JPS58138795A - Lubricating agent for mandrel bar - Google Patents
Lubricating agent for mandrel barInfo
- Publication number
- JPS58138795A JPS58138795A JP1890282A JP1890282A JPS58138795A JP S58138795 A JPS58138795 A JP S58138795A JP 1890282 A JP1890282 A JP 1890282A JP 1890282 A JP1890282 A JP 1890282A JP S58138795 A JPS58138795 A JP S58138795A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- water
- weight
- agent
- dispersing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
本発明は、マンドレルバ−潤滑剤に係り、特にスプレー
、塗布等にて短時間に厚塗りができ、かつ低温域（室温
から１００℃）での塗膜の乾燥時間が短かく、さらに、
乾燥塗膜が耐水性、１飯撃性、さらに潤滑性にも優れる
マンドレルバ−潤滑剤に関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a mandrel bar lubricant, which can be coated thickly in a short time by spraying or coating, and which has a short drying time in a low temperature range (room temperature to 100°C). Shorter and more
This invention relates to a mandrel bar lubricant that provides a dry coating film with excellent water resistance, instant impact properties, and lubricity.
今日最も広く行なわれているシームレス鋼管圧延等に用
いる潤滑剤は、油（廃ｆｄｉ）に黒鉛粉末を混合したも
のを用いて、マンドレルバ−にシャワーのようにかける
か、または、まずマンドレルバ−に油（廃油）のみをか
け、次にこのように黒鉛粉末をふりかける方法にて潤滑
性をもたしている。The lubricant used in seamless steel pipe rolling, etc., which is most widely used today, is a mixture of oil (waste FDI) and graphite powder, which is sprayed onto the mandrel bar like a shower, or by first applying oil to the mandrel bar. This method provides lubricity by applying only waste oil (waste oil) and then sprinkling graphite powder as shown above.
この場合、油を使用するため、臭、畑の発生が烈しく、
作業環境から考えても好ましくない。また、火災の危険
性もある。さらに均一なる潤滑性塗膜が得られない。In this case, since oil is used, there is a strong odor and odor.
It's not desirable from a work environment standpoint. There is also a risk of fire. Furthermore, a uniform lubricating coating film cannot be obtained.
一方、油を用いないものとして、水性または水溶性の潤
滑剤が考えられているが、短時間に厚塗りができなかっ
たり、低温域、すなわち室温から１００℃位の温度での
塗膜の乾燥に長時間を要するため、次の工程に移ること
が出来ず、ロスタイムが大きく問題となっている。また
、分散性が不十分であるため、スプレーノズルのつまり
ゃ、均一な塗膜が得られず、充分な潤滑効果が発揮する
ことができない欠点があった。On the other hand, water-based or water-soluble lubricants are considered as lubricants that do not use oil, but they may not be able to be applied thickly in a short period of time, or the coating film dries at low temperatures, i.e. from room temperature to about 100°C. Because it takes a long time to complete the process, it is not possible to move on to the next process, resulting in a major problem of lost time. Furthermore, since the dispersibility is insufficient, if the spray nozzle becomes clogged, a uniform coating film cannot be obtained, and a sufficient lubricating effect cannot be achieved.
本発明はこれらの欠点を除去するためになされたもので
水性ま、たは水溶性の潤滑剤であるため作業環境に優れ
、また、分散性に優れた懸濁液であり、スプレーノズル
のつまりもなく、短時間に均一な厚塗りが出来、かつ低
温域（室温から１００）
℃）での塗膜の乾燥時間が短かく、合理的であり、さら
に乾燥塗膜が耐水性、耐衝撃性さらに、潤滑性にも優れ
ているシームレス鋼管圧延等に用いられるマンドレルバ
−潤滑剤を提供しようとするものである。The present invention was developed to eliminate these drawbacks, and since it is a water-based or water-soluble lubricant, it is excellent in the working environment, and is a suspension with excellent dispersibility, which prevents clogging of spray nozzles. The drying time of the paint film at low temperatures (from room temperature to 100°C) is short and reasonable, and the dried paint film has good water resistance and impact resistance. Furthermore, it is an object of the present invention to provide a mandrel bar lubricant for use in rolling seamless steel pipes, etc., which has excellent lubricity.
