JPH11254859A - Card and label composite - Google Patents
Card and label compositeInfo
- Publication number
- JPH11254859A JPH11254859A JP7338598A JP7338598A JPH11254859A JP H11254859 A JPH11254859 A JP H11254859A JP 7338598 A JP7338598 A JP 7338598A JP 7338598 A JP7338598 A JP 7338598A JP H11254859 A JPH11254859 A JP H11254859A
- Authority
- JP
- Japan
- Prior art keywords
- label
- card
- curable composition
- tackiness
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、表裏面に被覆手段
を有したカードと、表面に被覆手段、裏面に粘着手段を
有したラベルとが、基材を同一として分離可能に連接し
てなるカード・ラベル複合体に関し、さらに詳しくは、
前記被覆手段と粘着手段が共に紫外線硬化型組成物から
なるカード・ラベル複合体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a card having a covering means on the front and back surfaces and a label having a covering means on the front surface and a sticking means on the back surface, which are made of the same base material and are connected in a separable manner. For more details on the card / label complex,
The present invention relates to a card / label composite wherein both the coating means and the adhesive means are made of an ultraviolet curable composition.
【０００２】[0002]
【従来の技術】カードの基本構成は、通常、プラスチッ
ク板や合成紙からなるカード基材を単独としてなるもの
や、カード本体の耐久性の向上を目的に、通常紙からな
るカード基材の表裏面に高分子フィルムを貼着してなる
ラミネートカードが、現在、様々な分野で普及している
が、本発明は後者のラミネートカードを対象とするもの
である。一方、ラベルの基本構成は、一般的に、ラベル
基材の裏面に感圧接着剤（粘着剤）を塗布してなり、上
述のカードと同様に、ラベル基材が通常紙からなる場合
には、その表面に高分子フィルムを貼着してなるラミネ
ートラベルが耐久性の面で好ましく、本発明はこのラミ
ネートラベルを対象とするものである。2. Description of the Related Art The basic structure of a card is usually such that a card base made of a plastic plate or synthetic paper is used alone, or a card base made of normal paper is used for the purpose of improving the durability of the card body. Laminated cards having a polymer film adhered to the back surface are now widespread in various fields, but the present invention is directed to the latter laminated cards. On the other hand, the basic structure of a label is generally such that a pressure-sensitive adhesive (adhesive) is applied to the back surface of a label base material. In view of durability, a laminated label having a polymer film adhered to the surface thereof is preferable, and the present invention is directed to this laminated label.
【０００３】そして、このような基本構成からなるカー
ドとラベルを同一の基材から複合して作成することのメ
リットとは、カードとラベルとが同一の生産ラインで製
造できるため、それぞれへの印刷や印字が同時に行うこ
とができるなど、生産性が非常に良い点が挙げられる。
また、カード部とラベル部が連接しているため、互いに
関連した役務で使用する場合、例えば、カード部を商品
情報の控え片として保持し、ラベル部を対象商品へ貼付
するといった商品管理での利用の場合など、カード及び
ラベルとして、それぞれ使用する直前で互いを分離する
ため、両者の照会作業などがなく、取り扱いが非常に便
利になる。The advantage of making a card and a label having such a basic structure by combining them from the same base material is that the card and the label can be manufactured on the same production line, so that printing on each of them can be performed. And productivity can be very high, for example, printing can be performed simultaneously.
In addition, since the card section and the label section are linked, when used in services related to each other, for example, the card section is held as a copy of product information, and the label section is attached to the target product, for example, in product management. In the case of use, for example, the card and the label are separated from each other immediately before they are used, so that there is no need to perform an inquiry operation for the two and the handling becomes very convenient.
