JPS5988723A - Lenticular screen - Google Patents

Abstract

PURPOSE:To obtain a screen having a sufficient thickness without changing the angle of diffusion of light by providing a two-layered structure to a screen and by using an optical material with a lower refractive index as the material of one of the layers having the surface of a lenticular lens and an optical material with a higher refractive index as the material of the substrate layer at the rear side. CONSTITUTION:A substrate 4 made of a material having a higher refractive index than the material of a lenticular lens 2B is laminated on the rear side of the lens 2B, and black stripes 3 are formed on the substrate 4 to obtain a lenticular screen 1B. When the light enters the substrate 4 through the lens 2B, it is refracted and passes through the screen 1B as shown by the arrows. Accordingly, the thickness Tb of the screen 1B is increased without changing the angle of diffusion of light.

Description

【発明の詳細な説明】 キュラースクリーンの改良に関する。[Detailed description of the invention] Concerning improvements to the cular screen.

たとえばプロジエクンヨンテレビの透過型スクリーンと
して、レンチキュラーレンズを利用し、裏面の映像光不
透過部分には外光を吸収する帯、いわゆるブラックスト
ライブを設けたスクリーンが多く用いられている。For example, the transmissive screen of a PROJE TV is often a screen that uses a lenticular lens and has a so-called black stripe, a strip that absorbs external light, on the back side of the screen that does not transmit image light.

この種のスクリーンの材料には、成形の容易さや軽量で
あるという利点を生かして、透明な合成樹脂とくにポリ
メチルメタクリレ−１・やポリスチレンが好んで採用さ
れている。Transparent synthetic resins, particularly polymethyl methacrylate-1 and polystyrene, are preferably used as materials for this type of screen, taking advantage of their ease of molding and light weight.

スクリーンを通してみえる画像の質を向」−させるため
には、レンズピッチを細かく、つ５まり曲率半径の小さ
なレンズを密に配列したレンチキュラーレンズを使用す
ることが好ましい。　一方、ブラックストライプタイプ
０のスクリーンでは、その構造上、レンズピッチを小さ
くすると、それだけ板厚を薄くしなければならない。　
すると、成形に困難が生じるばかりか、スクリーンの強
度か弱くなるという不都合が生じる。In order to improve the quality of the image seen through the screen, it is preferable to use a lenticular lens with a fine lens pitch, that is, a lenticular lens in which lenses with a small radius of curvature are closely arranged. On the other hand, in the black stripe type 0 screen, due to its structure, if the lens pitch is made smaller, the plate thickness must be made thinner.
This not only makes molding difficult, but also reduces the strength of the screen.

本発明の１」的は、このような問題を解決り、スクリー
ンを透過する光の拡散角を変更することなく、十分な板
厚をもったレンチキュラースクリーンを、低床なコスト
で提供することにある３゜本発明のレンチキュラースフ
１ノーンは、ブラックストライフ０タイフ０のレンチキ
ュラースクリーンにおいて、スクリーンを少なくとも２
層で構成し、レンチキュラーレンズ面の層には屈折率の
小さい光学材オ］を、そして裏面の基材層には屈折率の
大きい光学拐木」をそれぞれ使用したことを將徴とする
。The first objective of the present invention is to solve these problems and provide a lenticular screen with sufficient thickness at a low cost without changing the diffusion angle of light passing through the screen. A certain 3° lenticular screen of the present invention has at least 2 screens in a lenticular screen with 0 black strife and 0 tiff.
It is characterized by the use of an optical material with a low refractive index for the layer on the surface of the lenticular lens, and an optical material with a high refractive index for the base layer on the back surface.

以下、図面を参照して説明する。　第１図に示すように
、従来のブラックストライブタイプのレンチキュラース
クリーンＩＡは、透明な合成樹脂拐料で１枚に成形した
レンチキュラーレンズ２Ａに、ブラックストライフ０３
を設けたものであるから、矢印の方向の光線（／（適切
な拡散角度をＩｊえてブラックストライブの間を通過さ
せる／こめには、厚さはレンズピッチと月別の屈折率と
で定められ、Ｔａが限界である。This will be explained below with reference to the drawings. As shown in Fig. 1, the conventional blackstrive type lenticular screen IA has a lenticular lens 2A molded in one piece from a transparent synthetic resin material, and a blackstripe 03
Since the light beam in the direction of the arrow (/(passes between the black stripes with an appropriate diffusion angle), the thickness is determined by the lens pitch and the monthly refractive index. , Ta is the limit.

