JPS5925827A - Covering material made of synthetic resin for agriculture and its use - Google Patents

Abstract

PURPOSE:A material made of synthetic resin for agriculture, especially in a filmy state, useful for covering cultivation facilities such as house for agriculture, etc., suppressing the phenomena of the occurrence of fog in the vicinity of the inner surface of a covering material, obtained by blending the synthetic resin with a phosphoric ester-based surface active agent. CONSTITUTION:100pts.wt. resin (excluding plasticizer in the calculation), synthetic resin, especially advantageously polyvinyl chloride having 1,000-2,000 polymerization degree, containing 1-5wt% anti-fogging agent, is blended with 0.05- 5.0pts.wt. phosphoric ester-based surface active agent (especially compound shown by the formula II) shown by the formula O=P(OR)n.(OM)3-n [n is 1-3; R is CmH2m+1, CmH2m+1(OR')l, group shown by the formula I , CmH2m+1CONH (OR')l (m is 1-22; l is 1-20, R' is 2-4C alkylene); M is H, NH4, triethanolamine, alkali metal, alkaline earth metal]. A film having 0.03-0.2mm. thickness is preferable as the covering material for agriculture.

Description

【発明の詳細な説明】 本発明は、農業用被覆材及びその使用方法に関するもの
である。更に詳しくは、被覆材内表面近傍における霧発
生現象を抑制する能力のある合成樹脂製農業用被覆材、
及び施設栽培における該被覆材の使用方法に関するもの
である。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to agricultural coverings and methods of using the same. More specifically, a synthetic resin agricultural covering material capable of suppressing fog generation near the inner surface of the covering material;
and a method for using the covering material in facility cultivation.

近年、有用植物の生産性、市場性を高めるために、農業
用ビニルフィルムなどの農業用被覆材による被覆下に、
有用植物を促成、半促成又は抑制栽培する、いわゆるハ
ウス栽培やｌ・ンネル栽培が盛んに行われている。In recent years, in order to increase the productivity and marketability of useful plants, they are covered with agricultural covering materials such as agricultural vinyl film.
2. Description of the Related Art So-called house cultivation and L-channel cultivation, in which useful plants are cultivated under forced, semi-forced or suppressed conditions, are actively practiced.

この・・ウス栽培やトンネル栽培において、現在使用さ
れている合成樹脂被覆材、例えば塩化ビニル系樹脂フィ
ルムの大部分は、被覆材内表面（・・ウスやトンネルの
内部に面する側の表面をいう。以下同じ。）における水
滴の流下を促進し、日光の入射量を多くするために、界
面活性剤の一種である防曇剤（主としてソルビタン脂肪
酸エステル；グリセリン脂肪酸エステルなど。）を含ん
でいる。このような防曇剤を含む被覆材の被覆下では、
被覆材の内外での温度差が大きくなるため、被覆材の内
表面近傍において霧が発生するという現象が、しばしば
観察される。Most of the synthetic resin covering materials currently used in this field cultivation and tunnel cultivation, such as vinyl chloride resin films, Contains an antifogging agent (mainly sorbitan fatty acid ester; glycerin fatty acid ester, etc.), which is a type of surfactant, to promote the flow of water droplets and increase the amount of sunlight incident. . Under coating with coating materials containing such antifogging agents,
Due to the large temperature difference between the inside and outside of the coating, the phenomenon of fog generation near the inner surface of the coating is often observed.

この霧発生現象は、・・ウス栽培及びトンネル栽培等の
施設栽培にとって最も大切な晩秋ないし冬期に多く発生
する。霧発生現象の原因は、正確にはわからないが、ハ
ウス又はトンネル内の気温、湿度、・・ウス又はトンネ
ル内土壌の温度、含水量、ハウス又はトンネルへの日射
量、被覆材の濡れた面の親水性の程度などが微妙に影響
し合って、ハウス又はトンネル内の湿気が温度変化によ
って被覆材表面に順調に利着し、流れる現象が行なわれ
ず、一部の湿気が被覆材内表面近傍で霧状に々ることに
よるものと推定される。This fog phenomenon often occurs in late autumn or winter, which is the most important period for greenhouse cultivation such as greenhouse cultivation and tunnel cultivation. The cause of the fog generation phenomenon is not precisely known, but it is due to the temperature and humidity inside the greenhouse or tunnel, the temperature and moisture content of the soil inside the greenhouse or tunnel, the amount of solar radiation to the greenhouse or tunnel, and the wet surface of the covering material. Due to the subtle influence of the degree of hydrophilicity, the moisture inside the house or tunnel smoothly absorbs onto the surface of the sheathing material due to temperature changes, and some moisture remains near the inner surface of the sheathing material. It is presumed that this is due to the formation of a mist.

