JPH11229211A - Gloves - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide new gloves having antimicrobial property and deodorizing property, preventing roughened skin, or the like, of hands of a user and excellent in hand care effect. SOLUTION: The gloves are equipped with at least monolayer rubber layer or resin layer and contain a vegetable extract in at least either one layer of the rubber layer or the resin layer. The vegetable extract is extracted from at least one kind of material selected from the group comprising aloe, peach, peach leaf, Angelicae Radix, Glycyrrhizae Radix, citron, Houttuynia cordata Thunberg, rice bran, olive, beefsteak plant leaf, mugwort, coconut and seaweeds.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は手袋に関し、より詳
しくは、抗菌性、脱臭性等を有すると共に、手荒れを防
止する、ハンドケア効果に優れた手袋に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to gloves, and more particularly, to gloves having antibacterial properties, deodorizing properties, etc., and preventing hand roughness and having an excellent hand care effect.

【０００２】[0002]

【従来の技術】従来より、家庭ないし医療分野で幅広く
使用される手袋としては、ゴムまたは樹脂からなる層に
て形成されたタイプ（アンサポートタイプ）や、薄い布
性の手袋体の表面に、上記ゴムまたは樹脂の層を少なく
とも一層、被覆して形成されたタイプ（サポートタイ
プ）などが知られている。2. Description of the Related Art Conventionally, gloves widely used in the home or medical fields include a type formed of a layer made of rubber or resin (unsupported type) and a thin cloth glove body. A type (support type) formed by coating at least one layer of the rubber or resin is known.

【０００３】しかしながら、これらの手袋は、一般に、
生産性や製造コストという点が重視されているので、使
用者の手の大きさや形状が考慮されておらず、一定の形
状を有するものを大量に製造する工程が採用されてい
る。また最近では、使用者の手にぴったりフィットし
て、細かい作業を良好に行うために、延伸性フィルムを
使用した手袋が提案されている（特開平５−２４７７０
４号公報など）。[0003] However, these gloves are generally
Since importance is placed on productivity and manufacturing cost, the size and shape of the user's hand are not taken into account, and a process of manufacturing a large number of products having a certain shape is adopted. Recently, a glove using a stretchable film has been proposed in order to fit the user's hand and perform fine work well (Japanese Patent Application Laid-Open No. H5-24770).
No. 4 publication).

【０００４】しかしながら、前述した手袋、とくに上記
公報に開示の手袋においては、装着者の手と手袋とのフ
ィット性が高まる反面、手袋の通気性が悪くなるために
手に装着した際に発汗しやすく、手袋内部においては発
汗に伴って有害な細菌、ウイルス、カビなどが繁殖しや
すい環境が作られて、細菌などによる、使用者の手に肌
荒れが生じたり、皮膚病などが発症したりする問題があ
った。[0004] However, in the above-mentioned gloves, especially the gloves disclosed in the above-mentioned gazettes, while the fit between the gloves of the wearer and the gloves is improved, the gloves have poor air permeability and thus sweat when worn on the gloves. It is easy to cause harmful bacteria, viruses, molds, etc. to proliferate inside the gloves due to sweating, and the bacteria may cause rough skin on the user's hands or cause skin diseases etc. There was a problem.

【０００５】また、使用後に手袋を長期間放置すると、
作業時の発汗に起因した悪臭が発生して、その後の使用
者に不快感を起こさせる原因にもなっていた。そこで、
上記に開示された手袋に、抗菌性、抗カビ性、防臭性、
芳香性などを付与するために、手袋の表面に抗菌剤、抗
カビ剤、脱臭剤、芳香剤などの薬剤を塗布したり、ある
いは手袋の素材中に前記抗菌剤などの薬剤を含有させて
製造した手袋が提案されている。かかる構成の手袋によ
り、上述した手袋における細菌、カビ、悪臭の発生を防
止することができる。If the gloves are left for a long time after use,
An unpleasant odor due to sweating during the operation was generated, which also caused discomfort to the subsequent user. Therefore,
Gloves disclosed above, antibacterial, antifungal, deodorant,
Manufactured by applying agents such as antibacterial agents, antifungal agents, deodorants, fragrances, etc. to the surface of gloves, or by including agents such as the aforementioned antibacterial agents in the glove material to impart fragrance etc. Gloves have been proposed. With the glove having such a configuration, it is possible to prevent the occurrence of bacteria, mold, and odor in the glove described above.

【０００６】[0006]

【発明が解決しようとする課題】しかしながら、前記公
報に開示の手袋に、通常の抗菌剤、抗カビ剤、芳香剤な
どの薬剤、とくに、これらの薬剤として合成薬剤が使用
された場合には、使用者の手に対する考慮が不足してい
るため、使用者によっては、上記薬剤による薬物アレル
ギーを引き起こすなどの副作用の発生が懸念される。However, when gloves disclosed in the above publication are used with ordinary drugs such as antibacterial agents, antifungal agents, and fragrances, especially synthetic drugs as these agents, Due to the lack of consideration for the hands of the user, there is a concern that some of the above-mentioned drugs may cause side effects such as drug allergy.

【０００７】そこで、本発明の目的は、抗菌性や脱臭性
などを有すると共に、使用者の手の肌荒れなどを防止す
る、ハンドケア効果に優れた新規な手袋を提供すること
である。Accordingly, an object of the present invention is to provide a novel glove having an antibacterial property, a deodorizing property and the like, and an excellent hand care effect which prevents roughening of a user's hand and the like.

