JPH11309800A - Packaging material and bag - Google Patents

Abstract

PROBLEM TO BE SOLVED: To realize an excellent ink absorbency, a high printing density or the like by a method wherein the haze of a film, on which an ink accepting layer is provided, is set within a specified range. SOLUTION: An ink accepting layer is coated on a plastic film with a gravure coating method or the like. In this case, before the coating on the film, the surface treatment such as a corona discharge treatment or the like is executed on the film. Here, the thickness of the plastic film is set to be about 5-200 μm and the coating thickness of the ink accepting layer is set to be about 1-50 μm. Further, the haze of the film, onto which the ink accepting layer is laminated is set within the range of 10-90%. Furthermore, as a hydrophilic resin used for the ink accepting layer, a polyester resin or the like is used. Furthermore, in the polyester resin, a hardener such as a melamine or the like, a fluorine surface-active agent or the like are included and, at the same time, also at least either one of inorganic particles, organic particles, dyes and pigments is included. As a result, an excellent ink absorbency, high printing density and the like can be realized.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、電子写真や、イン
クジェットまたは熱転写プリンター等に用いられる包装
材料に関し、特にインクジェット記録において、インク
吸収性に優れ、印字濃度が高く、しかも耐水性、耐湿性
に優れた包装材料および袋に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a packaging material used for electrophotography, ink jet or thermal transfer printers, and more particularly to ink jet recording, which has excellent ink absorbency, high print density, water resistance and moisture resistance. Excellent packaging materials and bags.

【０００２】[0002]

【従来の技術】従来、包装材料及び袋の印字には印刷に
よるものが殆どで、大量生産を基本としてきた。しかし
近年、個人の趣味、趣向が細分化され、包装用の印字も
少量多品種に対応する必要に迫られてきた。このような
要求を満たすものとして、電子写真やインクジェット、
熱転写プリンターが実用化されている。2. Description of the Related Art Conventionally, printing of packaging materials and bags is mostly performed by printing, and has been based on mass production. However, in recent years, personal hobbies and preferences have been subdivided, and there has been a need for printing for packaging to cope with many kinds in a small amount. Electrophotography, inkjet,
Thermal transfer printers have been put to practical use.

【０００３】また、近年カラーコピー技術が完成の域に
達し、カラー複写機／プリンターが徐々に普及してい
る。中でもインクジェットプリンターの普及にはめざま
しいものがある。In recent years, color copying technology has reached the stage of completion, and color copiers / printers are gradually spreading. Above all, the spread of inkjet printers is remarkable.

【０００４】インクジェットプリンターにはノズルの詰
まりを防ぐために乾燥しにくいインクが用いられ、この
インクの成分は、バインダー、染料および／または顔
料、溶媒、添加剤などを水に溶解したものが一般的であ
る。従って、包装用基材としては吸水性の良いものを用
いることが必要であり、通常、インク吸収性の良い特別
な紙が用いられている。[0004] Ink jet printers use ink that is difficult to dry in order to prevent nozzle clogging, and the components of this ink are generally those obtained by dissolving binders, dyes and / or pigments, solvents, additives and the like in water. is there. Therefore, it is necessary to use a substrate having good water absorbency as a packaging base material, and special paper having good ink absorbency is usually used.

【０００５】[0005]

【発明が解決しようとする課題】一般に紙は耐水性、耐
湿性等に劣ることから、これらの欠点を有していないプ
ラスチックフィルムが適応できれば、種々の分野でその
利点が生かされる。Generally, paper is inferior in water resistance, moisture resistance and the like. Therefore, if a plastic film which does not have these disadvantages can be applied, the advantages can be utilized in various fields.

【０００６】インクジェットプリンターによる印字にお
いてインク吸収性の低い基材を用いると、インクの乾燥
が不十分となったり、あるいはまったく乾燥しないこと
も起こり、指でこすったり、重ね合わされたりすると、
印字部分が汚れて、事実上使用できない。これらの点を
改良する方法として、基材のインク吸収性を向上させる
ために、例えばポリビニルアルコール、でんぷん、ゼラ
チン、ヒドロキシエチルセルロースやメチルセルロース
などのセルロース誘導体、ポリアクリル酸、ポリメタク
リル酸やその塩類などの水溶性高分子受容層を設けるこ
とが提案されている（例えば、特開昭６１−５９２３９
号公報、特公平−２７９４１号公報、特公平２−３４７
９２号公報）。しかし、従来の受容層はインク吸収性を
満足しているにしても、耐水性が悪く、受容層や印字部
が水に溶けて印字画像が消失したり、また、表面がべと
ついて印字画像が滲んだり、積層した場合にブロッキン
グを生じたりするという問題点を有するものであった。When a substrate having low ink absorbency is used in printing by an ink jet printer, the ink may be insufficiently dried or may not be dried at all, and if rubbed with a finger or overlapped,
The printed area is dirty and practically unusable. As a method of improving these points, in order to improve the ink absorption of the substrate, for example, polyvinyl alcohol, starch, gelatin, cellulose derivatives such as hydroxyethylcellulose and methylcellulose, polyacrylic acid, polymethacrylic acid and salts thereof It has been proposed to provide a water-soluble polymer-receiving layer (for example, see JP-A-61-59239).
JP, JP-B-27941, JP-B-2-347
No. 92). However, even if the conventional receiving layer satisfies the ink absorbency, the water resistance is poor, and the receiving layer dissolves in water and the printed image disappears, and the printed image becomes sticky. Has a problem that bleeding or blocking occurs when laminated.

