JPH11276219A - Light emitting ornament - Google Patents
Light emitting ornamentInfo
- Publication number
- JPH11276219A JPH11276219A JP9843198A JP9843198A JPH11276219A JP H11276219 A JPH11276219 A JP H11276219A JP 9843198 A JP9843198 A JP 9843198A JP 9843198 A JP9843198 A JP 9843198A JP H11276219 A JPH11276219 A JP H11276219A
- Authority
- JP
- Japan
- Prior art keywords
- luminous
- stone
- light emitting
- sintered body
- phosphorescent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、残光性発光材料か
らなる焼結体である蓄光発光石を用いた装飾品に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative article using a phosphorescent luminous stone, which is a sintered body made of an afterglow luminescent material.
【０００２】[0002]
【従来の技術】従来から指輪やネックレス等の装身具に
は、天然の宝石類が愛用されているが、近年、天然宝石
を人工的に製造する技術が開発され、サファイアを始
め、トパーズ、ジルコン、ダイヤモンド等数多くの人造
宝石が合成されるようになった。これらの人造宝石の中
には、高屈折率を有し、且つ天然宝石と同じような硬
度、表面光沢を持つものもある。2. Description of the Related Art Natural jewelry has been used habitually for jewelry such as rings and necklaces. In recent years, techniques for artificially producing natural jewelry have been developed, and sapphire, topaz, zircon, Many artificial jewels such as diamonds have come to be synthesized. Some of these artificial jewels have a high refractive index and hardness and surface gloss similar to natural jewels.
【０００３】上記天然の宝石類には、螢石（フッ化カル
シウムでできた立方結晶体）に見られるように、紫外線
を吸収することで発光するものもあり、また、人造宝石
にしても研磨加工することで表面光沢を出して耀きを増
すことが可能である。[0003] Some of the above natural jewels emit light by absorbing ultraviolet rays, as seen in fluorite (cubic crystals made of calcium fluoride). By processing, it is possible to increase the brightness by giving a surface gloss.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、上記天
然宝石や人造宝石は、自然発光性を有していないため、
周囲の暗いところでは輝きが失われて装飾性を高めるこ
とができなかった。また、前記天然宝石・人造宝石と
も、紫外線を継続的に照射することで僅かながらも発光
及び残光現象が現れていたが、紫外線のないところでは
ほとんど現れない。このため、紫外線照射源を持つこと
のできない身飾り装飾品には不向きであった。However, since the above natural gems and artificial gems do not have natural luminescence,
The brightness was lost in the surrounding dark places, and the decorativeness could not be enhanced. Further, in both the natural jewels and the artificial jewels, the light emission and the afterglow phenomenon have appeared to a small extent due to the continuous irradiation of ultraviolet rays, but they hardly appear in places without ultraviolet rays. For this reason, it is not suitable for ornaments that cannot have an ultraviolet irradiation source.
【０００５】そこで、本発明の目的は、高輝度、長残光
特性を有した蓄光発光石を用い、さらに、これを加工・
研磨することで高級感を出させた発光装飾品を提供する
ことにある。Accordingly, an object of the present invention is to use a phosphorescent luminous stone having high luminance and long afterglow characteristics,
It is an object of the present invention to provide a luminous decorative article that has a high-quality appearance by polishing.
【０００６】[0006]
【課題を解決するための手段】上記課題を解決するため
に、本発明の請求項１に係る発光装飾品は、残光性発光
材料からなる焼結体であって、該焼結体の特性がモース
硬度６〜８、比重６〜８、発光波長４４０ｎｍ〜７００
ｎｍを有する蓄光発光石を加工・研磨し、装飾品とした
ことを特徴とする。According to a first aspect of the present invention, there is provided a luminous decorative article which is a sintered body made of an afterglow luminescent material. Has a Mohs hardness of 6 to 8, a specific gravity of 6 to 8, and an emission wavelength of 440 nm to 700.
It is characterized by processing and polishing phosphorescent luminous stones having nm to obtain decorative articles.
【０００７】また、本発明の請求項２に係る発光装飾品
は、加工・研磨した蓄光発光石の表面に光透過性の有色
被膜を形成したことを特徴とする。The luminous decorative article according to claim 2 of the present invention is characterized in that a light-transmitting colored film is formed on the surface of the processed and polished luminous luminous stone.
