JPH11347156A - Golf club head - Google Patents
Golf club headInfo
- Publication number
- JPH11347156A JPH11347156A JP10162338A JP16233898A JPH11347156A JP H11347156 A JPH11347156 A JP H11347156A JP 10162338 A JP10162338 A JP 10162338A JP 16233898 A JP16233898 A JP 16233898A JP H11347156 A JPH11347156 A JP H11347156A
- Authority
- JP
- Japan
- Prior art keywords
- sole
- weight
- shape
- welding
- plate piece
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、ゴルフクラブヘッ
ドに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a golf club head.
【0002】[0002]
【従来の技術】従来、図5又は図6と、図7に示すよう
にフェース部材12、クラウン部材13、ソール部材14等か
ら成る各部材とホーゼル部材15を溶接にて接合した中空
殻状のクラブヘッド16が知られている。ここで、ヘッド
を構成する各部材(フェース部材12、クラウン部材13、
ソール部材14等)の板厚が大きいと、プレス加工が困難
であったり、スプリングバックを起こして所望の形状に
ならず、溶接時に各部材の形状が合わなかったりする問
題が弾性限界の高い材質(チタン等)では生じていた。
板厚を大きくせずに所定のゴルフクラブヘッド重量と外
径寸法にするためには、平面板状のウエイト付加部材17
又は丸棒状のウエイト付加部材18をソール部材14の内面
19に溶接していた。2. Description of the Related Art Conventionally, as shown in FIG. 5 or FIG. 6 and FIG. 7, a hollow shell-like member is formed by welding each of a face member 12, a crown member 13, a sole member 14 and the like to a hosel member 15 by welding. A club head 16 is known. Here, each member constituting the head (face member 12, crown member 13,
If the plate thickness of the sole member 14) is large, press working is difficult, springback occurs, the desired shape is not obtained, and the shape of each member does not match at the time of welding. (Such as titanium).
In order to achieve a predetermined golf club head weight and outer diameter without increasing the thickness, a flat plate-shaped weight adding member 17 is required.
Alternatively, a round bar-shaped weight adding member 18 is attached to the inner surface of the sole member 14.
19 had been welded.
【0003】[0003]
【発明が解決しようとする課題】しかしながら、(図5
〜図7に示したような)従来のゴルフクラブヘッドで
は、ウエイト付加部材17,18がソール部材14の内面19の
形状と合わないために、ウエイト付加部材17,18とソー
ル部材14の内面19との間に隙間20ができ、打球時にウエ
イト付加部材17,18とソール部材14との間で共鳴が起こ
り、その不愉快な音がゴルファーに不快感・違和感を与
えていた。However, (FIG. 5
In the conventional golf club head (as shown in FIG. 7), since the weight adding members 17, 18 do not match the shape of the inner surface 19 of the sole member 14, the weight adding members 17, 18 and the inner surface 19 of the sole member 14 do not match. A gap 20 is formed between the ball and the ball, and resonance occurs between the weight adding members 17 and 18 and the sole member 14 at the time of hitting the ball, and the unpleasant sound gives the golfer discomfort and discomfort.
【0004】そこで本発明は、打球音に違和感がなく、
ゴルファーに不快感を与えないゴルフクラブヘッドを提
供することを目的とする。[0004] Accordingly, the present invention provides an uncomfortable feeling in hitting sound,
It is an object of the present invention to provide a golf club head that does not cause a golfer to feel uncomfortable.
【0005】[0005]
【課題を解決するための手段】上述の目的を達成するた
めに、本発明に係るゴルフクラブヘッドは、複数の金属
製部材を溶接して中空殻状に形成されるゴルフクラブヘ
ッドに於いて、ソール部内面に接合されたウエイト付加
板片の下面の形状が、該ソール部内面の湾曲面と略同一
形状に形成されている。また、ウエイト付加板片の周縁
部下面の曲率半径が、対応するソール部内面の曲率半径
よりも僅かに小さいものである。さらに、ウエイト付加
板片がソール部内面と接触する面積が、ウエイト付加板
片の下面の全面積に占める割合を、70%〜 100%とした
ものである。In order to achieve the above object, a golf club head according to the present invention is a golf club head formed by welding a plurality of metal members into a hollow shell shape. The shape of the lower surface of the weight addition plate piece joined to the inner surface of the sole portion is formed to be substantially the same as the curved surface of the inner surface of the sole portion. Further, the radius of curvature of the lower surface of the peripheral portion of the weight-added plate piece is slightly smaller than the radius of curvature of the corresponding inner surface of the sole portion. Further, the ratio of the area where the weight-added plate contacts the inner surface of the sole portion to the total area of the lower surface of the weight-added plate is set to 70% to 100%.
