JPS60163361A - Sealed lead storage battery - Google Patents
Sealed lead storage batteryInfo
- Publication number
- JPS60163361A JPS60163361A JP59018619A JP1861984A JPS60163361A JP S60163361 A JPS60163361 A JP S60163361A JP 59018619 A JP59018619 A JP 59018619A JP 1861984 A JP1861984 A JP 1861984A JP S60163361 A JPS60163361 A JP S60163361A
- Authority
- JP
- Japan
- Prior art keywords
- battery
- sealed lead
- electrolyte
- decrease
- charging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、トリクル充電状態や浮動充電状態で使用され
、停電時には負荷に信頼性の高い安定な電力を供給する
密閉形鉛蓄電池に関するものであ従来例の構成とその問
題点
この種の密閉形鉛蓄電池は、充電中に発生する酸素ガヌ
を負極板に吸収させる密閉方式を採用しているため、電
解液量を遊離の電解液がない状態ニ規制スルトともに、
吸液性に優れるガラス繊維セパレータを用い、ガヌ排気
口には安全弁を有し、極板群を収納する電槽等よシ構成
されている。[Detailed Description of the Invention] Industrial Application Field The present invention relates to a sealed lead-acid battery that is used in a trickle charge state or a floating charge state and provides reliable and stable power to a load during a power outage. Example configuration and its problems This type of sealed lead-acid battery uses a sealed method in which the negative electrode plate absorbs oxygen generated during charging, so the amount of electrolyte is reduced to a state where there is no free electrolyte. Both regulation Surut,
It uses a glass fiber separator with excellent liquid absorption properties, has a safety valve at the exhaust port, and is constructed with a battery container etc. that houses the electrode group.
しかし、この種の電槽材質がポリプロピレン樹脂(以下
、PP樹脂という)やアクリロニトリル−ブタジェシー
ヌチレン樹脂(以下ABS樹脂という)であるため、水
蒸気の透過度が25°Cで0.1〜3.0の會/24−
と高く、また、極板群と電槽間の空間が多いので、極板
群が電解液で満たされている従来の開放形鉛蓄電池に比
べて、トリクル充電中や浮動充電中に電槽表面よシ蒸発
する水分の量が多く、電解液減少の主要因となっている
。However, since the material of this type of battery case is polypropylene resin (hereinafter referred to as PP resin) or acrylonitrile-butylene ethylene resin (hereinafter referred to as ABS resin), the water vapor permeability is 0.1 to 3 at 25°C. .0 meeting/24-
In addition, because there is a large space between the plate group and the battery case, the surface of the battery case during trickle charging or floating charge is higher than that of conventional open lead-acid batteries, where the plate group is filled with electrolyte. A large amount of water evaporates, which is the main reason for the decrease in electrolyte solution.
そして、電解液の減少は、第1図に示すごとく、周囲温
度25℃のトリクル充電中における電解液峨少量ハと容
量イ、および40℃における電解液減少置部と容量口の
関係のように、電池の周囲温度が高くなるほど加速され
、電池の内部抵抗の増加、放電容量の減少、電解液の濃
縮による格子腐食の増大につながり、トリクル充電や浮
動充電で使用される密閉形鉛蓄電池の寿命が従来の開放
形鉛蓄穎、lΦに比べて短かい原因となっていた。As shown in Figure 1, the decrease in electrolyte is expressed by the relationship between electrolyte volume C and capacity A during trickle charging at an ambient temperature of 25°C, and between electrolyte decrease position and capacity port at 40°C. , which is accelerated as the ambient temperature of the battery increases, leading to an increase in the internal resistance of the battery, a decrease in discharge capacity, and an increase in lattice corrosion due to concentration of the electrolyte, which reduces the lifespan of sealed lead-acid batteries used in trickle charging and floating charging. This was the reason why the length was shorter than that of the conventional open lead-acid tube.
発明の目的
本発明は、このような従来の問題点を改良するもので、
電槽の表面からの水の蒸発を抑止する方策として、電槽
表面に樹脂で被覆した水蒸気透過性が非常に少ない金属
箔を接着することによって′電解液減少に起因する容量
劣化を防止し長寿命化を図ることをその目的とする。OBJECT OF THE INVENTION The present invention aims to improve these conventional problems.
As a measure to suppress water evaporation from the surface of the battery case, by adhering a resin-coated metal foil with very low water vapor permeability to the surface of the battery case, it is possible to prevent capacity deterioration caused by a decrease in electrolyte and increase the length of the battery case. The purpose is to extend the lifespan.
発明の構成
上記目的を達するため本発明の密閉形鉛蓄電池は、トリ
クル充電状態あるいは浮動充電状態で使用される密閉形
鉛蓄電池の電槽表面を金属箔で覆うことを特徴とする。Structure of the Invention In order to achieve the above object, the sealed lead-acid battery of the present invention is characterized in that the surface of the container of the sealed lead-acid battery used in a trickle charge state or a floating charge state is covered with metal foil.