本発明においては、（ａＪ粒度０．１〜５０ＩＬの黒鉛
粉末５〜４５重ｆｉｔｓと、（ｂ）粒度１−６０ ｉＬ
ノ％酸酸二ニル共重合体樹脂グラフト化デンプン、エス
テル化デンプン、エチレン−酢酸ビニル−塩化ビニル三
元共重合体樹脂、アクリル酸エステル共重合体樹脂、ポ
リエチレン樹脂、ポリプロピレン樹脂、スチレン共重合
体樹脂、ポリビニルアルコール樹脂、メタクリル樹脂、
メタクリル−スチレン共重合体樹脂給の群から選ばれる
少なくとも１種の樹脂粉末１〜１５重ｊ１％と、（Ｃ）
非イオン活性剤、アニオン活性剤、カルボキシメチルセ
ルロース、メチルセルロース、エチルセルロース等の分
Ｍ 剤０．１〜８重量鳴と、ざらに（ｄ）ナフテン酸コ
バルト、ナフテン酸亜鉛、ナフテン酸カルシウム、オク
チル酸亜鉛、オクチル酸カルシウム、ネオ酸カルシ）
ラム等の熱水剤０．１〜８重量優とを、（ｅ）水４５〜
７９５重量囁に混合（（ａ） ＋ （ｂ）十切十はン
十（ｅ） ） １．、ボールミル等を用い湿式にて均一
に溶解分散せしめて成る見掛は比重１．０〜１．δ、粘
度０．１〜１００ボイスを有するマンドレルバ−潤滑剤
を調製する。In the present invention, (aJ particle size 0.1-50 IL fits 5-45 graphite powder, and (b) particle size 1-60 iL
% dinylic acid copolymer resin grafted starch, esterified starch, ethylene-vinyl acetate-vinyl chloride terpolymer resin, acrylic ester copolymer resin, polyethylene resin, polypropylene resin, styrene copolymer resin, polyvinyl alcohol resin, methacrylic resin,
1% to 15% by weight of at least one resin powder selected from the group consisting of methacrylic-styrene copolymer resins, and (C)
Nonionic activators, anionic activators, carboxymethylcellulose, methylcellulose, ethylcellulose, etc. with a weight of 0.1 to 8%, and (d) cobalt naphthenate, zinc naphthenate, calcium naphthenate, zinc octylate, Calcium octylate, calci neoacid) 0.1 to 8% by weight of a hydrothermal agent such as rum, (e) 45 to 80% of water.
795 weight mixed ((a) + (b) Jukiri Juhan Ju (e)) 1. The apparent specific gravity of the product is uniformly dissolved and dispersed in a wet process using a ball mill or the like, with a specific gravity of 1.0 to 1. A mandrel bar lubricant having a viscosity of 0.1 to 100 voices is prepared.
しかして、該マンドレルバー＠清剤の前記組成（ａ＋ｂ
＋ｃ十ｄ十ｅ ）Ｃおいて、前記の（ａ）黒鉛粉末の組
成における数量限定、すなわち、５〜４５重ｉｔ％の下
限未満では潤滑性が著しく悪くなり、また上限を越える
場合は接着力が悪くなり共に不可である。Therefore, the above composition (a+b
+ c 1 d 1 e) In C, if the quantity is limited in the composition of the graphite powder (a), i.e., if it is less than the lower limit of 5 to 45 wt %, the lubricity will be significantly deteriorated, and if the upper limit is exceeded, the adhesive strength will be deteriorated. becomes worse and both are impossible.
また粒度に対しては５０μを越えると、前記マンドレル
バ−潤滑剤の分散性が悪く、また、接着性も十分に得ら
れず不可である。また、下限を０、ＩＰとしたのは、通
常工業的には入手可能であり、マンドレルパー潤滑剤の
粘度、安定性等から勘案して好適なためである。If the particle size exceeds 50 microns, the dispersibility of the mandrel bar lubricant will be poor, and sufficient adhesion will not be obtained. Further, the reason why the lower limit is set to 0 and IP is because it is normally available industrially and is suitable in consideration of the viscosity, stability, etc. of the mandrel per lubricant.
次に、樹脂粉末（ｂ）として、酢酸ビニル共重合体樹脂
としては、例えば、ヘキスト合成株式会社製商品名モビ
ニールＤＭ−２００等、グラフト化デンプンとしては、
例えば、日澱化学株式会社製商品名ＦＤＮＲＨ−２１０
、ＭＧ−２０等、工、Ｘチル化デンプンとしては、例え
ば、日澱化学株式会社製商品名、メチルスターチ、エチ
ルスターチ等、エエチレンー酢酸ビニルー塩化ビニル三
元共重合体樹脂としては、例えば、日本ゼオン株式会社
製商品名グラフトマー等、アクリル拳エステル共を合体
樹脂としては、例えば、日本合成化学工業株式会社製商
品名フーボニール等、ポリエチレン樹脂としては、例え
ば、製鉄化学株式会社製商品名、フローセン等、ポリプ
ロピレン樹脂としては、例えば、三井東圧化学株式会社
製商品名三井ノープレン等、スチレン共重合体樹脂とし
ては、例えば、檀水化成品工業株式金社製商品名ダイラ
ーク等、ポリビニルアルコール樹脂としては、例えば、
日本合成化学工業株式会社製商品名ゴー七ノール等、メ
タクリル樹脂としては、例えば、三食レイヨン株式会社
製商品名アクリコン等、メタクリル−スチレン共重合体
樹脂としては、ダイセル化学工業株式会社製商品名セビ
マンーＭＡＳ等を用いることができる。Next, as the resin powder (b), the vinyl acetate copolymer resin is, for example, Movinyl DM-200 manufactured by Hoechst Gosei Co., Ltd., and the grafted starch is:
For example, product name FDNRH-210 manufactured by Nippon Star Chemical Co., Ltd.