【0006】[0006]
【発明の実施の形態】以下、実施の形態を示す図面に基
づき、本発明を詳説する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail with reference to the drawings showing embodiments.
【0007】図1及び図2は本発明の実施の一形態を示
し、チタン又はチタン合金等の圧延板素材をプレス成形
にて加工された湾曲板片(金属製部材)から成るフェー
ス部材3、クラウン部材4、ソール部材5等が相互に溶
接され、中空殻状のヘッド殻部6を形成し、ヘッド殻部
6のヒール側上部にホーゼル部材7が溶接により固着さ
れている。そして、ソール部内面8に、下面10の形状が
ソール部内面8の湾曲面と略同一形状に形成されたウエ
イト付加板片9が、溶接・接着等により、接合されてい
る。なお、図2では、溶接後は、略 100%の面積でウエ
イト付加板片9の下面10がソール部内面8に密着してい
る。FIGS. 1 and 2 show an embodiment of the present invention, in which a face member 3 made of a curved plate piece (metal member) formed by pressing a rolled plate material such as titanium or a titanium alloy. The crown member 4, the sole member 5, and the like are welded to each other to form a hollow shell-shaped head shell 6, and a hosel member 7 is fixed to the upper portion of the head shell 6 on the heel side by welding. A weight-added plate 9 whose lower surface 10 has a shape substantially the same as the curved surface of the sole inner surface 8 is joined to the sole inner surface 8 by welding, bonding, or the like. In FIG. 2, after welding, the lower surface 10 of the weight-added plate 9 is in close contact with the inner surface 8 of the sole with an area of about 100%.
【0008】図3は本発明の第2の実施の形態を示し、
ウエイト付加板片9の曲面形状は、ウエイト付加板片9
が溶接にてソール部材5に接合される場合、熱歪みによ
って変形することを考慮にいれた形状になっている。即
ち、(溶接前に)ウエイト付加板片9の周縁部下面の曲
率半径を、対応するソール部内面8の曲率半径よりも
(僅かに)小さくしておく。ウエイト付加板片9は、溶
接にてソール部内面8に接合される際、熱歪みによって
ソール部内面8に近づくような力を(冷却に伴って)受
け、図3中に矢印P…にて示す如く、ウエイト付加板片
9の(周縁部を除く)中央領域は強くソール部内面8に
圧着(密着)する。このように、溶接完了状態にてソー
ル部内面8の湾曲面と略同一形状にウエイト付加板片9
の下面10の形状が形成され、ウエイト付加板片9の周縁
部下面の曲率半径R1 が、対応するソール部内面8の曲
率半径R0 よりも、僅かに小さく保持される。FIG. 3 shows a second embodiment of the present invention.
The curved shape of the weight-added plate 9 is
Is joined to the sole member 5 by welding, the shape takes into account that it is deformed by thermal strain. That is, the radius of curvature of the lower surface of the peripheral portion of the weight-added plate 9 (before welding) is made (slightly) smaller than the radius of curvature of the corresponding inner surface 8 of the sole portion. When the weight-added plate 9 is joined to the sole inner surface 8 by welding, the weight-added plate 9 receives a force (with cooling) approaching the sole inner surface 8 due to thermal strain, and is indicated by arrows P in FIG. As shown, the central region (excluding the peripheral portion) of the weight-added plate 9 strongly presses (closely contacts) the inner surface 8 of the sole portion. In this manner, the weight-added plate piece 9 has a shape substantially the same as the curved surface of the inner surface 8 of the sole portion when the welding is completed.
Is formed, and the radius of curvature R 1 of the lower surface of the peripheral portion of the weight-added plate 9 is kept slightly smaller than the radius of curvature R 0 of the corresponding inner surface 8 of the sole portion.
【0009】図4は図3を上方から見た平面図であっ
て、ウエイト付加板片9がソール部内面8と接触する面
積S1 が、ウエイト付加板片9の下面10の全面積S0 に
占める割合を、70%〜 100%としたものである。上記割
合が、70%より小さいと、打球時にウエイト付加板片9
とソール部との間で共鳴が起こり、その不愉快な音がゴ
ルファーに不快感を与えてしまう。FIG. 4 is a plan view of FIG. 3 as viewed from above, and the area S 1 where the weight-added plate 9 contacts the inner surface 8 of the sole is the total area S 0 of the lower surface 10 of the weight-added plate 9. The ratio is set to 70% to 100%. If the above ratio is less than 70%, the weight-added plate 9
Resonance occurs between the ball and the sole, and the unpleasant sound gives the golfer discomfort.
