JPH11182006A - Woody floor member - Google Patents
Woody floor memberInfo
- Publication number
- JPH11182006A JPH11182006A JP36455597A JP36455597A JPH11182006A JP H11182006 A JPH11182006 A JP H11182006A JP 36455597 A JP36455597 A JP 36455597A JP 36455597 A JP36455597 A JP 36455597A JP H11182006 A JPH11182006 A JP H11182006A
- Authority
- JP
- Japan
- Prior art keywords
- reinforcing layer
- base plate
- adhesive
- glass
- warpage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、表層に化粧単板を
有する木質床材に関する。TECHNICAL FIELD The present invention relates to a wooden flooring having a decorative veneer on a surface layer.
【0002】[0002]
【従来の技術】従来のこの種の木質床材では一般に、合
板を台板とし、その表層に0.25mm厚程度の化粧単
板を配して、表面を飾るとともに、台板の裏面側に、発
泡ウレタンや不織布などの非木質材料を配して、クッシ
ョン性を確保するようになっている。また、台板と化粧
単板の間に和紙を介在させ、この和紙を介して、台板と
化粧単板を相互に接着することにより、非常に薄い化粧
単板を和紙で拘束で補強し、化粧単板に経時的なひび割
れが発生するのを防止したものも知られている。2. Description of the Related Art In general, in this type of wooden flooring, a plywood is used as a base plate, and a decorative veneer having a thickness of about 0.25 mm is arranged on the surface of the base plate to decorate the surface and to attach the back surface of the base plate. In addition, a non-woody material such as urethane foam or nonwoven fabric is arranged to ensure cushioning. Also, by interposing Japanese paper between the base plate and decorative veneer and bonding the base plate and decorative veneer to each other through this Japanese paper, a very thin decorative veneer is reinforced with Japanese paper by restraint, and It is also known that a plate is prevented from cracking over time.
【0003】[0003]
【発明が解決しようとする課題】しかし、上述した従来
の木質床材は、台板と化粧単板を接着する際、和紙をあ
らかじめ台板に接着し、その後、さらに和紙の表面に接
着剤を塗布して化粧単板を接着しなければならず、この
接着作業に時間と手間がかかり、その分、製造コストが
増大するという問題がある。However, in the above-mentioned conventional wooden flooring material, when bonding the base plate and the decorative veneer, the Japanese paper is previously bonded to the base plate, and then the adhesive is further applied to the surface of the Japanese paper. The veneer veneer must be adhered by application, and this bonding operation takes time and labor, and there is a problem that the manufacturing cost increases accordingly.
【0004】また、化粧単板が非常に薄く、かつ化粧単
板および台板を構成する合板の硬度が低いとともに、和
紙の拘束力もそれほど大きくないので、上記木質床材
が、例えば、椅子を頻繁に動かすダイニングルームなど
で使用された場合には、化粧単板が割れたり、凹んだり
しやすいという欠点がある。Further, the decorative veneer is very thin, the hardness of the plywood constituting the decorative veneer and the base plate is low, and the binding force of Japanese paper is not so large. When used in a dining room or the like, the veneer is easily broken or dented.
