JPH11288624A - Electrical insulating composition and electric wire/cable - Google Patents
Electrical insulating composition and electric wire/cableInfo
- Publication number
- JPH11288624A JPH11288624A JP9167998A JP9167998A JPH11288624A JP H11288624 A JPH11288624 A JP H11288624A JP 9167998 A JP9167998 A JP 9167998A JP 9167998 A JP9167998 A JP 9167998A JP H11288624 A JPH11288624 A JP H11288624A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- polyethylene
- parts
- cable
- ketone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は電気絶縁組成物及び
電線・ケーブルに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an electric insulating composition and electric wires and cables.
【０００２】[0002]
【従来の技術】ポリエチレン、ポリプロピレン等のポリ
オレフィンは電気的特性が優れた炭化水素系高分子材料
であることから電線・ケーブルの絶縁被覆用電気絶縁組
成物として広く実用されている。特に、ポリエチレンを
架橋したいわゆる架橋ポリエチレンはポリエチレンの欠
点である耐熱性が優れていることから高電圧電線・ケー
ブルの絶縁被覆用電気絶縁組成物として広く実用されて
いる。2. Description of the Related Art Polyolefins such as polyethylene and polypropylene are widely used as electrical insulating compositions for insulating coatings of electric wires and cables because they are hydrocarbon polymer materials having excellent electrical properties. In particular, so-called cross-linked polyethylene obtained by cross-linking polyethylene is widely used as an electrical insulating composition for insulating coating of high-voltage wires and cables because of its excellent heat resistance, which is a drawback of polyethylene.
【０００３】しかし架橋ポリエチレン被覆高電圧電線・
ケーブルは高電圧、高湿度下若しくは湿潤下、高温等の
悪条件が長年月にわたり重なって負荷されたときに被覆
架橋ポリエチレン層内にトリー状欠陥、即ち水トリーが
発生し、酷いときにはその水トリー部より電気絶縁破壊
してしまうことが分かってきている。[0003] However, high-voltage electric wires coated with cross-linked polyethylene
Trees have tree-like defects, i.e., water trees, in the coated cross-linked polyethylene layer when harsh conditions such as high voltage, high humidity or humidity, high temperature, etc. are applied over many months, and when the water trees are severe, It has been found that electrical breakdown occurs from the part.
【０００４】このような架橋ポリエチレンの水トリーは
架橋ポリエチレン層内のボイド、架橋ポリエチレン層内
に混入している微量の異物、架橋ポリエチレン層内のア
ンバ（部分的に重合度が高くなったもの、または架橋に
より部分的に高分子量化したもの）等の局所的高電界部
の欠陥部に水が凝集し、その凝集した水を介して水トリ
ーが成長するものと言われている。[0004] The water tree of such cross-linked polyethylene is composed of voids in the cross-linked polyethylene layer, a small amount of foreign matter mixed in the cross-linked polyethylene layer, and amber in the cross-linked polyethylene layer (one having a high degree of polymerization, It is said that water aggregates at a defective portion of a local high electric field portion such as a partially high molecular weight by cross-linking, and the water tree grows through the aggregated water.
【０００５】なお、架橋ポリエチレン被覆高電圧電線・
ケーブルを水分が関与しない条件下で電気絶縁破壊し、
その電気絶縁破壊箇所について調べてみるとその絶縁破
壊の起点箇所は架橋ポリエチレン層内に混入している微
量の異物、架橋ポリエチレン層内のアンバ等であること
が分かってきている。[0005] It should be noted that high-voltage electric wires with cross-linked polyethylene
Electrical breakdown of the cable under conditions where moisture does not participate,
Examination of the electrical breakdown point shows that the starting point of the dielectric breakdown is a minute amount of foreign matter mixed in the cross-linked polyethylene layer, an amber in the cross-linked polyethylene layer, or the like.
【０００６】このようなことから電線・ケーブルメーカ
ーではこれらの欠陥部の発生を抑止するため原料ポリエ
チレンの品質管理、電線・ケーブルの製造技術等の改善
を積み重ね、その結果水トリーの発生を低減できるよう
になってきている。Accordingly, in order to suppress the occurrence of these defective portions, wire / cable manufacturers continuously improve the quality control of the raw material polyethylene and the technology for manufacturing the wires / cables, and as a result, the occurrence of water trees can be reduced. It is becoming.
