JPS58222175A - Application of solventless adhesive - Google Patents

Abstract

PURPOSE:To apply a solventless adhesive with a high reaction rate continuously over a long period, by feeding the adhesive under a specified condition for transfer printing. CONSTITUTION:Width controlling dams 21 which determine the width of application are provdied on both sides of and contact with No.1 roll 1 and No.2 roll 2 and a border plate 22 is set on the No.1 roll side in order to form an adhesive bank 19. An adhesive mixed in a mixer to the viscosity of 10,000-50,000 CPS at 20-35 deg.C is fed to the bank 19 through a hose 23 from a nozzle 20 affixed to a nozzle support 24 equipped with a wheel 26 which is moved on a roll 25 by a drive 27. The adhesive applied to the roll 1 is heated to 50-70 deg.C on No.3 roll 3 for reduction of the viscosity to 500-20,000 CPS and is transfer printed onto a web 5 supplied on No.4 roll 4.

Description

【発明の詳細な説明】 本発明は無溶剤型接着剤の塗膜［方法に関するもので、
特に反応速度の速い１液又は２液型の無溶剤接着剤をプ
ラスチックフィルム、紙、アルミ箔、又はこれらのラミ
ネートウェッブ等のウェッブに塗工する際に、（１）０
．２〜５ｇ／ｍ′の簿い無溶剤接着剤塗膜をウェッブの
巾方向及び流れ方向ともに均一に塗工しＸ（２）無溶剤
接着剤塗膜にオレンジピール、ブッ、スプリットマーク
等が発生しないようにして、透明度、透視度等の外観の
良い塗膜を得、（３）０２〜５　ｇ／　ｍ”、の薄い無
溶剤接着剤塗膜を１００〜６００ｍ／ｍｉｎの高速で塗
工し、（４）ポットライフ（硬化反応により初期粘度に
対し約１割粘度が上昇するまでの時間）が１０〜６０分
以下の反応速度が速い無溶剤接着剤を長時間連続して塗
工することを可能とした塗工方法を提供しようとするも
のである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for coating a solvent-free adhesive;
In particular, when applying a one-component or two-component solvent-free adhesive with a fast reaction rate to a web such as a plastic film, paper, aluminum foil, or a laminate web of these, (1) 0
．． Apply a thin solvent-free adhesive coating of 2 to 5 g/m' uniformly in both the width direction and flow direction of the web. (3) Apply a thin solvent-free adhesive coating of 02 to 5 g/m" at a high speed of 100 to 600 m/min. (4) Continuously applying a solvent-free adhesive with a fast reaction rate and a pot life (time taken for the viscosity to increase by about 10% of the initial viscosity due to curing reaction) of 10 to 60 minutes or less. The aim is to provide a coating method that makes it possible to

第１図、第２図は従来の反応速僚の遅いポットライフが
２時間以上の無溶剤接着剤の塗工装置の例を示すもので
ある。第１図に於て、８はコーティング部を示し７．１
番ロール１．２番ロール２．６番ロール３．４番ロール
４の４本のコーティングロールからなり、フィルムスブ
リット原理により接着剤を０２〜５ｇ／ｍの簿膜にして
第１ウエツブ５に転写する。FIGS. 1 and 2 show an example of a conventional coating apparatus for a solvent-free adhesive having a slow reaction rate and a pot life of 2 hours or more. In Fig. 1, 8 indicates the coating part 7.1
Consisting of four coating rolls: No. roll 1, No. 2 roll 2, No. 6 roll 3, and No. 4 roll 4, the adhesive is applied to the first web 5 using the film splint principle to form a film of 0.2 to 5 g/m. Transcribe.