【0005】この欠点を解消可能な木質床材として、 化粧単板を厚くしたもの 化粧単板に樹脂を含浸させて硬度を高めたもの 合板の代わりに、硬度の高いMDFを台板として使
用したもの も従来知られている。しかし、の木質床材は、化粧単
板が高価であることから、化粧単板が厚くなるのに伴っ
て、材料コストが増大してしまう。の木質床材は、樹
脂を含浸するための含浸装置が必要となり、設備コスト
が増大してしまう。また、のMDFを台板として使用
した木質床材は、反りが発生しやすいという欠点があ
る。これは、MDFの生産時に残留した内部応力が、床
材を製造する際の切断によって解放され、バランスを崩
すためである。なお、木質床材の反りは、MDFだけで
なく、合板を台板として用いた場合でも、発生すること
がある。このような合板の反りは、合板に和紙および化
粧単板を接着することによって合板構成のバランスが崩
れることや、合板を構成する材料の不均一性などに起因
していると考えられる。[0005] As a wooden flooring material capable of solving this drawback, a thick veneer veneer is used. A veneer veneer is impregnated with resin to increase its hardness. Some have been known in the past. However, since the decorative veneer is expensive, the material cost of the wooden flooring material increases as the decorative veneer becomes thicker. Wood flooring requires an impregnation device for impregnating the resin, which increases equipment costs. Wood flooring using MDF as a base plate has a drawback that warpage is likely to occur. This is because the internal stress remaining during the production of the MDF is released by cutting during the production of the flooring material, thus breaking the balance. In addition, the warp of the wooden flooring material may occur not only in the case of the MDF but also in the case where the plywood is used as the base plate. It is considered that such warpage of the plywood is caused by the loss of the balance of the plywood configuration due to the bonding of Japanese paper and decorative veneer to the plywood, and the non-uniformity of the material constituting the plywood.
【0006】本発明は、このような課題を解決するため
になされたものであり、製造コストをほとんど増大させ
ることなく、反りの発生を防止するとともに、表面の割
れを抑制することができる木質床材を提供することを目
的としている。SUMMARY OF THE INVENTION The present invention has been made to solve such a problem, and a wooden floor capable of preventing warpage and suppressing surface cracks without substantially increasing the manufacturing cost. It is intended to provide materials.
【0007】[0007]
【課題を解決するための手段】この目的を達成するた
め、本発明の木質床材は、木質の台板と、表裏方向に接
着剤が浸透可能に構成され、台板の表面に配された補強
層と、この補強層を介して、台板に接着された化粧単板
と、を備えていることを特徴としている。Means for Solving the Problems To achieve this object, the wooden flooring of the present invention has a wooden base plate and an adhesive which can be penetrated in the front and back directions, and is arranged on the surface of the base plate. It is characterized by comprising a reinforcing layer and a decorative veneer bonded to the base plate via the reinforcing layer.
【0008】この木質床材では、木質の台板と化粧単板
との間に介在し、接着された補強層によって、化粧単板
が拘束されることにより、その表面の発生が防止される
とともに、補強層によって化粧単板の硬度が補強される
ことにより、木質床材の表面に凹みが生じにくくなる。
また、この補強層によって、反りも生じにくくなる。さ
らに、この補強層は、表裏方向に接着剤が浸透可能に構
成されているので、例えば、補強層の表裏面の一方に塗
布された接着剤は、他方まで浸透する。したがって、補
強層の表裏面の一方に接着剤を塗布するだけで、台板と
化粧単板を相互に接着できるので、従来と比較し、接着
作業を簡素化でき、その分、製造コストを削減すること
ができる。In this wooden flooring material, the decorative veneer is interposed between the wooden base plate and the decorative veneer, and is bonded to the decorative veneer. In addition, since the hardness of the decorative veneer is reinforced by the reinforcing layer, the surface of the wooden flooring material is less likely to be dented.
In addition, the reinforcing layer also makes it difficult for warpage to occur. Further, since the reinforcing layer is configured so that the adhesive can penetrate in the front and back directions, for example, the adhesive applied to one of the front and back surfaces of the reinforcing layer penetrates to the other. Therefore, the base plate and the veneer can be bonded to each other simply by applying an adhesive to one of the front and back surfaces of the reinforcing layer, so that the bonding operation can be simplified as compared with the conventional case, and the manufacturing cost is reduced accordingly. can do.
【0009】この場合、補強層が、ガラス織布、ガラス
組布および寒冷紗の1つで構成されていることが好まし
い。In this case, it is preferable that the reinforcing layer is constituted by one of a glass woven fabric, a glass braided fabric and a cold gauze.
【0010】この構成では、補強層としての上記材料
が、いずれも接着剤を浸透可能なものであるので、上述
した接着作業の簡素化を実現することができる。また、
これらの材料はいずれも、比較的安価であるため、材料
コストもほとんど増大しない。In this configuration, since the above-mentioned materials as the reinforcing layer are all permeable to the adhesive, the above-described simplification of the bonding operation can be realized. Also,
Since all of these materials are relatively inexpensive, the cost of material hardly increases.
