JPH1161978A - Concrete structure and manufacture thereof - Google Patents
Concrete structure and manufacture thereofInfo
- Publication number
- JPH1161978A JPH1161978A JP21842697A JP21842697A JPH1161978A JP H1161978 A JPH1161978 A JP H1161978A JP 21842697 A JP21842697 A JP 21842697A JP 21842697 A JP21842697 A JP 21842697A JP H1161978 A JPH1161978 A JP H1161978A
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- concrete structure
- cross
- sectional
- section
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ＲＣコンクリート
構造物等における、コンクリート構造及びその製造方法
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a concrete structure for an RC concrete structure or the like and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】ＲＣコンクリート構造物等においては、
一般に、底板コンクリートと側壁コンクリートとが硬化
する際、それらの収縮量の差から、底板によって側壁の
変形（収縮）が拘束され、その結果、側壁にひび割れが
発生する。このひび割れは、水等の侵入を許し、側壁の
内部の鉄筋を腐食したり、漏水の原因となる。2. Description of the Related Art In RC concrete structures and the like,
In general, when the bottom plate concrete and the side wall concrete harden, the deformation (shrinkage) of the side wall is restrained by the bottom plate due to the difference in the amount of shrinkage, and as a result, the side wall is cracked. The cracks allow water and the like to enter, corrode the reinforcing steel inside the side wall, and cause water leakage.
【０００３】かかるひび割れは、発生自体を防止するこ
とが困難で、最近では、ひび割れを許容し、耐久性を低
下させないようにしてひび割れ３を発生させる技術が、
有望視されている。かかる観点から、側壁内に所定の間
隔で断面欠損部分を設け、ひび割れをこの予め決められ
た断面欠損部分に集中させる技術が採用されている。こ
の断面欠損部分は、いわゆるひび割れ誘発目地と呼ばれ
ている。なお、水密構造物の場合には、コンクリート中
に予め止水板を埋設しておくなど、適当な止水対策を施
さなければならない。[0003] It is difficult to prevent the occurrence of such cracks. Recently, a technique of allowing cracks and generating cracks 3 without reducing durability has been developed.
Promising. From this point of view, a technique has been adopted in which a cross-section defect portion is provided at a predetermined interval in a side wall, and cracks are concentrated on the predetermined cross-section defect portion. This cross-section defect is called a so-called crack-inducing joint. In the case of a watertight structure, it is necessary to take appropriate measures against water stoppage, such as burying a water stoppage plate in concrete in advance.
【０００４】特開平７−２０７７７４号公報には、かか
るコンクリートの目地構造が記載されている。この目地
構造では、ひび割れ誘発目地として、側壁の表面に所定
の間隔で溝が設けられており、側壁内部の溝と対向する
位置に一対の断面欠損用部材が埋設されている。各断面
欠損用部材は、溝に対向する突出部を有し、内部応力が
加わると、この突出部分から溝へと向かって亀裂が入り
やすくなる。Japanese Unexamined Patent Publication No. 7-207774 discloses a joint structure of such concrete. In this joint structure, grooves are provided at predetermined intervals on the surface of the side wall as crack-inducing joints, and a pair of cross-section deficient members are embedded at positions facing the grooves inside the side wall. Each section defect member has a protruding portion facing the groove, and when an internal stress is applied, a crack is easily formed from the protruding portion toward the groove.
【０００５】この凸状の断面欠損用部材は、溝に対向す
る面に、コンクリートに対して密着する高分子材料製の
粘着層が積層してあるので、ひび割れから外気及び水が
侵入しても、外気及び水が粘着層とコンクリートの界面
で阻止される。したがって、構造用鉄筋が、外気及び水
にさらされないので、構造用鉄筋の寿命を長くすること
ができる。[0005] In this convex member for sectional loss, an adhesive layer made of a polymer material that is in close contact with concrete is laminated on the surface facing the groove, so that even if outside air and water enter from cracks. , Outside air and water are blocked at the interface between the adhesive layer and the concrete. Therefore, the life of the structural reinforcing bar can be extended because the structural reinforcing bar is not exposed to the outside air and water.
【０００６】[0006]
【発明が解決しようとする課題】かかる従来の方法で
は、溝を形成するために台形の化粧目地材を型枠に釘留
めし、断面欠損用部材を結束線により鉄筋に縛りつける
工法が採用される。かかる工法では、溝と断面欠損用部
材との間のひび割れがずれることがある。In such a conventional method, a trapezoidal decorative joint material is nailed to a form in order to form a groove, and a method is employed in which a member having a sectional defect is tied to a reinforcing bar by a binding wire. . In such a construction method, cracks between the groove and the member for section loss may be shifted.