, MG-20, etc., methyl starch, ethyl starch, etc., and examples of ethyl-ethylene-vinyl acetate-vinyl chloride terpolymer resins include, for example, Japan Examples of resins combining acrylic esters such as Graftomer (trade name) manufactured by Zeon Co., Ltd. include Fuvonyl (trade name manufactured by Nippon Gosei Kagaku Kogyo Co., Ltd.), and polyethylene resins such as Frocene (trade name manufactured by Tetsuko Kagaku Co., Ltd.)). Examples of polypropylene resins include Mitsui Norprene (trade name, manufactured by Mitsui Toatsu Chemical Co., Ltd.); examples of styrene copolymer resins include, for example, Dilarc (trade name, manufactured by Dansui Kaseihin Kogyo Co., Ltd.); polyvinyl alcohol resins include, for example, ,for example,
For example, examples of methacrylic resins include the product name Go-Sevenol manufactured by Nippon Gosei Kagaku Kogyo Co., Ltd.; examples of methacrylic resins include the product name Acricon manufactured by Sanshoku Rayon Co., Ltd.; and the product name of methacrylic-styrene copolymer resins such as product name manufactured by Daicel Chemical Industries, Ltd. Sebiman-MAS, etc. can be used.
しかして、この樹脂粉末の）の数量限定、すなわち、１
〜１５重ＪＩ１１％の下限未＊になると、接着性が良く
なく、また、塗膜の潤滑性も悪く不可である。上限を越
えると分散安定性が悪く、また、塗膜の潤滑性も悪くな
るため不可である。Therefore, the quantity of this resin powder is limited, that is, 1
When the lower limit of 15 to 11% is reached, the adhesion is not good and the lubricity of the coating film is also poor, making it unacceptable. Exceeding the upper limit is not acceptable because the dispersion stability will be poor and the lubricity of the coating film will also be poor.
また粒度に対しては５０Ｐを越えると、前記マン、ドレ
ルバー潤滑剤の分散性が悪く、均一な塗膜を得るのに悪
影響を与え不可であり、ＩＰ未満では通常入手し難いた
めである。In addition, if the particle size exceeds 50P, the dispersibility of the Mann and Drelbar lubricant will be poor, and it will have an adverse effect on obtaining a uniform coating film, and if it is less than IP, it is usually difficult to obtain.
次に、分散剤（Ｃ）として、非イオン活性剤、すなわち
、水溶液中で電離しないものであるが、ポリエチレング
リコールアルキルエーテルＲ（ＯＯＨ。Next, as a dispersant (C), a nonionic activator, that is, one that does not ionize in an aqueous solution, is polyethylene glycol alkyl ether R (OOH).
ＯＨ，）ｎＯＨ：ポリエチレングリコール脂肪酸エステ
ルＲＣＯ（、ＯＯＨ，ＯＨ，）ｎＯＨ、例えばソルビタ
ン脂肪酸また、アニオン活性剤としてはナフタリン・ス
ルホン酸・ホルムアルデヒド縮金物、例えば花王アトラ
ス株式会社製商品名デモ−゛ルＮ等が好適である。また
カルボキシメチルセルロースとしては、例えば、第−工
業製薬株式会社製ＯＭＯ、メチルセルロースとしては、
例えば、松本油脂製薬株式会社製商品名マーボローズＭ
−１００、Ｍ −４０００等を用いることが出来る。OH,)nOH: polyethylene glycol fatty acid ester RCO(,OOH,OH,)nOH, such as sorbitan fatty acid. Also, as an anionic activator, naphthalene/sulfonic acid/formaldehyde condensate, such as Kao Atlas Co., Ltd. product name: Demo-l N etc. are suitable. In addition, examples of carboxymethylcellulose include OMO manufactured by Dai-Kogyo Seiyaku Co., Ltd., and examples of methylcellulose include:
For example, the product name Marborose M manufactured by Matsumoto Yushi Pharmaceutical Co., Ltd.
-100, M-4000, etc. can be used.
しかして、この分散剤（山の数量限定、すなわち、０．
１〜８重ｉ１％としたのは、０．１重＠ｑｂ未満では分
散効果が不足し、８重量鳴を越えると経済性から見ても
その必要なく、共に不可である。However, this dispersant (limited quantity, i.e. 0.
The reason for setting the weight of 1 to 8 weight i1% is that if it is less than 0.1 weight @qb, the dispersion effect will be insufficient, and if it exceeds 8 weight @qb, it is not necessary from an economic point of view, and both are not possible.
次にその作用機作が未詳であるが、一応離水剤（ｄ）と
して考えられるす７テン＠４１１４ｍ （コバルト、亜
鉛、カルシウム）としては、例えば、大日本インキ化学
工業株式会社製商品名デイクネー） （ＤＩ−ＯＮＡＴ
Ｅ） ２１１１１等、同じく合成脂肪酸金ｘ塙（オクチ
ル酸、ネオ酸）としては、例えば、大日本インキ化学工
業株式会社製商品名Ｚｎ −００ｔｏａｔｅ 、デイク
ネー） （ＤＩ（３ＮＡＴＥ ） Ｏａ等を用いること
が出来る。Next, although its mechanism of action is unknown, examples of Su7ten@4114m (cobalt, zinc, calcium), which can be considered as a water-releasing agent (d), include, for example, Dainippon Ink & Chemicals Co., Ltd. (trade name: Deikune). (DI-ONAT
E) 21111, etc., and the same synthetic fatty acids (octylic acid, neo acid), for example, Dainippon Ink & Chemicals Co., Ltd., trade name Zn-00toate, DI (3NATE) Oa, etc. can be used. I can do it.