【0011】これらの場合、表裏方向に接着剤が浸透可
能に構成され、台板の裏面に配された第2補強層と、こ
の第2補強層を介して、台板に接着されたクッション材
と、をさらに備えていることが好ましい。In these cases, a second reinforcing layer disposed on the back surface of the base plate and a cushion material bonded to the base plate via the second reinforcing layer are formed so that the adhesive can penetrate in the front and back directions. It is preferable to further include the following.
【0012】この構成では、クッション材によってクッ
ション性が得られる。また、台板に接着された第2補強
層によって、台板の撓みが直接、拘束されるので、台板
がMDFで構成されるような場合でも、第2補強層によ
って台板の反りの発生を防止でき、したがって、木質床
材全体の反りを防止することができる。また、第2補強
層が、表裏方向に接着剤が浸透可能に構成されているこ
とにより、台板とクッション材の接着作業を簡素化でき
ることは、台板と化粧単板の接着の場合と同様である。[0012] With this configuration, cushioning properties can be obtained by the cushion material. In addition, since the bending of the base plate is directly restrained by the second reinforcing layer bonded to the base plate, the warping of the base plate is generated by the second reinforcing layer even when the base plate is made of MDF. Therefore, the entire wooden flooring can be prevented from warping. In addition, since the second reinforcing layer is configured so that the adhesive can penetrate in the front and back directions, the work of bonding the base plate and the cushioning material can be simplified, as in the case of bonding the base plate and the decorative veneer. It is.
【0013】また、この場合、第2補強層が、ガラス織
布およびガラス組布の一方で構成されていることが好ま
しい。In this case, it is preferable that the second reinforcing layer is formed of one of a glass woven fabric and a glass braid.
【0014】この構成では、第2補強層として、比較的
剛性の高いガラス織布またはガラス組布が用いられるの
で、木質床材の反りをより確実に防止することができ
る。In this configuration, since a relatively rigid glass woven fabric or glass braid is used as the second reinforcing layer, the warp of the wooden flooring can be more reliably prevented.
【0015】[0015]
【発明の実施の形態】以下、本発明の好ましい実施形態
を、図面を参照しながら説明する。図1は、本発明の第
1実施形態による木質床材(以下、単に「床材」とい
う)を分解状態で示している。同図に示すように、この
床材1は、表側から順に、化粧単板2、第1補強層3
(補強層)、台板4、第2補強層5およびクッション材
6の5層構造を有している。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a preferred embodiment of the present invention will be described with reference to the drawings. FIG. 1 shows a wooden flooring (hereinafter simply referred to as “flooring”) according to a first embodiment of the present invention in an exploded state. As shown in the figure, this flooring 1 is composed of a decorative veneer 2 and a first reinforcing layer 3 in order from the front side.
(Reinforcing layer), a base plate 4, a second reinforcing layer 5, and a cushion material 6.
【0016】化粧単板2は、厚さ0.25mm程度の楢
やカバなどから成る無垢板で構成されている。第1補強
層3は、主として化粧単板2を補強するためのものであ
り、厚さ0.1〜0.2mm程度のガラス織布やガラス
組布などで構成されている。台板4は、厚さ6〜9mm
程度のラワン合板やMDFなどで構成されており、その
裏面には溝7が形成されている。The decorative veneer 2 is made of a solid board made of oak or hippo having a thickness of about 0.25 mm. The first reinforcing layer 3 is mainly for reinforcing the decorative veneer 2 and is made of a glass woven fabric or a glass braid having a thickness of about 0.1 to 0.2 mm. The base plate 4 is 6 to 9 mm thick
It is made of rawan plywood, MDF or the like, and a groove 7 is formed on the back surface thereof.