【０００８】また、本発明の請求項３に係る発光装飾品
は、加工・研磨した蓄光発光石を貴石の周辺に配したこ
とを特徴とする。A luminous decorative article according to a third aspect of the present invention is characterized in that the processed and polished luminous luminous stone is arranged around the precious stone.
【０００９】また、本発明の請求項４に係る発光装飾品
は、発光色が異なる少なくとも２種類の蓄光発光石を貴
石の周辺に配したことを特徴とする。A luminous decorative article according to a fourth aspect of the present invention is characterized in that at least two kinds of luminous luminous stones having different luminescent colors are arranged around the precious stone.
【００１０】また、本発明の請求項５に係る発光装飾品
は、加工・研磨した蓄光発光石を貴石と一体形成したこ
とを特徴とする。A luminous decorative article according to claim 5 of the present invention is characterized in that the processed and polished luminous luminous stone is formed integrally with the precious stone.
【００１１】また、本発明の請求項６に係る発光装飾品
は、発光色が異なる少なくとも２種類の蓄光発光石を貴
石と一体形成したことを特徴とする。[0011] The luminous ornament according to claim 6 of the present invention is characterized in that at least two kinds of luminous luminous stones having different luminescent colors are formed integrally with precious stone.
【００１２】また、本発明の請求項７に係る発光装飾品
は、加工・研磨してできた蓄光発光石の表層部に発生す
る微小空隙に、有色塗料を埋め込んで形成したことを特
徴とする。A luminous decorative article according to a seventh aspect of the present invention is characterized in that a colored paint is buried in minute voids generated in a surface layer of a phosphorescent luminous stone formed by processing and polishing. .
【００１３】[0013]
【発明の実施の形態】以下、添付図面に基づいて、本発
明に係る発光装飾品の実施の形態を説明する。この発光
装飾体は、発光体として人工的に造られた発光石（以
下、蓄光発光石という）を使用するものである。この蓄
光発光石は、太陽光や蛍光灯、熱、衝撃等、特に紫外線
で励起して結晶体そのものが有するエネルギーを可視光
として徐々に放出しながら、長時間発光し続ける焼結体
である。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a perspective view of a luminous ornament according to the present invention. This luminous decorative body uses a luminous stone artificially made as a luminous body (hereinafter referred to as a phosphorescent luminous stone). The luminous luminous stone is a sintered body that emits light for a long time while gradually emitting the energy of the crystal itself as visible light when excited by ultraviolet rays, such as sunlight, fluorescent lamps, heat, and shock.
【００１４】このような蓄光発光石は、残光性発光材料
からなる焼結体であって、該焼結体の特性がモース硬度
６〜８、比重６〜８、発光波長４４０ｎｍ〜７００ｎｍ
を有するもので、更にこの焼結体は大きな塊で得られる
ものであり、この大塊焼結体を加工研磨することにより
光沢のある発光石が得られる。Such a phosphorescent luminous stone is a sintered body made of an afterglow luminescent material, and the characteristics of the sintered body are a Mohs' hardness of 6 to 8, a specific gravity of 6 to 8, and an emission wavelength of 440 to 700 nm.
Further, this sintered body is obtained in a large lump, and a glossy luminous stone can be obtained by processing and polishing the large lump sintered body.
【００１５】上記残光性発光材料は、 一般式 （ＭＥｕ）Ａｌ2Ｏ4・(ＭＥｕ)Ｏ・ｎ(Ａｌ1
-a-b Ｂb Ｑa)2Ｏ4 〔式中、ａは０．０００５〜０．００２であり、ｂは
０．００１〜０．３５であり、ｎは１〜７である。Ｍは
Ｓｒ、Ｃａ及びＭｇから選ばれた少なくとも一種類であ
り、更にＱは、Ｄｙ，Ｙ，Ｎｄ，Ｃｅ，Ｇｄ，Ｔｂ，Ｈ
ｏ，Ｅｒ，Ｍｎ，Ｂｉ，Ｐｔ，Ｔｍ，Ｙｂ，Ｌａ及びＳ
ｍから選択される少なくとも１つである。〕で表される
ことを特徴とし、これから得られた蓄光発光石は高輝度
かつ長残光性を有し、高硬度、高比重で、各種の発光色
に発光する優れた人造宝石が得られる。特に焼結体の発
光色が、４００ｎｍ〜７００ｎｍのスペクトル色であ
り、残光時間も２０時間を有するものである。The afterglow light-emitting material has a general formula (MEu) Al2O4. (MEu) On (Al1
-ab Bb Qa) 2 O4 wherein a is 0.0005 to 0.002, b is 0.001 to 0.35, and n is 1 to 7. M is at least one selected from Sr, Ca and Mg, and Q is Dy, Y, Nd, Ce, Gd, Tb, H
o, Er, Mn, Bi, Pt, Tm, Yb, La and S
m is at least one selected from m. The phosphorescent luminous stone obtained from this has high luminance and long afterglow, high hardness, high specific gravity, and excellent artificial jewels that emit light of various colors can be obtained. . In particular, the emission color of the sintered body is a spectrum color of 400 nm to 700 nm, and the afterglow time also has 20 hours.
