JPS58136480A - Recording medium - Google Patents
Recording mediumInfo
- Publication number
- JPS58136480A JPS58136480A JP57019210A JP1921082A JPS58136480A JP S58136480 A JPS58136480 A JP S58136480A JP 57019210 A JP57019210 A JP 57019210A JP 1921082 A JP1921082 A JP 1921082A JP S58136480 A JPS58136480 A JP S58136480A
- Authority
- JP
- Japan
- Prior art keywords
- ink
- receiving layer
- recording medium
- support
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
本発明はインクの黴小液１ｉＩ４を飛翔させて、文字、
画ｇ／ＩＩを形成するインクジェット記録用媒体に関す
るものであり、特に多色記録で文字、画＊ｔ−形成する
のに適したインクジェット記録用媒体に関するものであ
る。DETAILED DESCRIPTION OF THE INVENTION The present invention is capable of printing letters, letters, etc. by flying small mold liquid 1iI4 of ink.
The present invention relates to an inkjet recording medium for forming images G/II, and particularly to an inkjet recording medium suitable for forming characters and images in multicolor recording.
近勢、インクジェット方式は、高速、高解像度、−低騒
音であシ、多色化が軽易でＴｏシ、記録パターンの一通
性が大きく、更に現像、定着が不要である等を特徴とし
て、漢字をはじめ、種々のカン−図形情報のハードコピ
ー、その他多くの用途に於ｉて急速に普及してｉる０更
に各種のインク液が使えること及び記録パターンの融通
性が太きｉことを利用して多色印刷やカラー写真像に代
る用途、例えにポスター等の分野Ｋｔで応用する試みが
為されている。The modern inkjet method is characterized by high speed, high resolution, low noise, easy multicolor printing, high consistency of recording pattern, and no need for development or fixing. It is rapidly becoming popular in many other applications, including hard copying of various cans and graphic information, and also takes advantage of the fact that various ink liquids can be used and the flexibility of recording patterns is high. Attempts have been made to apply this method to applications in place of multicolor printing and color photographic images, such as posters.
一般の印刷に使用される上質紙やコーテツド紙及び写真
のベース等に使用されるバライタ紙やレジンブーテッド
紙はインクの吸収性が着しく劣る丸め、これらを記録媒
体Ｋｖ！用し九場合インクジェット記録終了後もインク
が長時間表面に残〉、装置の−１１に触れた如、取扱い
看が触れたフ、゛連続して排出されたシートが重なりた
ヤして、記録面がこすられた場合、表面に残留している
インクでせっかく形成した画像が汚れる０又、多色記録
で社同−面に２色以上のインクが重なることがア）、イ
ンクドツト密度が高くなりた部分では、インクが吸収さ
れないまま混合して色彩性が低下したシ、或は流れ出す
などの問題があに実用性がない。更に水性インク等で形
成されたｊ像は光沢が不足し、水等がかかった場合再び
溶出したジして、ポスターの如く外気に曝される場合と
か、保存すること七前提としている写真用途などでは不
満足なものである。High-quality paper and coated paper used for general printing, and baryta paper and resin-booted paper used for photographic bases, etc., have poor ink absorption properties and are rolled up, so these are used as recording media Kv! If the ink remains on the surface for a long time even after the inkjet recording is finished, and if the handling device touches the -11 of the device, the continuously ejected sheets may overlap, causing the recording to fail. If the surface is rubbed, the ink remaining on the surface will smear the formed image.Also, in multicolor recording, two or more colors of ink may overlap on the surface (a), and the ink dot density will increase. In such areas, the ink may be mixed without being absorbed, causing problems such as decreased color quality or flow, which is impractical. In addition, images formed with water-based inks lack gloss, and if exposed to water, they may dissolve again, making them difficult to use when exposed to the outside air like posters, or for photographic applications that require preservation. That is unsatisfactory.
これらの問題を解決するために、従来からいくつかの提
案がなされてきた。例えば％開陥５５−５３５９１号に
は、金属の水溶性塩が記録の行われる表ｍＫ付与されて
ｉる記録紙が開示されている。また、％−紹５６−８４
９９２号にはポリカチオン高分子電解質を表面に含有す
る記録媒体に、水溶性の直接染料又は酸性染料を含有す
る水性インクで印写するインクジェット記録方法が開示
されている。さらに、％開開５５−１５０３９６号には
水性インクによジインクジエツト記録後、該水性インク
中の染料としてレーキを形成する耐水化剤を付与するイ
ンクジェット記録の耐水化法が、％開開５６−５８８６
９号には水溶性高分子を塗布したインク２エツト記録シ
ートに水性インクによジインクジエツト記録後、販水溶
性＾分子を不溶化する耐水化剤を付与するインクジェッ
ト記録シーＦの耐水化方法が、それぞれ開示されている
。Several proposals have been made to solve these problems. For example, Patent No. 55-53591 discloses a recording paper on which a water-soluble salt of a metal is added on the surface mK on which recording is performed. Also, %-Shao 56-84
No. 992 discloses an inkjet recording method in which printing is performed on a recording medium containing a polycationic polymer electrolyte on the surface with an aqueous ink containing a water-soluble direct dye or an acidic dye. Further, %Kaikai 55-150396 discloses a method for making inkjet recording water resistant by applying a water-resistant agent that forms a lake as a dye in the water-based ink after diinkjet recording with water-based ink.