【０００７】また、高透明の包装材料を用いた場合、内
容物はよく見えるが、印字画像が見づらい等の問題点を
有するものであった。Further, when a highly transparent packaging material is used, the contents can be seen well, but there is a problem that the printed image is difficult to see.

【０００８】本発明の課題は、かかる問題点を解決し、
インク吸収性に優れ、印字濃度が高く、内容物が可視化
でき、印字画像も読みやすく、しかも耐水性、耐湿性に
優れた包装材料及び袋を提供することにある。An object of the present invention is to solve such problems.
An object of the present invention is to provide a packaging material and a bag having excellent ink absorbency, high print density, visualization of contents, easy readability of printed images, and excellent water resistance and moisture resistance.

【０００９】[0009]

【課題を解決するための手段】上記課題を解決するため
に、本発明の包装材料は、少なくとも一部にプラスチッ
クフィルムが用いられ、かつ、該フィルムの少なくとも
一面にインク受容層が設けられた包装材料及び袋におい
て、インク受容層が設けられたフィルムのヘイズが１０
〜９０％の範囲にあることを特徴とするものからなる。According to the present invention, there is provided a packaging material comprising a plastic film at least partially and an ink receiving layer provided on at least one surface of the film. In the material and the bag, the haze of the film provided with the ink receiving layer is 10
９０90%.

【００１０】また、本発明に係る袋は、少なくとも一部
にプラスチックフィルムが用いられ、かつ、該フィルム
の少なくとも一面にインク受容層が設けられた袋におい
て、インク受容層が設けられたフィルムのヘイズが１０
〜９０％の範囲にあることを特徴とするものからなる。In the bag according to the present invention, a plastic film is used at least in part, and at least one surface of the film is provided with an ink receiving layer. Is 10
９０90%.

【００１１】[0011]

【発明の実施の形態】以下に、本発明を、望ましい実施
の形態とともに詳細に説明する。本発明のプラスチック
フィルムの材質としては、ポリエステル、ポリオレフィ
ン、ポリアミド、ポリエステルアミド、ポリエーテル、
ポリイミド、ポリアミドイミド、ポリスチレン、ポリカ
ーボネート、ポリ−ｐ−フェニレンスルフィド、ポリエ
ーテルエステル、ポリ塩化ビニル、ポリ（メタ）アクリ
ル酸エステルが好ましい。また、これらの共重合体やブ
レンド物やさらに架橋したものを用いることもできる。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with preferred embodiments. As the material of the plastic film of the present invention, polyester, polyolefin, polyamide, polyesteramide, polyether,
Polyimide, polyamide imide, polystyrene, polycarbonate, poly-p-phenylene sulfide, polyether ester, polyvinyl chloride, and poly (meth) acrylate are preferred. Further, these copolymers, blends, and further cross-linked ones can also be used.

【００１２】プラスチックフィルムが、表面処理、すな
わちコロナ放電処理（空気中、窒素中、炭酸ガス中な
ど）や易接着処理が施されたフィルムである場合、イン
ク受容層との密着性、耐水性、耐溶剤性などが改良され
るのでより好ましく使用される。易接着処理には各種の
方法を用いることができ、フィルム製造工程中でアクリ
ル系、ウレタン系、ポリエステル系などの各種接着剤を
塗布したもの、あるいは一軸または二軸延伸後のフィル
ムに上記のような各種接着剤を塗布したものなどが好適
に用いうる。When the plastic film has been subjected to a surface treatment, that is, a film subjected to a corona discharge treatment (in air, nitrogen, carbon dioxide, etc.) or an easy-adhesion treatment, adhesion to the ink receiving layer, water resistance, It is more preferably used because the solvent resistance and the like are improved. Various methods can be used for the easy adhesion treatment.Acrylic-based, urethane-based, and polyester-based adhesives are applied in the film manufacturing process, or the film after uniaxial or biaxial stretching is applied as described above. What applied various adhesives etc. can be used suitably.

【００１３】また、プラスチックフィルムは透明フィル
ムでも着色されたフィルムでもよい。The plastic film may be a transparent film or a colored film.

【００１４】このプラスチックフィルムの厚みは特に限
定されないが、通常、５μｍ以上２００μｍ以下、好ま
しくは１０μｍ以上１００μｍ以下、更に好ましくは２
０μｍ以上５０μｍ以下であるのが望ましい。Although the thickness of the plastic film is not particularly limited, it is usually 5 μm or more and 200 μm or less, preferably 10 μm or more and 100 μm or less, more preferably 2 μm or more and 100 μm or less.
It is desirable that the thickness be 0 μm or more and 50 μm or less.

