JPS6057346A - Image bearing member - Google Patents

Abstract

PURPOSE:To improve surface smoothness, cleanability, abrasion resistance, etc., by coating the image bearing layer of an image bearing member for bearing an electrostatic image and/or a toner image with a coating soln. contg. hydrophobic silica. CONSTITUTION:The image bearing layer of an image bearing member composed of a substrate 21 and said layer for bearing an electrostatic image and/or a toner image is coated with a coating soln. contg. hydrophobic silica. Said layer is, e.g., a photoconductive layer 22 or a protective layer 23 formed on the layer 22. The layer 22 may be a functionally separated type composed of an electrostatic charge generating layer and a charge transfer layer, and in this case, preferably, the transfer layer is overcoated with the generating layer. As a result, the image bearing member can be improved in surface smoothness, cleanability, abrasion resistance, and adhesion of the surface layer to the underlayer by incorporating the hydrophobic silic powder in the coating soln. for forming the surface layer on which an electrostatic image and/or a toner image is to be formed.

Description

【発明の詳細な説明】 本発明は、静電像および／またはトナー画像を保持する
ための像保持部材に関するもので、特に像保持部材の表
面性、耐摩耗性、耐久性を改良したものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to an image holding member for holding an electrostatic image and/or a toner image, and particularly an image holding member having improved surface properties, abrasion resistance, and durability. be.

本発明は、電子写真複写機、レーザープリンタ、または
画像表示装置などに用いられる像保持部材面上に各種情
報信号の入力に対応した静電像および／またはトナー画
像を形成する像保持層に関するものであシ、これらは種
々のプロセスによって形成される。そして、静電像およ
び／またはトナー画像が形成される像保持部材としては
、電子写真感光体と称せられる光導電層を有する像保持
部材と光導電層を有しない像保持部材とがある。像保持
部材は通常、支持体とその上にある像保持層から構成さ
れる。The present invention relates to an image holding layer that forms an electrostatic image and/or toner image corresponding to input of various information signals on the surface of an image holding member used in an electrophotographic copying machine, a laser printer, an image display device, etc. However, they are formed by various processes. Image holding members on which electrostatic images and/or toner images are formed include image holding members that have a photoconductive layer and those that do not have a photoconductive layer, which are called electrophotographic photoreceptors. Image bearing members typically consist of a support and an image bearing layer thereon.

電子写真感光体は、所定の特性を得るため、あるいは適
用される電子写真プロセスの種類に応じて種々の構成を
とる。例えに、支持体上に光導電層が形成される感光体
、及びその上に絶縁層を備えた感光体がある。この代表
的な例は例えば米国特許第２１１１６００４８号公報、
特公昭４１−１６４２９号公報、特公昭５Ｂ−１５４４
６号公報、特公昭４６−３７１３号公報、特公昭４２−
２３９１０号公報、特公昭４３−２４７４８号公報、特
公昭４２−１９７４７号公相ｖ号公報”Ｆ公昭５６−４
１２１号公報などに記載されている。Electrophotographic photoreceptors have various configurations in order to obtain predetermined characteristics or depending on the type of electrophotographic process to which they are applied. For example, there are photoreceptors in which a photoconductive layer is formed on a support, and photoreceptors in which an insulating layer is provided thereon. A typical example of this is, for example, US Pat. No. 2,111,60048,
Special Publication No. 41-16429, Special Publication No. 5B-1544
Publication No. 6, Special Publication No. 3713 (1973), Special Publication No. 42-
23910 Publication, Special Publication No. 43-24748, Special Publication No. 42-19747 Publication No. V "F Publication No. 56-4
It is described in Publication No. 121, etc.

また、光導電層を電荷発生層と電荷輸送層からなる積層
構造とした感光体がある。例えば、特開昭４９−１０５
５３７号、特開昭５１−９０８２７号、米国特許第３４
８４２３７号、米国特許第３８７１８８２号各公報に記
載されている。There is also a photoreceptor in which the photoconductive layer has a laminated structure consisting of a charge generation layer and a charge transport layer. For example, JP-A-49-105
No. 537, JP-A No. 51-90827, U.S. Patent No. 34
No. 84237 and US Pat. No. 3,871,882.

電子写Ｘ感光体には、所定の電子写真プロセスに適用さ
れて、静電像が形成され、このｗＰ電像が現像されて可
視化される。A predetermined electrophotographic process is applied to the electrophotographic X photoreceptor to form an electrostatic image, and this wP electrophotographic image is developed and visualized.

また、像保持部材として光導電層をイｊし、露光と同時
にトナー画像を形成する電子写真プロセスがある。（特
願昭５６−１９７４１０他）とのプ四セスを利用した一
例を第２図（ａ）と第２図（１））で示す。There is also an electrophotographic process in which a photoconductive layer is used as an image holding member and a toner image is formed simultaneously with exposure. (Japanese Patent Application No. 56-197410, etc.) An example of using the process is shown in FIG. 2(a) and FIG. 2(1)).

第２図（ａ）は上記方式の画像表示装置の一例の極く概
略構造を示す縦断側面図である。１は縦型の装置外装箱
、２はその外装箱の正面板面に大きく開口形成した表示
画像覗き窓で、一般にガラス板等の透明板３が張設され
る。FIG. 2(a) is a longitudinal sectional side view showing a very schematic structure of an example of an image display device of the above type. 1 is a vertical device exterior box; 2 is a display image viewing window formed with a large opening on the front surface of the exterior box; generally a transparent plate 3 such as a glass plate is attached thereto;

４は外装箱内の上部と下部とに並行に横設した駆動プー
リ（又はローラ）５と従動プーリ（同）６間に張設した
無端ベルト型の感光体（像保持体、以下単にベルトと略
記する）である。該ベルトは例えば第２図（ｂ）のよう
に合成樹脂シート或はフィルムなど透明で且つ抗張性に
富む強靭なペースシート材４１の外面に金属や金属酸化
物（酸化インジウム、酸化錫、酸化クロム）を薄く蒸着
して透明導電層４２を形成してなるものを透明導電性基
体層４３とし、その導電層４２面に光導電体Ｎ４４を塗
布法、蒸着法等で積層形成したもので、ベルト４の外周
面が光導電体層面である。そして該ベルト４は駆動プー
リ５の回転によシ矢示方向に回転駆動され、ベルト４の
張シ側外面が表示画像覗き窓２部を下から上へ移動通過
する。Reference numeral 4 denotes an endless belt type photoreceptor (image carrier, hereinafter simply referred to as belt) stretched between a driving pulley (or roller) 5 and a driven pulley (same) 6, which are installed horizontally in the upper and lower parts of the outer box. (abbreviated). For example, as shown in FIG. 2(b), the belt is made of a transparent and strong pace sheet material 41, such as a synthetic resin sheet or film, which is coated with metals or metal oxides (indium oxide, tin oxide, oxide, etc.) on the outer surface. A transparent conductive layer 42 is formed by thinly vapor-depositing chromium), which is used as a transparent conductive base layer 43, and a photoconductor N44 is laminated on the surface of the conductive layer 42 by a coating method, a vapor deposition method, etc. The outer peripheral surface of the belt 4 is the photoconductor layer surface. The belt 4 is rotationally driven in the direction of the arrow by the rotation of the drive pulley 5, and the tension side outer surface of the belt 4 moves past the display image viewing window 2 from the bottom to the top.

１０は上記回動ベルトの張）側ベルト部分とゆるみ側ベ
ルト部分の間の空間内に配収した光ビームスキャニング
方式の光像露光装置で、半導体レーザ（或はガスレーザ
）・ポリゴンミラー・ｆθレンズ等からなる。そして図
に省略した画像読取シ装置、電子計詐機等から時系列電
気デジタル画素信号Ｓの入力を受け、その信号に対応し
て変調されたレーザビームＬを従動プーリ６方向に発振
する。その発振されたビームは途中ミ２−１１によシ張
シ側ベルトの従動プーリ６寄シの裏面部位Ａに向かって
偏向され、スリット板１２のスリット１２ａを通してそ
のベルト裏面部位Ａをベルト幅方向に走査露光する。Reference numeral 10 denotes a light beam scanning type optical image exposure device disposed in the space between the tension side belt part and the slack side belt part of the rotating belt, which includes a semiconductor laser (or gas laser), a polygon mirror, and an f-theta lens. Consists of etc. Then, it receives a time-series electric digital pixel signal S from an image reading device, an electronic fraud device, etc. (not shown), and oscillates a laser beam L modulated in accordance with the signal in the direction of the driven pulley 6. The oscillated beam is deflected on the way by Mi 2-11 toward the back side part A of the driven pulley 6 of the side belt, and passes through the slit 12a of the slit plate 12 to pass the belt back part A in the belt width direction. scan and expose.

