JPH11293032A - Novel additive for resin - Google Patents

Novel additive for resin

Info

Publication number
JPH11293032A
JPH11293032A JP10099660A JP9966098A JPH11293032A JP H11293032 A JPH11293032 A JP H11293032A JP 10099660 A JP10099660 A JP 10099660A JP 9966098 A JP9966098 A JP 9966098A JP H11293032 A JPH11293032 A JP H11293032A
Authority
JP
Japan
Prior art keywords
resin
inorganic powder
additive
aluminosilicate
molding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP10099660A
Other languages
Japanese (ja)
Inventor
Hisanori Shinohara
久典 篠原
Toshio Kadoi
寿雄 角井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lion Corp
Original Assignee
Lion Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lion Corp filed Critical Lion Corp
Priority to JP10099660A priority Critical patent/JPH11293032A/en
Publication of JPH11293032A publication Critical patent/JPH11293032A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain an additive which effectively deodorizes and removes a bad small by using an inorganic powder as a major component which can destroy and remove a bad smell generating during kneading and molding a resin composition. SOLUTION: An inorganic powder which can deodorizes and remove a bad smell is preferably an aluminosilicate comprising substantially 5-80 mol.% of SiO2 , 5-65 mol.% of MOn/2 and 1-60 mol.% of Al2 O3 , wherein M is Zn, Cu, Ag, Co, Ni, Ti, Ba, Sn or Zr and n is mol weighted average valence. The aluminosilicate is preferably a layer aluminosilicate having a so-called phyllosilicate structure and is most preferably a composite aluminosilicate having a layer of the phyllosilicate structure and a metal oxide layer of octahedral structure laminated thereon.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、樹脂組成物の混練
及び成型時に発生する悪臭を消臭除去することができる
無機粉体を主成分として含有する樹脂用添加剤、及びこ
の樹脂用添加剤を用いて樹脂組成物の混練及び成型時に
発生する悪臭を消臭除去する方法に関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an additive for a resin containing, as a main component, an inorganic powder capable of deodorizing and removing an odor generated during kneading and molding of a resin composition, and an additive for the resin. The present invention relates to a method for removing and removing an offensive odor generated during kneading and molding of a resin composition using the same.

【0002】[0002]

【従来の技術】熱可塑性樹脂は成型性、機械的強度等に
優れているため、各種家電製品や自動車部品さらには日
用雑貨など様々な分野に多用されている。しかし、電気
絶縁性、可燃性、紫外線や熱による劣化性、という欠点
を有しており、これらの欠点を改善する方法として、樹
脂の混練又は成型時に帯電防止剤、難燃剤、紫外線吸収
剤、酸化防止剤等を添加する必要がある。更に、樹脂を
混練又は成型する時の温度としては、ポリプロピレン樹
脂やポリスチレン樹脂等の汎用樹脂の場合200℃〜3
00℃、ポリカーボネート樹脂やポリエチレンテレフタ
レート樹脂等のエンジニアリング樹脂では300℃以上
となる。このような高温では、混練又は成型時に樹脂自
体の有する臭気や樹脂が一部分解した悪臭が発生した
り、また、前記の添加剤が熱分解又は気化することによ
り不快な臭気が発生する。
2. Description of the Related Art Thermoplastic resins are widely used in various fields such as various home electric appliances, automobile parts and daily necessities because of their excellent moldability and mechanical strength. However, it has drawbacks of electrical insulation, flammability, deterioration by ultraviolet rays and heat, and as a method for improving these drawbacks, an antistatic agent, a flame retardant, an ultraviolet absorber at the time of kneading or molding a resin, It is necessary to add an antioxidant and the like. Furthermore, the temperature at which the resin is kneaded or molded is 200 ° C. to 3 ° C. for general-purpose resins such as polypropylene resin and polystyrene resin.
The temperature is 00 ° C. and 300 ° C. or higher for engineering resins such as polycarbonate resin and polyethylene terephthalate resin. At such a high temperature, an odor which the resin itself has during kneading or molding or a malodor resulting from partial decomposition of the resin is generated, or an unpleasant odor is generated due to thermal decomposition or vaporization of the additive.

【0003】この場合の対策としては、樹脂を取り扱う
工場全体に排気装置を設置するか、又は作業員自身がガ
スマスクなどを使用するということ等が考えられる。し
かしながら、工場全体に排気装置を設置するには相当の
費用が必要となり、又ガスマスクではあらゆる悪臭成分
を吸収することができないため、実際にはこれらのよう
な対策は殆どの場合、取られていないのが実情である。
更に、このような臭気は、作業員の健康を害するだけで
なく、工場周辺への環境破壊や工場周辺の住民の健康阻
害を招く恐れもある。
In this case, as a countermeasure, it is conceivable that an exhaust device is installed in the entire factory where the resin is handled, or that a worker himself uses a gas mask or the like. However, installing exhaust systems throughout the factory requires considerable expense, and gas masks cannot absorb all offensive odor components, so in practice such measures are almost always taken. There is no fact.
Further, such an odor may not only impair the health of workers, but also cause environmental destruction around the factory and impair the health of residents around the factory.

