JPS60261031A - Magnetic recording medium - Google Patents

Abstract

PURPOSE:To obtain a recording medium which has small running friction, excellent film strength, lubricity and head touch characteristic and high running durability and obviates the deterioration in the electromagnetic conversion characteristic by providing a top coat layer contg. a cholesterol compd. on a thin continuous film type magnetic layer. CONSTITUTION:The cholesterol compd. such as cholesterol, the ester of the long chain fatty acid of cholesterol or gamma-cholesterol is formed by vapor deposition or sputtering to a <=0.1mu, more preferably 5-100 Angstrom range on thin continuous film type magnetic layer formed on a substrate to form the top coat layer. The magnetic layer is formed preferably of the assemblage of the grains consisting of the columnar crystal structure contg. Co or Co and 1-3 kinds among Ni, Cr and O, having >=1.5 weight ratio of Co/Ni, contg. Cr at <=0.1 weight ratio of Cr/(Co or Co + Ni), having <=0.5 atomic ratio of O/(Co or Co + Ni) and inclined to the normal of the substrate. The magnetic recording medium having the top coat layer which is high in the film strength, etc. and obviates head clogging is thus obtd.

Description

【発明の詳細な説明】 ■　発明の背景 技術分野 本発明は、磁気記録媒体、特に連続薄膜型の磁性層を有
する磁気記録媒体のトップコート膜の改良に関する。DETAILED DESCRIPTION OF THE INVENTION (1) Background of the Invention Technical Field The present invention relates to improvements in top coat films for magnetic recording media, particularly magnetic recording media having a continuous thin film type magnetic layer.

先行技術とその問題点 ビデオ用、オーディオ用等の磁気記録媒体として、テー
プ化して巻回したときのコンパクト性から、連続薄膜型
の磁性層を有するものの開発が活発に行われている。Prior art and its problems As magnetic recording media for video, audio, etc., media having a continuous thin film type magnetic layer are being actively developed because of their compactness when wound into tapes.

このような連続薄膜型の媒体の磁性層としては、特性上
、基体法線に対し所定の傾斜角にて蒸着を行う、いわゆ
る斜め蒸着法によって形成したＣｏ、Ｃｏ−Ｎｉ、Ｃｏ
−０、Ｃｏ−Ｎｉ−〇系等の蒸着膜が最も好適である。Due to its characteristics, the magnetic layer of such a continuous thin film type medium is made of Co, Co-Ni, or Co, which is formed by the so-called oblique deposition method, in which deposition is performed at a predetermined angle to the normal to the substrate.
-0, Co--Ni--, etc.-based vapor deposited films are most suitable.

しかし、このような磁性層は、走行摩擦が大きく、膜強
度が低く、ヘッドタッチも悪く、特に走行耐久性が低く
、くりかえし走行によって出力が低下してしまう。However, such a magnetic layer has high running friction, low film strength, poor head touch, particularly low running durability, and output decreases due to repeated running.

また、ビデオ用の媒体では、スチルと称される静止画像
モードでの耐久時間が小さい。In addition, video media have a short durability in a still image mode called still.

さらに、いわゆるドロップアウトも多い。Furthermore, there are many so-called dropouts.

このような実状から、従来、斜め蒸着膜磁性層のトップ
コート膜が種々提案されている。Under these circumstances, various top coat films for obliquely deposited magnetic layers have been proposed.

例えば、直鎖の飽和脂肪酸ないしそのエステルの蒸着膜
や塗布ＩＮ（特開昭５３−８８７０４号公報、同５５−
９３５３３号、公報等）である。For example, a vapor-deposited film or coating IN of straight-chain saturated fatty acids or their esters (JP-A-53-88704, JP-A No. 55-53)
No. 93533, official gazette, etc.).

さらに、本出願人は、先に、リン酸エステルの蒸着膜を
トップコート膜に用いる旨を提案している（特願昭５７
−２３４８１８号、同５Ｂ−ＩＥ１５？５８号、同５８
−ＩＨ７２２号）。Furthermore, the present applicant has previously proposed the use of a vapor-deposited film of phosphoric acid ester as a top coat film (Patent Application No. 57
-234818, 5B-IE15?58, 58
-IH722).

