JPH11350293A - Net - Google Patents

Abstract

PROBLEM TO BE SOLVED: To produce a net resistant to shock of heavy material, etc., by using a thermoplastic synthetic fiber having respectively specific single fiber fineness, strength and elongation and setting the mesh size of the net within a specific range. SOLUTION: A knotless net or a raschel net is knit with a polyester or polyamide thermoplastic synthetic fiber having a total fineness of >=550 dtex, a single fiber fineness of <=3.5 dtex, preferably <=3.0 dtex, a strength of >=6.0 CN/dtex and an elongation of 15-40% to obtain a net having a mesh size of 10-200 mm, preferably 15-50 mm.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、各種の土木・建築
工事や、農林水産業や運送業における被覆・包装材料、
フィルター材料、補強材料に用いることができる。さら
に詳細には、熱可塑性合成繊維よりなる防雪ネット、落
石防止ネット、安全ネット、養生ネット、法面保護ネッ
ト、護岸吸い出し防止ネット等として用いられるネット
に関し、特に、例えば石や土砂の落下または重機の踏み
つけ等、重量物による衝撃に強いネットに関する。TECHNICAL FIELD The present invention relates to coating and packaging materials for various types of civil engineering and construction, agriculture, forestry and fisheries, and transportation.
It can be used for filter materials and reinforcing materials. More specifically, the present invention relates to a net used as a snow protection net, a rock fall prevention net, a safety net, a curing net, a slope protection net, a seawall suction prevention net made of thermoplastic synthetic fiber, and particularly, for example, for dropping stones and earth and sand or heavy machinery. It relates to a net that is resistant to the impact of heavy objects such as trampling.

【０００２】[0002]

【従来の技術】従来、例えば防波堤の施工の際の埋め立
て工事において、石や土砂の流出を防止するために土木
用のネットを敷設する。このような従来のポリエステル
またはポリプロピレン等の合成繊維からなるネットは施
工の際の石の落下や重機等の踏みつぶしによって裂傷を
生じやすく、本来のフィルターとしての役割を十分果た
すことができなかった。2. Description of the Related Art Conventionally, for example, in a landfill work for constructing a breakwater, a net for civil engineering is laid to prevent outflow of stones and earth and sand. Such conventional nets made of synthetic fibers such as polyester or polypropylene are apt to be torn due to dropping of stones during construction or crushing of heavy equipment or the like, and cannot sufficiently fulfill the role of the original filter.

【０００３】また例えば堤防の護岸や橋脚の洗堀防止を
目的として、ネットの中に石を詰めて補強材とする工法
があるが、投入される石や上流から流れてくる土砂等に
よって時として破れるという問題があった。For example, there is a construction method in which stones are stuffed into a net and used as a reinforcing material for the purpose of embankment of a dike or prevention of scouring of a pier. There was a problem of tearing.

【０００４】これらの問題を解決するために、金網等が
使用される等してきた。しかしながら金網は剛性が高く
て運搬に労力がかかり、また地面や石等の形状になじみ
にくいので局所的にこれらに接した部分に応力が集中し
て破断しやすく、また水場の近くでは錆によって著しく
強度が低下してしまう。さらに金網は剛性が高いことに
加えて重量が重いので、施工性に問題がある。In order to solve these problems, wire nets and the like have been used. However, wire mesh has high rigidity and requires labor for transportation, and it is difficult to adjust to the shape of the ground or stones, so stress concentrates locally on the parts that are in contact with them and easily breaks, and rust near water places The strength is significantly reduced. Further, the wire mesh has a high rigidity and a heavy weight, so that there is a problem in workability.

【０００５】合成繊維を使用する場合は破断しにくいよ
うに使用する糸量を増やしたネットにしたり、塩ビ等の
樹脂を被覆してグリッドにする等しているが、いずれも
使用する合成繊維や樹脂の量が増えるので、重量の増加
に伴う施工性の悪化やコストの上昇等の問題を避けられ
ない。When synthetic fibers are used, nets are used in which the amount of yarn used is increased so as not to be easily broken, or grids are formed by coating a resin such as polyvinyl chloride. Since the amount of resin increases, problems such as deterioration of workability and increase in cost due to increase in weight cannot be avoided.