１６は接着剤供給部で、タンク１４．１４、ポンプ１３
．１６、ホース１２．１２によって２構成分のそれぞれ
を圧送し、ミキサー１１によって混合し、ノズル１０か
ら１番ロール１と２番ロール２の間に供給する。１５は
サイドダムで、ロール１．２の両端部から接着剤が洩れ
るのを防いでいる。９はラミネート部で、接着剤を転写
された第１ウエツブ５と第２ウエツブ６とを圧着してラ
ミネートウェッブ７を形成する。16 is an adhesive supply unit, which includes a tank 14, 14, and a pump 13.
．． 16. Each of the two components is pumped by a hose 12.12, mixed by a mixer 11, and fed from a nozzle 10 between the No. 1 roll 1 and the No. 2 roll 2. A side dam 15 prevents the adhesive from leaking from both ends of the roll 1.2. Reference numeral 9 denotes a laminate section, which presses the first web 5 and second web 6 onto which the adhesive has been transferred to form a laminate web 7.

第２図は前記コーティング部８のロール［１コ方向の状
態を示すもので、ミキサ１．−ｙ％、、、　１１によっ
て混合された２液接着剤はノズル１０から１番ロール１
と２番ロール２の間にロール巾方向の全白に亘つて均等
に供給される。３番ロールろは塗工量に合せて屑糸しさ
れている。FIG. 2 shows the state of the coating section 8 in the direction of the roll [1]. The two-component adhesive mixed by -y%,..., 11 is transferred from nozzle 10 to roll 1
and No. 2 roll 2 evenly across the entire width of the roll. The No. 3 roll is lined with scraps according to the coating amount.

前記１番ロール１と２番ロール２の塗工量内部１８にあ
る接着剤は順次３番ロール乙に転写され、次に第１ウエ
ツブ５に転写されて消費されていく。The adhesive in the coating amount inside 18 of the first roll 1 and the second roll 2 is sequentially transferred to the third roll B, and then transferred to the first web 5 and consumed.

しかし塗工［１］外部１７にある接着剤は高粘度である
こと、又２番ロール２の周速がウェッブ速度の約１／１
ｏ、１番ロールの周速は約１／１００と低速のため、塗
工量内部１８と塗工量外部１７の間で接着剤はほとんど
横流れが生じないため、置換しにくく、この作用は接着
剤の粘度が高くなる程顕著となる。However, the adhesive on the outside 17 of coating [1] has a high viscosity, and the peripheral speed of the second roll 2 is approximately 1/1 of the web speed.
o. Since the circumferential speed of the No. 1 roll is as low as approximately 1/100, there is almost no lateral flow of adhesive between the coating amount inside 18 and the coating amount outside 17, making it difficult to replace the adhesive. The higher the viscosity of the agent, the more pronounced this becomes.

このためポットライフの短い接着剤を塗工する場合、運
転中に塗工量外部１７から接着剤が増粘し、塗工量のば
らつき、第１ウエツブの張力増加、ゲル化による塗工面
の外観不良等の不具合が発生する。さらに接着剤が部分
的にでも硬化すると、ロールを損傷するという重大な障
害が発生する。Therefore, when applying an adhesive with a short pot life, the viscosity of the adhesive increases from the outside 17 of the applied amount during operation, causing variations in the applied amount, increased tension in the first web, and appearance of the coated surface due to gelation. Problems such as defects occur. Furthermore, if the adhesive is even partially cured, a serious problem arises that can damage the roll.

さらにポットライフが短くかつ粘度が高い接着剤は急激
に増粘するため、塗工不可能となる等の不具合を免れな
い。Furthermore, adhesives with short pot lives and high viscosity rapidly thicken, resulting in problems such as inability to coat.

斜上の経緯により、第６図と第４図は本出願人が先に発
明したポットライフの短い接着剤を塗工できるようにし
た装置である。6 and 4 show an apparatus capable of applying an adhesive with a short pot life, which was previously invented by the present applicant.

