JPH11159152A - Reinforcing method for concrete columnar body - Google Patents
Reinforcing method for concrete columnar bodyInfo
- Publication number
- JPH11159152A JPH11159152A JP34208497A JP34208497A JPH11159152A JP H11159152 A JPH11159152 A JP H11159152A JP 34208497 A JP34208497 A JP 34208497A JP 34208497 A JP34208497 A JP 34208497A JP H11159152 A JPH11159152 A JP H11159152A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- concrete
- concrete column
- reinforcing
- reinforcing fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、橋脚、地下鉄の中
柱、建築物の柱など、土木構造物或いは建築構造物のコ
ンクリート柱状体の補強方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for reinforcing concrete pillars of civil engineering structures or building structures, such as bridge piers, middle pillars of subways, and pillars of buildings.
【０００２】[0002]
【従来の技術】従来、橋脚、地下鉄の中柱、建築物の柱
などの柱状体、特に鉄筋コンクリート（ＲＣ）或いは鉄
骨鉄筋コンクリート（ＳＲＣ）にて建造されたコンクリ
ート柱のような構造物を補強する方法としては、コンク
リート柱の回りに鉄筋コンクリートを巻き立てる方法、
鋼板を貼り付ける方法、炭素繊維シートを巻き付ける方
法などがある。2. Description of the Related Art Conventionally, a method of reinforcing a columnar body such as a pier, a middle pillar of a subway, or a pillar of a building, particularly a structure such as a concrete pillar constructed of reinforced concrete (RC) or steel reinforced concrete (SRC). As a method of rolling up reinforced concrete around concrete columns,
There are a method of attaching a steel sheet and a method of winding a carbon fiber sheet.
【０００３】鉄筋コンクリート（ＲＣ）を巻き立てる方
法は、重量が増加する、新たに断面の面積が増加する、
現場にてコンクリート打設を行うために養生期間が長
く、工期が長いなどの問題がある。鋼板を貼り付ける方
法は、貼り付けた鋼板を互に溶接するか或はボルト締め
にて接合する作業が必要であり、又、鋼板の重量が重
く、作業性が悪いなどの問題がある。炭素繊維シートを
巻き付ける方法は、炭素繊維をコンクリート柱に巻き付
けたときの炭素繊維の折れ或いは応力集中を避けるため
に、予めコンクリート柱の隅角部にＲ加工（湾曲状の面
取り加工）が必要であり、又炭素繊維シートを貼り付け
るためにコンクリート柱表面の下地処理に手間がかかる
といった問題を有している。特に、作業時間の短縮が要
求される地下鉄の中柱の補強などには、更に効率的でし
かもコストの安い補強方法が希求されている。[0003] The method of rolling up reinforced concrete (RC) involves increasing the weight, newly increasing the cross-sectional area,
There are problems such as a long curing period and a long construction period because concrete is cast on site. The method of attaching the steel plates requires welding the steel plates to each other or joining them by bolting, and has the problems that the steel plates are heavy and workability is poor. The method of winding the carbon fiber sheet requires a rounding (curved chamfering) in advance at the corner of the concrete column in order to avoid breaking or stress concentration of the carbon fiber when the carbon fiber is wound around the concrete column. In addition, there is a problem that it takes time and effort to prepare the surface of the concrete pillar for attaching the carbon fiber sheet. In particular, there is a need for a more efficient and inexpensive reinforcing method for reinforcing a middle pillar of a subway, which requires a reduction in working time.
【０００４】[0004]
【発明が解決しようとする課題】このような問題を解決
するべく、図９及び図１０に示すように、鋼板１（１
Ａ、１Ｂ）と炭素繊維シート１０を使用した、即ち、上
記鋼板貼り付け方法と炭素繊維シート巻き付け方法を組
合せた補強方法が提案されている。簡単に説明すると、
次の通りである。In order to solve such a problem, as shown in FIGS. 9 and 10, a steel plate 1 (1) is used.
A, 1B) and a carbon fiber sheet 10, that is, a reinforcing method combining the above-described steel plate attaching method and the carbon fiber sheet winding method has been proposed. Briefly,
It is as follows.
【０００５】この補強方法によれば、コンクリート柱１
００の表面に対する下地処理は必要ではない。つまり、
この補強方法では、先ず、両端部３が直角に所定の半径
Ｒにて曲げられ、断面がＵ字形状とされた２枚の鋼板１
（１Ａ、１Ｂ）が準備される。この鋼板１Ａ、１Ｂは、
互に対向するようにして、柱１００の両側よりボルトな
どにて取付けられる。鋼板１Ａ、１Ｂと柱１００との間
には空隙Ｇが設けられる。又、各鋼板１Ａ、１Ｂの端部
３は、柱１００の隅角部を覆って柱１００の他の両側面
へと延在する。しかし、この端部３は、柱１００の側面
中心部までは存在していない。鋼板１Ａ、１Ｂの重量を
軽減し作業性を向上させると言う点では、この端部延長
部の長さは小さい程良い。従って、両鋼板１Ａ、１Ｂの
端部３の間にはコンクリート表面を被覆していない離間
部分（Ｌ）が存在することとなる。According to this reinforcing method, the concrete column 1
No underlying treatment is necessary for the surface of 00. That is,
In this reinforcing method, first, two steel plates 1 whose both ends 3 are bent at a right angle at a predetermined radius R and whose cross section is U-shaped.
(1A, 1B) are prepared. These steel plates 1A and 1B
The columns 100 are attached with bolts from both sides thereof so as to face each other. A gap G is provided between the steel plates 1A and 1B and the column 100. The end 3 of each of the steel plates 1A, 1B covers the corner of the column 100 and extends to the other side surface of the column 100. However, the end 3 does not exist up to the center of the side surface of the pillar 100. From the viewpoint of reducing the weight of the steel plates 1A and 1B and improving the workability, the shorter the length of the end extension, the better. Therefore, a separated portion (L) that does not cover the concrete surface exists between the end portions 3 of both steel plates 1A and 1B.
【０００６】次いで、この両鋼板の離間部分（Ｌ）を覆
って各鋼板１Ａ、１Ｂの端部３の表面に炭素繊維シート
１０が貼り付けられる。炭素繊維シート１０の両端部
は、更に、各鋼板１Ａ、１Ｂの湾曲表面に沿って他の側
面へと所定の距離だけ延在して貼り付けられる。その
後、コンクリート表面と、鋼板及び炭素繊維シートとの
間には無収縮モルタルが充填される。Next, a carbon fiber sheet 10 is attached to the surface of the end 3 of each of the steel plates 1A and 1B so as to cover the space (L) between the two steel plates. Both end portions of the carbon fiber sheet 10 are further extended along a curved surface of each of the steel plates 1A and 1B to another side surface by a predetermined distance and attached. Thereafter, a non-shrink mortar is filled between the concrete surface and the steel plate and the carbon fiber sheet.
【０００７】この方法によれば、炭素繊維シート１０
は、コンクリート表面に取付けられた鋼板１Ａ、１Ｂの
表面に貼り付けられるので、コンクリート表面に対する
下地処理は不要である。又、炭素繊維シート１０は、鋼
板１Ａ、１Ｂの湾曲した角部に沿って貼り付けられるの
で、コンクリート柱隅角部のＲ加工も必要ではない。According to this method, the carbon fiber sheet 10
Is affixed to the surfaces of the steel plates 1A and 1B attached to the concrete surface, so that a foundation treatment for the concrete surface is unnecessary. Moreover, since the carbon fiber sheet 10 is stuck along the curved corners of the steel plates 1A and 1B, it is not necessary to perform the rounding of the corners of the concrete columns.