このような霧発生現象は、本発明者らの観察によれば、
ハウス又はトンネル内の地表面近傍。According to the observations of the present inventors, such a fog generation phenomenon is caused by
Near the ground surface inside a house or tunnel.

栽培植物の近傍及び被覆材内表面近傍でおこることが判
った。更に、被覆材及び被覆材内面は。It was found that this occurs near cultivated plants and near the inner surface of the covering material. Furthermore, the coating material and the inner surface of the coating material.

外気温の低下により冷却されて、・・ウス内との間に温
度差を生じ、ハウス内の暖かく、湿った空気が自然対流
により、被覆材内表面の近傍に移動すると空気中に含む
ことのできなくなった　３− 水蒸気が、凝縮して微小水滴と々す、霧状となって自然
対流によって、ノーウス又はトンネル内に拡がることが
判った。一旦発生した霧状の微小水滴が、自然対流の途
中で再度蒸発して消失する場合は、霧は・・ウス又はト
ンネル内には拡がらないが、蒸発消失速度が遅い場合に
は、・・ウス又はトンネル全体が濃い霧となることも判
った。It is cooled by the drop in outside temperature, creating a temperature difference with the inside of the greenhouse, and when the warm, humid air inside the greenhouse moves close to the inner surface of the sheathing material due to natural convection, the amount of air contained in the air increases. 3- It has been found that water vapor condenses into minute water droplets, forms a mist, and spreads inside the nous or tunnel through natural convection. If the mist-like minute water droplets once generated evaporate and disappear again during natural convection, the fog will not spread into the tunnel or the tunnel, but if the rate of evaporation and disappearance is slow... It was also found that the entire tunnel was covered in thick fog.

このような霧発生現象は、ノ・ウス又はトンネル内で栽
培する有用作物の葉、茎、花、実などを濡らし、病害発
生の原因となり、又は病害発生伝播の助けともなる。ま
た、栽培作物が濡れると、乾かすのに・−１熱が必要と
なり、・・ウス又はトンネル内の暖房のための燃料がそ
れだけ多く必要となる、等の不利を生ずる。さらに、ハ
ウス内の見通しが悪くなるため、農作業の能率が低下す
る等の弊害もある。Such a fog generation phenomenon wets the leaves, stems, flowers, fruits, etc. of useful crops grown in the nous or tunnels, causing disease outbreaks or helping the disease spread. Also, if the cultivated crops get wet, -1 heat is required to dry them, resulting in disadvantages such as the need for more fuel for heating the inside of the greenhouse or tunnel. Furthermore, since the visibility inside the greenhouse becomes poor, there are also disadvantages such as a decrease in the efficiency of agricultural work.

このような不利を解消するため、従来、・・ウスやトン
ネル内の気温変化を少しでも柔けるために、着色した農
業用合成樹脂フィルムを使用　４− したり、ハウス又はトンネル内の土壌をマルチングフィ
ルムで覆ったりして水の蒸発量を抑えたり、更にまた潅
水時間を工夫したり（例えば、゛夕方遅くなってから潅
水したり、潅水部分や潅水量を調節するなど）、潅水方
法、装置を改善する等の方策がとられてきた。しかし、
いずれの方法も、霧発生現象を完全に抑えるには、有効
なものではなかった。In order to overcome these disadvantages, conventional methods have been to use colored synthetic agricultural resin films or mulch the soil inside greenhouses or tunnels to soften the temperature changes inside greenhouses or tunnels. Covering the water with a film to reduce the amount of water evaporation, or adjusting the watering time (for example, watering later in the evening, adjusting the area and amount of water to be watered, etc.), watering methods and equipment. Measures have been taken to improve the but,
None of the methods were effective in completely suppressing the fog generation phenomenon.

本発明者らは、上記防曇性合成樹脂製農業用被覆材によ
る被覆下での、有用植物の施設栽培（ハウス栽培、トン
ネル栽培など）において、該被覆材の内表面近傍におい
て、しばしば発生する霧の発生を簡単に、かつ、効果的
に防止する方策について鋭意研究を重ねた結果、本発明
を完成するに至ったものである。The present inventors have discovered that in the facility cultivation of useful plants (house cultivation, tunnel cultivation, etc.) under the coating with the above-mentioned antifogging synthetic resin agricultural coating material, the occurrence of oxidation often occurs near the inner surface of the coating material. The present invention was completed as a result of extensive research into ways to easily and effectively prevent the occurrence of fog.

しかして本発明に従えば、リン酸エステル系界面活性剤
を含有することを特徴とする合成樹脂製農業用被覆材が
提供される。According to the present invention, there is provided a synthetic resin agricultural covering material characterized by containing a phosphate ester surfactant.