しかし、このような脂肪酸系やリン酸系トップコート膜
は、走行摩擦が大きく、また走行耐久性に劣り、くりか
えし走行によって、走行摩擦が増大し、電磁変換特性が
低下する。However, such fatty acid-based or phosphoric acid-based top coat films have high running friction and poor running durability, and repeated running increases running friction and deteriorates electromagnetic conversion characteristics.

さらに、くりかえし走行によって磁気ヘッドの目づまり
が生じ、これによる出力低下が生じる欠点がある。In addition, repeated running causes clogging of the magnetic head, resulting in a decrease in output.

従って、電磁変換特性を悪化しないで、ヘッド目づまり
を防止するトップコート膜が要望されている。Therefore, there is a need for a top coat film that prevents head clogging without degrading electromagnetic conversion characteristics.

■　発明の目的 本発明の目的は、走行摩擦が小さく、膜強度、潤滑性、
ヘッドタッチ性にすぐれ、走行耐久性が高く、加えて、
電磁変換特性の低下がなく、しかもヘッドの目づまりの
少ないトップコート膜を有する連続薄膜型の磁性層をも
つ磁気記録媒体を提供することにある。■ Purpose of the invention The purpose of the present invention is to reduce running friction, improve film strength, lubricity,
Excellent head touch, high running durability, and, in addition,
It is an object of the present invention to provide a magnetic recording medium having a continuous thin film type magnetic layer having a top coat film that does not cause deterioration in electromagnetic conversion characteristics and less clogging of the head.

このような目的は、下記の本発明によって達成される。Such objects are achieved by the invention described below.

すなわち本発明は、基体上に連続薄膜型の磁性層を有し
、この磁性層上にトップコート膜を有する磁気記録媒体
において、トップコート膜がコレステリン系化合物を含
有することを特徴とする磁気記録媒体である。That is, the present invention provides a magnetic recording medium having a continuous thin magnetic layer on a substrate and a top coat film on the magnetic layer, wherein the top coat film contains a cholesterin compound. It is a recording medium.

■　発明の具体的構成 以下、本発明の具体的構成について詳細に説明する。■Specific structure of the invention Hereinafter, a specific configuration of the present invention will be explained in detail.

本発明の磁気記録媒体は、基体上に磁性層を有する。The magnetic recording medium of the present invention has a magnetic layer on a substrate.

磁性層は、連続薄膜型の種々のものであってよく、通常
、コバルト、ニッケルあるｌ、Ｘはこれらを主成分とす
る。The magnetic layer may be of a continuous thin film type, and usually contains cobalt, nickel, and X as main components.

この場合、本発明においては、ＣＯを必須成分とし、Ｃ
ｏ　、Ｃｏ＋Ｎｉ　、Ｃｏ＋Ｏ，またはＣｏ＋Ｎｉ＋Ｏ
からなることが好ましい。In this case, in the present invention, CO is an essential component, and C
o, Co+Ni, Co+O, or Co+Ni+O
It is preferable to consist of.

すなわち、ＣＯ単独からなってもよく、ＣＯとＮｉとか
らなってもよい。That is, it may consist of CO alone, or it may consist of CO and Ni.

Ｃｏ＋Ｎｉである場合、Ｃｏ　／　Ｎ　ｉの重量比は、
１．５以上であることが好ましい。In the case of Co+Ni, the weight ratio of Co/Ni is
It is preferable that it is 1.5 or more.

さらに、ＣＯまたはＣｏ＋Ｎｉに加え、０が含まれてい
てもよい、　０が含まれたときには、電磁変換特性や走
行耐久性の点で、より好ましい結果を得る。Furthermore, in addition to CO or Co+Ni, 0 may be included. When 0 is included, more favorable results are obtained in terms of electromagnetic conversion characteristics and running durability.

このような場合、Ｏ／Ｃｏ（Ｎｉが含まれない場合）あ
るいはＯ／（Ｃｏ＋Ｎｉ）の原子比は、０．５以下、得
に０．１５〜０．４５であることが好ましい。In such a case, the atomic ratio of O/Co (if Ni is not included) or O/(Co+Ni) is preferably 0.5 or less, particularly 0.15 to 0.45.

