JPH11147375A - Heat-transfer sheet - Google Patents

Abstract

PROBLEM TO BE SOLVED: To improve the color reproducibility, the color-developing property, and the fastness of an obtained image regarding a recording of yellow by a method wherein C.I. solvent yellow 186 is contained in a dye which constitutes a heat-transfer layer, and is transferred onto a body to be transferred by migrating by heating. SOLUTION: This heat-transfer sheet 1 is constituted by providing a heat- transfer layer 3 on a base material sheet 2. For the heat-transfer layer 3, a dye which is transferred to a body to be transferred by migrating by heating is contained in a binder resin. Also, C.I. solvent yellow 186 is contained in the dye contained in the heat-transfer layer 3. Such a yellow heat-transfer sheet can develope dark and light colors in response to an imparted heat energy not only for a single color of a yellow color, but also when a full color image is formed by using sheets wherein magenta and cyan heat-transfer sheets are combined with the yellow heat-transfer sheet, the color reproducibility can be improved.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【産業上の利用分野】本発明は、熱転写シートに関し、
さらに詳しくはサーマルヘッド又はレーザー等を用いて
画像情報に応じた選択的な加熱印字を行うことにより、
被転写体上に画像を記録するのに適しており、特にイエ
ローの記録に好適な熱転写シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a thermal transfer sheet,
More specifically, by performing selective heating printing according to image information using a thermal head or laser, etc.,
The present invention relates to a thermal transfer sheet suitable for recording an image on a transfer target, and particularly suitable for yellow recording.

【０００２】[0002]

【従来の技術】近年、ＣＲＴディスプレイ上の画像をハ
ードコピーとして出力する方式として、電気信号によっ
て発熱が制御されるサーマルヘッド等によって熱転写シ
ートを加熱し、熱転写シートの色材層中の昇華染料を被
熱転写体に転写して画像を形成する熱転写方式が広く採
用されている。この方式は、イエロー、マゼンタ、シア
ンの三原色を重ね記録することで減法混色法を行い、フ
ルカラー画像を形成することが可能となる。上記熱転写
方式に用いられる熱転写シートは、一般的に昇華性染料
を含むバインダー樹脂を基材に塗布して色材層を形成し
たものが用いられている。2. Description of the Related Art In recent years, as a method for outputting an image on a CRT display as a hard copy, a thermal transfer sheet is heated by a thermal head or the like whose heat is controlled by an electric signal, and a sublimation dye in a color material layer of the thermal transfer sheet is removed. 2. Description of the Related Art A thermal transfer method of forming an image by transferring an image to a heat transfer target is widely used. According to this method, a subtractive color mixture method is performed by superimposing and recording three primary colors of yellow, magenta, and cyan, and a full-color image can be formed. As the thermal transfer sheet used in the thermal transfer system, a sheet obtained by applying a binder resin containing a sublimable dye to a base material to form a color material layer is generally used.

【０００３】[0003]

【発明が解決しようとする課題】熱転写方式における重
要な問題として、形成された画像の色再現性、感度、発
色濃度、堅牢性（耐熱移行性、耐光性）が挙げられる。
すなわち、熱転写シートに対しては、元の画像に対する
忠実な色再現性、低エネルギーの熱での十分な発色性、
高発色濃度、得られた画像の高堅牢性が要求される。し
かしながら、従来の熱転写シートは、これらの諸特性を
全て満足するには不十分であった。本発明は、上記の如
き従来の技術の問題点に鑑みなされたものであり、特に
イエローの記録に関して、上記の問題点を解決した熱転
写シートを提供することを課題とする。Important problems in the thermal transfer system include color reproducibility, sensitivity, color density, and fastness (heat transfer resistance, light resistance) of the formed image.
That is, for the thermal transfer sheet, faithful color reproducibility with respect to the original image, sufficient color development with low-energy heat,
High color density and high fastness of the obtained image are required. However, the conventional thermal transfer sheet was insufficient to satisfy all of these properties. SUMMARY OF THE INVENTION The present invention has been made in view of the above-described problems of the related art, and has as its object to provide a thermal transfer sheet that solves the above problems, particularly for yellow recording.

【０００４】[0004]

【課題を解決するための手段】前記課題を解決するため
に、請求項１においては、基材シート上に、バインダー
樹脂及び加熱により移行し被転写体上に転写する染料か
らなる熱転写層を設けた熱転写シートにおいて、該染料
がＣ．Ｉ．ソルベントイエロー１８６を含有することを
特徴とする熱転写シート、としたものである。In order to solve the above-mentioned problems, according to the present invention, a thermal transfer layer comprising a binder resin and a dye which is transferred by heating and transferred onto a transfer-receiving member is provided on a base sheet. Heat transfer sheet, the dye is C.I. I. A thermal transfer sheet containing Solvent Yellow 186.