【０００８】しかしながら、本発明者らの研究実験の結
果、通常の炭素繊維シートの施工方法では両鋼板の端部
にて形成される離間部分（Ｌ）の距離が大となればなる
程、図９及び図１０に示すように、この部分における炭
素繊維シートに下方及び内方への弛みが生じ安く、この
離間部分（Ｌ）において炭素繊維シート１０に弛みが生
じた場合には、この弛みにより炭素繊維シートによる応
力伝達が阻害され、補強効率が落ち、所期の補強効果が
得られないといった問題が発生する、ことが分かった。However, as a result of the research experiments conducted by the present inventors, as the distance between the separated portions (L) formed at the ends of the two steel sheets becomes larger in the ordinary carbon fiber sheet construction method, the figure becomes larger. As shown in FIGS. 9 and 10, the carbon fiber sheet at this portion is likely to be slacked downward and inward, and is cheap. When the carbon fiber sheet 10 is loosened at this separated portion (L), the slack is It has been found that the stress transmission by the carbon fiber sheet is hindered, the reinforcing efficiency is reduced, and the problem that the desired reinforcing effect cannot be obtained occurs.
【０００９】従って、本発明の目的は、コンクリート矩
形柱などの柱状体であっても、その下地処理及び隅角部
処理を不要とし、工期の短縮及びコストの低減を図るこ
とができ、しかも、強化繊維の拘束効果を向上させ、耐
力及び靭性の向上を図ることができ、所期の補強効果を
十分に達成することのできる、橋脚、地下鉄の中柱、建
築物の柱などのコンクリート柱状体の補強方法を提供す
ることである。Therefore, an object of the present invention is to eliminate the need for a base treatment and a corner treatment even for a columnar body such as a concrete rectangular column, thereby shortening the construction period and reducing the cost. Concrete pillars, such as bridge piers, metro pillars, and building pillars, which can improve the restraining effect of the reinforcing fiber, improve the yield strength and toughness, and sufficiently achieve the desired reinforcing effect. It is to provide a reinforcing method of.
【００１０】[0010]
【課題を解決するための手段】上記目的は本発明に係る
柱状体の補強方法にて達成される。要約すれば、本発明
の第１の態様によると、（ａ）断面が矩形とされる補強
すべきコンクリート柱状体の周囲に、外面がコンクリー
ト柱状体の周方向に湾曲し、コンクリート柱状体の軸線
方向に所定長さとされたプレキャスト成型品を据え付
け、プレキャスト成型品を据え付けた後のコンクリート
柱状体の外周囲に角部がないようにする工程、（ｂ）
前記プレキャスト成型品を据え付けた前記コンクリート
柱状体の外周囲に連続した強化繊維を巻き付け、次い
で、前記強化繊維を巻き付けたコンクリート柱状体の外
表面に樹脂を塗布して前記強化繊維に樹脂を含浸させる
か、又は、 前記プレキャスト成型品を据え付けた前記コンクリー
ト柱状体の外周囲に樹脂を塗布し、その上から連続した
強化繊維を巻き付け、必要に応じて、更に前記強化繊維
を巻き付けたコンクリート柱状体の外表面に樹脂を塗布
して前記強化繊維に樹脂を含浸させる、ようにした強化
繊維の巻き付け及び樹脂含浸工程、（ｃ）次いで、前記
強化繊維に含浸された樹脂を硬化する工程、を有するこ
とを特徴とするコンクリート柱状体の補強方法が提供さ
れる。The above object is achieved by a method for reinforcing a columnar body according to the present invention. In summary, according to the first aspect of the present invention, (a) around a concrete column to be reinforced having a rectangular cross section, the outer surface is curved in the circumferential direction of the concrete column, and the axis of the concrete column is (B) installing a precast molded product having a predetermined length in the direction so that there is no corner around the outer periphery of the concrete column after the precast molded product is installed;
A continuous reinforcing fiber is wound around the outer periphery of the concrete column on which the precast molded product is installed, and then a resin is applied to the outer surface of the concrete column around which the reinforcing fiber is wound to impregnate the reinforcing fiber with the resin. Or, a resin is applied to the outer periphery of the concrete column on which the precast molded product is installed, and a continuous reinforcing fiber is wound thereon, and, if necessary, a concrete column further wound with the reinforcing fiber. A step of applying a resin to the outer surface to impregnate the reinforcing fiber with the resin, and a step of winding the reinforcing fiber and impregnating the resin, and (c) then curing the resin impregnated in the reinforcing fiber. A method for reinforcing a concrete column is provided.
【００１１】本発明の第２の態様によると、（ａ）断面
が矩形とされる補強すべきコンクリート柱状体の周囲
に、外面がコンクリート柱状体の周方向に湾曲し、コン
クリート柱状体の軸線方向に所定長さとされたプレキャ
スト成型品を据え付け、プレキャスト成型品を据え付け
た後のコンクリート柱状体の外周囲に角部がないように
する工程、（ｂ）前記プレキャスト成型品を据え付けた
前記コンクリート柱状体の外周囲に、樹脂が塗布された
連続した強化繊維を巻き付ける工程、（ｃ）次いで、前
記樹脂を硬化する工程、を有することを特徴とするコン
クリート柱状体の補強方法が提供される。According to the second aspect of the present invention, (a) around the concrete column to be reinforced, whose cross section is rectangular, the outer surface is curved in the circumferential direction of the concrete column, and the axial direction of the concrete column is Installing a precast molded product having a predetermined length on the concrete column, so that there is no corner around the concrete column after the precast molded product is installed, (b) the concrete column having the precast molded product installed thereon. A step of winding a continuous reinforcing fiber coated with a resin around the outer periphery of the resin, and (c) a step of curing the resin.
【００１２】本発明の第３の態様によると、（ａ）断面
が矩形とされる補強すべきコンクリート柱状体の周囲
に、外面がコンクリート柱状体の周方向に湾曲し、コン
クリート柱状体の軸線方向に所定長さとされたプレキャ
スト成型品を据え付け、プレキャスト成型品を据え付け
た後のコンクリート柱状体の外周囲に角部がないように
する工程、（ｂ）支持シート上に強化繊維を一方向に
配列して形成される強化繊維シート表面に樹脂を塗布し
て強化繊維に樹脂を含浸させた後、前記プレキャスト成
型品を据え付けた前記コンクリート柱状体の外周面に貼
り付けるか、 前記コンクリート柱状体の外周面に樹脂を塗布し、そ
の上から強化繊維シートを貼り付け、前記コンクリート
柱状体の外周面へと押しつけることによって、強化繊維
に樹脂を含浸させ、必要に応じて、更に強化繊維シート
表面に樹脂を塗布するか、又は、 前記コンクリート柱状体の外周面にプライマを塗布
し、その上から強化繊維シートを貼り付け、その後、強
化繊維シートに樹脂を塗布して強化繊維に含浸させる、
ようにした強化繊維シートの巻き付け及び樹脂含浸工
程、（ｃ）次いで、前記強化繊維に含浸された樹脂を硬
化する工程、を有することを特徴とするコンクリート柱
状体の補強方法が提供される。According to a third aspect of the present invention, (a) around a concrete column to be reinforced having a rectangular cross section, the outer surface is curved in the circumferential direction of the concrete column, and the axial direction of the concrete column is (B) arranging reinforcing fibers in one direction on a support sheet, wherein a precast molded product having a predetermined length is installed on the support sheet so that there is no corner around the concrete column after the precast molded product is installed. After the resin is applied to the surface of the reinforcing fiber sheet formed by impregnating the reinforcing fiber with the resin, the precast molded product is attached to the outer peripheral surface of the concrete column, or the outer periphery of the concrete column. A resin is applied to the surface, a reinforcing fiber sheet is adhered from above, and pressed against the outer peripheral surface of the concrete column, whereby the reinforcing fiber contains the resin. Dipping, if necessary, further applying a resin to the surface of the reinforcing fiber sheet, or applying a primer to the outer peripheral surface of the concrete columnar body, pasting the reinforcing fiber sheet thereon, and then reinforcing the fiber sheet Apply resin to impregnate the reinforcing fibers,
A method of reinforcing a concrete columnar body, comprising the steps of winding the reinforcing fiber sheet and impregnating the resin as described above, and (c) subsequently curing the resin impregnated in the reinforcing fiber.