【０００４】[0004]
【発明が解決しようとする課題】現在、このような基本
構成からなるカードとラベルとを同一の基材から複合し
て作成する技術は、カードとラベルの作成手段の違いか
ら、好適な方法が確立されていない。すなわち、カード
・ラベル複合体を作成するためには、カード部の方で
は、高分子フィルムにホットメルト型接着剤を塗布し、
加熱・加圧処理により当該高分子フィルムをカード部の
表裏面に貼着させるための特殊な貼着機構を必要とする
し、一方、ラベル部の方でも、ラベル部の表面に高分子
フィルムを貼着する際に、同様の貼着機構を必要とする
のと同時に、感圧接着剤（粘着剤）の塗布装置やその定
着工程に特別な加熱装置などが必要であるため、生産性
やコスト面などに問題がある。At present, a technique for forming a card and a label having such a basic structure by combining them from the same base material is not suitable because of the difference in the means for forming the card and the label. Not established. That is, in order to make a card-label composite, in the card part, apply a hot melt type adhesive to the polymer film,
A special attaching mechanism is required to attach the polymer film to the front and back surfaces of the card section by heat and pressure treatments.On the other hand, even for the label section, the polymer film is applied to the surface of the label section. At the time of sticking, the same sticking mechanism is required, and at the same time, a special heating device is required for the application device of the pressure-sensitive adhesive (adhesive) and the fixing process, so productivity and cost are reduced. There is a problem with the surface.
【０００５】そこで、本発明は、カードとラベルとを同
一の基材から複合して作成でき、また、従来のような高
分子フィルムの貼着工程や感圧接着剤の定着工程などの
複雑な製造工程を要せず、さらに、生産時間を短縮で
き、もって、生産性やコスト面などに優れるカード・ラ
ベル複合体の提供を課題とする。Accordingly, the present invention provides a composite card and label from the same base material, and has complicated processes such as a conventional polymer film sticking step and a pressure-sensitive adhesive fixing step. An object of the present invention is to provide a card-label composite which does not require a manufacturing process, can further reduce the production time, and is excellent in productivity and cost.
【０００６】[0006]
【課題を解決するための手段】かかる課題に鑑み、本発
明者は、表裏面に被覆手段を有したカード部と、表面に
被覆手段、裏面に粘着手段を有したラベル部とが基材を
同一として分離可能に連接してなるカード・ラベル複合
体において、当該被覆手段と粘着手段が、共に硬化状態
によりタック性の有無を具点できる紫外線硬化型組成物
とすることで、上記課題を達成できることを見いだし、
本発明のカード・ラベル複合体を想到した。In view of the above problem, the present inventor has proposed that a card portion having a cover means on the front and back surfaces and a label portion having a cover means on the front surface and an adhesive means on the back surface comprise a substrate. The above object has been achieved by providing a card / label composite which is connected in the same manner and is separable and connected, in which the coating means and the adhesive means are both ultraviolet-curable compositions capable of providing tackiness depending on the curing state. Find out what you can do,
A card-label composite of the present invention has been devised.
【０００７】すなわち、本発明のカード・ラベル複合体
は、切取線を介して連接したカード部とラベル部からな
り、前記カード部の表裏面及び前記ラベル部の表面には
タック性のない完全硬化状態の紫外線硬化型組成物層が
施されると共に、前記ラベル部の裏面にはタック性のあ
る不完全硬化状態の紫外線硬化型組成物層が施されてな
ることを特徴とする。That is, the card / label composite of the present invention comprises a card portion and a label portion connected to each other via a cut-off line, and the front and back surfaces of the card portion and the surface of the label portion are completely cured without tackiness. And an ultraviolet-curable composition layer in an incompletely cured state having tackiness is applied to the back surface of the label portion.
【０００８】[0008]
【発明の実施形態】以下、本発明のカード・ラベル複合
体を、実施例と添付の図面に基づき、さらに具体的に説
明する。なお、ここにおいて、図１は本発明のカード・
ラベル複合体の表面平面図、図２は図１のＸ−Ｘ線断面
図である。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the card / label composite of the present invention will be described in more detail with reference to examples and the accompanying drawings. FIG. 1 shows a card according to the present invention.
FIG. 2 is a cross-sectional view taken along the line XX of FIG. 1.