【0010】[0010]
【実施例】図1と図2に示すように、本発明の実施例と
して、純チタンの板材をプレス成形して、フェース部材
3、クラウン部材4、およびソール部材5を作製した。
ソール部材5の内面側に、純チタン製のウエイト付加板
片9を溶接にて固着するとともに、フェース部材3、ク
ラウン部材4、およびソール部材5を相互に溶接して、
中空殻状のヘッド殻部6を形成した。このヘッド殻部6
のヒール側上端に純チタンの丸棒(φ22)に旋盤加工を
施して作製したホーゼル部材7を溶接にて固着した。そ
の際、ウエイト付加板片9は、その下面10の形状が、ソ
ール部材5内面の湾曲面と同一形状に形成されているも
のを用いて、ウエイト付加板片9がソール部内面8と接
触する面積S1 が、ウエイト付加板片9の下面10の全面
積S0に占める割合は、X線透過法によって測定する
と、89%であった。そのヘッドにシャフト等を嵌合等に
より一体化させて、ゴルフクラブを作製した。As shown in FIGS. 1 and 2, as an embodiment of the present invention, a face member 3, a crown member 4, and a sole member 5 were produced by press-forming a pure titanium plate.
A weight addition plate piece 9 made of pure titanium is fixed to the inner surface side of the sole member 5 by welding, and the face member 3, the crown member 4, and the sole member 5 are welded to each other.
A hollow shell-shaped head shell 6 was formed. This head shell 6
A hosel member 7 produced by lathing a round bar (φ22) of pure titanium was fixed to the upper end of the heel side by welding. At this time, the weight-adding plate 9 has a lower surface 10 formed in the same shape as the curved surface of the inner surface of the sole member 5, and the weight-adding plate 9 contacts the sole portion inner surface 8. area S 1 is the percentage of the total area S 0 of the lower surface 10 of the weight added plate piece 9, as measured by X-ray transmission method, was 89%. A shaft and the like were integrated with the head by fitting or the like to produce a golf club.
【0011】次に、従来例として、図5と図7に示すよ
うな形状の平面板状のウエイト付加部材17を、ソール部
材14の内面19に、隙間20が生ずるように溶接したものを
作製し、シャフトを取付けてゴルフクラブとした。この
とき、ウエイト付加部材17がソール部材14の内面19と接
触する面積が、ウエイト付加部材17の下面の全面積に占
める割合は、11%であった(X線透過法による測定)。
このような実施例(品)と従来例(品)の各ゴルフクラ
ブを用いて、10人による実打テストを行った。評価項目
は、音量、音の高さ、心地よさであり、各5段階で評価
した。音量は大きい方が点数が高く、音の高さは高い方
が点数が高く、心地よさは心地よい方が点数が高い。評
価結果を、表1及び表2に示す。Next, as a conventional example, a flat plate-shaped weight adding member 17 having a shape as shown in FIGS. 5 and 7 is welded to the inner surface 19 of the sole member 14 so as to form a gap 20. Then, a shaft was attached to the golf club. At this time, the ratio of the area where the weight adding member 17 was in contact with the inner surface 19 of the sole member 14 to the total area of the lower surface of the weight adding member 17 was 11% (measured by the X-ray transmission method).
Using each of the golf clubs of the embodiment (article) and the conventional example (article), an actual hit test was performed by 10 players. The evaluation items were sound volume, sound pitch, and comfort, and were evaluated on a five-point scale. The higher the volume, the higher the score, the higher the pitch, the higher the score, and the more comfortable, the higher the score. Tables 1 and 2 show the evaluation results.
【0012】[0012]
【表1】 [Table 1]
【0013】[0013]
【表2】 [Table 2]
【0014】表1及び表2より、打球音の音量は同程度
であったが、音の高さは従来例(品)の方が高く、心地
よさは本発明実施例(品)の方が良かった。従来例
(品)では、ソール部材14とウエイト付加部材17との隙
間20で共鳴が起こり、不快な音が発生したものと考えら
れる。From Tables 1 and 2, the sound volume of the hit ball sound was almost the same, but the pitch of the sound was higher in the conventional example (product), and the comfort was higher in the embodiment (product) of the present invention. Was good. In the conventional example (article), it is considered that resonance occurred in the gap 20 between the sole member 14 and the weight addition member 17, and an unpleasant sound was generated.