又、この金属箔の片面あるいは両面が樹脂によって被覆
され、かつその片面が蓄電池の電槽表面に対して接着性
を有しており、電槽表面積の26係以上を金属箔で覆う
ことが好41〜い。Further, it is preferable that one or both sides of the metal foil be coated with a resin, and that one side has adhesive properties to the surface of the battery case, and that 26 or more areas of the surface area of the battery case are covered with the metal foil. 41~.
このように構成することによシ、水の蒸発を防止し、電
解液の減少によって生ずる電池の内部抵抗の増加や容量
劣化を防止し、密閉形鉛蓄電池の寿命を大幅に延長する
ことができるというものである。With this configuration, it is possible to prevent water evaporation, prevent an increase in battery internal resistance and capacity deterioration caused by a decrease in electrolyte, and significantly extend the life of a sealed lead-acid battery. That is what it is.
実施例の説明
以下、本発明の実施例について、図面に基づいて説明す
る。DESCRIPTION OF EMBODIMENTS Hereinafter, embodiments of the present invention will be described based on the drawings.
第2図および第3図においては、電槽表面に貼りつける
金属箔シートの一例を示し、1は樹脂フィルムで、加工
性が良く軽量である厚さ10〜200μmのアルミニウ
ム箔等より成る金属箔2を補強したり、電気的あるいは
化学的に絶縁するためのもので、PP樹脂やポリエステ
ル樹脂およびポリ塩化ビニール樹脂等よりなり、熱溶着
やエポキシ系あるいはポリイソブチレン系の粘着斉1や
接着剤により第2図に示すように金属箔2の両面あるい
は第3図に示すように金属箔2の片面に接着されている
。In Figures 2 and 3, an example of a metal foil sheet to be attached to the surface of a battery case is shown. 1 is a resin film, and 1 is a metal foil made of aluminum foil or the like with a thickness of 10 to 200 μm, which is easy to process and lightweight. It is used to reinforce or insulate electrically or chemically, and is made of PP resin, polyester resin, polyvinyl chloride resin, etc., and can be bonded by heat welding, epoxy or polyisobutylene adhesive, or adhesive. It is bonded to both sides of the metal foil 2 as shown in FIG. 2, or to one side of the metal foil 2 as shown in FIG.
3は金属箔2を樹脂フィルム1で被覆したシートを電そ
う表面に接着するだめのアクリル酸エステル系の接着剤
である1、
以下、上記構成のシートを密閉形鉛蓄電池に貼りつけた
時の効果について説明する。3 is an acrylic ester adhesive for adhering a sheet made of metal foil 2 covered with resin film 1 to the surface of an electric battery. Explain the effects.
第4図は、金属箔に20ttmのアルミニウム箔、樹脂
フィルムにはエポキシ系接着剤でアルミニウム箔の両面
に接着した厚さ50μmのポリ塩化ビニール樹脂を用い
、アクリル酸エステル系の接着剤で12V、3Ah仕様
の密閉形鉛蓄電池の電彎表面積の10係、25%および
80係になるようそれぞれ貼9つけ、周囲温度60℃、
充電々圧13.8Vのトリクル充電を行なった時の電解
液の減少と容量の変化とを従来品と比較して示しており
、電槽表面積の80%に金属箔シー1−を貼シつけた電
池のa液量チと容置部、および電槽表面積の26%に金
属箔シートを貼シつけた電池の減液量トと容量ハ、電槽
表面積の10条に金属箔シートを貼りつけた電池の減液
量へと容量口、更には従来品の減液量ホと容量イの特性
を示す。In Figure 4, the metal foil is a 20ttm aluminum foil, the resin film is a 50μm thick polyvinyl chloride resin adhered to both sides of the aluminum foil with an epoxy adhesive, and the voltage is 12V with an acrylic ester adhesive. The curvature surface area of a sealed lead-acid battery with 3Ah specifications was 9 times 10 times, 25%, and 80 times, respectively, and the ambient temperature was 60°C.
The figure shows the decrease in electrolyte and the change in capacity when performing trickle charging at a charge voltage of 13.8V in comparison with a conventional product.A metal foil sheet 1- is pasted on 80% of the surface area of the battery case. Metal foil sheets were pasted on 26% of the surface area of the battery case. It shows the characteristics of the capacity and the amount of fluid loss of the attached battery, as well as the characteristics of the amount of fluid loss (E) and capacity (A) of the conventional product.