No. 9 describes a method for making inkjet recording sheet F water resistant, which involves applying a water resistant agent that insolubilizes water-soluble molecules after di-ink jet recording with water-based ink to a two-jet recording sheet coated with a water-soluble polymer. Disclosed.
更に、特開昭５５−１５０３７０号には合成パルプ紙に
インクジェット記録後、該合成パルプ紙の熱処理によシ
合成バルグｔ−ｍ融するインクジェット記録方法が、開
示されている。Further, JP-A-55-150370 discloses an inkjet recording method in which after inkjet recording on synthetic pulp paper, synthetic bulk t-m is melted by heat treatment of the synthetic pulp paper.
）ｉ１！に、特開昭５５−６１４９４号には紀―緘体表
面上に印画用インクを用いて形成した１１１ｍに１、ト
ナーを付着させるノンインパクト記録方法が開示されて
いる。史に特開昭５５−１１８２９号には２層以上のイ
ンク吸収層を設けた不透明度が５５．０〜９７．５−で
あるインクジェット記録用シートが開示されている。)i1! Furthermore, Japanese Patent Application Laid-Open No. 55-61494 discloses a non-impact recording method in which toner is deposited on every 111 m formed on the surface of a printing ink using printing ink. Historically, Japanese Patent Application Laid-Open No. 11829/1982 discloses an inkjet recording sheet having two or more ink absorbing layers and having an opacity of 55.0 to 97.5.
しかしながら、特開昭５５−５３５９１号、特開昭５６
−８４９９２号及び特開昭５５−１５０３９６号尋に代
表される技術思想は配録紙中に含まれた物質又はインク
シェド記録後に付与される物質でインク中の染料を難溶
性にすることで耐水性を得ようとするもので、ある程度
の改良は、得られるものの充分満足で舊るものではない
〇又、特開昭５５−１５０３７０号、特ｌ！！昭５６−
５８８６９号等にみられる技術思想はインクシェド記録
後、インク受理面そのものを耐水性にして、目的とする
耐水性や表面光沢金得ようとするもので、インクジェッ
ト記録後に定着工程を会費とし、工程管複雑にしている
。更に特開昭５５−６１４９４号等にみられる技術思想
は水性インクを他の溶料などに置きかえることで耐水仏
光沢等を得ようとするものであるが、これも−棟の現像
、定着工程と考えられインクジェット記録の％徴である
簡島性を減少させている。それ故、これらの問題を解決
した、先に述べた如き特性をかねそなえた記録用シート
が要望されてい次。However, JP-A-55-53591 and JP-A-56
-84992 and JP-A-55-150396, the technical idea is to make the dye in the ink poorly soluble with a substance contained in the recording paper or a substance applied after inkshed recording, thereby achieving water resistance. Although some improvement is obtained, it is not enough to give up.Also, JP-A-55-150370, special feature! ! 1972-
The technical concept seen in No. 58869 and others is to make the ink receiving surface itself water resistant after inkjet recording to achieve the desired water resistance and surface gloss. It's making it complicated. Furthermore, the technical idea found in Japanese Patent Application Laid-open No. 55-61494 and others attempts to obtain water-resistant gloss by replacing water-based ink with other solvents, but this also involves the development and fixing processes of the ridges. This is thought to reduce the simplicity, which is a characteristic of inkjet recording. Therefore, there is a need for a recording sheet that solves these problems and has the characteristics mentioned above.
不発ｕＡ（Ｄｉつの目的はインク吸収性が良好で、解１
度が高く、色再塊性及び着色ａ度が良好な多色インクジ
ェット記録１１ｉ−を得る方法を提供することである。Unexploded uA (Di purposes is good ink absorption, Solution 1
It is an object of the present invention to provide a method for obtaining multicolor inkjet recording 11i- which has a high color re-agglomeration property and a good color a degree.
本発明の一′）１つの目的はインクジェット記録後、特
別な操作をすることなしに耐水性で光沢のめるｍｌ録−
＊に得る方ａｔ提供することである。1') One object of the present invention is to provide ML recording with water resistance and gloss without any special operations after inkjet recording.
*It is to provide at the person who obtains.
