Abstract

PROBLEM TO BE SOLVED: To obtain a materials for pet urine treatment having urine water absorbing properties and deodorizing properties, easy to handle by aggregation after absorbing water and disposable as combustible waste. SOLUTION: This pet urine treating material is composed of either one of a granular inorganic porous substance or pulp-sludge coated with a mixture of paper powder and powder of a high water absorbing polymer. The production method comprises, coating the mixtures of the paper powder and the powder of the high water absorbing polymer to the water added inorganic porous substance or pulp-sludge on a vibrating plate and granulating. Either one of Zeolite, perlite, pumice stone, Akadama stone (a sort of ferriquartz produced from Sado island, Japan), Kanuma tuchi (earth of Kanuma tephra produced in Tochigi prefecture, Japan), activated charcoal is preferred as the inorganic porous substance, and a crosslinked sodium polyacrylate is preferred as the high water absorbing polymer.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明はネコなどペットの尿
を吸収する尿処理材とその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a urine treatment material for absorbing urine of pets such as cats and a method for producing the same.

【０００２】[0002]

【従来の技術】従来、ペットの尿処理材として、単独使
用による砂、ゼオライト（特開昭５７−１２９６２２
号）、ベントナイト、パルプなどの紙質に水を加えて造
粒したもの（実開昭５１−１３３６８５号、特公昭５４
−２４９４５号、実公昭５４−１７６７５号、特開昭５
５−１３２７５３号、特公平３−３８８１１号）などが
使用されているが、それぞれ吸水性や脱臭性などのバラ
ンスに欠け、満足すべき性能を有していない。すなわ
ち、砂は吸水性がなく、臭気が残る。紙は軽すぎ、かつ
静電気発生のため、ペットがこれを足や体に付けて部屋
中にまき散らす。また、紙は尿の吸水性が低く、塊状化
しにくく、脱臭性がない。ゼオライトはアンモニヤの脱
臭性にすぐれるが、吸水性がやや低い。ベントナイトは
使用により膨潤して塊状化するので取扱いやすいが、脱
臭性に欠ける。また、ゼオライトやベントナイトは可燃
ごみとはならず、その分野で廃棄することができない。2. Description of the Related Art Conventionally, as a urine treatment material for pets, sand or zeolite (Japanese Patent Application Laid-Open No. 57-129622) which is used alone.
No. 1), bentonite, pulp, etc. and granulated by adding water (Japanese Utility Model Publication No. 51-133885, Japanese Patent Publication No. 54)
No. 24945, Japanese Utility Model Publication No. Sho 54-17675,
Nos. 5-132753 and JP-B-3-38811) are used, but each of them lacks water-absorbing and deodorizing properties and does not have satisfactory performance. That is, the sand has no water absorption and leaves an odor. The paper is too light and generates static electricity, so pets can stick it on their feet or body and scatter them around the room. In addition, paper has low water absorption of urine, hardly clumps, and has no deodorizing property. Zeolite is excellent in deodorizing properties of ammonia, but has slightly lower water absorption. Bentonite is easy to handle because it swells and clumps with use, but lacks deodorizing properties. In addition, zeolite and bentonite do not become combustible waste and cannot be disposed of in that field.

【０００３】これらを解決するものとして、もみがらや
ピ−ナッツの殻、木粉などの天然有機物と高吸水性樹脂
を混合し、バインダ−で固形化し造粒したもの（特公平
３−４６０８９号）があり、高吸水性樹脂により尿を吸
収し、天然有機物で脱臭効果もあるというが、発明につ
いての実施例がなく、脱臭効果なども具体的に示されて
いない。In order to solve these problems, natural organic substances such as rice husks, peanut shells, and wood powder are mixed with a superabsorbent resin, solidified with a binder and granulated (Japanese Patent Publication No. 3-46089). ), Which absorbs urine with a highly water-absorbent resin and has a deodorizing effect with a natural organic substance. However, there is no working example of the invention, and the deodorizing effect is not specifically shown.