【０００８】[0008]

【課題を解決するための手段】上記課題を解決するため
の、本発明の手袋は、少なくとも一層のゴム層または樹
脂層を備えた手袋であって、前記ゴム層または樹脂層の
少なくとも一層に植物性エキスを含有させたことを特徴
とするものである。上記構成により得られる手袋は、手
袋の本体、すなわちゴム層または樹脂層中にに含まれた
植物性エキスが、手袋への抗菌性や脱臭性などを付与す
ると共に、使用者の手肌に潤い感、すべすべ感、つるつ
る感をもたせて手荒れを防止し、使用者のハンドケア効
果を高めることができる。According to the present invention, there is provided a glove having at least one rubber layer or resin layer, wherein at least one of the rubber layer and the resin layer has a plant. It is characterized by containing a sexual extract. In the glove obtained by the above-described structure, the vegetable extract contained in the main body of the glove, that is, the rubber layer or the resin layer, imparts antibacterial properties and deodorization properties to the glove and moisturizes the user's hand skin. It gives a feeling of smoothness, smoothness, and smoothness to prevent rough hands and enhance the effect of hand care for the user.

【０００９】特に本発明では、前記植物性エキスとし
て、アロエ、桃、桃の葉、トウキ末、甘草、柚子、ドク
ダミ、米ヌカ、オリーブ、シソの葉、ヨモギ、椰子の実
および海草からなる群より選ばれる少なくとも１種から
抽出されるエキスを使用するのが好ましい。また本発明
では、手袋の製造工程の簡素化ならびに品質の向上を考
慮すると、前記ゴム層をゴムラテックスから製造するの
が好適である。In the present invention, in particular, the above-mentioned plant extracts include aloe, peach, peach leaves, powder of touki, licorice, citron, dokudami, rice bran, olive, perilla leaves, mugwort, coconut and seaweed. It is preferable to use an extract extracted from at least one selected from the following. In the present invention, it is preferable to manufacture the rubber layer from rubber latex in consideration of simplification of a glove manufacturing process and improvement of quality.

【００１０】[0010]

【発明の実施の形態】以下に、本発明を説明する。本発
明の手袋は、ゴム層または樹脂層の少なくとも一層に、
植物性エキスを含有したものである。上記植物性エキス
としては、抗菌性や芳香性などを有し、かつ手肌にしっ
とり感や潤い感などを付与する植物エキスなら特に制限
はなく、従来より食品、生薬などで知られている公知の
植物から抽出されるエキスがあげられるが、とりわけ本
発明では、アロエ、桃、桃の葉、トウキ末、甘草、柚
子、ドクダミ、米ヌカ、オリーブ、シソの葉、ヨモギ、
椰子の実および海草からなる群より選ばれる少なくとも
１種から抽出されるエキスを使用するのが好ましい。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below. The glove of the present invention, at least one of the rubber layer or the resin layer,
It contains plant extracts. The plant extract is not particularly limited as long as it has antibacterial properties, aromatic properties, and the like, and imparts a moist feeling or a moist feeling to hand skin, and is conventionally known as a food, a crude drug and the like. Among the extracts extracted from the plant, aloe, peach, peach leaves, peach powder, licorice, citron, citron, dokudami, rice bran, olives, perilla leaves, mugwort,
It is preferable to use an extract extracted from at least one selected from the group consisting of coconut and seaweed.

【００１１】かかる植物性エキスは、(i) 人体に対して
高い安全性を有する、(ii)天然に存在する植物から抽出
されるエキスであるから、安価に、かつ容易に入手する
ことができる、等の利点を有するものである。なお、本
発明で使用する植物性エキスは、植物の産地、抽出方
法、使用形態、成分組成等に特に限定はない。[0011] Since such a plant extract is (i) an extract having high safety to the human body and (ii) an extract extracted from a naturally occurring plant, it can be obtained at low cost and easily. , Etc. The plant extract used in the present invention is not particularly limited in terms of plant production area, extraction method, use form, component composition, and the like.

【００１２】上記植物性エキスの配合量は、ゴム層また
は樹脂層の総重量に対して０．１〜１０重量％、好まし
くは３．０〜５．０重量％である。植物性エキスの配合
量が上記範囲未満の場合には、抗菌剤や抗カビ剤などの
薬剤を手袋に配合した際に生じる、肌荒れやアレルギー
反応を防止する効果を奏しない。一方、植物性エキスの
配合量が上記範囲を超えた場合には、コストアップにつ
ながる。The amount of the vegetable extract is 0.1 to 10% by weight, preferably 3.0 to 5.0% by weight, based on the total weight of the rubber layer or the resin layer. When the amount of the plant extract is less than the above range, the effect of preventing rough skin and allergic reaction caused when a drug such as an antibacterial agent or an antifungal agent is added to gloves is not exhibited. On the other hand, if the amount of the vegetable extract exceeds the above range, the cost will increase.

