JPS59221943A - Color display with distinct coloring - Google Patents

Abstract

PURPOSE:To obtain color display with high brightness and high contrast by providing a filter made of transparent thermoplastic resin and having absorption in the range of specific wave length, between an observer, and a polychrome CRT using glass containing Nd as panel glass CONSTITUTION:A filter, which is made of transparent thermoplastic resin while having absorption in the more than one range in wave length of 380-420nm, 480-530nm and 640-780nm and having almost no absorption for visible rays in the range of excepting said wave length, besides having not less than 30% of the whole ray transmittivity, is provided between an observer, and a color CRT using pael glass contaning neodymium. As said transparent thermoplastic resin, either one of, for instance, acrylic resin, styrene resin, polycarbonate, vinyl chloride resin, polyvinyl butyral and cellulose acetate is used.

Description

【発明の詳細な説明】 この発明はディスプレイ装置に関するものであシ、詳し
くは高コントラストで、波長選択性の向上した装置に関
するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a display device, and more particularly to a device with high contrast and improved wavelength selectivity.

カラー陰極線管のパネルガラスの内面には、赤、緑およ
び青の三原色で一組をなす螢光体が多数のドツトまたは
ストライプ状に配列されて螢光面が形成されている。こ
の螢光面に向けて電子銃より発射される電子°ビームを
、シャドーマスクまだはアパーチャグリルを通過させる
ことによりカラー画像がパネルガラスを通して観察され
る。On the inner surface of the panel glass of a color cathode ray tube, a fluorescent surface is formed by arranging a set of phosphors in the three primary colors of red, green, and blue in the form of a large number of dots or stripes. A color image is observed through a panel glass by passing an electron beam emitted from an electron gun toward this fluorescent surface through a shadow mask and an aperture grill.

しかるに、カラー陰極線管の画像をパネルガラスを通し
て見る場合、観察者の周囲に存在する外光１例えば窓か
らの入射太陽光、螢光灯等の室内照明光が螢光面に入射
し、赤、緑および青の光で構成される画像のコントラス
トを著しく低下させるという問題があった。However, when viewing images from a color cathode ray tube through a panel glass, external light existing around the viewer (e.g., sunlight coming in through a window, indoor illumination light from a fluorescent lamp, etc.) enters the fluorescent surface, causing red, There was a problem in that the contrast of an image composed of green and blue light was significantly reduced.

このため、外光によるコントラストの低下を防ぐ目的で
、パネルガラスＫ　ＮｉＯおよびＣｏｏの微量を添加し
てガラスを中性灰色に着色し、ガラスの明度を下げるこ
と、あるいはこのようなガラス製のフィルターを併用す
ることが行われて来だが、この中性灰色ガラスは、赤、
緑および青の発光スペクトルを含む可視波長域の全体に
わたって、はぼ一様な透過率を示すため、コントラスト
向上の目的でこの灰色ガラスの透過率を低下させると、
赤、緑および青の螢光体から発せられる光も吸収されて
画像の輝度が低下するという欠点があった。For this reason, in order to prevent the contrast from decreasing due to external light, it is necessary to add small amounts of panel glass K NiO and Coo to color the glass a neutral gray color to lower the brightness of the glass, or to use filters made of such glass. This neutral gray glass has been used in combination with red,
Because it exhibits fairly uniform transmission across the entire visible wavelength range, including the green and blue emission spectra, reducing the transmission of this gray glass for the purpose of improving contrast results in
The drawback is that the light emitted from the red, green, and blue phosphors is also absorbed, reducing the brightness of the image.