【００１５】本発明の包装材料において、インク受容層
が積層されたフィルムと貼り合わせて袋とする場合、片
方の基材は上記プラスチックフィルムの他に、紙、合成
紙、布、不織布、紙／プラスチックフィルム、布／プラ
スチックフィルム等を用いることができる。この場合、
インク受容層は袋の外面であることが望ましい。In the packaging material of the present invention, when a bag is formed by laminating with a film having an ink receiving layer laminated thereon, one of the substrates is paper, synthetic paper, cloth, nonwoven fabric, paper / Plastic films, cloth / plastic films, and the like can be used. in this case,
Preferably, the ink receiving layer is on the outer surface of the bag.

【００１６】本発明の袋において、基材表面に可変しな
い情報を記録したり、薬の袋として用いた場合、インク
受容層面に薬局名、効能・効果、注意事項等の情報を記
録して用いることが望ましい。In the bag of the present invention, when non-variable information is recorded on the surface of the base material or when used as a medicine bag, information such as a pharmacy name, efficacy / effect, and precautions is recorded and used on the ink receiving layer surface. It is desirable.

【００１７】本発明の包装材料及び袋のインク受容層と
して用いられる親水性樹脂としては、ポリエステル樹
脂、エチレン−酢酸ビニル共重合樹脂、アイオノマー樹
脂、ウレタン樹脂、ナイロン樹脂、エチレン−アクリル
酸共重合樹脂、エチレン−アクリル酸エチル共重合樹
脂、エチレン−アクリル酸メチル共重合樹脂、エチレン
−メタクリル酸共重合樹脂、エチレン−ビニルアルコー
ル共重合樹脂、ポリビニルアルコール樹脂、ポリビニル
ブチラール樹脂、ポリスチレン樹脂、ポリアルキレンオ
キシド樹脂、ポリビニルピロリドン樹脂、ゼラチン等が
使用できるが、これらに限定されない。The hydrophilic resin used as the ink receiving layer of the packaging material and the bag of the present invention includes polyester resin, ethylene-vinyl acetate copolymer resin, ionomer resin, urethane resin, nylon resin, ethylene-acrylic acid copolymer resin. , Ethylene-ethyl acrylate copolymer resin, ethylene-methyl acrylate copolymer resin, ethylene-methacrylic acid copolymer resin, ethylene-vinyl alcohol copolymer resin, polyvinyl alcohol resin, polyvinyl butyral resin, polystyrene resin, polyalkylene oxide resin , Polyvinylpyrrolidone resin, gelatin and the like can be used, but are not limited thereto.

【００１８】また、インクの染着性を向上させるため
に、カチオン性樹脂を含有することが好ましい。Further, in order to improve the dyeing property of the ink, it is preferable to contain a cationic resin.

【００１９】カチオン性樹脂としては、例えば、第４級
アンモニウム塩とスチレンやアクリル酸系エステルとの
共重合物等を使用できる。ここでいうアクリル酸系エス
テルとは、アクリル酸エステルおよびメタクリル酸エス
テルを指すもので、好ましくは脂肪酸アルコールのエス
テルである。例えば、メチルアクリレート、エチルアク
リレート、ブチルアクリレート、プロピルアクリレー
ト、メチルメタアクリレート、エチルメタアクリレー
ト、ブチルメタアクリレート、プロピルメタアクリレー
ト、２−ヒドロキシルエチルメタアクリレート、２−ヒ
ドロキシルエチルアクリレート等を使用できる。カチオ
ン性単量体としては、具体的には、例えば（メタ）アク
リロイルオキシトリメチルアンモニウムクロライド、
（メタ）アクリロイルオキシヒドロキシプロピルトリメ
チルアンモニウムクロライド、（メタ）アクリロイルオ
キシトリエチルアンモニウムクロライド、（メタ）アク
リロイルオキシジメチルベンジルアンモニウムクロライ
ド、（メタ）アクリロイルオキシトリメチルアンモニウ
ムメチルサルフェート等の（メタ）アクリル系単量体、
（メタ）アクリルアミドプロピルトリメチルアンモニウ
ムクロライド、（メタ）アクリルアミドプロピルジメチ
ルベンジルアンモニウムクロライド等の（メタ）アクリ
ルアミド系カチオン性単量体を使用できる。As the cationic resin, for example, a copolymer of a quaternary ammonium salt with styrene or an acrylic acid ester can be used. As used herein, the acrylic ester refers to an acrylic ester and a methacrylic ester, and is preferably an ester of a fatty acid alcohol. For example, methyl acrylate, ethyl acrylate, butyl acrylate, propyl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, propyl methacrylate, 2-hydroxylethyl methacrylate, 2-hydroxylethyl acrylate, and the like can be used. Specific examples of the cationic monomer include, for example, (meth) acryloyloxytrimethylammonium chloride,
(Meth) acrylic monomers such as (meth) acryloyloxyhydroxypropyltrimethylammonium chloride, (meth) acryloyloxytriethylammonium chloride, (meth) acryloyloxydimethylbenzylammonium chloride, (meth) acryloyloxytrimethylammonium methyl sulfate,
(Meth) acrylamide-based cationic monomers such as (meth) acrylamidopropyltrimethylammonium chloride and (meth) acrylamidopropyldimethylbenzylammonium chloride can be used.

