JPS60157845A - Manufacture of packaging bag - Google Patents

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.

Description

【発明の詳細な説明】 本発明は包装装本体の所定箇所に引裂予定部が設置ノら
れ、使用時にこの引裂予定部を手で引き裂くことにより
開封するようにした包装袋を製造する方法に関する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for manufacturing a packaging bag in which a tear portion is provided at a predetermined location on a packaging body, and the bag is opened by manually tearing the tear portion during use.

従来、プラスデックフィルムやアルミニウム伯を積層し
たプラスチックフィルムにより装本体を形成し、その内
部に所用の内容物を充容した後、開口部を密封し、内容
物を保存することが行なわれている。この袋内の内容物
を取り出ず場合は、袋を千〇破って開封するものである
が、この場合袋を破り易くするため、装本体の所定箇所
に引裂予定部を形成し、この引裂予定部から引ぎ裂くこ
とにより袋を手で容易に破り、開封し躾ｊるようにづる
ことが行なわれている。Conventionally, the packaging body is formed using a plastic film laminated with plastic film or aluminum foil, and after filling the inside with the desired contents, the opening is sealed to preserve the contents. . If the contents inside the bag are not taken out, the bag must be torn to pieces.In this case, in order to make the bag easier to tear, a tear area is formed at a predetermined location on the main body, and the tear area is The bag is easily torn by hand by tearing it from the intended part, and the bag is then opened and tamed.

このような引裂予定部を形成する方法としては、従来第
１図に示したように装本体ａに２本のテープｂ、ｂを所
定開閉離間して袋本体ａの引裂方向性の方向に合せて晶
付し、これら両フー１１）、ｂ間の間隙部ｂ′を引裂予
定部Ｃとする方法、第２図に示したように装本体ａに切
目ｄを形成り−ると共に、この切目ｄを被ってテープＣ
を貼イリし、−′ｆ記切目ｄを引裂予定部Ｃとする方法
が知られているが、これらの方法はテープを貼付するな
どの点で袋の＠迄が面倒Ｃある等の問題がある。また、
第３図に示したように装本体ａの所定縁部にＶ字状、そ
の伯の切込みｆを形成し、この切込み「を引裂予定部Ｃ
とづる方法もあり、この方法は特に装本休ａを結晶配列
が一方向性を有するプラスチックのフィルムを用いて形
成すると引き裂きが容易と（（るものであるが、切込み
ｆに他の物が引掛り易く、取り扱い性に問題がある。Conventionally, as shown in FIG. 1, a method for forming such a planned tear area is to open and close two tapes b, b at a predetermined distance on the bag body a, and align them with the direction of the tear direction of the bag body a. This method involves forming a cut d in the packaging body a as shown in FIG. Tape C over d
There is a known method in which the cut d indicated by -'f is set as the planned tearing area C, but these methods have problems such as the troublesome process of attaching tape to the bag. be. Also,
As shown in FIG. 3, a V-shaped notch f is formed at a predetermined edge of the packaging body a, and this notch is connected to the part to be torn C.
There is also a method called "cutting", and this method is especially easy to tear if the book binding a is formed using a plastic film with a unidirectional crystalline arrangement. It is easy to get caught and has problems in handling.

本発明はト記事情に鑑みなされたもので、切込みを設り
４Ｔいので取り扱い性の問題が改善され、かつ引裂予定
部において手で簡単に引き裂くことができる包装袋を能
率よく簡単に製造する方法を提供することを目的とする
。The present invention was made in view of the above circumstances, and it is possible to efficiently and easily manufacture a packaging bag which improves the problem of handling by providing a 4T incision and which can be easily torn by hand at the intended tearing area. The purpose is to provide a method.

即ち、本発明は上記目的を達成するため、プラスチック
フィルムらしくは金属ｖ１積層プラスチックフィルムか
らなる包装材料を用いて形成された包装装本体の所定箇
所に引裂予定部が設けられ、この引裂予定部を引き裂く
ことにより開封するようにした包装袋を’ＩＪｌｌｉす
る方法において、包装材料の所定箇所に近赤外線を照射
して近赤外線照射部を形成し、この照射部を引裂予定部
としたものである。That is, in order to achieve the above-mentioned object, the present invention includes a packaging body formed using a packaging material made of a metal V1 laminated plastic film, which is similar to a plastic film, and is provided with a planned tear portion at a predetermined location. In the method of 'IJlli' a packaging bag which is opened by tearing, a predetermined part of the packaging material is irradiated with near-infrared rays to form a near-infrared irradiated part, and this irradiated part is used as a part to be torn.