これらの目的は、インクジェット記録用シートとして透
ｕＡなシ゛−ト状支持体の片側に屈折率１５８以下のｌ
ｌｌ１料を主成分とするインク受壇層を設けた記録媒体
を用いることによって達成された０
却９、本発明によれｕ１インクジェット石インクを受縁
シートに噴射して記−縁を得るインクジェット記録方法
に於いて、骸受像シートが、少くとも一階の、インクｔ
ｌｉ理し＆透させ、保持するインク受理層を有し、該イ
ンク受理層が屈折率１．５８以下の主顔料からな〕、透
明な支持体表面に隣接して設妙られてｉるインジェット
記録用媒体が提供される。また本発明によれば透明な支
持体に隣接する鋏インク受理層に浸透したインクにより
て形成されたｌｋｉｇＩｔ透明支持体側から視ることを
４＄１［とするインタジェット記録用媒体が提供される
。These objectives were to use lubricants with a refractive index of 158 or less on one side of a transparent uA sheet-like support as an inkjet recording sheet.
Inkjet recording achieved by using a recording medium provided with an ink holder layer containing ll1 material as a main component. In the method, the image-receiving sheet has at least one layer of ink t.
The ink-receiving layer is made of a main pigment having a refractive index of 1.58 or less, and is designed adjacent to the transparent support surface. A jet recording medium is provided. Further, according to the present invention, there is provided an interjet recording medium which is formed by ink that has permeated into the scissors ink receiving layer adjacent to the transparent support and has a cost of 4 $1 when viewed from the side of the transparent support. .
透明支持体に隣接する、インク受理層は、皺インク受理
層Ｋｔで浸透して来た染料を隠蔽することの少な１１屈
接率１．５８以下の顔料を主成分とし接着剤等で透明支
持体上に設けた層であるＯ
本発明の記録用媒体に、インクジェット用インクを噴射
すると、インクは、インク受理層の空１１に浸透し、屈
折率１５８以下の顔料を主成分とする透明支持体に隣接
するインク受理層に到達し保持されて、−像を形成する
〇
従来はインクを噴射し、記録画像を得るインクジェット
船鱈方法に於いて、インクを噴射した側から記録ｌｉｉ
像を視ていた九めに、インクの吸収能力をあげればイン
クが深く浸透することによって色調の冴えが低下し、又
、インクが表面に多く留る様にすると吸収能力が不足す
る九め、これらのバランスをとることによって、用途（
−会せたインクジェット適性を確保するか、インク中の
染料とビヒクルを分離して吸着する能力を持つ塗層を設
ける等の方法が行われて自た。本発明に於いては、イン
クを深く浸透させて透明支持体に隣接するインク受理層
にまで到達したインクによって形成されたＩＩｊ像を透
明な支持体を透して視ると云う、従来いわゆる″記録シ
ートの裏側に相尚する部分ｔｅａとすると云う発想によ
りて、従来深く浸透してしまう染料をいかに表面に留め
るかに腐心した努力から解放されたために、Ｉ＆表層の
インク吸収能力は充分に付与出来、しかも吸収能力が高
い揚重発明に適している。又記録画像は支持体側を表面
として視る九め光沢に優れ、耐水性に優れている。The ink-receiving layer adjacent to the transparent support is transparently supported with an adhesive, etc., and is mainly composed of a pigment with a refractive index of 1.58 or less, which hardly hides the dye that penetrates into the wrinkled ink-receiving layer Kt. When inkjet ink is injected onto the recording medium of the present invention, the ink penetrates into the void 11 of the ink-receiving layer, and the transparent support is composed mainly of a pigment with a refractive index of 158 or less. It reaches the ink-receiving layer adjacent to the body and is retained, forming an image. Conventionally, in the inkjet method of ejecting ink and obtaining a recorded image, recording is performed from the side from which the ink is ejected.
As I was looking at the image, I realized that if you increase the ink absorption capacity, the ink will penetrate deeper and the tone will become less vivid, and if you allow more ink to stay on the surface, the absorption capacity will be insufficient. By balancing these, the application (
- Methods have been taken to ensure inkjet suitability, or to provide a coating layer that has the ability to separate and adsorb the dye and vehicle in the ink. In the present invention, the ink is penetrated deeply and the IIj image formed by the ink that has reached the ink receiving layer adjacent to the transparent support is viewed through the transparent support, which is conventionally known as " The idea of creating a tea portion that corresponds to the back side of the recording sheet frees us from the painstaking efforts to keep the dye, which previously penetrates deeply, on the surface, giving the I&surface layer sufficient ink absorption ability. Moreover, the recorded image has excellent gloss when viewed from the support side as the surface, and is excellent in water resistance.
本発明に於いては上述の如く、インク受理層に噴射され
たインクを吸収、浸透させ、屈折率１５８以下の顔料か
らなるインク受理層に到達したＩｉｉ像を支持体側から
視る関係上、画像は鏡像となる。従りて、正像の記録像
を形成するためにインク受塩層に噴射する画像自体ｔ−
鏡像にしておく必要がある。In the present invention, as described above, the ink jetted into the ink-receiving layer is absorbed and permeated, and the image III that has reached the ink-receiving layer made of a pigment with a refractive index of 158 or less is viewed from the support side. becomes a mirror image. Therefore, the image itself t-
It needs to be a mirror image.