【０００５】又、請求項２においては、基材シート上
に、バインダー樹脂及び加熱により移行し被転写体上に
転写する染料からなる熱転写層を設けた熱転写シートに
おいて、該染料がＣ．Ｉ．ソルベントイエロー１８６と
Ｃ．Ｉ．ソルベントイエロー９３との混合物であること
を特徴とする熱転写シート、としたものである。更に
又、請求項３においては、熱転写層中にシリコンオイル
もしくはシリコン樹脂が含有されていることを特徴とす
る請求項１又は請求項２記載の熱転写シート、としたも
のである。According to a second aspect of the present invention, there is provided a thermal transfer sheet provided with a thermal transfer layer made of a binder resin and a dye which is transferred by heating and transferred onto a transfer-receiving member on a base sheet. I. Solvent Yellow 186 and C.I. I. A thermal transfer sheet, which is a mixture with Solvent Yellow 93. Furthermore, in a third aspect, the thermal transfer sheet according to the first or second aspect is characterized in that the thermal transfer layer contains silicon oil or silicone resin.

【０００６】[0006]

【作用】染料として、Ｃ．Ｉ．ソルベントイエロー１８
６と適当な染料を適当な比率で混合した染料、または
Ｃ．Ｉ．ソルベントイエロー１８６を染料として単体で
使用することにより、従来からのイエロー熱転写シート
に諸性能で劣ることなく、高耐性に重点を置くもの、色
再現性、感度、発色濃度に重点を置くものなど、用途に
応じたイエロー熱転写シートを提供することが出来る。
また、Ｃ．Ｉ．ソルベントイエロー１８６とＣ．Ｉ．ソ
ルベントイエロー９３との混合物を使用することで、元
の画像に対する忠実な色再現性、低エネルギーの熱での
十分な発色性、高発色濃度、得られた画像の高堅牢性を
実現することが出来るイエロー熱転写シートを提供する
ことが出来る。[Function] As a dye, C.I. I. Solvent Yellow 18
6 and an appropriate dye in an appropriate ratio, or C.I. I. By using Solvent Yellow 186 alone as a dye, it is possible to focus on high resistance, color reproducibility, sensitivity, color density, etc., without deteriorating the performance of conventional yellow thermal transfer sheets. It is possible to provide a yellow thermal transfer sheet according to the application.
C.I. I. Solvent Yellow 186 and C.I. I. By using a mixture with Solvent Yellow 93, it is possible to realize faithful color reproducibility with respect to the original image, sufficient color development with low energy heat, high color density, and high robustness of the obtained image. A yellow thermal transfer sheet that can be provided can be provided.

【０００７】[0007]

【発明の実施の形態】以下に、好ましい実施態様を挙げ
て本発明を更に詳細に説明する。本発明の熱転写シート
（１）は、図１に示すように、基材シート（２）上に熱
転写層（３）を設けたものである。基材シート（２）の
材質は、コンデンサーペーパー等の紙またはポリエステ
ルフィルム、ポリスチレンフィルム、ポリプロピレンフ
ィルム、セロファン等が挙げられるが、特に好ましいの
はポリエステルフィルムである。基材シート（２）の厚
みは、２〜５０μｍ、より好ましくは２〜１６μｍであ
る。熱転写層（３）は、加熱により移行し被転写体に転
写する染料がバインダー樹脂中に含有されている。熱転
写層（３）に含有される染料は、本発明では、Ｃ．Ｉ．
ソルベントイエロー１８６、又はこれとＣ．Ｉ．ソルベ
ントイエロー９３との混合物を使用する。また、本発明
の上記イエロー熱転写シートをフルカラー画像形成に使
用する場合に、このイエロー熱転写シートと組み合わせ
て使用するマゼンタ熱転写層に使用するマゼンタの染料
としては、Ｃ．Ｉ．ディスパーズレッド６０、Ｃ．Ｉ．
ディスパーズバイオレット２６、Ｃ．Ｉ．ソルベントレ
ッド２７、Ｃ．Ｉ．ソルベントレッド１９等を使用する
ことができる。また、本発明の上記イエロー熱転写層を
フルカラー画像形成に使用する場合に、このイエロー熱
転写層と組み合わせて使用するシアンの熱転写層に使用
するシアンの染料としては、Ｃ．Ｉ．ディスパーズブル
ー３５４、Ｃ．Ｉ．ソルベントブルー６３、Ｃ．Ｉ．ソ
ルベントブルー３６、Ｃ．Ｉ．ディスパーズブルー２
４、等を使用することができる。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in more detail with reference to preferred embodiments. As shown in FIG. 1, the thermal transfer sheet (1) of the present invention has a thermal transfer layer (3) provided on a base sheet (2). Examples of the material of the base sheet (2) include paper such as condenser paper or a polyester film, a polystyrene film, a polypropylene film, and cellophane. A polyester film is particularly preferable. The thickness of the base sheet (2) is 2 to 50 μm, more preferably 2 to 16 μm. In the thermal transfer layer (3), the binder resin contains a dye which is transferred by heating and transferred to the transfer target. In the present invention, the dye contained in the thermal transfer layer (3) is C.I. I.
Solvent Yellow 186, or C.I. I. A mixture with Solvent Yellow 93 is used. When the yellow thermal transfer sheet of the present invention is used for forming a full-color image, the magenta dye used in the magenta thermal transfer layer used in combination with the yellow thermal transfer sheet includes C.I. I. Disperse Red 60, C.I. I.
Disperse Violet 26, C.I. I. Solvent Red 27, C.I. I. Solvent Red 19 or the like can be used. When the yellow thermal transfer layer of the present invention is used for forming a full-color image, the cyan dye used in the cyan thermal transfer layer used in combination with the yellow thermal transfer layer includes C.I. I. Disperse Blue 354, C.I. I. Solvent Blue 63, C.I. I. Solvent Blue 36, C.I. I. Disperse Blue 2
4, etc. can be used.