【００１６】この蓄光発光石の製造方法は、（ａ）粉枠
されている残光性発光材料を容器に充填した後、圧力の
調整ができる焼成炉に載置し、５〜８時間かけて炉内温
度を室温から１５５０℃〜１７００℃に昇温する工程、
（ｂ）この温度で２時聞〜５時間焼成して焼結体を形成
する工程、（ｃ）得られた焼結体を８時間〜１０時間か
けて室温まで冷却する工程からなることを特徴とするも
ので、この製造方法により高硬度かつ高比重で、また高
輝度かつ長残光性が保持された大塊焼結体が得られる。
なお、上記昇温工程において、１５００℃未満では焼成
が不十分で気泡等が混入し良好な品質の焼結体が得られ
ない。また、１７００℃を越えると脆くなり好ましくな
い。The method for producing this phosphorescent luminous stone is as follows: (a) After filling a container with the powdered afterglow luminescent material, the container is placed in a firing furnace whose pressure can be adjusted, and it takes 5 to 8 hours. Raising the furnace temperature from room temperature to 1550 ° C. to 1700 ° C.,
(B) baking at this temperature for 2 to 5 hours to form a sintered body, and (c) cooling the obtained sintered body to room temperature over 8 to 10 hours. According to this production method, a large-sized sintered body having high hardness, high specific gravity, high luminance and long afterglow can be obtained.
In the above temperature raising step, if the temperature is lower than 1500 ° C., sintering is insufficient and bubbles and the like are mixed in, and a sintered body of good quality cannot be obtained. On the other hand, if it exceeds 1700 ° C., it becomes brittle, which is not preferable.
【００１７】この蓄光発光石の製造方法において、冷却
工程の後、得られた焼結体を加工研磨することにより各
種の工芸品乃至装飾品が得られる。また本実施例におい
て、焼成炉内の雰囲気を還元雰囲気にすること、更にこ
の還元雰囲気を炭素を使用して造ることにより高輝度、
長残光性の優れた大塊焼結体が得られる。更に本実施例
の蓄光発光石の製造方法では、圧力が１．０２０ｋｇｆ
／ｃｍ2（１気圧）〜８．１６０ｋｇｆ／ｃｍ2（８気
圧）下で、好ましくは２．０４０ｋｇｆ／ｃｍ2（２気
圧）〜４．０８０ｋｇｆ／ｃｍ2（４気圧）下で焼結す
ることにより高硬度、高比重の大塊焼結体が効率的に得
られる。このような加圧焼結法のうち、熱間静水加圧法
〔ＨｌＰ〕を用いてもよい。また前記圧力が高い方が緻
密組織のものが得られる点で好ましいが、圧力が８．１
６０ｋｇｆ／ｃｍ2を越えると経済的にコストがかか
る。経済性を考慮すると４．０８０ｋｇｆ／ｃｍ2まで
がよい。更に圧力が１．０２０ｋｇｆ／ｃｍ2未満で
は、気泡の混入等が起こり品質的に好ましくない。更に
また温度の上昇及び降下が速過ぎると製品に亀裂が入る
等により大きな塊が得られない。In the method for producing a luminous luminous stone, after the cooling step, the obtained sintered body is processed and polished to obtain various crafts and ornaments. Further, in this embodiment, the atmosphere in the firing furnace is set to a reducing atmosphere, and furthermore, the reducing atmosphere is formed by using carbon, so that high brightness,
A large sinter having excellent long afterglow is obtained. Further, in the method for manufacturing the luminous luminous stone of the present embodiment, the pressure is 1.020 kgf.