【００１３】本発明の第４の態様によると、（ａ）断面
が矩形とされる補強すべきコンクリート柱状体の周囲
に、外面がコンクリート柱状体の周方向に湾曲し、コン
クリート柱状体の軸線方向に所定長さとされたプレキャ
スト成型品を据え付け、プレキャスト成型品を据え付け
た後のコンクリート柱状体の外周囲に角部がないように
する工程、（ｂ）必要に応じて前記コンクリート柱状体
の外周面にプライマを塗布し、その後、一方向に配列さ
れた強化繊維に樹脂を含浸させて形成される繊維強化プ
リプレグを、前記プレキャスト成型品を据え付けた前記
コンクリート柱状体の外周面に貼り付ける工程、（ｃ）
次いで、前記強化繊維に含浸された樹脂を硬化する工
程、を有することを特徴とするコンクリート柱状体の補
強方法が提供される。According to a fourth aspect of the present invention, (a) around a concrete column to be reinforced having a rectangular cross section, the outer surface is curved in the circumferential direction of the concrete column, and the axial direction of the concrete column is Installing a precast molded product having a predetermined length on the outer surface of the concrete column after the precast molded product is installed, and (b) an outer peripheral surface of the concrete column as necessary. A step of applying a primer to the concrete column, and then attaching a fiber-reinforced prepreg formed by impregnating a resin to the reinforcing fibers arranged in one direction to an outer peripheral surface of the concrete columnar body on which the precast molded product is installed, ( c)
Next, a step of curing the resin impregnated in the reinforcing fibers is provided.
【００１４】上記各発明にて、一実施態様によると、前
記コンクリート柱状体は、断面が矩形とされ、前記プレ
キャスト成型品は、前記コンクリート柱状体の各面に据
え付けられるか、或いは、前記コンクリート柱状体のい
ずれかの対向する両面に据え付けられる。又、本発明の
前記プレキャスト成型品は、プレキャストコンクリート
とすることができる。In one embodiment of the present invention, the concrete column has a rectangular cross section, and the precast molded product is installed on each surface of the concrete column, or the concrete column is Mounted on either opposing side of the body. Further, the precast molded product of the present invention can be precast concrete.
【００１５】好ましくは、前記強化繊維が巻き付けられ
た前記柱状体外表面にモルタルを塗るか、樹脂を吹き付
け、仕上げをなすことができる。Preferably, mortar is applied to the outer surface of the columnar body around which the reinforcing fibers are wound, or a resin is sprayed on the outer surface to finish the mortar.
【００１６】好ましくは、前記強化繊維は、炭素繊維；
ガラス繊維；ボロン、チタン、スチールなどの金属繊
維；アラミド、ポリエステル、ナイロンなどの有機繊
維；などから選択されるいずれかの繊維であるか、或い
は、前記繊維を複数種混入したハイブリッドタイプとさ
れる。又、前記樹脂は、少なくとも常温硬化型エポキシ
樹脂、熱硬化型エポキシ樹脂若しくはポリエステル系樹
脂；ポリアミド樹脂若しくはポリカーボネート樹脂；又
は、ＭＭＡなどのラジカル反応系樹脂を含む。Preferably, the reinforcing fibers are carbon fibers;
Any fiber selected from glass fibers; metal fibers such as boron, titanium, steel, and the like; organic fibers such as aramid, polyester, and nylon; or a hybrid type in which a plurality of the fibers are mixed. . Further, the resin includes at least a room-temperature curing epoxy resin, a thermosetting epoxy resin or a polyester resin; a polyamide resin or a polycarbonate resin; or a radical reaction resin such as MMA.
【００１７】[0017]
【発明の実施の形態】以下、本発明に係るコンクリート
柱状体の補強方法を図面に則して更に詳しく説明する。
図１〜図３を参照して、本発明の補強方法を、断面が矩
形とされる、本実施例では正方形（Ｗ１＝Ｗ２）の断面
とされる地下鉄の中柱のようなコンクリート矩形柱１０
０に適用した場合について説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a method of reinforcing a concrete column according to the present invention will be described in more detail with reference to the drawings.
Referring to FIGS. 1 to 3, the reinforcing method of the present invention is applied to a concrete rectangular pillar 10 such as a middle pillar of a subway which has a rectangular cross section, and in this embodiment, has a square (W1 = W2) cross section.
The case of applying to 0 will be described.
【００１８】本発明に従うと、コンクリート矩形柱１０
０の周囲の各側面に、予め、このコンクリート矩形柱１
００の断面寸法に合わせて作製されたプレキャスト成型
品２０が適合される。プレキャスト成型品２０は、外面
２０Ａがコンクリート矩形柱１００の周方向に湾曲した
湾曲面とされ、コンクリート矩形柱１００に適合される
他面２０Ｂは、本実施例では平面とされ、その幅（Ｗ）
は、コンクリート矩形柱１００の幅（Ｗ１＝Ｗ２）と同
じとされる。また、プレキャスト成型品２０のコンクリ
ート柱１００の軸線方向に沿った長さ（Ｌ）は、必要に
応じて種々の寸法とされる。このプレキャスト成型品２
０は、予め既設の工場或いは現場近くの仮設工場にて作
製される。通常、プレキャスト成型品２０は、プレキャ
ストコンクリートとされ、普通コンクリート、軽量骨材
コンクリート、気泡コンクリートなどから成る。斯かる
プレキャストコンクリート２０は、図２に示すように、
コンクリート矩形柱１００の各側面に接着剤、或いはボ
ルト（図示せず）などを使用して固定し、据え付けられ
る。According to the present invention, a concrete rectangular column 10
0 on each side around this concrete
A precast molded product 20 made to fit the section size of 00 is fitted. The outer surface 20A of the precast molded product 20 is a curved surface curved in the circumferential direction of the concrete rectangular column 100, and the other surface 20B adapted to the concrete rectangular column 100 is a flat surface in the present embodiment, and its width (W).