一方、磁性層中には、Ｃｏ　、Ｃｏ＋Ｎｉ　。On the other hand, the magnetic layer contains Co, Co+Ni.

ＣＯ＋０あるいはＣｏ＋Ｎｉ＋０に加え、Ｃｒが含有さ
れると、より一層好ましい結果を得る。When Cr is contained in addition to CO+0 or Co+Ni+0, even more favorable results are obtained.

これは、電磁変換特性が向上し、出力およびＳ／Ｎ比が
向上し、さらに膜強度が向上するからである。This is because electromagnetic conversion characteristics are improved, output and S/N ratio are improved, and film strength is further improved.

このような場合、Ｃｒ／Ｃｏ（Ｎｉが含まれない場合）
あるいはＣｒ／（Ｃｏ＋Ｎｉ）の重量比は、ｏ、ｉ以下
、得にｏ、ｏｏｉ〜０．１であることが好ましい。In such cases, Cr/Co (if Ni is not included)
Alternatively, the weight ratio of Cr/(Co+Ni) is preferably less than or equal to o, i, and particularly preferably from o, ooi to 0.1.

この場合、Ｃｒ　／　ＣｏあるいはＣｒ／（Ｃ。In this case, Cr/Co or Cr/(C.

＋Ｎ　ｉ）の重量比は、０．００５〜０．０５であると
、より一層好ましい結果を得る。Even more preferable results are obtained when the weight ratio of +N i) is 0.005 to 0.05.

なお、このような磁性層中には、さらに他の微量成分、
特に遷移金属元素、例えば、Ｆｅ。Note that such a magnetic layer also contains other trace components,
Especially transition metal elements, such as Fe.

Ｍ　ｎ　、　Ｖ　、　Ｚ　ｒ　、　Ｎ　ｂ　、　Ｔ　ａ
　、　Ｍ　ｏ　、　Ｗ　。M n , V , Z r , N b , T a
, M o , W .

Ｔｉ、Ｃｕ、Ｚｎ等が含まれていてもよい。Ti, Cu, Zn, etc. may be included.

このような磁性層は、通常、基体主面の法線に対して傾
斜した柱状結晶構造の粒子の集合体であることが好まし
い、　これにより、電磁変換特性が向上する。Such a magnetic layer is usually preferably an aggregate of particles having a columnar crystal structure tilted with respect to the normal to the main surface of the substrate. This improves electromagnetic conversion characteristics.

このような場合、柱状結晶構造の粒子は、基体の主面の
法線に対して、２０〜６００の範囲で傾斜していること
が好ましい。In such a case, the particles having a columnar crystal structure are preferably inclined in the range of 20 to 600 with respect to the normal to the main surface of the substrate.

また、各柱状結晶構造の粒子は、通常、磁性層の厚さ方
向全域に亘る長さをもち、その短径は一般に、５０〜５
００人程度とされる。Further, each particle having a columnar crystal structure usually has a length spanning the entire thickness direction of the magnetic layer, and its short axis is generally 50 to 5
It is said that there were about 00 people.

そして、ＣＯと必要に応じ添加されるＮｉ。Then, CO and Ni added as necessary.

Ｃｒ等は、この柱状結晶自体を構成するものであり、Ｏ
が添加されたとき、Ｏは通常、各柱状結晶構造粒子の表
面に、主として酸化物の形で存在している。Cr etc. constitute this columnar crystal itself, and O
When O is added, O usually exists mainly in the form of an oxide on the surface of each columnar crystal structure particle.

このような磁性層は、通常、０．０５〜０．５−の厚さ
に形成される。Such a magnetic layer is usually formed to a thickness of 0.05 to 0.5-.

この場合、磁性層は、基体上に直接設けられていてもよ
く、あるいは基体上に下地層を介して設けられていても
よい。In this case, the magnetic layer may be provided directly on the substrate, or may be provided on the substrate via an underlayer.

また、磁性層は通常、単一の層として形成されるが、場
合によっては中間層を介して、複数の層を積層して形成
されていてもよい。Further, although the magnetic layer is usually formed as a single layer, it may be formed by laminating a plurality of layers with an intermediate layer interposed therebetween as the case may be.

このような磁性層は、通常、斜め蒸着法によって形成さ
れる。Such a magnetic layer is usually formed by an oblique deposition method.