以下、本発明につき第４図乃至第７図を参照して更に詳
しく説明する。Hereinafter, the present invention will be explained in more detail with reference to FIGS. 4 to 7.

本発明の包装袋’Ｎ造方法は、まず第４図に水したよう
に包装材ＩＩ！！１１の所定箇所に近赤外線熱ｔＡＩｌ
１２から近赤外線を照射し、近赤外線照射部３を形成す
るものである。The packaging bag 'N manufacturing method of the present invention begins with packaging material II as shown in Figure 4. ! Near-infrared heat tAIl is applied to 11 predetermined locations.
Near-infrared rays are irradiated from 12 to form a near-infrared irradiating section 3.

ここで、包装材料としては、ボリエチレン、ポリプロピ
レン、ポリエステル、ポリアミド等のプラスチックより
なるフィルムを１ＩＩＨで用いるが又は複数層を適宜順
序でｌａ層したプラスチックフィルム、或いはアルミニ
ウム等の金属箔の片面又は両面に前記プラスチックのフ
ィルムをｍａｔ、、た金属箔積層プラスチックフィルム
が使用されるが、特に中間層を金ＢｆＩ！Ｉ層とし、最
外層をポリプロピレン、ポリエステル、ポリアミド等に
て形成すると共に、最内層を熱融着性プラスデックにて
形成したものが好適に用いられる。なお、本発明におい
て、前記プラスチックのフィルムや金属箔により複合フ
ィルムを形成する場合、紙を介在させても差支えない。Here, as the packaging material, a film made of plastic such as polyethylene, polypropylene, polyester, polyamide, etc. is used in 1IIH, or a plastic film made of la layers of multiple layers in an appropriate order, or a metal foil such as aluminum on one or both sides. A metal foil laminated plastic film is used for the plastic film, especially the middle layer is made of gold BfI! Preferably used is an I layer in which the outermost layer is made of polypropylene, polyester, polyamide, etc., and the innermost layer is made of heat-fusible Plus Deck. In the present invention, when forming a composite film using the plastic film or metal foil, paper may be interposed.

更に、−軸延伸フィルムをその延伸方向と引き裂き方向
とを一致さＵて配置積層した複合フィルｌ＼も９ｊ適に
用いられる。この場合、−軸延伸フィルムのＶＲ層位賄
は限られない。Furthermore, a composite film 1\, which is a stack of -axially stretched films arranged and laminated with their stretching direction and tearing direction coincident, is also suitably used. In this case, the VR layer position of the -axis stretched film is not limited.

また、近赤外線照射源としては、近赤外線を発生可能な
装置であればいずれも使用でき、例示するとキセノンラ
ンプ、ハロゲンランプ、レーザーなどが挙げられる。Further, as the near-infrared irradiation source, any device that can generate near-infrared rays can be used, and examples thereof include a xenon lamp, a halogen lamp, and a laser.

近赤外線を照射する場合は、第４図に示したように近赤
外線の通路途中にレンズ４やスリン［・５を配置し、包
装材料に近赤外線を絞って照射することが好ましい。In the case of irradiating near-infrared rays, it is preferable to place a lens 4 or Surin [5] in the path of the near-infrared rays as shown in FIG. 4, and irradiate the packaging material with the near-infrared rays.