Is the same as the width (W1 = W2) of the concrete rectangular column 100. The length (L) of the precast molded product 20 along the axial direction of the concrete column 100 is set to various dimensions as needed. This precast molded product 2
0 is prepared in an existing factory or a temporary factory near the site in advance. Usually, the precast molded product 20 is precast concrete and is made of ordinary concrete, lightweight aggregate concrete, cellular concrete, or the like. Such precast concrete 20, as shown in FIG.
It is fixed to each side of the concrete rectangular column 100 using an adhesive or a bolt (not shown) or the like and installed.
【００１９】コンクリート矩形中の各側面に固定し、据
え付けられた各プレキャストコンクリート２０にて画成
されるコンクリート柱１００の周方向外側湾曲面は、段
差のない一つの連続した閉曲面とされる。例えば、本実
施例のように、コンクリート柱１００が正方形（Ｗ１＝
Ｗ２）の断面とされる場合には、プレキャストコンクリ
ート２０を取り付けた後の各プレキャストコンクリート
２０にて画成される外側湾曲面の断面形状は、図３をも
参照すると理解されるように、円形とされる。又、図４
に示すように、長方形（Ｗ１＞Ｗ２）の断面を有するコ
ンクリート柱１００の場合には、プレキャストコンクリ
ート２０を取り付けた後の各プレキャストコンクリート
２０にて画成される外側湾曲面の断面形状は楕円形とさ
れる。The circumferentially outer curved surface of the concrete column 100 defined by each precast concrete 20 fixed and installed on each side surface of the concrete rectangle is a single continuous curved surface with no steps. For example, as in this embodiment, the concrete column 100 is square (W1 =
In the case of the cross section of W2), the cross-sectional shape of the outer curved surface defined by each precast concrete 20 after the precast concrete 20 is attached is circular as understood with reference to FIG. It is said. Also, FIG.
As shown in the figure, in the case of the concrete column 100 having a rectangular (W1> W2) cross section, the cross-sectional shape of the outer curved surface defined by each precast concrete 20 after the precast concrete 20 is attached is elliptical. It is said.
【００２０】上記説明では、プレキャストコンクリート
２０は、コンクリート矩形柱１００の各側面に設置する
ものとしたが、例えば図５に示すように、プレキャスト
コンクリート２０は、コンクリート矩形柱１００のいず
れかの対向する両面にのみ設置することができる。図５
に示すように、断面が長方形のコンクリート矩形柱１０
０の場合には、対向する長辺側のプレキャストコンクリ
ート２０を省略した方が、プレキャストコンクリート２
０の小型化の点などで好適である。In the above description, the precast concrete 20 is installed on each side of the concrete rectangular column 100. However, for example, as shown in FIG. Can be installed only on both sides. FIG.
As shown in FIG.
In the case of 0, it is better to omit the opposing precast concrete 20 on the long side.
It is suitable in terms of miniaturization of zero.
【００２１】上述のようにして、プレキャストコンクリ
ート２０がコンクリート矩形柱１００の所望の側面に接
着剤或いはボルトなどを使用して据え付けられると、そ
の外周面に連続した炭素繊維のような強化繊維３０が巻
き付けられる。この時、強化繊維３０は、必要に応じ
て、プレキャストコンクリート２０の外表面を軸線方向
に所定幅に亘って往復して巻き付け、複数層を形成する
ように巻き付けても良い。As described above, when the precast concrete 20 is installed on a desired side surface of the concrete rectangular column 100 using an adhesive or a bolt, a reinforcing fiber 30 such as a carbon fiber continuous on the outer peripheral surface thereof is formed. It is wound. At this time, the reinforcing fibers 30 may be wound around the outer surface of the precast concrete 20 in a reciprocating manner over a predetermined width in the axial direction, if necessary, to form a plurality of layers.
【００２２】炭素繊維３０は、各プレキャストコンクリ
ート２０、場合によってはコンクリート柱１００によっ
て画成される湾曲表面に沿って変形し、密着され、巻き
付け時に繊維が折れるようなことはない。このとき、プ
レキャストコンクリート２０の表面には、必須ではない
が、プライマを塗布しておくことが好ましい。その後、
炭素繊維３０が巻き付けられた表面にマトリクス樹脂が
含浸され、必要に応じて加熱することにより、硬化され
る。The carbon fibers 30 are deformed and adhered along the curved surface defined by each precast concrete 20, and possibly the concrete columns 100, so that the fibers do not break during winding. At this time, it is preferable, but not essential, to apply a primer to the surface of the precast concrete 20. afterwards,
The surface around which the carbon fibers 30 are wound is impregnated with a matrix resin, and is cured by heating if necessary.
【００２３】炭素繊維３０は、ＰＡＮ系繊維、ピッチ系
繊維などを使用することができ、炭素繊維の物性は、好
ましくは、弾性率は１．５×１０6 〜７．０×１０6 ｋ
ｇｆ／ｃｍ2 、引張強度は５０００〜７００００ｋｇｆ
／ｃｍ2 とされ、炭素繊維の目付量は、好ましくは１０
〜１０００ｇ／ｍ2 とされる。As the carbon fibers 30, PAN fibers, pitch fibers, and the like can be used. The physical properties of the carbon fibers are preferably 1.5 × 10 6 to 7.0 × 10 6 k.
gf / cm 2 , tensile strength is 5,000 to 70,000 kgf
/ Cm 2 and the basis weight of the carbon fiber is preferably 10
１０００1000 g / m 2 .
【００２４】強化繊維３０は、炭素繊維のみに限定され
るものではなく、その他に、ガラス繊維；ボロン、チタ
ン、スチールなどの金属繊維；アラミド、ポリエステ
ル、ナイロンなどの有機繊維；などを使用することもで
きる。又、必要に応じて、斯かる繊維を複数種混入して
ハイブリッドタイプとして使用することも可能である。
又、マトリクス樹脂としては、常温硬化型或は熱硬化型
のエポキシ樹脂、ポリエステル系樹脂などの熱硬化性樹
脂、又、所望に応じてポリアミド樹脂、ポリカーボネー
ト樹脂などの熱可塑性樹脂、更にはＭＭＡなどのラジカ
ル反応系樹脂を含むものを使用することができる。The reinforcing fibers 30 are not limited to carbon fibers, but may be glass fibers; metal fibers such as boron, titanium, and steel; and organic fibers such as aramid, polyester, and nylon. Can also. If necessary, a plurality of such fibers may be mixed and used as a hybrid type.
As the matrix resin, a room temperature or thermosetting epoxy resin, a thermosetting resin such as a polyester resin, or a thermoplastic resin such as a polyamide resin or a polycarbonate resin as required, and further, a MMA or the like Those containing a radical reaction type resin can be used.
【００２５】含浸した樹脂を硬化した後、炭素繊維のよ
うな強化繊維３０が巻き付けられた表面には仕上げモル
タルを塗るか、或いは塗料などを吹き付けて、仕上げを
行うことができる。After the impregnated resin is cured, the surface around which the reinforcing fibers 30 such as carbon fibers are wound can be finished by applying a finishing mortar or spraying a paint or the like.
