JPS5817830A - Production of novel auqeous dispersion of higher alcohol - Google Patents

Abstract

PURPOSE:To produce an aqueous dispersion of higher alcohol of superior properties used for various applications by mixing and dispersing a specific amt. of formalin with and into the water dispersion obtd. by adding water to a surfactant or dispersant, fats or oils, and higher alcohol. CONSTITUTION:Vegetable fat or oil such as soybean oil is added at 0.01- 0.15pts.wt. ratio to 0.6-3pts.wt. a surfactant such as anionic polyalkyl aryl sulfonate or a dispersant as a naphthalene sulfonic acid type high condensate ion product, and both are mixed and agitated. Higher alcohol such as lauryl alcohol is added at 0.1-3wt% to the fat or oil, and both are mixed; further clean water is added at 2-6pts.wt. thereto and is dispersed therein, whereby the aqueous dispersion is prepd. After the liquid is left standing for >=24hr, about 37% formalin is added at 1-10wt% to the fat or oil, and is mixed and dispersed. The higher alcohol aqueous dispersion having performance useful as a compounding additive for cement, waterproofing agent, non-shrinking agent, floor material, tile cement, etc. is obtained.

Description

【発明の詳細な説明】 この発明はセメント用配合剤、防水剤、無収縮剤、末剤
、タイル貼着剤、グラウト用無収縮剤等として有用な性
能を有する高級アルコール系水性分散液の製造法に関す
るものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to the production of a higher alcohol-based aqueous dispersion having useful performance as a cement compounding agent, waterproofing agent, non-shrinking agent, powder, tile adhesive, non-shrinking agent for grout, etc. It is about law.

この発明は界面活性剤又は分散剤と油脂を混合攪拌して
、さらに適量の高級アルコールを加えて混合攪拌し、こ
れに清水を加えて分散せしめた水性分散液囚を得、該水
性分散液囚にホルマリンを加えて混合し分散させて製造
した高級アルコール系水性分散液が、セメント用配合剤
、防水剤、無収縮剤、末剤、タイル貼着剤、グラウト用
無収縮剤として用いられる。This invention involves mixing and stirring a surfactant or a dispersant and an oil or fat, further adding an appropriate amount of higher alcohol, mixing and stirring, and adding fresh water to this to obtain a dispersed aqueous dispersion. A higher alcohol-based aqueous dispersion produced by adding formalin and mixing and dispersing it is used as a compounding agent for cement, a waterproofing agent, a non-shrinking agent, a powder, a tile adhesive, and a non-shrinking agent for grout.

この発明で得られる高級アルコール系水性分散液を配合
するセメントはポルトランドセメントの如く水と反応し
て硬化する能力を有する所詮セメントならば何れも使用
されるものである。The cement to which the aqueous higher alcohol dispersion obtained according to the present invention is blended may be any cement, such as Portland cement, which has the ability to harden by reacting with water.

つぎにこの発明で混合する化合物について詳記する。Next, the compounds to be mixed in this invention will be described in detail.

界面活性剤としては特にアニオン系ポリアルキルアリル
スルホン酸塩が好適で、あり、又分散剤としては、ナフ
タリンスルホン酸系高縮合物が特に好適であり、どちら
も油脂０．０１〜０．１５重量部に対して０．６〜３重
量部の範囲内で添加するのが好ましい。As the surfactant, anionic polyalkylaryl sulfonate is particularly suitable, and as the dispersant, naphthalene sulfonic acid-based high condensate is particularly suitable, both of which contain 0.01 to 0.15 weight of oil and fat. It is preferable to add within the range of 0.6 to 3 parts by weight.

界面活性剤又は分散剤と混合する油脂としては、植物油
脂である大豆油が好適であ位、例えば大豆油を界面活性
剤又は分散剤０．６〜３．０重量部に対してｏ、ｏｉ〜
０．１５重量部、好ましくは０．０５〜０．１重量部の
範囲内の腋で混合するのが好ましい。この範囲以外では
性能発現性が付与されない。As the oil and fat to be mixed with the surfactant or dispersant, soybean oil, which is a vegetable oil, is suitable. For example, soybean oil may be mixed with o.o.i. ~
It is preferred to mix in an amount of 0.15 parts by weight, preferably in the range of 0.05 to 0.1 parts by weight. Performance development is not imparted outside this range.