【００１３】また従来の手袋と同様に、本発明の手袋に
上記抗菌剤等を含有させて使用してもよい。その場合に
は、植物性エキス自体が抗菌剤等の役割を発揮するの
で、従来の手袋を使用した場合に比べて、少ない薬剤の
含有量で従来の手袋と同等の抗菌効果を発揮することが
できる。従って、上述したような薬剤による薬物アレル
ギーの発症を低減することが可能になる。As in the case of conventional gloves, the gloves of the present invention may be used by incorporating the above antibacterial agent and the like. In that case, the vegetable extract itself plays a role of an antibacterial agent, etc., so it can demonstrate the same antibacterial effect as conventional gloves with a smaller drug content than when using conventional gloves. it can. Therefore, it becomes possible to reduce the occurrence of drug allergy due to the above-mentioned drugs.

【００１４】本発明の手袋としては、次のような態様の
手袋が例示される。 ・ゴム層を備えた手袋（以下、単にゴム手袋という） (1) ゴム層（樹脂層に代えて樹脂層を用いても同様であ
る）単独で構成される手袋であって、前記ゴム層に植物
エキスを含有した手袋。 (2) 二層以上のゴム層にて形成された手袋であって、前
記二層以上のゴム層のうち、少なくとも最外層（手袋完
成後は最内層となる）に植物エキスを含有した手袋。 (3) コットン、レーヨン等の植毛を容易に行うために設
けたゴム層（以下、単に接着層という）と、少なくとも
一層のゴム層とから構成される手袋であって、少なくと
も最外層（手袋完成後は最内層となる）となる接着層に
植物エキスを含有した手袋。 (4) 薄い布製の手袋体の表面に、少なくとも一層のゴム
層を設けた手袋であって、前記ゴム層に植物エキスを含
有した手袋。 ・樹脂層を備えた手袋（以下、単に樹脂製手袋という） ゴム層に代えて樹脂層を設けることにより、上記(1) 〜
(4)に例示した手袋を作製することができる。 ・ゴム層と樹脂層とを備えた手袋 (5) 例えば共押し出し成形、ヒートシール、接着などに
よりゴム層と樹脂層とを重ねた多層構造を有する手袋で
あって、前記ゴム層または樹脂層の少なくとも一層に植
物性エキスを含有した手袋。The gloves of the present invention include the following gloves. -Gloves provided with a rubber layer (hereinafter simply referred to as rubber gloves) (1) Gloves composed solely of a rubber layer (the same applies to the case where a resin layer is used instead of the resin layer). Gloves containing plant extracts. (2) A glove formed of two or more rubber layers, wherein at least the outermost layer (which becomes the innermost layer after completion of the glove) of the two or more rubber layers contains a plant extract. (3) A glove composed of a rubber layer (hereinafter simply referred to as an adhesive layer) provided to facilitate flocking of cotton, rayon, or the like, and at least one rubber layer, and at least the outermost layer (glove completed) Gloves containing a plant extract in the adhesive layer that becomes the innermost layer. (4) A glove provided with at least one rubber layer on the surface of a thin cloth glove body, wherein the rubber layer contains a plant extract. -Gloves with a resin layer (hereinafter simply referred to as resin gloves) By providing a resin layer instead of a rubber layer, the above (1)-
The glove exemplified in (4) can be manufactured. Gloves having a rubber layer and a resin layer (5) For example, a glove having a multilayer structure in which a rubber layer and a resin layer are overlapped by co-extrusion molding, heat sealing, bonding, etc. Gloves containing at least one vegetable extract.

【００１５】本発明の手袋のうち、まず、ゴム手袋につ
いて説明する。上記ゴム手袋において、ゴム層を構成す
るゴムとしては、例えば天然ゴム、合成ゴムなどの未加
硫ゴムや、あるいはそれらのラテックスがあげられが、
とりわけ本発明では、ゴム手袋の製造工程の簡素化など
を考慮すると、ゴムラテックスを使用するのが好まし
い。First, rubber gloves of the gloves of the present invention will be described. In the rubber glove, the rubber constituting the rubber layer includes, for example, natural rubber, unvulcanized rubber such as synthetic rubber, or latex thereof.
In particular, in the present invention, it is preferable to use rubber latex in consideration of simplification of a rubber glove manufacturing process and the like.

【００１６】前記合成ゴムとしては、例えばニトリルゴ
ム、イソプレンゴム、ブタジエンゴム、クロロプレンゴ
ム、スチレン−ブタジエンゴムなどがあげられる。天然
ゴムのラテックスとしては、市販のアンモニア処理ラテ
ックスでも、新鮮なフィールドラテックスのいずれであ
ってもよい。また本発明では、上記天然ゴムと合成ゴム
（例えばイソプレンゴム、ブタジエンゴム、アクリロニ
トリルブタジエンゴムなど）との混合ラテックスを使用
して、天然ゴムと他のゴムからなるゴム手袋をも包含す
るものである。Examples of the synthetic rubber include nitrile rubber, isoprene rubber, butadiene rubber, chloroprene rubber, and styrene-butadiene rubber. The natural rubber latex may be either a commercially available ammonia-treated latex or a fresh field latex. The present invention also includes rubber gloves made of natural rubber and other rubbers using a mixed latex of the above natural rubber and synthetic rubber (for example, isoprene rubber, butadiene rubber, acrylonitrile butadiene rubber, etc.). .