【００２６】上述のように、本発明の補強方法による
と、コンクリート柱１００にプレキャスト成型品２０を
設置することにより、強化繊維３０を巻き付ける外周面
に角部がなくなくなるために、連続繊維巻き付け補強の
際に従来行われていたコンクリート柱１００の角部のＲ
加工が必要なくなる。又、鉄筋コンクリート（ＲＣ）を
巻き立てる方法に比べると、現場にてコンクリート打設
を行う必要もなく、養生期間が短く、施工性も良い。As described above, according to the reinforcing method of the present invention, by installing the precast molded product 20 on the concrete column 100, there is no corner on the outer peripheral surface around which the reinforcing fiber 30 is wound. At the corner of the concrete column 100 which has been conventionally performed
No processing is required. Further, compared with the method of rolling up reinforced concrete (RC), there is no need to cast concrete on site, the curing period is short, and the workability is good.
【００２７】又、本発明によれば、連続繊維３０で囲む
断面がプレキャスト成型品を使用することにより、コン
クリート矩形柱１００の矩形から円形或いは楕円形、又
は長円形となるために、より一層の拘束効果を得ること
ができ、その結果、特に靭性能力の大幅な向上が期待で
きる。Further, according to the present invention, the cross section surrounded by the continuous fibers 30 is changed from the rectangular shape of the concrete rectangular column 100 to a circular shape, an elliptical shape, or an oval shape by using a precast molded product. A restraining effect can be obtained, and as a result, a particularly significant improvement in toughness can be expected.
【００２８】本発明の補強方法によれば、図６（Ａ）に
示すように、コンクリート柱１００の全体に適用するこ
ともでき、又、図６（Ｂ）に示すように、柱頭、柱脚の
一部に適用することもできる。特に、靭性補強のみを目
的とした場合には、図６（Ｂ）に示すように、補強範囲
をコンクリート柱１００の上下領域に限定することによ
り、内空間をそれほど占有せずに補強することができ、
工期も短縮することが可能となる。According to the reinforcing method of the present invention, as shown in FIG. 6 (A), it can be applied to the entire concrete column 100, and as shown in FIG. It can also be applied to a part of. In particular, when the purpose is only toughening, as shown in FIG. 6B, the reinforcing range is limited to the upper and lower regions of the concrete column 100, so that the reinforcing can be performed without occupying much of the inner space. Can,
The construction period can be shortened.
【００２９】実施例２ 上記実施例１では、コンクリート矩形柱１００に据え付
けられたプレキャストコンクリート２０の外周面に連続
した炭素繊維のような強化繊維３０を巻き付け、その後
強化繊維３０が巻き付けられた表面にマトリクス樹脂を
含浸し、硬化するものとして説明したが、プレキャスト
コンクリート２０の外周面に（図５に示すような場合に
はコンクリート矩形柱１００の外周面にも）マトリクス
樹脂を塗布し、引き続いて、強化繊維３０を巻き付ける
こともできる。必要に応じて、更に、強化繊維３０が巻
き付けられた表面にマトリクス樹脂を塗布しても良い。
その後、マトリクス樹脂は、必要に応じて加熱すること
により、硬化される。Example 2 In Example 1, the reinforcing fibers 30 such as continuous carbon fibers are wound around the outer peripheral surface of the precast concrete 20 installed on the concrete rectangular column 100, and then the reinforcing fibers 30 are wound around the surface. Although it has been described that the matrix resin is impregnated and cured, the matrix resin is applied to the outer peripheral surface of the precast concrete 20 (and also to the outer peripheral surface of the concrete rectangular column 100 in the case as shown in FIG. 5). The reinforcing fibers 30 can also be wound. If necessary, a matrix resin may be applied to the surface around which the reinforcing fibers 30 are wound.
Thereafter, the matrix resin is cured by heating if necessary.
【００３０】強化繊維３０及びマトリクス樹脂は、実施
例１で説明したと同じものを使用し、実施例１と同様の
方法にて実施し得る。As the reinforcing fibers 30 and the matrix resin, the same ones as described in the first embodiment can be used, and can be carried out in the same manner as in the first embodiment.
【００３１】本実施例によっても、実施例１と同様の効
果を達成し得る。According to this embodiment, the same effect as that of the first embodiment can be achieved.
【００３２】実施例３ 上記実施例１及び２では、コンクリート矩形柱１００に
据え付けられたプレキャストコンクリート２０の外周面
に連続した炭素繊維のような強化繊維３０が巻き付けら
れ、その後マトリクス樹脂を含浸させるか、或いはプレ
キャストコンクリート２０等の外周面にマトリクス樹脂
を塗布しておき、この樹脂塗布表面に強化繊維を巻き付
けるものとしたが、強化繊維３０に予めマトリクス樹脂
を含浸しておき、プレキャストコンクリート２０等の外
周面にこの樹脂含浸強化繊維３０を巻き付けることもで
きる。この場合には、好ましくは強化繊維３０を巻き付
けるプレキャストコンクリート表面等にはプライマを塗
布しておくのがよい。強化繊維に含浸されたマトリクス
樹脂は、強化繊維３０をプレキャストコンクリート２０
の外周面に巻き付けた後、硬化される。Embodiment 3 In Embodiments 1 and 2, the reinforcing fibers 30 such as continuous carbon fibers are wound around the outer peripheral surface of the precast concrete 20 installed on the concrete rectangular column 100, and then the matrix resin is impregnated. Alternatively, the matrix resin is applied to the outer peripheral surface of the precast concrete 20 or the like, and the reinforcing fiber is wound around the resin applied surface. However, the reinforcing fiber 30 is impregnated with the matrix resin in advance, and the precast concrete 20 or the like is used. The resin-impregnated reinforcing fibers 30 can be wound around the outer peripheral surface. In this case, it is preferable to apply a primer to the surface of the precast concrete around which the reinforcing fibers 30 are wound. The matrix resin impregnated with the reinforcing fibers converts the reinforcing fibers 30 into the precast concrete 20.
And then cured.
【００３３】強化繊維３０及びマトリクス樹脂は、実施
例１で説明したと同じものを使用し、実施例１と同様の
方法にて実施し得る。As the reinforcing fibers 30 and the matrix resin, the same ones as described in the first embodiment can be used, and can be carried out in the same manner as in the first embodiment.
【００３４】本実施例によっても、実施例１と同様の効
果を達成し得る。According to this embodiment, the same effect as that of the first embodiment can be achieved.
【００３５】実施例４ 上記実施例１では、コンクリート矩形柱１００に据え付
けられたプレキャストコンクリート２０の外周面には、
連続した炭素繊維のような強化繊維３０が巻き付けられ
たが、図７に示すように、強化繊維シート５０を巻き付
けることもできる。Embodiment 4 In the above-described embodiment 1, the outer peripheral surface of the precast concrete 20 installed on the concrete rectangular column 100 has:
Although the reinforcing fibers 30 such as continuous carbon fibers are wound, a reinforcing fiber sheet 50 can be wound as shown in FIG.
【００３６】強化繊維シート５０は、図８（ａ）及び
（ｂ）を参照すると、その一実施例が示されるが、支持
シート５１上に強化繊維３０を、例えば接着剤５２を介
して一方向に配列して形成される。Referring to FIGS. 8A and 8B, an example of the reinforcing fiber sheet 50 is shown. The reinforcing fiber 30 is placed on a support sheet 51 by, for example, an adhesive 52 in one direction. Are formed in an array.
