JPH11269315A - Polyolefin film or sheet processable by high-frequency welder - Google Patents
Polyolefin film or sheet processable by high-frequency welderInfo
- Publication number
- JPH11269315A JPH11269315A JP10077390A JP7739098A JPH11269315A JP H11269315 A JPH11269315 A JP H11269315A JP 10077390 A JP10077390 A JP 10077390A JP 7739098 A JP7739098 A JP 7739098A JP H11269315 A JPH11269315 A JP H11269315A
- Authority
- JP
- Japan
- Prior art keywords
- vinyl acetate
- sheet
- polyolefin
- ethylene
- processable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は高周波ウエルダー加
工が可能なポリエチレン・ポリプロピレン等のポリオレ
フィンフイルム又はシートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyolefin film or sheet such as polyethylene or polypropylene which can be subjected to high frequency welding.
【0002】一般にポリエチレン、ポリプロピレン等は
高周波ウエルダー加工が不可能なであった。In general, high-frequency welding has not been possible with polyethylene, polypropylene and the like.
【0003】[0003]
【課題を解決するための手段】本発明者は、エチレン−
酢酸ビニルコポリマーをポリオレフィンに加えるとポリ
オレフィンフイルム又はシートは高周波ウエルダー可能
であることを発見して本発明に至った。Means for Solving the Problems The present inventors have developed ethylene-
The inventors have found that the addition of a vinyl acetate copolymer to a polyolefin allows the polyolefin film or sheet to be high frequency weldable.
【0004】すなわち本発明は、配合物中の酢酸ビニル
含有量が5〜20%なるようにエチレン−酢酸ビニルコ
ポリマーを添加したことを特徴とする高周波ウエルダー
加工が可能なポリオレフィンフイルム又はシートに関す
る。[0004] That is, the present invention relates to a polyolefin film or sheet capable of high-frequency welding, wherein an ethylene-vinyl acetate copolymer is added so that the vinyl acetate content in the composition is 5 to 20%.
【0005】上記の配合物とはエチレン−酢酸ビニルコ
ポリマーを加えたポリオレフィン配合物を意味する。酢
酸ビニル含有量が少ないエチレン−酢酸ビニルコポリマ
ーを使用する場合、そのコポリマーのポリオレフィンへ
の添加量を多くして、配合物中の酢酸ビニル含量を5〜
20%となるようにする。又酢酸ビニル含量の多いエチ
レン−酢酸ビニルコポリマーを使用する時は、そのコポ
リマーのポリオレフィンへの添加量を少なくする一般に
酢酸ビニル含量20〜40%のエチレン−酢酸ビニルコ
ポリマーが好ましく、そのコポリマーのポリオレフィン
への含有量は15〜45%である。[0005] The above-mentioned composition means a polyolefin composition to which an ethylene-vinyl acetate copolymer is added. When using an ethylene-vinyl acetate copolymer having a low vinyl acetate content, the amount of the copolymer added to the polyolefin is increased to increase the vinyl acetate content in the formulation to 5 to 5.
It should be 20%. When an ethylene-vinyl acetate copolymer having a high vinyl acetate content is used, an ethylene-vinyl acetate copolymer having a vinyl acetate content of 20 to 40% is generally preferred to reduce the amount of the copolymer added to the polyolefin. Is 15 to 45%.
【0006】配合物中の酢酸ビニル含量が5〜20%以
外では得られたポリオレフィンは完全に高周波ウエルダ
ー加工できない。[0006] If the vinyl acetate content of the formulation is other than 5 to 20%, the resulting polyolefin cannot be completely high frequency welded.
【0007】ポリオレフィンとは低密度乃至高密度ポリ
エチレン及びポリプロピレンである。[0007] Polyolefins are low density to high density polyethylene and polypropylene.
【0008】[0008]
【実施例】試験方法 試験No1〜No7の配合内容でシートの厚みが0.1
5m/mの試験片を作成し二枚重ねで高周波ウエルダー
加工を行ない溶着状態を比較した、その結果を表1に示
す。EXAMPLES Test method The thickness of the sheet was 0.1 with the content of Test Nos.
A test piece of 5 m / m was prepared, high frequency welding was performed on two test pieces, and the welded state was compared. The results are shown in Table 1.
【0009】[0009]
【表1】 [Table 1]
【0010】[0010]
【効果】配合物中の酢酸ビニル含有量が5〜20%以内
でのエチレン−酢酸ビニルコポリマーを含むポリエチレ
ン・ポリプロピレンのフイルム又はシートを高周波ウエ
ルダー加工すると全面接着し、引張ると材料破壊を起
す。When a high-frequency welding process is applied to a polyethylene / polypropylene film or sheet containing an ethylene-vinyl acetate copolymer having a vinyl acetate content of 5 to 20% or less in the composition, the whole surface is adhered, and the material is broken when pulled.
【0011】ウエルダー加工シールはヒートシールに比
べてシール部分の周囲が見栄えが悪くならないという利
点があるが、本発明に従えば、エチレン−酢酸ビニルコ
ポリマーを混入により、ポリオレフィンフイルムのウエ
ルダー加工シールが可能になり、その効果は顕著であ
る。Although the welded seal has the advantage that the appearance of the periphery of the seal portion does not deteriorate compared to the heat seal, according to the present invention, the welded seal of the polyolefin film can be obtained by mixing the ethylene-vinyl acetate copolymer. And the effect is remarkable.
フロントページの続き (51)Int.Cl.6 識別記号 FI C08L 31:04) B29K 23:00 Continued on the front page (51) Int.Cl. 6 Identification code FI C08L 31:04) B29K 23:00
Claims (1)
%なるようにエチレン−酢酸ビニルコポリマーを添加し
たことを特徴とする高周波ウエルダー加工が可能なポリ
オレフィンフイルム又はシート。1. The composition according to claim 1, wherein the content of vinyl acetate is from 5 to 20.
% Of a polyolefin film or sheet which can be subjected to high frequency welding, wherein an ethylene-vinyl acetate copolymer is added to the film.