最表層が本＠明で云う透明支持体に隣接するインク受塩
層である場合には、つｔｂインク受理層が一層で構成さ
れる場合には、鋏インク受理層を構成する顔料の屈折率
１．５８以下であることが必要である。又、インク受塩
層が２層以上の層構成で成る場合には、蝦下層つｔｅ透
明支持体に隣接する層の主顔料は屈折率１．５８以下で
あることが必要であるが、それ以外の層線顔料の屈折率
に留意する必要はなく、吸収能力、解像性、白色度、不
透明度と云った別の性能を付与することも可能である。When the outermost layer is an ink-receiving layer adjacent to the transparent support as referred to in this @mei, and when the ink-receiving layer is composed of one layer, the refractive index of the pigment constituting the ink-receiving layer is It is necessary that it is 1.58 or less. In addition, when the ink salt-receiving layer is composed of two or more layers, the main pigment in the layer adjacent to the transparent support must have a refractive index of 1.58 or less; There is no need to pay attention to the refractive index of the layered pigment other than that, and it is also possible to impart other properties such as absorption capacity, resolution, whiteness, and opacity.
特に屈折率１．５８以下の顔料で形成されるインク受塩
層の上に設けられる層は白く、不透明な程好ましく、通
常白色度で６０％以上、特に好ましくは７〇−以上であ
る〇更に全体として不透明な程画像が冴えるため支持体
側から一１定し次白色度が６０％以下にならない限ｐ最
上層を着色インキ受理層とすることも可能である。In particular, the layer provided on the ink salt-receiving layer formed of a pigment with a refractive index of 1.58 or less is preferably whiter and more opaque, and usually has a whiteness of 60% or more, particularly preferably 70% or more. Since the more opaque the overall image, the clearer the image, it is also possible to use the uppermost layer as a colored ink-receiving layer, as long as the whiteness does not become less than 60% after constant whiteness from the support side.
透明支持体に隣接するインク受理層の主顔料社旗折皐を
１，５８以下とすることが必要でＴｏシ、その理由は本
発明の、透明支持体側から、鋏インク受理層に形成され
実画像を視ることに起因している。つｇインク受理層中
に浸透して来たインクは、蛾下層である透明支持体に隣
接する屈接亭１．５８以下の主顔料からなる層に到達し
て、保持され画１ａを形成する。この時顔料の隠蔽力が
強い程、つまり屈折率がｉ％−程、透明支持体を透して
視る画像は色ｖ４０冴えがなくなり、色再現性が低下す
ることになる。It is necessary to make the main pigment size of the ink-receiving layer adjacent to the transparent support 1.58 or less. This is caused by viewing images. The ink that has permeated into the ink-receiving layer reaches the layer consisting of the main pigment with a diameter of 1.58 or less adjacent to the transparent support, which is the lower layer, and is retained to form the image 1a. . At this time, the stronger the hiding power of the pigment, that is, the higher the refractive index is i%, the less vivid the image viewed through the transparent support, and the lower the color reproducibility.
本発明で云うインク受理層とはインク受理層真向に噴射
され付着したインク滴を微小の空−によって吸収するこ
との出来る、主として顔料及び接着剤よ〕なる支持体上
に設けられた塗層を云う。更に支持体に隣接するインク
受理層とは、上記インク受理層が一層以上の層構造がら
なｐ、その最下層、つｔ６支持体に一番近い側の層を云
う。該インク受理層が一層から成る場合は、その一層が
支持体に隣接するインク受理層である。The ink-receiving layer referred to in the present invention is a coating layer provided on a support (mainly made of pigment and adhesive) that is capable of absorbing ink droplets that are sprayed directly in the direction of the ink-receiving layer and adhered thereto by means of minute voids. says. Further, the ink-receiving layer adjacent to the support means the layer in which the ink-receiving layer has a layer structure of more than one layer, the lowest layer thereof, and the layer closest to the support. When the ink-receiving layer is composed of layers, one of the layers is the ink-receiving layer adjacent to the support.
本発明で使用する屈折率１．５８以下の顔料としては、
メルク、炭酸カルシウム、硫酸カルシウム、水酸化マグ
ネシウム、塩基性炭＃１グネシクム、アル々す、合成シ
リカ、ケイ酸カルシウム、珪藻土、水酸化アル１−りム
、尿素樹脂、グラスチックピグメント等があシ、好まし
くは屈折率１．５５以下のケイ酸カルシウム、塩基性炭
酸マ！ネシクム、珪藻土、合成シリカ等である。Pigments with a refractive index of 1.58 or less used in the present invention include:
Merck, calcium carbonate, calcium sulfate, magnesium hydroxide, basic carbon #1 gnesicum, alrus, synthetic silica, calcium silicate, diatomaceous earth, aluminum hydroxide, urea resin, glass pigment, etc. , preferably calcium silicate with a refractive index of 1.55 or less, basic carbonate ma! These include nesicum, diatomaceous earth, and synthetic silica.