この場合、近赤外線の照射は、第５図〜第７図に参照符
号３ａで示したように、包装材料の幅方向一端縁から他
端縁にかけて連続帯状に照射するようにしてもよく、非
照射部分６を適宜間隔毎に段番ブるように鎖線状に照射
りるようにしてもよく、また従来の切り込みと同じよう
に包装材料の所定−縁に部分的に照射するようにしても
よい。ここで、近赤外線の包装材料に対する照射幅は、
１〜５＋＋＋ｍどすることが好適であり、また照射弾痕
はキビノンランプを例にとると包装材料１ｄ当り１００
へ２０００ワツ１〜、特に３００〜６００ワツトとする
ことが好ましい。更に、近赤外線の照射時間は０．０１
〜５秒、特に０．１〜１秒とすることが好ましい。また
、放電処理は、包装材料の最外層（この材料を用いて包
装袋を製造した場合において、包装袋の外面又は表面を
形成Ｊることになる側）に行なうことが好ましく、特に
前記包装材料を用いて形成した包装装本体に対し直接赤
外線照射を施す場合は、赤外線照射は包装材料の最外層
に施されるが、必ずしもこれに限られず、包装材料の裏
面側に行なったり、また近赤外線を照射したフィルムを
中間層として積層した複合フィルムを包装材料とし、こ
れを用いて包装装本体を形成することもできる。In this case, near-infrared rays may be irradiated in a continuous band form from one edge to the other edge in the width direction of the packaging material, as indicated by reference numeral 3a in FIGS. 5 to 7. The irradiation area 6 may be irradiated in a chain line pattern at appropriate intervals, or it may be irradiated partially at a predetermined edge of the packaging material in the same way as conventional cuts. good. Here, the irradiation width of near-infrared rays on the packaging material is:
It is preferable that the distance is 1 to 5 +++ m, and the irradiation bullet holes are 100 m per 1 d of packaging material, taking a Kibinon lamp as an example.
It is preferable to set it to 2000 Watts 1 to 300 to 600 Watts. Furthermore, the near-infrared irradiation time is 0.01
It is preferable to set the time to 5 seconds, particularly 0.1 to 1 second. In addition, it is preferable to perform the discharge treatment on the outermost layer of the packaging material (the side that will form the outer surface or surface of the packaging bag when the packaging bag is manufactured using this material), and particularly on the outermost layer of the packaging material. When applying direct infrared irradiation to the packaging body formed using It is also possible to use a composite film laminated with an irradiated film as an intermediate layer as a packaging material to form a packaging body.

上述したように、近赤外線を照射して近赤外線照射部を
形成した又は包装袋本体形成後近赤外線照射部を形成す
べき包装材料は、これを用いて公知の適宜な方法により
平袋、自立袋、テトラ状或いは直方体状パックなどの包
装装本体を製造するものであり、この場合ｆｉＪ記近赤
外線照射部を引裂予定部とＪるものである。As mentioned above, the packaging material that has been irradiated with near-infrared rays to form the near-infrared irradiated area, or that should be formed with the near-infrared irradiated area after forming the packaging bag body, can be made into a flat bag or free-standing by any known appropriate method. It is used to manufacture packaging bodies such as bags, tetra-shaped or rectangular parallelepiped packs, and in this case, the near-infrared irradiation part is referred to as the part to be torn.

例えば、予め近赤外線照射部を形成した包装材料を用い
て袋体を製造ツる場合は、近赤外線照射部を形成した包
装材料と同様に近赤外線照射部を形成したもしくは近赤
外ｍ照射部を形成していない包装材料とを重ね合せて必
要周側縁部を熱接着するか、或いは近赤外線照射部を形
成した包装材料を中央部から折り返し重ね合せてその必
要周側縁部を熱接盾さＵ、次いで重り合Ｖ下縁部を熱接
着させるか又は断面Ｖ字状もしくは逆Ｖ字状に折曲した
底部形成材料を前記重ね台は下縁部に熱接着する方法等
が採用される。第５〜７図番よこのようにしてＦ４３Ｍ
された袋体を示すもので、この袋体のＬ部中央部に近赤
外線照射部（引裂予定部〉３が（Ω置しているものであ
る。なＪ）　、第５図及び第７図に示したＪ：うにこの
近赤外線照射部（引裂予定部）３を囲ってこの部分を引
き裂（べきことを表示する表示部７を形成することがで
きる。For example, if a bag is manufactured using a packaging material on which a near-infrared irradiation area has been formed in advance, a near-infrared irradiation area or a near-infrared Either wrap the packaging material that does not have a near-infrared irradiation area and heat-bond the necessary peripheral edges, or fold the packaging material that has formed the near-infrared irradiation part from the center and overlap it, and heat-bond the necessary peripheral edges. A method of thermally bonding the lower edge of the shield U and then the overlapping V, or thermally bonding a bottom forming material bent into a V-shaped cross section or an inverted V-shaped cross section to the lower edge of the stacking table, etc. is adopted. Ru. F43M like this next to figures 5-7.
This figure shows a bag with a near-infrared irradiation part (the part to be torn) placed at (Ω) in the center of the L part of this bag, Figures 5 and 7. It is possible to form a display part 7 that surrounds the near-infrared irradiated part (part to be torn) 3 of the sea urchin shown in J: and displays that this part should be torn.

上述したようにして製造された包装装本体は、その内部
に清涼飲料水等の内容物を充容した後、その開口部をヒ
ートシール等の手段で密封するものである。After the packaging main body manufactured as described above is filled with contents such as a soft drink, the opening thereof is sealed by means such as heat sealing.