【０００８】本発明の熱転写シートは、イエロー色の単
色用はもちろん、該イエロー熱転写シートに、マゼンタ
及びシアンの熱転写シートを組み合わせて使用してフル
カラー画像を形成する際に、付与される熱エネルギーに
応じた濃淡の発色が可能で色再現性に優れ、更に、フル
カラー画像形成の場合に中間色の最も優れた広範囲な色
再現が可能となる。１つの熱転写シート上にイエロー、
マゼンタ、シアンの各色用の熱転写層を塗り分けて使用
するのにも好適である。熱転写層（３）中に含まれるバ
インダー樹脂としては、エチルセルロース、ヒドロキシ
エチルセルロース、エチルヒドロキシセルロース、ヒド
ロキシプロピルセルロース、メチルセルロース、酢酸セ
ルロース等のセルロース系樹脂、ブチラール樹脂、アセ
タール樹脂、フェノキシ樹脂、ポリカーボネート樹脂、
あるいはポリエステル樹脂、等が挙げられるが、なかで
もフェノキシ樹脂あるいはフェノキシ樹脂とブチラール
樹脂の混合物が耐熱性、染料の移行性等の点から好まし
い。バインダー樹脂のガラス転移点（以下では単にＴｇ
と称す）としては、５０℃以上が望ましく、もしＴｇが
５０℃を下回ると、昇華転写時に熱転写層（３）が被転
写体表面に融着しやすくなったり、熱転写リボンの保存
性に問題が生じたりするため好ましくない。熱転写層
（３）中の染料とバインダー樹脂との割合は、染料／樹
脂＝１０／１００〜３００／１００がよく、より好まし
くは、染料／樹脂＝３０／１００〜２００／１００であ
る。また、染料受容性を有する被転写体表面に昇華転写
する場合、熱転写層（３）と被転写体表面との熱時の融
着を防止するために、熱転写層（３）中に離型剤を添加
することが望ましい。The thermal transfer sheet of the present invention can be used not only for a single color of yellow, but also for the thermal energy applied when a full-color image is formed by using a combination of magenta and cyan thermal transfer sheets with the yellow thermal transfer sheet. According to the present invention, it is possible to form a color with a suitable density and excellent color reproducibility. Further, in the case of forming a full-color image, it is possible to reproduce a wide range of colors having the best intermediate colors. Yellow on one thermal transfer sheet,
It is also suitable to separately use the thermal transfer layers for magenta and cyan colors. Examples of the binder resin contained in the thermal transfer layer (3) include cellulose resins such as ethyl cellulose, hydroxyethyl cellulose, ethyl hydroxy cellulose, hydroxypropyl cellulose, methyl cellulose, and cellulose acetate, butyral resin, acetal resin, phenoxy resin, and polycarbonate resin.
Alternatively, a polyester resin, etc. may be mentioned, and among them, a phenoxy resin or a mixture of a phenoxy resin and a butyral resin is preferable in terms of heat resistance, dye transferability, and the like. The glass transition point of the binder resin (hereinafter simply referred to as Tg
If the Tg is lower than 50 ° C., the thermal transfer layer (3) tends to fuse to the surface of the transfer-receiving member during the sublimation transfer, and there is a problem in the storage stability of the thermal transfer ribbon. It is not preferable because it may occur. The ratio of the dye to the binder resin in the thermal transfer layer (3) is preferably dye / resin = 10/100 to 300/100, more preferably dye / resin = 30/100 to 200/100. In the case of sublimation transfer onto the surface of the transfer receiving material having dye receptivity, a release agent is provided in the thermal transfer layer (3) in order to prevent fusion of the thermal transfer layer (3) and the surface of the transfer receiving material when heated. Is desirably added.