【０００６】[0006]

【発明が解決しようとする課題】本発明は、このような
従来技術を背景になされたもので、例えば防波堤の施工
の際の土砂の落下によっても裂傷や破断を生じ難いとい
う特性を、樹脂被覆なしで、あるいは被覆樹脂量を減ら
して実現する、もしくは少ない糸量でも満足な特性を発
現するネットを提供しようとするものである。SUMMARY OF THE INVENTION The present invention is based on the background of the prior art, and is characterized by the fact that, for example, when a breakwater is dropped, earth and sand are less likely to be torn or ruptured by a resin coating. It is an object of the present invention to provide a net which can be realized without using the coating resin or by reducing the amount of the coating resin, or exhibiting satisfactory characteristics even with a small amount of yarn.

【０００７】[0007]

【課題を解決するための手段】本発明は上記課題を解決
するため、主として次の構成を有する。すなわち、単繊
維繊度３．５ｄｔｅｘ以下の熱可塑性合成繊維からなる
ことを特徴とするネットである。SUMMARY OF THE INVENTION The present invention mainly has the following constitution in order to solve the above-mentioned problems. That is, the net is made of a thermoplastic synthetic fiber having a single fiber fineness of 3.5 dtex or less.

【０００８】[0008]

【発明の実施の形態】本発明のネットを、例えば防波堤
の施工の際に用いれば、土砂の落下によっても裂傷・破
断を生じにくく、裂傷に起因する土砂や石等の流出を防
止することができる。また例えば堤防の護岸や橋脚の洗
堀防止を目的として、ネットの中に石を詰めて補強材と
する工法に使用する場合は、投入される石や上流から流
れてくる土砂や岩石等によって破れるということが少な
くなり、設備の維持・管理が容易になる。また本発明の
ネットは被覆材料をなくしたり減らしたりして使用でき
るので軽量性・柔軟性に優れ、従って施工性が良好であ
る。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS If the net of the present invention is used, for example, in the construction of a breakwater, it is difficult to cause tears and breaks even when the earth and sand falls, and it is possible to prevent the outflow of earth and sand, stones, etc. due to the tear. it can. For example, in the case of using a method of packing stones in a net and using it as a reinforcing material for the purpose of embankment protection of a dike or prevention of scouring of piers, it will be broken by stones input, earth and sand or rocks flowing from the upstream And the maintenance and management of the equipment becomes easier. Further, the net of the present invention can be used with or without a coating material, so that it is excellent in lightness and flexibility, and therefore, has good workability.

【０００９】以下、本発明を詳細に説明する。Hereinafter, the present invention will be described in detail.

【００１０】本発明のネットは網地であり、菱目、亀甲
目、角目等公知の網目を用いることができまた等辺でな
くともよい。網地種も、結節網、無結節網、ラッセル
網、もじ網、織網等いずれをも含むが、結節点が結び目
にならない網地は土砂や石等から加えられる応力が集中
せず破断しにくくなるので、結節を作らない無結節網や
ラッセル網が好ましい。[0010] The net of the present invention is a net, and a known mesh such as a rhombus, a turtle-shape, and a square may be used, and the net may not be equilateral. Netting types also include knotted nets, knotless nets, Russell nets, braided nets, woven nets, etc., but meshes where nodal points do not become knots do not concentrate stress applied from soil, stone, etc. A knotless net or a Russell net that does not form a knot is preferable because it becomes difficult.

