JPH11253718A - Air filter - Google Patents
Air filterInfo
- Publication number
- JPH11253718A JPH11253718A JP1216699A JP1216699A JPH11253718A JP H11253718 A JPH11253718 A JP H11253718A JP 1216699 A JP1216699 A JP 1216699A JP 1216699 A JP1216699 A JP 1216699A JP H11253718 A JPH11253718 A JP H11253718A
- Authority
- JP
- Japan
- Prior art keywords
- filter
- air filter
- dust
- woven fabric
- nonwoven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、エアーフィルタ
ー、たとえば集塵機用フィルター等において粉塵との衝
突、あるいはフィルター内部支持体である金網等により
擦過して発生するフィルター基材の毛羽立ちを抑制し、
かつパルスジェット後の粉塵離脱性の優れたエアーフィ
ルターに関するものである。The present invention relates to an air filter, for example, a filter for a dust collector, which suppresses fluffing of a filter substrate which is generated by rubbing with dust or rubbing by a wire mesh as a filter internal support,
The present invention also relates to an air filter having excellent dust release properties after pulse jet.
【０００２】[0002]
【従来の技術】エアーフィルター、たとえば集塵機用フ
ィルター等は、金属の研削工場や粉塵が多く発生する工
場での労働環境の改善に、比較的高価な有価物の回収に
と幅広く用いられている。2. Description of the Related Art Air filters, such as filters for dust collectors, are widely used for improving the working environment in metal grinding factories and factories that generate a lot of dust and for collecting relatively expensive valuable materials.
【０００３】これらの用途において、大部分がフィルタ
ー基材に織物、ニードルパンチした不織布を用いたバッ
グフィルターが使用されているが、近年、集塵機の高速
化・低負荷化および小型化への動きに伴い、フィルター
のタイプも、取替えや取付けが容易で、かつコンパクト
なカートリッジフィルターへ転向されつつある。[0003] In these applications, a bag filter using a woven fabric or a needle-punched non-woven fabric as a filter base material is mostly used. In recent years, however, there has been a movement to increase the speed, reduce the load and reduce the size of dust collectors. Accordingly, the type of filter is being converted to a compact cartridge filter that can be easily replaced or mounted.
【０００４】該カートリッジフィルターに使用されるフ
ィルター基材は、一般にプリーツ加工を施し、フィルタ
ーユニット中での表面積を大きくして濾過機能を高めた
ものが使用される。[0004] The filter base material used for the cartridge filter is generally pleated to increase the surface area in the filter unit to enhance the filtration function.
【０００５】かかるフィルター基材には、プリーツ加工
が可能で、そのために不織布を部分的に圧着し、ある程
度の硬さや強力を持たせたり、濾過性能を満足させるた
めに、不織布の見掛密度を高めたり、目付の高い不織布
が使用されている。かかるエアーフィルター用不織布と
して、一部共重合ポリエステル成分を含むポリエステル
連続フィラメントからなる部分的に圧着した不織布を使
用することが知られている。[0005] Such a filter base material can be pleated. For this reason, the nonwoven fabric is partially pressed to give a certain degree of hardness and strength, and the apparent density of the nonwoven fabric is reduced in order to satisfy the filtration performance. A nonwoven fabric with a high or high basis weight is used. It is known to use, as such a nonwoven fabric for an air filter, a partially pressed nonwoven fabric made of polyester continuous filaments partially containing a copolymerized polyester component.
【０００６】この不織布は、通常、紡糸口金から溶融紡
出された連続フィラメントをエアーサッカー等の手段に
より吸引延伸し、移動する網状体の上に開繊体積させ連
続フィラメントウェブとし、次いで同ウェブを部分的に
熱圧着するという方法で得られている。[0006] This non-woven fabric is usually drawn by drawing a continuous filament melt-spun from a spinneret by means of air sucker or the like, and is spread on a moving mesh body to form a continuous filament web. It is obtained by a method of partially thermocompression bonding.