【0004】[0004]

【発明が解決しようとする課題】本発明は、樹脂を混
練、成型する際に発生する樹脂自体の臭気及び樹脂自身
の分解により発生する臭気、更に樹脂に添加される添加
剤が原因で発生する臭気及び添加剤の分解により発生す
る臭気を吸着又は吸収することにより悪臭を有効に消
臭、除去することを目的とする新規な樹脂用添加剤を提
供する。
DISCLOSURE OF THE INVENTION The present invention is characterized by the odor of the resin itself generated during kneading and molding of the resin, the odor generated by the decomposition of the resin itself, and the additives generated in the resin. Provided is a novel resin additive for effectively eliminating or removing malodors by absorbing or absorbing odors and odors generated by decomposition of additives.

【0005】[0005]

【課題を解決するための手段】本発明者らは、鋭意研究
を重ねた結果、樹脂組成物を混練、成型する際に、消臭
機能を有する無機粉体を樹脂組成物に対して、0.01
〜30重量%添加することにより、その際に発生する悪
臭物質を吸収し、その悪臭物質を消臭除去することがで
きることを見出した。
Means for Solving the Problems As a result of intensive studies, the present inventors have found that when kneading and molding a resin composition, an inorganic powder having a deodorizing function is added to the resin composition in an amount of 0%. .01
By adding 〜30% by weight, it has been found that malodorous substances generated at that time can be absorbed and the malodorous substances can be deodorized and removed.

【0006】すなわち、本発明は、樹脂組成物の混練及
び成型時に発生する悪臭を消臭除去することができる無
機粉体を主成分として含有する樹脂用添加剤に関する。
[0006] That is, the present invention relates to a resin additive containing, as a main component, an inorganic powder capable of deodorizing and removing a bad odor generated during kneading and molding of a resin composition.

【0007】尚、本発明の樹脂用添加剤において、無機
粉体としては、アルミノ珪酸塩からなる無機粉体であ
り、かつ、モル%で表示して本質的に以下の組成を有す
る無機粉体が好ましい。 SiO2 :5〜80% MOn/2 :5〜65% Al23:1〜60% (式中、Mは、亜鉛、銅、銀、コバルト、ニッケル、
鉄、チタン、バリウム、スズおよびジルコニウムからな
る群より選ばれる一種以上の金属であり、nは金属Mの
モル加重平均原子価である)
In the resin additive of the present invention, the inorganic powder is an inorganic powder composed of an aluminosilicate, and has the following composition in mol%. Is preferred. SiO 2: 5~80% MO n / 2: 5~65% Al 2 O 3: 1~60% ( wherein, M is zinc, copper, silver, cobalt, nickel,
Is at least one metal selected from the group consisting of iron, titanium, barium, tin and zirconium, and n is the molar weighted average valence of metal M)

【0008】また、本発明は、上記の樹脂用添加剤を樹
脂組成物に対して0.01〜30重量%添加することに
よって、樹脂組成物の混練及び成型時に発生する悪臭を
消臭除去する方法に関する。
In the present invention, the above-mentioned resin additive is added in an amount of 0.01 to 30% by weight with respect to the resin composition, thereby eliminating and eliminating odors generated during kneading and molding of the resin composition. About the method.

【0009】[0009]

【発明の実施の形態】本発明で用いられる無機粉体とし
ては、樹脂組成物の混練及び成型時に発生する悪臭を消
臭除去することができるだけの消臭機能を有するもので
あれば、特に限定されるものではない。このような無機
粉体としては、多孔質珪酸塩類、活性炭、添着活性炭、
ゼオライト、モンモリロナイトやスメクタイトに代表さ
れる天然層状化合物、また、シリカ、活性アルミナ、活
性白土、酸化亜鉛等の両性金属酸化物等が挙げられる。
本発明においては、これらを1種類のみ使用しても構わ
ないが、2種類以上併用しても構わない。
BEST MODE FOR CARRYING OUT THE INVENTION The inorganic powder used in the present invention is not particularly limited as long as it has a deodorizing function capable of deodorizing and removing malodor generated during kneading and molding of a resin composition. It is not something to be done. Such inorganic powders include porous silicates, activated carbon, impregnated activated carbon,
Examples include natural layered compounds represented by zeolite, montmorillonite and smectite, and amphoteric metal oxides such as silica, activated alumina, activated clay, and zinc oxide.
In the present invention, only one of these may be used, but two or more of them may be used in combination.

【0010】無機粉体の粒子径としては、0.01〜1
0μmが好ましく、0.05〜5μmがさらに好まし
い。無機粉体の粒子径が10μmを超えると、樹脂物性
を劣化し、0.01μm未満の粒子は消臭無機粉体とし
ては実用的ではない。
[0010] The particle size of the inorganic powder is 0.01 to 1
0 μm is preferable, and 0.05 to 5 μm is more preferable. When the particle diameter of the inorganic powder exceeds 10 μm, the physical properties of the resin deteriorate, and particles having a particle diameter of less than 0.01 μm are not practical as a deodorant inorganic powder.