このレーザビームＬのベルト幅方向走査を主走査とし、
ベルト４の移動を幅走査としてベルト４の裏面に対して
順次に光像露光がなされる。This scanning of the laser beam L in the belt width direction is referred to as main scanning,
The movement of the belt 4 is performed as a width scan, and the back surface of the belt 4 is sequentially exposed to light images.

１５は上記レーザビーム走査露光を受けるベルト裏面部
位Ａに対応するベルト表側位置に配設した現像装置、１
４は張シ側ベルトのｈ面１１１ｊで露光部位Ａのベルト
移動方向下流側部位に配設した全面光照射用２ングであ
る。Reference numeral 15 denotes a developing device disposed at a position on the front side of the belt corresponding to the back side part A of the belt that receives the laser beam scanning exposure;
Reference numeral 4 designates a second ring for irradiating the entire surface with light, which is disposed on the h-plane 111j of the tension side belt at the downstream side of the exposure area A in the belt movement direction.

図示例の現像装置１３は現像剤収容箱１５と、その箱１
５内に横設し左側路半局面を箱内から外部に露出させた
ステンレススチール、アルミニウム等の非磁性体性の回
転現像スリーブ１６と、そのスリーブ１６内に挿入内蔵
させたマグネットロー２１７と、スリーブ外面に対する
現像剤塗布ブレード１８と、箱１５内に収容した現像剤
（導電性磁性トナー）Ｔとからなる。箱１５内の導電性
磁性トナーＴは回転現像スリーブ１６近傍部のトナーが
スリーブ内部のマグネットローシ１７の磁界に引かれて
磁気吸着層としてスリーブ外周面に保持されてスリーブ
と共に回動し、途中ブレード１８でその層厚が規制され
て整層化され、そのトナー整層面がスリーブの回動でベ
ルト裏面光像露光部位人に対応するベルト表面部に接触
通過する。The illustrated developing device 13 includes a developer storage box 15 and the box 1.
A rotary developing sleeve 16 made of a non-magnetic material such as stainless steel or aluminum, which is horizontally disposed inside the box and whose left side half curve is exposed to the outside from inside the box, and a magnet row 217 that is inserted and built into the sleeve 16. It consists of a developer applying blade 18 to the outer surface of the sleeve and a developer (conductive magnetic toner) T housed in a box 15. The conductive magnetic toner T in the box 15 is attracted by the magnetic field of the magnet roller 17 inside the sleeve, and is held on the outer peripheral surface of the sleeve as a magnetic adsorption layer, rotating together with the sleeve, and the toner near the rotating developing sleeve 16 is attracted by the magnetic field of the magnet roller 17 inside the sleeve. At step 18, the layer thickness is regulated and layered, and the toner layered surface comes into contact with and passes through the belt surface portion corresponding to the light image exposure area on the back side of the belt by rotation of the sleeve.

ベルト４側の導電層４２と現像スリーブ１６間には直流
バイアスを印加させてあシ、Ｅはその電源を示す。A DC bias is applied between the conductive layer 42 on the side of the belt 4 and the developing sleeve 16, and E indicates the power source.

而して画像表示はベルト４及び現像装置１６の駆動がな
された状態においてベルト４の裏面側の露光部位Ａに光
像露光が開始されると後述の原理によシベルト表面側に
現像スリーブ１６側の導電性トナーが選択的に付着して
謝光像に対応したトナー像が形成される。トナー画像の
形成されたベルト表面は画像覗き窓２の範囲内に回動位
置して一旦停止する。これによシ窓２部に画像表示がな
される。所定の一定時間経過後、又はベルト再回動釦操
作でベルト４は再回動し次の表示画像が窓２部に移行し
、ベル）の、一時停止、画像表示がなされる。この繰シ
返しによシ画像の順次表示がなされる。Accordingly, when image exposure is started on the exposure area A on the back side of the belt 4 while the belt 4 and the developing device 16 are driven, the image is displayed on the front side of the belt on the side of the developing sleeve 16 according to the principle described later. The conductive toner is selectively adhered to form a toner image corresponding to the X-ray image. The belt surface on which the toner image has been formed is rotated to a position within the range of the image viewing window 2 and once stopped. As a result, an image is displayed on the second window. After a predetermined period of time has elapsed, or by operating the belt re-rotation button, the belt 4 is rotated again and the next display image is moved to the window 2, and the bell (bell) is temporarily stopped and the image is displayed. By repeating this process, the images are sequentially displayed.

画像表示が終了しその後のベルト回動で再び現像装置１
３部位に至ったベルト表面の表示済みトナー画像は現像
装置の現像兼クリーニング作用でベルト表面から除去さ
れて現像装置側へ回収される。トナー画像の除去された
ベルト表面に紘引続いて露光部位Ａにおける光像露光パ
ターンに対応したトナー画像が順次に形成されそのトナ
ー画像がベルト４０回動に伴ない表示窓２部へ移行する
。After the image display ends, the belt rotates and the developing device 1 is turned on again.
The displayed toner images on the belt surface that have reached the three positions are removed from the belt surface by the developing and cleaning action of the developing device and are collected into the developing device. On the belt surface from which the toner image has been removed, toner images corresponding to the light image exposure pattern at the exposure area A are sequentially formed, and as the belt 40 rotates, the toner images are transferred to the display window 2 part.

全面光照射用ランプ１４は光像露光部位Ａを通過して表
面側にトナー画像の形成されたぺ〃ト良面側を幅方向一
様に光照射することによシベルト４の光導電体４４内部
の電気的状態を各部−株化させるために配設したもので
ある。The entire surface light irradiation lamp 14 passes through the light image exposure area A and irradiates the photoconductor 44 of the belt 4 uniformly in the width direction on the good side of the tape on which the toner image is formed on the front side. It is arranged to separate the internal electrical status of each part.

上記やように表示画像を光導電体を利用した像担持体面
にトナー像として形成して画像表示する方式のものは例
えばＣＲＴディスプレイ装置や液晶利用のディスプレイ
装置よシも解像性がよい、静止画像でちらつきがないの
で、又液晶ディスプレイのように角度依存性も小さいこ
とから画像が見易く目疲れが少ない、表示画像の必要な
ものについてはベルト面に形成されたトナー像を複写紙
面に転写する機構を付加することによシ答易に７１−ト
コピーを得ることができる等の利点を有する。特に上記
例のように無帯電、露光同時トナー画像形成方式で、且
つ現像とクリーニングを兼用させたものは装置構成が極
めて簡単なものとなシ実用性に富むものでおる。The above-mentioned system that displays images by forming them as toner images on the surface of an image carrier using a photoconductor has good resolution and is stationary compared to, for example, CRT display devices and display devices that use liquid crystals. Since the image does not flicker, and unlike a liquid crystal display, the angle dependence is small, the image is easy to see and reduces eye strain.For those that require a displayed image, the toner image formed on the belt surface is transferred to the copy paper surface. It has the advantage that 71 copies can be easily obtained by adding a mechanism. Particularly, as in the above example, a toner image forming system that is non-charging and uses simultaneous exposure, and also has both development and cleaning functions, has an extremely simple device configuration and is highly practical.

光導電層を有しなり像保持部旧の代表的なイ・Ｒ成は、
像保持層として絶縁層を有するものであシ、とＯ像保持
部材の用途の代表的な例を次に貌明する。Typical I/R configurations of old image holding parts that have a photoconductive layer are:
A typical example of the use of an image holding member having an insulating layer as an image holding layer will be explained below.