【0015】[0015]
【発明の効果】本発明は上述の如く構成されるので、次
に記載する効果を奏する。Since the present invention is configured as described above, the following effects can be obtained.
【0016】(請求項1によれば)ゴルフボールを打撃
した時(打球時)に、ウエイト付加板片9とソール部内
面8との間で共鳴が起こらず、快い打球音がして、ゴル
ファーに不快感を与えることがない。According to the first aspect, when the golf ball is hit (at the time of hitting the ball), resonance does not occur between the weight-added plate piece 9 and the inner surface 8 of the sole portion, and the golf player makes a pleasant hitting sound, Does not give any discomfort.
【0017】(請求項2によれば)ウエイト付加板片9
の周縁を溶接することで簡単に製作できる。ウエイト付
加板片9は、溶接にてソール部に接合されて後、溶接部
が冷却するにつれて、ソール部に近づくような力を受け
るので、ウエイト付加板片9の中央部領域は、ソール部
内面8の湾曲面に圧着し、打球時にウエイト付加板片9
とソール部内面8との間で一層共鳴が起こらず、打球音
がゴルファーに不快感を与えることがない。(According to claim 2) weight added plate piece 9
It can be easily manufactured by welding the periphery of. After the weight-added plate piece 9 is joined to the sole portion by welding, as the welded portion cools, it receives a force approaching the sole portion. Therefore, the central region of the weight-added plate piece 9 is the inner surface of the sole portion. 8 is pressed against the curved surface, and a weight-added plate 9
There is no further resonance between the ball and the inner surface 8 of the sole, and the hitting sound does not give a golfer any discomfort.
【0018】(請求項3によれば)打球時にウエイト付
加板片9とソール部内面8との間で共鳴が起こらず、不
愉快な音がゴルファーに不快感を与えることがない。According to the third aspect, resonance does not occur between the weight-added plate piece 9 and the inner surface 8 of the sole portion at the time of hitting a ball, and an unpleasant sound does not give an unpleasant feeling to a golfer.
【図面の簡単な説明】[Brief description of the drawings]
【図1】本発明の第1の実施の形態を示す分解斜視図で
ある。FIG. 1 is an exploded perspective view showing a first embodiment of the present invention.
【図2】断面図である。FIG. 2 is a sectional view.
【図3】第2の実施の形態を示す要部断面図である。FIG. 3 is a sectional view of a main part showing a second embodiment.
【図4】その平面図である。FIG. 4 is a plan view thereof.
【図5】従来例を示す分解斜視図である。FIG. 5 is an exploded perspective view showing a conventional example.
【図6】別の従来例を示す分解斜視図である。FIG. 6 is an exploded perspective view showing another conventional example.
【図7】断面図である。FIG. 7 is a sectional view.
8 ソール部内面 9 ウエイト付加板片 10 下面 R1 曲率半径 R0 曲率半径 S1 面積 S0 全面積8 sole inner surface 9 weight additional plate piece 10 lower surface R 1 radius of curvature R 0 of curvature radius S 1 area S 0 total area
Claims (3)
形成されるゴルフクラブヘッドに於いて、ソール部内面
8に接合されたウエイト付加板片9の下面10の形状が、
該ソール部内面8の湾曲面と略同一形状に形成されてい
ることを特徴とするゴルフクラブヘッド。1. In a golf club head formed by welding a plurality of metal members into a hollow shell shape, the lower surface 10 of a weight adding plate piece 9 joined to an inner surface 8 of a sole portion has a shape of:
A golf club head having substantially the same shape as the curved surface of the sole inner surface 8.
半径R1 が、対応するソール部内面8の曲率半径R0 よ
りも僅かに小さい請求項1記載のゴルフクラブヘッド。2. The golf club head according to claim 1, wherein the radius of curvature R 1 of the lower surface of the peripheral portion of the weight adding plate piece 9 is slightly smaller than the radius of curvature R 0 of the corresponding inner surface 8 of the sole portion.
接触する面積S1 が、ウエイト付加板片9の下面10の全
面積S0 に占める割合を、70%〜 100%とした請求項1
記載のゴルフクラブヘッド。Wherein an area S 1 of the weight-added plate piece 9 is in contact with the sole inner surface 8, claim a percentage of the total area S 0 of the lower surface 10 of the weight added plate piece 9, and 70 to 100% 1
The golf club head as described.