【０００７】[0007]
【発明が解決しようとする課題】ところが、このような
従来のエアーフィルター用不織布では、集塵機用フィル
ター等において、粉塵粒径大、高濃度、高流速等の厳し
い濾過条件下で使用された場合、粉塵がフィルター基材
と衝突し、毛羽立ちが発生することがあった。また、該
カートリッジフィルターの内部にはフィルター基材を支
持するための円筒状の金網の型枠が使用されているが、
この金網とフィルター基材の擦過によって、毛羽立ちが
しばしば発生することがあった。However, in such a conventional nonwoven fabric for an air filter, when used under severe filtering conditions such as a large dust particle size, a high concentration, and a high flow rate in a filter for a dust collector, etc. In some cases, dust collided with the filter substrate and fluff was generated. Further, a cylindrical wire mesh formwork for supporting the filter base material is used inside the cartridge filter,
Flushing often occurred due to the rubbing between the wire mesh and the filter substrate.
【０００８】また、一般にこのような集塵機用フィルタ
ー用途においては、フィルター基材の表面上に捕集され
た粉塵を逆流エアーにより間欠的に払い落としながら使
用するパルスジェット方式が、フィルター寿命の延長を
図るために採用されているが、その場合、前記該毛羽立
ち部分に粉塵が絡み付き、パルスジェット後の粉塵離脱
性が悪化し、さらにはフィルターの寿命が低下してしま
うという問題が発生していた。In general, in such a filter application for a dust collector, a pulse jet method in which dust collected on the surface of a filter substrate is intermittently blown off by backflow air is used to extend the life of the filter. However, in this case, dust is entangled with the fluffed portion, and the dust releasability after the pulse jet is deteriorated, and the life of the filter is shortened.
【０００９】本発明は、かかる問題を解決し、エアー濾
過時のフィルター基材の毛羽立ちが少なく、かつパルス
ジェット後の粉塵離脱性に優れた、集塵機用フィルター
としても十分な性能を持った、高寿命のエアーフィルタ
ーを提供することを目的とするものである。The present invention solves such a problem, and has a high performance as a filter for a dust collector, which has less fluffing of a filter substrate during air filtration, and has excellent dust release properties after pulse jet. It is intended to provide a long-life air filter.
【００１０】[0010]
【課題を解決するための手段】かかる目的を達成する本
発明のエアーフィルターは、部分的に圧着されたフィラ
メント不織布よりなるエアーフィルターであって、該不
織布は、少なくとも一方の表面に、ＪＩＳ Ｂ０６０１
に準じて求められる平均くぼみ深さが６０μｍ以下であ
る圧着くぼみ部を多数有し、かつ、該圧着くぼみ部の存
在する面側をフィルターの捕集面側にしてプリーツ賦型
されてなることを特徴とするエアーフィルターである。The air filter of the present invention that achieves the above object is an air filter made of a partially non-woven filament non-woven fabric, wherein the non-woven fabric is provided on at least one surface with JIS B0601.
Having a large number of crimped dents having an average dent depth of 60 μm or less, and pleated with the surface on which the crimped dents are present as the collecting surface of the filter. It is a characteristic air filter.
【００１１】また、かかる本発明のエアーフィルターに
おいて、好ましくは、圧着くぼみ部が、不織布の単位面
積当り１０〜５０個／ｃｍ2 存在することを特徴とする
ものである。Further, in the air filter of the present invention, preferably, the pressure-bonding concave portion is present in an amount of 10 to 50 / cm 2 per unit area of the nonwoven fabric.