本発明に従えば、１だ、合成樹脂製農業用被覆材による
被覆下に有用植物を栽培する方法において、該被覆材と
して、リン酸エステル系界面活性剤を含有する合成樹脂
製農業用被覆材を使用することを特徴とする、被覆材内
表面近傍における霧の発生を抑制する方法が提供される
。According to the present invention, in the method of cultivating useful plants under a covering with a synthetic resin agricultural covering material, the covering material is a synthetic resin agricultural covering material containing a phosphate ester surfactant. Provided is a method for suppressing the generation of fog near the inner surface of a coating material.

以下、本発明の詳細な説明する。The present invention will be explained in detail below.

本発明において、合成樹脂製農業用被覆材と張 は、ハウス又はトンネル等の栽培施設に層重り有用植物
を栽培する際に使用される、光透過性の合成樹脂基材か
ら成るもので、特にフィルム状の農業用資材をいう。In the present invention, the synthetic resin agricultural covering and upholstery are made of a light-transparent synthetic resin base material, which is used when cultivating useful plants in cultivation facilities such as greenhouses or tunnels. A film-shaped agricultural material.

本発明に従って、合成樹脂製農業用被覆材にリン酸エス
テル系界面活性剤が添加、配合される。リン酸エステル
系界面活性剤としては、次のような一般式（１１で示さ
れる化合物があげられる。According to the present invention, a phosphate ester surfactant is added and blended into a synthetic resin agricultural coating material. Examples of the phosphate surfactant include compounds represented by the following general formula (11).

０＝Ｐ（ＯＲ）ｎ−（ＯＭ）、ｎ　　・・・・・・・（
ＩＦ〔式（１）において、ｎは／〜３の中から選ばれる
整数であり；Ｒは一般式 ％式％ ） ） （式中、ｍは／〜ニスの中から選ばれた整数、ｌは／〜
スθの中から選ばれた整数　Ｒ／は炭素数２〜７個のア
ルキレン基を示す。）で表わされる基から選ばれたもの
であり；Ｍは水素原子、ＮＨ，，１−リエタノールアミ
ン基、アルカリ金属、アルカリ土類金属から選ばれたも
のである。〕上記一般式（Ｉｌで闘わされる化合物の具
体例としては、次のような化合物が挙げられるが、化合
物の例示は、本発明を限定するものではない。0=P(OR)n-(OM),n・・・・・・(
IF [In formula (1), n is an integer selected from /~3; R is a general formula% formula%) (wherein, m is an integer selected from /~varnish, l is /~
R/ represents an alkylene group having 2 to 7 carbon atoms. ); M is selected from a hydrogen atom, NH,, 1-liethanolamine group, an alkali metal, and an alkaline earth metal. ] Specific examples of compounds represented by the above general formula (Il) include the following compounds, but the examples of the compounds do not limit the present invention.

（１） 　８− 前記一般式（Ｉ）で表わされる化合物のうち、次の（１
１式で表わされる化合物が、特に優れた効果を発揮する
。(1) 8- Among the compounds represented by the general formula (I), the following (1)
A compound represented by formula 1 exhibits particularly excellent effects.

〔一般式（Ｉｌｌにおいて、ｍは／〜２２の中から選ば
れた整数、ｌは／〜２０の中から選ばれた整数、Ｒは炭
素数２〜ｑ個のアルキレン基を示す。〕」二配りン酸エ
ステル系界面活性剤は、それぞれ単独で使用することが
できるし、ス種又はそれ以上を組み合せて使用すること
ができる。このリン酸エステル系界面活性剤の、合成樹
脂製農業用被覆材への配合量は、臨界的ではなく、配合
すべきリン酸エステル系界面活性剤の種類や、合成樹脂
の種類に応じて広範に変えることができる。一般的には
、配合すべき合成樹脂材７００重量部（ただし可塑剤は
計算に含めない。[In the general formula (Ill), m is an integer selected from / to 22, l is an integer selected from / to 20, and R represents an alkylene group having 2 to q carbon atoms.] The phosphate ester surfactants can be used alone or in combination of two or more types.This phosphate ester surfactant can be used as a synthetic resin agricultural coating. The amount added to the material is not critical and can be varied widely depending on the type of phosphate ester surfactant to be added and the type of synthetic resin.In general, the amount of synthetic resin to be added 700 parts by weight of material (plasticizer is not included in the calculation.

以下同じ。）当り、少なくともＯ，Ｏ！ｉ重量部とする
ことができ、また、配合量の上限は厳密に制約されるも
のではないが、あ捷り多量に配合する−と、ブリードア
ウトや白濁を生ずるおそれがあるので通常はＳ、Ｏ重量
部以下で充分である。配合量の好適範囲は、合成樹脂材
７００重量部当りｏ、ｉ〜ス、０重量部である。same as below. ) hit, at least O,O! The upper limit of the blending amount is not strictly limited, but if too much is mixed in, it may cause bleed-out or cloudiness, so usually S, O parts by weight or less are sufficient. The preferred range of blending amount is o, i-s, 0 parts by weight per 700 parts by weight of the synthetic resin material.