本発明に従えば、第２図に示すように、レンチキュラー
スクリーン］、　Ｂ　ハ、レンチキュラーレンズ２Ｂの
裏面に、屈折率がより高い４′Ａ＄’ｌでつくった暴利
４がラミネートされており、その上にプラックストライ
フ０３が設けである。　九〇１　レンチキュラーレンズ
２Ｂから基材４へ入射するとき屈折して、矢印の径路で
スクリーンを透過する。According to the present invention, as shown in FIG. 2, a lenticular screen], B C, a profit 4 made of 4'A$'l having a higher refractive index is laminated on the back surface of the lenticular lens 2B, On top of that is Plax Strife 03. 901 When the light enters the base material 4 from the lenticular lens 2B, it is refracted and transmitted through the screen along the path indicated by the arrow.

このため拡散角は同じでも、スクリーンの厚さをＴＩ）
　”ｔで増すことができるわけである。Therefore, even though the diffusion angle is the same, the screen thickness is TI)
``It can be increased by t.

この原理は、第３図を参照すれば容易に理解できるであ
ろう。This principle can be easily understood by referring to FIG.

第３図において、レンチキュラーレンズに垂直に入射す
る平行光のうち、矢印の位置のものは角度θｌだけ傾い
て進み、スクリーンが屈折率１１１の単一の材料ででき
ている場合、これを透過したときの拡散角θうとθｌと
の間には、 ｎｌ５ｉｎθＩ＝ｓｉｎθ３ の関係がある。　屈折率ｎ２　（ｎ２＞　ｎｌ　）の基
材がある場合には、暴利に入るときの傾きθ２は、ｎ１
ｓｉｎθ＋　＝　ｒ＋２　Ｓ　Ｉ１１θ２であり、基材
から出るときの傾きθ４は、ｎ２ｓｉｎ　　θ２　＝ｓ
ｉｎ　　θイであるから、結局、 ｓｉｎθ４−＝ｓｉｎθ３ となる。In Figure 3, among the parallel lights incident perpendicularly on the lenticular lens, the one at the arrow position travels at an angle of θl, and if the screen is made of a single material with a refractive index of 111, it will be transmitted through the lenticular lens. There is a relationship between nl5inθI=sinθ3 between the diffusion angle θ and θl. If there is a base material with a refractive index n2 (n2>nl), the slope θ2 at the time of profiteering is n1
sinθ+ = r+2 S I11θ2, and the slope θ4 when exiting from the base material is n2sin θ2 = s
Since in θi, sin θ4−=sin θ3.

本発明のレンチキュラースクリーンの材木・１は、やは
り透明な熱可塑性樹脂が適当であって、種々のものが使
用できるが、代表的な材料は下記の占おりであって、あ
わせ記した屈折率の値を考慮して選択し組み合わせれば
よい。The lumber 1 of the lenticular screen of the present invention is suitably a transparent thermoplastic resin, and various materials can be used, but the typical material is the one shown below, with a refractive index as shown below. All you have to do is consider the value, select and combine them.

セルロースアセテートブチレー１−　　　　１．４７　
　小ポリエチレンテレフタレート　　　　　　１．６５
　　犬スクリーンの設計に関する事項、とくにレンチキ
ュラーレンズの層の厚さおよび基材の厚さは、レンズピ
ッチおよび使用拐料の屈折率とその組み合わせに応じて
、所望の拡散角かえられるように、上記の関係にもとづ
いて決定すればＪ：い。Cellulose acetate butyrate 1- 1.47
Small polyethylene terephthalate 1.65
Matters related to the design of the dog screen, especially the thickness of the lenticular lens layer and the thickness of the base material, should be adjusted according to the above-mentioned values so that the desired diffusion angle can be changed depending on the lens pitch, the refractive index of the lens material used, and their combination. J: Yes, if you decide based on the relationship.

具体例を示せば、次のとおりである。A specific example is as follows.

（従来品） レンチキュラーレンズ層だけ・・・・・・・Ｉ）ＭＭＡ
厚さ　ｌ　８９０　ｔ＊ （本発明品） レンチキュア　　”　ス／Ｆ？・・・・・・・・・・・
・・・・・ＰＭＭＡ厚さ　　２０μ 基材層・・・・・・・・・・・ＰＳ　　厚さ　２０１０
μ厚さ合泪　２０３０μ ２層のラミネートは１熱融着によってもよいし、適宜の
接着剤を使用してもよい。　ブラックストライプを設け
る技術は既知である。(Conventional product) Only lenticular lens layer...I) MMA
Thickness l 890 t* (Product of the present invention) Lenticure "S/F?"
・・・・・・PMMA thickness 20μ Base material layer・・・・・・・・・PS thickness 2010
μ Thickness: 2030 μ The two-layer laminate may be laminated by heat fusion, or an appropriate adhesive may be used. Techniques for providing black stripes are known.