【００２０】本発明においては、受容層の耐水性を向上
させるために、メラミン、エポキシ、イソシアネート、
オキサゾリン化合物、ジルコニウム化合物等の硬化剤を
用いることが好ましい。In the present invention, in order to improve the water resistance of the receiving layer, melamine, epoxy, isocyanate,
It is preferable to use a curing agent such as an oxazoline compound or a zirconium compound.

【００２１】さらに本発明においては、受容層のレベリ
ング性、インクの染着性を向上させるために、フッ素系
やシリコーン系界面活性剤を用いることが好ましい。中
でもフッ素界面活性剤が好ましい。フッ素界面活性剤と
しては、パーフルオロアルキルスルホン酸塩、パーフル
オロアルキルカルボン酸塩、パーフルオロアルキルエチ
レンオキシド付加物、パーフルオロアルキルトリメチル
アンモニウム塩、パーフルオロアルキルアミノスルホン
酸塩等のパーフルオロアルキル基含有フッ素系界面活性
剤等を使用できるが、これらに限定されない。中でも、
パーフルオロアルキルエチレンオキシド付加物が各種溶
剤に対する溶解性、低起泡性、表面張力低下能等に優れ
ており好ましい。Further, in the present invention, it is preferable to use a fluorine-based or silicone-based surfactant in order to improve the leveling property of the receiving layer and the dyeing property of the ink. Among them, a fluorine surfactant is preferable. Examples of the fluorine surfactant include perfluoroalkyl sulfonates, perfluoroalkyl carboxylate salts, perfluoroalkyl ethylene oxide adducts, perfluoroalkyl trimethyl ammonium salts, perfluoroalkyl group-containing fluorine such as perfluoroalkyl amino sulfonates, etc. A surfactant may be used, but is not limited thereto. Among them,
Perfluoroalkyl ethylene oxide adducts are preferred because they are excellent in solubility in various solvents, low foaming properties, surface tension lowering ability and the like.

【００２２】本発明のインク受容層は、無機粒子、有機
粒子、染料、顔料の少なくとも１種以上を含有すること
が好ましい。The ink receiving layer of the present invention preferably contains at least one of inorganic particles, organic particles, dyes and pigments.

【００２３】無機粒子としては、例えば、シリカ、クレ
ー、タルク、ケイソウ土、炭酸カルシウム、硫酸バリウ
ム、ケイ酸アルミ、合成ゼオライト、アルミナ、酸化亜
鉛、雲母などを使用できる。有機粒子としては、例え
ば、ポリメチルメタクリレート、ポリスチレン、それら
の共重合体、ポリ塩化ビニル、ポリエチレン、ポリプロ
ピレン、ポリ塩化ビニリデン、ポリカーボネートなどの
プラスチックピグメントを好ましく用いることができ
る。As the inorganic particles, for example, silica, clay, talc, diatomaceous earth, calcium carbonate, barium sulfate, aluminum silicate, synthetic zeolite, alumina, zinc oxide, mica and the like can be used. As the organic particles, for example, plastic pigments such as polymethyl methacrylate, polystyrene, copolymers thereof, polyvinyl chloride, polyethylene, polypropylene, polyvinylidene chloride, and polycarbonate can be preferably used.

【００２４】染料としては、例えば、アゾ系、アントラ
キノン系に代表される分散染料やカチオン染料、ビニル
スルホン系、トリアジン系、ピリミジン系に代表される
反応染料を用いることができる（例えば、（株）シーエ
ムシー「工業用色素の技術と市場：昭和５８年１２月２
６日発行」に記載されているようなもの）。As the dye, for example, disperse dyes and cationic dyes typified by azo and anthraquinones, and reactive dyes typified by vinylsulfone, triazine and pyrimidine can be used (for example, Co., Ltd.). CMC "Technology and Market of Industrial Dyes: December 2, 1983
6th)).

【００２５】顔料としては、例えば、アゾ顔料、フタロ
シアニン顔料、縮合多環顔料を用いることができる（例
えば、（株）シーエムシー「工業用色素の技術と市場：
昭和５８年１２月２６日発行」に記載されているような
もの）。As the pigment, for example, azo pigments, phthalocyanine pigments and condensed polycyclic pigments can be used (for example, CMC Co., Ltd., “Technology and Market of Industrial Dyes:
Issued on December 26, 1983).

【００２６】本発明においては、インク受容層が積層さ
れたフィルムのヘイズは１０〜９０％の範囲にあること
が必要である。ヘイズが上記範囲より高いと内容物が見
づらくなる。ヘイズが上記範囲より低いと印字画像が読
みづらくなる。さらに、上記ヘイズを２０〜９０％の範
囲にすると、内容物がより見やすく、印字画像がより読
みやすくなり好ましい。In the present invention, the haze of the film on which the ink receiving layer is laminated must be in the range of 10 to 90%. If the haze is higher than the above range, the contents become difficult to see. If the haze is lower than the above range, the printed image becomes difficult to read. Further, when the haze is in the range of 20 to 90%, the contents are more easily seen and the printed image is more easily read, which is preferable.