【０００４】また、製紙カスと高吸水性樹脂、あるい
は、これらに水溶性無機塩類を加えた混合物を造粒した
もの（特公平３−６７６７号）があり、パルプのみの場
合の吸水性と使用後のべとつきを改善するというが、脱
臭性に欠ける。それでも、水溶性無機塩類で比重を上
げ、飛散防止効果が得られるというが、トイレ処理をす
る場合は水質汚染問題をきたすおそれがある。類似のも
のに、パルプ又は紙粉に２種類の高吸水性樹脂を加えた
もの（特開平２−２６５９６８号）で、吸収後のゲル化
と高粘度化をはかっているが、脱臭性に欠ける。[0004] Further, there is a granulation of papermaking waste and a superabsorbent resin or a mixture of these and a water-soluble inorganic salt (Japanese Patent Publication No. 3-6767). It is said to improve later tackiness, but lacks deodorizing properties. Even so, it is said that the water-soluble inorganic salts can increase the specific gravity and provide a scattering prevention effect. However, when performing toilet treatment, there is a risk of causing water pollution problems. A similar product obtained by adding two types of superabsorbent resins to pulp or paper powder (Japanese Unexamined Patent Publication No. 2-265968). Gelling and viscosity increase after absorption, but lack in deodorizing properties. .

【０００５】ほかに、製紙スラッジと粘結用の吸水性ポ
リマ−による粒状体の表面にベントナイト粉末を付着さ
せたもの（特公平３−３２９６７号）があるが、使用に
より表面のベントナイトが膨潤して相互に付着し塊状化
するので、製紙スラッジの吸水性を阻害し、脱臭性も劣
る。類似のものに、紙粉と高吸水性樹脂とベントナイト
の混合物を粒状化したもの（特開平１−１９１６２６
号）もある。[0005] In addition, there is a method in which bentonite powder is adhered to the surface of a granular material made of paper sludge and a water-absorbing polymer for caking (Japanese Patent Publication No. 3-32967). Therefore, they adhere to each other and form agglomerates, which hinders the water absorption of papermaking sludge and degrades deodorization. A similar product is obtained by granulating a mixture of paper powder, superabsorbent resin and bentonite (Japanese Patent Laid-Open No. 1-191626).
No.).

【０００６】さらに、吸水ポリマ−にゼオライトの粉末
を加えたもの（特開昭５９−１７９１１４号）で吸水性
と消臭性が得られるというが、全体が粉末であるため、
使用の前後における取扱いが容易でない。Further, it is said that a water-absorbing polymer obtained by adding a zeolite powder to a water-absorbing polymer (Japanese Patent Application Laid-Open No. 59-179114) can provide water absorbing and deodorizing properties.
It is not easy to handle before and after use.

【０００７】その他、ゼオライト、ベントナイトおよび
木粉等の繊維質粉末にデキストリン等の水溶性糊剤を添
加、混和して造粒したもの（特開昭６０−１０２１２８
号）があり、消臭性あり、塊状化しやすく取扱いやすい
というが、吸水性が低い。In addition, fibrous powders such as zeolite, bentonite and wood flour are mixed with a water-soluble sizing agent such as dextrin and granulated (JP-A-60-102128).
No.), deodorant, easy to agglomerate and easy to handle, but low in water absorption.

【０００８】また、モンモリナイトを主成分とし、これ
にナトリウム化合物とマグネシウム化合物を加えたもの
（特公平６−７３４１９号）が、高吸水性とゲル化性が
あるというが、実施例でみるかぎり、吸水性が低い。[0008] Further, a product containing montmorillinite as a main component and a sodium compound and a magnesium compound added thereto (Japanese Patent Publication No. 6-73419) has high water absorption and gelling properties. Low water absorption.