【0011】上記無機粉体の中でも、消臭機能を有する
無機粉体としては、アルミノ珪酸塩からなる無機粉体で
あり、かつ、モル%で表示して本質的に以下の組成を有
する無機粉体が特に好ましい。 SiO2 :5〜80%、好ましくは25〜70% MOn/2 :5〜65%、好ましくは15〜60% Al23:1〜60%、好ましくは1〜45% (式中、Mは、亜鉛、銅、銀、コバルト、ニッケル、
鉄、チタン、バリウム、スズおよびジルコニウムからな
る群より選ばれる一種以上の金属であり、nは金属Mの
モル加重平均原子価である)
Among the above-mentioned inorganic powders, the inorganic powder having a deodorizing function is an inorganic powder made of aluminosilicate, and has the following composition in mol%. The body is particularly preferred. SiO 2: 5 to 80%, preferably 25~70% MO n / 2: 5~65 %, preferably 15~60% Al 2 O 3: 1~60 %, preferably 1 to 45% (in the formula, M is zinc, copper, silver, cobalt, nickel,
Is at least one metal selected from the group consisting of iron, titanium, barium, tin and zirconium, and n is the molar weighted average valence of metal M)

【0012】更に、前記アルミノ珪酸塩としては、いわ
ゆるフィロ珪酸塩構造を有する層状アルミノ珪酸塩(ア
ルミニウム含有フィロ珪酸塩)が好ましく、フィロ珪酸
塩構造を有する層に八面体構造金属酸化物層が積層して
構成された複合化アルミノ珪酸塩(アルミニウム含有複
合フィロ珪酸塩)が特に好ましい。
The aluminosilicate is preferably a layered aluminosilicate having a so-called phyllosilicate structure (aluminum-containing phyllosilicate), and an octahedral metal oxide layer is laminated on the layer having the phyllosilicate structure. The composite aluminosilicate (aluminum-containing composite phyllosilicate) is particularly preferable.

【0013】このアルミニウム含有複合フィロ珪酸塩
は、基本的には、SiO4 を基本とする四面体構造層
と、MO6 (Mは前記と同様;以下同じ)を基本とする
八面体構造層とが、酸素原子を共有する形で積層した粘
土鉱物型の二層構造を有している。尚、このアルミニウ
ム含有複合フィロ珪酸塩においては、通常、四面体構造
層SiO4 の一部のSiがAlにより置換され、八面体
構造層MO6 の一部のAlにより置換されて構成されて
いる。
This aluminum-containing composite phyllosilicate is basically composed of a tetrahedral structure layer based on SiO 4 and an octahedral structure layer based on MO 6 (M is the same as above; the same applies hereinafter). Has a clay mineral type two-layer structure in which oxygen atoms are shared. Incidentally, in this aluminum-containing composite phyllosilicate, usually, a part of Si of the tetrahedral structure layer SiO 4 is replaced by Al and a part of the octahedral structure layer MO 6 is replaced by Al. .

【0014】このようなアルミノ珪酸塩は、白色又は単
色の粉体として得られ、上記組成物比に相当する量の水
溶性珪酸塩、水溶性金属塩さらに水溶性アルミニウム塩
及び/又は水溶性アルミン酸塩を水の存在下に反応さ
せ、必要により得られる沈殿を水の存在下に加熱するこ
とにより製造される。その粉体の粒子径は、通常0.0
1〜10μmで、好ましくは0.05〜5μmである。
Such an aluminosilicate is obtained as a white or monochromatic powder, and a water-soluble silicate, a water-soluble metal salt, a water-soluble aluminum salt and / or a water-soluble alumina in an amount corresponding to the above composition ratio. It is produced by reacting the acid salt in the presence of water and heating the resulting precipitate in the presence of water. The particle size of the powder is usually 0.0
It is 1 to 10 μm, preferably 0.05 to 5 μm.

【0015】本発明の樹脂用添加剤は、樹脂の性質を改
善するために配合されるその他の樹脂用添加剤を配合し
た樹脂組成物に対して配合される。配合方法としては、
樹脂の混練前に配合されていればよい。特に、混練前に
簡単に樹脂と混合すれば、添加も容易となり、その機能
もより効果的に発現される。実用的には、混練の際の樹
脂の投入口から樹脂と同時に添加するのが良い。
[0015] The resin additive of the present invention is blended with a resin composition containing other resin additives blended to improve the properties of the resin. As a compounding method,
What is necessary is just to mix before resin kneading. In particular, if it is easily mixed with the resin before kneading, the addition becomes easy and the function is more effectively exhibited. Practically, it is preferable to add the resin simultaneously with the resin from the inlet of the resin at the time of kneading.

【0016】本発明の樹脂用添加剤が添加される樹脂と
しては、熱可塑性樹脂が好適である。熱可塑性樹脂とし
ては、特に制限はなく、ポリプロピレン樹脂、ポリスチ
レン樹脂、アクリル樹脂、ABS樹脂、AS樹脂、MS
樹脂、ポリカーボネート樹脂、ポリエチレンテレフタレ
ート樹脂、ポリアセタール樹脂、ナイロン樹脂、ポリフ
ェニレンエーテル樹脂等が挙げられる。
The resin to which the resin additive of the present invention is added is preferably a thermoplastic resin. The thermoplastic resin is not particularly limited, and may be polypropylene resin, polystyrene resin, acrylic resin, ABS resin, AS resin, MS resin.
Resins, polycarbonate resins, polyethylene terephthalate resins, polyacetal resins, nylon resins, polyphenylene ether resins, and the like.