【０００９】本実施例におけるカード・ラベル複合体１
は「商品管理カード・ラベル」として構成され、図１に
示す如く、カード部２及びラベル部３が、切取線Ｍ（ミ
シン線）を介して連接してなる。そして、「受領票」た
るカード部２及び「貼付票」たるラベル部３のそれぞれ
の表面には、予め、標題、商品情報欄、バーコードなど
の所定の印刷４が施され、さらに、商品名、規格、数量
などの可変情報５などが印字されている。なお、カード
部２の裏面にも書誌的事項などの印刷が施されている
が、ここでは図示しない。The card / label complex 1 in the present embodiment
Is configured as a "product management card / label", and as shown in FIG. 1, the card unit 2 and the label unit 3 are connected via a cutout line M (sewing line). Then, a predetermined print 4 such as a title, a product information field, a bar code, etc. is applied in advance to the surface of each of the card unit 2 serving as a "receipt slip" and the label unit 3 serving as a "sticking slip". , Standard, quantity and other variable information 5 are printed. Note that the back of the card unit 2 is also printed with bibliographic items and the like, but is not shown here.
【００１０】そして、図２に示す如く、カード・ラベル
複合体１の構成上の特徴は、カード部２の表裏面及びラ
ベル部３の表面にはタック性のない完全硬化状態の紫外
線硬化型組成物層ａが施されると共に、ラベル部３の裏
面にはタック性のある不完全硬化状態の紫外線硬化型組
成物層ｂが施されてなるところにある。なお、この不完
全硬化状態の紫外線硬化型組成物層ｂは、剥離紙６にて
保護されている。As shown in FIG. 2, the structure of the card-label composite 1 is characterized in that the front and back surfaces of the card portion 2 and the surface of the label portion 3 have a tack-free UV-curable composition in a completely cured state. The material layer a is applied, and the UV curable composition layer b in the incompletely cured state having tackiness is applied to the back surface of the label portion 3. The incompletely cured ultraviolet curable composition layer b is protected by a release paper 6.
【００１１】本発明における紫外線硬化型組成物とは、
紫外線照射により重合し、硬化層を形成し得る組成物で
あり、特に、不完全硬化状態でタック性があり、完全硬
化状態でタック性を失う性質を有するものから選択され
る。このような機能を具現できる組成物としては、例え
ば、ポリエステルアクリレート、エポキシアクリレー
ト、アルギドアクリレート、ウレタンアクリレートなど
の光重合性プリポリマ、モノマに光重合開始剤を加えて
なるものが挙げられる。The ultraviolet-curable composition of the present invention is:
A composition that can be polymerized by irradiation with ultraviolet light to form a cured layer, and is particularly selected from those having tackiness in an incompletely cured state and losing tackiness in a completely cured state. As a composition capable of realizing such a function, for example, a composition obtained by adding a photopolymerization initiator to a photopolymerizable prepolymer such as polyester acrylate, epoxy acrylate, argido acrylate, or urethane acrylate, or a monomer can be mentioned.