【００２７】インク受容層の塗布厚さは特に限定されな
いが、１〜５０μｍの範囲が好ましく、より好ましくは
２〜３０μｍである。これより薄いと得られる記録層の
インク吸収性が劣り、これより厚いと作業性が悪くなっ
たり、ブロッキングを生じやすくなり好ましくない。The coating thickness of the ink receiving layer is not particularly limited, but is preferably in the range of 1 to 50 μm, and more preferably 2 to 30 μm. If the thickness is smaller than this, the ink absorbability of the obtained recording layer is inferior. If the thickness is larger than this, workability deteriorates and blocking tends to occur, which is not preferable.

【００２８】本発明の包装材料及び袋には、静電気によ
る塵埃等の付着や走行性の点から、帯電防止性を付与す
るのが好ましい。帯電防止性を付与するには、プラスチ
ックフィルムの一方の面にインク受容層を設け、他方の
面に帯電防止層を設けたり、インク受容層に帯電防止剤
を添加するのが望ましい。The packaging material and the bag of the present invention are preferably provided with an antistatic property in view of adhesion of dust and the like due to static electricity and running properties. In order to impart antistatic properties, it is desirable to provide an ink receiving layer on one surface of the plastic film and provide an antistatic layer on the other surface, or to add an antistatic agent to the ink receiving layer.

【００２９】本発明でいう帯電防止層とは、帯電防止剤
からなる被覆層、帯電防止剤を含む樹脂層、金属あるい
は金属酸化物からなる蒸着層等であって、帯電防止剤に
は界面活性剤、導電性ポリマ、導電性カーボン微粒子、
金属あるいは金属酸化物微粒子等を使用できる。The antistatic layer in the present invention includes a coating layer made of an antistatic agent, a resin layer containing an antistatic agent, and a vapor-deposited layer made of metal or metal oxide. Agent, conductive polymer, conductive carbon fine particles,
Metal or metal oxide fine particles can be used.

【００３０】本発明におけるインク受容層には、本発明
の特性を損なわない範囲で各種の添加剤、例えば消泡
剤、増粘剤、酸化防止剤、紫外線防止剤、蛍光増白剤な
どを含有せしめてもよい。The ink receiving layer in the present invention contains various additives such as an antifoaming agent, a thickener, an antioxidant, an ultraviolet ray inhibitor, and a fluorescent whitening agent as long as the properties of the present invention are not impaired. You may do it.

【００３１】受容層の塗布方法は特に限定されないが、
グラビアコート法、リバースコート法、キスコート法、
ダイコート法、バーコート法などの方法を用いることが
できる。この際、フィルム上には塗布する前に必要に応
じて空気中あるいはそのほかの雰囲気中でのコロナ放電
処理や、プライマー処理などの表面処理を施すことによ
って、塗布性が良化するのみならず、受容層をより強固
にフィルム上に形成することができる。尚、塗剤濃度、
塗膜乾燥条件は特に限定されるものではないが、塗膜乾
燥は基材の諸特性に悪影響を及ぼさない範囲で行うのが
望ましい。The method of coating the receiving layer is not particularly limited,
Gravure coating, reverse coating, kiss coating,
Methods such as a die coating method and a bar coating method can be used. At this time, not only the coatability is improved by applying a surface treatment such as a corona discharge treatment or a primer treatment in the air or other atmosphere as necessary before coating on the film, The receiving layer can be more firmly formed on the film. In addition, the coating agent concentration,
The conditions for drying the coating film are not particularly limited, but the drying of the coating film is desirably performed within a range that does not adversely affect the properties of the substrate.

【００３２】[0032]

【実施例】まず、本発明における各種特性の評価方法に
ついて説明する。 （１）インクジェット印字性 エプソン（株）製インクジェットプリンターＰＭ７００
Ｃを用い、文字及び線画像をインクジェット印字し、印
字品質、インク吸収性を評価し、印字性を以下のように
判定した。尚、印字品質は拡大鏡を用いて肉眼観察にて
評価し、インク吸収性は印字直後印字部分を指で１回こ
すった場合のインクによる印字部の汚れ度合いにより評
価した。 （印字品質） ◎：非常に良好（ドットが均一で鮮明） ○：良好 △：やや劣る ×：ドットの流れ、はじき、にじみなどがある （インク吸収性） ◎：非常に良好（印字部がまったく汚れない） ○：良好 △：やや劣る ×：インクがとれ、印字部が汚れるDETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS First, a method for evaluating various characteristics according to the present invention will be described. (1) Inkjet printability Epson inkjet printer PM700
Using C, character and line images were ink-jet printed, print quality and ink absorbency were evaluated, and printability was determined as follows. The print quality was evaluated by visual observation using a magnifying glass, and the ink absorptivity was evaluated based on the degree of contamination of the printed portion with the ink when the printed portion was rubbed once with a finger immediately after printing. (Printing quality) ：: Very good (dots are uniform and clear) △: Good ：: Slightly poor ×: Dot flow, repelling, bleeding, etc. (Ink absorption) ：: Very good (printing part at all) ○: Good △: Slightly poor ×: Ink is removed and the printed part is stained

【００３３】（２）印字画像の耐水性 インクジェット印字した包装材料を水中に１分間浸漬
し、画像の流れ度合いを評価した。 ○：画像が全く流れない △：画像が僅かに流れる ×：画像が流れる(2) Water Resistance of Printed Image The packaging material on which ink-jet printing was performed was immersed in water for 1 minute, and the degree of flow of the image was evaluated. ：: Image does not flow at all △: Image flows slightly ×: Image flows