Sintering at a pressure of from 2 / cm 2 (1 atm) to 8.160 kgf / cm 2 (8 atm), preferably from 2.040 kgf / cm 2 (2 atm) to 4.080 kgf / cm 2 (4 atm), A large sinter having a high specific gravity can be obtained efficiently. Among such pressure sintering methods, a hot isostatic pressing method [HIP] may be used. A higher pressure is preferred in that a dense structure can be obtained, but the pressure is 8.1.
If it exceeds 60 kgf / cm 2, it costs economically. Considering economy, it is better to use 4.080 kgf / cm2. Further, if the pressure is less than 1.020 kgf / cm 2, air bubbles are mixed in and the quality is not preferable. Furthermore, if the temperature rises and falls too fast, large lumps cannot be obtained due to cracks in the product.
【００１８】この他、上記蓄光発光石の製造原料となる
粉砕された残光性発光材料には、各種の発光材料が用い
られ、特にその種類等によって限定されるものではな
い。In addition, various luminescent materials are used for the pulverized afterglow luminescent material used as a raw material for producing the luminous luminescent stone, and are not particularly limited by the kind or the like.
【００１９】上記製造方法では、冷却工程の後、得られ
た焼結体を加工研磨するが、この加工研磨としては、ダ
イヤモンド、コランダム、アルミナ、炭化硅素、窒化硼
素等の研削工具を用いて研削、切削等により加工され
る。特に好ましくはダイヤモンドである。また研磨剤と
しては、持に限定されるものではなく、金属酸化物、コ
ランダム、エメリー、ガーネット、軽石、トリポリ、炭
化硅素、アルミナ、ダイヤモンド等の粉末がある。また
上記製造方法において、焼成炉内の雰囲気は、還元雰囲
気で行い、この還元雰囲気としては、窒素と水素の混合
ガス、ＣＯガスが用いられ、また炭素で造った還元雰囲
気が好ましい。この炭素で造った雰囲気とは、容器の周
辺に木炭又は炭素粉末を適用することにより還元雰囲気
を形成したものである。In the above manufacturing method, after the cooling step, the obtained sintered body is processed and polished, and the polishing is performed using a grinding tool such as diamond, corundum, alumina, silicon carbide and boron nitride. , And the like. Particularly preferred is diamond. The abrasive is not limited to powder, but includes powders of metal oxides, corundum, emery, garnet, pumice, tripoly, silicon carbide, alumina, diamond and the like. In the above-mentioned production method, the atmosphere in the firing furnace is a reducing atmosphere. As the reducing atmosphere, a mixed gas of nitrogen and hydrogen and a CO gas are used, and a reducing atmosphere made of carbon is preferable. The atmosphere made of carbon means that a reducing atmosphere is formed by applying charcoal or carbon powder around the container.
【００２０】この蓄光発光石は、太腸光、蛍光灯、その
他の光で励起されて４４０ｎｍ〜７００ｎｍの波長域で
発光し、高輝度・長残光性に優れており、特に残光時問
は、４０〜６０時間以上である。また、発光色について
は、緑、青、黄、紫、赤の５種類のものが得られてい
る。これらの蓄光発光石の硬度は、発光色によってそれ
ぞれ異なるが、大体モース硬度６〜８を示し、非常に硬
度の高いものである。そして、研磨加工することで表面
に光沢が現れ、発光する光も非常に鮮明であるため、高
級感を感じさせるものである。The phosphorescent luminous stone is excited by a large intestine, a fluorescent lamp, or other light and emits light in a wavelength range of 440 nm to 700 nm, and has excellent high luminance and long afterglow. Is 40 to 60 hours or more. In addition, five kinds of emission colors, green, blue, yellow, purple, and red, are obtained. The hardness of these phosphorescent stones differs depending on the emission color, but is approximately 6 to 8 on the Mohs scale, and is extremely high. Then, the surface is polished by polishing, and the emitted light is very clear, giving a sense of quality.