界面活性剤又は分牧剤と油脂を十分混合攪拌して、さら
に高級アルコール（ラウリルアルコール）液状を油脂に
対して０．１〜３．０重量％、好ましくは０．６〜１．
０重１チの範囲内で加えて十分混合攪拌して、これに清
水を界面活性剤又は分散剤０．６〜３重量部に対して２
〜６重量部の範囲内で飽加し十分に混合攪拌し分散せし
めて得た水性分散液（２）を、２４時間放置することな
く、直ちに３７％ホルマリンを加えたのでは十分満足し
える良好な水性分散液即ち高級アルコール系水性分散液
が得られないので、上記で得られた水性分′散液＾を少
なくとも２４時間放置した後３．７ｓホルマリンを加え
て混合攪拌する。無収縮性でヒビワレ防ＬＥのコンクリ
ート、モルタルを得る為にはホルマリンの添加量は油Ｍ
＆に対して１〜１０重量ｓ１、好ましくは５〜６重４Ｎ
ｋｅｓの範囲内の量で加えるとよい。接着性の高いセメ
ントペーストを得たい場合はホルマ好ましくは１０〜２
０重量−の範囲内で加えるのが好ましい。仁の範囲以外
の添加量では十分満足される接着性を付与しうる高級ア
ルコール系水性分散液が得られない。The surfactant or grazing agent and the oil are sufficiently mixed and stirred, and further a liquid higher alcohol (lauryl alcohol) is added in an amount of 0.1 to 3.0% by weight, preferably 0.6 to 1.0% by weight, based on the oil.
Add 2 parts by weight of clean water to 0.6 to 3 parts by weight of surfactant or dispersant, mix thoroughly and stir.
The aqueous dispersion (2) obtained by saturation within the range of ~6 parts by weight, thorough mixing and stirring, and 37% formalin added immediately without leaving it for 24 hours gave a satisfactory result. Since an aqueous dispersion, that is, a higher alcohol-based aqueous dispersion, cannot be obtained, the aqueous dispersion obtained above is left to stand for at least 24 hours, and then formalin is added for 3.7 seconds and mixed and stirred. In order to obtain non-shrinkage and crack-proof concrete and mortar, the amount of formalin added is oil M.
1 to 10 weight s1 for &, preferably 5 to 6 weight 4N
It is best to add it in an amount within the range of kes. If you want to obtain a cement paste with high adhesiveness, forma preferably 10 to 2
It is preferable to add within the range of 0 weight. If the amount added is outside the above range, it will not be possible to obtain a higher alcohol-based aqueous dispersion that can provide sufficiently satisfactory adhesive properties.

良好な水性分散液＾にホルマリンを所定の割合で加えて
十分混合攪拌して高級アルコール系水性分散液が得られ
る０これを直ちにポルトランドセメントと混合したので
は十分満足しえる製品が得られないので、上記で得られ
た高級アルコール系水性分散液を少なくとも２４時間放
置することにより極めて良好な性能を有する高級アルコ
ール系水性分散液が得られる。Add formalin in a predetermined ratio to a good aqueous dispersion^ and stir thoroughly to obtain a higher alcohol-based aqueous dispersion.If you immediately mix this with Portland cement, you will not be able to obtain a fully satisfactory product. By allowing the aqueous higher alcohol dispersion obtained above to stand for at least 24 hours, an aqueous higher alcohol dispersion having extremely good performance can be obtained.

この発明で得られた高級アルコール系水性分数液は、セ
メント配合剤、防水剤、無収縮剤、末剤、タイル貼着剤
、グラウト用無収縮剤等としてすぐれた性能を発現し広
汎な用途を有している。The higher alcohol-based aqueous fraction liquid obtained by this invention exhibits excellent performance as a cement compounding agent, waterproofing agent, non-shrinking agent, powder, tile adhesive, non-shrinking agent for grout, etc., and has a wide range of uses. have.

さらに界面活性剤又分散剤の高度の分散性能の特性を害
Ｊることがなく、かつ顕著な性能特性を゛発現するもの
である。Furthermore, it does not impair the high dispersion properties of the surfactant or dispersant, and exhibits remarkable performance characteristics.

この発明で得られた高級アルコール系水性分散液は無溶
剤、無害、無臭、非可燃性で災害対策上問題を提起しな
い。The higher alcohol-based aqueous dispersion obtained by this invention is solvent-free, harmless, odorless, and non-flammable, and does not pose any problems in disaster prevention.

この発明で生成された高級アルコール系水性分散液は使
用時、水で希釈して希釈高級アルコール系水性分散液と
し、これをボルトランドセメットに混和するものである
。この発明の高級アルコール系水性分散液はセメントの
高度の分散性の特性を害することがなく、かつ顕著な性
能を発現する優れた特徴を有して謬る。When used, the higher alcohol aqueous dispersion produced in this invention is diluted with water to form a diluted higher alcohol aqueous dispersion, which is then mixed with Bortland Cemet. The higher alcohol-based aqueous dispersion of the present invention has the excellent characteristics of not impairing the highly dispersible properties of cement and exhibiting remarkable performance.

即ちこの発明で得られた高級アルコール系水。That is, higher alcohol water obtained by this invention.

性分散液は構造的に水溶性高分子の組織を形成し、これ
をセメントに混和するととＫより、かつセメントとの相
互効果により、セメント自体の粘性を増大させるととも
に優れた分散力によりセメントを超微粒子に分散し、し
かも大巾に少ない水セメント比、Ｗ／Ｃで優れた流動性
のセメントペーストが得られる。更にセメント／／／ペ
ーストの凝集力（しまり）が良好となり密度の＾い充填
性のよいモルタル、コンクリートを形成し優れた施工性
、作業性が改善向上される優れた特徴を有している。さ
らにセメントペーストの内部に保水性が長く、そのため
水の急激な蒸発を抑制し警手効果を著しく高める性能を
有している。更にセメントペーストの発熱を抑制し、さ
らにモルタル、コンクリートの練装置き経過時間の流動
性の低下がないなど優れた性能特性を有している。The water-soluble dispersion structurally forms a structure of water-soluble polymers, and when mixed with cement, it increases the viscosity of the cement itself and increases the viscosity of the cement due to the mutual effect with the cement. A cement paste that is dispersed into ultrafine particles and has excellent fluidity can be obtained with a significantly lower water-to-cement ratio (W/C). Furthermore, the cohesive force of the cement///paste is good, forming mortar and concrete with good density and filling properties, and has excellent workability and improved workability. Furthermore, the cement paste retains water for a long time, and therefore has the ability to suppress rapid evaporation of water and significantly enhance the guard effect. Furthermore, it has excellent performance characteristics such as suppressing the heat generation of cement paste and no decrease in fluidity over time in mortar and concrete kneading equipment.