（１）例えば、特公昭５２−７１１５号公報、特公昭５
２−８２０４号公報、特公昭４３−１５５９号公報に記
載されているように、電子写真感光体の繰返し使用性の
改善の目的で電子写真感光体に形成された静電像を光導
１６層を持たない像保持部材に転写して現ｆ象を行い、
次いでトナー画像は記録体に転写される。(1) For example, Japanese Patent Publication No. 52-7115, Japanese Patent Publication No. 52-7115,
As described in Japanese Patent Publication No. 2-8204 and Japanese Patent Publication No. 43-1559, an electrostatic image formed on an electrophotographic photoreceptor is coated with 16 photoconductive layers for the purpose of improving the repeatability of the electrophotographic photoreceptor. A phenomenon is performed by transferring the image to an image holding member that does not have the image,
The toner image is then transferred to a recording medium.

この電子写真プロセスに用いられる像保持部材。An image holding member used in this electrophotographic process.

（２）まだ、電子写真感光体に形成された静電像に対応
させて光導電層を持たない像保持部材に静電像を形成さ
せ諷他の電子写真プロセスとして、例えば、特公ＦＩｒ
３４ｓ−３ｏ　５２０号公報、特公昭４Ｂ−５０６５号
公報、特開昭５１−３４１号公報などに記載されている
ように、多数の微細な開口を有するスクリーン状の電子
写真感光体に所定の電子写真プロセスによって静電像を
形成し、この静ｌｉＬ像を介して光導電層を持たない像
保持部材にコロナ帯電処理を行なうことにより、コμす
のイオン流を変調させて静電像を光導電層を持たない像
保持部材に形成させて、これをトナー現像して記録体に
転写させて最終画像を形成するプロセスが挙げられる。(2) There are still other electrophotographic processes in which an electrostatic image is formed on an image holding member without a photoconductive layer in correspondence with an electrostatic image formed on an electrophotographic photoreceptor, for example,
34s-3o No. 520, Japanese Patent Publication No. 4B-5065, Japanese Patent Application Laid-open No. 51-341, etc., a screen-shaped electrophotographic photoreceptor having many fine openings is exposed to a predetermined number of electrons. An electrostatic image is formed by a photographic process, and an image holding member without a photoconductive layer is subjected to corona charging treatment via this electrostatic LiL image, thereby modulating the ion flow in the glass and exposing the electrostatic image to light. Examples include a process in which a conductive layer is formed on an image holding member without a conductive layer, developed with toner, and transferred to a recording medium to form a final image.

この電子写真プロセスに用いられる像保持部材。An image holding member used in this electrophotographic process.

（３）また、他の電子写真プロセスによれば、電子写真
感光体もしくは光導電層を持たない像保持部材に形成さ
れたトナー画像を直接記録体に転写しないでさらに他の
光導電層を持たない像保持部材に転写し、次いでこの像
保持部材から記録体にトナー画像を転写して定着する。(3) In addition, according to other electrophotographic processes, a toner image formed on an electrophotographic photoreceptor or an image holding member without a photoconductive layer is not directly transferred to a recording medium, but instead a toner image formed on an electrophotographic photoreceptor or an image holding member without a photoconductive layer is provided with another photoconductive layer. Then, the toner image is transferred from this image holding member to a recording medium and fixed.

この電子写真プロセスに用いられる像保持部材。このプ
ロセスはカラー画像の形成あるいは高速複写に特に有効
である。記録体は通常、紙、フィルムといった屈曲性に
富んだものが多く、そのために、三色画像を正確に位置
合せをしながら記録体に転写するよシも、変形を殆ど生
ずることがないような拐料で形成できる像保持部材に三
色画像を転写し、これを一度に記録体に転写した方がよ
シ正確に位置合せされたカラー画像が形成される。An image holding member used in this electrophotographic process. This process is particularly useful for forming color images or for high speed copying. Recording media are usually highly flexible, such as paper or film, so even if a three-color image is accurately aligned and transferred onto the recording media, there will be almost no deformation. A more accurately registered color image is formed by transferring a three-color image to an image-bearing member, which can be formed from a coating material, and then transferring it to a recording medium all at once.

また、複写の高速化に対しても、トナーｉ１！ＩＩ　ｉ
＆が像保持部材を経て記録体に転写されることは有効で
ある。In addition, toner i1! also helps speed up copying. II i
It is effective that & is transferred to the recording medium via the image holding member.

（４）また、他に、像保持部材を有する防電体に針電極
で電気信号を印加して静１！像を得、トナー像を形成す
る（実開昭５７−５５０６１他）。(4) In addition, an electric signal is applied to the electrically shielding body having the image holding member using a needle electrode. An image is obtained and a toner image is formed (Utility Model Publication No. 57-55061, etc.).

（５）　また、他に磁化容易スタイラスを用いて、磁性
粉や磁性流体のトナーを磁化信号に応じて像保持部面に
顕像化する。(5) Additionally, an easily magnetizable stylus is used to visualize magnetic powder or magnetic fluid toner on the image holding portion surface according to the magnetization signal.

（１）〜（５）のようなものに適用される像保持部拐は
、物理的特性、電気的特性が要求されるが、そればかシ
でなく像保持部材の耐久性およびクリーニング性も重要
な性質である。耐久性は像保持部材を繰シ返し使用する
場合に要求される性質であシ、クリーニング性は像保持
部材の表面に付着し、残留するトナーの除去の容易性を
め 丙φ性質であシ、鮮明な画像の形成、更にはクリーニグ
手段の損傷防止に著しく影響を与えるものである。The image holding member used in items (1) to (5) requires physical and electrical properties, but the durability and cleanability of the image holding member are also important. It is a characteristic. Durability is a property required when the image holding member is used repeatedly, and cleanability is the property required to remove residual toner that adheres to the surface of the image holding member. This significantly affects the formation of clear images and also the prevention of damage to the cleaning means.

従来の像保持部材では、表面平滑性、耐摩耗性が満足で
きる程十分なものでなく、繰シ返し使用するとクリーニ
ング不良などによる地汚れが目立つような欠点を有して
いる。Conventional image holding members do not have satisfactory surface smoothness and abrasion resistance, and have the disadvantage that when used repeatedly, scumming becomes noticeable due to poor cleaning.

本発明の目的は、前述の欠点を解消した新規な像保持部
材を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide a novel image holding member that eliminates the above-mentioned drawbacks.

本発明の別の目的は、像保持部材の表面性、りｙ−ニン
グ性、耐摩耗性が改良された像保持部材を提供すること
にある。Another object of the present invention is to provide an image holding member that has improved surface properties, y-wearing properties, and abrasion resistance.

本発明のかかる目的は、疎水性シリカを含有する像保持
部材によって達成される。Such objects of the present invention are achieved by an image bearing member containing hydrophobic silica.

従来の像保持部材で用いていたシリカ粉末拡、水を分散
媒としたもので、水の中でシリカ粒子が無数に分散し、
かつ安定化したものがあル、またメチ〃またはエテルア
ルコールなどの水と自く混合する親水性有ａ溶媒に分散
させたシリカ粒子が知られている。このような水分散系
のシリカ粉末は、樹脂の選択、限定や吸湿性に問題があ
った。The silica powder used in conventional image holding members is expanded using water as a dispersion medium, and countless silica particles are dispersed in the water.
Further, stabilized silica particles are known, as well as silica particles dispersed in a hydrophilic a-solvent that is easily miscible with water, such as methane or ether alcohol. Such water-dispersed silica powder has problems in the selection and limitation of resins and hygroscopicity.