【００１２】特に、紫外線照射量の調整によってタック
性の有無を具現し易い点で、末端にアクリロイル基、メ
タクリロイル基、アリル基、メタリル基などの不飽和基
を有する光重合性プレポリマと光重合性モノマと光重合
開始剤とを含有する紫外線硬化型組成物が最も好まし
い。先ず、上記光重合性プレポリマとは、例えば、ビス
フェノールＡのジグリシジルエーテルジアクリレート、
エポキシ樹脂と２−ヒドロキシエチルアクリレートとの
反応生成物、エポキシ樹脂のジグリシジルエーテルとジ
アリルアミンとの反応生成物などのエポキシ樹脂系プレ
ポリマや、グリシジルジアクリレートと無水フタル酸と
の開環共重合エステル、メタクリル酸二量体とポリオー
ルとのエステル、アクリル酸と無水フタル酸とプロピレ
ンオキシドから得られるポリエステル、ポリエチレング
リコールと無水マレイン酸とグリシジルメタクリレート
との反応生成物などの不飽和ポリエステル系プレポリマ
や、ポリビニルアルコールとＮ−メチロールアクリルア
ミドとの反応生成物、ポリビニルアルコールを無水コハ
ク酸でエステル化した後に、グルシジルメタクリレート
を付加させた反応生成物などのポリビニル系プレポリマ
や、ウレタン結合を介してポリオキシアルキレンセグメ
ント叉は飽和ポリエステルセグメント、あるいは、その
両方が連結し、両端末にアクリロイル基叉はメタクロイ
ル基を有するウレタン系プレポリマ、あるいは、エチレ
ン−無水マレイン酸共重合体とアリルアミンとの反応生
成物、メチルビニルエーテル−無水マレイン酸共重合体
と２−ヒドロキシエチルアクリレートとの反応生成物叉
は、これにさらにグルシジルアクリレートを反応させた
ものなどのポリアクリル酸系叉はマレイン酸共重合体系
プレポリマなどが挙げられる。In particular, the photopolymerizable prepolymer having an unsaturated group such as an acryloyl group, a methacryloyl group, an allyl group, or a methallyl group at the end thereof and a photopolymerizable polymer, because the presence or absence of tackiness can be easily realized by adjusting the amount of ultraviolet irradiation. An ultraviolet-curable composition containing a monomer and a photopolymerization initiator is most preferred. First, the photopolymerizable prepolymer is, for example, diglycidyl ether diacrylate of bisphenol A,
A reaction product of an epoxy resin and 2-hydroxyethyl acrylate, an epoxy resin prepolymer such as a reaction product of a diglycidyl ether of an epoxy resin and diallylamine, and a ring-opening copolymer ester of glycidyl diacrylate and phthalic anhydride; Esters of methacrylic acid dimer and polyol, polyesters obtained from acrylic acid, phthalic anhydride and propylene oxide, unsaturated polyester prepolymers such as reaction products of polyethylene glycol, maleic anhydride and glycidyl methacrylate, and polyvinyl alcohol Reaction product of N-methylolacrylamide and polyvinyl alcohol, such as a reaction product obtained by esterifying polyvinyl alcohol with succinic anhydride and then adding glycidyl methacrylate, or a urethane bond Reaction between a polyoxyalkylene segment or a saturated polyester segment, or both, and a urethane prepolymer having an acryloyl group or a methacryloyl group at both terminals or an ethylene-maleic anhydride copolymer and allylamine Polyacrylic acid or maleic acid copolymer such as a reaction product of methyl vinyl ether-maleic anhydride copolymer with 2-hydroxyethyl acrylate or a product obtained by further reacting glycidyl acrylate with the product. A prepolymer.
【００１３】また、末端不飽和基を有する光重合性プレ
ポリマと組み合わせて用いられる光重合性モノマとして
は、従来、紫外線硬化型組成物において、光重合性プレ
ポリマと併用されている光重合性モノマから任意に選択
できる。例えば、アクリル酸やメタクリル酸などの不飽
和カルボン酸叉はそのエステル、アルキルアクリレー
ト、シクロアルキルアクリレート、ハロゲン化アルキル
アクリレート、アルコキシアルキルアクリレート、ヒド
ロキシアルキルアクリレート、アミノアルキルアクリレ
ート、テトラヒドロフルフリルアクリレート、アリルア
クリレート、グリシジルアクリレート、ベンジルアクリ
レート、フェノキシアクリレート叉はメタクリレート