【００１７】次に、ゴムラテックスを用いて本発明のゴ
ム手袋を製造する方法について説明する。上記ゴム手袋
を製造するには、下記製造方法Ａ、Ｂに示すように、ア
ンサポートタイプまたはサポートタイプのゴム手袋を製
造するための、従来公知の製造方法が適用される。 製造方法Ａ．アンサポートタイプのゴム手袋 未加硫のゴムラテックスに、加硫剤、加硫促進剤、
加硫促進助剤等の各種添加剤を所定の割合で配合し、し
ばらく熟成させた後、上記植物性エキスを配合する。 所定の手袋形状のモールド（型）の表面に凝固剤を
塗布する。 上記のモールドを、のラテックスに浸漬した
後、引き上げて、型の表面にゴム層を成膜する工程を一
回行って、当該型の表面に一層のゴム層を形成する。 上記ゴム層をモールドごと加硫したのち、型からカ
バーを取り外して製造される。Next, a method for producing the rubber glove of the present invention using rubber latex will be described. In order to manufacture the rubber glove, a conventionally known manufacturing method for manufacturing an unsupported or support type rubber glove is applied as shown in the following manufacturing methods A and B. Manufacturing method A. Unsupported rubber gloves Unvulcanized rubber latex, vulcanizing agent, vulcanization accelerator,
Various additives such as a vulcanization accelerator are blended in a predetermined ratio, and after aging for a while, the above-mentioned vegetable extract is blended. A coagulant is applied to the surface of a predetermined glove-shaped mold. After the above-mentioned mold is immersed in latex, it is pulled up, and a step of forming a rubber layer on the surface of the mold is performed once to form one rubber layer on the surface of the mold. After vulcanizing the rubber layer together with the mold, the cover is removed from the mold to produce the rubber layer.

【００１８】上記製造方法Ａを用いることにより、上述
した(1) の態様の手袋を作製することができる。また
(2) の態様の手袋を作製するには、例えばでのゴム層
を成膜する工程を複数回行って、上記のモールドの表
面に二層以上のゴム層を形成させればよい。加硫時の温
度や条件は、従来公知の条件にて適宜設定されるが、ゴ
ム層中に含有される植物性エキスが変色または分解など
を起こさない条件で加硫される。具体的には、８０〜１
００℃で０．３〜０．８時間程度行うのがよい。By using the above-mentioned production method A, the glove of the above-mentioned embodiment (1) can be produced. Also
In order to produce the glove of the embodiment (2), for example, a step of forming a rubber layer may be performed a plurality of times to form two or more rubber layers on the surface of the mold. The temperature and conditions at the time of vulcanization are appropriately set under conventionally known conditions, but vulcanization is carried out under such conditions that the vegetable extract contained in the rubber layer does not undergo discoloration or decomposition. Specifically, 80-1
It is preferable to perform the process at 00 ° C. for about 0.3 to 0.8 hours.

【００１９】上記(3) の態様の手袋においては、前記ゴ
ム層に植物性エキスを含有していてもよいが、使用者の
手と直接接触する接着層に植物性エキスを含有している
ことが好適である。前記接着層は、手袋の型を、植物性
エキスを含有してないゴムラテックスを使用する以外は
上述した製造方法Ａと同様にしてゴム層を形成し、つい
でこのゴム層をモールドごと、天然ゴムラテックス、植
物性エキスおよび接着剤を配合した溶液に浸漬した後、
乾燥、加硫することにより、製造される。In the glove according to the embodiment (3), the rubber layer may contain a vegetable extract, but the adhesive layer which comes into direct contact with the user's hand contains the vegetable extract. Is preferred. The adhesive layer forms a rubber layer in the same manner as in the above-described production method A except that a rubber glove containing no vegetable extract is used as a glove mold. After dipping in a solution containing latex, vegetable extract and adhesive,
It is manufactured by drying and vulcanizing.

【００２０】上記接着剤としては、例えばアクリル系ま
たはウレタン系のエマルジョン、天然ゴムラテックスな
どがあげられる。 製造方法Ｂ．サポートタイプのゴム手袋 ’手袋の形状のモールド（型）に、薄い布製の手袋体
を装着し、この手袋体に凝固剤をしみこませる。 ’上記’の手袋体をモールドごと、前記のラテッ
クスに浸漬した後、引き上げて、型の表面にゴム層を成
膜する工程を一回または複数回行って、当該型の表面に
一層または二層以上のゴム層を形成する。 ’ゴム層が形成された手袋体を、モールドごと加熱し
て加硫させる。Examples of the adhesive include acrylic or urethane emulsions and natural rubber latex. Manufacturing method B. Support-type rubber gloves' A thin cloth glove body is attached to a glove-shaped mold, and the glove body is impregnated with a coagulant. After immersing the glove body of 'above' in the latex described above together with the mold, pulling it up, performing a step of forming a rubber layer on the surface of the mold one or more times, one or two layers on the surface of the mold The above rubber layer is formed. 'The glove body on which the rubber layer is formed is heated and vulcanized together with the mold.

【００２１】上記製造方法Ｂを用いることにより、上述
した(4) の態様の手袋を作製することができる。ところ
で、近年、天然ゴムからなるゴム製品が原因で患者が呼
吸困難、アナフィラキシー様症状（血管性浮腫、じんま
しん、虚脱、チアノーゼ等）などを引き起こすことが報
告されている。その原因は、天然ゴム中に不純物として
存在する蛋白質であると推測されている。By using the above-mentioned production method B, the glove of the above-mentioned embodiment (4) can be produced. In recent years, it has been reported that a rubber product made of natural rubber causes a patient to have difficulty breathing and anaphylaxis-like symptoms (angioedema, urticaria, collapse, cyanosis, etc.). The cause is presumed to be proteins present as impurities in natural rubber.