【００１１】本発明において目合いとは一つの網目の長
さをｍｍ単位で示した値を意味する。 本発明のネット
の目合いはその使用目的により異なるが、１０ｍｍ以
上、２００ｍｍ以下であることが好ましく、１５ｍｍ以
上、５０ｍｍ以下であるとさらに好ましい。目合いを１
０ｍｍ以上とすることにより細かい砂が詰まらずフィル
ター機能を有効に果たすことができ、またコストを下げ
ることができる。また目合いを２００ｍｍ以下とするこ
とによりネットでの所望の物体の捕捉が確実となり、ま
た使用する糸の繊度を不必要に大きくすることがなくな
るため耐衝撃圧縮特性を良好なものとすることができ
る。In the present invention, “mesh” means a value indicating the length of one mesh in mm. The mesh size of the net of the present invention varies depending on the purpose of use, but is preferably 10 mm or more and 200 mm or less, more preferably 15 mm or more and 50 mm or less. One eyesight
By setting the thickness to 0 mm or more, fine sand is not clogged, the filter function can be effectively performed, and the cost can be reduced. Also, by setting the mesh size to 200 mm or less, the desired object can be reliably captured by the net, and the impact compression property can be improved because the fineness of the yarn to be used is not unnecessarily increased. it can.

【００１２】さらに、本発明のネットは網地のみで構成
される必要はない。例えば塩化ビニルやエチレン−ビニ
ルアルコール（ＥＶＡ）、ポリウレタン等の樹脂で最小
限の被覆が行われても構わず、施工性を阻害しない範囲
での構造体とすればよい。Further, the net of the present invention does not need to be constituted only by netting. For example, the structure may be minimally coated with a resin such as vinyl chloride, ethylene-vinyl alcohol (EVA), or polyurethane, and may be a structure within a range that does not hinder workability.

【００１３】本発明のネットを構成する熱可塑性合成繊
維の単繊維繊度は３．５ｄｔｅｘ以下であることが必要
であり、３．０ｄｔｅｘ以下が好ましい。単繊維繊度が
３．５ｄｔｅｘを越えると十分な耐衝撃圧縮特性を発現
することができない。The single-filament fineness of the thermoplastic synthetic fiber constituting the net of the present invention must be 3.5 dtex or less, and preferably 3.0 dtex or less. If the single fiber fineness exceeds 3.5 dtex, sufficient impact compression resistance cannot be exhibited.

【００１４】単繊維繊度が小さい場合に耐衝撃圧縮特性
が向上する理由は、以下のように考えられる。すなわ
ち、単繊維繊度が小さい糸条が石等で押しつぶされた場
合、糸条断面の変形が速いために押しつぶし圧力が分散
しやすい。また、単糸−単糸間の表面積が広いために圧
縮変形のエネルギーが摩擦熱へ転換しやすく、発生した
熱も単繊維内へ蓄えられることなく放散しやすい。The reason why the impact compression resistance is improved when the single fiber fineness is small is considered as follows. That is, when a yarn having a small single fiber fineness is crushed by a stone or the like, the crushing pressure is easily dispersed because the cross section of the yarn is rapidly deformed. In addition, since the surface area between single yarns is large, the energy of compression deformation is easily converted to frictional heat, and the generated heat is easily dissipated without being stored in the single fibers.

【００１５】本発明のネットを構成する熱可塑性合成繊
維の強度は６．０ｃＮ／ｄｔｅｘ以上であることが好ま
しい。強度を６．０ｃＮ／ｄｔｅｘより大きくすること
によって、ネットとしての引張強度や引裂強度をより高
めることができ、また圧縮衝撃特性が向上し、さらにネ
ットを軽量化し、施工性を良好にすることができる。The strength of the thermoplastic synthetic fiber constituting the net of the present invention is preferably 6.0 cN / dtex or more. By increasing the strength to more than 6.0 cN / dtex, the tensile strength and tear strength of the net can be further increased, the compression impact characteristics can be improved, the net can be reduced in weight, and the workability can be improved. it can.