【００３４】（３）印字画像の耐湿性 インクジェット印字した包装材料を４０℃／８０％ＲＨ
の雰囲気中に１日間放置し、画像のにじみ度合いを評価
した。 ○：画像が全くにじまない △：画像が僅かににじむ ×：画像がにじむ(3) Moisture resistance of printed image The packaging material on which ink-jet printing was performed was subjected to 40 ° C./80% RH.
Was allowed to stand for one day in the atmosphere, and the degree of bleeding of the image was evaluated. ：: Image does not blur at all Δ: Image slightly blurs ×: Image blurs

【００３５】（４）ヘイズ スガ試験機（株）製直読ヘーズコンピュータＨＧＭ−２
ＤＰ（Ｃ光源用）を用いて測定した。(4) Haze Direct reading haze computer HGM-2 manufactured by Suga Test Machine Co., Ltd.
It measured using DP (for C light sources).

【００３６】次に、本発明を実施例に基づいて具体的に
説明するが、これに限定されるものではない。 実施例１ 常法によって製造されたポリエチレンテレフタレートの
ホモポリマーチップ（固有粘度：０．６２、融点：２５
９℃）を用いて、常法によって厚み３８μｍ、比重１．
４の二軸延伸ポリエステルフィルムを得た。このように
して得られたポリエステルフィルムの表面にコロナ放電
処理を行った。次に、コロナ放電処理面に受容層とし
て、ポリビニルアルコール（クラレ（株）製、ＬＭ−１
５）とカチオン性アクリル樹脂（日本純薬（株）製、ジ
ュリマーＳＰＯ−６０２）とポリビニルピロリドン（Ｂ
ＡＳＦ社製、ルビスコールＫ−９０）とジルコニウム系
硬化剤（第一希元素化学工業（株）、ジルコゾールＺＣ
−２）及びシリカ粒子（水澤化学（株）製、ミズカシル
Ｐ７０５）が固形分比で１００／５０／１００／５／１
００となるように水／メタノール＝２／１溶媒に溶解・
分散し、固形分２０％の溶液とし、乾燥後の厚みが３μ
ｍになるようにグラビアコーターにて塗布し、１２０℃
で１分間乾燥させ本発明の包装材料を得た。かくして得
られた包装材料の印字特性は表１に示した通りで、印字
性が良好で、耐水性、耐湿性も優れているものであっ
た。また、袋として用いた場合、内容物がよく見え判別
しやすく、印字画像も読みやすく良好であった。Next, the present invention will be specifically described based on examples, but the present invention is not limited to these examples. Example 1 A homopolymer chip of polyethylene terephthalate produced by a conventional method (intrinsic viscosity: 0.62, melting point: 25)
9 ° C.) and a thickness of 38 μm and a specific gravity of 1.
4 was obtained. The surface of the polyester film thus obtained was subjected to a corona discharge treatment. Next, polyvinyl alcohol (manufactured by Kuraray Co., Ltd., LM-1) was used as a receiving layer on the corona discharge treated surface.
5), a cationic acrylic resin (manufactured by Nippon Junyaku Co., Ltd., Julimer SPO-602) and polyvinylpyrrolidone (B
ASF, Rubiscol K-90) and a zirconium-based curing agent (Daiichi Kagaku Kagaku Kogyo Co., Ltd., Zircosol ZC)
-2) and silica particles (Mizukasil P705, manufactured by Mizusawa Chemical Co., Ltd.) in a solid content ratio of 100/50/100/5/1.
Dissolve in water / methanol = 2/1 solvent to give 00
Disperse to form a solution having a solid content of 20%, and the thickness after drying is 3 μm.
m with a gravure coater, 120 ° C
For 1 minute to obtain a packaging material of the present invention. The printing properties of the packaging material thus obtained were as shown in Table 1, and the printing properties were good, and the water resistance and moisture resistance were excellent. When used as a bag, the contents were clearly visible and easy to discriminate, and the printed image was also easy to read and was good.

【００３７】実施例２ 実施例１において受容層として、シリカ粒子（水澤化学
（株）製、ミズカシルＰ７０５）を固形分比で１５０部
とした以外は実施例１と同様にして本発明の包装材料を
得た。かくして得られた包装材料の印字特性は表１に示
した通りで、印字性が良好で、耐水性、耐湿性も優れて
いるものであった。また、袋として用いた場合、内容物
がよく見え判別しやすく、印字画像も読みやすく良好で
あった。Example 2 A packaging material of the present invention was prepared in the same manner as in Example 1 except that the solid content ratio of silica particles (Mizukasil P705, manufactured by Mizusawa Chemical Co., Ltd.) was changed to 150 parts. I got The printing properties of the packaging material thus obtained were as shown in Table 1, and the printing properties were good, and the water resistance and moisture resistance were excellent. When used as a bag, the contents were clearly visible and easy to discriminate, and the printed image was also easy to read and was good.