この発明の高級アルコール系水性分散液による高分子が
旺盛とな抄セメント、モルタル、コンクリートの初期強
度の発現性が付与されるとともに更に高強度及び超高強
度の発現性をも得られる特長も有している。The higher alcohol-based aqueous dispersion of this invention not only imparts initial strength development properties to cement, mortar, and concrete that are rich in polymers, but also has the feature of providing high strength and ultra-high strength development properties. are doing.

前記この発明の高級アルコール系水性分散液はセメント
との相乗効果によりモルタル、コンクリートの硬化を著
しく促進されるばかりでたく、且つセメント硬化体に強
靭性と強い防水性、さらに接着強度等を物理的に発現す
る性能を有しており、更にゴム状弾性をも付与し得るの
でセメント硬化体の最大の欠点である乾燥時のヒビワレ
の発生を防止できる作用効果を顕著に発揮する特徴を有
しているへ この発明の高級アルコール系水性分散液の高分子エネル
ギーの機能が高度に促進されるためセメントペーストが
細骨材及び粗骨材を強固に接着包容せしめるとともに、
更に骨材間に前述の如くゴム状弾性の特性を有するので
耐震性及び動的強度に対する強大な抵抗性を顕著に発現
する優れた特徴を有している。　　　　　　　　゛（・
・さらに高級アルコール系水性分散液のもつ高度の分子
が進んでコンクリート、モルタルの耐水性、耐蝕性、耐
候性、耐薬品性などが著しく発揮される特性をも有して
いる。The higher alcohol-based aqueous dispersion of the present invention not only significantly accelerates the hardening of mortar and concrete due to its synergistic effect with cement, but also provides physical properties such as toughness, strong waterproofing properties, and adhesive strength to hardened cement products. In addition, it has the ability to exhibit rubber-like elasticity, so it has a remarkable effect of preventing the occurrence of cracks during drying, which is the biggest drawback of hardened cement. Since the function of polymer energy in the higher alcohol-based aqueous dispersion of this invention is highly promoted, the cement paste can firmly adhere and encapsulate fine aggregate and coarse aggregate, and
Furthermore, since the aggregates have rubber-like elastic properties as described above, they have excellent characteristics of exhibiting remarkable earthquake resistance and great resistance to dynamic strength.゛（・
・Furthermore, the highly advanced molecules of the higher alcohol-based aqueous dispersion have properties that significantly improve the water resistance, corrosion resistance, weather resistance, chemical resistance, etc. of concrete and mortar.

史に吸水性、透水性がなく秀れた防水性と撥水性を発現
する。It exhibits excellent waterproofness and water repellency with no water absorption or permeability.

さらに早期高強度の発現性が付与されると共に長期材令
の強度も伸びる優れた特徴も有している。更にコンクリ
ートの耐久性を永久健全化さらに耐アルカリ性が良好と
な抄セメント中に含有されている水酸化カルシウムによ
る白華（アク）を防止できる優れた特長も有している〇
さらに製品に高硬度、高強度、耐水性、耐薬品性、耐候
性、耐蝕性、耐摩耗性、耐衝撃性、などを付与されると
共に耐汚染性をも付与されるなど優れた特長も有してい
る。Furthermore, it has the excellent feature of not only developing high strength at an early stage but also increasing strength in the long term. Furthermore, the durability of the concrete is permanently improved, and it also has excellent alkali resistance, which prevents efflorescence caused by the calcium hydroxide contained in the cement. Furthermore, the product has high hardness. It has excellent features such as high strength, water resistance, chemical resistance, weather resistance, corrosion resistance, abrasion resistance, impact resistance, etc., as well as stain resistance.

この発明の高級アルコール系水性分散液を混和したコン
クリートを打放し仕上げや、装飾コンクリートとして用
いた場合など色ムラがなく、しかも隣り合う部材間同志
の色合が均一で鮮かな躯体コンクリートを構成する特徴
を有している０ さらに乾燥収縮が小さく、かつ凍結融解の耐久性が一段
と向上し、かつ＾質のワーカプルな超高強度コンクリー
トが得られる優れた特徴を有している〇 この発明で好適に用いられる界面活性剤又分散剤を単独
でセメントに添加された場合の圧縮強塵よりもこの発明
で生成された高級アルコール系水性分散液をセメントに
混和した場合の方が著しい強度増加が得られる優れた特
徴も有している。When the concrete mixed with the higher alcohol-based aqueous dispersion of this invention is used as an exposed finish or as a decorative concrete, it is characterized by the fact that there is no color unevenness, and the color of adjacent members is uniform and bright. 0 Furthermore, it has excellent characteristics such as low drying shrinkage, further improved freeze-thaw durability, and the ability to obtain high-quality, workable, ultra-high strength concrete. Suitably used in this invention. It is an advantage that when the higher alcohol-based aqueous dispersion produced by this invention is mixed into cement, a remarkable increase in strength is obtained, compared to the case where a surfactant or dispersant is added alone to cement. It also has other characteristics.

この発明の高級アルコール系水性分散液を混和したコン
クリートは海水の塩分に対する強力な抵抗力が著しく改
善向上され更に耐蝕性が大である。さらに海洋構造物を
塩害風化から完全に保繰する優れた特性を発揮しコンク
リートの耐久性を大にならしめる特徴を有している。さ
らに耐衝撃性が強く、海面の浮遊物の衝撃に対して海洋
構築物の破損を防止し、また減少せしめる効果が顕著で
ある。Concrete mixed with the higher alcohol-based aqueous dispersion of the present invention has significantly improved strong resistance to salt in seawater and also has high corrosion resistance. Furthermore, it exhibits excellent properties that completely protect marine structures from salt damage and weathering, and has the characteristic of greatly increasing the durability of concrete. Furthermore, it has strong impact resistance, and has a remarkable effect of preventing and reducing damage to marine structures due to the impact of objects floating on the sea surface.