【００３７】支持シート５１としては、ガラスクロス、
ガラスペーパ（不織布）、アラミド繊維クロス、或いは
アラミド不織布などが使用される。支持シート５１の厚
さは、１〜５００μｍ、好ましくは５〜１００μｍ、接
着剤５２の厚さは１〜１００μｍ、好ましくは１０〜３
０μｍとされる。強化繊維シート５０全体の厚さは１０
〜１００μｍ程度である。As the support sheet 51, a glass cloth,
Glass paper (nonwoven fabric), aramid fiber cloth, or aramid nonwoven fabric is used. The thickness of the support sheet 51 is 1 to 500 μm, preferably 5 to 100 μm, and the thickness of the adhesive 52 is 1 to 100 μm, preferably 10 to 3 μm.
0 μm. The thickness of the entire reinforcing fiber sheet 50 is 10
About 100 μm.
【００３８】強化繊維シート５０をプレキャストコンク
リート２０の外周面に（図５に示すような場合にはコン
クリート矩形柱１００の外周面にも）設置する方法とし
ては、 （１）強化繊維シート５０表面にマトリクス樹脂を塗布
し、強化繊維３０に樹脂を含浸させた後、プレキャスト
コンクリート２０の外周面に貼り付ける。 （２）プレキャストコンクリート２０の外表面にマトリ
クス樹脂を塗布し、その上から強化繊維シート５０を貼
り付け、プレキャストコンクリート表面２０へと押しつ
けることによって、強化繊維３０に樹脂を含浸させる。
必要に応じて、更に強化繊維シート５０表面に樹脂を更
に塗布することもできる。 （３）プレキャストコンクリート２０の外表面にプライ
マを塗布し、その上にマトリクス樹脂を下塗りし、その
上から強化繊維シート５０を貼り付け、その後、強化繊
維シート５０にマトリクス樹脂を上塗りして強化繊維３
０に含浸させる。方法がある。The method of installing the reinforcing fiber sheet 50 on the outer peripheral surface of the precast concrete 20 (in the case shown in FIG. 5 also on the outer peripheral surface of the concrete rectangular column 100) is as follows. After a matrix resin is applied and the reinforcing fibers 30 are impregnated with the resin, they are attached to the outer peripheral surface of the precast concrete 20. (2) The matrix resin is applied to the outer surface of the precast concrete 20, the reinforcing fiber sheet 50 is adhered from above, and the reinforcing fiber 30 is impregnated with the resin by pressing against the precast concrete surface 20.
If necessary, a resin can be further applied to the surface of the reinforcing fiber sheet 50. (3) A primer is applied to the outer surface of the precast concrete 20, a matrix resin is undercoated thereon, a reinforcing fiber sheet 50 is adhered thereon, and then the matrix resin is overcoated on the reinforcing fiber sheet 50 to obtain a reinforcing fiber. 3
0 impregnation. There is a way.
【００３９】強化繊維シート５０は、連続した長尺のも
のをコンクリート柱の周りに所定巻き数だけ巻き付ける
こともできるが、コンクリート周長より短い長さのもの
を、複数枚使用し、各シートの端部が互いに重なるよう
にして、所定枚数だけ、必要に応じて、複数層となるよ
うに積層して巻き付ける方法でも良い。作業性から言え
ば、例えば幅２０〜５０ｃｍ、長さ１〜２．５ｍの寸法
に裁断された強化繊維シート５０が便利である。As the reinforcing fiber sheet 50, a continuous long sheet can be wound around a concrete column by a predetermined number of turns. However, a plurality of sheets having a length shorter than the concrete perimeter are used. A method of laminating and winding a predetermined number of sheets such that the ends overlap each other and, if necessary, a plurality of layers may be used. In terms of workability, for example, the reinforcing fiber sheet 50 cut to a size of 20 to 50 cm in width and 1 to 2.5 m in length is convenient.
【００４０】強化繊維３０に含浸されたマトリクス樹脂
は、強化繊維３０をプレキャストコンクリート２０の外
周面に巻き付けた後、硬化される。The matrix resin impregnated in the reinforcing fibers 30 is hardened after the reinforcing fibers 30 are wound around the outer peripheral surface of the precast concrete 20.
【００４１】強化繊維３０及びマトリクス樹脂は、実施
例１で説明したと同じものを使用し、実施例１と同様の
方法にて実施し得る。The same reinforcing fibers 30 and matrix resin as those described in the first embodiment are used, and the same method as in the first embodiment can be used.
【００４２】本実施例によっても、実施例１と同様の効
果を達成し得る。According to this embodiment, the same effect as that of the first embodiment can be achieved.
【００４３】実施例５ 上記実施例４では、マトリクス樹脂が含浸されていない
強化繊維シート５０を使用する態様について説明した
が、上記強化繊維シート５０にて支持シート５１の代わ
りに離型紙を使用し、この離型紙の上に、強化繊維３０
を一方向に配列して予めマトリクス樹脂を含浸し、半硬
化状態とした当業者には周知の繊維強化プリプレグシー
ト（図示せず）を使用することもできる。Embodiment 5 In Embodiment 4 described above, the mode in which the reinforcing fiber sheet 50 not impregnated with the matrix resin is used has been described. However, the reinforcing fiber sheet 50 uses release paper instead of the support sheet 51. On this release paper, reinforcing fibers 30
May be arranged in one direction and impregnated with a matrix resin in advance to make a semi-cured state, and a fiber-reinforced prepreg sheet (not shown) well known to those skilled in the art may be used.
【００４４】繊維強化プリプレグシートは、好ましく
は、プライマを塗布したプレキャストコンクリート２０
の外周面に（図５に示すような場合にはコンクリート矩
形柱１００の外周面にも）貼り付けられる。The fiber reinforced prepreg sheet is preferably made of a precast concrete 20 coated with a primer.
(In the case shown in FIG. 5 also on the outer peripheral surface of the concrete rectangular column 100).
【００４５】繊維強化プリプレグシートは、連続した半
硬化状態の繊維強化プリプレグを離型紙を剥がしなが
ら、コンクリート柱の周りに所定巻き数だけ巻き付ける
こともできるが、実施例４の強化繊維シートの場合と同
様に、コンクリート周長より短い長さのものを、複数枚
使用し、各シートの端部が互いに重なるようにして、所
定枚数だけ、必要に応じて、複数層となるように積層し
て巻き付けることもできる。作業性から言えば、例えば
幅２０〜５０ｃｍ、長さ１〜２．５ｍの寸法に裁断され
た強化繊維プリプレグシートが便利である。The fiber-reinforced prepreg sheet can be wound around the concrete column by a predetermined number of turns while peeling the release paper from the continuous semi-cured fiber-reinforced prepreg. Similarly, a plurality of sheets having a length shorter than the concrete perimeter are used, and a predetermined number of sheets are stacked and wound into a plurality of layers as necessary so that the ends of the sheets overlap with each other. You can also. From the viewpoint of workability, for example, a reinforcing fiber prepreg sheet cut to a size of 20 to 50 cm in width and 1 to 2.5 m in length is convenient.
【００４６】強化繊維に含浸された半硬化状態のマトリ
クス樹脂は、繊維強化プリプレグをプレキャストコンク
リート２０の外周面に巻き付けた後、硬化される。The semi-cured matrix resin impregnated with the reinforcing fibers is cured after the fiber-reinforced prepreg is wound around the outer peripheral surface of the precast concrete 20.