【００１６】本発明のネットを構成する熱可塑性合成繊
維の伸度は１５％以上４０％以下であることが好まし
い。伸度が１５％以上であると糸条に石等の重量物があ
たった際、糸条の変形をある程度大きくすることがで
き、圧縮応力が局部に集中しにくくなるため破断に至り
にくい。一方、伸度を４０％以下とすることによりネッ
トとしての十分な強度を得ることができ、軽量化に寄与
する。The elongation of the thermoplastic synthetic fiber constituting the net of the present invention is preferably 15% or more and 40% or less. When the elongation is 15% or more, when a heavy object such as a stone hits the yarn, the deformation of the yarn can be increased to some extent, and the compressive stress is less likely to be concentrated on a local portion, so that the yarn is hardly broken. On the other hand, by setting the elongation to 40% or less, sufficient strength as a net can be obtained, which contributes to weight reduction.

【００１７】また、本発明のネットを構成する熱可塑性
合成繊維の総繊度が５５０ｄｔｅｘ以上であることが好
ましい。総繊度が５５０ｄｔｅｘ以上である場合、ネッ
トの引張強度や引裂強度が十分となり、それに伴って圧
縮衝撃特性が高くなる。総繊度の上限は特になく、施工
性に悪影響を与えない範囲で大きな繊度の繊維を用いれ
ばよい。Further, it is preferable that the total fineness of the thermoplastic synthetic fiber constituting the net of the present invention is 550 dtex or more. When the total fineness is 550 dtex or more, the tensile strength and tear strength of the net are sufficient, and the compression impact characteristics are accordingly increased. There is no particular upper limit on the total fineness, and fibers having a large fineness may be used as long as the workability is not adversely affected.

【００１８】本発明のネットを構成する繊維は、上記の
ように機械的物性を得やすい点や、単繊維繊度を小さく
しやすいこと、また経済的な観点から熱可塑性合成繊維
であり、ポリエステル系繊維、ポリアミド系繊維、ポリ
フェニレンサルファイド系繊維、ポリエチレン系繊維、
ポリプロピレン系繊維等から選ばれた少なくとも１種で
あり、耐光性や耐熱性、強度等の面からポリエステル系
繊維またはポリアミド系繊維が好ましい。ポリエステル
系繊維としては、ポリエチレンテレフタレート、ポリブ
チレンテレフタレート、ポリエチレン２，６−ナフタレ
ート、ポリシクロヘキサンジメチレンテレフタレート、
ポリカプロラクトン、ポリ乳酸、ポリブチレンサクシネ
ート等からなる繊維が好ましい。これらの中でも、価
格、耐光性の点からポリエチレンテレフタレートが特に
好ましい。これらポリエステルのジカルボン酸成分の一
部をイソフタル酸、２,６−ナフタレンジカルボン酸、
１,４−シクロヘキサンジカルボン酸、アジピン酸、セ
バシン酸、ダイマー酸、スルホン酸金属塩置換イソフタ
ル酸、トリメリット酸、トリメシン酸等で置き換えても
良く、ジオール成分の一部をジエチレングリコール、ネ
オペンチルグリコール、１，４−シクロヘキサンジオー
ル、ビスフェノールＡのエチレンオキサイド付加物等で
置き換えることができる。また、ポリアミド系繊維とし
ては、ポリカプラミド、ポリヘキサメチレンアジパミ
ド、ポリテトラメチレンアジパミド、ポリヘキサメチレ
ンセバカミド、ポリドデカミド等からなる繊維が好まし
い。The fiber constituting the net of the present invention is a thermoplastic synthetic fiber from the viewpoint of easily obtaining mechanical properties as described above, reducing the fineness of a single fiber, and economically, and is a polyester-based fiber. Fiber, polyamide fiber, polyphenylene sulfide fiber, polyethylene fiber,
It is at least one selected from polypropylene fibers and the like, and polyester fibers or polyamide fibers are preferable in terms of light resistance, heat resistance, strength and the like. As the polyester fiber, polyethylene terephthalate, polybutylene terephthalate, polyethylene 2,6-naphthalate, polycyclohexane dimethylene terephthalate,
Fibers composed of polycaprolactone, polylactic acid, polybutylene succinate and the like are preferred. Among these, polyethylene terephthalate is particularly preferred in terms of price and light resistance. Part of the dicarboxylic acid component of these polyesters is isophthalic acid, 2,6-naphthalenedicarboxylic acid,
1,4-cyclohexanedicarboxylic acid, adipic acid, sebacic acid, dimer acid, sulfonic acid metal salt-substituted isophthalic acid, trimellitic acid, trimesic acid, etc. may be replaced. It can be replaced with 1,4-cyclohexanediol, an ethylene oxide adduct of bisphenol A, or the like. As the polyamide fibers, fibers composed of polycapramid, polyhexamethylene adipamide, polytetramethylene adipamide, polyhexamethylene sebacamide, polydodecamide and the like are preferable.