本発明に従い、−ト記リン酸エステル系界面活性剤が配
合される農業用被覆材を構成する合成樹脂材料としては
、一般にフィルム形成性の熱可塑性合成樹脂があげられ
る。具体的には塩化ビニル、エチレン、プロピレン、ア
クリル酸エステル、メタクリル酸エステル等の単量体の
単独又はこれら相互の共重合体、あるいはこれら単量体
中の少なくとも７種と他の共重合可能な単量体（例えば
酢酸ビニル、塩化ビニリデン等）との共重合体、含フツ
素樹脂、ポリエステル、ポリアミド等もしくはこれら重
合体のブレンド物があげられる。これらの中では、耐候
性、光透過性、経済性、強度等の観点から、塩化ビニル
系樹脂（すなわち、ポリ塩化ビニル及び塩化１１− ビニルを！ｉＯ重量重量上以上その共重合体）及びエチ
レン系樹脂（すなわち、ポリエチレン及びエチレンを５
０重量％り上含むその共重合体）が好適であり、最も有
利にはポリ塩化ビニルである。According to the present invention, the synthetic resin material constituting the agricultural covering material to which the phosphoric acid ester surfactant is blended is generally a film-forming thermoplastic synthetic resin. Specifically, monomers such as vinyl chloride, ethylene, propylene, acrylic esters, methacrylic esters, etc. alone or copolymers of these monomers, or at least seven of these monomers and other copolymers are possible. Examples include copolymers with monomers (eg, vinyl acetate, vinylidene chloride, etc.), fluorine-containing resins, polyesters, polyamides, etc., and blends of these polymers. Among these, vinyl chloride resins (i.e., polyvinyl chloride and 11-vinyl chloride, copolymers thereof) and ethylene based resins (i.e. polyethylene and ethylene)
Polyvinyl chloride is preferred, most preferably polyvinyl chloride.

これら合成樹脂基材には、本発明の農業用被覆材に防曇
性をもたせるため、従来から農業用塩化ビニル系樹脂フ
ィルムの分野で利用されている防曇剤を配合する。しか
して、本発明において用いることができる防曇剤として
は、主として非イオン系界面活性剤、例えばソルビタン
モノステアレート、ソルビタンジステアレート、ソルビ
タントリステアレート、ソルビタンモノパルミテート、
ソルビタンジパルミテート、ソルビタントリパルミテー
ト、ソルビタンモノベンゾエート、ソルビタンジベンゾ
エート、ソルビタントリベンゾエートなどのソルビタン
系界面活性剤；グリセリンラウレート、ジグリセリンパ
ルミテート、グリセリンステアレートなどのグリセリン
系界面活性剤；ポリエチレングリ−１２＝ コールステアレート、ポリエチレンクリコールハルミテ
ートなどのポリエチレングリコール系界面活性剤；アル
キルフェノールのアルキレンオキシド付加物；ソルビタ
ン／グリセリンの縮合物と有機酸とのエステル、等が包
含される。In order to impart antifogging properties to the agricultural coating material of the present invention, these synthetic resin base materials are blended with an antifogging agent that has been conventionally used in the field of agricultural vinyl chloride resin films. Therefore, the antifogging agent that can be used in the present invention mainly includes nonionic surfactants such as sorbitan monostearate, sorbitan distearate, sorbitan tristearate, sorbitan monopalmitate,
Sorbitan surfactants such as sorbitan dipalmitate, sorbitan tripalmitate, sorbitan monobenzoate, sorbitan dibenzoate, and sorbitan tribenzoate; glycerin surfactants such as glycerin laurate, diglycerin palmitate, and glycerin stearate; polyethylene Gly-12 = polyethylene glycol surfactants such as coal stearate and polyethylene glycol halumitate; alkylene oxide adducts of alkylphenols; esters of sorbitan/glycerin condensates and organic acids, and the like.

これら防曇剤は、それぞれ単独で、又は２種以上を組み
合わせて用いることができる。These antifogging agents can be used alone or in combination of two or more.

防曇剤の基体樹脂への配合量は、従来の農業用合成樹脂
フィルムに対して使用されている場合と同等とすること
ができる。一般的には、合成樹脂基材１００重量部当り
、７〜５重量部の範囲、好捷しくはハＳ〜３．．！；重
量部の範囲とすることができる。The amount of antifogging agent added to the base resin can be the same as that used for conventional agricultural synthetic resin films. Generally, the amount is in the range of 7 to 5 parts by weight, preferably 3 to 3 parts by weight, per 100 parts by weight of the synthetic resin base material. ．． ! ; can be in the range of parts by weight.