本発明で云う合成シリカとは、四塩化ケイ素の熱分解、
ケイ績す）ＩＪｔムの歌、二酸化炭素、アン毫ニウム塩
などによる複分解沈澱生成物等のいわゆるホワイトカー
ボン、ケイ酸ナトリクムの鍍などによる熱分解中イオン
交換樹脂層を通して得られるシリカゾル又はこのシリカ
ゾルを加熱熟成して得られるコロイダルシリカ、シリカ
ゾルをゲル化させ、その生成条件をかえることによりて
数セリ擢クロンから数十ミリ電クロン位の一次粒子がシ
ロ＋１ン結合をした三次元的な二次粒子となり九シリカ
ゲル、頁にはシリカゾル、ケイ酸ナトリクム、アル電ン
酸ナトリクＪ等會出発智質として８０℃〜１２０℃で加
熱して生成し友いわゆ委合成モレキーラーシーブ等、二
酸化ケイ素を主体とする合成ケイ素化合物である。The synthetic silica referred to in the present invention refers to thermal decomposition of silicon tetrachloride,
The silica sol obtained through the ion exchange resin layer during thermal decomposition by the so-called white carbon, such as double decomposition precipitated products by carbon dioxide, ammonium salt, etc., by sodium silicate, etc. By gelling colloidal silica and silica sol obtained by heat aging and changing the formation conditions, three-dimensional secondary particles in which primary particles of a few tens of millielectrons are bonded are formed. The particles are 9 silica gel, and the page contains silica sol, sodium silicate, sodium alkyl J, etc. As a starting material, it is heated at 80°C to 120°C to produce so-called synthetic molecular sieves, etc., which contain silicon dioxide. It is mainly a synthetic silicon compound.
本発明では上記、屈折率１．５８以下の主顔料からなる
インク受理層のみでも目的を達することが出来るが、透
明なシーＦに咳インク受珈層を設けただけの記録用媒体
は不透明度が低く、裏側が透けて見えるため白地部の冴
えがなく、黒ずんで見える。それ故該インク受塩鳩の上
に更に白色インク受理層ｔａけて白色ｍｅｓｏ１以上、
好ましくは７０ｇ６以上とすることが望ましい。白色Ｊ
１６０−以上の白色インク受理層としては通常、紙のコ
ーティングに使われる白色顔料を用いることが出来る。In the present invention, the above-mentioned purpose can be achieved with only the ink-receiving layer made of the main pigment with a refractive index of 1.58 or less, but the recording medium in which only the ink-receiving layer is provided on the transparent sheet F has a low opacity. Because the color is low and the back side is transparent, the white background is dull and appears dark. Therefore, a white ink-receiving layer is further provided on the ink-receiving layer, and white meso1 or more is added.
Preferably it is 70g6 or more. white J
As the white ink-receiving layer of 160 or more, white pigments commonly used for coating paper can be used.
白色顔料として社、例えにクレー、メルク、炭酸カルシ
ウム、硫酸カルシウム、硫酸バリウム、酸化チタン、酸
化亜鉛、硫化亜鉛、サテンホワイト、けい酸アルオニり
ム、水酸化アルミニウム、酸化けい素、けい酸カルシウ
ム、けいそう±、リトポン、尿素ホルマリン樹脂、プラ
スチックビグメイト等が単独あるいは２種類以上の混合
物として使用される。特に炭酸カルシウム、酸化チタン
、酸化亜鉛、酸化けい素、尿素ホルマリン樹脂、グラス
チックピグメント勢が望ましい。Examples of white pigments include clay, Merck, calcium carbonate, calcium sulfate, barium sulfate, titanium oxide, zinc oxide, zinc sulfide, satin white, aluminum silicate, aluminum hydroxide, silicon oxide, calcium silicate, Kisou±, lithopone, urea-formalin resin, plastic bigmate, etc. are used singly or as a mixture of two or more types. Particularly desirable are calcium carbonate, titanium oxide, zinc oxide, silicon oxide, urea-formalin resin, and glass pigments.
更に螢光染料、着色染料等を少量添加し、よ〉白く見せ
ゐことも可能である。Furthermore, it is possible to add a small amount of fluorescent dye, colored dye, etc. to make it look even whiter.
又、白色インク受理層の上に、更に白色、黒色又は有色
の着色インク受理層を設けることも可能で６９、この場
合は支持体側から測定した白色度がｓｏｎ以下にならな
いようにすることで、−倣の鮮明な記鋒用媒体を得るこ
とが出来る。It is also possible to further provide a white, black, or colored colored ink receiving layer on the white ink receiving layer69, and in this case, by ensuring that the whiteness measured from the support side does not become less than son, - It is possible to obtain a recording medium with a clear imitation.