【００１９】さらに、屋外で使用したり、川や海等水の
近くで使用する場合には、耐光性に優れ、水中強力の低
下が少ないポリエステル系繊維が特に好ましい。Further, when used outdoors or near waters such as rivers and seas, polyester fibers having excellent light resistance and little decrease in water strength are particularly preferred.

【００２０】本発明の熱可塑性合成繊維は通常の溶融紡
糸で得られるもので構わない。すなわち、上記熱可塑性
ポリマーを、例えばエクストルーダーやプレッシャーメ
ルター型紡糸機で溶融した後メタリングポンプによって
計量し、紡糸パック内等で濾過を行った後、口金から吐
出される。吐出された糸は冷却風等によって冷却・固化
された後、油剤を付与されて、引き取られ、その後延伸
される。延伸の前に一旦巻き取る２工程法を用いても、
紡糸後巻き取ることなく引き続いて延伸を行う直接紡糸
延伸法を用いてもどちらでも構わないが、生産性の良さ
からは直接紡糸延伸法が好ましい。引き取り速度は繊維
強度の観点から４０００ｍ／分以下、また生産性の観点
から３００ｍ／分以上であることが好ましい。延伸倍率
は引き取り速度によって変わり、得られた繊維の伸度が
上記したような範囲になるように調整されればよい。さ
らに、紡出直下、冷却・固化の前には加熱帯を設置して
糸条をポリマーの融点以上の温度に加熱し、繊維の強度
を高めることが好ましい。延伸は１段延伸でも２段以上
の多段延伸でも構わないが、強度を得る観点から２〜３
段延伸が好ましく、巻き取り前にはポリマーの融点より
２０〜８０℃程度低い温度で熱処理が行われることが好
ましく、また寸法安定性の観点から１〜２０％の弛緩処
理が行われることが好ましい。The thermoplastic synthetic fibers of the present invention may be those obtained by ordinary melt spinning. That is, the thermoplastic polymer is melted by, for example, an extruder or a pressure melter type spinning machine, measured by a metering pump, filtered in a spin pack, or the like, and then discharged from a spinneret. The discharged yarn is cooled and solidified by a cooling air or the like, applied with an oil agent, taken off, and then drawn. Even if a two-step method of winding once before stretching is used,
Either of the direct spinning and drawing methods in which the drawing is carried out without winding after spinning may be used, but the direct spinning and drawing method is preferred from the viewpoint of productivity. The take-up speed is preferably 4000 m / min or less from the viewpoint of fiber strength and 300 m / min or more from the viewpoint of productivity. The draw ratio changes depending on the take-up speed, and may be adjusted so that the elongation of the obtained fiber is in the above-mentioned range. Further, immediately after spinning and before cooling and solidification, a heating zone is preferably provided to heat the yarn to a temperature equal to or higher than the melting point of the polymer to increase the fiber strength. The stretching may be one-stage stretching or multi-stage stretching of two or more stages.
Step stretching is preferred, and heat treatment is preferably performed at a temperature about 20 to 80 ° C. lower than the melting point of the polymer before winding, and 1 to 20% relaxation treatment is preferably performed from the viewpoint of dimensional stability. .