【０００７】図４は、ひび割れがずれた誘発目地の断面
図である。鉄筋６に取り付けられた断面欠損用部材５の
突出部は、化粧目地材により形成された溝４と対向して
おらず、位置関係がずれている。かかるひび割れ誘発目
地では、ひび割れ３を断面欠損用部材５と溝４との間の
コンクリートに集中させることができない。FIG. 4 is a cross-sectional view of the induced joint where the crack has shifted. The projecting portion of the member for section loss 5 attached to the reinforcing bar 6 does not face the groove 4 formed by the decorative joint material, and the positional relationship is shifted. In such a crack-inducing joint, the crack 3 cannot be concentrated on the concrete between the member 5 for section loss and the groove 4.
【０００８】また、図５には、ひび割れがずれた他の例
の誘発目地の断面図を示す。構造用鉄筋６は剛性が低い
ため、断面欠損用部材と溝との距離を一定に保つことが
難しい。溝４と断面欠損用部材５との距離が長くなった
場合、図５に示すように、ひび割れ３は、溝４と断面欠
損用部材５の突出部との間に形成されない。FIG. 5 is a cross-sectional view of another example of the induced joint in which the crack has shifted. Since the structural reinforcing bar 6 has low rigidity, it is difficult to keep the distance between the groove member and the groove constant. When the distance between the groove 4 and the member for sectional loss 5 is long, the crack 3 is not formed between the groove 4 and the protrusion of the member for sectional loss 5 as shown in FIG.
【０００９】本発明は、溝以外のコンクリート表面にひ
び割れを起こさないコンクリート構造を得ることを目的
とする。An object of the present invention is to provide a concrete structure which does not crack on the concrete surface other than the grooves.
【００１０】[0010]
【課題を解決するための手段】本発明は、構造用鉄筋
と、前記構造用鉄筋を包含するように打設されたコンク
リートと、前記コンクリートに拘束された断面欠損用部
材とを備えており、前記断面欠損用部材が前記コンクリ
ートにひび割れを生じさせているコンクリート構造であ
って、前記断面欠損用部材が露出面と埋設面とを有して
おり、前記露出面が前記コンクリート構造の表面に露出
しており、前記埋設面が前記コンクリート中に埋設され
ており、前記ひび割れが前記埋設面と前記構造用鉄筋と
の間の前記コンクリートに生じているコンクリート構造
及びその製造方法である。According to the present invention, there is provided a structural reinforcing bar, concrete cast so as to include the structural reinforcing bar, and a member for section loss restrained by the concrete, A concrete structure in which the member for section loss has caused cracks in the concrete, wherein the member for section loss has an exposed surface and a buried surface, and the exposed surface is exposed to the surface of the concrete structure. A concrete structure wherein the buried surface is buried in the concrete, and wherein the cracks are formed in the concrete between the buried surface and the structural reinforcing bar, and a method of manufacturing the concrete structure.
【００１１】本発明のコンクリート構造では、コンクリ
ート構造の表面から構造用鉄筋に向けて、必要断面欠損
率を有する長さの断面欠損用部材をコンクリート中に配
置する。かかる断面欠損用部材と構造用鉄筋との間のコ
ンクリートには、ひび割れが生じる。[0011] In the concrete structure of the present invention, a member having a required section loss rate is disposed in the concrete from the surface of the concrete structure to the structural reinforcing bar, the member having a required section loss rate. Cracks occur in the concrete between the member for section loss and the structural reinforcing bar.
【００１２】従来の方法では、溝を形成するための目地
材を型枠に取り付け、断面欠損用部材をコンクリート中
の鉄筋に取り付けるため、手間もかかり、互いの位置ず
れをなくし、お互いを一定の間隔に保持することが難し
かった。本発明は、かかる問題を解決する。In the conventional method, a joint material for forming a groove is attached to a formwork, and a member for section loss is attached to a reinforcing steel bar in concrete. It was difficult to keep at intervals. The present invention solves such a problem.
【００１３】本発明のコンクリート構造及びその製造方
法によれば、断面欠損用部材をコンクリート構造の表面
側に配置するため、溝を必要としない。かかる構造及び
方法では、溝と断面欠損用部材との間にひび割れを生じ
させないので、ひび割れの位置ずれが起こりえない。ま
た、本発明のコンクリート構造及びその製造方法によれ
ば、断面欠損用部材をコンクリート構造の表面側に配置
し、その内部にひび割れを生じさせるため、断面欠損用
部材がひび割れを覆うこととなり、ひび割れがコンクリ
ート構造の表面に現れない。According to the concrete structure and the method of manufacturing the same of the present invention, the groove is not required because the member for section loss is arranged on the surface side of the concrete structure. In such a structure and method, no crack is generated between the groove and the member for lacking a cross-section, so that no positional displacement of the crack can occur. Further, according to the concrete structure and the method for manufacturing the same of the present invention, the member for section loss is arranged on the surface side of the concrete structure, and the inside of the structure is cracked. Does not appear on the surface of the concrete structure.