【０００７】しかしながら従来の水トリーの発生を低減
した架橋ポリエチレン絶縁被覆電線・ケーブルの電気絶
縁組成物では高温下の電気絶縁破壊電圧が低下したり、
誘電正接が大きくなったりするという難点があった。However, the conventional electric insulating composition of a crosslinked polyethylene insulated wire or cable which has reduced the generation of water trees has a low electric breakdown voltage at high temperatures,
There was a disadvantage that the dielectric loss tangent increased.
【０００８】[0008]
【発明が解決しようとする課題】本発明はかかる点に立
って為されたものであって、その目的とするところは前
記した従来技術の欠点を解消し、水トリーの発生が少な
く且つ高温下の電気絶縁破壊電圧が高く、しかも誘電正
接が小さいという優れた諸特性を有する電気絶縁組成物
及び電線・ケーブルを提供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of such a point, and an object of the present invention is to solve the above-mentioned disadvantages of the prior art, to reduce the occurrence of water trees and to reduce the temperature under high temperatures. It is an object of the present invention to provide an electric insulating composition and an electric wire / cable having excellent characteristics such as a high electric breakdown voltage and a small dielectric loss tangent.
【０００９】[0009]
【課題を解決するための手段】本発明の要旨とするとこ
ろは次の２点にある。The gist of the present invention lies in the following two points.
【００１０】（１）ポリエチレン若しくはエチレン共重
合体の１００重量部に対して、分子中にフェニル基とケ
トン結合とを有するアルキルフェニルケトンを０．０２
〜５０．０重量部配合して成ることを特徴とする電気絶
縁組成物及びそれを被覆して成る電線・ケーブル。(1) An alkyl phenyl ketone having a phenyl group and a ketone bond in a molecule of 0.02 to 100 parts by weight of polyethylene or an ethylene copolymer is used.
An electric insulating composition characterized by being blended in an amount of up to 50.0 parts by weight, and an electric wire / cable coated with the same.
【００１１】（２）ポリエチレン若しくはエチレン共重
合体の１００重量部に対して、分子中にフェニル基とケ
トン結合とを有するアルキルフェニルケトンとα−芳香
族置換α−メチルアルケンの不飽和二量体とを配合して
成ることを特徴とする電気絶縁組成物及びそれを被覆し
て成る電線・ケーブル。(2) With respect to 100 parts by weight of polyethylene or ethylene copolymer, unsaturated dimer of alkylphenyl ketone having a phenyl group and a ketone bond in the molecule and α-aromatic substituted α-methylalkene And an electric insulating composition, and an electric wire / cable coated with the same.
【００１２】[0012]
【発明の実施の形態】次に、本発明の電気絶縁組成物及
び電線・ケーブルの実施の形態について説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS Next, embodiments of the electric insulating composition and the electric wires / cables of the present invention will be described.
【００１３】本発明においてポリエチレン又はエチレン
共重合体とは工業的に実用されているものを用いること
ができる。In the present invention, the polyethylene or the ethylene copolymer may be those industrially practical.
【００１４】ここにおいてポリエチレンとしては低密度
ポリエチレン、直鎖状低密度ポリエチレン、中密度ポリ
エチレン、高密度ポリエチレン等がある。また、エチレ
ン共重合体としてはエチレン−プロピレン共重合体、エ
チレン−エチルアクリレート共重合体、エチレン−酢酸
ビニル共重合体、エチレン−スチレン共重合体等があ
る。また、本発明においてポリエチレン又はエチレン共
重合体としてはこれらに無水マレイン酸、ビニルシラン
等をグフフトしたものであってもよい。更に、これらの
２種以上を併用してもよく、その上これらの単独又は２
種以上のものに酸化防止剤、滑剤、着色剤等の他の配合
剤を添加しても差し支えない。Here, polyethylene includes low density polyethylene, linear low density polyethylene, medium density polyethylene, high density polyethylene and the like. In addition, examples of the ethylene copolymer include an ethylene-propylene copolymer, an ethylene-ethyl acrylate copolymer, an ethylene-vinyl acetate copolymer, and an ethylene-styrene copolymer. In the present invention, as the polyethylene or ethylene copolymer, those obtained by grafting maleic anhydride, vinylsilane, or the like thereto may be used. Further, two or more of these may be used in combination, and furthermore, these may be used alone or in combination.