本発明で用いる疎水性シリカ粉末は、例えば水分散系シ
リカ粒子のシラノール基を有機硅素ハロゲン化物または
アルコール類と置換するなどの方法で、シリカ粒子の表
面を疎水化処理を施すことによって疎水性有機溶媒に分
１１にさせることができる。このようなシリカ粉末は、
−次粒子径が数十〜数百又と非常に微細で、単位重量当
シの表面積が数十〜数百ｍ２／ｇと非常に大きいため、
溶媒中に分散させてもコロイド状に分散しかつ安定化し
たものである。また、この分散液から溶媒を蒸発させる
ことにより、コロイド状シリカは、物質の凹凸部に強固
に付着し、かつ良好な接着性を示す。つまシ、疎水性シ
リカ粉末を樹脂と有機溶媒中に混合、分散、塗工すると
、乾燥後には表面平滑性があり、接着性を増すことがで
きた。The hydrophobic silica powder used in the present invention is produced by hydrophobically treating the surface of the silica particles by, for example, replacing the silanol groups of the water-dispersed silica particles with an organosilicon halide or alcohol. The solvent can be allowed to run for 11 minutes. Such silica powder is
-The particle size is extremely fine, ranging from tens to hundreds of squares, and the surface area per unit weight is extremely large, ranging from tens to hundreds of m2/g.
Even when dispersed in a solvent, it remains colloidally dispersed and stabilized. Furthermore, by evaporating the solvent from this dispersion, colloidal silica firmly adheres to the uneven parts of the substance and exhibits good adhesive properties. When hydrophobic silica powder was mixed, dispersed, and applied in a resin and an organic solvent, the surface became smooth after drying, and adhesiveness was increased.

この種の疎水性シリカ粉末の市販品として、１アエロジ
＃Ｒ−９７２”（日本アエロシ／Ｉ／■製）。A commercially available product of this type of hydrophobic silica powder is 1 Aerosi #R-972'' (manufactured by Nippon Aerosi/I/■).

’　０８ＣＡＰ”、’　０８ＣＡＬ”（触媒化成工業■
製）、１ホワイトカーボン”などを用いることができる
。'08CAP'', '08CAL'' (Catalyst Chemical Industry ■
(manufactured by), 1 White Carbon, etc. can be used.

本発明の像保持部材は、前述の疎水性シリカ粉末を含有
させる点に特徴を有している。従ってこの種の像保持部
材は、静電像または／およびトナー画像を形成する表面
層中に疎水性シリカ粉末が含有されることにより、像保
持部材の表面平滑性、クリーニング性、耐摩耗性、表面
層と接着する下層との接着性を著しく改善することがで
きる。The image holding member of the present invention is characterized in that it contains the above-mentioned hydrophobic silica powder. Therefore, in this type of image holding member, hydrophobic silica powder is contained in the surface layer that forms an electrostatic image and/or a toner image, so that the image holding member has improved surface smoothness, cleanability, abrasion resistance, and Adhesion between the surface layer and the underlying layer to be adhered to can be significantly improved.

以下、本発明を図面に従って説明する。The present invention will be explained below with reference to the drawings.

像保持部材が電子写真感光体の場合には、導電基体、光
導電゛Ｗ１あるい娘保護層からなる。When the image holding member is an electrophotographic photoreceptor, it consists of a conductive substrate, a photoconductive layer W1, or a daughter protective layer.

本発明の好ましい具体例は、第１図（ａ）および（１）
）に示す如く、ピＩＪ　リウム系染料又はその共晶錯体
、チアピリリウム系染料又はその共晶錯体、シアニン系
染料、フタロシア二５ン系顔料、アントアントロン顔料
、ジベンズピレンキノンｇｌｌ、ビ２ントｐン顔料、ト
リスアゾ顔料、ジスアゾ顔料、アゾ顔料、インジゴ染料
、キナクリドン系顔料、非対称キノシアニン、キノシア
ニン顔料などの有機光導電性物質や酸化］１鉛、硫化カ
ドミウム、セレンなどの無機光導電性物質と疎水性シリ
カをバインダーとともに含有させた光導電層２２を導電
性基体２１の上に設けた電子写真感光体を用いることが
できる。A preferred embodiment of the present invention is shown in FIGS. 1(a) and (1).
) as shown in PIIJ Lium dyes or their eutectic complexes, Thiapyrylium dyes or their eutectic complexes, cyanine dyes, phthalocyanin pigments, anthoanthrone pigments, dibenzpyrenequinone gll, bi2nd p Inorganic photoconductive substances such as lead, cadmium sulfide, selenium, and hydrophobic An electrophotographic photoreceptor may be used in which a photoconductive layer 22 containing electroconductive silica together with a binder is provided on a conductive substrate 21.

本発明の別の具体例では、第２図（１））に示す如く、
光導電性物質をバインダとともに含有した光導電層２２
の保獲層２３として前述の疎水性シリカをバインダ中に
含有させた被膜を用いることができる。In another embodiment of the present invention, as shown in FIG. 2(1)),
Photoconductive layer 22 containing a photoconductive substance together with a binder
As the retention layer 23, a film containing the aforementioned hydrophobic silica in a binder can be used.

第１図（ａ）および（ｂ）に示す電子写真感光体で用い
た光導電層２２および保護ｊｔｌ　２５で用いるバイン
ダ樹脂としては、例えばアクリル樹脂、ポリアクリレー
ト、ポリエステル、ポリカーボネート、ポリスチレン、
アクリロニトリル−スチレンコポリマー、アクリａニト
リル−ブタジェンコポリマー、ポリビニルブチ９−　）
＠ｚ　、ポリビニルホルマール、ポリスルホン、ポリア
クリルアミド、ポリアミド、塩素化ゴムなどの絶縁性樹
脂、あるいはポリ＝Ｈ−ビニルカルバゾール、ポリビニ
ルアントラセン、ポリとニルピレンなどを適当な割合で
含有させることができ、バインダー樹脂に対する前述の
シリカ粉末の含有量は、バインダー樹脂１００重量部に
対して１〜２００重量部、好ましくは１〜１０重量部で
ある。又、分散法としては、ホモジナイザー、ボールミ
ル等一般的に月いられる分散法で目的は達成される。Examples of binder resins used in the photoconductive layer 22 and protective layer 25 used in the electrophotographic photoreceptor shown in FIGS. 1(a) and (b) include acrylic resin, polyacrylate, polyester, polycarbonate, polystyrene,
Acrylonitrile-styrene copolymer, acrylonitrile-butadiene copolymer, polyvinylbutylene 9-)
@z, insulating resins such as polyvinyl formal, polysulfone, polyacrylamide, polyamide, chlorinated rubber, or poly=H-vinylcarbazole, polyvinylanthracene, poly and nylpyrene, etc. can be contained in an appropriate ratio, and the binder resin The content of the above-mentioned silica powder is 1 to 200 parts by weight, preferably 1 to 10 parts by weight, based on 100 parts by weight of the binder resin. Further, as a dispersion method, the purpose can be achieved by a generally used dispersion method such as a homogenizer or a ball mill.

この具体例では、導電性基体２１の上に疎水性シリカ粉
末を含有する光導１！層２２を形成するか、あるいは光
導電層２２の上に疎水性シリカ粉末を含有する保農層２
３を形成することができる。In this embodiment, the light guide 1! contains hydrophobic silica powder on a conductive substrate 21! A protective layer 2 forming the layer 22 or containing hydrophobic silica powder on the photoconductive layer 22
3 can be formed.