【００２１】以下、上記蓄光発光石を利用した発光装飾
品の実施の形態を図１乃至図８に基づいて説明する。図
１は、所定形状に加工・研磨して表面の光沢を出した蓄
光発光石１を、リング２の台座部３に配して蓄光発光石
入りの指輪を構成した場合の実施例を示したものであ
る。図２は、上記蓄光発光石１の特性を試料１〜５につ
いて示したものである。この図に示したように、蓄光発
光石１は、宝石・貴石類と同等の硬度を有し、また発光
色として緑、青、黄、紫、赤の５種類を有している。さ
らに、初期発光輝度も高く、残光時間は最低でも１０時
間を超え、長いものでは４０時間に達している。このよ
うに、蓄光発光石１自身が優れた特性を有しているが、
この蓄光発光石１の表面をさらに研磨することで、天然
の宝石や貴石類と同等な光沢と色調が現れ、装飾品とし
て十分に利用できる。このような表面に光沢を出すこと
によって、周囲の明るいところでは、綺麗で滑らかな曲
面状に見え、しかも、青、緑、赤等の色調を放ち自然の
宝石・貴石と同等の高級感を与える。一方、周囲の暗い
ところでは、青、緑、赤等の色で発光するため、人工的
な美しさがあらわれる。また、遠方からでも、その発光
が際立って見えるので目印となり、夜間等の交通安全性
の面においても効果がある。図１は上記蓄光発光石１を
指輪に応用した例であるが、その他に、ネックレス、ブ
レスレット、イアリング、ヘアピン、ネクタイ、衣類の
ボタン類、靴や鞄等の飾り具としても利用できること勿
論である。Hereinafter, an embodiment of a luminous ornament using the luminous luminous stone will be described with reference to FIGS. FIG. 1 shows an embodiment in which a luminous luminous stone 1 processed and polished into a predetermined shape and having a glossy surface is arranged on a pedestal portion 3 of a ring 2 to form a ring containing luminous luminous stone. Things. FIG. 2 shows characteristics of the phosphorescent stone 1 for samples 1 to 5. As shown in the figure, the phosphorescent luminous stone 1 has the same hardness as jewels and precious stones, and has five emission colors of green, blue, yellow, purple and red. Furthermore, the initial light emission luminance is high, and the afterglow time exceeds at least 10 hours, and as long as 40 hours. As described above, the phosphorescent luminous stone 1 itself has excellent characteristics,
By further polishing the surface of the luminous luminous stone 1, the same luster and color tone as natural jewelry and precious stones appear, and can be sufficiently used as a decorative article. By giving a gloss to such a surface, it looks beautiful and smooth curved surface in bright surroundings, and gives off a color tone such as blue, green, red, etc. and gives the same luxury feeling as natural jewelry and precious stones . On the other hand, in a surrounding dark place, light is emitted in colors such as blue, green, and red, so that artificial beauty appears. In addition, the light emission can be seen even from a distance, so that it becomes a mark, which is effective in traffic safety at night and the like. FIG. 1 shows an example in which the luminous luminescent stone 1 is applied to a ring. In addition, the phosphorescent stone 1 can also be used as a decoration such as a necklace, a bracelet, an earring, a hairpin, a tie, buttons for clothes, shoes and bags. .
【００２２】図３は、研磨加工により光沢を出した蓄光
発光石１の表層部に光透過性のあるキャラコート被膜４
を薄く設けて全体をパール調に仕上げた場合の実施例を
示したものである。このような光透過性の被膜を設けた
ため、周囲の明るいところではパールのような発光色が
現れ、また暗いところでもややパールの色調を帯びた発
光色が現れる。これは、パール調の指輪やネックレス等
に適している。本実施例では、パール調の被膜を設けた
ものであるが、貴金属調の薄い被膜、あるいは蓄光発光
石１の色合いを変えたい場合は、蓄光発光石１と異なっ
た色彩の被膜を設けてもよい。このように様々な色調の
光透過性の被膜を形成することで、蓄光発光石１の発光
色も微妙に変化させることができ、バリエーション豊富
な蓄光発光石入りの装飾品が形成できる。FIG. 3 shows a light-transmitting character coat 4 on the surface layer of the luminous luminous stone 1 which has been made glossy by polishing.
Are shown in an embodiment in which the whole is finished in a pearl tone by providing a thin layer. Since such a light-transmitting film is provided, a luminescent color like pearl appears in a bright surrounding area, and a luminescent color with a slight pearl color tone appears in a dark place. This is suitable for pearl-like rings and necklaces. In the present embodiment, a pearl-like coating is provided. However, if it is desired to change the color of the phosphorescent luminous stone 1 or a color of the phosphorescent luminous stone 1, a coating different in color from the phosphorescent luminous stone 1 may be provided. Good. By forming the light-transmitting coatings of various colors as described above, the luminescent color of the luminous luminous stone 1 can also be finely changed, and decorative articles containing luminous luminous stones with various variations can be formed.