【００１２】[0012]
【発明の実施の形態】本発明は、エアーフィルターとし
て使用する不織布の表面の圧着部の深さが、エアー濾過
の際の粉塵との衝突、あるいはフィルター内部支持体で
ある金網等により擦過して発生するフィルター基材の毛
羽立ちに大きく影響を与えるという知見に基づき得られ
たものであり、具体的には、該不織布の圧着部の形状、
構造を特定なものにすると、粉塵、あるいはフィルター
内部支持体である金網等と、フィルター基材との摩擦抵
抗が大きく低減し、それによって毛羽立ちが抑制され、
かつ粉塵離脱性を向上させることができるという知見に
よるものである。BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, the depth of a pressure-bonded portion on the surface of a nonwoven fabric used as an air filter is determined by collision with dust at the time of air filtration, or by rubbing with a wire mesh or the like which is a support inside the filter. It has been obtained based on the finding that it greatly affects the fluffing of the filter substrate that occurs, and specifically, the shape of the crimped portion of the nonwoven fabric,
If the structure is specific, the frictional resistance between the dust, or the wire mesh, etc., which is the internal support of the filter, and the filter base material is greatly reduced, thereby suppressing fluffing,
Further, it is based on the finding that the dust release property can be improved.
【００１３】本発明者らの知見によれば、該不織布は、
部分的に圧着されたフィラメント不織布よりなるもので
あって、かつ、少なくとも一方の表面に、ＪＩＳ Ｂ０
６０１に準じて求められる平均くぼみ深さが６０μｍ以
下である圧着くぼみ部を多数有するとともに、該圧着く
ぼみ部の存在する面側をフィルターの捕集面側にしてプ
リーツ賦型がされることが重要である。According to the findings of the present inventors, the nonwoven fabric is
It is made of a filament non-woven fabric that has been partially pressed and has at least one surface on which JIS B0
It is important to have a large number of press-fitting recesses having an average recess depth of 60 μm or less according to 601 and to perform pleating by setting the surface on which the press-fitting recesses exist to the collecting surface side of the filter. It is.
【００１４】すなわち、かかる不織布の該圧着部のくぼ
みの深さと、フィルター基材の毛羽立ちとの関係を検討
したところ、該くぼみの平均深さがフィルター基材の毛
羽立ちと関係が深く、さらには、ＪＩＳ Ｂ０６０１表
面粗さ規格に準じて求められる算術平均粗さ（Ｒａ）、
たとえば、一般に、金属等の表面粗さを確認するために
使用される株式会社小坂研究所製の表面粗さ計ＳＥ−４
０Ｃ（ＪＩＳ Ｂ０６５１触針式表面粗さ測定器の規格
に基づく）を用いて測定することができるくぼみの平均
深さが、密接に関係する。That is, when the relationship between the depth of the depression of the press-bonded portion of such a nonwoven fabric and the fluffing of the filter substrate was examined, the average depth of the depression was closely related to the fluffing of the filter substrate. Arithmetic average roughness (Ra) determined according to JIS B0601 surface roughness standard,
For example, a surface roughness meter SE-4 manufactured by Kosaka Laboratory Co., Ltd., which is generally used to confirm the surface roughness of a metal or the like.
The average depth of the depression, which can be measured using OC (based on the standard of JIS B0651 stylus type surface roughness measuring instrument), is closely related.
【００１５】すなわち、不織布のかかる圧着部のくぼみ
の平均深さを６０μｍ以下とすることにより、従来の不
織布に比べ大幅にフィルター基材の毛羽立ちを抑制する
ことができることを見出だしたものであり、圧着部のく
ぼみの平均深さが６０μｍを越すと、フィルター基材の
毛羽立ちが幾何級数的に大きくなっていき、エアーフィ
ルターとして適さなくなる。また、該くぼみの平均深さ
を小さくすることは、不織布表面の凹凸が小さくなるこ
とであり、粉塵あるいはフィルター支持体である金網等
と、フィルター基材との摩擦抵抗が大きく低減されるこ
とを意味する。また、フィルター基材の毛羽立ちが抑制
されることから、該毛羽立ちへの粉塵の絡み付きも低減
され、パルスジェット後の粉塵離脱性が向上し、更には
寿命性能を向上させることができるのである。また、不
織布は、毛羽立ちの本質的な少なさから、フィラメント
不織布であることが重要である。That is, it has been found that by setting the average depth of the depressions of the press-bonded portion of the nonwoven fabric to 60 μm or less, the fluffing of the filter base material can be significantly suppressed as compared with the conventional nonwoven fabric. If the average depth of the depressions in the crimping portion exceeds 60 μm, the fluffing of the filter base material increases exponentially, making it unsuitable as an air filter. Further, reducing the average depth of the depressions means that the unevenness of the surface of the nonwoven fabric is reduced, and that the frictional resistance between the dust or the wire mesh as a filter support and the filter base material is greatly reduced. means. Further, since the fluffing of the filter substrate is suppressed, the entanglement of dust with the fluffing is reduced, the dust releasability after pulse jet is improved, and the life performance can be further improved. Further, it is important that the nonwoven fabric is a filament nonwoven fabric because of the inherently low fuzziness.