【００２２】しかも、かかる蛋白質は、その種類や量が
天然ゴムラテックスの産地や産出時期などによって異な
るために、天然ゴムの品質や加硫特性などにもばらつき
を生じさせたり、天然ゴムの物理特性を低下させる問題
があった。そこで本発明では、上記工程より得られたゴ
ム手袋を、さらに水に浸漬して蛋白質を洗浄（いわゆる
リーチング処理）し、ゴム層中の蛋白質を除去する工程
が採択される。Moreover, since the type and amount of such proteins differ depending on the place of production and the time of production of natural rubber latex, the quality and vulcanization characteristics of natural rubber vary, and the physical properties of natural rubber There was a problem of lowering. Therefore, in the present invention, a step of immersing the rubber glove obtained in the above step in water to wash the protein (so-called leaching treatment) to remove the protein in the rubber layer is adopted.

【００２３】よって、本発明の手袋におけるゴム物理特
性が良好になると共に、蛋白質に起因するアレルギー反
応を防止することができる。また本発明では、上記天然
ゴムラテックスに代えて、天然ゴムラテックス中の蛋白
質を従来公知の方法（例えば酵素分解法や遠心分離法な
ど）を用いて除去した、脱蛋白天然ゴムラテックスを使
用してもよい。Therefore, the gloves of the present invention can have good physical rubber properties and can prevent allergic reactions caused by proteins. In the present invention, instead of the natural rubber latex, a protein-free natural rubber latex obtained by removing a protein in a natural rubber latex by a conventionally known method (for example, an enzymatic decomposition method or a centrifugal separation method) is used. Is also good.

【００２４】さらに本発明では、ゴム手袋表面に滑性を
付与するために、約１００〜５００ｐｐｍの塩素水に、
通常５〜１０分間浸漬して塩素化（クロリネーション）
処理する工程が採択される。手袋の型は、例えば陶器、
セラミック製のものなどが使用可能であり、使用する手
袋と同一形状に形成されている。Further, in the present invention, in order to impart lubrication to the surface of the rubber glove, about 100 to 500 ppm of chlorine water is added to
Chlorination by immersion for 5-10 minutes (chlorination)
A processing step is adopted. Glove types are, for example, pottery,
A ceramic material or the like can be used, and is formed in the same shape as the glove to be used.

【００２５】上記ゴム手袋の製造方法Ａ、Ｂにおいて使
用される凝固剤としては、例えば硝酸カルシウム、炭酸
カルシウム、塩化カルシウムなどがあげられる。また本
発明においては、上記ゴム手袋の製造方法Ａ、Ｂのほか
に、静電気力を利用してゴム粒子を凝集させる凝固液法
や、感熱凝固剤を含有したゴムラテックスを用いる感熱
法によって、成膜処理を行うこともできる。Examples of the coagulant used in the above methods A and B for producing rubber gloves include calcium nitrate, calcium carbonate, calcium chloride and the like. In the present invention, in addition to the rubber glove production methods A and B, a coagulation solution method of aggregating rubber particles using electrostatic force or a heat-sensitive method using a rubber latex containing a heat-sensitive coagulant is used. Film treatment can also be performed.

【００２６】例えば上記感熱法を用いれば、型を加熱す
るだけで成膜が可能であり、凝固剤を型の表面に塗布し
たり、あるいは手袋体にしみこませたりする工程を省略
することができる。天然ゴムラテックスに配合される添
加剤としては、前述したように、加硫剤のほか、加硫促
進剤、加硫促進助剤（活性化剤）、老化防止剤、充填
剤、分散剤等の従来公知の種々の添加剤があげられる。For example, if the above-mentioned heat-sensitive method is used, a film can be formed only by heating the mold, and the step of applying a coagulant to the surface of the mold or soaking it into the glove body can be omitted. . As described above, additives to be added to the natural rubber latex include vulcanization accelerators, vulcanization accelerators, vulcanization accelerators (activators), antioxidants, fillers, dispersants, and the like. Conventionally known various additives can be used.

【００２７】上記加硫剤としては、例えば硫黄や有機含
硫黄化合物等があげられ、その配合量は、ゴムラテック
スの固形ゴム成分１００重量部に対して０．５〜３重量
部程度であるのが好ましい。加硫促進剤としては、例え
ばＰＸ（Ｎ−エチル−Ｎ−フェニルジチオカルバミン酸
亜鉛）、ＰＺ（ジメチルジチオカルバミン酸亜鉛）、Ｅ
Ｚ（ジエチルジチオカルバミン酸亜鉛）、ＢＺ（ジブチ
ルジチオカルバミン酸亜鉛）、ＭＺ（２−メルカプトベ
ンゾチアゾールの亜鉛塩）、ＴＴ（テトラメチルチウラ
ムジスルフィド）等があげられる。これらは単独でまた
は２種以上を混合して用いることができる。その配合量
は、ゴムラテックスの固形ゴム成分１００重量部に対し
て０．５〜３重量部程度であるのが好ましい。Examples of the vulcanizing agent include sulfur and organic sulfur-containing compounds. The amount of the vulcanizing agent is about 0.5 to 3 parts by weight based on 100 parts by weight of the solid rubber component of the rubber latex. Is preferred. Examples of the vulcanization accelerator include PX (zinc N-ethyl-N-phenyldithiocarbamate), PZ (zinc dimethyldithiocarbamate), E
Z (zinc diethyldithiocarbamate), BZ (zinc dibutyldithiocarbamate), MZ (zinc salt of 2-mercaptobenzothiazole), TT (tetramethylthiuram disulfide) and the like. These can be used alone or in combination of two or more. The compounding amount is preferably about 0.5 to 3 parts by weight based on 100 parts by weight of the solid rubber component of the rubber latex.