や、アルキレングリコール、ポリオキシアルキレングリ
コールのモノ叉はジアクリレート及びメタクリレート、
また、トリメチロールプロパントリアクリレート及びメ
タクリレート、アクリルアミド、メタクリアミド叉はそ
の誘導体、その他、スチレン、ビニルトルエン、ジビニ
ルベンゼン、Ｎ−ビニルカルバゾール、Ｎ−ビニルピロ
リドンなどが挙げられる。これらの光重合性モノマは単
独で用いてもよいし、２種類以上を組み合わせてもよ
い。また、その配合量は、末端不飽和基を有する光重合
性プレポリマに対し、重量比で２倍以下、好ましくは
０.５〜１.５倍の範囲内で配合される。The photopolymerizable monomer used in combination with the photopolymerizable prepolymer having a terminal unsaturated group may be a photopolymerizable monomer conventionally used in combination with a photopolymerizable prepolymer in an ultraviolet-curable composition. You can choose any. For example, unsaturated carboxylic acids such as acrylic acid and methacrylic acid or esters thereof, alkyl acrylate, cycloalkyl acrylate, halogenated alkyl acrylate, alkoxyalkyl acrylate, hydroxyalkyl acrylate, aminoalkyl acrylate, tetrahydrofurfuryl acrylate, allyl acrylate, Glycidyl acrylate, benzyl acrylate, phenoxy acrylate or methacrylate, alkylene glycol, polyoxyalkylene glycol mono- or diacrylate and methacrylate,
Further, trimethylolpropane triacrylate and methacrylate, acrylamide, methacrylamide or a derivative thereof, and styrene, vinyltoluene, divinylbenzene, N-vinylcarbazole, N-vinylpyrrolidone, and the like can be given. These photopolymerizable monomers may be used alone or in combination of two or more. The compounding amount is 2 times or less, preferably 0.5 to 1.5 times by weight of the photopolymerizable prepolymer having a terminal unsaturated group.
【００１４】さらに、前記光重合性プレポリマ及び光重
合性モノマと共に用いられる光重合開始剤としては、公
知のものの中から任意に選択できる。例えば、ベンゾイ
ンやベンゾインエチルエーテル、ベンゾイン−ｎ−ポロ
ピルエーテル、ベンゾイン−イソプロピルエーテル、ベ
ンゾイン−イソブチルエーテルなどのベンゾインアルキ
ルエーテル類や、２，２−ジメトキシ−２−フェニルア
セトフェノン、ベンゾフェノン、ベンジル、ジアセチ
ル、ジフェニルスルフィド、エオシン、チオニンなどが
挙げられる。これらの光重合開始剤は単独で用いてもよ
いし、２種類以上を組み合わせてもよい。その配合量
は、末端不飽和基を有する光重合性プレポリマと光重合
性モノマの合計量１００重量部に対し、０．１〜１０重
量部の範囲内で配合される。The photopolymerization initiator used together with the photopolymerizable prepolymer and the photopolymerizable monomer can be arbitrarily selected from known ones. For example, benzoin alkyl ethers such as benzoin, benzoin ethyl ether, benzoin-n-propyl ether, benzoin-isopropyl ether, benzoin-isobutyl ether, 2,2-dimethoxy-2-phenylacetophenone, benzophenone, benzyl, diacetyl, Examples include diphenyl sulfide, eosin, and thionin. These photopolymerization initiators may be used alone or in combination of two or more. The compounding amount is 0.1 to 10 parts by weight based on 100 parts by weight of the total of the photopolymerizable prepolymer having a terminal unsaturated group and the photopolymerizable monomer.
【００１５】なお、本発明における紫外線硬化型組成物
には、所望により、熱重合禁止剤、粘着付与剤、粘度調
整剤、老化防止剤、安定剤、着色剤、微粒子充填剤など
を含有させることができる。The UV-curable composition of the present invention may contain, if desired, a thermal polymerization inhibitor, a tackifier, a viscosity modifier, an antioxidant, a stabilizer, a colorant, a fine particle filler and the like. Can be.