【0017】第2補強層5は、主として台板4の反りを
防止するためのものであり、第1補強層3と同様、ガラ
ス織布やガラス組布などで構成されており、その厚さ
は、0.2mm程度である。クッション材6は、厚さ3
〜6mm程度の発泡ウレタンなどで構成されている。以
上の構成の材料2〜6を順に積層し、接着することによ
って、床材1が形成され、全体として12〜15mm程
度の板厚に仕上げられる。The second reinforcing layer 5 is mainly for preventing warpage of the base plate 4 and, like the first reinforcing layer 3, is made of glass woven fabric or glass braided cloth, and has a thickness. Is about 0.2 mm. The cushion material 6 has a thickness of 3
It is made of urethane foam of about 6 mm or so. The flooring material 1 is formed by sequentially laminating and adhering the materials 2 to 6 having the above-described configurations, and is finished to a thickness of about 12 to 15 mm as a whole.
【0018】以上の構成の床材1によれば、台板4と化
粧単板2との間に介在し、接着された第1補強層3によ
って、化粧単板2が拘束されることにより、その表面の
割れの発生を防止できるとともに、第1補強層によって
化粧単板2の硬度が補強されることにより、床材1の表
面の凹みを抑制することができる。また、台板4に接着
された第2補強層によって、台板4の撓みを直接、拘束
するので、台板4をMDFで構成した場合でも、台板4
の反りを防止でき、したがって、床材1全体の反りを防
止することができる。According to the flooring material 1 having the above-described structure, the decorative veneer 2 is restrained by the first reinforcing layer 3 which is interposed between the base plate 4 and the veneer veneer 2 and adhered. The generation of cracks on the surface can be prevented, and the hardness of the decorative veneer 2 is reinforced by the first reinforcing layer, so that dents on the surface of the flooring 1 can be suppressed. Further, since the bending of the base plate 4 is directly restrained by the second reinforcing layer bonded to the base plate 4, even when the base plate 4 is formed of the MDF, the base plate 4 may be used.
Of the floor material 1 can be prevented.
【0019】さらに、この第1および第2の補強層3、
5を構成するガラス織布やガラス組布は、その表裏方向
に接着剤が浸透可能である。したがって、第1および第
2の補強層3、5の表裏面の一方に接着剤を塗布するだ
けで、台板4と化粧単板2、および台板4とクッション
材6を、それぞれ相互に接着することができる。したが
って、第1および第2の補強層3、5を構成要素に加え
ることにより接着作業の負担を増大させることはなく、
特に、和紙を補強層とし、和紙に接着剤を塗布しなかっ
た従来と比較し、接着作業を簡素化でき、その分、製造
コストを削減することができる。Further, the first and second reinforcing layers 3,
In the glass woven fabric and the glass braid fabric constituting 5, the adhesive can penetrate in the front and back directions. Therefore, the base plate 4 and the decorative veneer 2 and the base plate 4 and the cushion material 6 are bonded to each other only by applying an adhesive to one of the front and back surfaces of the first and second reinforcing layers 3 and 5. can do. Therefore, adding the first and second reinforcing layers 3 and 5 to the components does not increase the burden of the bonding operation,
In particular, the bonding operation can be simplified and the manufacturing cost can be reduced accordingly, as compared with the conventional case where the washi is used as the reinforcing layer and the adhesive is not applied to the washi.
【0020】図2は、本発明の第2実施形態による床材
を示している。この床材11は、台板12を3層構造、
すなわち、上から順にMDF13、第3補強層14およ
びラワン合板15で構成するとともに、他の部分は第1
実施形態の床材1と同様に構成し、床材11全体として
7層構造としたものである。第3補強層14は、MDF
13およびラワン合板15の反りを防止するためのもの
であり、第2補強層5と同様、ガラス織布やガラス組布
で構成されている。他の構成は、前述した第1実施形態
と同じであるので、同じ構成要素については、同じ参照
番号を付して、詳細な説明は省略する。FIG. 2 shows a flooring according to a second embodiment of the present invention. This flooring 11 has a base plate 12 having a three-layer structure,
That is, the MDF 13, the third reinforcing layer 14, and the Lauan plywood 15 are arranged in this order from the top, and the other parts are the first
The flooring 1 has the same structure as the flooring 1 of the embodiment, and has a seven-layer structure as a whole. The third reinforcing layer 14 is made of MDF
The second reinforcing layer 5 is made of a glass woven fabric or a glass braid, similarly to the second reinforcing layer 5. The other configuration is the same as that of the above-described first embodiment. Therefore, the same components are denoted by the same reference numerals, and detailed description will be omitted.