しかしてこの離水剤（ｄ）の数量限定すなわち、０．１
〜８重量鳴とじたのは、０．１重量％未満では、イ
低温域（室温から１００℃）にて塗膜が短時間で乾燥せ
ず不可であり、８重ｉ１％を越えると経済性から見ても
その必要なく不可である。However, the quantity of water releasing agent (d) is limited, i.e. 0.1
~ 8 weight% The reason for this is that if it is less than 0.1% by weight, the coating film will not dry in a short time in the low temperature range (room temperature to 100°C), and if it exceeds 8weight i1%, it will not be economical. Even from this point of view, it is unnecessary and impossible.
次に木幹〕の数量限定、すなわち４５〜９５重艦囁の上
限を越えると、マンドレルバ−潤滑剤の見掛は比重およ
び粘度が低下しすぎて、分散性が悪くなるので不可であ
り、下限を越えると見掛は比重および粘度が上昇し塗布
性が悪くなり不可であるＯ
本発明による、マンドレルバ−潤滑剤は室温から５００
°Ｃの範囲にて塗布されるのが望ましい。Next, if the quantity limit of [tree trunk] is exceeded, that is, the upper limit of 45 to 95 heavy ships, the apparent specific gravity and viscosity of the mandrel bar lubricant will decrease too much, and the dispersibility will deteriorate, so it is not possible, and the lower limit If the lubricant exceeds 500% from room temperature, the apparent specific gravity and viscosity will increase and the coating properties will deteriorate.
Preferably, the coating is applied in the °C range.
５００°Ｃ以上の温度にて塗布する場合は、前記マンド
レルパー潤滑剤に珪酸ナトリウム、珪酸カリ、ホウ酸ナ
トリウム等を添加することが望ましい。When coating at a temperature of 500° C. or higher, it is desirable to add sodium silicate, potassium silicate, sodium borate, etc. to the mandrel per lubricant.
また、塗膜の酸化消耗を減少する必要のある場合は、リ
ン酸塩およびその混合物を添加することが望ましい。It is also desirable to add phosphates and mixtures thereof when it is necessary to reduce oxidative wear of the coating.
以下さらに実施例にて本発明を説明する。The present invention will be further explained below with reference to Examples.
実施例１゜
（ａ）粘度０．１〜５０／”の黒鉛粉末１５重量うと、
Φ）粒度ｌ〜５０／”の酢酸ビニル共重合体樹脂、すな
わち、ヘキスト合成株式会社製商品名モビニールＤ Ｍ
−２００４，５重量囁と、仲）分散剤としてカルボキ
シメチルセルロース、すなわち、第一工業製薬株式会社
製商品名セロゲン７ Ａ Ｏ，５重輩唾と、（ｄ）離水
剤としてす７テン酸コ・バルト、すなわち、大日本イン
キ化学工業株式会社製商品名、ＤＩＣＮＡ−ＴＥｇｌｌ
ｌ ２重瀘優と、＜６）水７８重Ｉｔ％とを混合（ａ＋
ｂ＋ｃ＋ｄ＋ｅ ）し、ボールミルにて均一に溶解分散
せしめた見掛比重１．１０ 、粘度２．２ポイズの懸濁
液を得た。この懸濁液を、峯温状態のマンドレルバ−に
スプレーにて塗布したところ短時間にて厚ざ１００Ｐの
乾燥した黒鉛フィルムが得られた。もちろん乾燥した黒
鉛フィルムは耐水性に優れており、接着性も十分であっ
た。ＷＩ！擦係数は０．０６であった。例えば、シーム
レス鋼管の圧延用に好適な効果が得られる。Example 1゜(a) 15 weight of graphite powder with a viscosity of 0.1 to 50/'',
Φ) Vinyl acetate copolymer resin with a particle size of 1 to 50/'', i.e., product name Movinyl DM manufactured by Hoechst Synthesis Co., Ltd.
-2004, 5-weight, (middle) carboxymethyl cellulose as a dispersant, i.e., Daiichi Kogyo Seiyaku Co., Ltd. trade name: Celogen 7 A O, 5-weight, (d) 7-thenic acid as a water-releasing agent. Baltic, i.e., product name manufactured by Dainippon Ink and Chemicals Co., Ltd., DICNA-TEgll
l Mix 2 layers of water and <6) 78 weight It% of water (a+
(b+c+d+e) and uniformly dissolved and dispersed in a ball mill to obtain a suspension having an apparent specific gravity of 1.10 and a viscosity of 2.2 poise. When this suspension was applied by spraying onto a mandrel bar at a peak temperature, a dry graphite film with a thickness of 100 P was obtained in a short time. Of course, the dried graphite film had excellent water resistance and sufficient adhesion. WI! The friction coefficient was 0.06. For example, effects suitable for rolling seamless steel pipes can be obtained.