用いる斜め蒸着法としては、公知の斜め蒸着法を用いれ
ばよく、基体法線に対する入射角の最小値は、３０°以
上とすることが好ましし旭。As the oblique evaporation method to be used, a known oblique evaporation method may be used, and the minimum value of the incident angle with respect to the normal to the substrate is preferably 30° or more.

なお、蒸着条件および後処理法等は、公知の条件および
方法に従えばよい、　この場合、有効な後処理法として
は、磁性層中へのＯ導入のための公知の各種処理法等が
ある。Incidentally, the vapor deposition conditions, post-treatment method, etc. may be in accordance with known conditions and methods. In this case, effective post-treatment methods include various known treatment methods for introducing O into the magnetic layer. .

このような磁性層上には、コレステリン系の化合物から
なるトップコート膜が形成される。A top coat film made of a cholesterin-based compound is formed on such a magnetic layer.

本発明に用いるコレステリン（コレステロール）系化合
物は、コレステロール、γ−コレステリン、ｉ−コレス
テリン等や、これらの誘導体である。Cholesterin (cholesterol) compounds used in the present invention include cholesterol, γ-cholesterin, i-cholesterin, etc., and derivatives thereof.

特にコレステロール、γ−コレステリン、ｉ−コレステ
リン、ないしそのカルボン酸エステルが好ましい。Particularly preferred are cholesterol, γ-cholesterin, i-cholesterin, and carboxylic acid esters thereof.

エステル化に用いるカルボン酸は、特に、炭素原子数６
〜２２のものが好ましい。In particular, the carboxylic acid used for esterification has 6 carbon atoms.
-22 are preferred.

コレステロール、γ−コレステリン、ｉ−コレステリン
またはこれらのカルボン酸エステＪしであって、カルボ
ン酸の炭素原子数が６〜２２のものは、走行摩擦が減少
し、しかも走行耐久性、電磁変換特性が向上し、目づま
りも減少する。Cholesterol, γ-cholesterin, i-cholesterin, or carboxylic acid esters thereof, in which the carboxylic acid has 6 to 22 carbon atoms, reduce running friction, and improve running durability and electromagnetic conversion. Characteristics are improved and clogging is reduced.

このような炭素原子数のカルボン酸、飽和体であっても
、内部に不飽和二重結合をもつものであってもよい。Carboxylic acids having such a number of carbon atoms may be saturated or may have an internal unsaturated double bond.

不飽和二重結合をもつ場合、二重結合の数については特
に制限はないが、特に１〜４であることが好ましい。When having unsaturated double bonds, the number of double bonds is not particularly limited, but is preferably 1 to 4.

また、飽和体あるいは不飽和体である場合とも、カルボ
ン酸は鎖状であるが、場合によっては、５員ないし６員
の環（通常、飽和環）状部を、鎖状部中ないし鎖状部端
部に有していてもよい、　また、アリール部を鎖状部中
ないし鎖状部端部に有していてもよい。In addition, carboxylic acids are chain-like whether they are saturated or unsaturated, but in some cases, a 5- or 6-membered ring (usually a saturated ring) may be added to the chain. Alternatively, the aryl part may be present in the chain part or at the end of the chain part.

そして、これらは直鎖であっても、また分岐を有するも
のであってもよい。These may be linear or branched.

分岐を有する場合、分岐は、カルボキシ基の結合手と逆
側の端部側に存在し、特に末端に、例えばジメチル、ジ
エチル、ジプロピル等が結合した直鎖アルキルであるこ
とが好ましい。When it has a branch, the branch exists on the end side opposite to the bond of the carboxy group, and is particularly preferably a linear alkyl chain to which dimethyl, diethyl, dipropyl, etc. are bonded to the terminal.

このようなカルボン酸は、非置換体であっても、また置
換体であってもよい。Such carboxylic acids may be unsubstituted or substituted.

置換体である場合、置換基の数には特に制限はない。In the case of a substituent, there is no particular restriction on the number of substituents.