【００１４】更に、本発明のコンクリート構造の製造方
法では、溝形成用の目地材と断面欠損用部材とを型枠に
取り付けることができる。かかる方法によれば、型枠上
で溝と断面欠損用部材とを三次元的に任意に配置するこ
とができ、溝と断面欠損用部材との位置関係がずれるこ
となく、溝と断面欠損用部材との間に生じるコンクリー
トのひび割れを溝に集中させることができる。Further, in the method for manufacturing a concrete structure according to the present invention, the joint material for forming a groove and the member for lacking a cross section can be attached to a mold. According to such a method, the groove and the member for cross-sectional loss can be arbitrarily arranged three-dimensionally on the formwork, and the positional relationship between the groove and the member for cross-sectional loss is not shifted. Cracks in concrete generated between the members can be concentrated in the grooves.
【００１５】[0015]
【発明の実施の形態】本発明では、断面欠損用部材が基
部と突出部とを有しており、基部がコンクリート構造の
表面に露出し、突出部が構造用鉄筋に対向しているのが
好ましい。これにより、断面欠損用部材の突出部分の形
状に沿って、これを取り巻くコンクリートに内部応力が
加わるので、この突出部分から構造用鉄筋へと向かって
亀裂が入りやすくなる。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS In the present invention, the member for section loss has a base and a protrusion, the base is exposed on the surface of the concrete structure, and the protrusion faces the structural reinforcing bar. preferable. As a result, an internal stress is applied to the concrete surrounding the projecting portion of the member for cross-sectional deficiency along the shape of the projecting portion, so that a crack is easily formed from the projecting portion toward the structural reinforcing bar.
【００１６】また、本発明では、断面欠損用部材が突堤
部を有しており、この突堤部がコンクリートにより周囲
から拘束されているのが好ましい。かかる突堤部は、断
面欠損用部材がコンクリートから引き抜けなくなるアン
カー効果を発揮する。また、この突堤部は、断面欠損用
部材とコンクリートとの界面の長さを長くするため、止
水板効果を発揮する。突堤部は、かかる効果を発揮すれ
ば、種々の形状で設けることができる。Further, in the present invention, it is preferable that the member for sectional loss has a pier, and the pier is restrained from the surroundings by concrete. Such a jetty exhibits an anchoring effect that prevents the member for sectional loss from pulling out of concrete. In addition, the jetty portion exerts a water stoppage effect in order to increase the length of the interface between the member for section loss and concrete. The jetty portion can be provided in various shapes as long as such an effect is exhibited.
【００１７】更に、本発明では、断面欠損用部材と構造
用鉄筋との間に、更に他の断面欠損用部材を配置し、断
面欠損用部材と他の断面欠損用部材との間のコンクリー
トにひび割れを生じさせるのが好ましい。かかるコンク
リート構造では、断面欠損用部材によるひび割れが他の
断面欠損用部材で止まるため、コンクリート構造内部の
止水性を高めることができる。Further, in the present invention, another member for sectional loss is disposed between the member for sectional loss and the structural reinforcing bar, and concrete is interposed between the member for sectional loss and another member for sectional loss. It is preferable to cause cracking. In such a concrete structure, since the cracks caused by the member for section loss stop at other members for section loss, the water stopping property inside the concrete structure can be enhanced.
【００１８】本発明にかかる断面欠損用部材がコンクリ
ートと接する部分には、コンクリートに対して密着する
高分子材料製の粘着層が設けられているのが好ましい。
粘着層は、コンクリートと断面欠損用部材との隙間から
外気や水が侵入するのを防止することができ、外気及び
水が断面欠損用部材と構造用鉄筋との間のひび割れを伝
って構造用鉄筋に達するのを阻止することができる。こ
れにより、構造用鉄筋の寿命を長くすることができる。
かかる粘着層としては、特に、ブチルゴム製の粘着剤を
断面欠損用部材の芯材に対して張りつけたものが好まし
い。ブチルゴム系粘着剤は、コンクリートとの接着性が
高いからである。It is preferable that a portion of the member for cross-sectional defect according to the present invention which is in contact with concrete is provided with an adhesive layer made of a polymer material which is in close contact with concrete.
The adhesive layer can prevent the outside air and water from entering from the gap between the concrete and the member for section loss, and the outside air and water pass through the crack between the member for section loss and the structural rebar, and It can be prevented from reaching the rebar. Thereby, the life of the structural reinforcing bar can be prolonged.
