JPS58521Y2 - metallic gloss paper - Google Patents
metallic gloss paperInfo
- Publication number
- JPS58521Y2 JPS58521Y2 JP6707578U JP6707578U JPS58521Y2 JP S58521 Y2 JPS58521 Y2 JP S58521Y2 JP 6707578 U JP6707578 U JP 6707578U JP 6707578 U JP6707578 U JP 6707578U JP S58521 Y2 JPS58521 Y2 JP S58521Y2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- paper
- cured
- solvent
- resin layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
本考案は装飾用、印刷用とくにラベルに適する金属光沢
紙に関する。[Detailed Description of the Invention] The present invention relates to metallic glossy paper suitable for decoration, printing, and especially labels.
従来この種の金属化紙は基紙に接着剤層を介してアルミ
ニウム箔を貼合わせた、いわゆるアルミ箔紙が主流であ
ったが、最近は省資源の観点から上記アルミニウム箔(
厚さは通常7〜15μ)をアルミニウム真空蒸着層(厚
さは概七〇、025〜0.125μ)に代替えしようと
いう試みが進行中である。Traditionally, this type of metallized paper was mainly aluminum foil paper, in which aluminum foil was bonded to a base paper via an adhesive layer, but recently, from the perspective of resource conservation, aluminum foil (
Efforts are underway to replace the aluminum vacuum deposited layer (typically 7-15 microns thick) with a vacuum-deposited layer of aluminum (approximately 70,025-0.125 microns thick).
更にラベル用としては、主として適用されるピン類の回
収洗浄時に必要なアルカリ量が本来のラベル除去以外に
アルミニウム自身の溶解によって無制限に浪費されると
いう悩みがあり、この点からも前記アルミニウム箔をこ
れよりも遥かに負担の軽いアルミニウム真空蒸着層に置
換えたいという願望が強い。Furthermore, for labels, there is a problem that the amount of alkali required when collecting and cleaning pins, which is mainly applied, is wasted indefinitely by melting the aluminum itself in addition to the original label removal. There is a strong desire to replace this with an aluminum vacuum-deposited layer, which is a much lighter burden.
基紙にクレーなどの微粉末と接着剤を主剤とする塗被層
を設けて紙の凹凸および多孔性を被覆し、その上に金属
蒸気の受理接着性のよい耐熱性樹脂層を介してアルミニ
ウムを真空蒸着し、最後にその上に無色會たは有色のラ
ッカ一層を金属保護層として設けると、アルミ箔紙に優
るとも劣らぬ金属光沢を有する金属化紙が得られること
は公知である。A coating layer mainly composed of fine powder such as clay and adhesive is provided on the base paper to cover the unevenness and porosity of the paper, and then a heat-resistant resin layer that accepts metal vapor and has good adhesion is applied to the coating layer. It is known that metallized paper with a metallic luster comparable to that of aluminum foil paper can be obtained by vacuum evaporating lacquer and finally applying a layer of colorless or colored lacquer as a metal protective layer.
但しこれを更にラベルを適するものとするには、上記樹
脂層がピン類の回収洗浄時に常用される高温のアルカリ
液を容易に浸透させる必要がある一刀、ラベルがピン類
に貼られる際は専らアルカリで溶解した糊料たとえばカ
ゼイン糊が基紙の裏面全体に塗布されて自然乾燥にまか
せるため、上記樹脂層は低温のアルカリ液浸透を遮断し
て極めて薄いアルミニウム真空蒸着層の白化ないしは腐
蝕を防止する必要もある。However, in order to make the label even more suitable, the resin layer needs to be easily penetrated by the high-temperature alkaline solution commonly used when collecting and cleaning pins. Since a glue dissolved in alkali, such as casein glue, is applied to the entire back side of the base paper and left to dry naturally, the resin layer blocks the penetration of low-temperature alkaline liquid and prevents whitening or corrosion of the extremely thin vacuum-deposited aluminum layer. There is also a need to do so.
このような微妙な機能を具備し、かつ高度の金属真空蒸
着機能を有する樹脂層を介在させた金属化紙は未だ公知
ではない。A metallized paper that has such delicate functions and has a resin layer interposed therebetween that has a high level of metal vacuum deposition function is not yet known.
本考案は近年商品化され、用途開発の緒についた紫外線
硬化性の無溶剤型アクリル系樹脂塗料を適用すれば、以
上述べた要点のすべてを満足する金属化紙が得られるこ
とを発見し提案するものである。This invention has been commercialized in recent years, and it was proposed after discovering that by applying a UV-curable solvent-free acrylic resin paint, a metallized paper that satisfies all of the above-mentioned points can be obtained. It is something to do.
即ち本考案は図面において、基紙1の両面に微粉末と接
着剤を主剤とする塗被層2,2′を設けてなる一方の塗
被層2の上に紫外線で硬化させた無溶剤型アクリール系
樹脂層3、アルミニウム真空蒸着層4、紫外線で硬化さ
せた無色渣たは有色の無溶剤型アクリル系樹脂層3′を
順次形成せしめてなる金属光沢紙の構造を要旨とするが
、本考案の新規性は紫外線で硬化させた無溶剤型アクリ
ル系樹脂層3および3′の存在にある。That is, the present invention is shown in the drawings in which coated layers 2 and 2' mainly composed of fine powder and adhesive are provided on both sides of a base paper 1, and a solvent-free type coated layer 2 is cured with ultraviolet rays on one coated layer 2. The gist of this paper is the structure of a metallic glossy paper formed by sequentially forming an acrylic resin layer 3, an aluminum vacuum-deposited layer 4, and a colorless residue cured by ultraviolet rays or a colored solvent-free acrylic resin layer 3'. The novelty of the invention lies in the presence of solvent-free acrylic resin layers 3 and 3' cured by ultraviolet light.