特に好適な置換基としては、塩素、臭素、フッ素等のハ
ロゲン、アルコキシ基、アリーロキシ基（フェノキシ基
等）、アルキルカルボニル基、アリールカルボニル基、
アルキルカルボニルオキシ基、アリールカルボニルオキ
シ基、アルコキシカルボニル基、アリーロキシカルボニ
ル基、アシルアミノ基、カルバモイル基、スルホナミド
基、スルファモイル基など、あるいはこれらの１種以上
が連結したものなどがある。Particularly suitable substituents include halogens such as chlorine, bromine, and fluorine, alkoxy groups, aryloxy groups (phenoxy groups, etc.), alkylcarbonyl groups, arylcarbonyl groups,
Examples include an alkylcarbonyloxy group, an arylcarbonyloxy group, an alkoxycarbonyl group, an aryloxycarbonyl group, an acylamino group, a carbamoyl group, a sulfonamide group, a sulfamoyl group, or a combination of one or more of these groups.

そして、このような置換体では、置換基のアルキル部な
いし場合によってはアリール部の炭素原子数を含めた総
炭素原子数が、上記の範囲でなければならない。In such a substituent, the total number of carbon atoms including the number of carbon atoms in the alkyl part or, in some cases, the aryl part of the substituent, must be within the above range.

なお、脂肪酸は、好ましくは置換基を有しない直鎖アル
キルないレアルケニルカルポン酸、特にアルキルカルボ
ン酸である。The fatty acid is preferably a straight-chain alkyl realkenylcarboxylic acid having no substituents, particularly an alkylcarboxylic acid.

これら各化合物は、公知の方法に従い合成して用いても
よく、また市販のものを用いてもよい。Each of these compounds may be synthesized and used according to a known method, or commercially available ones may be used.

次に、本発明で使用される化合物の具体例を挙げる。Next, specific examples of compounds used in the present invention will be given.

ＣＩ　コレステロール ０２　つレスチロールのＣ７Ｈａ５ＣＯＯＨエステルＸ
＝Ｃ７Ｈ１５ＣＯ Ｃ３コレステロールのｃｕＨ２３ＣＯＯＨエステルＸ＝
Ｃ１１Ｈ２３ＣＯ Ｃ４コレステロールのＣ１３Ｈ２７ＣｏｏｌエステルＸ
＝Ｃ１３Ｈ２７ＣＱ Ｃ５コレステロールのＣ１５Ｈ３，Ｃ０ＯＨエステルＸ
＝Ｃ１５Ｈ３，Ｃ０ Ｃ６コレステロールのＣ４７Ｈ３ＳＣＯＯＨエステルＸ
＝Ｃ１７Ｈ３６ＣＯ Ｃ７コレステロールのＣｌ８Ｈ，Ｃ０ＯＨエステルＸ＝
Ｃ１８１（３７ＣＯ Ｃ８コレステロールのＣｌｇＨ，Ｃ０ＯＨエステルＸ＝
Ｃ１９）１．ｃ。CI Cholesterol 02 Restylol C7Ha5COOH ester X
=C7H15CO C3 cholesterol cuH23COOH ester X=
C11H23CO C13H27Cool ester of C4 cholesterol
=C13H27CQ C5 cholesterol C15H3,C0OH ester X
=C15H3,C0 C47H3SCOOH ester of C6 cholesterol X
=C17H36CO C7 cholesterol Cl8H,C0OH ester X=
C181 (37CO C8 Cholesterol ClgH, C0OH ester X=
C19)1. c.

Ｃ９コレステロールのＣ２ＩＨ，Ｃ０ＯＨエステルＸ＝
Ｃ２ＩＨ＠Ｃ０ Ｃ１０コレステロールのＰ−（ｎ−Ｃ４Ｈｓ）Ｃ６Ｈ４
ＣＨ２Ｃ０ＯＨエステル Ｘ＝Ｐ−（ｎ−Ｃ４Ｈ９）Ｃ８Ｈ４ＣＨ２ＣＯＣｌ１　
ニルステロールのｎ−Ｃｚ３Ｈ２７ＣＨ＝ＣＨＣＯＯＨ
ｚステルＸ＝ｎ−Ｃ４３Ｈ２７ＣＨ＝ＣＨＣＯ Ｃ１２γ−コレステリン Ｃ１３γ−コレステリンのＣ，Ｈ２３ＣＯＯＨエステル
Ｘ＝Ｃ，１（２３ｃ。C2IH,C0OH ester of C9 cholesterol X=
C2IH@C0 C10 cholesterol P-(n-C4Hs)C6H4
CH2C0OH ester X=P-(n-C4H9)C8H4CH2COCl1
Nylsterol n-Cz3H27CH=CHCOOH
z Stel X=n-C43H27CH=CHCO C12γ-cholesterin C13γ-C,H23COOH ester of cholesterin