【００３８】実施例３ 実施例１において受容層として、シリカ粒子（水澤化学
（株）製、ミズカシルＰ７０５）を固形分比で２０部と
した以外は実施例１と同様にして本発明の包装材料を得
た。かくして得られた包装材料の印字特性は表１に示し
た通りで、印字性が良好で、耐水性、耐湿性も優れてい
るものであった。また、袋として用いた場合、内容物が
よく見え判別しやすく、印字画像も読みやすく良好であ
った。Example 3 A packaging material of the present invention was prepared in the same manner as in Example 1 except that the solid content ratio of silica particles (Mizukasil P705, manufactured by Mizusawa Chemical Co., Ltd.) was 20 parts. I got The printing properties of the packaging material thus obtained were as shown in Table 1, and the printing properties were good, and the water resistance and moisture resistance were excellent. When used as a bag, the contents were clearly visible and easy to discriminate, and the printed image was also easy to read and was good.

【００３９】実施例４ 実施例１においてプラスチックフィルムとして、ポリプ
ロピレンフィルムを用いた以外は同様にして本発明の包
装材料を得た。かくして得られた包装材料の印字特性は
表１に示した通りで、印字性が良好で、耐水性、耐湿性
も優れているものであった。また、袋として用いた場
合、内容物がよく見え判別しやすく、印字画像も読みや
すく良好であった。Example 4 A packaging material of the present invention was obtained in the same manner as in Example 1, except that a polypropylene film was used as the plastic film. The printing properties of the packaging material thus obtained were as shown in Table 1, and the printing properties were good, and the water resistance and moisture resistance were excellent. When used as a bag, the contents were clearly visible and easy to discriminate, and the printed image was also easy to read and was good.

【００４０】実施例５ 実施例１において受容層として、シリカ粒子（水澤化学
（株）製、ミズカシルＰ７０５）の代わりにアゾ系ブル
ー染料を固形分比で２０部とした以外は実施例１と同様
にして本発明の包装材料を得た。かくして得られた包装
材料の印字特性は表１に示した通りで、記録性が良好
で、耐水性、耐湿性も優れているものであった。また、
袋として用いた場合、内容物がよく見え判別しやすく、
印字画像も読みやすく良好であった。Example 5 The same procedure as in Example 1 was carried out except that the azo blue dye was used as a receiving layer in a solid content ratio of 20 parts instead of silica particles (Mizukasil P705, manufactured by Mizusawa Chemical Co., Ltd.). Thus, a packaging material of the present invention was obtained. The printing characteristics of the packaging material thus obtained were as shown in Table 1, and the recording material was good, and the water resistance and the moisture resistance were excellent. Also,
When used as a bag, the contents are easy to see and distinguish,
The printed image was easy to read and good.

【００４１】比較例１ 実施例１において、受容層として、シリカ粒子（水澤化
学（株）製、ミズカシルＰ７０５）を含まない以外は同
様にして包装材料を得た。かくして得られた包装材料の
印字特性は表１に示した通りで、印字性が良好で、耐水
性、耐湿性も優れているものであり、袋として用いた場
合、内容物がよく見え判別しやすいものであったが、印
字画像が読みづらいものであった。Comparative Example 1 A packaging material was obtained in the same manner as in Example 1 except that the receiving layer did not contain silica particles (Mizukasil P705, manufactured by Mizusawa Chemical Co., Ltd.). The printing characteristics of the packaging material thus obtained are as shown in Table 1, and have good printability, and excellent water resistance and moisture resistance. It was easy, but the printed image was difficult to read.

【００４２】比較例２ 実施例１において、受容層として、シリカ粒子（水澤化
学（株）製、ミズカシルＰ７０５）を固形分比で２００
部とした以外は実施例１と同様にして包装材料を得た。
かくして得られた包装材料の印字特性は表１に示した通
りで、印字画像ににじみが見られ、また袋として用いた
場合、内容物がよく見えず判別しにくいものであった。Comparative Example 2 In Example 1, silica particles (Mizukasil P705, manufactured by Mizusawa Chemical Co., Ltd.) were used as the receiving layer in a solid content ratio of 200.
A packaging material was obtained in the same manner as in Example 1 except that the above parts were used.
The printing characteristics of the packaging material thus obtained were as shown in Table 1. The printed image was blurred, and when used as a bag, the contents were not easily seen and were difficult to distinguish.

【００４３】実施例６ 実施例１で得られた包装材料と一般上質紙（坪量６５ｇ
／ｍ² ）を酢酸ビニル・アクリル共重合樹脂（日栄化工
（株）製、ライフボンド）を用いて３端部を貼り合わせ
て袋を作製した。得られた袋のインク受容層面に、薬局
名、薬の効能・効果、注意事項等を印字した袋の中に薬
を入れたところ、薬局名、薬の効能・効果、注意事項等
も読みやすく、薬も見やすく薬袋用として非常に良好で
あった。Example 6 The packaging material obtained in Example 1 and general high-quality paper (basis weight: 65 g)
/ M ² ) using a vinyl acetate / acrylic copolymer resin (manufactured by Niei Chemical Co., Ltd., Life Bond) at three ends to form a bag. When the medicine is placed in the bag with the name of the pharmacy, the efficacy and effect of the medicine, and precautions printed on the ink receiving layer of the obtained bag, the pharmacy name, the efficacy and effect of the medicine, and precautions are also easy to read. The medicine was easy to see and was very good for medicine bags.