実施例２゜
前記実施例１の斡）の黒鉛粉末８０重ｉｔ％と、前記実
施例１の（ｂ）の酢酸ビニル共重合体樹脂１０重蓋優と
、（Ｃ）分散剤としてメチルセルロース、すなわち、松
本油脂製薬株式会社製商品名マーボローズＭ−１００１
重量僑と、（ｄ）離水剤としてナフテン酸亜鉛、すなわ
ち、大日本インキ化学工業株式会社製商品名ｚｎ −Ｈ
ａｐｈｔｈｅｎａｔｅ ａ重量優と、（＋３３水５６重
量％とを混合（ａ＋ｂ＋ｃ＋ｄ＋ｅ ）し、ボールミル
にて均一に溶解分散せしめた見掛比重１．２５、粘度２
５ボイズの懸濁液を得た。この懸濁液を室温状態のマン
ドレルバ−にスプレーにて塗布したところ短時間にて厚
さ８００Ｐの乾燥した黒鉛フィルムが得られた。もちろ
ん乾燥した黒鉛フィルムは耐水性に優れており、接着性
も十分であった。摩擦係数は０．０６であった。例えば
、シームレス鋼管の圧延用に好適である。Example 2 80% by weight of the graphite powder of the above Example 1 (b), 10% of the vinyl acetate copolymer resin of (b) of the above Example 1, and (C) methylcellulose as a dispersant, i.e. , manufactured by Matsumoto Yushi Pharmaceutical Co., Ltd. Product name: Marborose M-1001
and (d) zinc naphthenate as a water releasing agent, i.e., trade name zn-H manufactured by Dainippon Ink and Chemicals Co., Ltd.
Aphthenate a by weight and (+33 water 56% by weight) were mixed (a+b+c+d+e) and uniformly dissolved and dispersed in a ball mill, with an apparent specific gravity of 1.25 and a viscosity of 2.
A suspension of 5 voids was obtained. When this suspension was sprayed onto a mandrel bar at room temperature, a dry graphite film with a thickness of 800P was obtained in a short time. Of course, the dried graphite film had excellent water resistance and sufficient adhesion. The friction coefficient was 0.06. For example, it is suitable for rolling seamless steel pipes.
実施例８
（Ｑ粒度０．１〜５０ｐの無鉛粉末１０重量％と、（ｂ
）粒度１〜５０ＩＬのエステル化デンプン、すなわち松
本油脂製薬株式会社製商品名ＮＧ−２０，８重量％と、
（０２分散剤として、非イオン界面活性剤のソルビタン
脂肪酸エステルミ゛すなわち、花王石鹸株式会社製商品
名エマゾール８１０ ０．３ 重量％と、（ｄ）離水剤
としてオクチル酸亜鉛、すなわち、大日本インキ化学工
業株式会社製商品名亜鉛オクトｘ −ト（Ｚｎ −０ｃ
ｔｏａｔｅ ） １重量％と、（ｅ）水８５．７重量％
とを混合（ａ＋ｂ＋ｃ＋ｄ＋ｅ ）Ｌ／、ボールミルに
て均一に溶解分散せしめた見掛比重１．０８、粘度０．
６８ポイズの懸濁液を得た。この懸ｍ液をｘ湿状態のマ
ンドレルバ−にスプレーにて塗布したところ、短時間に
て厚さ２５１Ｌの乾燥した黒鉛フィルムが得られた。も
ちろん乾燥した黒鉛フィルムは耐水性に優れており、接
着性も十分であった。摩擦係数は０．０８であった。例
えば、シームレス鋼管の圧延用に好適である。Example 8 (10% by weight of lead-free powder with a Q particle size of 0.1 to 50p and (b
) 8% by weight of esterified starch with a particle size of 1 to 50 IL, i.e., trade name NG-20, manufactured by Matsumoto Yushi Pharmaceutical Co., Ltd.;
(02 As a dispersant, 0.3% by weight of sorbitan fatty acid ester, a nonionic surfactant, manufactured by Kao Soap Co., Ltd. under the trade name Emazol 810; (d) As a water-releasing agent, zinc octylate, namely Dainippon Ink Chemical Co., Ltd.) Manufactured by Kogyo Co., Ltd. Product name Zinc Octo
toate) 1% by weight and (e) 85.7% by weight of water.
(a+b+c+d+e) L/, which was uniformly dissolved and dispersed in a ball mill with an apparent specific gravity of 1.08 and a viscosity of 0.
A suspension of 68 poise was obtained. When this suspended liquid was sprayed onto a wet mandrel bar, a dry graphite film with a thickness of 251 L was obtained in a short time. Of course, the dried graphite film had excellent water resistance and sufficient adhesion. The friction coefficient was 0.08. For example, it is suitable for rolling seamless steel pipes.