さて、第６図と第４図において、１番ロール１と２番ロ
ール２に接して塗工量を決定する巾決め゛ダム２１を両
側に配設し、１番ロール１側に中板２２を配置し、第５
図の如く接着剤バンク１９を形成できるように構成して
おり、ミキサー１１で混合された接着剤は、供給ホース
２３→供給ノズル２０→接着剤バンク１９の経路で送ら
れる。Now, in FIGS. 6 and 4, width-determining dams 21 are provided on both sides of the first roll 1 and second roll 2 to determine the coating amount, and an intermediate plate 22 is placed on the first roll 1 side. Place the fifth
As shown in the figure, the adhesive is configured to form an adhesive bank 19, and the adhesive mixed in the mixer 11 is sent along the route of supply hose 23→supply nozzle 20→adhesive bank 19.

前記ノズル２０はその先端が接着剤バンク１９中にした
る状態に配置すると共に、車輪２６を有するノズル支持
体２４に固定され、ノズル支持体２４とともにレール２
５上をロール巾方向に駆動される。The nozzle 20 is arranged with its tip dripping into the adhesive bank 19, and is fixed to a nozzle support 24 having wheels 26, and is attached to the rail 2 together with the nozzle support 24.
5 in the roll width direction.

ノズル駆動部２７はノズル２０、ノズル支持体２４をロ
ール巾方向に駆動するもので、ノズル２０を両側の巾決
めダム２１間で往復駆動する。The nozzle drive unit 27 drives the nozzle 20 and the nozzle support 24 in the roll width direction, and drives the nozzle 20 back and forth between the width determining dams 21 on both sides.

さて、上記の装置を用いてもポットライフの短い、特に
粘度の高い接着剤の良好な塗工がむずかしいため、 １）粘度の高い接着剤あるいは増粘した接着剤を６番ロ
ールから第１ウエツブに転写すると、第５図の如く接着
剤２９がスプリット点３０できれいに分割されず、その
結果塗工面に荒れが発生する（第６図）。転写が悪いと
第６図の如くスプリット点３１が荒れ、スプリットマー
クといわれるブップッが発生し、その結果塗工面があれ
る。Now, even if the above-mentioned device is used, it is difficult to properly apply adhesives with short pot lives, especially those with high viscosity. 5, the adhesive 29 is not divided neatly at the split point 30 as shown in FIG. 5, and as a result, the coated surface becomes rough (FIG. 6). If the transfer is poor, the split point 31 becomes rough as shown in FIG. 6, causing a bump called a split mark, and as a result, the coated surface becomes rough.

２）第７図のｔｔｎ＜、１番ロール１から第１ウエツブ
５に転写されるまでの間に、１番ロール１はもつとも周
速が遅く、かつロール−ｆ＝の接着剤の厚みが厚いが、
これが順次周速が大となり、接着剤の厚さは薄くなる。2) In Fig. 7, ttn<, during the period from the first roll 1 to the first web 5, the circumferential speed of the first roll 1 is slow, and the adhesive on the roll -f= is thick. but,
As the circumferential speed increases, the thickness of the adhesive decreases.

このため、スプリット点６０から１番ロールへと、遠く
なるに従って接着剤は滞留し、増粘しやすい状態となる
。ポットライフの短い接着剤、特に２液型接着剤はその
粘度が時間に対して指数関数的に増加し・、温度が高い
程この傾向は強くなる等の不具合があった。Therefore, as the distance from the split point 60 to the first roll increases, the adhesive tends to stagnate and thicken. Adhesives with a short pot life, especially two-component adhesives, have the disadvantage that their viscosity increases exponentially with time, and this tendency becomes stronger as the temperature increases.

本発明者は種々の接着剤を色々な条件下で実験した結果
、」−記の原因とこれに対する解決策をみ出だした。即
ち、１）接着剤の粘度は低温で高く高温で低い。２）ポ
ットライフは温度の低い程長い。As a result of experimenting with various adhesives under various conditions, the inventor of the present invention discovered the cause of the problem and a solution to the problem. That is, 1) the viscosity of the adhesive is high at low temperatures and low at high temperatures. 2) The lower the temperature, the longer the pot life.