Other compounding agents such as antioxidants, lubricants, coloring agents, etc. may be added to more than one kind.
【００１５】本発明において用いられる分子中にフェニ
ル基とケトン結合とを有するアルキルフェニルケトンと
してはｎ−オクタノフェノン、ｎ−デカノフェノン、ラ
ウロフェノン、ｎ−テトラデカノフェノン、ｎ−ヘキサ
デカノフェノン、ｎ−ヘプタデカノフェノン、ｎ−オプ
タデカノフェノン、４′−ｎ−オクチルアセトフェノ
ン、４−ｎ−オクタノイルビフェニル、１，９−ジフェ
ニル−１，３，６，８−ノナテトラエン−５−オン、２
−イソプロポキシ−１，２−ジフェニルエタン等があ
る。これらは単独又は２種以上を適宜併用して使用する
ことができる。The alkylphenyl ketone having a phenyl group and a ketone bond in the molecule used in the present invention includes n-octanophenone, n-decanophenone, laurophenone, n-tetradecanophenone and n-hexadecanophenone. N-heptadecanophenone, n-optadedecanophenone, 4'-n-octylacetophenone, 4-n-octanoylbiphenyl, 1,9-diphenyl-1,3,6,8-nonatetraen-5-one , 2
-Isopropoxy-1,2-diphenylethane and the like. These can be used alone or in combination of two or more.
【００１６】本発明においてポリエチレン又はエチレン
共重合体１００重量部に対して、アルキルフェニルケト
ンの配合量を０．０２〜５０．０重量部に限定したのは
０．０２重量部以下では電界緩和効果及びボウタイトリ
ー低減効果が乏しく、逆に５０．０重量部以上では電気
的特性が急激に悪化するからである。In the present invention, the amount of the alkyl phenyl ketone is limited to 0.02 to 50.0 parts by weight per 100 parts by weight of polyethylene or ethylene copolymer. This is because the effect of reducing the bow titley is poor, and conversely, if the content is 50.0 parts by weight or more, the electrical characteristics rapidly deteriorate.
【００１７】また、α−芳香族置換α−メチルアルケン
の不飽和二量体の配合量が０．０５重量部以下ではスコ
ーチ抑止効果が小さく、逆に０．０５重量部以上では電
気特性が急激に悪化するからである。When the amount of the unsaturated dimer of α-aromatic substituted α-methylalkene is less than 0.05 part by weight, the effect of suppressing scorch is small, and when it is more than 0.05 part by weight, the electrical characteristics are sharp. This is because it becomes worse.
【００１８】本発明の電気絶縁組成物は電線・ケーブル
に被覆してから架橋することが望ましい。It is preferable that the electric insulating composition of the present invention is crosslinked after covering the electric wire / cable.
【００１９】電気絶縁組成物の架橋手段としては過酸化
物架橋剤による架橋、シラン架橋剤による水架橋、電子
線照射による照射架橋等がある。The means for crosslinking the electrically insulating composition includes crosslinking with a peroxide crosslinking agent, water crosslinking with a silane crosslinking agent, irradiation crosslinking by electron beam irradiation, and the like.
【００２０】ここにおいて過酸化物架橋剤としてはジク
ミルパーオキサイド、１−（２−ｔｅｒｔ−ブチルパー
オキシイソプロピル）−１−イソプロピルベンゼン又は
１−（２−ｔｅｒｔ−ブチルパーオキシイソプロピル）
−３−イソプロピルベンゼン、１，３−ビス−（ｔｅｒ
ｔ−ブチルパーオキシイソプロピル）ベンゼン、２，５
−ジ（ｔｅｒｔ−ブチルパーオキシ）ヘキサン、２，５
−ジメチル−２，５（ｔｅｒｔ−ブチルパーオキシ）−
ヘキシン−３等がある。これらは単独又は２種以上を適
宜併用して使用することができる。Here, the peroxide crosslinking agent is dicumyl peroxide, 1- (2-tert-butylperoxyisopropyl) -1-isopropylbenzene or 1- (2-tert-butylperoxyisopropyl).