実施例４゜
体樹脂すなわち、日本ゼオン株式会社製商品名グラフト
マー４重１ｌｉ１％と、（Ｃ）分散剤として非イオン界
面活性剤のポリオキシエチレン脂肪酸エステル、すなわ
ち、花王石鹸株式会社製商品名ニスノール １１．５
重ｆｉ％と、（ｄＪＪｌｌ！水剤としてオクチル酸コバ
ルト、すなわち、大日本インキ化学工業株式会社製商品
名００− ｏｃｔｏａｔｅ １．５重蓋優と、（ｅ）水
７８８重量％を混合（ａ＋ｂ＋ｃ＋ｄ＋ｅ ）し、ボー
ルミルにて均一に溶解分散せしめた見掛比重１．１０゜
粘度１．８ボイスの懸濁液を得た。この懸濁液を表面温
度が６０℃のマンドレルバーにスプレーにて塗布したし
たところ短時間にて厚さ８０ｐ−の乾燥した黒鉛フィル
ムが得られた。もちろん乾燥した黒鉛フィルムは耐水性
に優れており、接着性も十分であった。摩擦係数は０．
０９であった。例えば、シームレス鋼管の圧延用に好適
である。Example 4 ゜ body resin, i.e. Graftomer 4x 1li 1% (trade name, manufactured by Nippon Zeon Co., Ltd.) and (C) a polyoxyethylene fatty acid ester of a nonionic surfactant as a dispersant, i.e., Nisnol (trade name, manufactured by Kao Soap Co., Ltd.) 11.5
(a+b+c+d+e) A suspension with an apparent specific gravity of 1.10° and a viscosity of 1.8 voice was obtained by uniformly dissolving and dispersing in a ball mill.This suspension was sprayed onto a mandrel bar with a surface temperature of 60°C. As a result, a dried graphite film with a thickness of 80 p- was obtained in a short time.Of course, the dried graphite film had excellent water resistance and sufficient adhesion.The coefficient of friction was 0.
It was 09. For example, it is suitable for rolling seamless steel pipes.
実施例５゜
（ａ）粒度０．１〜５０ ／”の黒鉛粉末２０重量−囁
と、（ｂ）粒度１〜５０μのアクリル酸エステル供重合
体樹脂、すなわち、日本合成化学工業、株式会社製商品
名コーポニール７重量喝と、（Ｃ）分数剤として、アニ
オン活性剤のナフタリン・スルホン酸曹ホルムアルデヒ
ド縮金物、すなわち、花王アトラス株式会社製商品名デ
モールＮ２重量％と、（ｄ）離水剤としてす７テン酸カ
ルシウム、すなわち、大日本インキ化学工業株式会社製
商品名Ｏａ −Ｎａｐｈｔｈｅ−ｎａｔｅ ８重ＪＩｋ
％と、（ｅ）水６８重ｉｔ％とを混合（ａ ＋ ｂ 十
、Ｃ十ｄ＋ｅ）し、ボールミルにて均一に溶解分散せし
めた見掛比重１゜２１、粘度１８ボイズの懸濁液を得た
。この懸濁液を表面温度が６０°Ｃのマンドレルバ−に
スプレーにて塗布したところ短時間にて厚さ２８０Ｐの
乾燥した黒鉛フィルムが得られた。もちろん乾燥した黒
鉛フィルムは耐水性に優れており、接着性も十分であっ
た。摩擦係数は０．０７であった。Example 5 (a) 20% by weight of graphite powder with a particle size of 0.1 to 50/'' and (b) an acrylic acid ester donor polymer resin with a particle size of 1 to 50 microns, i.e. manufactured by Nippon Gosei Kagaku Kogyo Co., Ltd. Coponil 7 (trade name), (C) fractional agent, naphthalene sulfonate formaldehyde condensate as an anionic activator, namely, Kao Atlas Co., Ltd. trade name Demol N2% by weight, and (d) as a water-repelling agent. Calcium Naphthenate, namely, Dainippon Ink & Chemicals Co., Ltd., trade name Oa-Naphthe-nate 8-layer JIk
% and (e) 68 wt. Obtained. When this suspension was sprayed onto a mandrel bar having a surface temperature of 60 DEG C., a dry graphite film with a thickness of 280 P was obtained in a short time. Of course, the dried graphite film had excellent water resistance and sufficient adhesion. The friction coefficient was 0.07.
例えば、シームレス鋼管の圧延用に好適な効果が得られ
る。For example, effects suitable for rolling seamless steel pipes can be obtained.
実施例６
（ａ）粒度０．１〜５ｏＰの黒鉛粉末８５重蓋囁と、（
ｂ）粒度１〜５０Ｐのポリエチレン樹脂、すなわち、製
鉄化学株式会社製商品名フローセン５重鰍鳴と、（Ｃ）
分散剤としてメチルセルロース、すなわち松本油脂製薬
株式会社製商品名マーボローズＭ −６００８重量囁と
、Ｕ）Ｉｌｌ水剤としてオクチル酸カルシウム、すなわ
ち、大日本インキ化学工業株式会社製商品名カルシウム
オクトエート（ｃａ −ｏｃｔｏａｔｅ）２重量優と、
＜６）水５５重ＩＩｋ％とを混合（ａ十す十Ｃ＋ｄ＋ｅ
）し、ボールミルにて均一に溶解分散せしめた見掛比重
１．２５、粘度８５ボイズの懸濁液を得た。この懸濁液
を表面温度か８０°Ｃのマンドレルバ−にスプレーにて
塗布したところ短時間にて＊ぎ４００Ｐの乾燥した黒鉛
フィルムが得られた。もちろん乾燥した黒鉛フィルムは
耐水性に優れており、接着性も十分であった。摩擦係数
は０．０６であった。例えば、シームレス鋼管の圧延用
に好適である。Example 6 (a) 85 layers of graphite powder with a particle size of 0.1 to 5oP and (
b) A polyethylene resin with a particle size of 1 to 50P, i.e., product name Flocene 5-fold Ajimei manufactured by Tetsutsu Kagaku Co., Ltd., and (C)
As a dispersing agent, methylcellulose (trade name: Marborose M-6008, manufactured by Matsumoto Yushi Pharmaceutical Co., Ltd.) was used, and as a U)Ill solution, calcium octoate (trade name, calcium octoate (ca.), manufactured by Dainippon Ink and Chemicals Co., Ltd. -octoate) 2 weight Yu,
<6) Mix 55wt IIk% of water (a ten su ten C + d + e
) and uniformly dissolved and dispersed in a ball mill to obtain a suspension having an apparent specific gravity of 1.25 and a viscosity of 85 voids. When this suspension was sprayed onto a mandrel bar whose surface temperature was 80 DEG C., a dry graphite film of 400 P was obtained in a short time. Of course, the dried graphite film had excellent water resistance and sufficient adhesion. The friction coefficient was 0.06. For example, it is suitable for rolling seamless steel pipes.