【００１６】また、カード部の表裏面及びラベル部の表
面への紫外線硬化型組成物の塗布量は、１〜４０ｇ／ｍ
2、好ましくは１０〜３０ｇ／ｍ2、さらに好ましくは１
５〜２５ｇ／ｍ2の範囲が適当である。そして、その硬
化状態は、紫外線照射量と共に紫外線硬化型組成物の塗
布量の増減により調整してもよく、例えば、ラベル部の
表裏面の紫外線硬化型組成物層は完全硬化状態と不完全
硬化状態とに分かれるため、紫外線硬化型組成物を同じ
種類のものとした場合、紫外線照射条件にもよるが、そ
れぞれの完全硬化状態と不完全硬化状態を効率的に具現
するためには、ラベル部の表面と裏面への塗布量の比率
を１：４〜２：３程度とするのがよい。The amount of the ultraviolet curable composition applied to the front and back surfaces of the card portion and the front surface of the label portion is 1 to 40 g / m 2.
2 , preferably 10 to 30 g / m 2 , more preferably 1 to 30 g / m 2 .
A range of 5 to 25 g / m 2 is appropriate. The curing state may be adjusted by increasing or decreasing the application amount of the ultraviolet-curable composition together with the amount of ultraviolet irradiation.For example, the ultraviolet-curable composition layers on the front and back surfaces of the label portion are completely cured and incompletely cured. When the UV-curable composition is of the same type, it depends on the UV irradiation conditions. The ratio of the amount of coating on the front surface and the back surface is preferably about 1: 4 to 2: 3.
【００１７】本実施例におけるカード部２及びラベル部
３の表裏面の紫外線硬化型組成物は共に同じポリエステ
ルアクリレート系の紫外線硬化型組成物を使用し、その
塗布量は、完全硬化状態の紫外線硬化型組成物層ａの好
適な形成のために、カード部２の表裏面及びラベル部３
の表面に対しては１０ｇ／ｍ2とし、不完全硬化状態の
紫外線硬化型組成物層ｂの好適な形成のために、ラベル
部３の裏面に対しては１５ｇ／ｍ2とした。ただし、塗
布工程の効率化を優先するならば、カード部２及びラベ
ル部３の表裏面への紫外線硬化型組成物の塗布量は同じ
とし、紫外線照射量の増減により硬化状態を調整するの
が好ましい。In the present embodiment, the same ultraviolet curing composition of polyester acrylate is used as the ultraviolet curing composition on the front and back surfaces of the card section 2 and the label section 3. For the preferred formation of the mold composition layer a, the front and back surfaces of the card portion 2 and the label portion 3
10 g / m 2 for the surface of the label portion 3 and 15 g / m 2 for the back surface of the label portion 3 in order to favorably form the ultraviolet-curable composition layer b in an incompletely cured state. However, if the efficiency of the coating process is prioritized, the amount of the UV-curable composition applied to the front and back surfaces of the card unit 2 and the label unit 3 should be the same, and the curing state should be adjusted by increasing or decreasing the amount of UV irradiation. preferable.
【００１８】紫外線硬化型組成物層の完全硬化状態と不
完全硬化状態を具現するためには、紫外線照射条件をそ
れぞれ個別に設定する。例えば、本実施例においては、
所定の紫外線照射装置（高圧水銀灯ランプ２本、ランプ
出力６０〜１２０ｗ／ｃｍ、照射距離１０ｃｍ）を用
い、ライン速度を１０ｍ／分の条件下で、完全硬化状態
のタック性のない紫外線硬化型組成物層ａを施すために
ランプ出力を１２０ｗ／ｃｍに設定し、一方、不完全硬
化状態で任意のタック性を有する紫外線硬化型組成物層
ｂを施すためにランプ出力を６０ｗ／ｃｍに設定してそ
れぞれ紫外線照射を行うことで所望の硬化状態が得られ
た。In order to realize a completely cured state and an incompletely cured state of the ultraviolet-curable composition layer, ultraviolet irradiation conditions are individually set. For example, in this embodiment,
Using a predetermined ultraviolet irradiation device (two high-pressure mercury lamps, lamp output: 60 to 120 w / cm, irradiation distance: 10 cm), at a line speed of 10 m / min, an ultraviolet-curable composition in a completely cured state without tackiness. The lamp power was set to 120 w / cm to apply the material layer a, while the lamp output was set to 60 w / cm to apply the UV-curable composition layer b having an arbitrary tackiness in an incompletely cured state. The desired cured state was obtained by irradiating each with ultraviolet rays.