まだ、別の試みとして、可視光波長において選択的な透
過−吸収の特性を具ｆｆ１ｉさせるだめにＮｄ２Ｏ３を
０．１〜５．０％含有させ、更にこのガラスの色調節の
だめにＣｒ２０３の若子量を添加した、謂ゆるＮｄ含有
ガラスをＣＲＴのノ（ネルガラスとして使用し、これに
より螢光体より発する赤。As another attempt, we added 0.1 to 5.0% Nd2O3 to achieve selective transmission-absorption characteristics at visible light wavelengths, and further added young molecular weight of Cr203 to adjust the color of this glass. So-called Nd-containing glass doped with Nd is used as flannel glass for CRTs, which emits red light from the phosphor.

緑、青の光を十分に透過し、それ以外の波長の光、とく
に黄色光を十分に吸収する特性を利用して、所要の色感
を有し、高コントラスト、高輝度の）Ｊラ−画像を得る
ことが提唱されている。Utilizing the property of sufficiently transmitting green and blue light and sufficiently absorbing light of other wavelengths, especially yellow light, it is possible to produce high-contrast, high-brightness) It is proposed to obtain images.

しかしながら、この場合は、Ｎｄの特性吸収である５７
０〜６１０　ｎｍについてのみ選択性を発揮するが、そ
の他の波長帯については波長選択性かないため十分な色
選択性がない。However, in this case, 57
It exhibits selectivity only for 0 to 610 nm, but has no wavelength selectivity for other wavelength bands, so it does not have sufficient color selectivity.

従って、この発明の目的は、Ｎｄ入りガラスをパネルガ
ラスとして使用した多色ＣＲＴＯ色選択性を向上するこ
とであり、高輝度・高コントラストのカラー・ディスプ
レーを提供することにある。この目的は、この発明によ
れば、（ａ）　　ネオジムを含有するパネルガラスを使
用したカラー・ＣＲＴ および （ｂ）　　前記のＣＲ，Ｔと観察者の間に位置し、透明
な熱可塑性樹脂よりなり、３８０〜４２０　ｎｒｎ　。Therefore, an object of the present invention is to improve the color selectivity of a multicolor CRTO using Nd-containing glass as a panel glass, and to provide a color display with high brightness and high contrast. This purpose, according to the present invention, consists of (a) a color CRT using panel glass containing neodymium; and (b) a color CRT located between the CR, T and the observer and made of a transparent thermoplastic resin. , 380-420 nrn.

４８０〜５３０ｎｍ、６４０〜７８０　ｎｍのうち少な
くとも一つの波長域に吸収を有し、かつ前記以外の波長
域の可視光線に対して吸収　　　・をほとんど有せず、
かつ全光線透過率が３０％以上であるフィルター よりなる色彩が鮮明なカラー・ディスプレーにより達成
される。It has absorption in at least one wavelength range from 480 to 530 nm and 640 to 780 nm, and has almost no absorption for visible light in wavelength ranges other than the above,
Moreover, a clear color display made of a filter with a total light transmittance of 30% or more is achieved.

この発明でいう（ａ）ネオジムを′含有するパネルガラ
スとは基礎ガラス成分の他ＫＮｄ２０３　を含むガラス
を総称する。このようなガラスの組成・製法については
例えば、特開昭５７−５０７５２号公報に記載されてい
る。In this invention, (a) panel glass containing neodymium is a general term for glass containing KNd203 in addition to the basic glass component. The composition and manufacturing method of such glass are described, for example, in Japanese Patent Application Laid-Open No. 57-50752.

この発明でいう（ｂｌのフィルターの基体樹脂として使
用される透明な熱可塑性樹脂としては、例えばアクリル
系樹脂、スチレン系樹脂、ポリカーボネ一ト、塩化ビニ
ル樹脂、ポリビニルブチラール、酢酸セルロース等があ
る。しかして、該基体樹脂に着色料等を含有させて得ら
れる光学樹脂拐料の全光線透過率は３０％以上であるこ
とが必要であり、好捷しくけ５０％以上である。Transparent thermoplastic resins used as the base resin of the filter (BL) referred to in this invention include, for example, acrylic resins, styrene resins, polycarbonate, vinyl chloride resins, polyvinyl butyral, and cellulose acetate. Therefore, it is necessary that the total light transmittance of the optical resin composition obtained by incorporating a colorant or the like into the base resin is 30% or more, and preferably 50% or more.