【０００９】以上のほかにも、種々の提案がみられる
が、以下に示すいずれにも実施例による具体的な効果が
示されていないので、尿処理剤として具有すべき吸水性
や消臭性、塊状化性等がバランスよく得られているかど
うか不明のものばかりである。すなわち、茶殻に製紙ス
ラッジ又はパルプや紙粉と、木粉、結着剤、吸水剤を組
合わせたもの（特開平６−７０５１号）があり、脱臭性
や殺菌性等があるという。また、製紙スラッジと木粉、
ゼオライト、吸水ポリマ−、界面活性剤、香料、ｐＨ指
示薬をを混合したもの（特開昭６１−２０２６３７号）
もある。[0009] In addition to the above, various proposals have been made, but none of the following shows the specific effects of the examples, and therefore, the water absorbing and deodorizing properties to be possessed as a urine treatment agent are required. It is unclear whether or not agglomeration and the like are obtained in a well-balanced manner. That is, there is a combination of papermaking sludge or pulp or paper powder with wood flour, a binder, and a water absorbing agent (Japanese Patent Application Laid-Open No. 6-7051). Also, papermaking sludge and wood flour,
A mixture of zeolite, water-absorbing polymer, surfactant, fragrance, and pH indicator (Japanese Patent Application Laid-Open No. 61-202637)
There is also.

【００１０】さらに、各種パルプと無機充填剤からなる
もの（特公平３−８７３８号）が粒状物の飛散を防ぎ、
パルプスラッジと１０〜３０重量％の炭酸カルシウムか
らなるもの（特開平２−１７７８３３号）が、取扱いや
すく脱臭性もあるという。[0010] In addition, a mixture of various pulp and an inorganic filler (Japanese Patent Publication No. 3-8738) prevents scattering of particulate matter,
A pulp sludge comprising 10 to 30% by weight of calcium carbonate (JP-A-2-177833) is said to be easy to handle and deodorizable.

【００１１】パルプ系粒状物の表面にカルボキシメチル
セルロ−スを被覆したもの（特公平４−４８４０７号）
が、使用後塊状化して廃棄処理が容易であるという。[0011] Pulp-based granular material coated on its surface with carboxymethyl cellulose (Japanese Patent Publication No. 4-48407)
However, it is said that it is agglomerated after use and is easily disposed of.

【００１２】ビ−トモスの粒状体に高吸水性ポリマ−を
添加した紙粉を被覆したもの、さらに、ビ−トモスに脱
臭補助材としてゼオライト粉末や活性化したフライアッ
シュ、活性炭粉末のいずれかを約３〜５％添加したもの
（特開平８−３０８４２０号）も提案されている。その
特長は水分と臭気の吸収性ならびに水分吸収後の保形性
にあるというが、その保形性が実際にはよくなく、廃棄
処理に手間どり、また、排尿後、ネコがその場を足で蹴
る習性により、尿吸収後の尿処理材が散乱するという欠
点もあり、実用上問題がある。A beet moss granule coated with a paper powder containing a superabsorbent polymer added thereto, and a beet moss further coated with zeolite powder, activated fly ash or activated carbon powder as a deodorizing aid. There has also been proposed one containing about 3 to 5% (Japanese Patent Laid-Open No. 8-308420). Its features are absorption of moisture and odor and shape retention after moisture absorption.However, the shape retention is actually not good, and it is troublesome to dispose of the cat. There is also a drawback that the urine treatment material after urine absorption is scattered due to the habit of kicking, and there is a practical problem.

【００１３】[0013]

【発明が解決しようとする課題】本発明はネコなどペッ
ト用の尿処理材として、尿の吸水性ならびに脱臭性があ
り、吸水後の塊状化により廃棄処理しやすく、可燃ごみ
として廃棄処理可能なものを提供せんとするものであ
る。DISCLOSURE OF THE INVENTION The present invention is a urine treatment material for pets such as cats, which has water absorption and deodorization properties of urine, and is easy to dispose by agglomeration after water absorption, and can be disposed of as combustible waste. They don't offer anything.