As the pressure-sensitive adhesive layer, a layer in which a pressure-sensitive adhesive made of butyl rubber is adhered to the core material of the member for sectional defect is particularly preferable. This is because the butyl rubber-based pressure-sensitive adhesive has high adhesiveness to concrete.
【００１９】本発明にかかる断面欠損用部材には、この
部材がコンクリートにひび割れを生じさせる部分に、硬
化前のコンクリート中の水分を吸収して膨張する水膨張
性高分子材料の層が設けられているのが好ましい。かか
る層は、硬化前のコンクリート中の水分を吸収して、断
面欠損用部材を変形させる。このため、コンクリートは
変形前の断面欠損用部材の応力に加え、断面欠損用部材
の変形による応力も受けることになる。In the member for cross-sectional deficiency according to the present invention, a layer of a water-swellable polymer material which absorbs moisture in concrete before hardening and expands is provided at a portion where the member cracks in concrete. Is preferred. Such a layer absorbs moisture in the concrete before hardening, and deforms the member for sectional loss. For this reason, the concrete receives not only the stress of the member for sectional loss before deformation but also the stress due to the deformation of the member for sectional loss.
【００２０】水膨張性高分子材料には、コンクリート中
の水分により膨張圧を生じ、この膨張圧により、確実に
誘発目地部にひび割れを集中させることができる材料を
用いることができる。かかる材料には、一般的水膨張性
ゴム材料として、天然ゴム、若しくは合成ゴムの１種又
は２種以上をブレンドしたベースポリマーに対し、吸水
性ポリマーを添加したものを用いることができる。As the water-swellable polymer material, there can be used a material which generates an expansion pressure due to moisture in the concrete and which can reliably concentrate cracks at the induced joints by the expansion pressure. As such a material, a general water-swellable rubber material obtained by adding a water-absorbing polymer to a base polymer obtained by blending one or two or more of natural rubber or synthetic rubber can be used.
【００２１】合成ゴムには、スチレンブタジエンゴム等
の一般的な物を用いることができ、吸水性ポリマーに
も、ポリアクリル酸塩系等を用いることができる。ま
た、かかる吸水性ポリマーは必ずしも使用する必要はな
く、例えば合成ゴムに、シリカ・ベントナイト等の充填
剤を適度に添加しても、水膨張性組成物を得ることがで
きる。当然、かかる組成物を作るにあたっては、一般的
によく知られている加工助剤、架橋剤、架橋助剤、架橋
促進剤、充填剤、可塑剤、軟化剤、老化防止剤、補強
剤、粘着付与剤、発泡剤、吸水剤等を使用することがで
きる。A general material such as styrene-butadiene rubber can be used as the synthetic rubber, and a polyacrylate salt or the like can be used as the water-absorbing polymer. It is not necessary to use such a water-absorbing polymer. For example, even if a filler such as silica / bentonite is appropriately added to synthetic rubber, a water-swellable composition can be obtained. Of course, in making such compositions, generally well-known processing aids, crosslinking agents, crosslinking aids, crosslinking accelerators, fillers, plasticizers, softeners, anti-aging agents, reinforcing agents, adhesives An imparting agent, a foaming agent, a water absorbing agent and the like can be used.
【００２２】本発明では、断面欠損用部材のコンクリー
トと接する面に、コンクリートに対して密着する高分子
材料製の粘着層と水膨張性高分子材料の層とを互いに領
域を分けて設けることができる。本発明にかかる水膨張
性高分子材料の層は、コンクリート中の水分を吸収して
膨張するため、コンクリートと断面欠損用部材との隙間
から外気や水が侵入するのを防止することもできる。In the present invention, an adhesive layer made of a polymer material and a layer of a water-swellable polymer material which are in close contact with the concrete are provided on the surface of the member for cross-sectional deficiency in contact with the concrete, with the regions separated from each other. it can. The layer of the water-swellable polymer material according to the present invention absorbs moisture in the concrete and expands, so that it is also possible to prevent outside air and water from entering from the gap between the concrete and the member for section loss.
【００２３】断面欠損用部材は、コンクリートを打設す
る際に、流動するコンクリートによって変形しない剛性
を有していなければならない。このため、断面欠損用部
材には芯材を用いるのが好ましい。芯材としては、具体
的には、耐久性のある金属硬質ゴム、硬質プラスチック
等の剛性材料を例示することができる。The member for lacking a cross section must have a rigidity that is not deformed by flowing concrete when the concrete is poured. For this reason, it is preferable to use a core material for the member for sectional loss. As the core material, specifically, a rigid material such as a durable metal hard rubber or a hard plastic can be exemplified.