【0017】その他の樹脂用添加剤としては、ラバーダ
イジェスト社発行の「便覧ゴム・プラスチック配合薬
品」又は大成社発行の「新版・プラスチック配合剤−基
礎と応用」に記載されている添加剤であれば特に制限な
く使用される。
Other additives for the resin include those described in "Handbook of Rubber / Plastic Compounds" issued by Rubber Digest Co., Ltd. or "New Edition / Plastic Compounding Agents-Fundamentals and Applications" issued by Taisei Corporation. Used without any particular restrictions.

【0018】本発明の樹脂用添加剤を用いることによ
り、樹脂を混練及び成型する際に発生する樹脂自体の臭
気及び樹脂自体の分解により発生する臭気、また、標記
のその他の樹脂用添加剤を含む樹脂組成物を混練及び成
型する際にその他の樹脂用添加剤が原因で発生する臭気
及びその他の樹脂用添加剤自体の分解により発生する臭
気を吸着又は吸収することにより悪臭を消臭、除去する
ことができる。更に、本発明の樹脂用添加剤を用いるこ
とにより、これらのその他の樹脂用添加剤の性能を劣化
させることなく使用することができる。
By using the resin additive of the present invention, the odor of the resin itself generated during kneading and molding of the resin, the odor generated by the decomposition of the resin itself, and the other additive for resin described in the title can be reduced. Deodorizes and removes odors by adsorbing or absorbing odors caused by other resin additives and the decomposition of other resin additives themselves when kneading and molding the resin composition containing can do. Furthermore, by using the resin additive of the present invention, these other resin additives can be used without deteriorating the performance.

【0019】その他の樹脂用添加剤としては、具体的に
は、帯電防止剤、難燃剤、可塑剤、安定剤、酸化防止
剤、紫外線吸収剤、充填剤、発泡剤、滑剤、着色剤等が
挙げられる。そして、これらの具体的な化合物は標記の
文献に記載・例示されているものが使用できる。以下に
その一例を示す。
Specific examples of other resin additives include an antistatic agent, a flame retardant, a plasticizer, a stabilizer, an antioxidant, an ultraviolet absorber, a filler, a foaming agent, a lubricant, and a colorant. No. As these specific compounds, those described and exemplified in the title literature can be used. An example is shown below.

【0020】帯電防止剤としては、アニオン性界面活性
剤(アルキルリン酸エステル塩型、アルキルスルホン酸
塩型、アルキルアリールスルホン酸塩型、ポリオキシエ
チレンアルキルエーテル硫酸エステル型、ポリオキシエ
チレンアルキルフェノールエーテル硫酸エステル型
等)、カチオン性界面活性剤(第4級アンモニウム塩
型、イミダゾリン型、ピリジニウム塩型等)、非イオン
性界面活性剤(ポリオキシエチレン脂肪酸エステル型、
ポリオキシエチレンアルキルエーテル型、ポリオキシエ
チレンアルキルフェノールエーテル型、ポリオキシエチ
レンアルキルアミン型、ソルビタン脂肪酸エステル型
等)、両性界面活性剤(ベタイン型など)、無機塩、エ
ステル類、1価又は多価アルコール、脂肪酸アミン、脂
肪酸アミド等が挙げられる。
Examples of the antistatic agent include anionic surfactants (alkyl phosphate ester type, alkyl sulfonate type, alkyl aryl sulfonate type, polyoxyethylene alkyl ether sulfate ester type, polyoxyethylene alkylphenol ether sulfate) Ester type), cationic surfactants (quaternary ammonium salt type, imidazoline type, pyridinium salt type etc.), nonionic surfactants (polyoxyethylene fatty acid ester type,
Polyoxyethylene alkyl ether type, polyoxyethylene alkyl phenol ether type, polyoxyethylene alkylamine type, sorbitan fatty acid ester type, etc.), amphoteric surfactant (betaine type, etc.), inorganic salts, esters, monohydric or polyhydric alcohol , Fatty acid amines, fatty acid amides and the like.

【0021】難燃剤としては、無機化合物、リン酸エス
テル及びリン化合物、塩素系難燃剤、臭素系難燃剤、反
応型難燃剤(含ハロゲン有機化合物、含リン,含ハロゲ
ンポリオール等)等が挙げられる。
Examples of the flame retardant include inorganic compounds, phosphate esters and phosphorus compounds, chlorine-based flame retardants, bromine-based flame retardants, and reactive flame retardants (halogen-containing organic compounds, phosphorus-containing, halogen-containing polyols, and the like). .