【００２１】ネットの網地強度は施工現場や用途によっ
て異なるが、例えば防波堤や堤防の吸い出し防止に使わ
れる場合には２５ｋｇｆ以上、好ましくは３０ｋｇｆ以
上である。２５ｋｇｆ未満であると、波力や埋め立て土
砂による衝撃や集中応力によって、裂傷を生じやすい。
このような網地強度は、構成する熱可塑性合成繊維の強
度を高めたり、織り密度を高くする等して効率的に得る
ことが可能であるが、ネットの軽量化の目的から、前記
したように強度の高い原糸を使用することが好ましい。The net strength of the net varies depending on the construction site and application, but is, for example, 25 kgf or more, and preferably 30 kgf or more when used for preventing breakwaters or embankments from being sucked out. If the weight is less than 25 kgf, tears are likely to occur due to impact or concentrated stress due to wave force or landfill sand.
Such a net strength can be efficiently obtained by increasing the strength of the thermoplastic synthetic fibers constituting the woven fabric or increasing the weaving density, but for the purpose of reducing the weight of the net, as described above. It is preferable to use a high-strength raw yarn.

【００２２】以下、実施例により本発明の特徴を具体的
に説明する。Hereinafter, the features of the present invention will be described specifically with reference to examples.

【００２３】[0023]

【実施例】本実施例における測定方法を以下に示す。EXAMPLE A measuring method in this example is described below.

【００２４】（ａ）繊維の強度、伸度 試料を気温２０℃、湿度６５％の温調室にてテンシロン
引張試験機を用い、糸長２５ｃｍ、引張速度３０ｃｍ／
分で測定した。(A) Fiber strength and elongation A sample was taken in a temperature controlled room at a temperature of 20 ° C. and a humidity of 65% using a Tensilon tensile tester, with a yarn length of 25 cm and a tensile speed of 30 cm /.
Measured in minutes.

【００２５】（ｂ）ネットの網地強度および伸長度 図２のように作製した図３に示す試料を定速伸長型引張
試験機によって、気温２０℃、湿度６５％の室内で試験
片を、引張速度２０ｃｍ／分の条件で矢印の方向に引張
試験を行う。図２は引張試験用サンプルを、ネットから
サンプリングする方法を示すものであり、図３はサンプ
ルを引張試験機に取り付け、矢印の方向に強力を測定す
る状況を示すものである。(B) Net Mesh Strength and Degree of Elongation The sample shown in FIG. 3 prepared as shown in FIG. 2 was subjected to a constant-speed elongation type tensile tester in a room at a temperature of 20 ° C. and a humidity of 65%. A tensile test is performed in the direction of the arrow at a tensile speed of 20 cm / min. FIG. 2 shows a method for sampling a tensile test sample from a net, and FIG. 3 shows a situation where the sample is attached to a tensile tester and strength is measured in the direction of the arrow.

【００２６】（ｃ）耐光性試験 ＪＩＳ Ｌ ０８４２の規定により、カーボンフェード
メーターによる光照射（６３℃×光照射５００時間）を
行い、照射後の強力を測定し、強力保持率を求めた。(C) Light Resistance Test According to the provisions of JIS L 0842, light irradiation (63 ° C. × 500 hours of light irradiation) was performed using a carbon fade meter, and the strength after irradiation was measured to determine the strength retention.

【００２７】また水中強度については、２０℃の水中に
２４時間浸漬して強力を測定し、強力保持率を求めた。Regarding the strength in water, the strength was measured by immersion in water at 20 ° C. for 24 hours, and the strength retention was determined.

【００２８】実施例１ ネットを構成する原糸として、引張強度６．２ｃＮ／ｄ
ｔｅｘ、伸度３５％、総繊度１５００ｄｔｅｘで、単繊
維繊度２．０ｄｔｅｘのポリエチレンテレフタレートフ
ィラメントを使用した。これを８本合わせて網糸とし、
一辺が２５ｍｍのラッセル網ネットを作製した。糸使い
を表１に、製織されたネットの特性を表２に示す。Example 1 The yarn constituting the net had a tensile strength of 6.2 cN / d.
A polyethylene terephthalate filament having a single fiber fineness of 2.0 dtex having a tex of 35% and an elongation of 35% and a total fineness of 1500 dtex was used. Eight of these are combined into a mesh thread,
A Russell net having a side of 25 mm was produced. Table 1 shows the use of yarn and Table 2 shows the characteristics of the woven net.