この発明の高級アルコール系水性分散液とセメントを混
合すればセメントペーストの強度及び曲げ強度、更に引
張強度、剪断強度等が者しく高める作用効果を顕著に発
揮されるので強度増進剤としても使用できる。When the higher alcohol-based aqueous dispersion of this invention is mixed with cement, the effect of significantly increasing the strength, bending strength, tensile strength, shear strength, etc. of the cement paste is exhibited, so it can also be used as a strength enhancer. .

東に海砂を、川砂の変りに用いても鉄筋、鉄骨々ど騙蝕
されることがなく、かつ完全に防錆化する性能を有して
いる。Even if sea sand is used instead of river sand, it will not corrode the reinforcing bars and steel frames, and it has the ability to completely prevent rust.

更に鉄筋に対する付着力（接着力）が強固に付与される
特長も有している。Furthermore, it has the feature of providing strong adhesion (adhesive force) to reinforcing bars.

この発明で生成された高級アルコール系水性分散液は特
異な構造を発現されるので寒冷時５℃低温以下でもコン
クリートの充填作業が可能で、しかも十分な強度の発現
性が付与される優れた特性を発揮する。更に凍結融解耐
久性が極めて優れる特徴も有している。The higher alcohol-based aqueous dispersion produced by this invention has a unique structure, so it can be filled with concrete even in cold temperatures of 5 degrees Celsius or lower, and has excellent properties such as being able to develop sufficient strength. demonstrate. Furthermore, it has the characteristic of extremely excellent freeze-thaw durability.

前記の如く、この発明で得られた高級アルコール系水性
分散液はポルトランドセメ゛ント系のものならば使用で
きるが、セメントとしては、普通セメント、早強セメン
ト、白色セメント、高炉セメント、フライアッシュセメ
ント等の外石膏、炭酸カルシウム、ドロマイトプラスタ
ー、粘土等の各種土木建築素材の無機質粉末なども広範
囲に亘り使用できるものである。As mentioned above, the higher alcohol-based aqueous dispersion obtained in this invention can be used as long as it is made of Portland cement, but examples of cement include ordinary cement, early strength cement, white cement, blast furnace cement, fly ash cement, etc. In addition, inorganic powders of various civil engineering and construction materials such as gypsum, calcium carbonate, dolomite plaster, and clay can also be used over a wide range.

この発明の高級アルコール系水性分散液がこのように優
れた効果を奏するのは単に界面活性剤又は分散剤と油脂
さらに高級アルコール、清水、およびホルマリンとのみ
の関連によるものではなく、界面活性剤又は分散剤と油
脂さらに高級アルコール、清水、史にホルマリンから得
られる高級アルコール系水性分散液の各化合物間に化学
反応が起き特異な性能を示すためと考えられる。The superior effects of the higher alcohol-based aqueous dispersion of the present invention are not simply due to the relationship between the surfactant or dispersant and oils and fats, higher alcohol, clear water, and formalin; This is thought to be due to chemical reactions occurring between the dispersant, fats, oils, higher alcohols, fresh water, and various compounds in higher alcohol-based aqueous dispersions obtained from formalin, resulting in unique performance.

以上詳記した如く、この発明の高級アルコール系水性分
散液の組成は界面活性剤又は分散剤は油ＢｌｒＩ０．０
１〜０．１５重醍部に対して０．６〜３重量部を十分混
合攪拌し、更に高級アルコール（ラウリルアルコール）
液状を油脂に対して０．１〜３１１１％の範囲内の敬で
加えて十分混合攪拌して、これに清水を界面活性剤又は
分散剤０．６〜３重量部に対し２〜６重敬部の範囲内で
力りえて十分混合攪拌し分散せしめた水性分散液ｌ〜に
１テ１にホルマリンを加えて混合したのでは十分、菊址
しえる性能を有する高級アルコール系水性分散液が得ら
れないので、上記で得られた水性分赦数回を少なくとも
２４時間放置して、得られた水性分散数回にホルマリン
を加えて十分混合攪拌するが、ホルマリンの添加量は、
無収縮性及びヒビワレ防止を発現せしめる場合において
は油脂に対して１〜１０重量％の範囲内の量で加えると
よい。史に接着性を発現せしめる場合においては、油脂
に対して１０〜３０重量％の範囲内で加えられる。水性
分散数回を少なくとも２４時間放置した後上記割合のホ
ルマリンを加えて十分混合攪拌し分散させた高級アルコ
ール系水性分散液を直にポルトランドセメントと混合し
たのでは十分満足しうる性能が得られないので、上記で
得られた高級アルコール系水性分散液を少なくとも２４
時間放置することにより極めて良好な高級アルコール系
水性分散液となり水以外のものの含徽は２０〜６０チで
あり、２０℃で粘度は３０〜６０ＣＰである。As detailed above, the composition of the higher alcohol-based aqueous dispersion of the present invention is such that the surfactant or dispersant is oil BlrI0.0.
Thoroughly mix and stir 0.6 to 3 parts by weight per 1 to 0.15 parts of heavy alcohol, and then add higher alcohol (lauryl alcohol).
Add the liquid in a proportion of 0.1 to 3111% based on the fat and oil, mix thoroughly, and add 2 to 6 parts of clean water to 0.6 to 3 parts by weight of surfactant or dispersant. It is sufficient to add formalin to 1 part of an aqueous dispersion that has been thoroughly mixed and dispersed within the range of 1 to 1 to obtain a higher alcohol-based aqueous dispersion having a stable performance. Therefore, the aqueous dispersion obtained above is left for at least 24 hours, and formalin is added to the obtained several aqueous dispersion and thoroughly mixed and stirred. However, the amount of formalin added is
In order to achieve non-shrinkage properties and prevent cracking, it may be added in an amount of 1 to 10% by weight based on the fat or oil. In order to develop adhesive properties, it is added in an amount of 10 to 30% by weight based on the fat or oil. After several aqueous dispersions have been carried out for at least 24 hours, formalin of the above proportion is added, thoroughly mixed and stirred, and the dispersed higher alcohol-based aqueous dispersion is directly mixed with Portland cement, but sufficient performance cannot be obtained. Therefore, the higher alcohol-based aqueous dispersion obtained above was diluted with at least 24
By standing for a period of time, it becomes an extremely good higher alcohol-based aqueous dispersion, containing 20 to 60 centimeters of substances other than water, and having a viscosity of 30 to 60 CP at 20°C.