【００１４】[0014]

【課題を解決するための手段】ここにおいて本発明者
は、これを解決するペット用尿処理材として、粒状無機
多孔体、パルプスラッジのいずれかを紙粉と高吸水性樹
脂粉末の混合物で被覆してあるものを見出し、その製造
方法として、粒状無機多孔体、パルプスラッジのいずれ
かに水を添加したものに、紙粉と高吸水性樹脂粉末の混
合物を振動板上で被覆し造粒すればよく、これらにおい
て、無機多孔体がゼオライト、パ−ライト、軽石、赤
玉、鹿沼土、活性炭のいずれかであり、高吸水性樹脂粉
末は架橋型ポリアクリル酸ナトリウムが最好適であるこ
とを見出すにいたった。In order to solve this problem, the present inventor coated a granular inorganic porous material or a pulp sludge with a mixture of paper powder and superabsorbent resin powder as a pet urine treatment material. As a manufacturing method, a mixture of paper powder and superabsorbent resin powder was coated on a diaphragm with water added to either a granular inorganic porous material or pulp sludge, and granulation was performed. In these, the inorganic porous body is any of zeolite, perlite, pumice, akadama, Kanuma soil, and activated carbon, and the crosslinked sodium polyacrylate is most preferable as the superabsorbent resin powder. I found it.

【００１５】[0015]

【発明の実施の形態】本発明において尿処理材の芯材と
して、粒状無機多孔体やパルプスラッジを使用すること
ができ、粒状無機多孔体には、ゼオライトやパ−ライ
ト、軽石、赤玉、鹿沼土、活性炭、クリストバライト、
セピオライト、ケイソウ土などがあげられる。なお、軽
石は火山レキも含み、ケイソウ土は焼結してから使用す
る。これらのほか、天然有機物粉末として、木粉やもみ
がら、ピ−ナッツの豆皮ならびに殻なども芯材に使用す
ることができる。これらは脱臭性と吸水性を有し、ゼオ
ライトはとくにアンモニヤに対する消臭効果が大であ
る。しかしながら、これらは吸水性に限界があるので、
単独使用では不充分である。BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, a granular inorganic porous material or pulp sludge can be used as a core material of a urine treatment material. Examples of the granular inorganic porous material include zeolite, perlite, pumice, Akadama, and Kanuma. Earth, activated carbon, cristobalite,
Sepiolite, diatomaceous earth, and the like. Pumice also includes volcanic rock, and diatomaceous earth is used after sintering. In addition, as natural organic powder, wood flour, rice husk, peanut husks and shells can be used as the core material. These have a deodorizing property and a water absorbing property, and zeolite has a large deodorizing effect especially on ammonia. However, these have limited water absorption,
Use alone is not sufficient.

【００１６】そこで、粒状無機多孔体等の吸水性を補足
するため、粒状無機多孔体やパルプスラッジの表面を紙
粉で被覆することにした。紙粉には微細孔があり、これ
により尿液が毛細管現象により吸収される。Therefore, in order to supplement the water absorption of the granular inorganic porous material and the like, the surface of the granular inorganic porous material and the pulp sludge are coated with paper powder. Paper powder has micropores, which allow urine to be absorbed by capillary action.