【0021】したがって、本実施形態の床材11では、
第1実施形態の床材1で得られる効果に加えて、第2お
よび第3の補強層14により、MDF13およびラワン
合板15の反りを防止することによって、床材11の反
りを防止することができる。Therefore, in the flooring material 11 of the present embodiment,
In addition to the effect obtained by the flooring 1 of the first embodiment, the second and third reinforcing layers 14 prevent the MDF 13 and the Lauan plywood 15 from warping, thereby preventing the flooring 11 from warping. it can.
【0022】次に、床材の補強層として、ガラス織布や
ガラス組布を用いた場合の、前述した反り防止効果を確
認するために実施した試験について説明する。この試験
は、以下の条件により、試験体を作製するとともに、そ
の初期反り量、およびその後の経時的な変化反り量を測
定したものである。 A.試験体の構成 図3に示すように、各厚さが2.5mmの3層のラワン
単板21、21、21を積層した7.5mm厚の合板構
成とし、各2枚のラワン単板21、21間に、 ガラス繊維を挿入しないもの、ガラス繊維22とし
て、ガラス不織布、ガラス織布、ガラス組布をそ
れぞれ挿入した試験体Sをそれぞれ用意した(表1参
照)。およびの試験体は、本発明の実施形態による
ものに相当する一方、ガラス繊維を挿入していないの
試験体、およびガラス不織布が接着剤の浸透性を有しな
いの試験体は、比較のためのものである。各試験体S
の寸法は、厚さ7.5×長さ367×幅56mmであ
る。また、接着剤は、水性ビニルウレタンとレゾルシノ
ールをそれぞれ使用した。 B.試験数 それぞれ1体とした。 C.初期反り量 上記構成の試験体Sの接着を完了してから1週間後に、
各試験体Sの反り量(矢高)を測定し、初期反り量とし
た。なお、「矢高」とは、図4に符号Aで示すように、
試験体Sが反ったときの凹側の面の長さ方向の両端間を
結ぶ線からその面の頂点までの距離として定義される。 D.変化反り量 上記初期反り量の測定後、試験体SをASTM試験に準
じた温湿度条件中に投入し、各試験体Sの初期反り量を
基準とした相対的変化量を、変化反り量として測定し
た。なお、この温湿度条件とは、具体的には、23℃・
95%・24時間→48℃・28%・24時間→23℃
・95%・72時間→48℃・28%・48時間であ
る。また、図4に示すように、このような条件変化にお
いて、乾燥→湿潤の条件変化の場合と、湿潤→乾燥の条
件変化の場合とで、試験体の反りの方向が互いに異なっ
たため、変化反り量を、乾燥→湿潤の場合の反り方向の
値を負値(−)とし(図4(b))、逆の場合の反り方
向の値を正値(+)として(図4(a))、それぞれ表
示した。Next, a description will be given of a test conducted to confirm the above-described effect of preventing warpage when a glass woven fabric or a glass braid is used as a reinforcing layer of a flooring material. In this test, a test body was prepared under the following conditions, and the initial warpage amount and the subsequent warpage change warpage amount were measured. A. 3. Structure of Test Specimen As shown in FIG. , 21 were prepared without glass fiber inserted, and as a glass fiber 22, a specimen S in which a glass non-woven fabric, a glass woven fabric, and a glass braid were inserted respectively was prepared (see Table 1). The and test specimens correspond to those according to the embodiment of the present invention, whereas the test specimen without glass fiber inserted and the test specimen with glass non-woven fabric having no adhesive permeability were used for comparison. Things. Each specimen S
Has a thickness of 7.5 × length of 367 × width of 56 mm. As the adhesive, aqueous vinyl urethane and resorcinol were used. B. The number of tests was one each. C. Initial warpage One week after completing the adhesion of the specimen S having the above configuration,
The amount of warpage (arrow height) of each test piece S was measured and used as the initial amount of warpage. In addition, "arrow height" means, as shown by the symbol A in FIG.