次にこの発明の実施例を具体的に示す。Next, examples of the present invention will be specifically shown.

実施例１ アニオン系ボロアルキルアリルスルホン酸塩（界面活性
剤）を３に４と大豆油３００ｔを十分混合攪拌し、さら
に高級アルコール（ラウリルアルコール）液状を１．８
？加えて十分混合攪拌して、これに清水５６５３．２ｆ
を加えて十分混合撹拌し分散せしめた水性分散数回を２
４時間放置することにより良好な水性分散数回き８９５
５ｆが得られた。８９５５ｆの該水性分散液η１に３７
チホルマリンを４５ｆ加えて十分混合攪拌し分散させた
高級アルコール系水性分散液を２４時間放置することに
より茶褐色を得た高級アルコール系水性分散液（防水剤
）、（無収縮剤）９Ｋｆを得た。粘度は２０℃でａｏｃ
ｐであった。得られた高級アルコール系水性分散液はセ
メントに対して３．０重量％を標準として添か口する。Example 1 Three to four parts of anionic boroalkylaryl sulfonate (surfactant) and 300 tons of soybean oil were thoroughly mixed and stirred, and 1.8 tons of liquid higher alcohol (lauryl alcohol) was added.
? Add 5653.2f of fresh water to this and mix thoroughly.
Add aqueous dispersion several times by thoroughly mixing and stirring to disperse
Good aqueous dispersion several times by leaving for 4 hours 895
5f was obtained. 37 to the aqueous dispersion η1 of 8955f.
A higher alcohol-based aqueous dispersion prepared by adding 45 f of thiformin, stirring thoroughly, and dispersing it was left for 24 hours to obtain a brown-brown higher alcohol-based aqueous dispersion (waterproofing agent) (non-shrinking agent) of 9 Kf. . Viscosity is aoc at 20℃
It was p. The obtained higher alcohol-based aqueous dispersion is added to the cement at a standard amount of 3.0% by weight.

このようにして得られた高級アルコール系水性分散液を
用いて下記の通りの配合で試験を行なった （備考１）仕方配合 セメント：砂比（Ｃ／Ｓ）は１／３で一定とし、高級ア
ルコール系水性分散液はセメント重量に対して３．０（
チ）加えてフロー値１８０±１０−に調節した。試験体
の養生は室内（温度２０℃、湿度６０〜８０１ＲＨ）Ｋ
放置して気乾養生した試験結果は表−１に示す。（、ｒ
ｘｓ−Ｒｓ２ｏｔ　）の方法による。Using the higher alcohol-based aqueous dispersion obtained in this way, tests were conducted with the following formulation (Note 1) Method: The cement:sand ratio (C/S) was kept constant at 1/3, and the The alcohol-based aqueous dispersion has a ratio of 3.0 (
h) In addition, the flow value was adjusted to 180±10−. The test specimen was cured indoors (temperature 20℃, humidity 60-801RH).
Table 1 shows the test results of the samples left to dry in the air. (, r
xs-Rs2ot) method.

表−１ 上記表−１の通抄無混入モルタルと比し大巾な圧縮、曲
げ強度の増加が得ら〜れることか確認された。Table 1 It was confirmed that a large increase in compression and bending strength could be obtained compared to the mortar without any mixed paper in Table 1 above.

防水性能をＪＩ８Ａ−１４０４（、建築用セメント防水
剤）Ｋ準じて試験を行なった。その結果透水比が０．２
３であ抄防水性能にすぐれていることが判明し九〇 実施例２ 実施例１で得られた高級アルコール系水性分散液を用い
てポルトランドセメント重量に対して３％配合したコン
クリートを用いて無収縮剤の実験を下記の通妙の配合比
で行なった。The waterproof performance was tested according to JI8A-1404 (cement waterproofing agent for construction) K. As a result, the water permeability ratio is 0.2
90 Example 2 Using the higher alcohol-based aqueous dispersion obtained in Example 1, concrete was mixed with 3% based on the weight of Portland cement. Experiments on the shrinkage agent were conducted using the following combination ratio.

（備考ｌ）仕方配合 上記仕方配合の性能試験は下記の通りである。(Note 1) How to mix The performance test for the above formulation is as follows.

