔｉ１ｔ　Ｍ＆’０系ペース
ト）を塗布して、溶融ろうの付着を防止するようにして
いる。しかしながら、この場合は付着防止剤をメツシュ
ベルト１に塗布するのに手間がか＼る上に、ろう材の付
着を確実に防止することができない。結局、メツシュベ
ルト１は溶融ろうの付着による溶損のために破損して短
期間で使用が困難となり、１ケ月毎に父換を行なってお
り大変不経済であった。Conventionally, meshbel I-1 was formed using a wire made of stainless steel (8US 310, etc.) in consideration of heat resistance. However, in this case, there is a drawback that when the mesh belt 1 passes through the heating section 3 of the furnace during brazing, molten solder adheres to the wire 5 of the mesh belt 1 and the wire is likely to be melted and damaged. For this reason, Metschwert 1
An anti-adhesion agent (A4Os Ti1t M&'0 type paste) is applied to the surface to prevent molten solder from adhering. However, in this case, it takes time and effort to apply the anti-adhesion agent to the mesh belt 1, and it is not possible to reliably prevent the brazing material from adhering. In the end, the mesh belt 1 was damaged due to melting damage caused by the adhesion of molten solder, and became difficult to use in a short period of time, and the belt had to be replaced every month, which was very uneconomical.

〔発明の目的〕[Purpose of the invention]

本発明は前記事情を考慮してなされたもので、溶融ろう
の付着による溶損を防止して耐久性を高めるとともに、
付着防止剤塗布工程を不要として経済性を高めたろう付
は炉用ベルトを提供するものである。The present invention has been made in consideration of the above circumstances, and it prevents melting damage due to adhesion of molten solder and improves durability.
Brazing provides a furnace belt that is more economical by eliminating the need for an anti-adherent coating step.

本発明のろう偵は炉用ベルトは、重量比でクロム１０〜
３５％、アルミニウム２〜１０％、チタン、ジルコニウ
ム、ハフニウム、イツトリウム、セリウム、ランタンの
いずれが１種才たは複数種２％以下、残部鉄からなる合
金製で、且つ少くとも溶融ろうが接する部分の表面に酸
化層を有する拐料で構成されたものである。The wax furnace belt of the present invention has a weight ratio of chromium 10 to 10.
35% aluminum, 2% to 10% aluminum, 2% or less of one or more of titanium, zirconium, hafnium, yttrium, cerium, and lanthanum, the balance being iron, and at least the part that comes in contact with molten solder. The material is made of a fine material with an oxidized layer on its surface.

この発明のベルトを構成するθ金の組成において、クロ
ムは溶ろうに対する耐付着性をもたせる、ずなわぢ溶］
蝕ろうに対するぬれ性を低下させるためのもので、１０
％以上であると、効果が８着になり、一方、府尉の脆化
を考慮すると、３５％以下が好ましい。内には、１５〜
３０％か一層好ましい。アルミニウムはホ避表面に生成
する酸化層に不可欠の酸化アルミニウムの生成源となる
もので、２％以上あると、溶融ろうの剥離効果が充分と
なり、−勇肌工性の点から１０％以下か奸才しい。更に
は２〜４％カ好ｔＬ、い。チタン、ジルコニウム、ハフ
ニウム、イツトリウム、セリウム、ランタンは１．材を
表面の酸化層を緻密にしその剥離を防止するが、ホ屑の
脆化の点から、２％以下が奸才しく、更ζこは、１％以
下が奸才しい。In the composition of the θ gold constituting the belt of this invention, chromium provides adhesion resistance to melted solder.
It is used to reduce wettability against corrosive wax, and has a rating of 10
% or more, the effect will be 8th place.On the other hand, considering the embrittlement of Fujo, 35% or less is preferable. Inside is 15~
30% or more preferred. Aluminum is a source of aluminum oxide, which is essential for the oxidized layer that forms on the surface of the recess, and if the content is 2% or more, the peeling effect of the molten solder will be sufficient. So clever. Furthermore, 2 to 4% is preferable. Titanium, zirconium, hafnium, yttrium, cerium, and lanthanum are 1. The oxidation layer on the surface of the material is made dense to prevent its peeling, but from the viewpoint of embrittlement of dust, it is recommended to use 2% or less, and 1% or less is recommended for oxidation.

表面の酸化層は、溶融ろうに対する耐付着性をもたせる
もので、酸化アルミニウムを含む基体合金の酸化物層で
ある。The oxide layer on the surface provides adhesion resistance to molten solder and is an oxide layer of the base alloy containing aluminum oxide.

本発明のベルトの一例としてメツシュベルトを製作する
場合には、前記の組成をなす合金により線材を製造し、
この線材を所定の網目例えば第２図で示す網目に編んで
ベルトを構成する。When manufacturing a mesh belt as an example of the belt of the present invention, a wire rod is manufactured from an alloy having the above composition,
This wire is woven into a predetermined mesh, for example the mesh shown in FIG. 2, to construct a belt.

そして、このベルトを酸化１ｇ　１ｔ＋］気中にて加熱
して、４η材の表面ｌこ酸化膜を形成する。得られたメ
ツシュベルトは、メツシュベルトコンベア型ろう付は炉
に装着して使用する。Then, this belt is heated in an atmosphere of 1 g of oxidation and 1 t+] to form an oxide film on the surface of the 4η material. The obtained mesh belt is used by being attached to a furnace for mesh belt conveyor type brazing.