アクリル系樹脂としては、アルキル炭素数１〜４のアル
ギルメタクリレートの単独重合体ｉたは該アルキルメタ
クリレート５０モル％以上と他の共重合性単量体との共
重合体がある。このようなアルキルメタクリレートとし
ては、メチルメタクリレート、エチルメタクリレート、
ｎ−プロピルメタクリレ−１・、イングロビルメタノリ
レート、ｎ−ブチルメタクリレート、　５ｅｔ−ブチル
メタクリレート、ｔｅｒｔ−ブチルメタクリレートなど
があるが、メチルメタクリレートが特に好まし込。Examples of the acrylic resin include a homopolymer of argyl methacrylate having 1 to 4 alkyl carbon atoms, or a copolymer of 50 mol% or more of the alkyl methacrylate and another copolymerizable monomer. Such alkyl methacrylates include methyl methacrylate, ethyl methacrylate,
Examples include n-propyl methacrylate-1, inglovir methanolylate, n-butyl methacrylate, 5et-butyl methacrylate, tert-butyl methacrylate, and methyl methacrylate is particularly preferred.

共重合性単量体としては、これを使用して得られる共重
合体の透明性を損わないものであれば使用できる。Any copolymerizable monomer can be used as long as it does not impair the transparency of the copolymer obtained using it.

スチレン系樹脂としては、スチレンまたはその置換体の
単独重合体または該スチレン化合物５０モル％以上と他
の共重合性単量体との共重合体がある。このようなスチ
レン化合物としてハ、スチレン、α−メチルスチレン、
α−クロロスチレン、ビニルトルエン等がある。他の共
重合性単量体としては、前記アクリル系樹脂において使
用される共重合性単量体がある。Examples of the styrene resin include a homopolymer of styrene or a substituted product thereof, or a copolymer of 50 mol% or more of the styrene compound and another copolymerizable monomer. Such styrene compounds include styrene, α-methylstyrene,
Examples include α-chlorostyrene and vinyltoluene. Other copolymerizable monomers include copolymerizable monomers used in the acrylic resin.

塩化ビニル系樹脂としては、塩化ビニルの単独重合体ま
たは該塩化ビニル５０％以上とその他の共重合性単量体
上の共重合体がある。他の共重合性単量体としては、前
記アクリル系樹脂において使用される共重合性単量体が
ある。Examples of vinyl chloride resins include homopolymers of vinyl chloride and copolymers of 50% or more of vinyl chloride and other copolymerizable monomers. Other copolymerizable monomers include copolymerizable monomers used in the acrylic resin.

ポリカーボネート１１１１旨としては、例えば４，４′
−イソプロピリデンジフエノールポリカーボネートのよ
うなビスフェノール型ポリカーボネートの他に、米国特
許第３，３０５，５２０号およびクリストファー・フォ
ックス共著「ポリカーボネート」第１６１〜１７６頁（
１９６２年発行）に記載されている他のポリカーボネー
ト類、ジエチレングリコールビスアリルカーボネート等
が挙げられる。As polycarbonate 1111, for example, 4,4'
- In addition to bisphenol-type polycarbonates such as isopropylidene diphenol polycarbonate, U.S. Pat.
(published in 1962), diethylene glycol bisallyl carbonate, and the like.

前記透明性熱可塑性樹脂のうち、好１しくけアクリル系
樹脂、スチレン系樹脂、塩化ビニル不側５旨およびポリ
カーボネートであり、もつとも好１しくけアクリル系樹
脂およびスチレン系樹１指である。Among the transparent thermoplastic resins, preferred are acrylic resin, styrene resin, vinyl chloride resin, and polycarbonate, and most preferred are acrylic resin and styrene resin.