長さ１ｍ両端の断面１６　Ｘ　Ｉ　Ｂｅｎｔ、中央断面
８×８ｃｒｎのくびれをつけたコンクリート両端を鋼製
フレームにボルトを固定してコンクリート収縮を拘束し
た際の亀裂発生鷹での所要日数である。試験は常時温度
２０℃、湿度４５％に調節した恒温、恒湿の室内で実施
した。This is the number of days required for cracks to occur when constricted concrete with a cross section of 16 x I Bent at both ends and a center cross section of 8 x 8 crn is fixed to a steel frame with bolts to restrain concrete shrinkage. The test was conducted in a constant temperature and humidity room that was constantly adjusted to a temperature of 20° C. and a humidity of 45%.

この発明高級アルコール系水性分散液配合コンクリート
は亀裂発生までの所要日数が大巾に伸びるので、普通の
建物の場合理鍮的には亀裂がはいらないことが確認され
た。Since the concrete containing the higher alcohol-based aqueous dispersion of the present invention takes a significantly longer period of time to develop cracks, it has been confirmed that ordinary buildings do not develop cracks.

実施例３ 実施例１で得られた高級アルコール系水性分散液を用い
て、ポルトランドセメン）３１１に対して３％を添加し
たセメント１：３砂、重量配合Ｗ１０５５％、モルタル
配合したものを用いてＪＩＳＲ５２０１による曲げ接着
強度試験を行なった。試験結果は表−２に示す。Example 3 Using the higher alcohol-based aqueous dispersion obtained in Example 1, cement 1:3 sand containing 3% of Portland cement 311, weight ratio W 1055%, and mortar were mixed. A bending adhesive strength test was conducted according to JISR5201. The test results are shown in Table-2.

表−２ 上記表−２の性能試験は下記の通りである０ＪＩＳＲ５
２０１に準じて、４Ｘ４Ｘ１６３のモルタルの供試体を
７日間水中養生し、長さ方向に垂直に切断して４Ｘ４Ｘ
８３の供試体を型枠に収め、上記の通りの゛配合した生
モルタルを型枠の中に流し込み１本の供試体を作成し、
材令１日で型枠から脱型して（気温２０℃、湿度７０〜
９０チ）湿空養生を行ない材令７日、２８日で曲げ破壊
による接着強度を測定しＫｇ／ｃｎを算出した。供試体
Ｆ１９本の平均値を示す。Table-2 The performance test of Table-2 above is as follows: 0JISR5
201, a 4X4X163 mortar specimen was cured in water for 7 days, cut vertically in the length direction, and 4X4X
83 specimens were placed in a mold, and raw mortar mixed as above was poured into the mold to create one specimen.
Remove the mold from the formwork after 1 day of age (temperature 20℃, humidity 70~
90ch) Humid air curing was performed, and the adhesive strength by bending fracture was measured on the 7th and 28th day, and Kg/cn was calculated. The average value of 19 specimens F is shown.

実施例４ 実施例１で得ら−れた高級アルコール系水性分散液を用
いて、白色ポルトランドセメント重量に対して３％配合
した。Example 4 The higher alcohol-based aqueous dispersion obtained in Example 1 was blended in an amount of 3% based on the weight of white Portland cement.

セメント１；２天然骨材エメリーｆ３−を混合して、フ
ロー値１８０±１０−でこの発明のセメント系床材を調
整した。このものを用いて露天コンクリート床に１０ｍ
＋厚に塗布施工したところ明るいカラフルな美しい床を
表現し、耐摩耗性の発現性がち抄、さらに硬度、剛性が
付与され、さらに耐衝撃性は展性に富んだ強固な表面と
なって局部的に強い衝撃をうけてもその力を吸収分散さ
せる性能を有することを確認できた。さらに長期間に亘
り晴雨繰り返しの苛酷な使用条件でもヒビワレが々く、
コンクリート面に完全に接着され、さらに何等剥離する
傾向を認めなかった。Cement 1;2 natural aggregate emery f3- was mixed to prepare the cement flooring material of the present invention with a flow value of 180±10-. Use this to install on an open concrete floor for 10m.
+ When applied thickly, it creates a bright, colorful and beautiful floor, exhibits excellent abrasion resistance, hardness and rigidity, and has impact resistance that creates a malleable and strong surface that can be applied locally. It was confirmed that the material has the ability to absorb and disperse the force even if it is subjected to a strong impact. Furthermore, even under harsh usage conditions of repeated rain and shine over a long period of time, it often cracks.
It adhered completely to the concrete surface and showed no tendency to peel off.

実施例５ 実施例１で得られた高級アルコール系水性分散液を用い
て、普通セメント重量に対して３チ配合した。セメント
１：３重量比、セメント水比Ｗ／Ｃ４６％に調整した゛
。Example 5 Using the higher alcohol-based aqueous dispersion obtained in Example 1, 3 parts were blended based on the weight of ordinary cement. The weight ratio of cement was adjusted to 1:3 and the cement water ratio W/C was adjusted to 46%.

この発明のタイル貼着剤を用いて外壁面にタイルを貼着
した。Tiles were adhered to an external wall surface using the tile adhesive of this invention.

この発明の高級アルコール系水性分散液を配合したモル
タルを用いて施工すると、高級アルコール系水性分散液
の有する滑性により施工作業性の向上を得ることができ
た。When the mortar containing the higher alcohol-based aqueous dispersion of the present invention was used for construction, construction workability was improved due to the lubricity of the higher alcohol-based aqueous dispersion.