【００２９】[0029]

【表１】 [Table 1]

【表２】 実施例２ 引張強度８．０ｃＮ／ｄｔｅｘ、破断時の伸度が１７
％、単繊維繊度が２．０ｄｔｅｘのポリエチレンテレフ
タレートフィラメントを使用した。糸使いを表１に、製
織されたネットの特性を表２に併せて示す。[Table 2] Example 2 Tensile strength: 8.0 cN / dtex, elongation at break: 17
% Polyethylene terephthalate filament having a single fiber fineness of 2.0 dtex was used. Table 1 shows the use of yarn, and Table 2 shows the properties of the woven net.

【００３０】実施例３ 引張強度６．２ｃＮ／ｄｔｅｘ、破断時の伸度が３５
％、単繊維繊度が３．４ｄｔｅｘのポリエチレンテレフ
タレートフィラメントを使用した。糸使いを表１に、製
織されたネットの特性を表２に併せて示す。Example 3 Tensile strength: 6.2 cN / dtex, elongation at break: 35
%, A single fiber fineness of 3.4 dtex was used as the polyethylene terephthalate filament. Table 1 shows the use of yarn, and Table 2 shows the properties of the woven net.

【００３１】実施例４ 引張強度７．０ｃＮ／ｄｔｅｘ、破断時の伸度が３５
％、単繊維繊度が２．０ｄｔｅｘポリヘキサメチレンア
ジパミドフィラメントを使用した。糸使いを表１に、製
織されたネットの特性を表２に併せて示す。Example 4 Tensile strength: 7.0 cN / dtex, elongation at break: 35
%, A single fiber fineness of 2.0 dtex polyhexamethylene adipamide filament was used. Table 1 shows the use of yarn, and Table 2 shows the properties of the woven net.

【００３２】比較例１ 引張強度６．２ｃＮ／ｄｔｅｘ、破断時の伸度が３５
％、単繊維繊度が４．０ｄｔｅｘのポリエチレンテレフ
タレートフィラメントを使用した。糸使いを表１に、製
織されたネットの特性を表２に併せて示す。Comparative Example 1 Tensile strength: 6.2 cN / dtex, elongation at break: 35
%, A polyethylene terephthalate filament having a single fiber fineness of 4.0 dtex was used. Table 1 shows the use of yarn, and Table 2 shows the properties of the woven net.

【００３３】実施例５ 引張強度８．０ｃＮ／ｄｔｅｘ、破断時の伸度が１２
％、単繊維繊度が２．０ｄｔｅｘのポリエチレンテレフ
タレートフィラメントを使用した。糸使いを表１に、製
織されたネットの特性を表２に併せて示す。Example 5 Tensile strength: 8.0 cN / dtex, elongation at break: 12
% Polyethylene terephthalate filament having a single fiber fineness of 2.0 dtex was used. Table 1 shows the use of yarn, and Table 2 shows the properties of the woven net.

【００３４】実施例６ 引張強度５．０ｃＮ／ｄｔｅｘ、破断時の伸度が４５
％、単繊維繊度が２．０ｄｔｅｘのポリエチレンテレフ
タレートフィラメントを使用した。糸使いを表１に、製
織されたネットの特性を表２に併せて示す。Example 6 Tensile strength: 5.0 cN / dtex, elongation at break: 45
% Polyethylene terephthalate filament having a single fiber fineness of 2.0 dtex was used. Table 1 shows the use of yarn, and Table 2 shows the properties of the woven net.