本発明のスクリーンは、上記の例のように、従来のもの
にくらべて、厚さを７．４％寸だけそれ以上、増すこと
ができる。　その結果、スクリーンは十分な強度をもつ
ことができる、１　光学的（’Ｉ能は、２層構成とする
ことにＪ：つでも、実質−１−影響を受けない。　寸／
こ、十詔の例でいえば、組み合わせは薄いＰＭＭＡと厚
いＩ）Ｓであって、廉価なＰＳが主体となるから、寸ず
材料代が節減できる３、成形においても、市販さノ９て
いる厚さ２０／ｌ稈度のＰＭＭＡフィルムをロールエン
ボソンク法ニヨリレンチギュラーレンズにすると同時に
、基材１）Ｓ十へ熱融着により一体化できるから、加工
費も低床ですむ。　この」：うにして、前記した本発明
の目的が達成できるのである３、The screen of the present invention, as in the above example, can be increased in thickness by 7.4% compared to the conventional screen. As a result, the screen can have sufficient strength; the optical performance is virtually unaffected by the two-layer construction.
In the example of Juyaku, the combination is thin PMMA and thick I)S, and since the inexpensive PS is the main material, the cost of materials can be reduced3.In molding, it is also possible to use commercially available materials. At the same time, a PMMA film with a thickness of 20/l and a culm density of 20/l can be made into a Nyori lenticular lens using the roll embossing method, and at the same time, it can be integrated with the base material 1) S1 by heat fusion, so the processing cost can be kept low. In this way, the above-mentioned object of the present invention can be achieved.

【図面の簡単な説明】[Brief explanation of the drawing]

第１図は、従来のブラックストライブタイプのレンチキ
ュラースクリーンの構成と作用を示す、拡大断面図であ
る３、 第２図に１、不発りｊによるレンチキュラースクリーン
を示す、第１図と同様な図である３、第３図は、本発明
により透過光の拡散角を変えないでスクリーンを厚くで
きる片肌を説明する図である。 １Ａ　・従来のレンチキュラースクリーン１Ｂ・・本発
明のレンチキュラースクリーン２Ａ、２Ｂ・　レンチキ
ュラーレンズ ３・・　ブラックストライブ ４・・基　材 特許出願人　　大日本印刷株式会社 代理人　弁理士　　須　賀　総　夫 牙１図 才８図1 is an enlarged sectional view showing the structure and function of a conventional black stripe type lenticular screen. 3. FIG. 3. FIG. 3 is a diagram illustrating one side of the screen that can be made thicker without changing the diffusion angle of transmitted light according to the present invention. 1A - Conventional lenticular screen 1B - Lenticular screen of the present invention 2A, 2B - Lenticular lens 3 - Black stripe 4 - Base material Patent applicant Dainippon Printing Co., Ltd. Agent Patent attorney Sou Suga 1 Figure 8 years old

Claims (1)

【特許請求の範囲】[Claims] （１）　　ブラックストライプタイプのレンチキュラー
スクリーンにおいて、スクリーンを少なくとも２層で構
成し、レンチキュラーレンズ面の層には屈折率の小さい
光学４：Ａ別を、そして裏面の基材層には屈折率の大き
い光学材料をそれぞれ使用したことを特徴とするスクリ
ーン。 ＋２１　　光学材料として、セルローストリアセテ−１
・。 セルローストリアセテ−１・、セルロースアセテートブ
チレート、ポリメチルメタクリレート。 ニトロセルロース、ホリ塩化ビニル、　ホ’）　カーボ
ネート、ポリスチレンおよびポリエチレンテレフタレ−
１・から、その屈折率にもとついてえらんだ２種の合成
樹脂を組み合わせて使用した特許請求の範囲第１項のス
クリーン。(1) In a black stripe type lenticular screen, the screen is composed of at least two layers, the layer on the lenticular lens surface has an optical 4:A layer with a low refractive index, and the base material layer on the back side has a high refractive index. A screen characterized by the use of different optical materials. +21 Cellulose triacetate-1 as an optical material
・. Cellulose triacetate-1, cellulose acetate butyrate, polymethyl methacrylate. Nitrocellulose, polyvinyl chloride, carbonate, polystyrene, and polyethylene terephthalate
1. The screen according to claim 1, which uses a combination of two types of synthetic resins selected based on their refractive indexes.