又、前述の光導電層２２は、電荷発生層と電荷輸送層と
に機能分離した積層借造体とすることもできる。電荷発
生層としては、アモルファスシリコンフィルム、銅フタ
ロシアニン蒸着フィルム、セレン−テルル蒸着フィルム
、ペリレン系顔料の蒸着フィルムあるいはスクエアリッ
ク酸メチン染料の蒸着フィルムなどを導電性基体２１の
上に設けることによりて形成でき、又ジスアゾ顔料やト
リスアゾ顔料などのアゾＬｔＩ料、銅フタロシアニン、
塩化アルミニラムノタロシアニン、バナジルフタロシア
ニン、メタル７リーフタ四シアニンなどの７タロシアニ
ン顔料、ビ１７　リウム系染料又はその共晶錯体、チア
ピリリウム系染料又はその共晶錯体をバインダ中に分散
させて形成した被覆層を導電性基体２１（設けることに
よって得られる。電荷輸送層れ好ましくは電荷発生層の
上にオーバコートされて形成される。この電荷輸送層は
電子輸送性物質又は正孔輸送性物質をバインダ中に含有
させて得られる。電子輸送性物質としては、りｐルアニ
ル、フロモアニル、テトラシアノエチレン、テトラシア
ノキノジメタン、２，４．７−　）ジニトロ−９−フル
オレノン、２．４．５．７−テトラニトロ−９−フルオ
レノン、２，４．７−　）リニ）ａ−９−ジシアノメチ
レンフルオレノン、　２，４，５．７−テト２ニトロキ
サントン、２，４．８−）リート正孔輸送性物質として
は、ピレン、Ｎ−エチルカルバゾール、Ｎ−インフロビ
ルカルバゾール、Ｎ−メチル−Ｍ−フェニルヒドラジノ
−３−メチリデン−９−エチルカルバゾール、　Ｎ、Ｎ
−ジフェニルヒドラジノ−６−メチリヂン−９−エチル
カルバゾール、Ｎ、Ｎ−ジフェニルヒト２シノー３−メ
チリデン−１０−エチルフェノチアジン、Ｎ、Ｎ−ジフ
ェニルヒドラジノ−３−メチリデン−１０−エテルフェ
ノキサジン、アージエチルアミノベンズアルデヒドーＮ
、Ｎ−ジフェニルヒト２シン、　ＸＳ−ジエチルアミノ
ベンズアルデヒド−Ｎ−α−ナフチル−Ｎ−フエニルヒ
ド２シン、Ｐ−ピロリジノベンズアルデヒド−Ｎ、Ｎ−
ジンエニルヒドラゾン、１，５．１−　）ジメチルイン
ドレニン−ω−アルデヒド−Ｎ、Ｎ−ジフェニルヒト２
シン、Ｐ−ジエチルベンズアルデヒド−６−メチルベン
ズチアゾリノン−２−ヒドラゾン等のヒドラゾｙ類、２
，５−ビス（Ｐ−ジエチルアミノフェニル）　−１，１
，４−オキサジアゾール、１−フェニル−３−（Ｐ−ジ
エチルアミノスチリル）−５−（１’−ジエチルアミノ
フェニル）ピラゾリン、１−（キノリル＋２）　）　−
３−（Ｐ−ジエチルアミノスチリル）−５−（Ｐ−ジエ
チルアミノフェニル）ピラゾリン、１−〔ピリジル（２
）　）　−３−（Ｐ−ジェチルアミノスチリｋ）＋５　
＋　（Ｐ−ジエチルアミノフェニル）ピラゾリン、１−
〔６−メ）キシ−ピリジル＋２）　）　−３−（Ｐ−ジ
ェチルアミノスチリｋ）−５−（Ｐ−ジエチルアミノフ
ェニル）ピラゾリン、１−〔ピリジル（５）　）　−３
−（１’　−ジエチルアミノステリル）−５−（Ｐ−ジ
エチルアミノフェニル）ピラゾリン、１−〔レピジル（
２）　）　−３−（Ｐ−ジエチルアミノスチリル）−５
−（Ｐ−ジエチルアミノフェニル）ピラゾリン、１−（
ピリジル（２）　）　−５−（Ｐ−ジエチルアミノスチ
リル）−４−メチ／Ｉ／−５−（Ｐ　−ジエチルアミノ
フェニル）ピラゾリン、１−〔ピリジル（２）　）　−
５−（α−メチル−Ｐ−ジエチルアミノスチリル）−５
−（Ｐ−ジエチルアミンフェニル）ピラゾリン、１−フ
ェニル−３−（Ｐ−ジエチルアミノスチリル）−４−メ
チル−５−（Ｐ−ジエチルアミノフェール）ピラゾリ／
、１−フェニル−６−（α−べ／ジルーＰ−ジエチルア
ミノスチリル）−５−（Ｐ−ジエチルアミノフェニル）
ピラゾリン、スピルピラゾリンなどのピラゾリン類、２
−（Ｐ−ジエチルアミノステリル）−６−ジニチルアミ
ノベンズオキサソール、２−（Ｐ−ジエチルアミノフェ
ニル）−４−（ｐ−ジエチルアミノフエニ＃　）　−５
−（２−クロロフェニル）オキサゾール等のオキサゾー
ル系化合物、２−（Ｐ−ジエチルアミノスチリル）−６
−ジニチルアミノベンゾチアゾール等のチアゾ−〃系化
合物、ビス（４−ジエチルアミノ−２−メチルフェニル
）−フェニルメタン等のトリアリールメタン系化合物、
１．１−ビス（４−Ｎ、Ｎ−ジエチルアミノ−２−メチ
ルフェニル）へブタン、１．１．２．２−テトラキス（
４−Ｎ、Ｎ−ジメチルアミン−２−メチルフェニル）エ
タン等のボリアリールアルヵンル１、トリフェニルアミ
ン、ボ１ｊＮ−ビニルカルバゾール、ポリビニルピレン
、ポリビニルアント２セン、ポリビニルアクリジン、ポ
リ−９−ビニルフェニルアントラセン、ピレンーホルム
アルテヒト樹脂、エチルカルバゾールホルムアルデヒド
樹脂等がある。Further, the above-mentioned photoconductive layer 22 can also be a laminated structure in which the charge generation layer and the charge transport layer are separated in function. The charge generation layer is formed by providing an amorphous silicon film, a copper phthalocyanine vapor-deposited film, a selenium-tellurium vapor-deposited film, a perylene pigment vapor-deposited film, a squaric acid methine dye vapor-deposited film, etc. on the conductive substrate 21. Also, azo LtI materials such as disazo pigments and trisazo pigments, copper phthalocyanine,
A coating formed by dispersing a 7-thalocyanine pigment such as aluminum chloride rhamnotalocyanine, vanadyl phthalocyanine, metal 7-leaf tetracyanine, a bi17ium dye or its eutectic complex, a thiapyrylium dye or its eutectic complex in a binder. The charge transport layer is preferably formed by overcoating the charge generating layer. Examples of the electron transporting substance include lyp-ruanyl, fluoroanil, tetracyanoethylene, tetracyanoquinodimethane, 2,4.7-) dinitro-9-fluorenone, 2.4.5. 7-tetranitro-9-fluorenone, 2,4.7-)lini) a-9-dicyanomethylenefluorenone, 2,4,5.7-teto-2-nitroxanthone, 2,4.8-)rito hole transport properties The substances include pyrene, N-ethylcarbazole, N-inflovircarbazole, N-methyl-M-phenylhydrazino-3-methylidene-9-ethylcarbazole, N,N
-diphenylhydrazino-6-methylidene-9-ethylcarbazole, N,N-diphenylhydrazino-3-methylidene-10-ethylphenothiazine, N,N-diphenylhydrazino-3-methylidene-10-ethylphenoxazine, Diethylaminobenzaldehyde N
, N-diphenylhydehyde, XS-diethylaminobenzaldehyde-N-α-naphthyl-N-phenylhydride, P-pyrrolidinobenzaldehyde-N,N-
Dienylhydrazone, 1,5.1-) dimethylindolenine-ω-aldehyde-N,N-diphenylhydro2
hydrazoyl compounds such as P-diethylbenzaldehyde-6-methylbenzthiazolinone-2-hydrazone, 2
,5-bis(P-diethylaminophenyl) -1,1
,4-oxadiazole, 1-phenyl-3-(P-diethylaminostyryl)-5-(1'-diethylaminophenyl)pyrazoline, 1-(quinolyl+2)) -
3-(P-diethylaminostyryl)-5-(P-diethylaminophenyl)pyrazoline, 1-[pyridyl(2
) ) -3-(P-jethylaminostirik)+5
+ (P-diethylaminophenyl)pyrazoline, 1-
[6-Me)xy-pyridyl+2) -3-(P-diethylaminostirik)-5-(P-diethylaminophenyl)pyrazoline, 1-[pyridyl(5)) -3
-(1'-diethylaminosteryl)-5-(P-diethylaminophenyl)pyrazoline, 1-[lepidyl(
2) ) -3-(P-diethylaminostyryl)-5
-(P-diethylaminophenyl)pyrazoline, 1-(
Pyridyl(2)) -5-(P-diethylaminostyryl)-4-methy/I/-5-(P-diethylaminophenyl)pyrazoline, 1-[Pyridyl(2))-
5-(α-methyl-P-diethylaminostyryl)-5
-(P-diethylaminophenyl)pyrazoline, 1-phenyl-3-(P-diethylaminostyryl)-4-methyl-5-(P-diethylaminophel)pyrazoly/
, 1-phenyl-6-(α-be/gi-P-diethylaminostyryl)-5-(P-diethylaminophenyl)
Pyrazolines such as pyrazoline and spirpyrazoline, 2
-(P-diethylaminosteryl)-6-dinithylaminobenzoxasol, 2-(P-diethylaminophenyl)-4-(p-diethylaminophenyl) -5
-(2-chlorophenyl)oxazole and other oxazole compounds, 2-(P-diethylaminostyryl)-6
-Thiazo-based compounds such as -dinithylaminobenzothiazole, triarylmethane-based compounds such as bis(4-diethylamino-2-methylphenyl)-phenylmethane,
1.1-bis(4-N,N-diethylamino-2-methylphenyl)hebutane, 1.1.2.2-tetrakis(
Polyaryl alkanes such as 4-N,N-dimethylamine-2-methylphenyl)ethane, triphenylamine, polyvinylpyrene, polyvinylant-2cene, polyvinyl acridine, poly-9-vinyl Examples include phenylanthracene, pyrene-formaltehyde resin, and ethylcarbazole formaldehyde resin.