【００２４】断面欠損率は、本発明にかかるコンクリー
ト構造の厚さに対する、断面欠損用部材の長さの合計に
よって決まる。ＲＣコンクリート構造では、一般に、こ
の断面欠損率が２０％〜３０％以上必要と言われてい
る。この点で、もし断面欠損用部材の長さの合計が不足
する場合には、更に、構造用鉄筋の内側に内側断面欠損
用部材を埋設することができる。The sectional defect rate is determined by the sum of the lengths of the members for sectional defect with respect to the thickness of the concrete structure according to the present invention. In the RC concrete structure, it is generally said that this section loss rate is required to be 20% to 30% or more. At this point, if the total length of the member for section loss is insufficient, the member for section loss can be further embedded inside the structural reinforcing bar.
【００２５】この内側断面欠損用部材は、断面欠損に必
要な長さを確保するという観点からは、異物として埋設
されていれば十分なので、上記した芯材のみからなって
いてもよい。しかし、ひび割れが内側断面欠損用部材に
沿っても発生するので、このひび割れからの漏水等を一
層完全に防止するという観点からは、内側断面欠損用部
材のうち少なくとも幅方向に延びる突出部分には、上記
した粘着層を形成し、所定の方向にひび割れを集中させ
るために、上記した水膨張性高分子材料の層で芯材を被
覆することが好ましい。From the viewpoint of securing the length necessary for the cross-sectional defect, the member for the internal cross-sectional defect is sufficient if it is embedded as a foreign substance, and therefore may be composed of only the above-described core material. However, since cracks also occur along the member for losing the inner cross section, from the viewpoint of more completely preventing water leakage or the like from the crack, at least a protruding portion extending in the width direction of the member for losing the inner cross section is used. In order to form the above-mentioned adhesive layer and concentrate cracks in a predetermined direction, it is preferable to coat the core with the above-mentioned water-expandable polymer material layer.
【００２６】内側断面欠損用部材には貫通孔を設け、こ
の貫通孔に対して結束線を挿通し、この結束線によって
内側断面欠損用部材を構造用鉄筋に対して縛りつけるこ
とができる。これにより、内側断面欠損用部材を溶接す
る場合とは異なり、短時間で容易に内側断面欠損用部材
を固定することができる。A through hole is provided in the member for losing the inner cross section, and a binding wire is inserted into the through hole, and the member for losing the inner cross section can be bound to the structural reinforcing bar by the binding wire. Thereby, unlike the case of welding the member for losing the inner cross section, the member for losing the inner cross section can be easily fixed in a short time.
【００２７】上記した内側断面欠損用部材には、一対の
フランジ部分を設け、各フランジ部分をそれぞれ構造用
鉄筋に対して固定するのが好ましい。これにより、内側
断面欠損用部材が、２箇所で確実に構造用鉄筋に対して
固定されるため、コンクリートを流し込んだ時に、一
層、内側断面欠損用部材が移動、変形しにくくなる。It is preferable to provide a pair of flange portions on the above-mentioned member for deficient inner cross section, and to fix each flange portion to the structural reinforcing bar. Thereby, since the member for losing the inner cross section is securely fixed to the structural reinforcing bar at two places, the member for losing the inner cross section becomes more difficult to move and deform when the concrete is poured.
【００２８】[0028]
【実施例】図面を参照して、本発明を実施例に基づきよ
り詳細に説明する。図１は、本発明の一実施例に係るコ
ンクリート構造の断面図であり、図２は、本発明の他の
実施例に係るコンクリート構造の断面図である。図３
は、内側断面欠損用部材を設けたコンクリート構造の断
面図である。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in more detail with reference to the drawings. FIG. 1 is a sectional view of a concrete structure according to one embodiment of the present invention, and FIG. 2 is a sectional view of a concrete structure according to another embodiment of the present invention. FIG.
FIG. 2 is a cross-sectional view of a concrete structure provided with a member for deficient inner cross section.
【００２９】図１に示すように、本発明のコンクリート
構造では、目地材９は長さ１２を有しており、必要断面
欠損率を有する。目地材９の基部９ｃは、型枠材７に釘
８により取付け、コンクリート打設後、コンクリート２
中に埋込まれる。この目地材９は、突出部９ｄを有して
おり、型枠材７と平行に突出部９ｄの両側に張り出す突
堤部９ａ、９ｂと、型枠材７の反対側端部に突起９ｅを
有している。As shown in FIG. 1, in the concrete structure of the present invention, the joint material 9 has a length 12 and has a required sectional defect rate. The base 9c of the joint material 9 is attached to the form member 7 with a nail 8, and after the concrete is cast, the concrete 2
Embedded inside. The joint material 9 has a protruding portion 9 d, and ridges 9 a and 9 b projecting on both sides of the protruding portion 9 d in parallel with the form material 7, and a protrusion 9 e on the opposite end of the form material 7. Have.