【００４４】[0044]

【表１】 [Table 1]

【００４５】表１から判るように、インク受容層が積層
されたフィルムのヘイズを１０〜９０％の範囲内に制御
することにより、内容物がよく見え判別しやすく、また
印字画像も読みやすい包装材料が得られる。As can be seen from Table 1, by controlling the haze of the film on which the ink receiving layer is laminated within the range of 10 to 90%, the contents are easily seen and discriminated, and the printed image is easy to read. The material is obtained.

【００４６】[0046]

【発明の効果】以上説明したように、本発明の包装材料
は、インク吸収性に優れ、印字濃度が高く、内容物が可
視化でき、印字画像も読みやすく、しかも耐水性、耐湿
性に優れたものであり、特にカラーインクジェットプリ
ンター用包装材料として好ましく使用できる。さらに、
電子写真複写機やファブリックインク受容体やカーボン
インク受容体、昇華型を含む感熱転写インク受容体およ
びオフセット印刷、フレキソ印刷などの用途において好
ましく用いることができる。また、透明プラスチックフ
ィルムを用い、インク受容層に染料を含有させたものは
ＯＨＰフィルムとしても有効に使用できる。As described above, the packaging material of the present invention has excellent ink absorbency, high print density, visualization of contents, easy readability of printed images, and excellent water resistance and moisture resistance. And particularly preferably used as a packaging material for a color inkjet printer. further,
It can be preferably used in electrophotographic copying machines, fabric ink receivers, carbon ink receivers, thermal transfer ink receivers including sublimation types, and applications such as offset printing and flexographic printing. A transparent plastic film containing a dye in the ink receiving layer can be effectively used as an OHP film.

【００４７】また、包装材料の裏面に粘着層を積層する
ことにより、各種ラベルとしても有効に使用できる。Further, by laminating an adhesive layer on the back surface of the packaging material, it can be effectively used as various labels.

【００４８】さらに、本発明の袋はヘイズを規定するこ
とにより、印字画像が見やすく、内容物も判別しやすい
ため、薬袋等に有効に使用できる。Furthermore, the bag of the present invention can be used effectively for medicine bags and the like because the printed image is easy to see and the contents can be easily identified by defining the haze.

Claims (9)

【特許請求の範囲】[Claims] 【請求項１】 少なくとも一部にプラスチックフィルム
が用いられ、かつ、該フィルムの少なくとも一面にイン
ク受容層が設けられた包装材料において、インク受容層
が設けられたフィルムのヘイズが１０〜９０％の範囲に
あることを特徴とする包装材料。1. A packaging material in which a plastic film is used at least in part and an ink receiving layer is provided on at least one surface of the film, wherein the haze of the film provided with the ink receiving layer is 10 to 90%. Packaging material characterized by being in the range. 【請求項２】 インク受容層が設けられたフィルムのヘ
イズが２０〜９０％の範囲にある、請求項１に記載の包
装材料。2. The packaging material according to claim 1, wherein the haze of the film provided with the ink receiving layer is in the range of 20 to 90%. 【請求項３】 インク受容層が無機粒子、有機粒子、染
料、顔料の少なくとも１種を含有している、請求項１ま
たは２に記載の包装材料。3. The packaging material according to claim 1, wherein the ink receiving layer contains at least one of inorganic particles, organic particles, a dye, and a pigment. 【請求項４】 インク受容層がインクジェット記録用受
容層である、請求項１ないし３のいずれかに記載の包装
材料。4. The packaging material according to claim 1, wherein the ink receiving layer is an ink jet recording receiving layer. 【請求項５】 プラスチックフィルムがポリエステル、
ポリオレフィン、ポリスチレンのいずれかからなり、か
つ、該プラスチックフィルムの厚みが５μｍ以上２００
μｍ以下である、請求項１ないし４のいずれかに記載の
包装材料。5. The plastic film is made of polyester,
Polyolefin or polystyrene, and the thickness of the plastic film is 5 μm or more and 200 μm or more.
The packaging material according to any one of claims 1 to 4, which has a size of not more than μm. 【請求項６】 少なくとも一部にプラスチックフィルム
が用いられ、かつ、該フィルムの少なくとも一面にイン
ク受容層が設けられた袋において、インク受容層が設け
られたフィルムのヘイズが１０〜９０％の範囲にあるこ
とを特徴とする袋。6. A bag in which a plastic film is used at least in part and at least one surface of the film is provided with an ink receiving layer, the haze of the film provided with the ink receiving layer is in the range of 10 to 90%. A bag characterized in that: 【請求項７】 基材が紙又は高分子フィルムである、請
求項６に記載の袋。7. The bag according to claim 6, wherein the substrate is paper or a polymer film. 【請求項８】 袋の内容物についての説明がプラスチッ
クフィルムに記載され、かつ該内容物をプラスチックフ
ィルムを通して見ることが出来ることを特徴とする請求
項６または７に記載の袋。8. The bag according to claim 6, wherein the contents of the bag are described on a plastic film, and the contents can be viewed through the plastic film. 【請求項９】 薬の袋である、請求項６ないし８のいず
れかに記載の袋。9. The bag according to claim 6, which is a medicine bag.