It is defined as the distance from a line connecting both ends in the length direction of the concave surface when the specimen S is warped to the vertex of the surface. D. After measuring the initial warpage amount, the test specimen S is put into a temperature and humidity condition according to the ASTM test, and a relative change amount based on the initial warpage amount of each test specimen S is defined as a change warpage amount. It was measured. The temperature and humidity conditions are, specifically, 23 ° C.
95% / 24 hours → 48 ° C / 28% / 24 hours → 23 ° C
・ 95% ・ 72 hours → 48 ° C. ・ 28% ・ 48 hours. In addition, as shown in FIG. 4, in such a condition change, the direction of the warp of the test specimen was different between the case of the change of the condition of dry → wet and the case of the change of the condition of wet → dry. As for the amount, the value of the warping direction in the case of dry → wet is defined as a negative value (−) (FIG. 4B), and the value of the warping direction in the opposite case is defined as a positive value (+) (FIG. 4A). , Respectively.
【0023】以上のようにして測定した各試験体Sの初
期反り量を、表1および図5に示す。これらの図表か
ら、ラワン単板21、21間にガラス織布またはガラス
組布を挿入した場合の初期反り量が、ガラス不織布を挿
入した場合と同様、0.4〜1.1mmであるのに対
し、挿入しない場合の初期反り量は1.8〜4.5mm
であり、ガラス織布などの挿入によって、反りを大幅に
抑制できることがわかる。The initial warpage of each specimen S measured as described above is shown in Table 1 and FIG. From these charts, it can be seen that the initial warpage when the glass woven fabric or the glass braid is inserted between the Lauan veneers 21 and 21 is 0.4 to 1.1 mm as in the case where the glass nonwoven fabric is inserted. On the other hand, the initial warpage when not inserted is 1.8 to 4.5 mm.
It can be seen that the warpage can be greatly suppressed by inserting a glass woven cloth or the like.
【0024】[0024]
【表1】 [Table 1]
【0025】また、各試験体Sの変化反り量を、表2な
らびに図6および図7に示す。これらの図表から、ガラ
ス織布またはガラス組布を挿入した試験体Sは、挿入し
ていないものと比較して、変化反り量が非常に小さく、
ガラス織布などの挿入によって、反り量の経時的変化も
大幅に抑制でき、反りの少ない状態を安定して維持でき
ることがわかる。Table 2 and FIGS. 6 and 7 show the amount of change in warpage of each specimen S. From these charts, the specimen S into which the glass woven fabric or the glass braid is inserted has a very small amount of change warpage as compared with the specimen without the insertion.
It can be seen that the time-dependent change in the amount of warpage can be greatly suppressed by inserting a glass woven cloth or the like, and a state in which warpage is small can be stably maintained.
【0026】[0026]
【表2】 [Table 2]
【0027】なお、本発明は、説明した実施形態に限定
されることなく、種々の態様で実施することができる。
例えば、実施形態では、化粧単板と台板の間に介在する
第1補強層をガラス織布やガラス組布で構成したが、こ
の第1補強層として、化粧単板を補強でき且つ接着剤の
浸透性を有するものであれば、他の適当な材料を採用す
ることが可能である。例えば、第1補強層を寒冷紗で構
成してもよく、その場合の材質は、ガラスに限らず、レ
ーヨンなどの人工繊維や綿などの天然繊維とすることが
できる。また、裏面側に設けたクッション材を省略した
床材も、本発明の範囲内のものである。その他、本発明
の趣旨を逸脱しない範囲で、細部の構成を適宜、変更す
ることができる。The present invention is not limited to the embodiments described above, but can be implemented in various modes.