しかして、本発明のメツシュベルトに用いる線材は、溶
融ろうに対する耐付着性が良好で、ろう付は粂件下にて
各種ろう材（銅ろう、銀ろう、ニッケルろう、ハンダな
ど）とのぬれ性か惑いので、溶融ろうが付着することが
ない。従つて、本発明のメツシュベルトは、ろう伺は炉
に装着して使用する場合に、炉内にて溶融ろうが線材ζ
こ付着せず、溶融ろうによる線材の溶損を防止できる。Therefore, the wire rod used in the mesh belt of the present invention has good adhesion resistance to molten solder, and has good wettability with various brazing materials (copper solder, silver solder, nickel solder, solder, etc.) under the brazing material. Since it is confusing, molten wax will not stick to it. Therefore, when the mesh belt of the present invention is used by attaching the solder wire to a furnace, the wire rod ζ melts in the furnace.
This prevents the wire from being eroded and damaged by the molten solder.

このため、線材に付着防止剤を塗布する必要がない。Therefore, there is no need to apply an anti-adhesion agent to the wire.

〔発明の実施例〕[Embodiments of the invention]

クロム２０％−アルミニウム３％−チタン０．３％−ジ
ルコニウム０．３％−残部鉄からなる合金により形成さ
れた月経３ｇの緑林を編んでメツシュベルトを製作した
。このメツシュベルトを連ｊ＋５？ろう付は炉に装着し
て、露点−２０℃の４水素辱囲電下で１２００℃、１時
間の連続酸化処理を行ない、線材の表面に酸化膜を形成
した。その後に、ろう付は炉においてＣＨ４不完全燃焼
雰囲気（弱還元雰囲気）下ζこて湿層１１２０℃で銅ろ
う材を用いたろう伺は作業を連続的に行なった。この、
時果、メツシュベルトは約３０００時間以上使用できた
。これに対して比較例としてステンレスｍ４（ｓｕｓ３
ｏｔ）からなる線材によりメツシュベルトを製作し、こ
のメツシュベルトの線材に付着防止剤としてΔ１２ｏ、
−″Ｉ’１０２Ｍ７０系ペーストを塗布した。A mesh belt was made by knitting 3 g of green forest made of an alloy consisting of 20% chromium, 3% aluminum, 0.3% titanium, 0.3% zirconium, and the balance iron. Is this metschbelt a series j + 5? For brazing, the wire was placed in a furnace and subjected to continuous oxidation treatment at 1200°C for 1 hour under a tetrahydrogen atmosphere with a dew point of -20°C to form an oxide film on the surface of the wire. Thereafter, brazing was performed continuously in a furnace using a copper brazing filler metal at a wet layer of 1120° C. under a CH4 incomplete combustion atmosphere (weakly reducing atmosphere). this,
As a result, Metschbelt could be used for over 3,000 hours. On the other hand, as a comparative example, stainless steel m4 (sus3
A mesh belt is manufactured using a wire rod consisting of ot), and Δ12o,
-''I'102M70 series paste was applied.

そして、このメツシュベルトをろう付は炉に装着して、
＋１ｉ、ｌ記の場合と同一条件でろう付けを行なった。Then, attach this mesh belt to the furnace for brazing,
Brazing was performed under the same conditions as in +1i and 1.

この結果、このメツシュベルトは約５００時間使用でき
た。従って、本発明のメツシュベルトは６倍以上の寿命
を突することが判る。As a result, this mesh belt could be used for about 500 hours. Therefore, it can be seen that the mesh belt of the present invention has a service life that is 6 times longer.

〔発明の効果〕〔Effect of the invention〕

本発明のろうイ」け炉用ベルトは以上説明したようζこ
、ろう付は炉における液融ろうによる溶損を防止して寿
命を高め、且つ付着防止剤の塗布を不要にして経済性を
向上できる。As explained above, the belt for a brazing furnace of the present invention has the advantage that brazing prevents melting damage caused by liquid melting solder in the furnace, increases the service life, and eliminates the need to apply an anti-adhesive agent, making it economical. You can improve.

【図面の簡単な説明】[Brief explanation of the drawing]

第１図はベルトコンベア型ろう付は炉を概略的ζこ示す
正面図、第２図はベルトの一部を拡大して示す平１ｍ図
である。 １・・・メツシュベルト、５・・・線材。FIG. 1 is a front view schematically showing a furnace for belt conveyor type brazing, and FIG. 2 is a 1 m plan view showing an enlarged part of the belt. 1... Metschbelt, 5... Wire rod.

Claims (2)

【特許請求の範囲】[Claims] （１）重量比でクロム１０〜３５％、アルミニウム２〜
１０％、チタン、ジルコニウム、ハフニウム、イツトリ
ウム、セリウム、ランタンのいずれか１種才たは複数種
２％以下、残部鉄からなる合金製で、且つ少くとも溶融
ろうと接する部分の表面に酸化層を有する材料で構成さ
れていることを特徴とするろう付は炉用ベルト。(1) Chromium 10-35%, aluminum 2-2% by weight
Made of an alloy consisting of 10% titanium, zirconium, hafnium, yttrium, cerium, lanthanum or less than 2% of any of them, and the balance iron, and has an oxide layer on the surface of at least the part that comes into contact with the molten solder. Brazing belts for furnaces are characterized by being composed of materials. （２）ベルトがメツシュベルトである特許請求の範囲第
１項に記載のろう付は炉用ベルト。(2) The brazing belt for a furnace according to claim 1, wherein the belt is a mesh belt.