この発明により生成された下地モルタルは作業性が良好
な上、保水性が付与されさらに強度が極めて高く、接着
性に富み、さらに無収縮性で、圧着工法に使用する下地
モルタルとして最適である。The base mortar produced by this invention has good workability, water retention, extremely high strength, excellent adhesive properties, and non-shrinkage properties, making it ideal as a base mortar for use in crimping methods.

さらに硬化した下地モルタルの透水性は０で現象は完全
に解消し、内部に浸透する水、湿気の氷結による凍害を
防止する優れた性能を有していることが確認された。Furthermore, the water permeability of the hardened base mortar was 0, and the phenomenon was completely resolved, confirming that it had excellent performance in preventing freezing damage caused by water penetrating into the interior and freezing of moisture.

さらにヒビワレの発生がなく、かつヒビワレの発生を防
止する作用効果を発揮し更に無収縮性のため温度変化に
よる強度劣化は無く、高い強度は永久的に維持出来るの
で高水密性と相俟って自然破壊は絶無となるのである。In addition, it does not cause cracks and exhibits the effect of preventing cracks from occurring.Furthermore, because it is non-shrinkable, there is no strength deterioration due to temperature changes, and high strength can be maintained permanently, so it is combined with high water tightness. There will be no destruction of nature.

この発明の高級アルコール系水性分散液（タイル貼着剤
）を混和した下地モルタルと従来糊剤の比較は下記の通
りである。A comparison between the base mortar mixed with the higher alcohol-based aqueous dispersion (tile adhesive) of the present invention and a conventional adhesive is as follows.

以上の如く、この発明の高級アルコール系水性分散液を
混和したモルタル（タイル貼着剤）は無収縮性で、透呆
性は改良され、水密性は向上し、強度は増加するためす
ぐれた性状が得られるとともにコテ滑べりが良好なため
施′工の作業性を容易にし工期を短縮し、経費の低減を
はかることができる等幾多の優れた性能の特徴を有する
ものである。As described above, the mortar (tile adhesive) mixed with the higher alcohol-based aqueous dispersion of the present invention has excellent properties because it is non-shrinkable, has improved permeability, improved watertightness, and increased strength. It has a number of excellent performance characteristics, such as being able to obtain good trowel slippage, making the work easier, shortening the construction period, and reducing costs.

実施例６ ナフタリンスルホン酸系高縮合物（分散剤）を６　Ｋｅ
と大豆油３００ｔを十分混合攪拌し、さらに高級アルコ
ール（ラウリルアルコール）液状３Ｆを加えて十分混合
攪拌して、これに清水５、６５２−を加えて十分混合攪
拌し分散せしめた水性分散液（２）を２４時間放置する
ことにより良好な水性分散液１１．９５５Ｋｆ囚が得ら
れた。Example 6 Naphthalene sulfonic acid-based high condensate (dispersant)
and 300 tons of soybean oil were sufficiently mixed and stirred, further added with higher alcohol (lauryl alcohol) liquid 3F and sufficiently mixed and stirred, and to this was added Shimizu 5,652- and thoroughly mixed and stirred to obtain an aqueous dispersion (2 ) was allowed to stand for 24 hours to obtain a good aqueous dispersion of 11.955 Kf.

該水性分散液１１．９５５Ｋｆ囚と３７チホルマリンを
４５ｆ加えて十分混合攪拌して得た高級アルコール系水
性分散液を２４時間放置することによね良好な高級アル
コール系水性分散液（グラウト用無収縮剤）　１２　Ｋ
ｙを得た。The aqueous dispersion 11.955 Kf and 45 f of 37-th formalin were added, thoroughly mixed and stirred, and the resulting higher alcohol aqueous dispersion was left to stand for 24 hours to form a good higher alcohol aqueous dispersion (non-shrinkable for grouting). agent) 12K
I got y.

粘度は２０℃で４６ｃｐであった。The viscosity was 46 cp at 20°C.

これを用いてポルトランドセメントに対して４重ａＳ配
合した。セメント水比Ｗ／Ｃ５Ｇｍ！（七メン）１：１
砂重量比）の配合モルタルを調整したグラウト用モルタ
ルを用いて、機械プラント据付けの基礎等の施工に優れ
た性質を有する。また保水性に優れ施工作業は良好とな
り、流動性（作業性）がよく、プリージングがなく、沈
下がなく、流動性がよいため空隙がなく、施工作業容鵬
となり能率が向上するっ 早期高強度の発現性があり、さらに付着剪断強度にすぐ
れかつ硬化したモルタルは沈下収縮がなく、空隙を完全
に充填し、機械ペースプレートに完全接着し、早期高強
度の発現性により機械装置据付は工期を大巾に短縮でき
た。また、耐油、耐水性にすぐれ、さらに耐久性は永久
的である。This was used to blend quadruple aS into Portland cement. Cement water ratio W/C5Gm! (Seven men) 1:1
Using a grouting mortar with an adjusted mortar composition (sand weight ratio), it has excellent properties for construction of foundations for mechanical plant installations, etc. In addition, it has excellent water retention, which makes construction work easier, and has good fluidity (workability), no pleating, no settling, and good fluidity, so there are no voids, which makes construction work easier and improves efficiency. Furthermore, the cured mortar has excellent adhesive shear strength and does not suffer from settling and shrinkage, completely fills the voids and completely adheres to the mechanical pace plate, and the early development of high strength reduces the construction period for mechanical equipment installation. I was able to shorten it to a large width. It also has excellent oil and water resistance, and is permanently durable.