実施例７゜
（ａ）粒度０．１〜５０Ｐの黒鉛粉末１５重量囁と、（
ｂ）粒度１〜５０Ｐのポリプロピレン樹脂、スなわち、
三井東圧化学株式会社製商品名三井ノーブレン６重量優
と、（Ｃ）分散剤として非イオン界面活性剤のポリオキ
シエチレンアルキルエーテル、すなわち、花王石鹸株式
会社製商品名エマルゲン１．５クネート（ＤＩ（３ＮＡ
ＴＥ） Ｏａ ２．５重量％と、（ｅｌ）水７５重量僑
とを混合（ａ＋ｂ＋ｃ＋ｄ＋ｅ ）Ｌ、、ボールミルに
て均一に溶解分散せしめた見掛比重１．１４゜粘度２．
０ボイスの懸濁液を得た。この−濁液を表ｉ［１＆が８
０℃のマンドレルバ−にスプレーにて塗布したところ短
時間にて厚さ９０／−Ｌの乾燥した黒鉛フィルムが得ら
れた。もちろん乾燥した黒鉛フィルムは耐水性に優れて
おり、接着性も十分であった。摩擦係数は０．０８であ
った。例えば、シームレス鋼管の圧延用に好適である。Example 7゜(a) 15% of graphite powder with a particle size of 0.1 to 50P and (
b) polypropylene resin with a particle size of 1 to 50P, i.e.
Mitsui Noblen 6 Weight Yu (trade name, manufactured by Mitsui Toatsu Chemical Co., Ltd.) and (C) polyoxyethylene alkyl ether, a nonionic surfactant as a dispersant, namely, Emulgen 1.5 Cunate (trade name, manufactured by Kao Soap Co., Ltd.) (DI). (3NA
TE) 2.5% by weight of Oa and 75% by weight of (el) water were mixed (a+b+c+d+e)L, and uniformly dissolved and dispersed in a ball mill to give an apparent specific gravity of 1.14° and a viscosity of 2.
A suspension with 0 voices was obtained. This cloudy liquid is expressed as i [1 & is 8
When applied by spraying onto a mandrel bar at 0°C, a dry graphite film with a thickness of 90/-L was obtained in a short time. Of course, the dried graphite film had excellent water resistance and sufficient adhesion. The friction coefficient was 0.08. For example, it is suitable for rolling seamless steel pipes.
実施例８
前記実施例１の（ｂ）酢酸ビニル共重合体樹脂の代りに
、ポリビニルアルコール樹脂、すなわち、日本合成化学
工業株式会社製商品名ゴー七ノールを用い、ボールミル
にて均一に溶解分散せしめた見掛比重１．１ｇ 、粘度
８．１ポイズの懸濁液を得た。Example 8 In place of the vinyl acetate copolymer resin (b) in Example 1, a polyvinyl alcohol resin, namely Go-Sevenol, a trade name manufactured by Nippon Gosei Kagaku Kogyo Co., Ltd., was used and uniformly dissolved and dispersed in a ball mill. A suspension having an apparent specific gravity of 1.1 g and a viscosity of 8.1 poise was obtained.
この懸濁液を用いて表面温度１００℃のマンドレルバ−
にスプレーにて塗布したところ短時間にて厚さ７０μの
乾燥した黒鉛フィルムが得られた。Using this suspension, a mandrel bar with a surface temperature of 100°C was prepared.
When applied by spraying, a dry graphite film with a thickness of 70 μm was obtained in a short time.
もちろん乾燥した黒鉛フィルムは耐水性に漬れて
１おり接着性も十分であった。摩擦係数はＯ，ＯＳで
あった。例えば、シームレス鋼管の圧延用に好適である
〇
実施例９
前記実施例２のΦ）酢酸ビニル共重合体樹脂の代りに、
メタクリル樹脂、すなわち、三菱レイヨン株式会社製商
品名アクリコンを用いてボールミルにて均一に溶解分散
せしめた見掛比重ｔ、２７、粘度２８ボイズの懸濁液を
得た。この懸濁液を用いテ表１７１度１ ｏ ｏ℃のマ
ンドレルバく−にスプレーにて塗布したところ、短時間
にて厚さ８８０Ｐの乾燥した黒鉛フィルムが得られた。Of course, the dried graphite film is soaked in water resistance.