【００２８】加硫促進助剤としては、例えば亜鉛華等が
あげられる。その配合量は、ゴムラテックスの固形ゴム
成分１００重量部に対して０．５〜３重量部であるのが
好ましい。老化防止剤としては、一般に、非汚染性のフ
ェノール類が好適に用いられるが、アミン類を使用して
もよい。老化防止剤の配合量は、ゴムラテックスの固形
ゴム成分１００重量部に対して０．５〜３重量部程度で
あるのが好ましい。[0028] Examples of the vulcanization accelerating aid include zinc white. The compounding amount is preferably 0.5 to 3 parts by weight based on 100 parts by weight of the solid rubber component of the rubber latex. In general, non-staining phenols are preferably used as the antioxidant, but amines may be used. The compounding amount of the antioxidant is preferably about 0.5 to 3 parts by weight based on 100 parts by weight of the solid rubber component of the rubber latex.

【００２９】充填剤としては、例えばカオリンクレー、
ハードクレー、炭酸カルシウム等があげられる。その配
合量は、ゴムラテックスの固形ゴム成分１００重量部に
対して１０重量部以下であるのが好ましい。また、上記
各添加剤のゴムラテックス中への分散を良好にするため
に分散剤を配合してもよい。かかる分散剤としては、例
えば各種陰イオン系界面活性剤等があげられる。分散剤
の配合量は、分散対象である成分における重量の０．３
〜１．０重量％程度であるのが好ましい。As the filler, for example, kaolin clay,
Hard clay, calcium carbonate and the like can be mentioned. The compounding amount is preferably 10 parts by weight or less based on 100 parts by weight of the solid rubber component of the rubber latex. In addition, a dispersant may be blended in order to improve the dispersion of the additives in the rubber latex. Examples of such a dispersant include various anionic surfactants. The amount of the dispersant is 0.3% of the weight of the component to be dispersed.
It is preferably about 1.0% by weight.

【００３０】上記ゴム手袋において、ゴム層の厚さは、
ゴムの破断などのおそれがない範囲で適宜選択され、通
常０．１５〜０．５ｍｍ、好ましくは０．２〜０．４ｍ
ｍであるのがよい。厚さ調整は、例えば前述した凝固剤
の型への付着量を調整することにより行うことができ
る。また上記ゴム手袋は、手袋の着脱が容易でかつ良好
なフィット性を発揮するのに必要な伸縮性を有するよう
に、ＪＩＳ Ｋ ６２５１に従った測定法で求めた伸び
が、通常７００〜１０００％、好ましくは８００〜９０
０％であるのがよい。In the above rubber glove, the thickness of the rubber layer is
It is appropriately selected within a range where there is no risk of rubber breakage, and is usually 0.15 to 0.5 mm, preferably 0.2 to 0.4 m
m is good. The thickness can be adjusted, for example, by adjusting the amount of the coagulant adhering to the mold. The elongation of the rubber glove determined by a measurement method according to JIS K6251 is usually 700 to 1000% so that the glove can be easily attached / detached and has elasticity necessary for exhibiting good fit. , Preferably 800 to 90
It is better to be 0%.

【００３１】さらに上記ゴム手袋は、装着者の手への手
袋の装着が容易になるように、ＪＩＳ Ｋ ６２５１に
従った測定法で求めた引張応力が、通常、２０〜４０Ｍ
Ｐａ、好ましくは２５〜３５ＭＰａであるのがよい。次
に、本発明の手袋のうち、樹脂製手袋について説明す
る。 製造方法Ｃ．アンサポートタイプの樹脂製手袋 (a) 樹脂をその融点以上に加熱して融解させた融液、ま
たは適当な有機溶媒に溶解した溶液を調製し、その融液
または溶液中に植物性エキスを配合する。 (b) 所定の手袋形状のモールド（型）を、上記(a) の融
液または溶液に浸漬した後、引き上げて、融液の場合に
は冷却し、溶液の場合には乾燥して、型の表面に樹脂層
を成膜する工程を一回または複数回行って、当該型の表
面に一層または二層以上の樹脂層を形成する。 製造方法Ｄ．サポートタイプの樹脂製手袋 (a)'手袋の形状のモールド（型）に、薄い布製の手袋体
を装着する。 (b)'上記(a)'の手袋体をモールドごと、前記(a) の融液
または溶液に浸漬した後、引き上げて、融液の場合には
冷却し、溶液の場合には乾燥して、型の表面に樹脂層を
成膜する工程を一回または複数回行って、当該型の表面
に一層または二層以上の樹脂層を形成する。Further, the rubber glove has a tensile stress of usually 20 to 40 M, which is determined by a measuring method in accordance with JIS K6251 so that the glove can be easily worn on the wearer's hand.
Pa, preferably 25 to 35 MPa. Next, among the gloves of the present invention, a resin glove will be described. Manufacturing method C. Unsupported resin gloves (a) Prepare a melt that has been heated and melted above the melting point of the resin, or a solution dissolved in an appropriate organic solvent, and blend the vegetable extract in the melt or solution. I do. (b) After immersing the mold (mold) of the specified glove shape in the melt or solution of (a) above, pull it up, cool in the case of melt, and dry in the case of solution, The step of forming a resin layer on the surface of the mold is performed once or plural times to form one or more resin layers on the surface of the mold. Manufacturing method D. Support-type resin gloves (a) 'Attach a thin cloth glove to a glove-shaped mold. (b) After immersing the glove body of '(a)' together with the mold in the melt or solution of (a) above, pull up, cool in the case of the melt, and dry in the case of the solution. The step of forming a resin layer on the surface of the mold is performed once or a plurality of times to form one or more resin layers on the surface of the mold.