該増色インク受層層としては、上記白色インク受理層に
使用した顔料中、それらに着色染料、着色顔料を加えて
着色層としてもよいし、着色顔料、炭素粉末勢を単独で
使用することも可能である。The color-enhancing ink-receiving layer may be a colored layer by adding a colored dye or a colored pigment to the pigments used in the white ink-receiving layer, or a colored pigment or carbon powder may be used alone. is also possible.
本発明で云う白色度の測定は／−ンタ一式比色光度針を
用−でｆｆｌ８Ｐ８１２３の方法に従って行つた０即ち
、主波長４！＄１１１Ｉ−の實色フィルターを用い、Ｊ
ｊ定すべ龜試料は数枚用意し、重ね合せて＃ｊ定すると
自党が透漏せず１０Ｇ−反射するだけの枚数を重ねて、
支持体側に入射光線が鳴るように照射して測定される０
接着剤としては、例えば、酸化澱粉、エーテル化澱粉、
エステル化澱粉、デキストリン等の澱粉類、カルボキシ
メチルセルロース、ヒト−キシエチルセルレース等のセ
ルロース−導体、カゼイン、イツテン、大豆蛋白、ポリ
ビエルアルーール及び七の−導体、無水！レイン酸樹脂
、Ａ常のスチレン−ブタジェン共重合体、メチルメタク
リエートープタジエｙ共重合体等の共役ジエン系重合体
ラテックス、アクリル酸エステル及びメタクリル酸エス
テルの重合体又は共重合体勢のアクリル系重合体ラテッ
タス、エテレン酢酸ビール共重合体等のビニル系重合体
ラテックス、或はこれらの各゛種重合体のカルボ中シル
基等の宴能基含有単量体による盲能基変性重合体ラテッ
クス、メツ擢ン樹脂等の熱硬化合成＋Ｍ脂系縁着剤等が
用いられる。The measurement of whiteness as referred to in the present invention was carried out using a colorimeter set of colorimetric needles according to the method of ffl8P8123. Using a true color filter of $111I-, J
Prepare several samples, stack them together, and stack enough samples to reflect 10G without letting your own party see through.
Measured by irradiating the support side with an incident light beam. Examples of adhesives include oxidized starch, etherified starch,
Starches such as esterified starch and dextrin, cellulose-conductors such as carboxymethylcellulose and human-xyethylcellulose, casein, ittene, soybean protein, polyvinyl alcohol, and seven-conductors, anhydrous! Reic acid resin, conjugated diene polymer latex such as ordinary styrene-butadiene copolymer, methyl methacrylate-butadiene copolymer, acrylic ester polymer or copolymer of acrylic acid ester and methacrylic ester Vinyl-based polymer latex such as polymer latettas, ethylene acetate beer copolymer, or blind functional group-modified polymer latex with a monomer containing a functional group such as a syl group in the carboxyl group of each of these polymers, A thermosetting synthetic resin such as Metsu resin + M resin edge adhesive, etc. are used.
これらの接着剤は顔料１００部に対して２部〜３０部、
好ましくは５部〜２０部添加される。These adhesives are used in an amount of 2 to 30 parts per 100 parts of pigment.
Preferably 5 parts to 20 parts are added.
更に必要ならば顔料分散剤、増粘剤、流動変性剤、消泡
剤、抑泡剤、離鳳剤、着色削等を適宜配合することは特
性を損なわ壜い限り何ら差し支えない。Furthermore, if necessary, pigment dispersants, thickeners, flow modifiers, antifoaming agents, foam inhibitors, release agents, coloring removers, etc. may be added as appropriate, as long as the properties are not impaired.
本発明の塗工機としては、一般に顔料塗被紙の製造に用
いられているグレードコーター、エアーナイフコーター
、四−ルコーター、プラッシ島コーター、カーテンコー
ター、チャンルックスコーター、パーコーター、グラビ
アコーター勢いずれも適用出来る。The coating machines of the present invention include grade coaters, air knife coaters, four-wheel coaters, plush island coaters, curtain coaters, chunk coaters, per coaters, and gravure coaters that are generally used in the production of pigment-coated paper. Can be applied.
塗布後の乾燥は通常の乾燥方法、例えばガスヒーター、
電気ヒーター、蒸気加熱ヒーター、熱風加熱等の各種方
式で、乾燥して、慮布シート會作る。Drying after application is done using a normal drying method, such as using a gas heater,
Dry and create cloth sheets using various methods such as electric heaters, steam heating heaters, hot air heating, etc.
塗層は１回に必要量を設けてもよいし、又２回以上の重
ね塗）によって必要量とすることも可能である。The coating layer may be applied in the required amount at one time, or may be applied in the required amount by overcoating two or more times.