-3-isopropylbenzene, 1,3-bis- (ter
t-butylperoxyisopropyl) benzene, 2.5
-Di (tert-butylperoxy) hexane, 2,5
-Dimethyl-2,5 (tert-butylperoxy)-
Hexin-3 and the like. These can be used alone or in combination of two or more.
【００２１】また、これらの架橋剤はα−芳香族置換α
−メチルアルケンの不飽和二量体と併用するとスコーチ
しにくくすることができる。These crosslinking agents are α-aromatic substituted α
When used in combination with an unsaturated dimer of -methyl alkene, scorch can be suppressed.
【００２２】このようなα−芳香族置換α−メチルアル
ケンとしてはα−メチルスチレン、パラ−メチル−α−
メチルスチレン、パラ−イソプロピル−α−メチルスチ
レン、メタ−メチル−α−メチルスチレン、メタ−エチ
ル−α−メチルスチレン、ａｒ−ジメチル−α−メチル
スチレン、ａｒ−クロル−α−メチルスチレン、ａｒ−
クロル−ａｒ−メチル−α−メチルスチレン、ａｒ−ジ
エチル−α−メチルスチレン、ａｒ−メチル−ａｒ−イ
ソプロピル−α−メチルスチレン等がある。Such α-aromatic substituted α-methylalkenes include α-methylstyrene and para-methyl-α-
Methylstyrene, para-isopropyl-α-methylstyrene, meta-methyl-α-methylstyrene, meta-ethyl-α-methylstyrene, ar-dimethyl-α-methylstyrene, ar-chloro-α-methylstyrene, ar-
Chlor-ar-methyl-α-methylstyrene, ar-diethyl-α-methylstyrene, ar-methyl-ar-isopropyl-α-methylstyrene and the like.
【００２３】また、このようなα−芳香族置換α−メチ
ルアルケンの不飽和二量体の具体例としては、例えばα
−メチルスチレンの不飽和二量体である２、４−ジフェ
ニル−４−メチル−１−ペンテン等がある。Specific examples of such unsaturated dimers of α-aromatic substituted α-methylalkene include, for example, α
And 2,4-diphenyl-4-methyl-1-pentene which is an unsaturated dimer of methylstyrene.
【００２４】本発明においてはこれらの配合剤に加えて
他の配合剤、例えば酸化防止剤、滑剤、着色剤、充填剤
等を配合することができる。In the present invention, in addition to these additives, other additives such as antioxidants, lubricants, coloring agents, fillers and the like can be added.
【００２５】[0025]
【実施例】次に、本発明の電気絶縁組成物及び電線・ケ
ーブルの実施例を従来の比較例と共に説明する。EXAMPLES Next, examples of the electric insulating composition and electric wires / cables of the present invention will be described together with conventional comparative examples.
【００２６】（１）電気絶縁組成物の秤量、採取 まず、表１の上欄に示す成分表に従って実施例及び比較
例の電気絶縁組成物をそれぞれ秤量、採取した。(1) Weighing and Sampling of Electrical Insulating Composition First, the electrical insulating compositions of Examples and Comparative Examples were weighed and collected according to the component table shown in the upper column of Table 1.
【００２７】（２）電気絶縁組成物のペレット作成 上記（１）で秤量、採取した実施例及び比較例の電気絶
縁組成物をそれぞれ熱混練ロールで混練し、それからシ
ートを作成した。(2) Preparation of pellets of electrical insulating composition The electrical insulating compositions of Examples and Comparative Examples weighed and collected in the above (1) were kneaded with hot kneading rolls, respectively, to form sheets.