３）粘度が低い程転写は良好である。3) The lower the viscosity, the better the transfer.

以上のような接着剤固有の特性を利用して、次のような
供給、転写を行えばよい。１）１番ロールに常温近辺の
高粘度で供給する。２）転写は温度を高くし、低粘度で
転写する。The following supply and transfer may be performed by utilizing the unique characteristics of the adhesive as described above. 1) Feed to the No. 1 roll at a high viscosity around room temperature. 2) Transfer is performed at high temperature and with low viscosity.

第８図は上記の解決策に基く接着剤の供給と転写に最も
適した温度・粘度領域を示すもので、供給領域Ａは温度
２０〜３０°Ｃ１粘度１０，０００〜５０，０ＯＯＯＰ
Ｓであり、転写領域Ｂは温度５０〜７０°Ｃ５粘度５０
０〜２．００００ＰＳである。夫々の領域を通過する粘
度特性Ｃを備えた接着剤を用いて塗工すれば、２液性接
着剤による塗工が具合よく行われる。Figure 8 shows the most suitable temperature and viscosity range for adhesive supply and transfer based on the above solution. Supply range A is temperature 20-30°C, viscosity 10,000-50,000°C.
S, and the transfer area B has a temperature of 50 to 70°C, a viscosity of 50
It is 0 to 2.0000PS. If an adhesive having a viscosity characteristic C that passes through each region is used for coating, coating with a two-component adhesive can be performed satisfactorily.

また、接着剤にこのような温度勾配を付与する手段は公
知の方法で可能である。たとえばジャケット構造のロー
ルに温水を通すか、あるいはロール外部から赤外線を以
て加熱する方法でよい。又ロールごとに夫々温度制御す
ることも公知の方法でこれ又可能である。Furthermore, means for imparting such a temperature gradient to the adhesive can be achieved using known methods. For example, hot water may be passed through a jacketed roll, or heating may be performed from outside the roll using infrared rays. It is also possible to control the temperature of each roll individually using known methods.

以上の通り、本発明によれば１番ロールに高粘度の接着
剤を供給し、転写部は高温にして低温度で行うから、 １）滞留し易い１番ロールに常温近辺の２０〜３００Ｃ
で粘度１０，０００〜５０，０００　ＣｊＩＰＢ：で供
給するので、硬化反応が遅く、ポットライフが長いので
高粘度でも増粘し離い。As described above, according to the present invention, a high viscosity adhesive is supplied to the No. 1 roll, and the transfer part is kept at a high temperature and the adhesive is kept at a low temperature.
Since it is supplied with a viscosity of 10,000 to 50,000 CjIPB, the curing reaction is slow and the pot life is long, so even at high viscosity it does not thicken and separate.

２）転写部は低粘度のため、接着剤はスプリット点で清
いに分割され塗工面が荒れない。しかも湿度は５０〜７
０°Ｃと高く、ポットライフが短い状態であるが、６番
ロール上の接着剤は十分に薄く、がつウェッブ速度と同
速で転写されるので、ポットライフが短い状態は塗工に
障害を起さない。従ってポットライフの短い接着剤は一
般に接着性能が高く、硬化反応も早いため、付加価値の
高いラミネート製品を得ることができると共に生産性も
高くなる等の効果を有する。2) Since the transfer part has a low viscosity, the adhesive is divided neatly at the split point and the coated surface is not rough. And the humidity is 50-7
Although the temperature is high at 0°C and the pot life is short, the adhesive on the No. 6 roll is sufficiently thin and is transferred at the same speed as the web speed, so a short pot life will hinder the coating. Does not cause Therefore, adhesives with a short pot life generally have high adhesive performance and a fast curing reaction, so that they have effects such as being able to obtain laminate products with high added value and increasing productivity.