【００４７】強化繊維３０は、実施例１で説明したと同
じものを使用することができ、マトリクス樹脂として
は、、少なくとも常温硬化型エポキシ樹脂、熱硬化型エ
ポキシ樹脂若しくはポリエステル系樹脂等の熱硬化性マ
トリクス樹脂が好適である。The reinforcing fibers 30 may be the same as those described in Embodiment 1, and the matrix resin may be at least a thermosetting epoxy resin, a thermosetting epoxy resin, or a thermosetting epoxy resin or the like. A suitable matrix resin is preferred.
【００４８】本実施例によっても、実施例１と同様の効
果を達成し得る。According to this embodiment, the same effect as that of the first embodiment can be achieved.
【００４９】[0049]
【発明の効果】以上説明した如くに、本発明に係るコン
クリート柱状体の補強方法は、断面が矩形とされる補強
すべきコンクリート柱状体の周囲に、外面がコンクリー
ト柱状体の周方向に湾曲し、コンクリート柱状体の軸線
方向に所定長さとされたプレキャスト成型品を据え付
け、プレキャスト成型品を据え付けた後のコンクリート
柱状体の外周囲に角部がないようにし、次いで、プレキ
ャスト成型品が据え付けられた前記コンクリート柱状体
の外周囲に、連続した強化繊維、強化繊維シート、或い
は繊維強化プリプレグ等を巻き付け、その後、巻き付け
前に或いは巻き付け後に強化繊維に含浸された樹脂を硬
化する構成とされるので、コンクリート矩形柱などの柱
状体であっても、その下地処理及び隅角部処理を不要と
し、工期の短縮及びコストの低減を図ることができ、し
かも、強化繊維の拘束効果を向上させ、耐力及び靭性の
向上を図ることができ、所期の補強効果を十分に達成す
ることができる、という作用効果を奏し得る。As described above, according to the method for reinforcing a concrete column according to the present invention, the outer surface of the concrete column having a rectangular cross section is curved in the circumferential direction of the concrete column to be reinforced. Then, a precast molded product having a predetermined length in the axial direction of the concrete column was installed, so that there was no corner around the outer periphery of the concrete column after the precast molded product was installed, and then the precast molded product was installed. Around the outer periphery of the concrete column, a continuous reinforcing fiber, a reinforcing fiber sheet, or a fiber reinforced prepreg is wound, and thereafter, the resin impregnated in the reinforcing fiber is hardened before or after winding, so that the resin is hardened. Even for pillars such as concrete rectangular pillars, groundwork and corner treatment are not required, shortening the construction period and In addition, it is possible to reduce the strike, improve the restraining effect of the reinforcing fiber, improve the yield strength and toughness, and achieve the desired reinforcing effect sufficiently. obtain.
【図１】本発明に係るコンクリート柱状体の補強方法の
一実施例を説明する斜視図である。FIG. 1 is a perspective view illustrating an embodiment of a method for reinforcing a concrete column according to the present invention.
【図２】コンクリート矩形柱にプレキャスト成型品を据
え付ける方法を説明する斜視図である。FIG. 2 is a perspective view illustrating a method of installing a precast molded product on a concrete rectangular column.
【図３】本発明に従って補強されたコンクリート矩形柱
の断面図である。FIG. 3 is a sectional view of a concrete rectangular column reinforced according to the present invention.
【図４】本発明に係るコンクリート柱状体の補強方法を
説明する他の実施例の斜視図である。FIG. 4 is a perspective view of another embodiment illustrating a method of reinforcing a concrete column according to the present invention.
【図５】本発明に係るコンクリート柱状体の補強方法を
説明する他の実施例の斜視図である。FIG. 5 is a perspective view of another embodiment illustrating a method of reinforcing a concrete column according to the present invention.
【図６】本発明に係るコンクリート柱状体の補強方法を
説明する正面図である。FIG. 6 is a front view illustrating a method of reinforcing a concrete column according to the present invention.
【図７】本発明に係るコンクリート柱状体の補強方法の
他の実施例を説明する斜視図である。FIG. 7 is a perspective view illustrating another embodiment of a method for reinforcing a concrete column according to the present invention.
【図８】図８（ａ）は、強化繊維シートの断面図であ
り、図８（ｂ）は、強化繊維シートの斜視図である。FIG. 8A is a cross-sectional view of a reinforcing fiber sheet, and FIG. 8B is a perspective view of the reinforcing fiber sheet.
【図９】従来の鋼板貼り付け方法と炭素繊維シート巻き
付け方法を組合せた補強方法を説明するためのコンクリ
ート柱の斜視図である。FIG. 9 is a perspective view of a concrete column for explaining a reinforcing method combining a conventional method of attaching a steel sheet and a method of winding a carbon fiber sheet.
【図１０】図９に示すコンクリート柱の断面図である。FIG. 10 is a sectional view of the concrete column shown in FIG. 9;
２０ プレキャスト成型品 ３０ 強化繊維 ４０ 仕上げ（モルタル、樹
脂） ５０ 強化繊維シート １００ コンクリート柱状体Reference Signs List 20 precast molded product 30 reinforcing fiber 40 finishing (mortar, resin) 50 reinforcing fiber sheet 100 concrete column
Claims (10)
ンクリート柱状体の周囲に、外面がコンクリート柱状体
の周方向に湾曲し、コンクリート柱状体の軸線方向に所
定長さとされたプレキャスト成型品を据え付け、プレキ
ャスト成型品を据え付けた後のコンクリート柱状体の外
周囲に角部がないようにする工程、（ｂ）前記プレキ
ャスト成型品を据え付けた前記コンクリート柱状体の外
周囲に連続した強化繊維を巻き付け、次いで、前記強化
繊維を巻き付けたコンクリート柱状体の外表面に樹脂を
塗布して前記強化繊維に樹脂を含浸させるか、又は、 前記プレキャスト成型品を据え付けた前記コンクリー
ト柱状体の外周囲に樹脂を塗布し、その上から連続した
強化繊維を巻き付け、必要に応じて、更に前記強化繊維
を巻き付けたコンクリート柱状体の外表面に樹脂を塗布
して前記強化繊維に樹脂を含浸させる、ようにした強化
繊維の巻き付け及び樹脂含浸工程、（ｃ）次いで、前記
強化繊維に含浸された樹脂を硬化する工程、を有するこ
とを特徴とするコンクリート柱状体の補強方法。1. (a) Around a concrete column to be reinforced having a rectangular cross section, an outer surface is curved in the circumferential direction of the concrete column, and has a predetermined length in the axial direction of the concrete column. Installing the article and removing the corners around the concrete column after the precast molded article is installed; (b) reinforcing fibers continuous around the outside of the concrete column where the precast molded article is installed Then, a resin is applied to the outer surface of the concrete pillar around which the reinforcing fiber is wound, and the resin is impregnated into the reinforcing fiber, or the outer periphery of the concrete pillar on which the precast molded article is installed. A resin is applied, and a continuous reinforcing fiber is wound thereon, and if necessary, a concrete wrapper further wound with the reinforcing fiber. Applying a resin to the outer surface of the columnar body and impregnating the reinforcing fiber with the resin, winding the reinforcing fiber and impregnating the resin, and (c) then curing the resin impregnated in the reinforcing fiber, A method for reinforcing a concrete columnar body, comprising:
ンクリート柱状体の周囲に、外面がコンクリート柱状体
の周方向に湾曲し、コンクリート柱状体の軸線方向に所
定長さとされたプレキャスト成型品を据え付け、プレキ
ャスト成型品を据え付けた後のコンクリート柱状体の外
周囲に角部がないようにする工程、（ｂ）前記プレキャ
スト成型品を据え付けた前記コンクリート柱状体の外周
囲に、樹脂が塗布された連続した強化繊維を巻き付ける
工程、（ｃ）次いで、前記樹脂を硬化する工程、を有す
ることを特徴とするコンクリート柱状体の補強方法。2. (a) Around a concrete column to be reinforced having a rectangular cross section, the outer surface is curved in the circumferential direction of the concrete column, and has a predetermined length in the axial direction of the concrete column. A step of installing the article and eliminating the corners around the concrete column after the precast molded article is installed; (b) applying resin to the outer periphery of the concrete column where the precast article is installed. Winding a continuous reinforcing fiber thus obtained, and (c) subsequently curing the resin.