1, the adhesion was also sufficient. The friction coefficient was O, OS. For example, it is suitable for rolling seamless steel pipes. Example 9 Instead of Φ) vinyl acetate copolymer resin in Example 2,
A suspension having an apparent specific gravity t of 27 and a viscosity of 28 boids was obtained by uniformly dissolving and dispersing a methacrylic resin, ie, Acricon (trade name, manufactured by Mitsubishi Rayon Co., Ltd.) in a ball mill. When this suspension was applied by spraying onto a mandrel vacuum at a temperature of 171° C., a dry graphite film with a thickness of 880 P was obtained in a short period of time.
もちろん乾燥した黒鉛フィルムは耐水性に優れており、
接着性も十分であった。摩擦係数は０．０７であった。Of course, dried graphite film has excellent water resistance.
Adhesion was also sufficient. The friction coefficient was 0.07.
例えば、シームレス鋼管の圧延用に好適である。For example, it is suitable for rolling seamless steel pipes.
実施例１０
前記実施例９のΦ）メタクリル樹脂の代りに、メタクリ
ル−スチレン共重合体樹脂、すなわちダイセル化学工業
株式金社製商品名セビアンーＭＡＳヲ用いて、ボールミ
ルにて均一に、溶解分散せしめた見掛比重１．２７、粘
度２６ボイスの懸濁液を得た。この懸濁液を用いて表面
温度１００℃のマンドレルバ−にスプレーにて塗布した
ところ知時間にて厚さ８１０Ｐの乾燥した黒鉛フィルム
が得られた。もちろん乾燥した黒鉛フィルムは耐水性に
優れており、接着性も十分であった。摩擦係数は０．０
７であった。例えば、シームレス鋼管の圧延用に好適で
ある◇
特許出願人 日本黒鉛工業株式会社Example 10 In place of the methacrylic resin (Φ) in Example 9, a methacrylic-styrene copolymer resin, namely Sevian-MAS (trade name, manufactured by Daicel Chemical Industries, Ltd.), was used and uniformly dissolved and dispersed in a ball mill. A suspension having an apparent specific gravity of 1.27 and a viscosity of 26 voices was obtained. This suspension was applied by spraying onto a mandrel bar with a surface temperature of 100 DEG C., and a dry graphite film with a thickness of 810 P was obtained within a certain period of time. Of course, the dried graphite film had excellent water resistance and sufficient adhesion. Friction coefficient is 0.0
It was 7. For example, it is suitable for rolling seamless steel pipes ◇ Patent applicant Nippon Graphite Industries Co., Ltd.
Claims (1)
ｉｓと、（ｂ）粒度１〜５０Ｐの酢酸ビニル共重合体樹
脂、グラフト化デンプン、エステル化デンプン、エチレ
ン−酢酸ビニル−塩化ビニル三元共重合体樹脂、アクリ
ル酸エステル共重合体樹脂、ポリエチレン樹脂、ポリプ
ロピレン樹脂、スチレン共重合体樹脂、ポリビニルアル
コール樹脂、メタクリル醸樹脂、メタクリル酸−スチレ
ン共重合体樹脂等の群から選ばれる少なくとも１種の樹
脂粉末１〜１５重量弔と、（Ｃ）非イオン活性剤、アニ
オン活性剤、カルボキシメチルセルロース、メチルセル
ロース、エチルセルロース等の分１［ＦＪｏ、１〜８重
量囁と、さらにｆｄ）ナフテン酸コノくルト、ナフテン
酸亜鉛、ナフテン酸カルシウム、オクチル酸亜鉛、オク
チル酸カルシウム、ネオ酸カルシウム等の離水剤０．１
〜８重＠＊とを、（８）水４５〜９５重量優に混合（（
ａＪ ＋（ｂ） ＋ （０） ＋（ｄＪ＋（ｅＪ）Ｌ、
ボールミル等を用い温式にて均一に溶解分散せしめて成
る見掛は比重１．０〜１．８、粘度０．１〜１００ポイ
ズを有することを特徴とするマンドレルバー１ｍｌ ？
ｉｌ 剤。L (~graphite powder with particle size 0.1~50P-5~45 weight i
is and (b) vinyl acetate copolymer resin with a particle size of 1 to 50P, grafted starch, esterified starch, ethylene-vinyl acetate-vinyl chloride terpolymer resin, acrylic ester copolymer resin, polyethylene resin , polypropylene resin, styrene copolymer resin, polyvinyl alcohol resin, methacrylic resin, methacrylic acid-styrene copolymer resin, etc., and (C) non-ionic resin powder of 1 to 15% by weight. activators, anionic activators, carboxymethylcellulose, methylcellulose, ethylcellulose, etc. [FJo, 1 to 8 wt. Water releasing agents such as calcium, neoacid calcium, etc. 0.1
~8 weight@* and (8) 45 to 95 weight of water ((
aJ + (b) + (0) + (dJ + (eJ)L,
1 ml of mandrel bar characterized by having an apparent specific gravity of 1.0 to 1.8 and a viscosity of 0.1 to 100 poise, which is obtained by uniformly dissolving and dispersing it in a hot manner using a ball mill or the like.
IL agent.