さらに、この発明による（ｂ）のフィルターにおいては
、前記透明性熱可塑性樹脂に対して、０．０００１〜０
．５重量％、好ましくは０．０００３〜０．１重量％の
３８０−４２０　ｎｍ、４８０−５３０ｎｍ、５６０〜
６１０　ｎｍおよび６４０〜７８０ｎｍのうち少なくと
も一つの波長域に吸収を有し、前記以外の波長域の可視
光線に対しては吸収をほとんどまたは全く有しない着色
料を配合して選択的吸収を行なわせる。このような作用
を有する着色料としては、例えば、つぎに記すような染
料、顔料または紫外線吸収剤があり、これらは単量体ま
だはプレポリマーに混合されて重合されるか、あるいは
基体樹脂に配合される。Furthermore, in the filter (b) according to the present invention, the amount of the transparent thermoplastic resin is 0.0001 to 0.
．． 380-420 nm, 480-530 nm, 560-5% by weight, preferably 0.0003-0.1% by weight
Selective absorption is achieved by blending a coloring agent that has absorption in at least one wavelength range of 610 nm and 640 to 780 nm and has little or no absorption for visible light in wavelength ranges other than the above. . Examples of coloring agents that have such an effect include dyes, pigments, and ultraviolet absorbers as described below. It is blended.

３８０〜４２０　ｎｒｎの波長域に対して主たる吸収を
有する着色料としては、サリチル酸フェニル、サルチル
酸パラーｔｅｒｔ−ブチルフェニル等のサリチル酸エス
テル類、２−（２’−ヒドロキシ−５′−メチルフェニ
ル）ヘンシトリアゾール、２−　（２’−ヒドロキン−
３７、５７−ジーｔｅｒｔ−ブチルフェニル）−５−ク
ロロベンゾトリアゾール等のベンゾトリアゾール類、２
−ヒドロキシ−４−メトキシベンゾフェノン、２−ヒド
ロキシ−４−メトキシ−４′−クロロベンゾフェノン、
２．２′−ジヒドロキシ−４−オクトキシベンゾフェノ
ン等のベンゾフェノン類等の紫外線吸収剤がある。Coloring agents that have a main absorption in the wavelength range of 380 to 420 nrn include salicylic acid esters such as phenyl salicylate and para-tert-butylphenyl salicylate, and 2-(2'-hydroxy-5'-methylphenyl)hensilicylate. triazole, 2-(2'-hydroquine-
Benzotriazoles such as 37,57-di-tert-butylphenyl)-5-chlorobenzotriazole, 2
-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-methoxy-4'-chlorobenzophenone,
There are ultraviolet absorbers such as benzophenones such as 2.2'-dihydroxy-4-octoxybenzophenone.

４８０〜５３０　ｎｍの波長域に対して主たる吸収を有
する着色料としては、ホスタゾール・レッドＧＧ（ヘキ
ス１社’ＪＲ）、パリオゲン・レッド３７３０（ＢＡＳ
Ｆ社製）、ダイヤレジン・レッドＨＳ　（三菱化成工業
株式会社製）、ダイヤレジン・レッドＳ（三菱化成工業
株式会社製）、アマゲラスト・ピンクＰ４Ｂ（アメリカ
ン・アニリン社製）、オレンジＣ−タイプ（バーキュレ
ス社製）等の赤色系色素がある。Examples of colorants that have main absorption in the wavelength range of 480 to 530 nm include Hostazol Red GG (Hex 1 Company's JR) and Paliogen Red 3730 (BAS
F Company), Diamond Resin Red HS (Mitsubishi Chemical Industries, Ltd.), Diamond Resin Red S (Mitsubishi Chemical Industries, Ltd.), Amagelast Pink P4B (American Aniline Company), Orange C-Type ( There are red pigments such as Vercules (manufactured by Vercules).