【００２３】図４は、基体６の中心に宝石５（ダイヤモ
ンド）を配置し、その周囲に多数の蓄光発光石１をネッ
クレスとした場合の実施例を示したものである。これ
は、明るいところでは、色彩性豊かな装飾感が得られ、
一方、暗いところにおいては、蓄光発光石１の発する光
で宝石５の輝きを一層際立たせる効果がある。FIG. 4 shows an embodiment in which a jewel 5 (diamond) is arranged at the center of a base 6 and a large number of luminous luminous stones 1 are necklaces around it. This means that in bright places, a richly colorful decorative feeling can be obtained,
On the other hand, in a dark place, the light emitted from the luminous luminous stone 1 has the effect of making the jewel 5 more brilliant.
【００２４】図５は、宝石入りの指輪に発光色の異なっ
た蓄光発光石を２種類以上、宝石５の周囲にちりばめて
形成した指輪の実施例を示したものである。この実施例
では宝石５の周囲に赤色発光の蓄光発光石１ａと、青色
発光の蓄光発光石１ｂとを交互に配して形成したもので
ある。このような構成とすることで、多数の発光色が混
合され、変化に富んだ色合いになり、装飾性を高めるこ
とができる。FIG. 5 shows an embodiment of a ring in which two or more kinds of luminous luminescent stones having different emission colors are studded around a jewel 5 on a ring containing a jewel. In this embodiment, red light-emitting luminous stones 1a and blue light-emitting luminous luminous stones 1b are alternately arranged around the jewel 5. With such a configuration, a large number of light-emitting colors are mixed, resulting in a variety of shades, and decorativeness can be enhanced.
【００２５】図６は、リング２の上に形成された台座部
３に蓄光発光石１を配し、その上に光透過性を有する宝
石５を配置して一体接合した指輪の実施例を示したもの
である。このような構成とすることで、例えば、緑色の
エメラルド石に緑色発光の蓄光発光石１を接合すると外
観全体がエメラルド石に見え、エメラルド石自体が発光
したように見える。一方、宝石５の色合いと異なった発
光色を示す蓄光発光石１を接合することで、宝石５の色
合いと微妙に異なった発光色が得られ、奇抜な色彩効果
を出させることができる。FIG. 6 shows an embodiment of a ring in which the luminous luminous stone 1 is arranged on a pedestal portion 3 formed on a ring 2 and a light-transmitting jewel 5 is arranged thereon and integrally joined. It is a thing. With such a configuration, for example, when the phosphorescent luminescent stone 1 emitting green light is bonded to green emerald stone, the entire appearance looks like emerald stone, and the emerald stone itself appears to emit light. On the other hand, by joining the luminous luminous stones 1 having a different luminescent color from the color of the jewel 5, a luminescent color slightly different from the color of the jewel 5 can be obtained, and a quirky color effect can be obtained.
【００２６】図７は、発光色が異なる２種類以上の蓄光
発光石を用いて製作したカメオの実施例を示したもので
ある。ここでは、カメオの中心となる部分に黄色発光の
蓄光発光石１ｃを用いて富士山の浮き彫りを施すと共
に、その周囲に赤色発光の蓄光発光石１ａと、青色発光
の蓄光発光石１ｂとを交互にちりばめて形成してある。
このように、カメオの中心部分にも蓄光発光石を用いる
ことができると共に、２種類以上の発光色が混ざり合う
ので、色彩も豊かで色鮮やかな装飾品が形成できる。FIG. 7 shows an embodiment of a cameo manufactured using two or more kinds of luminous luminous stones having different emission colors. Here, the center part of the cameo is embossed with Mt. Fuji using luminous luminous stones 1c of yellow luminescence, and luminous luminous stones 1a of red luminescence and luminous luminous stones 1b of blue luminescence are alternately provided therearound. It is studded and formed.
As described above, the phosphorescent luminous stone can be used also in the central portion of the cameo, and since two or more kinds of luminescent colors are mixed, a colorful and colorful ornament can be formed.