本発明で使用する支持体とは、セロファン、ガラス及び
熱可塑性合成樹脂フィルム岬が使用出来、熱可ｍ性樹脂
フィルムとしては、通常、ポリエステル、ポリスチレン
、ポリ塩化ビニル、ポリメチルメタクリレート、酢酸セ
ルー−ス等、透明なシートが用いられる。更にこれらの
シートとインク受理層との接着性を改養するため、コロ
ナ放電処理、その他の一般的な処理中、クリヤーな下引
ｍｅ設けることも可能である。この場合の下引層として
は透明な程望ましく、通常ゼラチン、ニトロセルロース
等の憫請層が用いられる。The support used in the present invention can be cellophane, glass, or a thermoplastic synthetic resin film. Examples of the thermoplastic resin film are usually polyester, polystyrene, polyvinyl chloride, polymethyl methacrylate, and cellulose acetate. A transparent sheet such as a transparent sheet is used. Furthermore, in order to improve the adhesion between these sheets and the ink-receiving layer, a clear undercoat can be provided during corona discharge treatment and other common treatments. In this case, the subbing layer is desirably transparent, and a subbing layer such as gelatin or nitrocellulose is usually used.
支持体に塗禎層會設けただけのシートは、平滑性に劣り
、インクジェットによる多色記録後のＩｍ像が今一つ見
栄えがしないｏしたがりて、前述のように塗布、乾燥後
、例えばスーツ（−カレンダー、グロスカレンダーなど
で加熱加圧下ロールエラグ間を通して表面の平滑性を与
えることによルインクジェット画摩の仕上）をよくする
ことも可能である０
以下に本発明の実施例を挙げて説明するがこれｂｏｔｎ
ｃ限定されるｔのではない。尚実施例Ｋ１１ｎで示す部
及びチは重量部及び重量−を意味する。A sheet simply provided with a coating layer on a support has poor smoothness, and the Im image after multicolor recording by inkjet does not look very good. Therefore, after coating and drying as described above, for example, a suit - It is also possible to improve the finish of inkjet embodies by imparting surface smoothness through the roll lag under heat and pressure using a calendar, gloss calender, etc. The present invention will be explained below with reference to examples. This is botn
c not limited to t. Note that parts and parts in Example K11n mean parts by weight and -.
以下に実施ガ中の諸物性値の測定方法を示す０（１）イ
ンクＷｋ収速度
インクジェット用水性インクのインク滴ｏ、ｏｏｏａ＊
ｔ−ｔ＆面に付着させ次瞬間から全部が吸収される壜で
の時間′に顕＊−下で一１定しだ０（秒）
（２）色彩性
シアン、マゼンタ、イエロー、ブラックの４色の水性イ
ンクをインクジェット装置で印字したものについて、そ
の色Ｏ鎖［を支持体−からサクラデンシトメーターアＤ
ム４Ｓで測定し良。Ink droplets o, oooa* of water-based ink for inkjet 0(1) Ink Wk Yield
It is attached to the t-t surface and from the next instant it is completely absorbed in the bottle. The water-based ink was printed using an inkjet device, and the color O chain [was transferred from the support to the cherry densitometer D].
Measured with 4S and found good.
（３） 白色度
ハンタ一式比色光度計を用いてＪｌ！１Ｐ８１２３の方
法に従りて、記録用媒体の支持体側から測定した０
実施例１
コロナ処１ｉｔｕた７５＃ｍのポリエステルフィルムに
、ホリビ：ｒ−〃アルコール１５部、コロイダルシリカ
（屈折率１．４！＄）１００部よｐなる固型分２０ｇ４
の塗布液を固型分で片面１５〜９になるようにエアーナ
イフコーターで塗布した。これを実施例１０記録用媒体
とし＊、Ｏ
実施例２
実施例１の配録用媒体Ｏインク受理層の上に、酸化チタ
ン１００部、ポリビニルアル；−ル１０部よりなる固型
分２０１６の塗布液を固型分で９１７Ｑになるようにエ
アーナイフコーターで塗布して実施例２の記録用媒体と
じ危。(3) Whiteness Jl! using a Hunter set colorimetric photometer! Example 1 A corona-treated 75#m polyester film was coated with 15 parts of Horibi:r- alcohol and colloidal silica (refractive index 1.4). !$) 100 parts p solid content 20g4
The coating liquid was applied using an air knife coater so that the solid content was 15 to 9 on one side. This was used as a recording medium in Example 10. *Example 2 A solid component 2016 consisting of 100 parts of titanium oxide and 10 parts of polyvinyl alcohol was added on the ink-receiving layer of the recording medium of Example 1. The coating solution was coated with an air knife coater so that the solid content was 917Q, and the recording medium of Example 2 was bound.