本発明に係る農業用被覆材を構成する合成樹脂基材はま
た、必要に応じて、通常の各種樹脂添加物、例えば可塑
剤、滑剤、熱安定剤、帯電防止剤、紫外線吸収剤、顔料
、染料等を、通常の量で含むことができる。The synthetic resin base material constituting the agricultural covering material according to the present invention may also contain various conventional resin additives, such as plasticizers, lubricants, heat stabilizers, antistatic agents, ultraviolet absorbers, pigments, Dyes and the like can be included in conventional amounts.

例えば、本発明において好適な軟質塩化ビニル系樹脂に
ついていえば、重合度が約ｉｏｏ。For example, the soft vinyl chloride resin suitable for the present invention has a degree of polymerization of about io.

〜２０００のポリ塩化ビニル１０θ重量部に対して、可
塑剤を約、７０〜７０重量部の割合で配合することがで
きる。用いうる好適な可塑剤としては、例えばジ−ｎ−
オクチルフタレート、シーニーエチルへキシルフタレー
ト、ジベンジルフタレート、ジインデシルフタレート、
ジドデシルフタレート、ジウンデシルフタｖ−）％のフ
タル酸誘導体；ジイソオクチルフタレート等のイソフタ
ル酸誘導体；ジ−ｎ−ブチルアジペート、ジオクチルア
ジペ−１・等のアジピン酸誘導体；ジ−ｎ−ブチルマレ
ート等のマレイン酸誘導体；）ＩＪ−ｎ−ブチルシトレ
ート等のクエン酸誘導体；モノブチルイタコネート等ノ
イタコン酸誘導体；ブチルオレート等のオレイン酸誘導
体；グリセリンモノシトレート等のリシノール酸誘導体
：その他トリクレジルホスフェート、エポキシ化大豆油
、エポキシ樹脂系可塑剤等があげられる。The plasticizer can be blended at a ratio of about 70 to 70 parts by weight to 100 parts by weight of polyvinyl chloride of 2000 to 2000 parts by weight. Suitable plasticizers that can be used include, for example, G-n-
Octyl phthalate, ethylhexyl phthalate, dibenzyl phthalate, diindecyl phthalate,
Phthalic acid derivatives such as didodecyl phthalate and diundecyl phthalate (v-)%; isophthalic acid derivatives such as diisooctyl phthalate; adipic acid derivatives such as di-n-butyl adipate and dioctyl adipate-1; di-n-butyl maleate, etc. Maleic acid derivatives;) Citric acid derivatives such as IJ-n-butyl citrate; Noitaconic acid derivatives such as monobutyl itaconate; Oleic acid derivatives such as butyl oleate; Ricinoleic acid derivatives such as glycerin monocitrate; Other tricresyl phosphate , epoxidized soybean oil, epoxy resin plasticizers, etc.

また、合成樹脂基材に含ませうる滑剤または熱安定剤と
しては、例えばポリエチレンフックス、ビスアマイド、
ステアリン酸、ステアリン酸亜鉛、ステアリン酸バリウ
ム、ステアリン酸カルシウム、リシノール酸バリウム等
があげられる。紫外線吸収剤としては、例えばベンゾト
リアゾール系、ベンゾエート系、べ／シフエノン系、シ
アノアクリレート系、フェニルザリシレート系等の紫外
線吸収剤があげられる。また、顔料及び染料としては、
例えば酸化チタン、シリカ、群青、フタロシアニンブル
ー等があげられる。In addition, examples of lubricants or heat stabilizers that can be included in the synthetic resin base material include polyethylene Fuchs, bisamide,
Examples include stearic acid, zinc stearate, barium stearate, calcium stearate, barium ricinoleate, and the like. Examples of the ultraviolet absorber include benzotriazole-based, benzoate-based, ben/cyphenon-based, cyanoacrylate-based, and phenylzalycylate-based ultraviolet absorbers. In addition, as pigments and dyes,
Examples include titanium oxide, silica, ultramarine blue, and phthalocyanine blue.

こわら樹脂添加物は、通常の含有量、例えば前記合成樹
脂基材１００重量部当り、５重量部以下の少量で含ませ
うる。The stiff resin additive may be included in a conventional amount, for example, in a small amount of 5 parts by weight or less per 100 parts by weight of the synthetic resin base material.

基材となる合成樹脂に、防曇剤、リン酸エステル系界面
活性剤、更に要すれば各種樹脂添加物を台筐せるには、
通常の配合技術、混合技術、例えばリボンブレンダー、
バンバリーミキサ−、スーパーミキサー、その他の配合
機、混合機によって混合した後、フィルム化することに
より可能である。In order to add antifogging agents, phosphate ester surfactants, and various resin additives to the base synthetic resin,
Conventional compounding techniques, mixing techniques such as ribbon blenders,
This can be done by mixing with a Banbury mixer, super mixer, or other compounding machine or mixer, and then forming the mixture into a film.