【００１７】しかしながら、紙粉だけでは相互に、かつ
ゼオライト等の粒状無機多孔体やパルプスラッジの表面
に付着しないので、高吸水性樹脂粉末を介在させる。高
吸水性樹脂粉末は架橋型ポリアクリル酸ナトリウムやで
んぷん−アクリル酸ナトリウムのグラフト共重合体、ビ
ニルアルコ−ルとアクリル酸の共重合体などをはじめと
して多くの種類が知られており、それ自体、水の吸収能
力がきわめてすぐれ、多量の水を吸収してゲル化する性
質を有している。とくに、架橋型ポリアクリル酸ナトリ
ウムが本発明目的に最好適であることが判明している。
紙粉を相互に、かつゼオライト等の粒状無機多孔体やパ
ルプスラッジの表面に対し付着させるため、尿処理材の
製造過程において、芯材となるゼオライト等の粒状無機
多孔体やパルプスラッジに予め少量の水を添加しておく
必要がある。However, since the paper powder alone does not adhere to each other and to the surface of the granular inorganic porous material such as zeolite or the pulp sludge, the superabsorbent resin powder is interposed. Many types of superabsorbent resin powders are known, including crosslinked sodium polyacrylate and starch-sodium acrylate graft copolymers, copolymers of vinyl alcohol and acrylic acid, and as such, It has a very good water absorption capacity and has the property of absorbing a large amount of water and gelling. In particular, it has been found that crosslinked sodium polyacrylate is most suitable for the purposes of the present invention.
In order to adhere paper powder to each other and to the surface of pulp sludge and granular inorganic porous material such as zeolite, a small amount of pulp sludge is added to pulp sludge and zeolite as core material in the manufacturing process of urine treatment material. Of water must be added.

【００１８】本発明のペット用尿処理材として、吸水性
と脱臭性のバランスを保持しながら、比較的高価な紙粉
と高吸水性樹脂粉末の最適使用量を選択して、取扱いや
すい大きさの粒状体にする。この観点から、芯材となる
ゼオライト等の粒状無機多孔体やパルプスラッジの粒径
は０．２〜１０ｍｍのものを使用する。芯材には水を予
め加えておくが、水は高吸水性樹脂粉末を介して紙粉を
相互に付着させ、同時に、紙粉をゼオライト等の粒状無
機多孔体やパルプスラッジの表面に付着させ、被覆する
ために不可欠である。この目的達成のため，ゼオライト
等の粒状無機多孔体やパルプスラッジの表面を湿潤させ
る程度に適度の水を加えておくと効果的であることが判
明している。ゼオライト等の粒状無機多孔体やパルプス
ラッジを被覆する紙粉や高吸水性樹脂粉末は粒径０．５
ｍｍ以下のものが適当である。これら相互の結合やゼオ
ライト等の粒状無機多孔体やパルプスラッジへの被覆、
すなわちペット用尿処理材とする粒状体の成形は，芯材
のゼオライト等の粒状無機多孔体やパルプスラッジと紙
粉、高吸水性樹脂粉末の混合物を市販の円型振動機に供
給しておこない、造粒後、乾燥させたものを使用する。As the urine-treating material for pets of the present invention, while maintaining the balance between water absorption and deodorizing properties, the optimum use amount of relatively expensive paper powder and super-absorbent resin powder is selected, and the size is easy to handle. Into a granular material. From this viewpoint, a granular inorganic porous material such as zeolite or a pulp sludge serving as a core material having a particle size of 0.2 to 10 mm is used. Water is added to the core material in advance, but the water causes the paper powder to adhere to each other via the superabsorbent resin powder, and at the same time, causes the paper powder to adhere to the surface of the granular inorganic porous material such as zeolite or the pulp sludge. Indispensable for coating. In order to achieve this object, it has been found effective to add an appropriate amount of water to such an extent that the surface of the granular inorganic porous material such as zeolite or the pulp sludge is wetted. Paper powder or highly water-absorbent resin powder that coats a granular inorganic porous material such as zeolite or pulp sludge has a particle size of 0.5.
mm or less is suitable. Coupling of these mutual bonds and granular inorganic porous materials such as zeolite and pulp sludge,
In other words, the formation of the granular material used as urine treatment material for pets is performed by supplying a granular inorganic porous material such as zeolite as a core material or a mixture of pulp sludge, paper powder and superabsorbent resin powder to a commercially available circular vibrator. After granulation, the dried product is used.