ンクリート柱状体の周囲に、外面がコンクリート柱状体
の周方向に湾曲し、コンクリート柱状体の軸線方向に所
定長さとされたプレキャスト成型品を据え付け、プレキ
ャスト成型品を据え付けた後のコンクリート柱状体の外
周囲に角部がないようにする工程、（ｂ）支持シート
上に強化繊維を一方向に配列して形成される強化繊維シ
ート表面に樹脂を塗布して強化繊維に樹脂を含浸させた
後、前記プレキャスト成型品を据え付けた前記コンクリ
ート柱状体の外周面に貼り付けるか、 前記コンクリート柱状体の外周面に樹脂を塗布し、そ
の上から強化繊維シートを貼り付け、前記コンクリート
柱状体の外周面へと押しつけることによって、強化繊維
に樹脂を含浸させ、必要に応じて、更に強化繊維シート
表面に樹脂を塗布するか、又は、 前記コンクリート柱状体の外周面にプライマを塗布
し、その上から強化繊維シートを貼り付け、その後、強
化繊維シートに樹脂を塗布して強化繊維に含浸させる、
ようにした強化繊維シートの巻き付け及び樹脂含浸工
程、（ｃ）次いで、前記強化繊維に含浸された樹脂を硬
化する工程、を有することを特徴とするコンクリート柱
状体の補強方法。3. (a) Around a concrete column to be reinforced having a rectangular cross section, the outer surface is curved in the circumferential direction of the concrete column, and has a predetermined length in the axial direction of the concrete column. A step of installing the article and eliminating the corners around the concrete pillar after the precast molded article is installed, (b) a reinforcing fiber sheet formed by arranging reinforcing fibers in one direction on a support sheet After applying resin to the surface and impregnating the reinforcing fibers with the resin, the resin is applied to the outer peripheral surface of the concrete column where the precast molded product is installed, or the resin is applied to the outer peripheral surface of the concrete column. By attaching a reinforcing fiber sheet from above and pressing against the outer peripheral surface of the concrete columnar body, the reinforcing fiber is impregnated with a resin, and if necessary, further. A resin is applied to the surface of the modified fiber sheet, or a primer is applied to the outer peripheral surface of the concrete columnar body, a reinforcing fiber sheet is attached thereon, and then the resin is applied to the reinforcing fiber sheet to form a reinforcing fiber. Impregnated,
A method for reinforcing a concrete columnar body, comprising the steps of winding the reinforcing fiber sheet and impregnating the resin as described above, and (c) then curing the resin impregnated in the reinforcing fiber.
ンクリート柱状体の周囲に、外面がコンクリート柱状体
の周方向に湾曲し、コンクリート柱状体の軸線方向に所
定長さとされたプレキャスト成型品を据え付け、プレキ
ャスト成型品を据え付けた後のコンクリート柱状体の外
周囲に角部がないようにする工程、（ｂ）必要に応じて
前記コンクリート柱状体の外周面にプライマを塗布し、
その後、一方向に配列された強化繊維に樹脂を含浸させ
て形成される繊維強化プリプレグを、前記プレキャスト
成型品を据え付けた前記コンクリート柱状体の外周面に
貼り付ける工程、（ｃ）次いで、前記強化繊維に含浸さ
れた樹脂を硬化する工程、を有することを特徴とするコ
ンクリート柱状体の補強方法。4. (a) Precast molding in which the outer surface is curved in the circumferential direction of the concrete column and has a predetermined length in the axial direction of the concrete column around the concrete column to be reinforced to have a rectangular cross section. Installing the article and eliminating the corners around the outer periphery of the concrete column after the precast molded article has been installed; (b) applying a primer to the outer peripheral surface of the concrete column as necessary;
Then, a step of attaching a fiber-reinforced prepreg formed by impregnating the reinforcing fibers arranged in one direction with a resin to an outer peripheral surface of the concrete columnar body on which the precast molded product is installed, (c) Then, the reinforcing Curing the resin impregnated in the fibers. A method for reinforcing a concrete column.
とされ、前記プレキャスト成型品は、前記コンクリート
柱状体の各面に据え付けられる請求項１〜４のいずれか
の項に記載のコンクリート柱状体の補強方法。5. The concrete column according to claim 1, wherein the concrete column has a rectangular cross section, and the precast molded product is installed on each surface of the concrete column. Reinforcement method.
とされ、前記プレキャスト成型品は、前記コンクリート
柱状体のいずれかの対向する両面に据え付けられる請求
項１〜４のいずれかの項に記載のコンクリート柱状体の
補強方法。6. The concrete column according to claim 1, wherein the concrete column has a rectangular cross section, and the precast molded article is mounted on either of the opposite surfaces of the concrete column. How to reinforce concrete columns.
ャストコンクリートである請求項１〜４のいずれかの項
に記載のコンクリート柱状体の補強方法。7. The method for reinforcing a concrete column according to claim 1, wherein the precast molded product is a precast concrete.
体外表面にモルタルを塗るか、樹脂を吹き付ける請求項
１〜７のいずれかの項に記載のコンクリート柱状体の補
強方法。8. The method for reinforcing a concrete column according to claim 1, wherein mortar is applied or resin is applied to an outer surface of the column around which the reinforcing fiber is wound.
維；ボロン、チタン、スチールなどの金属繊維；アラミ
ド、ポリエステル、ナイロンなどの有機繊維；などから
選択されるいずれかの繊維であるか、或いは、前記繊維
を複数種混入したハイブリッドタイプとされる請求項１
〜８のいずれかの項に記載のコンクリート柱状体の補強
方法。9. The reinforcing fiber is any fiber selected from carbon fiber; glass fiber; metal fiber such as boron, titanium, and steel; organic fiber such as aramid, polyester, and nylon; 2. A hybrid type in which a plurality of the fibers are mixed.
9. The method for reinforcing a concrete columnar body according to any one of Items 8 to 8.
ポキシ樹脂、熱硬化型エポキシ樹脂若しくはポリエステ
ル系樹脂；ポリアミド樹脂若しくはポリカーボネート樹
脂；又は、ＭＭＡなどのラジカル反応系樹脂を含む請求
項１〜９のいずれかの項に記載のコンクリート柱状体の
補強方法。10. The resin according to claim 1, wherein the resin includes at least a room temperature curing epoxy resin, a thermosetting epoxy resin or a polyester resin; a polyamide resin or a polycarbonate resin; or a radical reaction resin such as MMA. The method for reinforcing a concrete columnar body according to any of the above items.