この結果より、アルシミニウム箔竹の金属箔を電槽表面
に貼9つけると、貼りつけた表面積に反比例して電解液
減少が少なくなり、電槽表面積の約25%をアルミニウ
ム箔で覆うと効果か見られ、電池の端子音Wと朗気口部
を除く電槽表面積の約(イ)係を被覆すると、電池重旦
の減少、すなわち電解液量の減少ば、従来品の50〜6
0チになり、電油ソI゛命も従来品の1.5〜2倍に伸
びている。These results show that when aluminum foil (bamboo) metal foil is attached to the surface of a battery case, the decrease in electrolyte decreases in inverse proportion to the surface area of the battery case, and that covering approximately 25% of the surface area of the battery case with aluminum foil is effective. As can be seen, when approximately (a) of the surface area of the battery case excluding the battery terminal sound W and air opening is covered, the battery weight decreases, that is, the electrolyte volume decreases by 50 to 6% compared to the conventional product.
0, and the life of the electro-oil solenoid is 1.5 to 2 times longer than that of conventional products.
このように本実施例によれば、トリクル充電状態や浮動
充電状態で使用される密閉形鉛蓄電池の電解?&減少が
大幅に少なくなるので、電解液減少によって生ずる電池
内部抵抗の増加や放電容量の低下を押さえることができ
、特に電解液減少の多い高温状態での蓄電池使用におい
て、電池寿命を大幅に伸ばすという効果を有する。As described above, according to this embodiment, the electrolysis of a sealed lead-acid battery used in a trickle charge state or a floating charge state is possible. & Since the decrease in electrolyte is significantly reduced, it is possible to suppress the increase in battery internal resistance and decrease in discharge capacity caused by decrease in electrolyte, and significantly extend the battery life, especially when using storage batteries in high temperature conditions where electrolyte decreases frequently. It has this effect.
発明の効果
以上のように本発明によれば次の効果を得ることができ
る。Effects of the Invention As described above, according to the present invention, the following effects can be obtained.
(1) I−IJクル充電状態や浮動充電状態で使用さ
れる密閉形鉛蓄電池の電槽表面を水蒸気透過性の小さい
金属箔で偵うことにより、電解液の減少か少なくなり、
電解Ml少によって生ずる内部抵抗の増加や容昂劣化が
押さ乏−られて蓄7L池寿命か向」二する。(1) By covering the surface of the container of a sealed lead-acid battery used in the I-IJ cycle charging state or floating charging state with a metal foil with low water vapor permeability, the amount of electrolyte is reduced.
The increase in internal resistance and deterioration in capacity caused by the decrease in electrolytic Ml are suppressed and the life of the 7L battery is shortened.
(2)周囲温度か高い状態でトリクル充電や浮動充電を
行なっても、電解液減少による寿命低下を防止できる。(2) Even if trickle charging or floating charging is performed at high ambient temperatures, it is possible to prevent a decrease in the lifespan due to a decrease in electrolyte.
第1図は従来の密閉形鉛蓄電池をトリクル充電した時の
減液量と容量との関係を示す特性図、第2図は本発明の
第1の実施例における密閉形鉛蓄電池の電槽表面に貼り
つける金属箔と樹脂を貼9合わせたシートの断面図、第
3図は同じく第2の実施例を示す断面図、第4図は密閉
形鉛蓄電池の減液量と容量との関係を示す特性図である
。
1・・・・・樹脂フィルム、2・・・・金属箔、3・・
・・・接着剤。
代理人の氏名 弁理士 中 尾 敏 男 ほか1名第1
図
トリクル充a河閏 (牛)
第2図 第3図
第 4′図
トリクツム元e期間(午)Fig. 1 is a characteristic diagram showing the relationship between the amount of liquid loss and capacity when a conventional sealed lead acid battery is trickle charged, and Fig. 2 is the surface of the container of a sealed lead acid battery according to the first embodiment of the present invention. Figure 3 is a cross-sectional view of the second embodiment, and Figure 4 shows the relationship between the amount of fluid loss and capacity of a sealed lead-acid battery. FIG. 1...Resin film, 2...Metal foil, 3...
···glue. Name of agent: Patent attorney Toshio Nakao and 1 other person No. 1
Fig. Trickle-filling River Leap (Cow) Fig. 2 Fig. 3 Fig. 4'
Claims (3)
用される密閉形鉛蓄電池であって、蓄電池の電槽表面を
金属箔で覆ったことを特徴とする密閉形鉛蓄電池。(1)l-! A sealed lead-acid battery is used in a one-cycle charging state or a floating charging state, and is characterized in that the surface of the battery case is covered with metal foil.
され、かつその片面が蓄電池の電槽表面に対して接着性
を有することを特徴とする特許請求の範囲第1項記載の
密閉形鉛蓄電池。(2) The sealed lead-acid battery according to claim 1, wherein one or both sides of the metal foil are coated with a resin, and one side of the metal foil has adhesive properties to the surface of the battery case.
特徴とする特許請求の範囲第1項記載の密閉形鉛蓄電池
。(3) The sealed lead-acid battery according to claim 1, wherein 25% or more of the surface area of the battery case is covered with metal foil.