【００１９】[0019]

【実施例】以下、実施例により本発明をさらに具体的に
説明する。芯材となる粒径０．２〜１０ｍｍのゼオライ
ト１００重量部に水１５重量部を含浸させたものを円型
振動機の一方のフィ−ダ−に供給し、同時に、粒径０．
５ｍｍ以下の紙粉（日本製紙（株）製、ＫＣフロックＷ
−１００）１６重量部に粒径０．５ｍｍ以下の架橋型ポ
リアクリル酸ナトリウム（三洋化成工業（株）製、サン
フレッシュＳＣＬ−１）９重量部を加えてたものを他の
フィ−ダ−より供給する。これらの材料を円型振動機の
円周に沿って移動させることにより、高吸水性樹脂粉末
の架橋型ポリアクリル酸ナトリウムがゼオライトのもつ
水分を吸収して膨潤し、粘着性を帯びて紙粉を相互に付
着させながら、ゼオライトに付着させ、振動によりその
付着力が増強されながら造粒体が得られ、排出される。
得られた製品は８０〜９０℃で２０分間乾燥してペット
用尿処理材とする。The present invention will be described more specifically with reference to the following examples. 100 parts by weight of zeolite having a particle size of 0.2 to 10 mm serving as a core material and impregnated with 15 parts by weight of water are supplied to one feeder of a circular vibrator.
Paper powder of 5 mm or less (KC Flock W, manufactured by Nippon Paper Industries Co., Ltd.)
-100) 16 parts by weight of 9 parts by weight of crosslinked sodium polyacrylate (Sunfresh SCL-1 manufactured by Sanyo Chemical Industries, Ltd.) having a particle size of 0.5 mm or less was added to another feeder. Supply from By moving these materials along the circumference of the circular vibrator, the cross-linked sodium polyacrylate of the superabsorbent resin powder absorbs the moisture of the zeolite and swells, and becomes sticky to the paper powder. Are adhered to zeolite while adhering to each other, and the granules are obtained and discharged while the adhesion is enhanced by vibration.
The obtained product is dried at 80 to 90 ° C. for 20 minutes to obtain a urine treating material for pets.

【００２０】なお、ゼオライト使用の場合の実用し得る
配合割合を述べれば、固形物中、ゼオライト３０〜９２
重量％、紙粉５〜３５重量％、高吸水性樹脂粉末３〜３
５重量％であり、水はゼオライトの７〜３５重量％相当
を使用すればよい。When the zeolite is used, the practicable mixing ratio is described as follows.
% By weight, paper powder 5 to 35% by weight, superabsorbent resin powder 3 to 3
5% by weight, and water may be used in an amount of 7 to 35% by weight of zeolite.

【００２１】ゼオライトの場合と同様にして、パ−ライ
ト、軽石、赤玉、鹿沼土、活性炭、パルプスラッジを芯
材とするペット用尿処理材が得られる。それらの配合割
合を第１表に示す。In the same manner as in the case of zeolite, a urine-treating material for pets having pearlite, pumice stone, Akadama, Kanuma soil, activated carbon, and pulp sludge as core materials is obtained. Table 1 shows the compounding ratios.

【００２２】[0022]

【表１】 [Table 1]

【００２３】得られたペット用尿処理材の水分吸収性能
ならびにアンモニア吸着性能について第２表に示す。な
お、比較のため、他のペット用尿処理材についての各性
能を第３表に示す。水分吸収性能は、時計皿に各試料を
１０．０ｇ計量して、メスピペットにより上から徐々に
水をふりかけ、試料が飽和状態になり、試料のまわりに
水分がにじみ出た点を終点とし、余剰水を取り除いて測
定した。Table 2 shows the water absorption performance and ammonia absorption performance of the obtained urine treating material for pets. For comparison, Table 3 shows the performance of other pet urine treatment materials. Moisture absorption performance was measured by weighing 10.0 g of each sample on a watch glass, sprinkling water gradually from above with a mesipette, saturating the sample, and ending the point where water oozed around the sample. The measurements were taken with water removed.