【０００９】添加する離型剤としては、シリコン系のも
のが好ましく、シリコンオイル、あるいはシリコン樹脂
を用いることができるが、主鎖にシリコンを変性したシ
リコン変性樹脂がより好ましい。このようなシリコン変
性樹脂を離型剤として昇華転写用インキに添加し成膜す
ると、シリコン変性樹脂の離型成分であるシリコン部分
が、昇華転写用インキとの相溶性が低さから、表面にブ
リードする。また、主鎖は昇華転写用インキと相溶性が
高いため、一体化されている。この結果、熱転写層
（３）の表面には離型成分であるシリコン部分がリッチ
となり、熱時の良好な離型性を有することが可能とな
る。また、このシリコン部分は主鎖と結合しているた
め、この主鎖と昇華転写用インキとの相溶性によりシリ
コン部分が熱転写層（３）から離脱することが無く、保
存性にも優れている。このような離型剤に用いられる主
鎖としては、アクリル系樹脂、セルロース系樹脂、ビニ
ル系樹脂、ポリエステル系樹脂、あるいはポリアミド系
樹脂等が挙げられるが、なかでも昇華転写インキ中のバ
インダー樹脂との相溶性の点から、アクリル系樹脂、ポ
リエステル樹脂が特に望ましい。離型剤の添加量は、昇
華転写用インキの固形分に対して０．１％〜１０％程度
が望ましい。離型剤の添加量が０．１％を下回ると、熱
時の融着防止の効果が乏しく、また１０％以上である
と、熱転写層（３）の皮膜強度が低下したり、昇華転写
用インキ中のバインダー樹脂が離型剤の主鎖を担持しき
れなくなるため、熱転写リボンの保存性等に問題が生じ
るため好ましくない。熱転写層（３）は、好ましくは適
当な溶剤中に前記の染料、バインダー樹脂その他の添加
剤を加えて各成分を溶解又は分散させて熱転写層用イン
キを調製し、これを上記の基材シート上に塗布及び乾燥
させて形成する。この様にして形成する染料担持層は、
０．２〜５μｍ、好ましくは０．４〜３μｍ程度の厚さ
である。The release agent to be added is preferably a silicone-based release agent, and silicone oil or silicone resin can be used, but a silicon-modified resin in which silicon is modified in the main chain is more preferred. When such a silicon-modified resin is added to a sublimation transfer ink as a release agent and formed into a film, the silicon portion, which is a release component of the silicon-modified resin, has a low compatibility with the sublimation transfer ink, so that the surface of the silicon-modified resin is low. Bleed. In addition, the main chain has high compatibility with the ink for sublimation transfer, and is therefore integrated. As a result, the surface of the thermal transfer layer (3) is rich in the silicon portion, which is a release component, so that it is possible to have a good release property when heated. Further, since the silicon portion is bonded to the main chain, the silicon portion does not separate from the thermal transfer layer (3) due to the compatibility between the main chain and the ink for sublimation transfer, and the storage stability is excellent. . Examples of the main chain used for such a release agent include an acrylic resin, a cellulose resin, a vinyl resin, a polyester resin, and a polyamide resin, among which a binder resin in a sublimation transfer ink is used. From the viewpoint of compatibility, acrylic resins and polyester resins are particularly desirable. The addition amount of the release agent is preferably about 0.1% to 10% based on the solid content of the ink for sublimation transfer. When the amount of the release agent is less than 0.1%, the effect of preventing fusion during heating is poor, and when the amount is more than 10%, the film strength of the thermal transfer layer (3) is reduced, or for sublimation transfer. Since the binder resin in the ink cannot fully support the main chain of the release agent, there is a problem in the storage stability and the like of the thermal transfer ribbon, which is not preferable. The thermal transfer layer (3) is preferably prepared by adding the above-mentioned dye, binder resin and other additives to a suitable solvent to dissolve or disperse each component to prepare an ink for the thermal transfer layer, It is formed by coating and drying on the top. The dye-carrying layer thus formed is
The thickness is about 0.2 to 5 μm, preferably about 0.4 to 3 μm.