Ｃ１４γ−コレステリンのＣ１０）１．Ｃ０ＯＨエステ
ルＸ＝Ｃ１７Ｈ３，、ＣＯ Ｃｌ５　γ−コレステリンのＣ２３Ｈ４３ＣＯＯＨエス
テルＸ＝Ｃ２ＩＨａＣＯ Ｃ１８ｉ−コレステリン Ｃｌ７　ｉ−コレステリンのＣ１１Ｈ２３ＣＯＯＨｚス
テルＸ＝ＣｕＨ２３ＣＯ Ｃ１８１−コレステリンのｃ１７Ｈ３６ｃｏｏＨエステ
ルＸ−Ｃｊ７Ｈ３５ＣＯ Ｃ１９ｉ−コレステリンのＣ２１Ｈ４３ＣＯＯＨエステ
ルＸ＝Ｃ２ＩＨ，Ｃ０ Ｃ２０ｉ　−ｍｌ　Ｌ／　スフ　ｊ）　７（７）　ｎ　
−Ｃ１３Ｈ２？　ＣＨ＝　ＣＨＣ００ＨニスｒｋＸ＝ｎ
−Ｃ１３Ｈ２７ＣＨ＝ＣＨＣＯ これら上記式で示される化合物は、公知の方法に従い合
成して使用したり、あるいは市販のものを用いればよい
、　この場合、化合物は、複数種併用して用いてもよい
。C10 of C14γ-cholesterin)1. C0OH ester X=C17H3,,CO Cl5 C23H43COOH ester of γ-cholesterin 7H35CO C19i-C21H43COOH of cholesterin Ester
-C13H2? CH=CHC00H varnish rkX=n
-C13H27CH=CHCO These compounds represented by the above formula may be synthesized according to known methods or commercially available ones may be used. In this case, a plurality of compounds may be used in combination.

このようなコレステロール系化合物からな名トップコー
ト膜は、単分子層以上０．１−以下、特に３００Å以下
、より好ましくは５〜１００人の厚さとされる。The top coat film made of such a cholesterol-based compound has a thickness of 0.1 to 0.1 Å or more, particularly 300 Å or less, more preferably 5 to 100 Å thick.

そして、このようなトップコート膜は、蒸着ないしスパ
ッタリングによって形成することが好ましい。Preferably, such a top coat film is formed by vapor deposition or sputtering.

蒸着ないしスパッタリングによらず、塗布等によるとき
には、膜厚をうすくして、しかも均一な厚さで設層する
ことがむずかしい。When using coating, etc., instead of vapor deposition or sputtering, it is difficult to form a thin layer with a uniform thickness.

なお、蒸着ないしスパッタリングの際の条件は、公知の
条件に従えばよい。Note that the conditions for vapor deposition or sputtering may be in accordance with known conditions.

用いる基体には特に制限はないが、特に可とう性の基体
、特にポリエステル、ポリイミド、ポリプロピレン等の
樹脂性のものであることが好ましい。There are no particular restrictions on the substrate used, but a particularly flexible substrate, particularly one made of resin such as polyester, polyimide, polypropylene, etc., is preferred.

また、その厚さは、種々のものであってよいが、特に５
〜２０−であることが好ましい。In addition, the thickness may be various, but especially 5.
It is preferable that it is -20-.

そして、その磁性層形成面の裏面には、バックコート層
を形成することができる。A back coat layer can be formed on the back surface of the magnetic layer forming surface.

■　発明の具体的作用効果 本発明の磁気記録媒体は、ビデオ用、オーディオ用等の
磁気記録媒体として有用である。(2) Specific effects of the invention The magnetic recording medium of the present invention is useful as a magnetic recording medium for video, audio, and the like.

本発明ニよれば、コレステリン系化合物からなるトップ
コート膜を用いるので、走行摩擦が減少する。According to the present invention, since the top coat film made of a cholesterin compound is used, running friction is reduced.