【0022】可塑剤としては、フタル酸誘導体、イソフ
タル酸誘導体、テトラヒドロフタル酸誘導体、アジピン
酸誘導体、アゼライン酸誘導体、セバシン酸誘導体、ド
デカン−2−酸誘導体、マレイン酸誘導体、フマル酸誘
導体、トリメリット酸誘導体、クエン酸誘導体、イタコ
ン酸誘導体、オレイン酸誘導体、リシノール酸誘導体、
ステアリン酸誘導体、スルホン酸誘導体、リン酸誘導
体、グルタール酸誘導体、グリコール誘導体、グリセリ
ン誘導体、パラフィン誘導体、エポキシ誘導体、重合系
可塑剤等が挙げられる。
Examples of the plasticizer include phthalic acid derivatives, isophthalic acid derivatives, tetrahydrophthalic acid derivatives, adipic acid derivatives, azelaic acid derivatives, sebacic acid derivatives, dodecane-2-acid derivatives, maleic acid derivatives, fumaric acid derivatives, and trimellitate. Acid derivatives, citric acid derivatives, itaconic acid derivatives, oleic acid derivatives, ricinoleic acid derivatives,
Examples include stearic acid derivatives, sulfonic acid derivatives, phosphoric acid derivatives, glutaric acid derivatives, glycol derivatives, glycerin derivatives, paraffin derivatives, epoxy derivatives, and polymerization plasticizers.

【0023】安定剤としては、鉛系安定剤、金属石鹸
(カルシウム石鹸、バリウム石鹸、カドミウム石鹸、亜
鉛石鹸、鉛石鹸等)、金属液状安定剤、有機スズ安定剤
(ラウレート系、マレエート系、マルカプタイド系
等)、アンチモン系安定剤、非金属安定剤(エポキシ化
合物、亜リン酸エステル等)等が挙げられる。
Examples of the stabilizer include lead-based stabilizers, metal soaps (calcium soap, barium soap, cadmium soap, zinc soap, lead soap, etc.), metal liquid stabilizers, and organotin stabilizers (laurate, maleate, marcaptide) , Etc.), antimony stabilizers, non-metallic stabilizers (epoxy compounds, phosphites, etc.).

【0024】酸化防止剤としては、ナフチルアミン系酸
化防止剤、ジフェニルアミン系酸化防止剤、p−フェニ
レンジアミン系酸化防止剤、キノリン系酸化防止剤、ヒ
ドロキノン誘導体、モノフェノール系酸化防止剤、ビ
ス,トリス,ポリフェノール系酸化防止剤、チオビスフ
ェノール系酸化防止剤等が挙げられる。
Examples of the antioxidant include naphthylamine antioxidants, diphenylamine antioxidants, p-phenylenediamine antioxidants, quinoline antioxidants, hydroquinone derivatives, monophenol antioxidants, bis, tris, Examples thereof include polyphenol-based antioxidants and thiobisphenol-based antioxidants.

【0025】紫外線吸収剤としては、ベンゾフェノン系
紫外線吸収剤、サルチレート系紫外線吸収剤、ベンゾト
リアゾール系紫外線吸収剤、アクリロニトリル系紫外線
吸収剤、金属錯塩系紫外線吸収剤、ヒンダードアミン系
紫外線吸収剤等が挙げられる。
Examples of the ultraviolet absorber include a benzophenone ultraviolet absorber, a saltylate ultraviolet absorber, a benzotriazole ultraviolet absorber, an acrylonitrile ultraviolet absorber, a metal complex salt ultraviolet absorber, and a hindered amine ultraviolet absorber. .

【0026】充填剤としては、炭酸カルシウム、タル
ク、クレー、ケイ酸及びケイ酸塩、アスベスト、マイカ
粉、ガラス繊維,球、有機質充填剤等が挙げられる。
Examples of the filler include calcium carbonate, talc, clay, silicic acid and silicate, asbestos, mica powder, glass fiber, sphere, organic filler and the like.

【0027】発泡剤としては、重炭酸ナトリウム、重炭
酸アンモニウム、ホウ水素化ナトリウム等の無機発砲
剤、アゾ系発砲剤(アゾジカルボンアミド、アゾビスイ
ソブチロニトリル等)、ニトロソ系発砲剤(ジニトロソ
ペンタメチレンテトラミン、N,N´−ジニトロソ−
N,N´−ジメチルテレフタルアミド等)、ヒドラジド
発砲剤(p−トルエンスルホニルヒドラジド、p,p´
−オキシ−ビス(ベンゼンスルホニルヒドラジド)、ベ
ンゼンスルホニルヒドラジド等)、トリヒドラジノトリ
アジン等の有機発砲剤等が挙げられる。
Examples of the foaming agent include inorganic foaming agents such as sodium bicarbonate, ammonium bicarbonate and sodium borohydride; azo foaming agents (such as azodicarbonamide and azobisisobutyronitrile); Nitrosopentamethylenetetramine, N, N'-dinitroso-
N, N'-dimethylterephthalamide, etc.), hydrazide foaming agents (p-toluenesulfonylhydrazide, p, p '
-Oxy-bis (benzenesulfonyl hydrazide), benzenesulfonyl hydrazide, etc.) and organic foaming agents such as trihydrazinotriazine.