紫外線硬化性の無溶剤型アクリル系樹脂塗料とは、官能
基を有するアクリル系の官能基を有するモノマー、オリ
ゴマーないし樹脂の混合物に紫外線用重合開始剤を添加
した、実質的に無溶剤の塗料であって、その塗被層はわ
ずか1〜5秒の紫外線照射によって硬化を完了するもの
である。UV-curable solvent-free acrylic resin paint is a substantially solvent-free paint that is made by adding a UV polymerization initiator to a mixture of acrylic monomers, oligomers, or resins that have functional groups. The coating layer can be completely cured by UV irradiation for only 1 to 5 seconds.
上記塗料は力任前の鋼板に防錆用仮保護層とし2て適用
され、加工後は高温のアルカリ液で脱脂と同時に洗い落
されるという用途例もあって、本考案には最適のもので
ある。The above-mentioned paint is applied as a temporary protective layer for rust prevention to a steel plate before being worked, and after processing, it is washed off at the same time as degreasing with a high-temperature alkaline solution, so it is the most suitable for this invention. It is.
本考案の実施例としては、上記塗料の一種である日本ペ
イント■製のユービコート・クリヤーを印刷用両面コー
ト紙の一方の塗被面(クレーなどの微粉末と接着剤が主
剤)にリバースロールコータ−で約4μの厚さに塗布後
、直ちに80W/cm高圧水銀灯の集光下を617L/
分の速度で紫外線照射して鏡面状に硬化した樹脂層を形
成後、予備乾燥および真空脱気を経てアルミニウムを真
空度10””Hgで真空蒸着して厚さ0.1μの蒸着層
を形成し、最後に無色筐たは金色に染色したユービコー
ト・クリヤーを再び前記条件で塗布、硬化してなる金属
光沢紙を得た。As an example of the present invention, Ubicoat Clear manufactured by Nippon Paint, which is a type of the above-mentioned paint, was coated on one coated surface of double-sided coated printing paper (mainly consisting of fine powder such as clay and adhesive) using a reverse roll coater. - After coating to a thickness of about 4μ, immediately apply 617L/cm under the focused light of an 80W/cm high-pressure mercury lamp.
After forming a mirror-hardened resin layer by irradiating with ultraviolet light at a rate of 10 minutes, pre-drying and vacuum degassing are performed, and then vacuum evaporating aluminum at a vacuum level of 10"Hg to form a 0.1μ thick deposited layer. Finally, a colorless case or gold-dyed Ubicoat clear was applied again under the above conditions and cured to obtain metallic gloss paper.
本考案の上記実施例による金属光沢紙は、適切な印刷を
施しラベル化して、各種アルカリで溶解したカゼイン糊
を裏面全体に塗布してガラス板に貼付けて自然乾燥した
カヘアルミニウム真空蒸着層の白化ないしは腐蝕は全く
認められず、更にこれを約70℃に加温した4%力性ソ
ーダ溶液に浸漬したところ、十数分間でラベルが容易に
剥離することを確認した。The metallic gloss paper according to the above embodiment of the present invention is labeled with appropriate printing, coated with casein glue dissolved in various alkalis on the entire back side, pasted on a glass plate, and air-dried to whiten the Kahe aluminum vacuum deposited layer. No corrosion was observed at all, and when this was immersed in a 4% strength soda solution heated to about 70°C, it was confirmed that the label was easily peeled off in about 10 minutes.
なお、本考案は上記実施例にのみ限定されるものではな
い。Note that the present invention is not limited to the above embodiments.
図面は本考案による金属光沢紙の要部断面図である。
1・・・・・・基紙、2,2′・・・・・・微粉末と接
着剤を主剤とする塗被層、3・・・・・・紫外線で硬化
させた無溶剤型アクリル系樹脂層、4・・・・・・アル
ミ−j’4d着層、3′・・・・・・紫外線で硬化させ
た無色lたは有色の無溶剤型アクリル系樹脂層。The drawing is a sectional view of the main part of the metallic glossy paper according to the present invention. 1...Base paper, 2,2'...Coating layer containing fine powder and adhesive as main ingredients, 3...Solvent-free acrylic system cured with ultraviolet rays Resin layer, 4...aluminum-j'4d adhesion layer, 3'...colorless or colored solvent-free acrylic resin layer cured by ultraviolet rays.
Claims (1)
2′を設けてなる一方の塗被層2の上に、紫外線で硬化
させた無溶剤型アクリル系樹脂層3、アルミニウム真空
蒸着層4、紫外線で硬化させた無色または有色の無溶剤
型アクリル系樹脂層3′を順次形成せしめてなる金属光
沢紙。On both sides of the base paper 1, a coating layer 2 whose main ingredients are fine powder and adhesive,
2', a solvent-free acrylic resin layer 3 cured by ultraviolet rays, an aluminum vacuum-deposited layer 4, and a colorless or colored solvent-free acrylic resin layer 4 cured by ultraviolet rays. A metallic glossy paper formed by sequentially forming resin layers 3'.