【図面の簡単な説明】[Brief explanation of the drawing]

第１図は反応速度が遅く、ポットライフの長い無溶剤接
着剤の塗工装置。 第２図は第１図のコーティング部のロール巾方向からみ
た詳細 第３図はポットライフの短い接着剤の供給装置。 第４図は第６図における供給部のロール巾方向からみだ
図。 第５図と第６図は高粘度の接着剤あるいは増粘した接着
剤を転写した場合の状態を示し、第５図は良好な転写、
第６図は不良転写状態を示す。 第７図は１番ロールから６番ロールにいたる接着剤厚み
の変化を示す。 第８図は本発明の供給領域と転写領域を示す図。 図において； １１番ロール　　　　２２番ロール ３６番ロール　　　　４４番ロール ５　第１ウエツブ　　　　６　第２ウエツブ７　　ラミ
ネートウェッブ　　　８　　コーティング部９　ラミネ
ート部　　　　１０．ノズル１′１：５ １１　　ミキサー　　　　　１２．１２　　ホース１３
．１５　　ポンプ　　　　　１４．１４　タンク１５　
　サイドダム　　　　　１６　　接着剤供給部１７　　
塗工中外部　　　　　１８　　塗工中内部１９　　接着
剤バンク　　　　　２０　　供給ノズル２１　　巾決め
ダム　　　　　２２　　巾　板２３　　供給ホース　　
　　　２４　　ノズル支持体２５　　レール　　　　　
　　２６　　車　輪２７　　ノズル駆動部　　　　　２
９　　接着剤６０　　　スプリット点３１　　　荒れた
スプリット点Ａ　供給領域　　　　　　Ｂ　転写領域Ｃ
粘度特性曲線 以　　上 出願人　住友重機械工業株式会社 復代理人　弁理士人　橋　　　勇 第１図 ６ 第２図 ） 第３図 第４図 Ｎ７図 第８図 ；ｌＬ反°ＣFigure 1 shows a coating device for a solvent-free adhesive with a slow reaction rate and long pot life. Fig. 2 shows a detailed view of the coating section shown in Fig. 1 from the roll width direction. Fig. 3 shows a supply device for an adhesive with a short pot life. FIG. 4 is a view of the supply section in FIG. 6 viewed from the roll width direction. Figures 5 and 6 show the state when high viscosity adhesive or thickened adhesive is transferred, and Figure 5 shows good transfer,
FIG. 6 shows a defective transfer state. FIG. 7 shows the change in adhesive thickness from the first roll to the sixth roll. FIG. 8 is a diagram showing the supply area and transfer area of the present invention. In the figure: Roll No. 11 Roll No. 22 Roll No. 36 Roll No. 44 5 First web 6 Second web 7 Laminated web 8 Coating section 9 Laminating section 10. Nozzle 1'1:5 11 Mixer 12.12 Hose 13
．． 15 Pump 14.14 Tank 15
Side dam 16 Adhesive supply section 17
Outside during coating 18 Inside during coating 19 Adhesive bank 20 Supply nozzle 21 Width determining dam 22 Width plate 23 Supply hose
24 Nozzle support 25 Rail
26 Wheel 27 Nozzle drive unit 2
9 Adhesive 60 Split point 31 Rough split point A Supply area B Transfer area C
Above viscosity characteristic curve Applicant: Sumitomo Heavy Industries, Ltd. Sub-Agent, Patent Attorney Isamu Hashi (Fig. 1 6 Fig. 2) Fig. 3 Fig. 4 Fig. N7 Fig. 8;

Claims (1)

【特許請求の範囲】[Claims] 温度２０〜６０°０１粘度１０，０００交０．０ＯＯＯ
ＰＳの領域で接着剤を供給し、温度５０〜７０°０１粘
度５００〜２、　ｏｏｏｃｐｓの領域で転写することを
特徴とする無溶剤型接着剤の塗工方法。Temperature 20~60°01 Viscosity 10,000 AC 0.0OOOO
A method for applying a solvent-free adhesive, characterized in that the adhesive is supplied in a PS range, and transferred in a temperature range of 50 to 70 degrees, a viscosity of 500 to 2, and ooocps.