実施例３
実施例１の記録用媒体のインタ受理層の上に尿素ホルム
アルデヒドＩＩ［１ｌ１００部酸化澱粉１０部よｐなる
固皺分１５−の塗布液を固振分で３１７ｄになるように
エアーナイフコーターで塗布して、実施例３の記録用媒
体とした。Example 3 On the interreceptive layer of the recording medium of Example 1, a coating solution of urea formaldehyde II [1 l, 100 parts, 10 parts of oxidized starch, p] was applied with an air knife so that the solid content was 317 d. The recording medium of Example 3 was obtained by coating with a coater.
実施例４
実施例２の記録用媒体のインク受理層の上に更に、炭酸
カルシウム８０部、カーボンブラック２０部、ポリビニ
ルアルコール８部よりなる塗布液を固蓋分で３１／−に
なるようにエアーナイフコーターで塗布して実施例４の
記録用媒体とした。Example 4 A coating solution consisting of 80 parts of calcium carbonate, 20 parts of carbon black, and 8 parts of polyvinyl alcohol was further applied to the ink receiving layer of the recording medium of Example 2 by air to make the solid lid ratio 31/-. The recording medium of Example 4 was obtained by coating with a knife coater.
実施例５
平均粒径２０ｓ１にのシリカゲル９０部（屈折率１．４
５）炭酸カル７９１１０部、ポリビニルアルコール３０
ｓよりなる固蓋分２０チの塗布液をｔｔｔａｉｔ分で１
６１／ｄになるように、親水性下引き層を設けた５０−
翼のポリエステルフィルムに塗布して実施例δの記録用
、媒体とした。Example 5 90 parts of silica gel with an average particle size of 20s1 (refractive index 1.4)
5) Cal carbonate 79110 parts, polyvinyl alcohol 30
20 pieces of coating liquid for solid lid made of s is 1 piece for tttait.
50- with a hydrophilic undercoat layer so that the ratio is 61/d
It was applied to the polyester film of the wing to provide a recording medium for Example δ.
比較例１
実施例１で使用したと同じコロナ処理ｔＬ九１５−翼の
ポリエステルフィルムに、アンシレックス（屈折率１．
６２） １００部、ポリビニルアルコール１５部よｐな
る固渥分２０饅の塗布液を固渥分で片面１５１／ｗｌに
なるようにエアーナイフコーターで塗布し良。これを比
較例１の記録用媒体とした。Comparative Example 1 The same corona-treated tL915-wing polyester film used in Example 1 was coated with Ansilex (refractive index 1.
62) Apply a coating solution of 100 parts of polyvinyl alcohol and 15 parts of polyvinyl alcohol with a hardness of 20 times using an air knife coater so that the hardness is 151/wl on one side. This was used as the recording medium of Comparative Example 1.
比較例」
比較例１で用い次アンシレックスの代りに酸化亜鉛（屈
折率２３７） を用いた他は比較例１と全く同様にして
比較例２の記録用媒体を得た０実施例１〜！Ｓ１比較例
１．２について測定した結果１に表１に示す。Comparative Example A recording medium of Comparative Example 2 was obtained in exactly the same manner as Comparative Example 1, except that zinc oxide (refractive index 237) was used in place of Ansilex used in Comparative Example 1.0 Example 1~! The results measured for S1 Comparative Example 1.2 are shown in Table 1.
実施例による測定値は色彩性が嵐好でインクジェット適
性を損なわない記録用媒体であることがわかる
表 １Table 1 shows that the measured values according to the examples show that the recording medium has excellent color properties and does not impair inkjet suitability.
Claims (1)
支持体側から測定した白色度が６０％以上である記録用
媒体に於いて、皺支持体が透明媒体でＴｏ）、かつ支持
体に隣接するインタ受理層の主成分である顔料の屈折率
が１ｊ８以下であることを特徴とする記録用媒体。 λ 支持体に隣接するインク受理層の上に白色インク受
理層を設け、白色ｇＩＬを６０−以上とする特許請求の
範囲第一項記載の記録用媒体。 ３、支持体に隣接するインク受理層の上に白色インク受
理層を設け、又は設けずに、更に着色インク受理層を設
けて白色＆を６０−以上とする特許請求の範ｓｇ−項又
は第二項記載の記録用媒体。[Claims] 1. Providing at least one ink-receiving layer on the support,
In a recording medium whose whiteness measured from the support side is 60% or more, the wrinkled support is a transparent medium (To), and the refractive index of the pigment that is the main component of the interreceptive layer adjacent to the support is 1j8 A recording medium characterized by the following: The recording medium according to claim 1, wherein a white ink receiving layer is provided on the ink receiving layer adjacent to the λ support, and the white gIL is 60 or more. 3. A white ink-receiving layer is provided on the ink-receiving layer adjacent to the support, or a colored ink-receiving layer is further provided on the ink-receiving layer adjacent to the support, so that white & is 60 or more. The recording medium described in item 2.