この場合、本発明方法によって製造された包装袋は、引
裂予定部が近赤外線の照射により形成され、包装材料に
ＶＪ目を入れたり、切り込みを形成したりなど、包装材
料をに１接接触損傷して引裂予定部を形成゛する方法と
は異なり、包装材料を直接損傷することがないので、引
裂予定部の強度低下が可及的に防止され、従って内容物
の充容、保存、運搬時等において非常に取り扱い性が良
好なものである。　また、内部に収容された内容物を取
り　。In this case, in the packaging bag manufactured by the method of the present invention, the planned tear portion is formed by near-infrared irradiation, and the packaging material is damaged by direct contact with the packaging material, such as by making VJ marks or making cuts. Unlike the method of "forming the planned tear area", since the packaging material is not directly damaged, a decrease in the strength of the planned tear area is prevented as much as possible. It is very easy to handle. Also, remove the contents stored inside.

出す場合は、引裂予定部に冶ってこの予定部の形成方向
に千で引き裂き、開封りるものであるが、近赤外線照射
により形成された引裂予定部は手で簡単に引き裂くこと
ができるのぐ、使用１１［が良好なものである。When disposing of the package, the package should be opened by attaching it to the intended tear area and tearing it in the direction of formation of the intended tear area, but the intended tear area formed by near-infrared irradiation can be easily torn by hand. 11 is in good condition.

以上説明したように、本発明はシラスナックフィルムも
しく番よ金属箔積層プラスブックフィルムからなる包装
材料を用いて形成された包装装本体の所定箇所に引裂予
定部が設けられ、この引裂予定部を引き裂くことにより
ｆｉｌ封するようにした包装袋を製造ザる方法においで
１包装月ｒ；の所定箇所に近赤外線を照射して近赤外線
照射部を形成し、この照０４部を引裂予定部どしたのぐ
、取り扱い竹がよく、かつ千′Ｃ筒中に引き裂くことが
できる包装袋を比較的制御が容易な電気的処理により能
率Ｊ、（製３１シすることができるものである。As explained above, the present invention provides a portion to be torn at a predetermined location of a packaging body formed using a packaging material made of Shirasunac film or Banyo metal foil laminated plus book film. In the method of manufacturing a packaging bag that is sealed by tearing it, near-infrared rays are irradiated to a predetermined location of one package to form a near-infrared irradiation area, and this irradiated part is used as a part to be torn. A packaging bag that is easy to handle, easy to handle, and can be torn into 1,000-cylindrical tubes can be manufactured with high efficiency by electrical processing that is relatively easy to control.

４　、　図１ｆｉｉ（７）簡１１ｔ７．ｉｌｊ明第１図
及び第２図はそれぞれ従来の引裂予定部が形成された袋
の一例を示′？ＩＩｔ略断面図、第３図′は従来の引裂
予定部が形成された袋の他の例を承り概略正面図、第４
図は本発明の引裂予定部の形成方法の一例を説明する概
略図、第５図乃至第７図はそれぞれ本発明方法によって
製造された包装袋の一例を示１概略正面図である。4, Figure 1fii (7) Simple 11t7. Figures 1 and 2 each show an example of a bag in which a conventional tear portion is formed. IIt is a schematic sectional view, and FIG. 3' is a schematic front view, and FIG.
The figure is a schematic diagram illustrating an example of the method of forming the tear portion of the present invention, and FIGS. 5 to 7 are schematic front views each showing an example of a packaging bag manufactured by the method of the present invention.

１・・・包Ｍ初判、２・・・近赤外線照射源、３・・・
近赤外線照射部（引裂予定部）第１図　第２図 第４図 第３　ト４1...M first edition, 2...Near infrared irradiation source, 3...
Near-infrared irradiation area (part to be torn) Fig. 1 Fig. 2 Fig. 4 Fig. 3

Claims (1)

【特許請求の範囲】[Claims] １、プラスチックフィルムもしくは金属箔積層プラスチ
ックフィルムからなる包装材料を用いて形成された包装
装本体の所定箇所に引裂予定部が設けられ、この引裂予
定部を引き裂くことによりｍ１封Ｊるようにした包装袋
を製造する方法において、包装祠料の所定箇所に近赤外
線を照射して近赤外線照射部を形成し、この照射部を引
裂予定部としたことを特徴とする包装袋の製造方法。1. A package that is formed using a packaging material made of a plastic film or a metal foil laminated plastic film, and has a planned tear portion at a predetermined location on the packaging body, and is sealed by tearing the planned tear portion. A method for manufacturing a packaging bag, characterized in that a predetermined location of a packaging material is irradiated with near-infrared rays to form a near-infrared irradiated area, and this irradiated area is used as a planned tearing area.