【００３２】上記樹脂性手袋の製造方法Ｃ，Ｄに使用さ
れる樹脂としては、植物性エキスが分解または変色しな
い温度で融解する樹脂を使用するか、あるいは有機溶媒
に溶解しやすい樹脂を使用するのが好ましく、例えばポ
リ塩化ビニル（ＰＶＣ）、ポリウレタン、ポリオレフィ
ンなどがあげられる。また本発明では、上記製造方法
Ｃ，Ｄにおける(a) において、植物性エキスが分解等を
起こしにくい温度で調製される、樹脂の溶液を用いて、
当該溶液中に植物性エキスを含有させるのが好ましい。As the resin used in the methods C and D for producing resinous gloves, a resin that melts at a temperature at which the plant extract does not decompose or discolor, or a resin that is easily dissolved in an organic solvent is used. It is preferable to use, for example, polyvinyl chloride (PVC), polyurethane, polyolefin and the like. Further, in the present invention, in (a) in the above production methods C and D, a resin solution prepared at a temperature at which the plant extract is unlikely to decompose or the like is used,
It is preferable to include a plant extract in the solution.

【００３３】上記樹脂製の手袋において、樹脂層の厚さ
は、手袋の破断などのおそれがない範囲で適宜選択さ
れ、通常０．１５〜０．５ｍｍ、好ましくは０．２〜
０．４ｍｍであるのがよい。厚さ調整は、例えば前述し
た成膜工程の回数を調整することにより行うことができ
る。In the resin glove, the thickness of the resin layer is appropriately selected within a range that does not cause the glove to be broken, and is usually 0.15 to 0.5 mm, preferably 0.2 to 0.5 mm.
It is preferably 0.4 mm. The thickness can be adjusted, for example, by adjusting the number of times of the film formation process described above.

【００３４】[0034]

【実施例】以下、実施例を示して本発明の手袋を詳細に
説明する。 実施例１ ゴム固形分６０重量％の天然ゴムラテックスに、硫黄、
酸化亜鉛（ＺｎＯ）およびジブチルジチオカルバミン酸
亜鉛（ＢＺ）を重量比率で天然ゴムラテックス：硫黄：
ＺｎＯ：ＢＺ＝１００：１：１：０．５となるように配
合してラテックス組成物を調製し、ついで、このラテッ
クス組成物総量に対して５０％アロエ水を２重量％添加
した。EXAMPLES The gloves of the present invention will be described in detail below with reference to examples. Example 1 To a natural rubber latex having a rubber solid content of 60% by weight, sulfur,
Zinc oxide (ZnO) and zinc dibutyldithiocarbamate (BZ) in a weight ratio of natural rubber latex: sulfur:
A latex composition was prepared by blending such that ZnO: BZ = 100: 1: 1: 0.5, and 2% by weight of 50% aloe water was added to the total amount of the latex composition.

【００３５】一方、１００℃に加温した手袋の型を２０
％硝酸カルシウムエタノール溶液（凝固剤）に１０秒間
浸漬し、３００ｍｍ／ｍｉｎで型を引上げた後、オーブ
ンにて１００℃で１分間乾燥させた。この手袋の型を上
記アロエ水含有の天然ゴムラテックスに３０秒間浸漬し
た後、３００ｍｍ／ｍｉｎで型を引き上げ、室温で数分
間乾燥した。On the other hand, a glove mold heated to 100.degree.
After immersing in a 10% ethanol solution of calcium nitrate (coagulant) for 10 seconds, the mold was pulled up at 300 mm / min, and dried in an oven at 100 ° C. for 1 minute. After immersing the glove mold in the natural rubber latex containing aloe water for 30 seconds, the mold was pulled up at 300 mm / min and dried at room temperature for several minutes.