６４０〜７８０　ｎｒｎの波長域において主たる吸収を
有する着色料としては、ユウビニル・プルーフ０２（Ｉ
３ＡＳＦ社製）、オイル・ブルー６１５（オリエント化
学工業株式会社製）、マクロレックス、・グリーン５１
３（バイエル社製）、セイカゲン・オ・ブルーＧＫ−１
２００（’大日精化工業株式会社製）、スミトンシアニ
ン・ブルーＨ１３−１（住友化学工業株式会社製）等の
青色系色素がある。As a colorant having main absorption in the wavelength range of 640 to 780 nrn, Euvinyl Proof 02 (I
3ASF), Oil Blue 615 (Orient Chemical Industry Co., Ltd.), Macrolex, Green 51
3 (manufactured by Bayer), Seikagen O Blue GK-1
There are blue pigments such as 200 (manufactured by Dainichiseika Chemical Industries, Ltd.) and Sumitonsyanine Blue H13-1 (manufactured by Sumitomo Chemical Industries, Ltd.).

５６０〜６１０　ｎｍの波長域に主たる吸収を有する着
色料としては、適切なものはないが、上記の３波長域に
主たる吸収を有する着色料のうち、５６０〜６１０　ｎ
ｍの波長域にも吸収を有するものが好ましく使用される
。このような着色料には、例えばユウビニル・ブルーフ
０２（ＢＡＳＦ社製）がある。There is no suitable colorant that has a main absorption in the wavelength range of 560 to 610 nm, but among the colorants that have a main absorption in the above three wavelength ranges, 560 to 610 nm is suitable.
Those having absorption also in the wavelength range of m are preferably used. Such colorants include, for example, Euvinyl Bruch 02 (manufactured by BASF).

以上述べたようにこの発明によれば外光の存在下でも画
像の高コントラストと高輝度がともに得られ、しかも安
価であるという利点がある。As described above, the present invention has the advantage that both high contrast and high brightness of images can be obtained even in the presence of external light, and it is inexpensive.

フィルターの基体が熱可塑性樹脂であるので、可視光の
種々の波長域で吸収能を有する着色料を任意に添加する
ことができるという利点があり、特Ｋ　３８０〜４２０
　ｎｒｎ　、４８０−５３０ｎｍ、５６０〜６１０　ｎ
ｍおよび６４０〜７８０ｎｍのうち少なくも一つの波長
域に吸収を有しかつ前記以外の波長域の可視光線に対し
て吸収をほとんど有しない着色料を１種以上含有させる
ことにより赤、緑および青の三原色の螢光体の発光スペ
クｉ・ルのうち、最大強度の波長の光を選択的に透過さ
せ、捷だスペクトル中のその他の波長の光を選択的に吸
収して、上記の効果をさらに高めるとともに色純度を改
善して色再現性を向」ニさせることができる。Since the base of the filter is a thermoplastic resin, it has the advantage of being able to optionally add colorants that have the ability to absorb visible light in various wavelength ranges.
nrn, 480-530nm, 560-610n
red, green, and blue by containing one or more colorants that have absorption in at least one wavelength range of m and 640 to 780 nm and have almost no absorption of visible light in wavelength ranges other than the above. The above effect is achieved by selectively transmitting the light of the wavelength of maximum intensity among the emission spectra of the three primary colors of the phosphor and selectively absorbing the light of other wavelengths in the narrow spectrum. It is possible to further increase color purity and improve color reproducibility.