また、その膜強度、潤滑性、ヘッドタッチ性もきわめて
高い。Furthermore, its film strength, lubricity, and head touchability are extremely high.

このため、電磁変換特性が良く、しかも走行による電磁
変換特性の劣化が減少する。　さらに走行による目づま
りが非常に少なくなり、このため電磁変換特性の劣化が
少ない。Therefore, the electromagnetic conversion characteristics are good, and deterioration of the electromagnetic conversion characteristics due to running is reduced. Furthermore, clogging due to running is extremely reduced, and therefore electromagnetic conversion characteristics are less likely to deteriorate.

■　発明の具体的実施例 以下に本発明の具体的実施例について詳細に説明する。■Specific embodiments of the invention Specific examples of the present invention will be described in detail below.

実施例 Ｃｏ　／　Ｎ　ｉの重量比４／ｌのＣｏＮｉ合金、およ
びＣｏ　／　Ｎ　ｉ　／　Ｃｒ　（７）重量比が７５／
２０／　５　（７）　Ｃｏ　Ｎ　ｉ　Ｃｒ合金を用い、
ｌ〇−厚のポリエチレンテレフタレート（ＰＥＴ）フィ
ルム上に、それぞれ、斜め蒸着法により、磁性層を０．
２μｓ厚にて形成し、サンプルＡＯおよびＢＯを作製し
た。Examples CoNi alloy with Co/Ni weight ratio of 4/l and Co/Ni/Cr (7) weight ratio of 75/l
20/5 (7) Using CoNiCr alloy,
A magnetic layer is deposited on a polyethylene terephthalate (PET) film having a thickness of 0.1 mm by oblique vapor deposition.
Samples AO and BO were produced by forming a film with a thickness of 2 μs.

斜め蒸着における入射角は４５°とし、蒸着雰囲気は、 Ｐ　ａ　、　＝　２　Ｘ　１０−２Ｐ　ａ、Ｐ　＝　Ｉ
　Ｘ　１０−２Ｐ　ａとした。The incident angle in oblique evaporation is 45°, and the evaporation atmosphere is P a , = 2 x 10-2 P a , P = I
X 10-2P a.

２ 得られた磁性層は、ともに対応する合金の組成をもち、
ともにＯ／　（Ｃｏ＋Ｎ１）−０，２（原子比）であり
、基体主面法線に対し、約４０°傾斜した、短径０．０
１μの厚さ方向全域に亘ってした、成長した柱状結晶粒
子の集合体であった・ また、イオンエツチングを行いながらオージェ分光分析
を行ったところ、ＣＯは表面近くで少なく、また０は化
学シフトしており、しかも表面近くにいプロファイルを
もち、０が柱状粒子の表面に金属と結合した状態で存在
していることが確認された。2 The obtained magnetic layers both have the corresponding alloy composition,
Both have O/(Co+N1)-0.2 (atomic ratio), are inclined at approximately 40° to the normal to the main surface of the substrate, and have a minor axis of 0.0.
It was an aggregate of columnar crystal grains that had grown over the entire thickness direction of 1μ.Also, when Auger spectroscopy was performed while performing ion etching, it was found that CO was small near the surface, or 0 was due to chemical shift. Moreover, it was confirmed that 0 was present on the surface of the columnar particles in a state bonded to metal, and had a dark profile near the surface.

次いで、上記ＡＯおよびＢＯの磁性層上に、各種有機化
合物を蒸発源として、ＦＡ、＝　４　ｘｌ　０−”　Ｐ
　ａの雰囲気にて、ｏ　、　ｏ　１ｇ厚の表１に示され
るトップコート膜を形成して、サンプルＡｔ−Ａ３およ
びＢ１−Ｂ２を得た。Next, various organic compounds were used as evaporation sources on the AO and BO magnetic layers, and FA, = 4 xl 0-"P
Samples At-A3 and B1-B2 were obtained by forming top coat films having a thickness of 1 g and shown in Table 1 in an atmosphere of a.