For example, in the embodiment, the first reinforcing layer interposed between the decorative veneer and the base plate is made of a glass woven fabric or a glass braided cloth. However, as the first reinforcing layer, the decorative veneer can be reinforced and the adhesive can penetrate. Other suitable materials can be employed as long as they have properties. For example, the first reinforcing layer may be made of a cold gauze. In this case, the material is not limited to glass, but may be artificial fibers such as rayon or natural fibers such as cotton. Further, a floor material in which the cushion material provided on the back side is omitted is also within the scope of the present invention. In addition, the detailed configuration can be appropriately changed without departing from the spirit of the present invention.
【0028】[0028]
【発明の効果】以上詳述したように、本発明の木質床材
は、製造コストをほとんど増大させることなく、反りの
発生を防止するとともに、表面の割れを抑制することが
できるなどの効果を有している。As described in detail above, the wood flooring material of the present invention has the effects of preventing warpage and suppressing surface cracking without substantially increasing the production cost. Have.
【図1】本発明の第1実施形態による木質床材の構成を
示す分解図である。FIG. 1 is an exploded view showing a configuration of a wooden flooring according to a first embodiment of the present invention.
【図2】本発明の第2実施形態による木質床材の構成を
示す分解図である。FIG. 2 is an exploded view showing a configuration of a wooden flooring according to a second embodiment of the present invention.
【図3】反り防止確認のための試験で用いた試験体の構
成を示す分解図である。FIG. 3 is an exploded view illustrating a configuration of a test body used in a test for preventing warpage.
【図4】試験体の反りの状況を示す分解図である。FIG. 4 is an exploded view showing a state of warpage of a test body.
【図5】試験体の初期反り量を示すグラフである。FIG. 5 is a graph showing an initial warpage amount of a test body.
【図6】接着剤として水性ビニルウレタンを用いた場合
の試験体の変化反り量を示すグラフである。FIG. 6 is a graph showing the amount of change in warpage of a test sample when aqueous vinyl urethane is used as an adhesive.
【図7】接着剤としてレゾルシノールを用いた場合の試
験体の変化反り量を示すグラフである。FIG. 7 is a graph showing the amount of change in warpage of a test sample when resorcinol is used as an adhesive.
【符号の説明】 1 木質床材 2 化粧単板 3 第1補強層 4 台板 5 第2補強層 6 クッション材 11 木質床材 12 台板 14 第3補強層[Description of Signs] 1 Wooden floor material 2 Decorative veneer 3 First reinforcing layer 4 Base plate 5 Second reinforcing layer 6 Cushion material 11 Wooden floor material 12 Base plate 14 Third reinforcing layer
Claims (4)
面に配された補強層と、 この補強層を介して、前記台板に接着された化粧単板
と、を備えていることを特徴とする木質床材。1. A wooden base plate, a reinforcing layer configured to allow an adhesive to penetrate in a front-to-back direction, a reinforcing layer disposed on a surface of the base plate, and bonded to the base plate via the reinforcing layer. A wooden flooring comprising: a decorative veneer.
および寒冷紗の1つで構成されていることを特徴とす
る、請求項1に記載の木質床材。2. The wooden flooring according to claim 1, wherein the reinforcing layer is made of one of a glass woven fabric, a glass braided fabric, and a cold gauze.
れ、前記台板の裏面に配された第2補強層と、 この第2補強層を介して、前記台板に接着されたクッシ
ョン材と、をさらに備えていることを特徴とする、請求
項1または2に記載の木質床材。3. A second reinforcing layer arranged on the back surface of the base plate so that an adhesive can penetrate in a front-to-back direction, and a cushion material bonded to the base plate via the second reinforcing layer. The wood flooring according to claim 1 or 2, further comprising:
ラス組布の一方で構成されていることを特徴とする、請
求項3に記載の木質床材。4. The wooden flooring according to claim 3, wherein the second reinforcing layer is formed of one of a glass woven fabric and a glass braided fabric.