【００２８】次に、得られた実施例及び比較例の電気絶
縁組成物のシートをそれぞれペレタイザーにかけ、電気
絶縁組成物のペレット物とした。Next, the obtained sheets of the electrical insulating composition of the example and the comparative example were each subjected to a pelletizer to obtain pellets of the electrical insulating composition.
【００２９】（３）架橋ポリエチレン絶縁電線の製造 次に、押出機により導体断面積１００mm2 の軟銅線撚線
の直上に０．７mm厚さの内部半導電層、その内部半導電
層上に上記（２）で得た実施例及び比較例の電気絶縁組
成物のペレット物、更にその電気絶縁組成物層の上に
０．７mm厚さの外部半導電層を１工程で押し出し被覆す
ることによりポリエチレン絶縁ケーブルを得た。(3) Manufacture of cross-linked polyethylene insulated wire Next, an extruder is used to form an inner semiconductive layer having a thickness of 0.7 mm directly on a soft copper wire having a conductor cross section of 100 mm 2 , and the above semiconductive layer is formed on the inner semiconductive layer. The polyethylene is obtained by extruding and coating in a single step a 0.7 mm-thick external semiconductive layer on the pellets of the electrical insulating compositions of the examples and comparative examples obtained in (2), and further on the electrical insulating composition layers. An insulated cable was obtained.
【００３０】次に、得られた実施例及び比較例のポリエ
チレン絶縁ケーブルを高温の窒素ガス雰囲気下の乾式架
橋管内を通過させることによりポリエチレン絶縁層を架
橋させ、実施例及び比較例の架橋ポリエチレン絶縁ケー
ブルを得た。Next, the polyethylene insulated cables of Examples and Comparative Examples were passed through a dry cross-linking tube under a high-temperature nitrogen gas atmosphere to cross-link the polyethylene insulated layer. Got the cable.
【００３１】図１はかくして得られた実施例１の架橋ポ
リエチレン絶縁ケーブルの断面図を示したものであって
１は導体、２は内部半導電層、３は架橋ポリエチレン絶
縁層、４は外部半導電層である。FIG. 1 shows a cross-sectional view of the crosslinked polyethylene insulated cable of Example 1 thus obtained, wherein 1 is a conductor, 2 is an inner semiconductive layer, 3 is a crosslinked polyethylene insulating layer, and 4 is an outer half. It is a conductive layer.
【００３２】（４）架橋ポリエチレン絶縁ケーブルの評
価試験ａ．高温下の交流絶縁破壊電圧の測定 実施例及び比較例の架橋ポリエチレン絶縁ケーブルをそ
れぞれ温度９０℃に加熱下でまず交流電圧を１７０ｋｖ
で１０分印加し、それから５ｋｖ／１０分の昇圧速度で
段階的に昇圧印加し、その電気絶縁破壊電圧を測定し
た。(4) Evaluation test of crosslinked polyethylene insulated cable a. Measurement of AC Breakdown Voltage at High Temperature First, the cross-linked polyethylene insulated cables of Examples and Comparative Examples were heated to a temperature of 90 ° C., and the AC voltage was first increased to 170 kV.
For 10 minutes, and then stepwisely increased the voltage at a rate of 5 kv / 10 minutes to measure the electric breakdown voltage.
【００３３】ｂ．ボウタイトリー試験 まず、実施例及び比較例の架橋ポリエチレン絶縁ケーブ
ルをそれぞれ温度９０℃の温水中に浸漬しすると共に導
体と水との間に５０Ｈｚ、９ｋｖの交流電圧を印加し、
その状態で５００日おいた。 B. Bow Titlery Test First, the crosslinked polyethylene insulated cables of the Examples and Comparative Examples were each immersed in warm water at a temperature of 90 ° C., and an AC voltage of 50 Hz, 9 kv was applied between the conductor and the water,
500 days in that state.
【００３４】次に、５００日終了後実施例及び比較例の
架橋ポリエチレン絶縁ケーブルをそれぞれ断面スライス
した。Next, after 500 days, the cross-linked polyethylene insulated cables of Examples and Comparative Examples were sliced in cross section.