【００２７】図８は、蓄光発光石１の表層部に出来た多
数の微小な空隙７に、この蓄光発光石１と異なった色調
の塗料を埋め込んで模様を構成した装飾品の例である。
このような空隙７は、蓄光発光石１の形成過程における
高温・高圧処理の中で内部に溜まったガスが抜けた痕
で、数μ〜１０数μｍの様々な形状となって現れる。こ
の微小な空隙７は、蓄光発光石１を研磨加工することよ
って表層部に現れてくる。そして、この微小な空隙７の
中に蓄光発光石１と異なる色の塗料を練り込み固着する
ことで点描模様が形成される。FIG. 8 shows an example of a decorative product in which a pattern is formed by embedding a paint having a color tone different from that of the luminous luminous stone 1 into a large number of minute voids 7 formed in the surface layer of the luminous luminous stone 1.
Such voids 7 are traces from which gas accumulated inside during the high-temperature and high-pressure treatment in the process of forming the luminous luminous stone 1 appears, and appear in various shapes of several μm to several tens μm. The minute voids 7 appear in the surface layer by polishing the phosphorescent stone 1. Then, a paint of a color different from that of the phosphorescent stone 1 is kneaded and fixed into the minute voids 7 to form a stippling pattern.
【００２８】なお、上記実施例以外に、仏像等の各種置
物の全部あるいは一部に蓄光発光石を用いてもよい。こ
の場合でも様々に異なった発色が現れ、装飾効果を高め
る上で有効である。In addition to the above embodiments, phosphorescent luminous stones may be used for all or a part of various ornaments such as Buddha statues. Even in this case, various different colors appear, which is effective in enhancing the decorative effect.
【００２９】[0029]
【発明の効果】以上説明したように、本発明に係る発光
装飾品によれば、発光輝度が高く、且つ長時間の残光特
性を持つ蓄光発光石を用いたことで、紫外線照射源を持
たない身飾り装飾品に応用可能となる。また、蓄光発光
石の原石に加工・研磨を加えたことで、宝石や貴石類と
同等な高級感ある発光装飾品が製造可能である。As described above, according to the luminous ornament according to the present invention, the use of the luminous luminous stone having a high luminous luminance and a long-lasting afterglow characteristic allows the luminous ornament to have an ultraviolet irradiation source. Not applicable to decorative ornaments. In addition, by adding processing and polishing to the gemstone of the phosphorescent luminous stone, it is possible to manufacture a high-quality luminous decorative product equivalent to jewelry and precious stones.
【００３０】また、請求項２の発光装飾品によれば、蓄
光発光石の表面に光透過性の有色被膜を形成したので、
蓄光発光石の発光色を微妙に変化させることができ、バ
リエーション豊富な蓄光発光石入りの装飾品が形成でき
る。According to the second aspect of the present invention, the light-transmitting colored film is formed on the surface of the luminous luminous stone.
The luminescent color of the phosphorescent stone can be subtly changed, and a variety of decorative articles containing the phosphorescent stone can be formed.
【００３１】また、請求項３の発光装飾品によれば、蓄
光発光石を貴石の周辺に配置したので、蓄光発光石の発
する光で宝石の輝きを一層際立たせることができる。According to the third aspect of the present invention, since the phosphorescent luminous stones are arranged around the precious stones, the glow of the jewel can be further enhanced by the light emitted from the phosphorescent luminous stones.
【００３２】また、請求項４の発光装飾品によれば、発
光色が異なる少なくとも２種類の蓄光発光石を貴石の周
辺に配置したので、多数の発光色が混合され、変化に富
んだ色合いになって装飾性を高めることができる。According to the luminous ornament of the fourth aspect, since at least two kinds of luminous luminous stones having different luminescent colors are arranged around the precious stone, a large number of luminescent colors are mixed to provide a variety of colors. As a result, the decorativeness can be enhanced.
【００３３】また、請求項５の発光装飾品によれば、蓄
光発光石と貴石とを一体化したので、明るい所では宝石
や貴石の美しさが見える一方、暗い所では宝石や貴石が
発光しているように見えてその美しさを際立たせること
ができる。According to the luminous ornament of claim 5, since the luminous luminous stone and the precious stone are integrated, the beauty of the jewel or the precious stone can be seen in a bright place, while the jewel or the precious stone emits light in a dark place. It can look like it and make its beauty stand out.