【００１６】本発明の基本思想は、エアーフィルターと
して使用する不織布表面の圧着部の深さを浅くし、粉塵
との衝突あるいはフィルター支持体である金網等との擦
過により発生するフィルター基材の毛羽立ちを抑制し、
かつパルスジェット後の粉塵離脱性を向上させることに
ある。従って、該圧着くぼみ部の存在する面側をフィル
ターの捕集面側にしてプリーツ賦型がされるものであ
る。The basic idea of the present invention is to reduce the depth of the pressure-bonded portion on the surface of the non-woven fabric used as an air filter, and to make the filter substrate fluff generated by collision with dust or rubbing with a wire mesh or the like as a filter support. To suppress
Another object of the present invention is to improve dust releasability after pulse jet. Therefore, pleating is performed by setting the surface on which the crimping concave portion exists to the collecting surface of the filter.
【００１７】本発明で言う部分的に圧着されたくぼみ部
を多数有する不織布とは、不織布を構成している連続フ
ィラメント間が熱と圧力によって融着し、部分的にくぼ
みがあること、すなわち、フィラメント密度が高くなっ
た部分が点在するものである。In the present invention, the nonwoven fabric having a large number of partially press-fitted hollow portions means that continuous filaments constituting the nonwoven fabric are fused by heat and pressure, and there is a partial hollow. The portion where the filament density is high is scattered.
【００１８】このように、部分的に圧着させるために
は、通常、加熱した一対のエンボスロールが使用される
が、本発明においては、エンボスロールの形態、組合わ
せ等について特に限定されるものではない。As described above, a pair of heated embossing rolls is usually used for partial pressure bonding. However, in the present invention, the form and combination of the embossing rolls are not particularly limited. Absent.
【００１９】また、圧着部の不織布全体の面積に占める
割合も、特に限定されるものではないが、より少ない方
が好ましく、たとえば、好ましくは１０〜３０％、さら
に好ましくは１５〜２０％の範囲で占めるのがよい。具
体的には、好ましくは１０〜５０個／ｃｍ2 、さらに好
ましくは２５〜３５個／ｃｍ2 の範囲がよい。 本発明の
フィルター用不織布は、目付１００ｇ／ｍ2 以上であ
り、また、剛軟度が５００ｍｇ以上であるものを使用す
るのが好ましく、さらにこれらの両方の要件を満足する
ものが特に好ましい。これは、該フィルター用不織布が
プリーツ加工を施し使用されることから、ある程度の硬
さや強力を持たすのが好ましく、目付および剛軟度のい
ずれかが外れた場合には、プリーツ加工が困難であるば
かりか、プリーツ形態を保持することも困難なものとな
るのである。また、フィルター性能においても満足でき
るものが得られにくくなる傾向がでてくるものである。Further, the press-fitted portion occupies the entire area of the nonwoven fabric.
The ratio is not particularly limited, but is smaller.
Preferably, for example, preferably 10 to 30%, more preferably
Preferably, it should be occupied in the range of 15 to 20%. Ingredient
Physically, preferably 10-50 / cmTwo, Even better
Preferably 25 to 35 pieces / cmTwoRange is good. Of the present invention
Non-woven fabric for filter has a basis weight of 100 g / mTwoIs over
Use a material with a stiffness of 500 mg or more.
Preferably satisfy both of these requirements
Are particularly preferred. This is because the nonwoven fabric for the filter
Because it is pleated and used
It is preferable to have pod strength, low weight and softness
If the slippage is lost, if pleating is difficult
It is also difficult to maintain the pleat form
Because Also satisfied with the filter performance
However, there is a tendency that products cannot be easily obtained.