【００３５】次に、得られた架橋ポリエチレン絶縁層ス
ライス物をメチレンブルー水溶液に浸漬し、それから煮
沸染色処理した。Next, the obtained crosslinked polyethylene insulating layer slice was immersed in an aqueous methylene blue solution, and then subjected to boiling dyeing treatment.
【００３６】次に、このように染色処理した架橋ポリエ
チレン絶縁層スライス物を光学顕微鏡で観察し、ボウタ
イトリーの累積発生個数を計数した。Next, the crosslinked polyethylene insulating layer slice thus dyed was observed with an optical microscope, and the cumulative number of bow title trees was counted.
【００３７】ｃ．誘電正接の測定 実施例及び比較例の架橋ポリエチレン絶縁ケーブルにつ
いてそれぞれ電界１０ｋｖ／mm下での誘電正接を測定し
た。[0037] c. Measurement of dielectric loss tangent The dielectric loss tangent of each of the crosslinked polyethylene insulated cables of Examples and Comparative Examples was measured under an electric field of 10 kv / mm.
【００３８】結果は誘電正接の値が０．０５％以下のも
のを○、０．０５％以上のものを×で表示した。The results are indicated by ○ when the dielectric loss tangent is 0.05% or less, and by X when the value is 0.05% or more.
【００３９】（５）試験結果 試験結果は表１の下欄に示す通りである。(5) Test Results The test results are as shown in the lower column of Table 1.
【００４０】[0040]
【表１】 [Table 1]
【００４１】（６）試験結果の評価 比較例１の架橋ポリエチレン絶縁ケーブルはボウタイト
リーの累積発生個数が最も多く、耐トリー性が最も悪
い。(6) Evaluation of Test Results The crosslinked polyethylene insulated cable of Comparative Example 1 has the largest number of bow title trees and the worst tree resistance.
【００４２】比較例２の架橋ポリエチレン絶縁ケーブル
はボウタイトリーの累積発生個数が少なく、耐トリー性
が良好である。しかし比較例２の架橋ポリエチレン絶縁
ケーブルは高温下の交流絶縁破壊電圧が低く、その上誘
電正接も悪い×評価であった。The crosslinked polyethylene insulated cable of Comparative Example 2 has a small number of bow title trees and a good tree resistance. However, the crosslinked polyethylene insulated cable of Comparative Example 2 had a low AC breakdown voltage at high temperatures and a poor dielectric loss tangent.
【００４３】これらに対して実施例１〜５の架橋ポリエ
チレン絶縁ケーブルはボウタイトリーの累積発生個数が
少なく、耐トリー性が良好で且つ高温下の交流絶縁破壊
電圧が高く、しかも誘電正接も○評価といずれも優れた
結果を示した。On the other hand, the crosslinked polyethylene insulated cables of Examples 1 to 5 have a small number of bow title trees, good tree resistance, high AC breakdown voltage at high temperature, and a dielectric loss tangent of ○. And all showed excellent results.
【００４４】[0044]
【発明の効果】本発明の電気絶縁組成物及び電線・ケー
ブルは耐トリー性が良好で且つ高温下の交流絶縁破壊電
圧が高く、しかも上誘電正接も小さくという優れたもの
であり、工業上有用である。Industrial Applicability The electrical insulating composition and electric wires and cables of the present invention have excellent tree resistance, high AC breakdown voltage at high temperatures, and a small dielectric loss tangent, and are industrially useful. It is.
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明の実施例１の架橋ポリエチレン絶縁ケー
ブルの断面図を示したものである。FIG. 1 is a cross-sectional view of a crosslinked polyethylene insulated cable according to a first embodiment of the present invention.