実施例１ ホスタゾール・レッドＧＧ（ヘキスト社製）０．０００
５，９．オイル・ブルー６１５（オリエント化学工業株
式会社製）ｏ、ｏｏｏｓｇ、および２−（２７−ヒトロ
ギンー３’　、　５’−ジーｔｃｒｔ−ブチルフェニル
）−５−クロロベンゾトリアゾール０．０４　、！７を
、メチルメタクリレートｓａｇおよびメタクリル酸２０
９の混合液に溶解し、２．２′−アゾビスイソブチロニ
トリル０．００５　、！９を重合開始剤として添加ＷＥ
　ｊＷしたのち、ガラス板と塩化ビニル樹脂製ガスケッ
トを用いて組んだセル中に注入した。減圧下に脱泡した
のち、７０°Ｃで８時間、ついで１２０°Ｃで１時間重
合してセルを解体し、厚さ３　ｍｍの樹脂板を得だ。こ
の樹脂板の、ＡＳＴＭ　Ｄ１００３　Ｋよる全光線透過
率は７５％で、４００　ｎｍ以下、５００ｎｍおよび６
７０　ｎｍ付近に吸収極大を有し、とれをネオジムを含
有するパネルガラスを使用したカラー・ＣＲＴの前面に
設置することにより、高コントラストで色彩の鮮明なカ
ラー画像を得ることができだ。Example 1 Hostazol Red GG (manufactured by Hoechst) 0.000
5,9. Oil Blue 615 (manufactured by Orient Chemical Industry Co., Ltd.) o, ooosg, and 2-(27-hytrogin-3', 5'-di-tcrt-butylphenyl)-5-chlorobenzotriazole 0.04,! 7, methyl methacrylate sag and methacrylic acid 20
9 and 2,2'-azobisisobutyronitrile 0.005,! 9 was added as a polymerization initiator WE
After heating, it was injected into a cell assembled using a glass plate and a vinyl chloride resin gasket. After defoaming under reduced pressure, polymerization was carried out at 70°C for 8 hours and then at 120°C for 1 hour to dismantle the cells and obtain a resin plate with a thickness of 3 mm. The total light transmittance of this resin plate according to ASTM D1003K is 75%, and it has a total light transmittance of 400 nm or less, 500 nm and 6
It has an absorption maximum around 70 nm, and by installing it in front of a color CRT using panel glass containing neodymium, it is possible to obtain color images with high contrast and clear colors.

実施例２ ダイヤレジン・レッドｒＩｓ　（三菱化成工業株式会社
製）ｏ、ｏｏｏｓｇ、オイル・ブルー６１５０．０Ｏ１
７，９および２−　（２’−ヒドロキシ−３′。Example 2 Diamond resin red rIs (manufactured by Mitsubishi Chemical Industries, Ltd.) o, ooosg, oil blue 6150.0O1
7,9 and 2-(2'-hydroxy-3'.

５′−ジーｔｅｒｔ−ブチルフェニル）−５−クロロベ
ンゾトリアゾールｏ、ｏ　ｓ　ｇを、メチルメタクリレ
ート５０．９およびスチレン５０！ｉの混合液に溶解し
、２，２′−アゾビスイソブチロニトリルｏ、ｏ　ｉ　
ｇを重合開始剤として添加して、実施例１と同様にして
重合を行ない、厚さ３７１１１＋の樹脂板を得た。この
樹脂板の全光線透過率は６６％で可視部の分光透過率曲
線は第２図（曲線Ａ）に示すとおりであった。これを、
第１図に示す分光透過率を有するネオジムを含有するパ
ネルガラスを使用したカラーＣＩｔ　Ｔと組合せて用い
ることにより、高コントラストおよび色純度の改善され
たノノラー画像が得られた。5'-tert-butylphenyl)-5-chlorobenzotriazole o,osg, methyl methacrylate 50.9 and styrene 50! Dissolve in the mixture of 2,2'-azobisisobutyronitrile o, o i
g was added as a polymerization initiator, polymerization was carried out in the same manner as in Example 1, and a resin plate with a thickness of 37111+ was obtained. The total light transmittance of this resin plate was 66%, and the spectral transmittance curve in the visible region was as shown in FIG. 2 (curve A). this,
When used in combination with a color CIt T using a neodymium-containing panel glass having the spectral transmittance shown in FIG. 1, a non-color image with high contrast and improved color purity was obtained.