【００２０】本発明のフィルター用不織布は、ポリエス
テル系フィラメントで構成されているのが好ましく、特
に好ましくは、ポリエステル系複合フィラメント、それ
も芯鞘構造を有する複合フィラメントで構成されている
ものが好ましい。かかる複合フィラメントとしては、鞘
成分が芯成分に対し２０℃以上低い融点を持つ共重合ポ
リエステルからなることが、目付の高い不織布を得る上
で非常に好ましい。更に、芯鞘構造とは、一般的な同心
円が最も好ましいが、偏芯円形、異型断面型としてもよ
い。また、かかるポリエステル系フィラメントに酸化チ
タン、カーボンブラック等の添加剤を含んでもよいこと
は言うまでもない。本発明において、共重合ポリエステ
ル成分とは、アジピン酸、イソフタル酸、等を共重合し
たポリエステルであり、酸化チタン、カーボンブラック
等の添加剤を含んでもよいことは言うまでもない。The nonwoven fabric for a filter of the present invention is preferably composed of polyester-based filaments, particularly preferably polyester-based composite filaments, which are also composed of composite filaments having a core-sheath structure. For such a composite filament, it is very preferable that the sheath component is made of a copolymer polyester having a melting point lower than that of the core component by 20 ° C. or more in order to obtain a nonwoven fabric having a high basis weight. Further, the core-sheath structure is most preferably a general concentric circle, but may be an eccentric circular shape or an irregular cross-sectional shape. Needless to say, such polyester-based filaments may contain additives such as titanium oxide and carbon black. In the present invention, the copolymerized polyester component is a polyester obtained by copolymerizing adipic acid, isophthalic acid, and the like, and it is needless to say that additives such as titanium oxide and carbon black may be included.
【００２１】本発明においては、前述のとおり、かかる
不織布を圧着くぼみ部の存在する面側をフィルター捕集
面側にしてプリーツ賦型されるが、プリーツの加工方法
は特に限定されないが、例えば、ロータリー式プリーツ
加工機などを用いることができる。In the present invention, as described above, such a nonwoven fabric is pleated by setting the surface on which the pressure-bonded recessed portion is present on the filter collecting surface side. The method of processing the pleats is not particularly limited. A rotary pleating machine or the like can be used.
【００２２】本発明にかかるエアーフィルターを、たと
えば、集塵機用フィルター装置に使用すると、粉塵との
衝突、あるいはフィルター内部支持体である金網等との
擦過により発生するフィルター基材の毛羽立ちを抑制
し、かつパルスジェット後の粉塵離脱性を向上させるこ
とにより、高寿命のエアーフィルター装置を提供するこ
とができるものである。When the air filter according to the present invention is used, for example, in a filter device for a dust collector, it suppresses fluffing of a filter substrate caused by collision with dust or rubbing with a wire mesh as a filter internal support, Further, it is possible to provide a long-life air filter device by improving the dust separation property after the pulse jet.
【００２３】[0023]
【実施例】次に、実施例に基づいて本発明を具体的に説
明する。なお、実施例における各種特性は、次の方法に
より測定した。Next, the present invention will be specifically described based on examples. Various characteristics in the examples were measured by the following methods.
【００２４】くぼみの平均深さ：くぼみの平均深さは、
表面粗さ測定器（株式会社小坂研究所製の表面粗さ計Ｓ
Ｅー４０Ｃ：ＪＩＳ Ｂ０６５１触針式表面粗さ測定器
の規格に基づく）を使用して、ＪＩＳーＢ０６０１表面
粗さ規格に準じて求められる算術平均粗さ（Ｒａ）を表
す。算術平均粗さは、カットオフ値２．５ｍｍ、評価長
さ８ｍｍで測定した。毛羽立ち特性：テーバ形磨耗試験
機により、ＪＩＳ Ｌ−１０９６に準じた、摩耗輪、荷
重条件で１００回磨耗後、外観を観察した。Average depth of depression: The average depth of depression is
Surface roughness measuring device (Surface roughness meter S manufactured by Kosaka Laboratory Co., Ltd.)