１５− 合成樹脂をフィルム化するには、それ自体公知の方法、
例えば溶融押出法、溶液流延法、カレンダー法等を採用
すればよい。15- To form a film from a synthetic resin, a method known per se,
For example, a melt extrusion method, a solution casting method, a calender method, etc. may be employed.

本発明に係る農業用被覆材の厚さは、余り薄いと強度が
不充分で好捷しくなく、逆に余り厚すぎるとフィルム化
作業、その後の取り扱い（フィルムを切ってハウス型に
接合する作業、・・ウスに展張する作業等を含む）等に
不便をきたすので、０．０３〜０．２籠の範囲とするの
がよい。If the thickness of the agricultural covering material according to the present invention is too thin, the strength will be insufficient and it will be undesirable. On the other hand, if it is too thick, it will be difficult to make it into a film, and the subsequent handling (cutting the film and joining it into a house shape) , etc.), etc.), so it is preferable to set the cage in the range of 0.03 to 0.2.

以上述べたとおり、本発明に係る農業用被覆材は、従来
行なわれていると同様にして、・・ウス、トンネル等の
農園芸施設に展張し、有用植物の栽培に利用することが
できる。As described above, the agricultural covering material according to the present invention can be spread over agricultural and horticultural facilities such as cages and tunnels in the same manner as conventional methods and used for cultivating useful plants.

前述したように、リン酸エステル系界面活性剤を含ませ
た本発明に係る農業用被覆材が展張されたハウス又はト
ンネルにおいては、後記実施例からも明らかなとおり、
被覆材内表面近傍における霧の発生が効果的に抑制され
る。その抑制効果は極めて強力で、従来から霧が多発す
１６− るといわれていた晩秋ないし冬場でも、霧発生を実質的
に完全に抑制することができ、有用植物の病害発生及び
伝播の阻止に顕著な効果がある。更に、従来のように、
濯水等に細心の注意を払う必要がない。しかも、本発明
に係る農業用被覆材は、このような霧発生抑制効果を長
期に亘って持続することができる。従って、本発明に係
る農業用被覆材は、有用植物の施設栽培において、利用
価値が極めて甚大である。As mentioned above, in the greenhouse or tunnel in which the agricultural covering material according to the present invention containing a phosphate ester surfactant is spread, as is clear from the examples below,
The generation of fog near the inner surface of the coating material is effectively suppressed. Its suppressive effect is extremely strong, and even in late autumn and winter, when it has traditionally been said that fog occurs often, it can virtually completely suppress the occurrence of fog, and it is effective in preventing the occurrence and spread of diseases on useful plants. It has a remarkable effect. Furthermore, as before,
There is no need to pay close attention to rinsing etc. Moreover, the agricultural covering material according to the present invention can maintain such a fog generation suppressing effect over a long period of time. Therefore, the agricultural covering material according to the present invention has extremely great utility value in the facility cultivation of useful plants.

以下、本発明を実施例にもとづいて詳細に説明するが、
本発明はその要旨を超えない限り、以下の例に限定され
るものではない。Hereinafter, the present invention will be explained in detail based on examples.
The present invention is not limited to the following examples unless it exceeds the gist thereof.

実施例／〜１０．比較例／〜３ ポリ塩化ビニル（Ｐ＝／３ｏｏ　）　　１０θ重量部ジ
オクチル７タレート　　　　　　５θ　〃Ｂａ−Ｚｎ系
液状安定剤　　　　　　　λ　〃Ｂａ−Ｚｎ系粉末状安
定剤　　　　　　／　ｌンルビタンモノパルミテートコ
〃 を基本組成とし、これに１７表に示すリン酸エステル系
界面活性剤を、／重量部混合し、その混合物を７ｇ０℃
に加温したカレンダーに供給し、常法によりフィルム化
し、厚さ０．７闘のフィルムを作成した。Examples/~10. Comparative Example/~3 Polyvinyl chloride (P=/3oo) 10θ parts by weight Dioctyl 7-talate 5θ Ba-Zn liquid stabilizer λ Ba-Zn powder stabilizer / Rubitan monopalmitate co〃Basic The following composition was prepared, and the phosphoric acid ester surfactant shown in Table 17 was mixed therein in parts by weight, and 7g of the mixture was heated at 0°C.
The mixture was fed into a calender heated to 100 mL and formed into a film using a conventional method to form a film with a thickness of 0.7 mm.

比較のため、リン酸エステル系界面活性剤を混合しなか
ったもの（比較例／）、市販されている厚み０．／、ｍ
の農業用防曇性ポリ塩化ビニルフィルム（比較例２）及
び市販されている厚み０、／酩の農業用防曇性ポリエチ
レンフィルム（比較例３）を準備した。For comparison, a sample containing no phosphate ester surfactant (comparative example/), a commercially available sample with a thickness of 0. /, m
A commercially available anti-fog polyvinyl chloride film for agricultural use (Comparative Example 2) and a commercially available anti-fog polyethylene film for agricultural use (Comparative Example 3) with a thickness of 0.5 mm were prepared.