長期強度も優れているため機械、橋梁の基礎としての支
持力が充分であり衝撃に十分耐えるものである。さらに
適用範囲が広く嬉かに顕著に優れた性能を発現するグラ
ウト用無収縮剤である。It also has excellent long-term strength, so it has sufficient support as the foundation for machines and bridges, and can withstand shocks. Furthermore, it is a non-shrinking agent for grout that has a wide range of applications and exhibits significantly superior performance.

この発明高級アルコール系水性分散液（グラウト用無収
縮剤）を普通セメントに対して４重１％を添加したグラ
ウト用セメントにつき物理的試験を行なった。その結果
を表−３に示す。A physical test was conducted on a grouting cement prepared by adding the higher alcohol-based aqueous dispersion (non-shrinking agent for grout) of the present invention in an amount of 1% by weight of 4 parts to ordinary cement. The results are shown in Table-3.

但し従来との比較のため、この発明の実施例６で用いる
分散剤を単独でセメントに対して２重ｔチ添加したもの
の結果も併記した。However, for comparison with the conventional example, the results are also shown in which the dispersant used in Example 6 of the present invention was added alone to cement twice.

表−３ 上記表−３よりみてこの発明品が優れていることが判る
。Table 3 From Table 3 above, it can be seen that this invention product is superior.

注：測定方法 １．７０−値（ｗ　）　　　ＪＩｅ３−５２０１による
。Note: Measurement method 1.70-value (w) According to JIe3-5201.

２、　ブリージｙグ率（％　）ＪＩＳＡ−１１２３によ
る。2. Breeze rate (%) According to JISA-1123.

３、圧縮強度（Ｋｆ／ａＡ）　　　ＪＩ８−５２０１に
よる。3. Compressive strength (Kf/aA) According to JI8-5201.

４、沈下率（ｑｂ） 直径５　ｃｍ　ｓ高さ１０譚のステンレス鋼製円筒内に
モルタルを充填し直ちに表面仕上げを行ないモルタル容
器上端の沈下をマイクロメーターにより５点測定してそ
の平均沈下率を求めた。4. Settlement rate (qb) Fill a stainless steel cylinder with a diameter of 5 cm and a height of 10 cm with mortar, immediately finish the surface, measure the settlement of the upper end of the mortar container at 5 points with a micrometer, and calculate the average settlement rate. I asked for it.

５、付着剪断強度（ＫＩＩ／−） 鋼製リング（内径１５．６　ｔ！１ｌＩｓ外径１６．５
ｃ＋＋＋。5. Adhesive shear strength (KII/-) Steel ring (inner diameter 15.6 t!lIs outer diameter 16.5
c+++.

高さ４国）の中にモルタルを充填し、一定材今後モルタ
ル外縁部を鋼製円板（径１５　ｃｍ　％高さ４、５　ｃ
ｙｎ　）を用いて上方より加圧しモルタルを押出すその
時の荷重Ｐ（Ｋ４）；モルタル充填ハング内表面積（Ａ
）（ｃＩＩ）とし、付着剪断強度Ｓは次の式により求め
た。Fill mortar into the mortar (height: 4 cm), then use a certain material to cover the outer edge of the mortar with a steel disc (diameter: 15 cm, height: 4, 5 cm).
Load P (K4) at which time the mortar is pushed out by applying pressure from above using
) (cII), and the adhesion shear strength S was determined by the following formula.

Ｓ＝Ｐ／Ａ 以上詳記した如く、この発明高級アルコール系水性分散
液（グラウト用無収縮剤）を使用すれば従来品に比較し
、流動性に＊れ、しかも作業性が向上し、付着剪断強度
が飛躍的に増大し、しかも早期高強度も付与され重ねて
ワーカ−ビリティが良好となり理想的な施工ができるも
のである。S=P/A As detailed above, the use of the higher alcohol-based aqueous dispersion (non-shrinking agent for grout) of the present invention improves fluidity*, improves workability, and improves adhesion compared to conventional products. The shear strength increases dramatically, and high early strength is also imparted, resulting in good workability and ideal construction.

以上詳記した如く、この発明高級アルコール系水性分散
液を使用すれば、強度、接着性、無収縮性でヒビワレを
防止できる作用効果を顕著に発揮し、更に耐震性に対す
る強力な抵抗性を発現する顕著な特徴を有しており、爽
に耐アルカリ性などを始めとする化学的性質が特にすぐ
れる性能を発現すると共に、広汎な用途を有しており、
更に耐久性にすぐれる特徴を有しており、この発明が極
めて優れていることを如実に示すもので工業的に極めて
有益な発明である。As detailed above, if the higher alcohol-based aqueous dispersion of the present invention is used, it will significantly exhibit the effect of preventing cracking due to its strength, adhesiveness, and non-shrinkage properties, and will also exhibit strong earthquake resistance. It has a remarkable characteristic of being resistant to alkali, exhibits particularly excellent chemical properties, and has a wide range of uses.
Furthermore, it has a feature of excellent durability, which clearly shows that the present invention is extremely superior, and is an industrially extremely useful invention.

１７５175

Claims (1)

【特許請求の範囲】[Claims] 油脂と適量の高級アルコールを界面活性剤又は分散剤で
水に分散させた水性分散液＾を得、該水性分散液（ＡＲ
Ｋホルマリンを加えて混合攪拌することを特徴とする新
規高級アルコール系水性分散液の製造法。An aqueous dispersion is obtained by dispersing fats and oils and an appropriate amount of higher alcohol in water using a surfactant or a dispersant, and the aqueous dispersion (AR
A method for producing a novel higher alcohol-based aqueous dispersion, which comprises adding K-formalin and mixing and stirring.