１）出力 ＶＨ５のＶＴＲを改造し、５　Ｍ　Ｈｚまで測定できる
ようにしたものを用いた。　゛ 中心周波数５　Ｍ　Ｈｚで記録再生した場合の、初期の
出力と５０パス後の出力の低下（ｄＢ）を比較した。1) A VTR with an output of VH5 was modified so that it could measure up to 5 MHz.゛When recording and reproducing at a center frequency of 5 MHz, the initial output and the decrease in output (dB) after 50 passes were compared.

２）目づまり 出力測定に用いたと同様のデツキを用い５０回走行時の
目づまりを計測した。2) Using the same deck as used for clogging output measurement, clogging was measured after running 50 times.

結果を表１に示す。The results are shown in Table 1.

表１に示される結果から、本発明による効果があきらか
である。From the results shown in Table 1, the effects of the present invention are clear.

すなわち本発明のコレステリン系の化合物を用いたトッ
プコート膜を有する磁気記録媒体は、５０パス後の出力
低下が２ｄＢ以下と非常に少なく、しかも目づまりをお
こさない。That is, the magnetic recording medium having the top coat film using the cholesterin-based compound of the present invention has a very small output drop of 2 dB or less after 50 passes, and does not cause clogging.

Claims (9)

【特許請求の範囲】[Claims] （１）基体上に連続薄膜型の磁性層を有し、この磁性層
上にトップコート膜を有する磁気記録媒体において、ト
ップコート膜がコレステリン系化合物を含有することを
特徴とする磁気記録媒体。(1) A magnetic recording medium having a continuous thin magnetic layer on a substrate and a top coat film on the magnetic layer, wherein the top coat film contains a cholesterin compound. . （２）トップコート膜が、気相被着によって形成された
膜である特許請求の範囲第１項に記載の磁気記録媒体。(2) The magnetic recording medium according to claim 1, wherein the top coat film is a film formed by vapor phase deposition. （３）トップコート膜の厚さが、３００Å以下である特
許請求の範囲第１項または第２項に記載の磁気記録媒体
。(3) The magnetic recording medium according to claim 1 or 2, wherein the top coat film has a thickness of 300 Å or less. （４）磁性層が、Ｃｏ、またはＣｏとＮｉ、Ｃｒおよび
Ｏのうちの１〜３種とを含む特許請求の範囲第１項ない
し第３項のいずれかに記載の磁気記録媒体。(4) The magnetic recording medium according to any one of claims 1 to 3, wherein the magnetic layer contains Co, or Co and one to three of Ni, Cr, and O. （５）磁性層が、Ｎｉを含み、Ｃｏ　／　Ｎ　ｉの重量
比が１．５以上である特許請求の範囲第４項に記載の磁
気記録媒体。(5) The magnetic recording medium according to claim 4, wherein the magnetic layer contains Ni and has a Co/Ni weight ratio of 1.5 or more. （６）磁性層が、Ｃｒを含み、Ｃｒ／（ＣｏまたはＣｏ
＋Ｎｉ）の重量比が０．１以下である特許請求の範囲第
４項または第５項に記載の磁気記録媒体。(6) The magnetic layer contains Cr, Cr/(Co or Co
The magnetic recording medium according to claim 4 or 5, wherein the weight ratio of +Ni) is 0.1 or less. （７）磁性層が、０を含み、Ｏ／（ＣｏまたはＣｏ＋Ｎ
ｉ）の原子比が０．５以下である特許請求の範囲第４項
ないし第６項のいずれかに記載の磁気記録媒体。(7) The magnetic layer contains 0, O/(Co or Co+N
The magnetic recording medium according to any one of claims 4 to 6, wherein the atomic ratio of i) is 0.5 or less. （８）磁性層が、基体本線に対して傾斜した柱状結晶構
造粒子の集合体である特許請求の範囲第１項ないし第７
項のいずれかに記載の磁気記録媒体。(8) Claims 1 to 7, wherein the magnetic layer is an aggregate of grains with a columnar crystal structure tilted with respect to the main line of the substrate.
The magnetic recording medium according to any one of paragraphs. （９）磁性層の厚さが、０．０５〜０．５−である特許
請求の範囲第１項ないし第８項のいずれかに記載の磁気
記録媒体。(9) The magnetic recording medium according to any one of claims 1 to 8, wherein the magnetic layer has a thickness of 0.05 to 0.5.