【００１９】なお、本実施例のカード・ラベル複合体１
の使用法について述べると、ラベル部３は、その裏面の
タック性のある不完全硬化状態の紫外線硬化型組成物層
ｂをもって商品に貼付され、一方、カード部２は、商品
が受取人に配達された後に、控え片（受領証）として切
取線Ｍにてラベル部３から分離され、配達人が持ち帰
り、その後の商品管理システムで利用される。また、カ
ード部２及びラベル部３はタック性のない完全硬化状態
の紫外線硬化型組成物層ａをもって、それぞれの耐久性
が向上されると同時に、所定の印刷４や可変情報５は、
これをもって保護されるため、印刷や印字が擦れなどに
より消失することがない。The card / label composite 1 of the present embodiment
The label section 3 is attached to the product with the tacky and incompletely cured UV-curable composition layer b on the back surface, while the card section 2 is used to deliver the product to the recipient. After that, it is separated from the label unit 3 by a cut-off line M as a reminder (receipt), brought back by the delivery person, and used in the subsequent product management system. The card portion 2 and the label portion 3 have a UV-curable composition layer a in a completely cured state having no tackiness, and their durability is improved.
Since it is protected by this, printing or printing does not disappear due to rubbing or the like.
【００２０】[0020]
【発明の効果】以上述べたように、本発明のカード・ラ
ベル複合体によれば、表裏面に被覆手段を有したカード
と、表面に被覆手段、裏面に粘着手段を有したラベルと
が、基材を同一として分離可能に連接してなるカード・
ラベル複合体が効率的に作成できると共に、当該被覆手
段と粘着手段が共に硬化状態によりタック性の有無を具
点できる紫外線硬化型組成物とすることで、従来のよう
な複雑な製造工程を要せず、さらに、生産時間を短縮で
き、もって、生産性やコスト面などに優れるなどの効果
を泰するものである。As described above, according to the card / label composite of the present invention, the card having the covering means on the front and back surfaces, and the label having the covering means on the front surface and the adhesive means on the back surface, Cards made of the same base material and connected in a separable manner
By using a UV-curable composition in which both the coating means and the adhesive means can provide tackiness depending on the curing state, a complicated manufacturing process as in the related art is required. Without this, the production time can be further shortened, and the effects such as excellent productivity and cost can be achieved.
【図１】本発明のカード・ラベル複合体の表面平面図。FIG. 1 is a top plan view of a card-label composite of the present invention.
【図２】図１のＸ−Ｘ線断面図。FIG. 2 is a sectional view taken along line XX of FIG.
１ カード・ラベル複合体 ２ カード部 ３ ラベル部 ４ 所定の印刷 ５ 可変情報 ６ 剥離紙 ａ タック性のない完全硬化状態の紫外線硬化型組成物
層 ｂ タック性のある不完全硬化状態の紫外線硬化型組成
物層 Ｍ 切取線DESCRIPTION OF SYMBOLS 1 Card / label composite 2 Card part 3 Label part 4 Predetermined printing 5 Variable information 6 Release paper a UV-curable composition layer in a completely cured state without tackiness b UV-curable in a completely cured state with tackiness Composition layer M Cutting line
Claims (1)
ル部からなり、前記カード部の表裏面及び前記ラベル部
の表面にはタック性のない完全硬化状態の紫外線硬化型
組成物層が施されると共に、前記ラベル部の裏面にはタ
ック性のある不完全硬化状態の紫外線硬化型組成物層が
施されてなるカード・ラベル複合体。1. A card part and a label part which are connected via a cut-off line, and a front side and a back side of the card part and a surface of the label part are provided with a UV-curable composition layer in a completely cured state having no tackiness. And a label / label composite in which a tacky incompletely cured ultraviolet-curable composition layer is applied to the back surface of the label portion.