一］二記７３種のフィルムについて、以下の方法で霧発
生試験と防曇性の評価を行なった。1] 2) The 73 types of films listed above were subjected to fog generation tests and antifogging evaluations using the following methods.

（１）霧発生試験 三重系−志郡の圃場に、間口ｊ’、＋７７１、棟高３ｍ
、奥行１５ｍのパイプ／’ｔウス／−ｔｌＨ１ｉし、各
棟に上記フィルムの７種を被覆した（昭和３−６年１０
月コ乙日）。ノ・ウス内ではホウレン草を栽培しつつ、
ハウス内での霧の発生状況を肉眼で観察し評価した。そ
の結果を１７表に示す。(1) Fog generation test Mie system - Shigun field, frontage j', +771, ridge height 3m
, a pipe with a depth of 15 m/'tus/-tlH1i was constructed, and each building was coated with seven types of the above films (1920-1939
month). While growing spinach in NOUS,
The occurrence of fog inside the greenhouse was visually observed and evaluated. The results are shown in Table 17.

霧の発生程度の評価は、パイプノ・ウスにフィルムを被
覆ｌ−た直後の３−日間（昭和５乙年７θ月２７日〜Ｉ
Ｏ月３７日）と、被覆後ダカ月経過した頃のＳ日間（昭
和３−７年λ月、２．２日〜λ月ス乙日）に行なった。The degree of fog generation was evaluated during the 3-day period immediately after coating the pipes with the film (from July 27, 1933 to I
The test was carried out on the 37th day of October 1999) and on the S days (from the 2.2nd day of λ month 1939 to the 2nd day of λ month 1937), which was around the time that 1 month had passed since the coating.

霧の発生程度は、午前７時から午後６時までの間、７時
間ごとに７日当り７．２回観察して、結果を「霧の発生
評価」として数値で１７表に示した。The degree of fog occurrence was observed 7.2 times per 7 hours every 7 hours from 7 a.m. to 6 p.m., and the results are shown numerically in Table 17 as a "fog occurrence evaluation."

「霧の発生評価」の数値Ｕ５それぞれ次のような意義を
有する。Each numerical value U5 of "fog generation evaluation" has the following significance.

「／」・・・・・ハウス内に霧の発生が全く見られない
か、フィルム内表面近傍にの みわずかに発生１〜でいる状態。"/": No fog is observed in the house, or only a small amount of fog is generated near the inner surface of the film.

「、２」・・・・・ハウス全体に霧が発生しているが、
／ｋｍ先の・・ウスの奥が明瞭に識 別できる状態。``,2''...There is fog throughout the house,
/km away...the back of the house can be clearly identified.

「３」・・・・・ハウス全体に霧がやや濃く発生し、／
Ｓｍ先の・・ウスの奥を明瞭には 識別できない状態。"3"...The whole house has a slightly thick fog, /
A state in which it is not possible to clearly identify the back of the mouse ahead of Sm.

「１．ｔ」・・・・・ハウス全体に霧が濃く発生し、１
５〜１９− ｍ先のハウスの奥が全く識別でき ない状態。"1.t"...Dense fog has formed throughout the house, 1
The back of the house 5 to 19 meters away cannot be discerned at all.

「平均値」とけ、霧発生状況を観察し７’′ｃ、を日間
の数値を平均した値を意味し、「最高値」とは、Ｓ日間
のうちで観察された最も高い値を意味する。"Average value" means the value obtained by averaging the values for each day, and "highest value" means the highest value observed in S days. .

（２）　　防曇性の評価 愛知県名古屋布の圃場に、間０．２ｍ１棟高Ωｍ１奥行
λθｍの片屋根型・・ウスに、前記７３種のフィルムを
被覆しく昭和５Ａ年１０月ｇ日）、展張してから／週間
、３力月、乙カ月及び９力月の期間経過した際、各々の
フィルムの防曇性を肉眼で観察し、評価した。(2) Evaluation of anti-fogging properties A single-roof type house with a width of 0.2 m, a height of Ωm, and a depth of λθm was coated with the above 73 types of films in a field in Nagoyafu, Aichi Prefecture (October g, 1932). After a week, three months, two months, and nine months had elapsed after the film was spread, the antifogging properties of each film were visually observed and evaluated.

その結果を１７表に示す。The results are shown in Table 17.

「防曇性の評価」の数値は、それぞれ次のような意義を
有する。The numerical values of "antifogging performance evaluation" have the following meanings.