【００３０】突堤部９ａ、９ｂは、目地材９が型枠材７
の脱型時に引き抜けないためのアンカー効果と、コンク
リート２と目地材９との界面の長さを長くして止水する
止水板効果を併せ持つ。突起９ｅは、ひび割れを発生さ
せ易くする。また、突出部９ｃと突堤部９ａ、９ｂの表
面には、コンクリートと密着するブチルゴム１１が積層
されており、より止水性を増している。In the jetty portions 9a and 9b, the joint material 9 is
It has both an anchor effect to prevent the concrete 2 from being pulled out when the mold is removed and a water-stop plate effect to increase the length of the interface between the concrete 2 and the joint material 9 to stop water. The projections 9e facilitate the generation of cracks. Further, on the surfaces of the projecting portion 9c and the jetty portions 9a and 9b, a butyl rubber 11 which is in close contact with concrete is laminated, so that the waterproofness is further increased.
【００３１】このコンクリート構造では、突起９ｅと構
造用鉄筋６との間にひび割れ１０が形成される。このひ
び割れ１０は、構造用鉄筋６を越えてコンクリート構造
内部にまで到達する。In this concrete structure, a crack 10 is formed between the projection 9e and the structural reinforcing bar 6. The crack 10 reaches the inside of the concrete structure beyond the structural reinforcing bar 6.
【００３２】図２に示すコンクリート構造では、目地材
１５と構造用鉄筋６との間に他の断面欠損用部材１６を
介在させる。目地材１５は、この断面図で見て、横方向
に伸びている基部１５ｃと、下方向に伸びている突出部
１５ｄとを有している。突出部１５ｄには、両側に突堤
部１５ａ、１５ｂが張り出させる。突出部１５ｄの先端
と突堤部１５ａ、１５ｂの構造用鉄筋６側の面には、コ
ンクリートと密着するブチルゴム１７を積層する。基部
１５ｃと突堤部１５ａ、１５ｂは、釘１８ａ、１８ｂを
それぞれの両端で貫通させ、型枠材７に固定する。In the concrete structure shown in FIG. 2, another member 16 for deficient cross section is interposed between the joint material 15 and the structural reinforcing bar 6. The joint material 15 has a base portion 15c extending in the lateral direction and a projecting portion 15d extending in the downward direction as viewed in the cross-sectional view. Jetty portions 15a and 15b project from both sides of the projecting portion 15d. A butyl rubber 17 that is in close contact with concrete is laminated on the end of the protruding portion 15d and the surface of the jetty portions 15a and 15b on the structural reinforcing bar 6 side. The base 15c and the jetty portions 15a, 15b allow the nails 18a, 18b to penetrate at both ends thereof, and are fixed to the formwork material 7.
【００３３】他の断面欠損用部材１６は、内側の止水を
兼ねたひび割れ誘発部材であり、２０〜３０ｃｍ間隔
で、ボルト１４ａ、１４ｂにより型枠材７に固定する。
この断面欠損用部材１６は、突出部分１６ｂが略三角形
の山形をなしており、突出部分１６ｂの両側に、それぞ
れ細長い平板形状のフランジ部分１６ａ、１６ｃを形成
する。突出部分１６ｂ及びフランジ部分１６ａ、１６ｃ
の全体は、芯材１９によって形成し、芯材１９のうち、
山形の突出部分１６ｂとフランジ部分１６ａ、１６ｃと
が、粘着層２０により被覆する。The other member 16 for deficient cross-section is a crack-inducing member that also serves as a water stop inside, and is fixed to the form member 7 with bolts 14a and 14b at intervals of 20 to 30 cm.
The projecting portion 16b of the member 16 has a substantially triangular mountain shape, and elongated plate-like flange portions 16a and 16c are formed on both sides of the projecting portion 16b. Projecting portion 16b and flange portions 16a, 16c
Is formed by the core material 19, and of the core material 19,
The projection 16b and the flanges 16a, 16c are covered with the adhesive layer 20.
【００３４】かかるコンクリート構造では、目地材１５
の突出部１５ｄの先端と他の断面欠損用部材１６の突出
部分１６ｂとの間に所望のひび割れ２１が形成される。In such a concrete structure, the joint material 15
A desired crack 21 is formed between the tip of the protruding portion 15d and the protruding portion 16b of the member 16 for another section loss.