E-40C: based on the standard of JIS B0651 stylus type surface roughness measuring device), and the arithmetic average roughness (Ra) determined according to JIS-B0601 surface roughness standard. The arithmetic average roughness was measured at a cutoff value of 2.5 mm and an evaluation length of 8 mm. Fluffiness: The appearance was observed with a Taber abrasion tester after 100 times of wear under a worn wheel and load conditions according to JIS L-1096.
【００２５】外観変化は以下のように定義し、判定を行
った。The change in appearance was defined as follows and evaluated.
【００２６】Ａ級 ： まったく毛羽立ちがない。Class A: No fluff at all.
【００２７】Ｂ級 ： 少し毛羽立ちはあるが目立たな
い。Class B: slightly fluffy but not noticeable.
【００２８】Ｃ級 ： 毛羽立ちが目立つ 目付：ＪＩＳ Ｌ１０９６に準じて求めた。Class C: Fluff is noticeable Weight: Determined according to JIS L1096.
【００２９】剛軟度：ＪＩＳ Ｌ１０９６ ガーレ法に
準じて求めた。Softness: Determined according to the JIS L1096 Gurley method.
【００３０】エアーフィルター性能：不織布をロータリ
ー式プリーツ加工機で表側をフィルター捕集面側にして
プリーツ賦型をしてエアーフィルターを作成して、粉塵
捕集−粉塵払落（パルスジェット）の繰返しテストを、
エアーフィルターモデル装置を用いて、下記条件にて評
価を行った。Air filter performance: An air filter is prepared by pleating the non-woven fabric with the rotary side pleating machine with the front side facing the filter collecting surface side to create an air filter, and repeating dust collection and dust removal (pulse jet) Test
Evaluation was performed under the following conditions using an air filter model device.
【００３１】 実施例１、２ 融点が２６０℃のポリエチレンテレフタレートを芯成
分、融点が２３０℃のイソフタル酸共重合ポリエステル
を鞘成分とし、芯成分と鞘成分の重量比をそれぞれ、８
５：１５、７０：３０とした複合連続フィラメントを単
糸繊度２ｄで溶融紡出し、空気圧により開繊した後、移
動するネット上に堆積させ、一対の加熱エンボスロール
を使用し、表面温度２１０℃、線圧を６０ｋｇ／ｃｍで
圧着し、目付２６０ｇ／ｍ2 、厚さ０．６ｍｍのフィラ
メント不織布を得た。これら不織布の表面のくぼみの平
均深さは、それぞれ表／裏＝２５／２０μｍ、４５／４
０μｍであった。[0031] Examples 1 and 2 Polyethylene terephthalate having a melting point of 260 ° C. was used as a core component, and isophthalic acid copolymerized polyester having a melting point of 230 ° C. was used as a sheath component.
5:15, 70:30 composite continuous filaments were melt spun at a single yarn fineness of 2d, opened by air pressure, then deposited on a moving net, using a pair of heated embossing rolls, surface temperature 210 ° C. The filament was pressed at a linear pressure of 60 kg / cm to obtain a filament nonwoven fabric having a basis weight of 260 g / m 2 and a thickness of 0.6 mm. The average depth of the depressions on the surface of these nonwoven fabrics was front / back = 25/20 μm and 45/4, respectively.
It was 0 μm.
【００３２】それぞれより深いくぼみがある側を捕集面
とし、プリーツ加工してフィルター性能を評価した。Each side having a deeper hollow was used as a collecting surface, and was pleated to evaluate the filter performance.
【００３３】毛羽立ち特性は、両水準ともＡ級と良好で
あり、より深いくぼみのある表面を濾過面として評価し
たエアーフィルター性能においても、払落２００回後も
さらに使用可能であり、満足のいく高寿命性能が得られ
た。結果を図１と表１に示す。The fluffing property is as good as class A at both levels, and the air filter performance evaluated with the surface having a deeper depression as a filtration surface can be further used even after 200 times of dropping, which is satisfactory. High life performance was obtained. The results are shown in FIG.