又、光導電層を設けていない像保持部材の具体例は、第
１図（Ｃ）で明らかにされている。すなわち、本発明の
別の具体例では、四′シ１図（ｃ）に７」＜す様に導電
性基体２１の上に疎水性シリカ粉末をバインダ中に含有
させぞ得た表面Ｊｅｊ２４を設けることができる。Further, a specific example of an image holding member without a photoconductive layer is shown in FIG. 1(C). That is, in another embodiment of the present invention, a surface 24 obtained by containing hydrophobic silica powder in a binder is provided on the conductive substrate 21 as shown in Figure 1(c). be able to.

表面層２４は、適当な電気抵抗をもたせるために、酸化
チタン、酸化亜鉛、酸化錫などｉ４肖な顔料または染料
を含有させることもできる。The surface layer 24 may also contain pigments or dyes such as titanium oxide, zinc oxide, tin oxide, etc. to provide suitable electrical resistance.

導電性基体２１は、基体自体が導電性をもつもの例えば
、アルミニウム、銅、ステンレスなどの材料をシリンダ
ー状また紘シート状にして用いることができる。その他
にアルミニウム、アルミニウム合金、酸化インジウム、
酸化錫、酸化インジウム−酸化錫合金などを真空蒸着法
によって被膜形成された層を有するプラスチック（例え
ば、ポリエチレン、ポリプロピレン、ポリ塩化ビニル、
ポリエチレンテレツクレート、アクリル樹脂、ポリフッ
化エチレンな、！’）、４電性粒子（例えば、カーボン
ブラック、銀粒子など）を適当なバインダとともにプラ
スチックの上に被覆した基体、導電性粒子をプラスチッ
クや紙に含浸した基体や導電性ポリマーを有するプラス
チックなどを用いることができる。The conductive substrate 21 can be made of a material that is conductive itself, such as aluminum, copper, or stainless steel, and can be used in the form of a cylinder or a sheet. In addition, aluminum, aluminum alloy, indium oxide,
Plastics (e.g., polyethylene, polypropylene, polyvinyl chloride,
Polyethylene telecrate, acrylic resin, polyfluoroethylene! '), a substrate made of a plastic coated with tetraelectric particles (e.g. carbon black, silver particles, etc.) together with a suitable binder, a substrate made of plastic or paper impregnated with conductive particles, a plastic containing a conductive polymer, etc. Can be used.

又、導電性基体２１と光導電層２２あるいは表面層２４
の中間に、バリヤー機能と接着機能をもり下引層を設け
ることもできる。下引層は、カゼイン、ポリビニルアル
コール、ニトロセルロース、エチレン−アクリル酸コポ
リマー、ポリアミド（ナイロン６、プーイ目ン６６、ナ
イロ７６１０　、共重合ナイロン、アルコキシメチル化
ナイロンなど）、ポリウレタン、ゼ２ブーン、酸化アル
ミニウムなどによって形成できる。Further, the conductive substrate 21 and the photoconductive layer 22 or the surface layer 24
An undercoat layer may be provided between the layers to provide a barrier function and an adhesive function. The undercoat layer is made of casein, polyvinyl alcohol, nitrocellulose, ethylene-acrylic acid copolymer, polyamide (nylon 6, Poohime 66, nylon 7610, copolymerized nylon, alkoxymethylated nylon, etc.), polyurethane, Ze2boon, oxidation. It can be formed from aluminum or the like.

以上の説明から明らかであるが、水元ＩＪＩｊは静電像
および／またはトナー画像を作成して画像形成を行う装
置において、画家品質を安定に保この結果は、昨保持表
面に関連する小であり、作像方式に依らず、すべての画
像形成方式に有効であると言える。従って以下に示す実
施例に限られることはない。As is clear from the above explanation, Mizumoto IJIj maintains stable artist quality in devices that form images by creating electrostatic images and/or toner images. It can be said that it is effective for all image forming methods, regardless of the image forming method. Therefore, the present invention is not limited to the examples shown below.

実施例　１ １．０重量部の下記の電−発生物質、０．５Ｊｉ量部の
セルロース樹脂と ９８．５重量部のメチルエチルケトン（ＭＩＩＣＫ）　
ｅ　ｔンドミルで混合分散することによって電荷発生層
用塗布液ｔｌ−調整した。この塗布液をアルミニウムシ
リンダーの上に浸漬コーティング法により塗布し、乾燥
して電荷発生層を形成した。乾燥後の膜厚は０．１μで
あった。Example 1 1.0 parts by weight of the following electron-generating material, 0.5 parts by weight of cellulose resin and 98.5 parts by weight of methyl ethyl ketone (MIICK)
A coating solution for a charge generation layer was prepared by mixing and dispersing with an et mill. This coating solution was applied onto an aluminum cylinder by a dip coating method and dried to form a charge generation layer. The film thickness after drying was 0.1μ.

次に下記溝造式の電荷輸送物質を１０重量部とスチレン
樹脂２０重量部および電荷輸送物質疎水性シリカ粉末１
アエロジルＲ−９７２”（日本アエシジル社製）１重量
部をトルエン１２０重量部中に分散させて電荷輸送用途
工液を調整した。この塗工液を先に形成した電荷発生層
の上に浸漬コーティング法によシ塗布した。次いでこの
塗膜を１００℃、６０分間加熱乾燥させることによって
、電荷輸送層を形成した。その乾燥膜厚は１５μであっ
た。Next, 10 parts by weight of the charge transport material of the following Mizozo type, 20 parts by weight of styrene resin, and 1 part of the charge transport material hydrophobic silica powder were added.
A charge transport solution was prepared by dispersing 1 part by weight of Aerosil R-972'' (manufactured by Nippon Aesigil Co., Ltd.) in 120 parts by weight of toluene. This coating solution was dip-coated on the previously formed charge generation layer. The charge transport layer was formed by heating and drying this coating film at 100° C. for 60 minutes.The dry film thickness was 15 μm.

比較例　１ 実施例１の電子写真感光体を作成した時に用いた電荷輸
送層中の疎水性シリカ粉末６アエロジルＲ−９７，２”
（同上）を除ｉた以外は実施例１と全く同様の方法で比
較用感光体をａｌｌｉ整した。Comparative Example 1 Hydrophobic silica powder 6 Aerosil R-97,2'' in the charge transport layer used when producing the electrophotographic photoreceptor of Example 1
A comparative photoreceptor was prepared in exactly the same manner as in Example 1 except that (same as above) was removed.

実施例１と比較例１それぞれで調整した電子写真感光体
をコロナ帯電工程、ハロゲンランプを光源としだ画＠Ｂ
光工程、乾式トナー現１象工程、普通紙へのトナー転写
工程、ウレタンゴムブレードによるクリー二ング工程と
除電り光工程を有する電子複写機に取シ付けて、連続２
０００枚のコピー画像を形成した。実施例１で調整した
感光体で得られたコピー画像は初期のものと、２０００
枚目のものとを比較したところ、画質（地汚れ）の点で
ほとんど変化しておらず、何れも良好な画質であること
が判明した。比較例１で調整した感光体は、初期で得ら
れたコピー画像に較べ、２０００枚目で得られたコピー
画像は、地汚れが著しく、良好な画質のものでなかった
。The electrophotographic photoreceptors prepared in Example 1 and Comparative Example 1 were subjected to a corona charging process, and a halogen lamp was used as a light source.
It is installed in an electronic copying machine that has a light process, a dry toner development process, a toner transfer process to plain paper, a cleaning process using a urethane rubber blade, and a static electricity removal light process, and can be used continuously for two
000 copy images were formed. The copy images obtained with the photoreceptor adjusted in Example 1 are the initial one and the 2000
When compared with the second image, it was found that there was almost no change in image quality (background stains), and both images were of good quality. In the photoreceptor prepared in Comparative Example 1, the copy image obtained on the 2000th sheet had significant background staining and was not of good image quality compared to the copy image obtained at the initial stage.