【００２４】アンモニア吸着性能は、３Ｌのテストパッ
クに各試料を２００ｍｌ入れ、０．５％のアンモニア水
１０ｃｃをふりかけた後、各時間経過後にパック内の残
留アンモニア濃度をアンモニア検知管で測定した。The ammonia adsorption performance was determined by placing 200 ml of each sample in a 3 L test pack, sprinkling 10 cc of 0.5% aqueous ammonia, and measuring the residual ammonia concentration in the pack after each time with an ammonia detector tube.

【００２５】[0025]

【表２】 [Table 2]

【表３】 [Table 3]

【００２６】測定結果から、水分吸収性能ならびにアン
モニア吸着性能とも顕著な効果が認められる。しかしな
がら、芯材が赤玉の場合は水分吸収性能が若干劣るが、
アンモニア吸着性能がすぐれるし、また、活性炭の場合
は両性能とも若干劣るが実用に供し得る。From the measurement results, remarkable effects are recognized on both the water absorption performance and the ammonia adsorption performance. However, when the core material is red ball, the moisture absorption performance is slightly inferior,
Ammonia adsorption performance is excellent, and activated carbon can be put to practical use although both performances are slightly inferior.

【００２７】なお、実施例のペット用尿処理材の各かさ
比重を第４表に、比較例のそれを第５表に示すが、軽す
ぎても飛散しやすく、かさ比重０．４前後で、ある程度
軽いほうが持ち運びやすく、輸送費の面からも好まし
い。Table 4 shows the specific gravity of each of the urine treatment materials for pets in the example, and Table 5 shows the specific gravity of the comparative example. Lighter to some extent is easier to carry and is preferable in terms of transportation costs.

【００２８】[0028]

【表４】 [Table 4]

【表５】 [Table 5]

【００２９】[0029]

【発明の効果】本発明のペット用尿処理材はネコなどの
ペット用に尿の吸水能力が大で、かつ尿を吸収して団塊
となるので廃棄の際、取扱いが容易であり、脱臭性もか
なりあるので衛生的である。また、表面部が燃焼するの
で可燃ごみとして廃棄することができる。The pet urine treating material of the present invention has a large water absorbing capacity for urine for pets such as cats, and is easy to handle at the time of disposal because it absorbs urine and forms a lump. It is also sanitary because there is considerable. Further, since the surface portion burns, it can be discarded as combustible waste.

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 粒状無機多孔体、パルプスラッジのいず
れかを紙粉と高吸水性樹脂粉末の混合物で被覆してある
ペット用尿処理材。1. A pet urine treatment material in which one of a granular inorganic porous material and pulp sludge is coated with a mixture of paper powder and superabsorbent resin powder. 【請求項２】 粒状無機多孔体、パルプスラッジのいず
れかに水を添加したものに、紙粉と高吸水性樹脂粉末の
混合物を振動板上で被覆し造粒するペット用尿処理材の
製造方法。2. Manufacture of a urine treating material for pets in which a mixture of paper powder and superabsorbent resin powder is coated on a diaphragm and granulated by adding water to either the granular inorganic porous material or pulp sludge. Method. 【請求項３】 無機多孔体がゼオライト、パ−ライト、
軽石、赤玉、鹿沼土、活性炭のいずれかである請求項１
記載のペット用尿処理材又は請求項２記載のペット用尿
処理材の製造方法。3. An inorganic porous material comprising zeolite, perlite,
2. A pumice, Akadama, Kanuma soil, or activated carbon.
A method for producing the pet urine treating material according to claim 2 or the pet urine treating material according to claim 2. 【請求項４】 高吸水性樹脂粉末が架橋型ポリアクリル
酸ナトリウムである請求項１記載のペット用尿処理材又
は請求項２記載のペット用尿処理材の製造方法。4. The method for producing a pet urine treatment material according to claim 1, wherein the superabsorbent resin powder is cross-linked sodium polyacrylate.