【００３５】図３には、コンクリートが硬化した後のコ
ンクリート構造を示す。コンクリート構造の側壁には、
図１に示す目地材９が埋め込まれており、目地材９と構
造用鉄筋６との間のコンクリート２にひび割れ１０が生
じる。内側断面欠損部材１３は、コンクリート側壁２の
必要断面欠損率が不足する場合に、構造用鉄筋６の内側
に埋設する。FIG. 3 shows the concrete structure after the concrete has hardened. On the side wall of the concrete structure,
The joint material 9 shown in FIG. 1 is embedded, and a crack 10 occurs in the concrete 2 between the joint material 9 and the structural reinforcing bar 6. The inner cross-section defect member 13 is embedded inside the structural reinforcing bar 6 when the required cross-section defect rate of the concrete side wall 2 is insufficient.
【００３６】図３に示す内側断面欠損用部材１３は、１
つの直線形状のフランジ部分１３ａと、直線形状の突出
部分１３ｂとからなる。フランジ部分１３ａと突出部分
１３ｂとは、互いにほぼ直角をなしており、突出部分１
３ｂの相互間のコンクリート２ａにひび割れ２２が生じ
ている。The member 13 for deficient inner cross section shown in FIG.
It comprises two linear flange portions 13a and a linear projection portion 13b. The flange portion 13a and the protruding portion 13b are substantially perpendicular to each other, and
Cracks 22 are formed in the concrete 2a between the portions 3b.
【００３７】[0037]
【発明の効果】本発明によれば、施工が簡単で、所望の
ひび割れがより確実に断面欠損部材から発生するひび割
れ誘発型のコンクリート構造が得られる。また、本発明
では、断面欠損部材をコンクリート構造の表面側から配
置するため、ひび割れが構造物表面には現れず、現れる
場合にも溝に集中することとなり、構造物の美観が損な
われない。According to the present invention, it is possible to obtain a concrete structure of a crack-inducing type in which construction is simple and a desired crack is more reliably generated from a member having a sectional defect. Further, in the present invention, since the member having a cross-sectional defect is arranged from the surface side of the concrete structure, cracks do not appear on the surface of the structure, and when they do appear, they are concentrated in the groove, so that the appearance of the structure is not impaired.
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明の実施例に係るコンクリート構造の断面
図である。FIG. 1 is a sectional view of a concrete structure according to an embodiment of the present invention.
【図２】本発明の他の実施例に係るコンクリート構造の
断面図である。FIG. 2 is a sectional view of a concrete structure according to another embodiment of the present invention.
【図３】本発明の更に他の実施例に係るコンクリート構
造の断面図である。FIG. 3 is a sectional view of a concrete structure according to still another embodiment of the present invention.
【図４】ひび割れがずれた誘発目地の断面図である。FIG. 4 is a cross-sectional view of an induced joint where a crack has shifted.
【図５】ひび割れがずれた他の誘発目地の断面図であ
る。FIG. 5 is a cross-sectional view of another induction joint where a crack has shifted.
２ コンクリート側壁 ２ａ 構造用鉄筋の内側部分 ３ ひび割れ ４ 溝 ５ 断面欠損用部材 ６ 構造用鉄筋 ７ 型枠材 ８ａ、８ｂ、１８ａ、１８ｂ 釘 ９、１３、１５、１６ 断面欠損用部材 ９ａ、９ｂ、１５ａ、１５ｂ 突堤部 ９ｃ、１５ｃ 基部 ９ｄ、１５ｄ 突出部 ９ｅ 突起 １０、２１、２２ ひび割れ １３ａ、１６ａ、１６ｃ フランジ部分 １３ｂ 突出部分 １７、２０ 粘着層 １９ 芯材 2 Concrete side wall 2a Inside portion of structural reinforcing bar 3 Crack 4 Groove 5 Member for cross-sectional defect 6 Structural reinforcing bar 7 Forming material 8a, 8b, 18a, 18b Nail 9, 13, 15, 16 Member for cross-sectional defect 9a, 9b, 15a, 15b Jetty 9c, 15c Base 9d, 15d Projection 9e Projection 10, 21, 22 Crack 13a, 16a, 16c Flange 13b Projection 17,20 Adhesive layer 19 Core material
Claims (8)
るように打設されたコンクリートと、前記コンクリート
に拘束された断面欠損用部材とを備えており、前記断面
欠損用部材が前記コンクリートにひび割れを生じさせて
いるコンクリート構造であって、 前記断面欠損用部材が露出面と埋設面とを有しており、
前記露出面が前記コンクリート構造の表面に露出してお
り、前記埋設面が前記コンクリート中に埋設されてお
り、前記ひび割れが前記埋設面と前記構造用鉄筋との間
の前記コンクリートに生じていることを特徴とする、コ
ンクリート構造。1. A structural reinforcing bar, a concrete cast so as to include the structural reinforcing bar, and a member for cross-sectional defect restrained by the concrete, wherein the member for cross-sectional defect is the concrete. Concrete structure causing cracks, wherein the member for sectional loss has an exposed surface and a buried surface,
The exposed surface is exposed on the surface of the concrete structure, the buried surface is buried in the concrete, and the crack is formed in the concrete between the buried surface and the structural reinforcing bar. Characterized by a concrete structure.