さらに、２０００枚目のコピー画像が得られた後に、感
光体を取９出して、その表面を観察したところ、本発明
に係る実施例１の感光体の表面は、はとんど汚染されて
いなかりたが、比較例１の感光体紘、残留トナーが付着
され、そのトナーを除去すると、感光体表面に傷、摩耗
した跡が観られ、汚染されていることが判明した。Further, after the 2000th copy image was obtained, the photoreceptor was taken out and its surface was observed, and it was found that the surface of the photoreceptor of Example 1 according to the present invention was hardly contaminated. However, residual toner was adhered to the photoconductor of Comparative Example 1, and when the toner was removed, scratches and abrasion marks were observed on the photoconductor surface, indicating that it was contaminated.

実施例　２ 酸化亜鉛粉体１５１ｉとローズベンガル染料ｏ、ｏ　ｓ
　ｇと疎水性シリカ粉末６アエロジ／Ｉ／Ｒ−９７２”
（同上）２ｇおよびアクリル樹脂６ダイヤナールＬＲ４
７２″（三菱レーヨン■＃り８．９をトルエン２０ｍ１
とメチルアルコール２ｔｄ中Ｋｍ合し、ボールミルで分
散して、分散液を調整した。この溶液をアルミニウムシ
リンダーの上ニ浸漬コーティング法で塗布し、１００℃
、４０分間乾燥した。その乾燥膜厚は１５μであった。Example 2 Zinc oxide powder 151i and rose bengal dye o, o s
g and hydrophobic silica powder 6Aeroge/I/R-972”
(Same as above) 2g and acrylic resin 6-dial LR4
72″ (Mitsubishi Rayon ■#8.9 in toluene 20m1
and Km in 2 td of methyl alcohol and dispersed in a ball mill to prepare a dispersion. This solution was applied onto an aluminum cylinder by dip coating method and heated to 100°C.
, dried for 40 minutes. The dry film thickness was 15μ.

この感光体を実施例１で用−九電子写真複写機に取９付
け、同様の方法で、コピー画像を作成したところ、初期
で得たコピー画像と２０００枚目で得たコピー画像には
はとんど画質の点で変化がなく、何れも良好な画質であ
った。又、２０００枚目のコピー終了後電子写真複写機
からこの感光体を取り出して表面を観察したが、表面に
は残留トナーによる付着は全くなく、クリーンで傷跡の
ない表面でありた。When this photoreceptor was attached to the electrophotographic copying machine used in Example 1 and copy images were created in the same manner, there was a difference between the initial copy image and the 2000th copy image. There was almost no change in image quality, and the image quality was good in all cases. Further, after copying the 2000th sheet, the photoreceptor was removed from the electrophotographic copying machine and its surface was observed, and it was found that there was no residual toner adhering to the surface, and the surface was clean and free from scratches.

実施例　３ 実施例２で６アエロジルＲ−９７２”を除−た以外は同
様の処方で光導電層を作成し九、さらにその上にボリア
リレート樹脂”Ｕ−１００″（ユニチカ■製）３０重量
部と疎水性シリカ粉末６アエロジルＲ−９７２’　（同
上）２重量部をクロルベンゼン１００重量部中で分散さ
せて、この溶液を先に形成した光導電層の上に浸漬コー
ティング法により塗布し、１００℃、５０分間乾燥して
保護層とした。この乾燥膜厚は１μであった。Example 3 A photoconductive layer was prepared using the same recipe as in Example 2 except that 6AEROSIL R-972'' was omitted, and then 30 weight of polyarylate resin ``U-100'' (manufactured by Unitika) was added on top of it. and 2 parts by weight of hydrophobic silica powder 6 Aerosil R-972' (same as above) are dispersed in 100 parts by weight of chlorobenzene, and this solution is applied onto the previously formed photoconductive layer by a dip coating method, A protective layer was obtained by drying at 100° C. for 50 minutes.The dry film thickness was 1 μm.

実施例３で作成した感光体を実施例１で用いた電子写真
複写機に取り付け、同様の方法でコピー画像を作成した
ところ、両方とも初期で得たコピー画像と２０００枚目
で得たコピー画像には、はとんど画質の点で変化がなく
、何れも良好な画質で必りた。又、２００．０枚目のコ
ピー終了後電子写真複写機からこの感光体を取り出して
表面を観察したが、表面には残留トナーによる付着は全
くなく、クリーンで傷跡のない表面であった。When the photoreceptor produced in Example 3 was attached to the electrophotographic copying machine used in Example 1 and copy images were produced in the same manner, both the initial copy image and the 2000th copy image were obtained. There was almost no change in image quality, and all images were of good quality. Further, after copying the 200.0th sheet, the photoreceptor was removed from the electrophotographic copying machine and its surface was observed, and it was found that there was no residual toner adhering to the surface, and the surface was clean and free from scratches.

実施例　４ Ｃｕ及びＩｎヲドープして半導体レーザー（８２０ｎｍ
）に感度を有すｃｄｓ粉体１００重量部及び平均分子量
１００００のポリブチルメタクリレート７重量部をメチ
ルエチルケトンで分散液とし、四−ルミルで混練して塗
工液を調整した。Example 4 A semiconductor laser (820 nm) doped with Cu and In
) and 7 parts by weight of polybutyl methacrylate having an average molecular weight of 10,000 were made into a dispersion liquid in methyl ethyl ketone and kneaded in a four-lumen mill to prepare a coating liquid.

この塗工液を透明導電性ベースフィルムＣＦ；ＬＥＣ−
ＫＩＧ（ダイセル化学工業■＃り上に四−ルコーターで
塗布し、光導電層をｔ燥膜厚６ｏμとなるように形成し
た。This coating solution was applied to a transparent conductive base film CF; LEC-
The photoconductive layer was coated on KIG (Daicel Chemical Industry Co., Ltd.) using a four-layer coater to form a photoconductive layer with a dry film thickness of 6 μm.

次にＴｌＯ２顔料４０重量部、ポリメチレフ１０重量部
（新日本製鉄化学工業■エスチレンＭ日−２００）、疎
水性シリカ粉末（日本アエμジル社製、アエ四ジルＲ−
９７２）　１重量部をトルエンに加えて、固形分比５０
重量パーセントの溶液に混合し、サンドミルで分散を行
な一塗工液をＷ・ｑ整した。ＴｌＯ２顔料は、画像表示
面の白色度を増すためと表面層の電気抵抗を調節する目
的で添加した。Next, 40 parts by weight of TlO2 pigment, 10 parts by weight of Polymethylenef (Nippon Steel Chemical Co., Ltd. Estyrene M-200), hydrophobic silica powder (manufactured by Nippon Aeμsil Co., Ltd., Ae4sil R-
972) Add 1 part by weight to toluene to make a solid content ratio of 50
The solution was mixed with a weight percent solution and dispersed using a sand mill to prepare a coating solution with W and q. The TlO2 pigment was added for the purpose of increasing the whiteness of the image display surface and adjusting the electrical resistance of the surface layer.

この塗工液を先に形成した光導電層の上に四−ルコータ
ーを用いて、乾燥膜厚が５μとなるように塗布、乾燥し
た。This coating solution was applied onto the previously formed photoconductive layer using a four-wheel coater so that the dry film thickness was 5 μm, and then dried.

ここで作成した像保持ベルトｆｃｆＸｃ２図に示す。The image holding belt fcfXc2 created here is shown in FIG.