実施例３ パリオゲン・レッド３７３０　（ＢＡ　Ｓ　Ｆ社製）０
．１ｇ、ユウビニル・プルーフ０２（１３ＡＳＦ社製）
　０．１．９および２−（２’−ヒドロキシ−３′。Example 3 Paliogen Red 3730 (manufactured by BASF) 0
．． 1g, Yuvinyl Proof 02 (manufactured by 13ASF)
0.1.9 and 2-(2'-hydroxy-3'.

５′−ジーｔｅｒｔ−ブチルフェニル）−５−クロロベ
ンゾトリアゾール０．７ｇを、アクリル樹脂ペレット（
「パラベットＧ」、協和ガス化学工業株式会社製）１０
００ｆｌと混合して、２１（１〜２２０℃の温度で射出
成形し、厚さ３話の樹脂板を得た。この樹脂板の全光線
透過率は６２％、可視部の分光透過率曲線は第２図（曲
線Ｂ）Ｋ示すとおりであり、４００ｎｍ以下、４９０ｎ
ｍ。0.7 g of 5'-di-tert-butylphenyl)-5-chlorobenzotriazole was added to acrylic resin pellets (
"Parabet G", manufactured by Kyowa Gas Chemical Industry Co., Ltd.) 10
00fl and injection molded at a temperature of 21 (1 to 220°C) to obtain a resin plate with a thickness of 3 stories.The total light transmittance of this resin plate was 62%, and the spectral transmittance curve in the visible region was As shown in Figure 2 (curve B) K, 400nm or less, 490n
m.

５２５　ｎｍ　、　６０５　ｎｍおよび６７０ｎｍ付近
に吸収極大を有する。これをネオジムを含有するパネル
ガラスを使用したカラ＝−ＣＲＴの前面フィルターとし
て設置し、高コントラストで色彩の鮮明なカラー画像が
得られた。It has absorption maxima around 525 nm, 605 nm and 670 nm. This was installed as a front filter of a color CRT using panel glass containing neodymium, and a color image with high contrast and clear colors was obtained.

【図面の簡単な説明】[Brief explanation of the drawing]

第１図は従来のＮｄ含有ガラスの光透過曲線であり、第
２図はこの発明のディスプレーのフィルターの光透過曲
線である。FIG. 1 is a light transmission curve of a conventional Nd-containing glass, and FIG. 2 is a light transmission curve of a display filter of the present invention.

Claims (1)

【特許請求の範囲】 １）（ａ）　　ネオジムを含有するパネルガラスを使用
したカラー・ＣＲＴ および （ｂ）　　前記のＣＲＴと観察者の間に位置し、透明な
熱可塑性樹脂よりなり、３８０〜４２０ｎｍ、、４８０
〜５３０　ｎｍおよび６４０〜７８０ｎｍのうち少なく
とも一つの波長域に吸収を有し、かつ前記以外の波長域
の可視光線に対して吸収をほとんど有せず、かつ全光線
透過率が３０％以上であるフィルターよりなる色彩が鮮
明なカラー・ディスプレー。 ２）フィルターを構成する透明な熱可塑性樹脂がアクリ
ル樹脂まだｄ、スチレン樹脂である特許請求の範囲第１
項に記載のカラー、ディスプレー。[Claims] 1) (a) A color CRT using panel glass containing neodymium; and (b) located between the CRT and the observer, made of a transparent thermoplastic resin, and having a wavelength of 380 to 420 nm. ,,480
It has absorption in at least one wavelength range from ~530 nm and 640 to 780 nm, has almost no absorption to visible light in wavelength ranges other than the above, and has a total light transmittance of 30% or more. Color display with clear colors created by filters. 2) Claim 1 in which the transparent thermoplastic resin constituting the filter is an acrylic resin or a styrene resin.
Colors and displays listed in section.