【００３４】また、請求項６の発光装飾品によれば、発
光色が異なる少なくとも２種類の蓄光発光石と貴石とを
一体化したので、明るい所では色彩豊かで色鮮やかな装
飾品が形成できる一方、暗い所では色の異なる発光色が
混在してその美しさを際立たせることができる。According to the luminous ornament of claim 6, since at least two kinds of luminous luminous stones and precious stones having different emission colors are integrated, a colorful and colorful ornament can be formed in a bright place. On the other hand, in a dark place, different emission colors can be mixed to enhance the beauty.
【００３５】また、請求項７の発光装飾品によれば、蓄
光発光石の表層部に発生する微小な空隙に、蓄光発光石
とは異なる色の塗料を埋め込むことによって、模様の付
いた蓄光発光石を形成することができる。According to the luminous decorative article of the present invention, a paint having a color different from that of the luminous luminous stone is embedded in minute voids generated in the surface layer of the luminous luminous stone, thereby providing a luminous light with a pattern. Stones can be formed.
【図１】本発明に係る発光装飾品の第１実施例を示す指
輪の断面図である。FIG. 1 is a sectional view of a ring showing a first embodiment of a luminous decorative article according to the present invention.
【図２】上記発光装飾品に用いられる蓄光発光石の発色
毎の硬度、残光時間等を比較した特性表である。FIG. 2 is a characteristic table comparing the hardness, the afterglow time, and the like for each color of the phosphorescent luminous stone used in the light-emitting decorative article.
【図３】上記発光装飾品の第２実施例を示す平面図であ
る。FIG. 3 is a plan view showing a second embodiment of the light emitting decorative article.
【図４】上記発光装飾品の第３実施例を示す断面図であ
る。FIG. 4 is a sectional view showing a third embodiment of the light emitting decorative article.
【図５】上記発光装飾品の第４実施例を示す平面図であ
る。FIG. 5 is a plan view showing a fourth embodiment of the light emitting decorative article.
【図６】上記発光装飾品の第５実施例を示す断面図であ
る。FIG. 6 is a sectional view showing a fifth embodiment of the light emitting decorative article.
【図７】上記発光装飾品の第６実施例を示す平面図であ
る。FIG. 7 is a plan view showing a sixth embodiment of the light emitting decorative article.
【図８】上記発光装飾品の第７実施例を示す平面図であ
る。FIG. 8 is a plan view showing a seventh embodiment of the light emitting decorative article.
１ 蓄光発光石 ２ リング ３ 台座部 1 phosphorescent stone 2 ring 3 pedestal
Claims (7)
て、該焼結体の特性がモース硬度６〜８、比重６〜８、
発光波長４４０ｎｍ〜７００ｎｍを有する蓄光発光石を
加工・研磨し、装飾品としたことを特徴とする発光装飾
品。1. A sintered body comprising an afterglow luminescent material, wherein the sintered body has a Mohs hardness of 6 to 8, a specific gravity of 6 to 8,
A luminous decorative article obtained by processing and polishing a phosphorescent luminous stone having an emission wavelength of 440 nm to 700 nm to obtain a decorative article.
光透過性の有色被膜を形成したことを特徴とする請求項
１記載の発光装飾品。2. A light-emitting decorative article according to claim 1, wherein a light-transmitting colored film is formed on the surface of the processed and polished phosphorescent stone.
周辺に配したことを特徴とする請求項１記載の発光装飾
品。3. The luminous decorative article according to claim 1, wherein said processed and polished luminous luminous stone is arranged around a precious stone.
発光石を貴石の周辺に配したことを特徴とする請求項１
記載の発光装飾品。4. The luminescent stone according to claim 1, wherein at least two kinds of luminous luminescent stones having different emission colors are arranged around the precious stone.
The luminous ornament as described.
一体形成したことを特徴とする請求項１記載の発光装飾
品。5. The luminous decorative article according to claim 1, wherein said processed and polished luminous luminescent stone is formed integrally with precious stone.
発光石を貴石と一体形成したことを特徴とする請求項１
記載の発光装飾品。6. The precious stone, wherein at least two kinds of luminous luminous stones having different emission colors are formed integrally with the precious stone.
The luminous ornament as described.
表層部に発生する微小空隙に、有色塗料を埋め込んで形
成したことを特徴とする請求項１記載の発光装飾品。7. The luminous decorative article according to claim 1, wherein a colored paint is buried in minute voids generated in a surface layer of the phosphorescent stone formed by the processing and polishing.