【００３４】比較例１ 融点が２６０℃のポリエチレンテレフタレートを芯成
分、融点が２３０℃のイソフタル酸共重合ポリエステル
を鞘成分とし、芯成分と鞘成分の重量比を５０：５０と
した複合連続フィラメントを単糸繊度２ｄで溶融紡出
し、空気圧により開繊した後、移動するネット上に体積
させ、一対の加熱エンボスロールを使用し、表面温度を
２１０℃、線圧を６０ｋｇ／ｃｍで圧着し、目付２６０
ｇ／ｍ2 、厚さ０．６ｍｍの不織布を得た。この不織布
表面のくぼみの平均深さは表／裏＝７０／６５μｍであ
った。Comparative Example 1 A composite continuous filament having a core component of polyethylene terephthalate having a melting point of 260 ° C., a sheath component of isophthalic acid copolymerized polyester having a melting point of 230 ° C., and a weight ratio of the core component and the sheath component of 50:50 was used. After melt-spun with a single-filament fineness of 2d and opened by air pressure, the volume is put on a moving net, and a pair of heated embossing rolls is used to press-bond at a surface temperature of 210 ° C. and a linear pressure of 60 kg / cm. 260
g / m 2, to obtain a thickness of 0.6mm of the nonwoven fabric. The average depth of the depressions on the surface of the nonwoven fabric was front / back = 70/65 μm.
【００３５】毛羽立ち特性は、Ｃ級と実施例１、２品に
比べて悪く、また表を濾過面として評価したエアーフィ
ルター性能評価においても、払落約１５０回で使用限界
に達し、満足のいくエアーフィルター寿命が得られなか
った。結果を図１、表１に示す。The fluffing property is worse than that of the C class and the products of Examples 1 and 2, and in the air filter performance evaluation using the table as a filtration surface, the usage limit is reached after about 150 drops, and it is satisfactory. The air filter life was not obtained. The results are shown in FIG.
【００３６】[0036]
【表１】 [Table 1]
【００３７】[0037]
【発明の効果】本発明のエアーフィルターによれば、例
えば、集塵機用フィルター等において、粉塵との衝突、
あるいはフィルター内部支持体である金網等により擦過
して発生するフィルター基材の毛羽立ちを抑制し得るも
のであり、かつパルスジェット後の粉塵離脱性を向上さ
せ得るものであり、高寿命のエアーフィルターを提供す
ることができる。According to the air filter of the present invention, for example, in a dust collector filter or the like, collision with dust,
Alternatively, it can suppress fluffing of the filter base material generated by rubbing with a wire mesh or the like which is a filter internal support, and can improve dust release property after pulse jet, and has a long life air filter. Can be provided.
【図１】図１は、実施例、比較例における粉塵負荷量と
払落回数との関係例を示すグラフである。FIG. 1 is a graph showing an example of a relationship between a dust load amount and a number of removal times in Examples and Comparative Examples.
Claims (2)
りなるエアーフィルターであって、該不織布は、少なく
とも一方の表面に、ＪＩＳ Ｂ０６０１に準じて求めら
れる平均くぼみ深さが６０μｍ以下である圧着くぼみ部
を多数有し、かつ、該圧着くぼみ部の存在する面側をフ
ィルターの捕集面側にしてプリーツ賦型されてなること
を特徴とするエアーフィルター。1. An air filter comprising a filament non-woven fabric partially press-bonded, wherein said non-woven fabric has at least one surface having a pressure-recessed portion having an average depression depth of 60 μm or less determined according to JIS B0601. An air filter characterized in that the air filter is pleat-shaped with the surface on which the pressure-recessed recessed portion is present as the collecting surface of the filter.
〜５０個／ｃｍ2 存在することを特徴とするエアーフィ
ルター。2. The non-woven fabric according to claim 1, wherein the pressure-recessed dent portion is 10
An air filter characterized by the presence of up to 50 / cm 2 .