【００３６】ついで上記ゴム膜を、オーブンにて１００
℃で３０分間加硫し、型から取り外して、ゴム膜の厚さ
が約０．４ｍｍであるゴム手袋を得た。さらに、この手
袋を水槽に１０分間浸漬してリーチング処理し、ついで
２５０ｐｐｍの塩素水に２分間浸漬してクロリネーショ
ン処理を行った後、水で洗浄し、乾燥することにより、
本発明の手袋を得た。 実施例２ 実施例１と同様にしてゴム膜を成形し、このゴム膜を５
０％アロエ水含有の接着液に１０秒間浸漬し、３００ｍ
ｍ／ｍｉｎで型を引上げた後、コットンパイルを吹きつ
けた。ついで上記ゴム膜を、オーブンにて１００℃で３
０分間加硫し、型から取り外して、ゴム手袋を得、さら
に、この手袋を水槽に１０分間浸漬してリーチング処理
し、乾燥することにより、本発明の手袋を得た。 実施例３ ＰＶＣペースト１００重量部に、可塑剤（フタル酸ジオ
クチル，ＤＯＰ）１００重量部、熱安定剤２重量部およ
び増粘剤４重量部を配合してＰＶＣ樹脂組成物を調製
し、ついで、このＰＶＣ樹脂組成物中に、陶器製の手袋
の型を浸漬した後、１６０〜１８０℃でゲル化させ、手
袋本体（樹脂層）を得た。Then, the above rubber film was placed in an oven for 100 hours.
Vulcanized at 30 ° C. for 30 minutes and removed from the mold to obtain a rubber glove having a rubber film thickness of about 0.4 mm. Further, the glove was immersed in a water tank for 10 minutes to perform a leaching treatment, and then immersed in 250 ppm chlorine water for 2 minutes to perform a chlorination treatment, followed by washing with water and drying.
The glove of the present invention was obtained. Example 2 A rubber film was formed in the same manner as in Example 1, and this rubber film was
Immerse in adhesive solution containing 0% aloe water for 10 seconds, 300m
After pulling up the mold at m / min, a cotton pile was sprayed. Then, the above rubber film was placed in an oven at 100 ° C for 3 hours.
It was vulcanized for 0 minutes and removed from the mold to obtain a rubber glove. The glove was immersed in a water bath for 10 minutes, subjected to leaching treatment, and dried to obtain a glove of the present invention. Example 3 A PVC resin composition was prepared by mixing 100 parts by weight of a PVC paste, 100 parts by weight of a plasticizer (dioctyl phthalate, DOP), 2 parts by weight of a heat stabilizer and 4 parts by weight of a thickener. After immersing a ceramic glove mold in this PVC resin composition, it was gelled at 160 to 180 ° C. to obtain a glove body (resin layer).

【００３７】次に、上記手袋本体を、アクリル系エマル
ジョン１００重量部に対して５０％アロエ水を５重量部
配合した接着剤に浸漬した後、レーヨンパイルを植毛
し、１４０〜１６０℃で約１０分間乾燥した。ついで型
から取り外して、本発明の樹脂製手袋を得た。なお、型
から取り外した後、植物エキスを含有した層（接着層）
は最内層である。Next, the glove body was immersed in an adhesive prepared by blending 5 parts by weight of 50% aloe water with respect to 100 parts by weight of an acrylic emulsion, and then rayon pile was planted. Dried for minutes. Then, it was removed from the mold to obtain the resin glove of the present invention. After removal from the mold, the layer containing the plant extract (adhesive layer)
Is the innermost layer.

【００３８】上記実施例１〜３の手袋を実際に装着して
みたところ、手袋内部に含有したアロエ成分（植物性エ
キス）が滲み出し、手肌にしっとり感、潤い感、すべす
べ感が認められた。また使用後の悪臭も認められなかっ
た。When the gloves of Examples 1 to 3 were actually worn, the aloe component (vegetable extract) contained inside the gloves oozed out, and a moist feeling, a moist feeling and a smooth feeling were recognized on the hand skin. Was. No odor after use was observed.

【００３９】[0039]

【発明の効果】本発明の手袋は、手袋内部に含有した植
物性エキス成分が滲み出し、手袋内部の細菌の発育およ
び悪臭の発生を防止すると共に、手肌にしっとり感、潤
い感、すべすべ感を与えることで手荒れを防止し、手肌
のスキンケア効果に優れたものである。According to the gloves of the present invention, the vegetable extract contained in the gloves oozes out to prevent the growth of bacteria and the generation of offensive odors inside the gloves, and the hand skin feels moist, moist and smooth. By giving, hand roughness is prevented and the skin care effect of hand skin is excellent.

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】少なくとも一層のゴム層または樹脂層を備
えた手袋であって、前記ゴム層または樹脂層の少なくと
も一層に植物性エキスを含有させたことを特徴とする手
袋。1. A glove comprising at least one rubber layer or resin layer, wherein at least one of said rubber layer or resin layer contains a vegetable extract. 【請求項２】前記植物性エキスが、アロエ、桃、桃の
葉、トウキ末、甘草、柚子、ドクダミ、米ヌカ、オリー
ブ、シソの葉、ヨモギ、椰子の実および海草からなる群
より選ばれる少なくとも１種から抽出されるエキスであ
る請求項１記載の手袋。2. The plant extract is selected from the group consisting of aloe, peach, peach leaves, powder of touki, licorice, citron, dokudami, rice bran, olive, perilla leaves, mugwort, coconut and seaweed. The glove according to claim 1, which is an extract extracted from at least one kind. 【請求項３】前記ゴム層が、ゴムラテックスから製造さ
れる請求項１記載の手袋。3. The glove according to claim 1, wherein said rubber layer is made of rubber latex.