を有しており、前記基部が前記コンクリート構造の表面
に露出しており、前記突出部が前記構造用鉄筋の方向に
向かって突出していることを特徴とする、請求項１記載
のコンクリート構造。2. The member for section loss has a base and a protrusion, the base is exposed on the surface of the concrete structure, and the protrusion is directed toward the structural reinforcing bar. The concrete structure according to claim 1, wherein the concrete structure protrudes.
いることを特徴とする、請求項１又は２記載のコンクリ
ート構造。3. The concrete structure according to claim 1, wherein the member for section loss has a jetty portion.
の間に、他の断面欠損用部材が配置されており、前記ひ
び割れが前記断面欠損用部材の埋設面と前記他の断面欠
損用部材との間の前記コンクリートに生じていることを
特徴とする、請求項１〜３のいずれか一項記載のコンク
リート構造。4. A member for another cross-section defect is disposed between the member for a cross-section defect and the structural reinforcing bar, and the crack is formed between the embedding surface of the member for a cross-section defect and the other cross-section defect. The concrete structure according to any one of claims 1 to 3, wherein the concrete structure is generated in the concrete between members.
用部材とが高分子材料製の粘着層を有しており、前記粘
着層が前記コンクリートに対して密着していることを特
徴とする、請求項１〜４のいずれか一項記載のコンクリ
ート構造。5. The member for sectional loss and the other member for sectional loss have an adhesive layer made of a polymer material, and the adhesive layer is in close contact with the concrete. The concrete structure according to any one of claims 1 to 4, wherein
用部材とが水膨張性高分子材料の層を有しており、前記
水膨張性高分子材料の層が、前記コンクリート中の水分
を吸収して膨張しており、前記コンクリートに対して密
着していることを特徴とする、請求項１〜５のいずれか
一項記載のコンクリート構造。6. The cross-sectional defect member and the other cross-sectional defect member have a layer of a water-expandable polymer material, and the layer of the water-expandable polymer material has a water content in the concrete. The concrete structure according to any one of claims 1 to 5, wherein the concrete structure absorbs and expands, and is in close contact with the concrete.
るように打設されたコンクリートと、前記コンクリート
に拘束された断面欠損用部材とを備えているコンクリー
ト構造の製造方法であって、 前記断面欠損用部材が露出面と埋設面とを有しており、
前記露出面を型枠に取り付け、前記コンクリートを打設
し、前記埋設面を前記コンクリート中に埋設し、前記型
枠を脱型し、前記露出面を前記コンクリート構造の表面
に露出させ、前記埋設面と前記構造用鉄筋との間の前記
コンクリートにひび割れを生じさせることを特徴とす
る、コンクリート構造の製造方法。7. A method for producing a concrete structure, comprising: a structural reinforcing bar, concrete cast so as to include the structural reinforcing bar, and a member for section loss restrained by the concrete. The member for cross-sectional loss has an exposed surface and a buried surface,
Attaching the exposed surface to a formwork, casting the concrete, embedding the buried surface in the concrete, removing the formwork, exposing the exposed surface to the surface of the concrete structure, A method for manufacturing a concrete structure, characterized in that cracks are generated in the concrete between a surface and the structural reinforcing bar.
るように打設されたコンクリートと、前記コンクリート
の表面に形成された溝と、前記コンクリートに拘束され
た断面欠損用部材とを備えているコンクリート構造の製
造方法であって、 前記溝を形成するための目地材と、前記断面欠損用部材
とを、相対向するように型枠に取り付け、前記コンクリ
ートを打設し、前記型枠を脱型し、前記溝と前記断面欠
損用部材と間の前記コンクリートにひび割れを生じさせ
ることを特徴とする、コンクリート構造の製造方法。8. A structural rebar, a concrete cast so as to include the structural rebar, a groove formed in a surface of the concrete, and a member for sectional loss restrained by the concrete. A method for manufacturing a concrete structure, comprising: joining a joint material for forming the groove and the member for cross-sectional defect to a formwork so as to face each other; casting the concrete; Removing the mold from the mold and causing cracks in the concrete between the groove and the member for section loss.