【００３５】試験例 本発明の効果を実証するために、上記の実施例および比
較例について、以下の衝撃試験を行った。この衝撃試験
状況の模式的側面図を図１に示す。Test Examples In order to demonstrate the effects of the present invention, the following impact tests were performed on the above Examples and Comparative Examples. FIG. 1 shows a schematic side view of this impact test situation.

【００３６】コンクリート路地盤の上に、２ｍ四方の実
施例１〜３および比較例１〜３のネットを敷設した。次
いで路地盤より高さ１．５ｍのところから、径５〜１０
ｃｍの玉石をネットの中央部に落下させた。かかる衝撃
試験の後、注意して石を取り除き、ネット中央の６０ｃ
ｍ四方分を縦１５ｃｍ横７．５ｃｍの短冊状に裁断し
た。こうして取り出した３２個の試験片について網地強
度の測定を行い、衝撃試験前の試験片との引張強度を比
較して、衝撃試験後強力および衝撃試験後強力保持率を
計算した。その結果を表２に併せて示した。表２による
と、実施例１〜６の各ネットは衝撃試験後強力保持率が
７０％以上と高い。The nets of Examples 1 to 3 and Comparative Examples 1 to 3 each having a length of 2 m were laid on the concrete ground. Next, from a height of 1.5 m above the alley ground, a diameter of 5 to 10
cm stone was dropped on the center of the net. After such an impact test, the stone was carefully removed and the center 60c
m squares were cut into strips measuring 15 cm long and 7.5 cm wide. The net strength was measured for the 32 test pieces taken out in this way, and the tensile strength after the impact test and the strength retention after the impact test were calculated by comparing the tensile strength with the test piece before the impact test. The results are shown in Table 2. According to Table 2, each net of Examples 1 to 6 has a high strength retention of 70% or more after the impact test.

【００３７】[0037]

【発明の効果】本発明によれば、例えば防波堤の施工の
際の土砂の落下によっても裂傷を生じ難く、施工性のす
ぐれた軽量のネットを得ることができる。According to the present invention, it is possible to obtain a lightweight net which is less likely to be torn even by falling of earth and sand at the time of construction of a breakwater and which has excellent workability.

【図面の簡単な説明】[Brief description of the drawings]

【図１】衝撃試験状況の模式的側面図。FIG. 1 is a schematic side view of an impact test situation.

【図２】引張試験用サンプルを、ネットからサンプリン
グする方法を示す平面図。FIG. 2 is a plan view showing a method of sampling a tensile test sample from a net.

【図３】引張試験機により、矢印の方向に強力を測定す
る状況を示す側面図。FIG. 3 is a side view showing a situation where strength is measured in the direction of an arrow by a tensile tester.

Claims (5)

【特許請求の範囲】[Claims] 【請求項１】 単繊維繊度３．５ｄｔｅｘ以下の熱可塑
性合成繊維からなることを特徴とするネット。1. A net comprising a thermoplastic synthetic fiber having a single fiber fineness of 3.5 dtex or less. 【請求項２】 単繊維繊度が３．０ｄｔｅｘ以下である
ことを特徴とする請求項１のネット。2. The net according to claim 1, wherein the single fiber fineness is 3.0 dtex or less. 【請求項３】 熱可塑性合成繊維の強度が６．０ｃＮ／
ｄｔｅｘ以上、かつ伸度が１５％以上４０％以下である
ことを特徴とする請求項１または２記載のネット。3. The thermoplastic synthetic fiber has a strength of 6.0 cN /
3. The net according to claim 1, wherein the dtex is not less than dtex and the elongation is not less than 15% and not more than 40%. 【請求項４】 熱可塑性合成繊維がポリエステル系繊維
またはポリアミド系繊維である請求項１〜３記載のネッ
ト。4. The net according to claim 1, wherein the thermoplastic synthetic fiber is a polyester fiber or a polyamide fiber. 【請求項５】 目合いが１０ｍｍ以上２００ｍｍ以下で
あることを特徴とする請求項１〜４記載のネット。5. The net according to claim 1, wherein the mesh size is 10 mm or more and 200 mm or less.