画像表示装置に懸架駆動して画像表示′ｆ、繰り返し５
０００回行なったところ、初期と５０００回目で得た表
示画像にｔｔｉとんど画質の点で変化がなく、何れも良
好な画質であった。又、５０００回の画像表示終了後、
画像表示面を観察したが、表面の汚れがはとんどなく、
クリーンで傷跡のない表面であった。Drive suspended on the image display device to display the image 'f, repeat 5
When the test was repeated 000 times, there was almost no change in image quality between the initial and 5000th display images, and all images were of good quality. Also, after displaying the image 5000 times,
I looked at the image display surface, but there was a lot of dirt on the surface.
The surface was clean and free of scratches.

実施例　５ 像保持ベルトとしてポリエステルフィルム上にＣｒＯ２
薄膜を設け、磁気チー　上に実施例４に示した表面層を
乾燥膜厚１０ミクロンに塗工したものを作成した。Example 5 CrO2 on polyester film as image holding belt
A thin film was prepared by coating the surface layer shown in Example 4 on a magnetic chip to a dry film thickness of 10 microns.

該ベルトを用いた作像工程鉱第２図に示した装置と同様
な構成にした、但しレーザスキャナーの代シに現像ステ
ーションムの前に磁気ヘッドを付備して、バーコード状
のパターン信号を入力して磁化潜像を作成した。又、第
６図の現像機において、回転スリーブ１６に内蔵した固
定マグネットロールは現像部位の着磁を行わないものを
用いた。これは磁気潜像を乱さない事を目的としたもの
である。この装置で作成したトナー像は、ＯＣＲヘッド
で十分読み出せるコントラストを有して−た。又、消去
工程は像保持ベルトの背面より熱的にクウェンチして行
ったこの構成において、像保持ベルトは繰り返し作像に
対して、常に安定なＯＣＲ読み出し信号が得られた。The image forming process using the belt was constructed in the same way as the apparatus shown in Figure 2, except that instead of a laser scanner, a magnetic head was installed in front of the developing station, and a bar code pattern signal was generated. A latent magnetization image was created by inputting In addition, in the developing machine shown in FIG. 6, the fixed magnet roll built into the rotating sleeve 16 is one that does not magnetize the developing area. This is for the purpose of not disturbing the magnetic latent image. The toner image created with this device had sufficient contrast to be readable by an OCR head. Further, in this configuration in which the erasing process was performed by thermally quenching from the back side of the image holding belt, stable OCR read signals were always obtained even when images were repeatedly formed on the image holding belt.

【図面の簡単な説明】[Brief explanation of drawings]

第１図（＆）、第１図（ｂ）および第１図ＴＯ）は本発
明の像保持部材の断面図である。第２図（ＩＬ）は表示
装置の一例の概略を示す傅成図で、第２図（１））はそ
の現像装置部分の拡大断面図である。 ２１・・・導電性基体 ２２・・・光導電層 ２５・・・保護層 ２４・・・表面層 特許出願人　キャノン株式会社 ４１　＆ＰＬ 手続補正書印先 特許庁長官　志　賀　学　殿 １、事件の表示 昭和５８年特許願第１６５４６８号 ２、発明の名称 像保持部材 ３、補正をする者 事件との関係　特許出願人 住所　東京都大田区下丸子３−３０−２名称　（１００
）キャノン株式会社 代表者　賀　来　龍　三　部 ４、代理人 居所　〒１４６東京都大田区下丸子３−３０７２５、補
正の対象 明　細　書 ６、補正の内容 （１）特許請求の範囲を別紙のとおり訂正する。 （２）明細書第１２頁第１５行〜第１６行の「本発明の
かかる目的は一一一−−達成される。」を「本発明のか
かる目的は、疎水性シリカを含有させた塗布液を塗布す
ることによって形成した像保持層を有する像保持部材に
よって達成される。」と訂正する。 （３）同上第１４頁第９行の「表面層中」を「表面層を
形成する塗布液中」と訂正する。 「この具体例では、導電性基体２１の上に疎水性シリカ
粉末を含有させた光導電層２２形成用塗布液を塗布する
ことによって光導電層２２を形成するか、あるし？は光
導電層２２の上に疎水性シリカ粉末を含有させた保護層
２３形成用塗布液を塗布することによって保護層２３を
形成することができる。」と訂正する。 ２、特許請求の範囲 とを特徴とする像保持部材。 （２〕前記像保持層が、光導電層の保［Ｆである特許請
求の範囲第１項記載の像保持部材。 （３）前記像保持層が、光導電層である特許請求の範囲
第１項記載の像保持部材。 （４）前記光導電層が電荷発生層と電荷輸送層の積層構
造体である特許請求の範囲第２項又は第３項記載の像保
持部材。 （５）前記電荷輸送層が電荷発生層の上にオーバコート
されている特許請求の範囲第４項記載の像保持部材。FIG. 1(&), FIG. 1(b) and FIG. 1TO) are cross-sectional views of the image holding member of the present invention. FIG. 2 (IL) is a schematic diagram showing an example of a display device, and FIG. 2 (1) is an enlarged sectional view of a developing device portion thereof. 21...Conductive substrate 22...Photoconductive layer 25...Protective layer 24...Surface layer Patent applicant: Canon Co., Ltd. 41 &PL Procedural amendments stamped by the Commissioner of the Japan Patent Office Mr. Manabu Shiga 1, of the case Display Patent Application No. 165468 of 1982 2, Name Image Holding Member 3 of the Invention, Relationship with the Amendment Person Case Patent Applicant Address 3-30-2 Shimomaruko, Ota-ku, Tokyo Name (100)
) Canon Co., Ltd. Representative: Ryu Kaku, Department 4, Agent address: 3-30725 Shimomaruko, Ota-ku, Tokyo 146, Specification to be amended Document 6, Contents of the amendment (1) The scope of the patent claims has been corrected as shown in the attached sheet. do. (2) On page 12, lines 15 and 16 of the specification, the phrase "Such objects of the present invention are achieved" has been replaced with "Such objects of the present invention are achieved by applying coatings containing hydrophobic silica." This is achieved by an image holding member having an image holding layer formed by applying a liquid.'' (3) "In the surface layer" on page 14, line 9 of the same document is corrected to "in the coating liquid that forms the surface layer." In this specific example, the photoconductive layer 22 is formed by applying a coating liquid for forming the photoconductive layer 22 containing hydrophobic silica powder onto the conductive substrate 21. The protective layer 23 can be formed by applying a coating liquid for forming the protective layer 23 containing hydrophobic silica powder onto the protective layer 22.'' 2. An image holding member characterized by the claims. (2) The image holding member according to claim 1, wherein the image holding layer is a photoconductive layer. (3) The image holding member according to claim 1, wherein the image holding layer is a photoconductive layer. The image holding member according to claim 1. (4) The image holding member according to claim 2 or 3, wherein the photoconductive layer is a laminated structure of a charge generation layer and a charge transport layer. (5) The image holding member according to claim 3. 5. An image bearing member according to claim 4, wherein a charge transport layer is overcoated on the charge generation layer.

Claims (5)

【特許請求の範囲】[Claims] （１）静電像および／またはトナー画像を保持するため
の像保持部材において、その像保持Ｊｔ４が疎水性シリ
カを含有することを特徴とする像保持部材。(1) An image holding member for holding an electrostatic image and/or a toner image, wherein the image holding member Jt4 contains hydrophobic silica. （２）　前記像保持層が、光導電層の保護層である特許
請求の範囲第１項記載の像保持部材。(2) The image holding member according to claim 1, wherein the image holding layer is a protective layer for a photoconductive layer. （３）　前記像保持層が、光導電層である特許請求の範
囲第１項記載の像保持部材。(3) The image holding member according to claim 1, wherein the image holding layer is a photoconductive layer. （４）　前記光導電層が電荷発生層と電荷輸送層の積層
構造体である特許請求の範囲第２項又は第３項記載の像
保持部材。(4) The image holding member according to claim 2 or 3, wherein the photoconductive layer is a laminated structure of a charge generation layer and a charge transport layer. （５）前記電荷輸送層が電荷発生層の上にオーバコート
されている特許請求の範囲第４項記載の像保持部材。(5) The image holding member according to claim 4, wherein the charge transport layer is overcoated on the charge generation layer.