【0028】滑剤としては、パラフィン及び炭化水素樹
脂、脂肪酸、脂肪酸アミド、脂肪酸エステル、脂肪アル
コール、脂肪酸と多価アルコールの部分エステル、金属
石鹸類、天然ワックス、シリコーン等が挙げられる。
Examples of the lubricant include paraffin and hydrocarbon resin, fatty acid, fatty acid amide, fatty acid ester, fatty alcohol, partial ester of fatty acid and polyhydric alcohol, metal soaps, natural wax, silicone and the like.

【0029】着色剤としては、染料、無機顔料(酸化チ
タン、ベンガラ、黄鉛、カドミウム系顔料、群青、カー
ボンブラック等)、有機顔料(不溶性アゾ顔料、溶性ア
ゾ顔料、縮合アゾ顔料、フタロシアニン系顔料、建築染
料系顔料、キナクリドン系顔料、ジオキサジン系顔料、
染付レーキ顔料等)、有機蛍光顔料、真珠箔等が挙げら
れる。
Examples of the coloring agent include dyes, inorganic pigments (titanium oxide, red iron oxide, graphite, cadmium pigments, ultramarine, carbon black, etc.), and organic pigments (insoluble azo pigments, soluble azo pigments, condensed azo pigments, phthalocyanine pigments). , Architectural dye pigments, quinacridone pigments, dioxazine pigments,
Dyed lake pigments, etc.), organic fluorescent pigments, pearl foils and the like.

【0030】本発明の樹脂用添加剤の樹脂組成物に対す
る含有量は、0.01〜30重量%、好ましくは0.0
5〜20重量%、更に好ましくは0.1〜15重量%で
ある。樹脂用添加剤の含有量が0.01重量%より低く
なると、混練時や成型時の樹脂由来の臭気や添加剤が原
因で発生する臭気を効率よく除去することができない。
一方、含有量が30重量%を超えると成型後の樹脂物性
が低下し、実使用が不可能となる。
The content of the resin additive of the present invention in the resin composition is 0.01 to 30% by weight, preferably 0.0 to 30% by weight.
It is 5 to 20% by weight, more preferably 0.1 to 15% by weight. When the content of the resin additive is lower than 0.01% by weight, it is not possible to efficiently remove the odor derived from the resin during kneading or molding and the odor generated due to the additive.
On the other hand, if the content exceeds 30% by weight, the physical properties of the resin after molding are reduced, and practical use becomes impossible.

【0031】[0031]

【実施例】次に、本発明を実施例によりさらに詳細に説
明する。尚、以下の例において、「%」は「重量%」を
表す。
Next, the present invention will be described in more detail with reference to examples. In the following examples, “%” represents “% by weight”.

【0032】実施例1〜3及び比較例1 ポリプロピレン樹脂(出光石油化学(株)性、商品名
“J750H”)に、帯電防止剤(ライオン・アクゾ
(株)製、商品名“アーモスタット410”)を0.5
%及びアルミノ珪酸塩(ライオン(株)製、商品名“ラ
イオナイトSF”、組成比:SiO2 /ZnO/Al2
3=38/47/15(モル比)、粒子径3〜5μ
m)を樹脂組成物に対して表1に示す量添加して、ラボ
プラストミルを用いて、200℃で5分間混練した後、
200℃、150kgfで5分間板状に成型し、性能評
価を行った。尚、悪臭の除去消臭評価は、下記のように
して行い、また、帯電防止性能評価は20℃、60R.
H.の雰囲気下に樹脂板を一昼夜保存した後、ASTM
D 257に従い表面抵抗計を用いて表面抵抗値を測
定した。結果を表1に示す。
Examples 1-3 and Comparative Example 1 A polypropylene resin (manufactured by Idemitsu Petrochemical Co., Ltd., trade name "J750H") was added to an antistatic agent (Lion Akzo Co., Ltd., trade name "Armostat 410"). ) To 0.5
% And aluminosilicates (Lion Co., Ltd., trade name "Lion Night SF", the composition ratio: SiO 2 / ZnO / Al 2
O 3 = 38/47/15 (molar ratio), particle size 3-5 μm
m) was added to the resin composition in an amount shown in Table 1, and kneaded at 200 ° C. for 5 minutes using a Labo Plastomill.
It was molded into a plate at 200 ° C. and 150 kgf for 5 minutes, and the performance was evaluated. The evaluation of the removal and deodorization of offensive odor was performed as follows, and the evaluation of antistatic performance was performed at 20 ° C. and 60R.
H. After storing the resin plate in the atmosphere of the day and night, ASTM
The surface resistance was measured using a surface resistance meter according to D257. Table 1 shows the results.