１ 導体 ２ 内部半導電層 ３ 架橋ポリエチレン絶縁層 ４ 外部半導電層 Reference Signs List 1 conductor 2 inner semiconductive layer 3 crosslinked polyethylene insulating layer 4 outer semiconductive layer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｃ０９Ｄ 5/25 Ｃ０９Ｄ 5/25 Ｈ０１Ｂ 9/02 Ｈ０１Ｂ 9/02 Ａ (72)発明者 奥山 健 茨城県日立市日高町５丁目１番１号 日立 電線株式会社パワーシステム研究所内────────────────────────────────────────────────── ─── Continued on the front page (51) Int.Cl. 6 Identification symbol FI C09D 5/25 C09D 5/25 H01B 9/02 H01B 9/02 A (72) Inventor Ken Okuyama 5 Hidakacho, Hitachi City, Ibaraki Prefecture Chome 1-1 Hitachi Power Systems Co., Ltd. Power System Laboratory
Claims (5)
１００重量部に対して、分子中にフェニル基とケトン結
合とを有するアルキルフェニルケトンを０．０２〜５
０．０重量部配合して成ることを特徴とする電気絶縁組
成物。1. An alkyl phenyl ketone having a phenyl group and a ketone bond in a molecule of 0.02 to 5 parts by weight per 100 parts by weight of polyethylene or ethylene copolymer.
An electrical insulating composition comprising 0.0 parts by weight.
フェノン、ｎ−デカノフェノン、ラウロフェノン、ｎ−
テトラデカノフェノン、ｎ−ヘキサデカノフェノン、ｎ
−ヘプタデカノフェノン、ｎ−オプタデカノフェノン、
４′−ｎ−オクチルアセトフェノン、４−ｎ−オクタノ
イルビフェニル、１，９−ジフェニル−１，３，６，８
−ノナテトラエン−５−オン、２−イソプロポキシ−
１，２−ジフェニルエタンの中から選ばれた１種２種以
上の混合物であることを特徴とする請求項１記載の電気
絶縁組成物。2. The method according to claim 1, wherein the alkylphenyl ketone is n-octanophenone, n-decanophenone, laurophenone, n-octanophenone.
Tetradecanophenone, n-hexadecanophenone, n
-Heptadecanophenone, n-optadecanophenone,
4'-n-octyl acetophenone, 4-n-octanoylbiphenyl, 1,9-diphenyl-1,3,6,8
-Nonatetraen-5-one, 2-isopropoxy-
2. The electrical insulating composition according to claim 1, wherein the composition is a mixture of at least one selected from 1,2-diphenylethane.
１００重量部に対して、分子中にフェニル基とケトン結
合とを有するアルキルフェニルケトンとα−芳香族置換
α−メチルアルケンの不飽和二量体とを配合して成るこ
とを特徴とする電気絶縁組成物。3. An unsaturated dimer of an alkyl phenyl ketone having a phenyl group and a ketone bond in the molecule and an α-aromatic substituted α-methyl alkene, based on 100 parts by weight of polyethylene or ethylene copolymer. An electrical insulating composition characterized by comprising:
縁層を被覆して成る電線・ケーブルにおいて、前記絶縁
層はポリエチレン若しくはエチレン共重合体の１００重
量部に対して分子中にフェニル基とケトン結合とを有す
るアルキルフェニルケトンを０．０２〜５０．０重量部
配合した電気絶縁組成物から成ることを特徴とする電線
・ケーブル。4. An electric wire or cable in which an insulating layer is coated directly above a conductor or via a semiconductive layer, wherein the insulating layer is a phenyl group in a molecule with respect to 100 parts by weight of polyethylene or ethylene copolymer. A wire or cable comprising an electrical insulating composition containing 0.02 to 50.0 parts by weight of an alkylphenyl ketone having a ketone bond.
縁層を被覆して成る電線・ケーブルにおいて、前記絶縁
層はポリエチレン若しくはエチレン共重合体の１００重
量部に対して分子中にフェニル基とケトン結合とを有す
るアルキルフェニルケトンとα−芳香族置換α−メチル
アルケンの不飽和二量体とを配合した電気絶縁組成物か
ら成ることを特徴とする電線・ケーブル。5. An electric wire or cable comprising an insulating layer coated directly on a conductor or via a semiconductive layer, wherein the insulating layer is a phenyl group in a molecule with respect to 100 parts by weight of polyethylene or ethylene copolymer. A wire or cable comprising an electrical insulating composition containing an alkyl phenyl ketone having an alkylphenyl ketone and a unsaturated dimer of α-aromatic substituted α-methylalkene.