JPS5891125A - Production of rolling roll - Google Patents
Production of rolling rollInfo
- Publication number
- JPS5891125A JPS5891125A JP18919381A JP18919381A JPS5891125A JP S5891125 A JPS5891125 A JP S5891125A JP 18919381 A JP18919381 A JP 18919381A JP 18919381 A JP18919381 A JP 18919381A JP S5891125 A JPS5891125 A JP S5891125A
- Authority
- JP
- Japan
- Prior art keywords
- roll
- depth
- hardened layer
- rolling roll
- progressive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
本発明は、圧延ロールの製造法に係り、特に冷間圧延用
ワークロールに好適な鍛鋼ロールの製造法に関する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for manufacturing a rolling roll, and particularly to a method for manufacturing a forged steel roll suitable for a work roll for cold rolling.
冷間圧延用ワークロールの熱処理法として、低周波誘導
炉により漸進加熱後、漸進水焼入れし、次いでサブゼロ
処理する方法は知られている。たとえば、特開昭52−
7.4522号公報参照。As a heat treatment method for cold rolling work rolls, a method is known in which progressive heating is performed in a low frequency induction furnace, followed by gradual water quenching, followed by subzero treatment. For example, JP-A-52-
See Publication No. 7.4522.
かかる熱処理法は、焼入れ硬化層の深いロールを得るの
に好適であり、前述の公開公報ではショア硬さH890
以上を有する硬化層深さが22+m+に達す・るものが
得られている。Such a heat treatment method is suitable for obtaining a roll with a deep quench hardening layer, and the above-mentioned publication discloses a roll with a Shore hardness of H890.
A hardened layer having a depth of 22+m+ has been obtained.
本発明の目的は、前述の公開公報に記載されているもの
よりも更に大きい焼入れ硬化層深さを有するロールの製
造法を提供するにある。It is an object of the present invention to provide a method for manufacturing rolls having a greater depth of quench hardening than that described in the above-mentioned publications.
本発明は、マンガン0.7〜1.5重量係、クロム4〜
5重量%を含有するロール材に対して、前述の熱処理法
を施すものである。The present invention has a weight ratio of 0.7 to 1.5 for manganese and 4 to 1.5 for chromium.
The above heat treatment method is applied to a roll material containing 5% by weight.
前述の熱処理法によって得られる硬化層深さはロール材
の成分組成によって異なることがわかった。前述の熱処
理法の効果が最大限に発揮されるロール材は、マンガン
0.7〜1.5重量係とクロム4〜5重量%を含有する
ものであることを見出した。It was found that the depth of the hardened layer obtained by the above heat treatment method differs depending on the component composition of the roll material. It has been found that the roll material that exhibits the maximum effect of the heat treatment method described above contains 0.7 to 1.5% by weight of manganese and 4 to 5% by weight of chromium.
本発明によれば、−例としてショア硬さHa90以上を
有する硬化層深さが401mに達するものが得られる。According to the invention, it is possible to obtain, for example, a case having a hardness of Shore hardness Ha of 90 or more and a hardened layer depth of up to 401 m.
実施例
エレクトロスラグ再溶解によって製造した第1表に示す
化学成分を有するロール材に対して、低周波誘導炉に上
る漸進加熱、漸進水焼入れ及び・サブゼロ処理を施した
。ロール材は、マンガ/及びクロムを除いてほぼ同じ含
有量にした。。試料の寸法は600鳩φである。漸進加
熱の温度は950’C。EXAMPLE A roll material manufactured by electroslag remelting and having the chemical components shown in Table 1 was subjected to gradual heating in a low frequency induction furnace, gradual water quenching and sub-zero treatment. The roll materials had approximately the same content except manga/chromium. . The dimensions of the sample are 600 mm. The temperature of gradual heating is 950'C.
ロールの送り速度は35rm/minとしだ。サブゼロ
処理は一100℃とし冷媒に液体窒素を用いた。The feed speed of the roll was 35 rm/min. The sub-zero treatment was carried out at -100°C and liquid nitrogen was used as the refrigerant.
第1表
各試料のショア硬さH[190以上を有する焼入れ硬化
層深さは第2表の通りである。Table 1: The depth of the quenched hardened layer having Shore hardness H[190 or more of each sample is shown in Table 2.
マンガン量とHg90以上を有する焼入れ硬化層深さと
の関係を第1図に示し、同じくクロム量との関係を第2
図に示す。低周波誘導炉による漸進加熱、焼入れ及びサ
ブゼロ処理の効果は、マンガン量及びクロム量゛によっ
て著しい影響を受けることが明らかである。Figure 1 shows the relationship between the amount of manganese and the depth of the hardened layer with Hg90 or more, and the relationship with the amount of chromium is shown in Figure 2.
As shown in the figure. It is clear that the effectiveness of progressive heating, quenching and sub-zero treatment with a low frequency induction furnace is significantly influenced by the amount of manganese and the amount of chromium.
以上、本発明によれば焼入れ硬化層深さの著しく大きい
ロールを得ることができる。As described above, according to the present invention, it is possible to obtain a roll having a significantly large quench hardening layer depth.
晶警crystal police
Claims (1)
%を含有するロール材を低周波誘導炉により漸進加熱し
てから漸進焼入れし、次いでサブゼロ処理することを特
徴とする圧延ロールの製造法。1. A rolling roll characterized in that a roll material containing 0.7 to 1.5% by weight of manganese and 4 to 5% by weight of chromium is gradually heated in a low frequency induction furnace, then gradually quenched, and then subjected to sub-zero treatment. manufacturing method.