【0033】(悪臭の消臭除去評価方法)まず、樹脂組
成物と消臭性無機粉体とを混練及び成型した際に感じる
臭気を官能で以下の基準に従い評価した。また、できあ
がった製品に相当するものの評価を次のように行なっ
た。消臭性無機粉体を配合し、混練及び成型した樹脂板
を約2×3mmのチップ状に裁断し、100gの沸騰し
た水に裁断した樹脂チップ(10g)を添加して、30
分間煮沸した。その際、30分間、ふたをしたままで臭
気が逃げないようにし、30分後にそれらの臭気を官能
で以下の基準に従い評価した。 ◎:全く臭気なし ○:わずかに臭気を感じる △:悪臭を若干感じる ×:悪臭を強く感じる
(Evaluation Method of Deodorizing Removal of Odor) First, the odor felt when the resin composition and the deodorant inorganic powder were kneaded and molded was evaluated organoleptically according to the following criteria. In addition, evaluations of products corresponding to the completed products were performed as follows. The resin plate obtained by mixing the deodorizing inorganic powder, kneading and molding was cut into chips of about 2 × 3 mm, and the cut resin chips (10 g) were added to 100 g of boiling water.
Boil for a minute. At that time, the odor was prevented from escaping while the lid was kept for 30 minutes, and the odor was evaluated organoleptically according to the following criteria after 30 minutes. ◎: No odor at all ○: Slight odor △: Slight odor ×: Strong odor

【0034】[0034]

【表1】 消臭性無機粉体 除去消臭評価 表面抵抗値 添加量(%) 混練・成型時 煮沸時 (Ω) 実施例1 1.0 ◎ ◎ 8×1011 実施施2 5.00 ◎ ◎ 3×1012 実施例3 10.00 ◎ ◎ 1×1013 比較例1 なし × × 5×1011 [Table 1] Deodorant inorganic powder Removal and deodorization evaluation Surface resistance value addition amount (%) During kneading / molding During boiling (Ω) Example 1 1.0 ◎ ◎ 8 × 10 11 Example 2 5.00 ◎ ◎ 3 × 10 12 Example 3 10.00 ◎ ◎ 1 × 10 13 Comparative Example 1 None × × 5 × 10 11

【0035】実施例4〜6及び比較例2 ポリプロピレン樹脂(出光石油化学(株)製、商品名
“J750H”)に、リン系の難燃剤(日本化学(株)
製、商品名“ヒシガードCP”)を7%及びアルミノ珪
酸塩(ライオン(株)製、商品名“ライオナイトS
F”)を樹脂に対して表2に示す量添加して、ラボプラ
ストミルを用いて、200℃で5分間混練した後、20
0℃、150kgfで5分間板状に成型し、性能評価を
行った。尚、悪臭の除去消臭評価は、実施例1〜3に従
って行った。結果を表2に示す。
Examples 4 to 6 and Comparative Example 2 A polypropylene resin (trade name "J750H" manufactured by Idemitsu Petrochemical Co., Ltd.) was added to a phosphorus-based flame retardant (Nippon Chemical Co., Ltd.).
7% and aluminosilicate (manufactured by Lion Corporation, trade name "Lionite S")
F ″) was added to the resin in the amount shown in Table 2, and kneaded at 200 ° C. for 5 minutes using a Labo Plastomill.
The plate was molded at 0 ° C. and 150 kgf for 5 minutes, and the performance was evaluated. The evaluation of the removal and deodorization of offensive odor was performed according to Examples 1 to 3. Table 2 shows the results.

【0036】[0036]

【表2】 消臭性無機粉体 除去消臭評価 添加量(%) 混練・成型時 煮沸時 実施例4 1.0 ○ ◎ 実施例5 5.00 ◎ ◎ 実施例6 10.00 ◎ ◎ 比較例2 なし × × [Table 2] Deodorant inorganic powder Removal deodorant evaluation addition amount (%) During kneading / molding During boiling Example 4 1.0 ○ ◎ Example 5 5.00 ◎ ◎ Example 6 10.00 ◎ ◎ Comparative Example 2 None × ×

【0037】実施例7〜9及び比較例3 ポリプロピレン樹脂(出光石油化学(株)性、商品名
“J750H”)に、水酸化マグネシウムを30%、赤
燐を10%、タルクを8%及びアルミノ珪酸塩(ライオ
ン(株)製、商品名“ライオナイトSF”)を樹脂組成
物に対して表3に示す量配合し、押出機を用いて、バレ
ル温度160〜240℃で混練した後、射出成型機を用
いて、シリンダー温度190〜210℃、金型温度50
℃で成型したサンプルを用いて同様にペレット化し、実
施例1〜3と同様に除去消臭評価を行った。結果を表3
に示す。
Examples 7 to 9 and Comparative Example 3 To a polypropylene resin (manufactured by Idemitsu Petrochemical Co., Ltd., trade name "J750H"), 30% of magnesium hydroxide, 10% of red phosphorus, 8% of talc and 8% of alumino were used. Silicate (manufactured by Lion Corporation, trade name "Lionite SF") was mixed with the resin composition in an amount shown in Table 3, kneaded using an extruder at a barrel temperature of 160 to 240 ° C, and then injected. Using a molding machine, cylinder temperature 190-210 ° C, mold temperature 50
Using a sample molded at a temperature of 0 ° C., pelletization was performed in the same manner, and removal and deodorization evaluation was performed in the same manner as in Examples 1 to 3. Table 3 shows the results
Shown in

【0038】[0038]

【表3】 消臭性無機粉体 除去消臭評価 添加量(%) 混練・成型時 煮沸時 実施例7 1.0 △ ○ 実施例8 7.00 ○ ○ 実施例9 20.00 ◎ ◎ 比較例3 なし × × [Table 3] Deodorant inorganic powder Removal / deodorization evaluation addition amount (%) During kneading / molding Boiling Example 7 1.0 △ ○ Example 8 7.00 ○ ○ Example 9 20.00 ◎ ◎ Comparative Example 3 None × ×

【0039】実施例10〜12及び比較例4 ポリプロピレン樹脂(出光石油化学(株)性、商品名
“J750H”)とポリエチレン樹脂(三菱ポリエチレ
ン(株)、商品名“HD−HY540”)との混合物
(ポリプロピレン樹脂/ポリエチレン樹脂=60/40
(重量比))にタルクを25%、モノグリセライドを
0.5%及びアルミノ珪酸塩(ライオン(株)製、商品
名“ライオナイトSF”)を樹脂組成物に対して表4に
示す量配合し、混練機を用いて、バレル温度180〜2
30℃で混練した後、押出機を用いて170〜220℃
で溶融押出し、50℃のロール上で0.3mmのシート
としたサンプルを同様にペレット化し、実施例1〜3と
同様に除去消臭評価を行った。結果を表4に示す。
Examples 10 to 12 and Comparative Example 4 A mixture of a polypropylene resin (manufactured by Idemitsu Petrochemical Co., Ltd., trade name "J750H") and a polyethylene resin (Mitsubishi Polyethylene Corp., trade name "HD-HY540") (Polypropylene resin / polyethylene resin = 60/40
(Weight ratio)), 25% of talc, 0.5% of monoglyceride and aluminosilicate (trade name “Lionite SF”, manufactured by Lion Corporation) were added to the resin composition in the amounts shown in Table 4. Using a kneader, barrel temperature 180 to 2
After kneading at 30 ° C, 170-220 ° C using an extruder
Then, a sample formed into a 0.3 mm sheet on a roll at 50 ° C. was pelletized in the same manner as above, and the removal and deodorization evaluation was performed in the same manner as in Examples 1 to 3. Table 4 shows the results.

【0040】[0040]

【表4】 消臭性無機粉体 除去消臭評価 添加量(%) 混練・成型時 煮沸時 実施例10 1.0 △ ○ 実施例11 7.00 ○ ○ 実施例12 15.00 ◎ ◎ 比較例4 なし × × [Table 4] Deodorant inorganic powder Removal / deodorization evaluation addition amount (%) During kneading / molding During boiling Example 10 1.0 △ ○ Example 11 7.00 ○ ○ Example 12 15.00 ◎ ◎ Comparative Example 4 None × ×

【0041】[0041]

【発明の効果】本発明の樹脂用添加剤を用いると、樹脂
を混練及び成型する際に発生する樹脂特有の臭気や、帯
電防止剤、酸化防止剤及び難燃剤等の添加剤から由来さ
れる臭気を、消臭性の無機粉体が吸着又は吸収すること
により悪臭が除去、消臭されるため、周辺環境が良好な
ものとなる。
When the resin additive of the present invention is used, it is derived from additives such as an antistatic agent, an antioxidant and a flame retardant, which are peculiar to the resin when the resin is kneaded and molded. Since the odor is removed or deodorized by the adsorption or absorption of the deodorant inorganic powder, the surrounding environment becomes favorable.

Claims (3)

【特許請求の範囲】[Claims] 【請求項1】 樹脂組成物の混練及び成型時に発生する
悪臭を消臭除去することができる無機粉体を主成分とし
て含有する樹脂用添加剤。
1. An additive for a resin containing, as a main component, an inorganic powder capable of deodorizing and removing a malodor generated during kneading and molding of a resin composition.
【請求項2】 無機粉体がアルミノ珪酸塩からなる無機
粉体であり、かつ、モル%で表示して本質的に以下の組
成を有する無機粉体である請求項1に記載の樹脂用添加
剤。 SiO2 :5〜80% MOn/2 :5〜65% Al23:1〜60% (式中、Mは、亜鉛、銅、銀、コバルト、ニッケル、
鉄、チタン、バリウム、スズおよびジルコニウムからな
る群より選ばれる一種以上の金属であり、nは金属Mの
モル加重平均原子価である)
2. The additive for a resin according to claim 1, wherein the inorganic powder is an inorganic powder composed of an aluminosilicate, and has essentially the following composition expressed in mol%. Agent. SiO 2: 5~80% MO n / 2: 5~65% Al 2 O 3: 1~60% ( wherein, M is zinc, copper, silver, cobalt, nickel,
Is at least one metal selected from the group consisting of iron, titanium, barium, tin and zirconium, and n is the molar weighted average valence of metal M)
【請求項3】 請求項1又は2に記載の樹脂用添加剤を
樹脂組成物に対して0.01〜30重量%添加すること
によって、樹脂組成物の混練及び成型時に発生する悪臭
を消臭除去する方法。
3. The odor generated during kneading and molding of the resin composition is eliminated by adding 0.01 to 30% by weight of the resin additive according to claim 1 or 2 to the resin composition. How to remove.
JP10099660A 1998-04-10 1998-04-10 Novel additive for resin Pending JPH11293032A (en)