「／」・・・・・水が薄膜状に付着し、水滴が認められ
ない状態。"/": Water adheres in a thin film and no water droplets are observed.

「ユ」・・・・・水が薄膜状に付着しているが、わずか
に大粒の水滴が認められる状 態。"Yu": Water is attached in a thin film, but slightly large water droplets are observed.

一２〇− 「３」・・・・・部分的に細かい水滴の付着が認められ
る状態。120- "3": Condition in which small water droplets are observed to be partially attached.

「り」・・・・・フィルム内表面全面に、細かい水滴の
付着が認められる状態。"Ri": Condition in which fine water droplets are observed on the entire inner surface of the film.

／ 牙　　／　　表 〔注〕×１　リン酸エステル系化合物番号は、さきに構
造式を例示した化合物の番号を 意味する。/ Fang / Table [Note] x 1 The phosphate ester compound number means the number of the compound whose structural formula is exemplified above.

×２　市販されている農業用ポリ塩化ビニルフィルム ※３　市販されている農業用ポリエチレンフィルム １７表の結果より、次のことが明らかである。×2 Commercially available agricultural polyvinyl chloride film *3 Commercially available agricultural polyethylene film From the results in Table 17, the following is clear.

（１）本発明に係る農業用被覆材を使用した場合は、被
覆材内表面近傍における霧の発生が効果的ＶＣ抑制され
る。(1) When the agricultural covering material according to the present invention is used, the generation of fog near the inner surface of the covering material is effectively suppressed by VC.

（２）　　本発明に係る農業用被覆材は、従来から知ら
れている防曇剤と併用することにより、防曇性を一層向
−」二し、かつ、防曇効果を一層持続することができる
。(2) By using the agricultural covering material according to the present invention in combination with a conventionally known antifogging agent, it is possible to further improve the antifogging property and further maintain the antifogging effect. can.

出　願　人　　　三菱モンザント化成株式会社代　理　
人　　弁理士　良否側　　− （ほか７名）Applicant Mitsubishi Monzanto Chemicals Co., Ltd. Representative
Person Patent attorney Liability side - (7 others)

Claims (4)

【特許請求の範囲】[Claims] （１）リン酸エステル系界面活性剤が配合されてなるこ
とを特徴とする、合成樹脂製農業用被覆材。(1) A synthetic resin agricultural covering material characterized by containing a phosphate ester surfactant. （２）　リン酸エステル系界面活性剤が、下記（１１式
で表わされる化合物であることを特徴とする特許請求の
範囲牙（１）項記載の農業用被覆材。 ０＝Ｐ（ＯＲ）ｎ・（ＯＭ）ａ−ｎ　　・・・・・・・
（１１〔式（Ｉｌにおいて、ｎは／〜３の中から選ばれ
る整数であり；Ｒは一般式 ％式％ ） ） （式中、ｍは７〜２．２の中から選ばれた整数、ｌは／
〜−〇の中から選ばれた整数、Ｒ′は炭素数−〜グ個の
アルキレン基を示す）で表わされる基から選ばれたもの
であり；Ｍは水素原子、ＮＨ，、ｌ−リエタノールアミ
ン基、アルカリ金属、アルカリ土類金属の中から選ばれ
たものである。〕(2) The agricultural covering material according to claim (1), wherein the phosphate ester surfactant is a compound represented by the following formula (11): 0=P(OR)n・(OM)a-n ・・・・・・・・・
(11 [Formula (Il, n is an integer selected from / to 3; R is the general formula % formula %) (wherein, m is an integer selected from 7 to 2.2, l is /
An integer selected from 〜-〇, R′ represents an alkylene group with carbon number 〜〜g); M is a hydrogen atom, NH,, l-reethanol It is selected from amine groups, alkali metals, and alkaline earth metals. ] （３）合成樹脂が、可塑剤３０〜７０重量部、防曇剤／
〜Ｓ重量重量部源れた防曇性軟質塩化ビニル系樹脂であ
ることを特徴とする特許請求の範囲１・（１）項々いし
牙（コ）項記載の農業用被覆材。(3) Synthetic resin contains 30 to 70 parts by weight of plasticizer, antifogging agent/
The agricultural covering material according to claim 1, (1), characterized in that it is an antifogging soft vinyl chloride resin containing .about.S parts by weight. （４）　　合成樹脂製農業用被覆材による被覆下に有用
植物を栽培する方法において、該被覆材として、リン酸
エステル系界面活性剤が配合されてなる合成樹脂製農業
用被覆相を使用することを特徴とする、被覆材内表面近
傍における霧の発生を抑制する方法。(4) In a method of cultivating useful plants under a covering with a synthetic resin agricultural covering material, a synthetic resin agricultural covering layer containing a phosphate ester surfactant is used as the covering material. A method for suppressing fog generation near the inner surface of a coating material, characterized by: