JPH11335880A - Metal cleaner, and method for removing rust from metal - Google Patents
Metal cleaner, and method for removing rust from metalInfo
- Publication number
- JPH11335880A JPH11335880A JP15683898A JP15683898A JPH11335880A JP H11335880 A JPH11335880 A JP H11335880A JP 15683898 A JP15683898 A JP 15683898A JP 15683898 A JP15683898 A JP 15683898A JP H11335880 A JPH11335880 A JP H11335880A
- Authority
- JP
- Japan
- Prior art keywords
- metal
- amino acid
- rust
- cleaner
- arginine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、金属クリーナー及
び該金属クリーナーを用いた金属の錆落し方法に関する
ものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a metal cleaner and a method for removing metal rust using the metal cleaner.
【０００２】[0002]
【従来の技術】従来、錆落しその他の金属クリーナーと
して各種のものが知られているが、強酸や強アルカリを
用いたものは安全性の点で問題がある。また、水洗後、
腐食が進行しやすい。研磨剤を用いたものは金属に傷を
つけることがあるという問題がある。2. Description of the Related Art Conventionally, various kinds of rust removers and other metal cleaners are known, but those using a strong acid or a strong alkali have a problem in terms of safety. Also, after washing with water,
Corrosion easily progresses. The one using the abrasive has a problem that the metal may be damaged.
【０００３】[0003]
【発明が解決しようとする課題】本発明の目的は、上記
のような不都合を解消し、安全性が高く、かつ清浄、水
洗後の腐食の進行が遅く、清浄効果の持続性の良好な金
属クリーナー及びこのような金属クリーナーを用いた金
属の錆落し方法を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned disadvantages, to improve the safety, to promote the progress of corrosion after cleaning and washing with water, and to improve the persistence of the cleaning effect. An object of the present invention is to provide a cleaner and a method for removing rust of metal using such a metal cleaner.
【０００４】[0004]
【課題を解決するための手段】（１） 本発明は、アミ
ノ酸又はアミノ酸誘導体の水溶液からなる金属クリーナ
ーである。本発明の対象は金属クリーナーであり、金属
の錆落しを主目的として金属体を清浄化することに特徴
を有しているものである。このような金属クリーナー
は、アミノ酸又はアミノ酸誘導体を水に混合し、攪拌し
て溶解せしめることにより得ることができる。Means for Solving the Problems (1) The present invention is a metal cleaner comprising an aqueous solution of an amino acid or an amino acid derivative. The object of the present invention is a metal cleaner, which is characterized by cleaning a metal body mainly for the purpose of removing rust of metal. Such a metal cleaner can be obtained by mixing an amino acid or an amino acid derivative with water and stirring to dissolve it.
【０００５】本発明の金属クリーナーは、本質的な構成
成分がアミノ酸又はアミノ酸誘導体であることから、取
扱・使用上、安全性が高い。[0005] The metal cleaner of the present invention is highly safe in handling and use since the essential constituents are amino acids or amino acid derivatives.
【０００６】〔作用〕 本発明の金属クリーナーを金属
表面に適用すると、アミノ酸のキレート効果により金属
表面に作用し、錆を取り除くことができる。また、アミ
ノ酸の膜が金属表面に形成され、金属が酸化しにくく、
清浄効果が持続する。[Action] When the metal cleaner of the present invention is applied to a metal surface, the metal cleaner acts on the metal surface by the chelating effect of amino acids to remove rust. In addition, a film of amino acids is formed on the metal surface, and the metal is hardly oxidized,
The cleaning effect lasts.
【０００７】（２） 好ましくは、前記アミノ酸は、ア
ルギニン、アラニン、グリシン、グルタミン酸及びセリ
ンの中のいずれか１種であるか、あるいはアルギニンと
他のアミノ酸とを混合したものであることを特徴とする
金属クリーナーである。(2) Preferably, the amino acid is one of arginine, alanine, glycine, glutamic acid and serine, or a mixture of arginine and another amino acid. Metal cleaner.
【０００８】上記各アミノ酸はいずれも良好な清浄効果
を示す。またアルギニンと他のアミノ酸とを混合したも
のは、１種類のアミノ酸を用いたものに比べて清浄効果
が優れている。Each of the above amino acids has a good cleaning effect. In addition, a mixture of arginine and another amino acid has a superior cleaning effect as compared with a mixture using one kind of amino acid.
【０００９】（３） さらに好ましくは、前記他のアミ
ノ酸は、アラニン、プロリン及びグリシンの中のいずれ
か１種であることを特徴とする金属クリーナーである。(3) More preferably, the other amino acid is a metal cleaner characterized by being one of alanine, proline and glycine.
【００１０】本発明者は、各種アミノ酸の水溶液につい
て種々研究した結果、アミノ酸として、アルギニンと、
アラニン、プロリン及びグリシンの中のいずれかとを混
合したものを用いた本発明の金属クリーナーは、清浄直
後のきれいさ及び数箇月経過後における清浄効果の持続
性においても優れているとの知見を得た。As a result of various studies on aqueous solutions of various amino acids, the present inventors have found that arginine and
It has been found that the metal cleaner of the present invention using a mixture of any of alanine, proline and glycine is excellent in cleanliness immediately after cleaning and persistence of the cleaning effect after several months. Was.
【００１１】（４） また、アルギニンと前記他のアミ
ノ酸（例えばアラニン、プロリン及びグリシンの中のい
ずれか１種）との混合比（重量比）が３：１〜１：１、
好ましくは２：１〜１：１であることを特徴とする金属
クリーナーである。(4) The mixing ratio (weight ratio) of arginine to the other amino acid (for example, any one of alanine, proline and glycine) is 3: 1 to 1: 1,
Preferably, the metal cleaner has a ratio of 2: 1 to 1: 1.
【００１２】アルギニンと前記他のアミノ酸との混合比
を特定したもので、上記の混合比のものは、清浄直後の
きれいさ及び清浄効果の持続性においても優れており、
したがって、使用時の配合量を減らせる、また錆落しを
スピードアップできる。また、アルギニンは溶解性が高
いので、アルギニンが他のアミノ酸よりも多い方が溶解
性の点でも有利である。[0012] The mixture ratio of arginine and the other amino acids is specified, and the mixture ratio described above is excellent in cleanliness immediately after cleaning and persistence of the cleaning effect.
Therefore, the amount of compounding during use can be reduced, and rust removal can be speeded up. Since arginine has high solubility, it is advantageous that arginine is more soluble than other amino acids in terms of solubility.
【００１３】（５） アミノ酸又はアミノ酸誘導体の水
溶液中に目的とする金属を浸した後、該金属の錆を落と
し、次いで、水洗し、水分を除去することからなる金属
の錆落し方法である。(5) A method for removing rust of a metal, comprising immersing a target metal in an aqueous solution of an amino acid or an amino acid derivative, removing rust of the metal, and then washing with water to remove water.
【００１４】本発明の金属の錆落し方法は、上記（１）
〜（４）の金属クリーナーを用いて金属の錆落しを行う
ものである。目的とする金属を浸す時間は、使用するア
ミノ酸又はアミノ酸誘導体の水溶液の種類と濃度や金属
の種類と錆の程度等によって異なるが、例えば、１％程
度の水溶液の場合、３０分程度でよい。The method for removing rust of a metal according to the present invention is described in the above (1).
The metal rust is removed using the metal cleaners of (4) to (4). The time for immersing the target metal depends on the type and concentration of the aqueous solution of the amino acid or amino acid derivative to be used, the type of metal and the degree of rust, etc. For example, in the case of an aqueous solution of about 1%, it may be about 30 minutes.
【００１５】目的とする金属を浸してから取り出した
後、通常、布等で軽く拭くようにして該金属の錆を落と
す。次いで、水洗し、乾いた布で水分を取る、あるいは
乾燥機等で乾燥させる等により水分を除去する。After the target metal is immersed and taken out, rust of the metal is usually removed by lightly wiping with a cloth or the like. Next, the substrate is washed with water and removed with a dry cloth, or dried with a drier or the like to remove the moisture.
【００１６】[0016]
【実施例】〔実施例１〜１５〕表１及び表２に記載の各
アミノ酸（試料）１ｇを精製水９９ｇに混合し攪拌して
溶解し、金属クリーナーを得た。この金属クリーナー
（１％水溶液）について、試験を行った。EXAMPLES Examples 1 to 15 1 g of each amino acid (sample) shown in Tables 1 and 2 was mixed with 99 g of purified water and dissolved by stirring to obtain a metal cleaner. A test was conducted on this metal cleaner (1% aqueous solution).
【００１７】試験は、錆びた銅板と真鍮板を、比較がで
きるように半分だけ上記１％水溶液に２時間浸した後、
取り出して水洗し、水気を拭き取り台紙に張り付け、そ
のきれいさを次に示す６段階評価により行った。また、
３箇月後の状態についても評価をして清浄効果の持続性
についても確かめた。その結果を表１及び表２に示す。
実施例の金属クリーナーは、いずれも良好な清浄効果を
有することがわかる。In the test, the rusted copper plate and the brass plate were immersed in the above-mentioned 1% aqueous solution by half for comparison for 2 hours.
The sample was taken out, washed with water, wiped off the moisture, stuck to the backing paper, and evaluated for cleanliness according to the following six-grade evaluation. Also,
The condition after three months was also evaluated to confirm the persistence of the cleaning effect. The results are shown in Tables 1 and 2.
It can be seen that the metal cleaners of the examples all have a good cleaning effect.
【００１８】〔評価〕 ６：非常にきれい ５：きれい ４：ややきれい ３：変化なし ２：やや悪い １：悪い[Evaluation] 6: Very clean 5: Clean 4: Somewhat clean 3: No change 2: Somewhat bad 1: Bad
【００１９】(例）４−２：直後はややきれいであるが
３箇月後やや悪い(Example) 4-2: Slightly clean immediately after, but slightly bad three months later
【００２０】[0020]
【表１】 [Table 1]
【００２１】[0021]
【表２】 [Table 2]
【００２２】〔比較例１〜４〕比較例として酸、アルカ
リの各水溶液について実施例と同様の試験を行った。上
記実施例と同様の方法で評価した。その結果を表３に示
す。[Comparative Examples 1 to 4] As comparative examples, tests similar to those of the examples were conducted for each aqueous solution of acid and alkali. Evaluation was performed in the same manner as in the above example. Table 3 shows the results.
【００２３】[0023]
【表３】 [Table 3]
【００２４】〔実施例１６〜２１〕Ｌ−アルギニンと表
４に記載の各アミノ酸とを表４に記載の配合比（単位：
ｇ）で精製水に混合し攪拌して溶解し、金属クリーナー
を得た。これを常水で３０倍に希釈した。この希釈溶液
（０．９％水溶液）について上記実施例と同様の試験を
行った。上記実施例と同様の方法で評価した。その結果
を表５に示す。[Examples 16 to 21] L-arginine and each of the amino acids listed in Table 4 were mixed in the ratio shown in Table 4 (unit:
In g), the mixture was mixed with purified water and dissolved by stirring to obtain a metal cleaner. This was diluted 30 times with ordinary water. This diluted solution (0.9% aqueous solution) was subjected to the same test as in the above example. Evaluation was performed in the same manner as in the above example. Table 5 shows the results.
【００２５】[0025]
【表４】 [Table 4]
【００２６】[0026]
【表５】 [Table 5]
【００２７】なお、本発明の金属クリーナーの使用の際
の濃度については、一般に高い方が洗浄効果及びその持
続性が高いが、０．５％以上の濃度では、特に大きな差
はない。したがって、０．５〜１．５％程度の希釈率に
おける使用が経済性及び清浄力の両面で優れているの
で、好ましい。In general, the higher the concentration of the metal cleaner of the present invention at the time of use, the higher the cleaning effect and the sustainability thereof, but there is no significant difference at a concentration of 0.5% or more. Therefore, use at a dilution ratio of about 0.5 to 1.5% is preferable because it is excellent in both economic efficiency and detergency.
【００２８】以上、実施例を説明したが、上記実施例は
例示であり、本発明は上記実施例に限定されるものでは
ないのは勿論である。Although the embodiment has been described above, the above embodiment is merely an example, and the present invention is not limited to the above embodiment.
【００２９】[0029]
【発明の効果】以上説明したように、本発明の金属クリ
ーナー及び金属の錆落し方法によれば、強酸や強アルカ
リと異なり、皮膚に付着しても皮膚を傷めるおそれがな
いので、安全性が高く、また、清浄した後の錆の発生
(戻り）も遅いので、その効果は極めて大きい。As described above, according to the metal cleaner and the metal rust removing method of the present invention, unlike strong acids and strong alkalis, there is no danger of damaging the skin even if it adheres to the skin. High and rust after cleaning
(Return) is also slow, so the effect is extremely large.
Claims (5)
らなる金属クリーナー。1. A metal cleaner comprising an aqueous solution of an amino acid or an amino acid derivative.
ン、グリシン、グルタミン酸及びセリンの中のいずれか
１種であるか、あるいはアルギニンと他のアミノ酸とを
混合したものであることを特徴とする請求項１記載の金
属クリーナー。2. The method according to claim 1, wherein the amino acid is any one of arginine, alanine, glycine, glutamic acid and serine, or a mixture of arginine and another amino acid. The described metal cleaner.
ン及びグリシンの中のいずれか１種であることを特徴と
する請求項２記載の金属クリーナー。3. The metal cleaner according to claim 2, wherein the other amino acid is any one of alanine, proline, and glycine.
比が３：１〜１：１であることを特徴とする請求項２又
は３記載の金属クリーナー。4. The metal cleaner according to claim 2, wherein the mixing ratio of arginine to the other amino acid is from 3: 1 to 1: 1.
に目的とする金属を浸した後、該金属の錆を落とし、次
いで、水洗し、水分を除去することからなる金属の錆落
し方法。5. A method for removing rust of a metal, comprising immersing a target metal in an aqueous solution of an amino acid or an amino acid derivative, removing the rust of the metal, and then washing with water to remove water.