【００１０】また、熱転写リボンのサーマルヘッド等に
よる印画時に、サーマルヘッド等が熱転写シート（１）
に付着して熱転写リボンのスムーズな走行性を妨害する
のを防ぐために、図２に示す如く熱転写シート（１）の
熱転写層（３）が塗布されていない側に、バックコート
層（４）を設けることが望ましい。このようなバックコ
ート層（４）に用いられる材料としては、ニトロセルロ
ース、ポリエステル樹脂、アクリル樹脂、ビニル樹脂等
にシリコンオイルを含有させたもの、または、シリコン
変性したもの等が挙げられる。また、耐熱性を向上させ
る目的で、架橋剤を併用しても良い。バックコート層
（４）を設ける際の塗布厚は、０．１〜４μｍ程度が好
ましい。Further, when printing a thermal transfer ribbon with a thermal head or the like, the thermal head or the like causes the thermal transfer sheet (1)
As shown in FIG. 2, a back coat layer (4) is provided on the side of the thermal transfer sheet (1) on which the thermal transfer layer (3) is not applied as shown in FIG. It is desirable to provide. Examples of the material used for the back coat layer (4) include nitrocellulose, polyester resin, acrylic resin, vinyl resin, and the like containing silicon oil, or silicon-modified material. Further, a crosslinking agent may be used in combination for the purpose of improving heat resistance. The coating thickness when providing the back coat layer (4) is preferably about 0.1 to 4 μm.

【００１１】以上の如き熱転写シートを用いて、画像を
形成する為に使用する被転写体は、その記録面が前記の
染料に対して染料受容性を有するものであればいかなる
ものでもよく、又、染料受容性を有しない紙、金属、ガ
ラス、合成樹脂等である場合には、その少なくともー方
の表面に染料受容層を形成すればよい。染料受容性を有
する樹脂としては、例えば、ポリエチレン、ポリプロピ
レン等のポリオレフィン系樹脂、アセタール樹脂、ポリ
塩化ビニル樹脂、塩化ビニル−酢酸ビニル共重合樹脂、
ポリエステル樹脂、ポリスチレン樹脂、オレフィンと他
のビニルモノマーとの共重合樹脂、アイオノマー、セル
ロース系樹脂、ポリカーボネート樹脂等が挙げられる。
また、染料受容層中には、熱転写時における熱転写シー
トと被転写体との融着を防止するために、必要に応じて
シリコンオイル等の離型剤を添加しても良い。染料受容
層の厚みとしては、２〜２０μｍ程度が好ましい上記の
如き本発明の熱転写シート及び上記の如き被転写体を使
用して熱転写を行う際に使用する熱エネルギーの付与手
段は、従来公知の付与手段がいずれも使用することが出
来、エネルギーをコントロールすることにより、階調画
像を得ることが可能となる。The transfer member used to form an image using the above-described thermal transfer sheet may be any transfer member whose recording surface has a dye-accepting property with respect to the above-mentioned dye. In the case of paper, metal, glass, synthetic resin or the like having no dye receptivity, a dye receiving layer may be formed on at least one of the surfaces. Examples of the resin having a dye-accepting property include polyethylene, a polyolefin resin such as polypropylene, an acetal resin, a polyvinyl chloride resin, a vinyl chloride-vinyl acetate copolymer resin,
Examples include polyester resins, polystyrene resins, copolymer resins of olefins and other vinyl monomers, ionomers, cellulosic resins, and polycarbonate resins.
If necessary, a release agent such as silicone oil may be added to the dye-receiving layer in order to prevent fusion between the thermal transfer sheet and the transfer-receiving body during thermal transfer. The thickness of the dye-receiving layer is preferably about 2 to 20 μm. Means for applying thermal energy used when performing thermal transfer using the thermal transfer sheet of the present invention as described above and the transfer-receiving body as described above are conventionally known. Any of the applying means can be used, and a gradation image can be obtained by controlling the energy.

【００１２】[0012]

【実施例】次に実施例を挙げて本発明を更に具体的に説
明する。なお、文中部又は％とあるのは特に断りのない
限り重量基準である。Next, the present invention will be described more specifically with reference to examples. In the following, “parts” or “%” is based on weight unless otherwise specified.

【００１３】（実施例１）下記組成の熱転写層用インキ
組成物を調製し、裏面に耐熱処理を施した厚さ５．４μ
ｍのポリエチレンテレフタレートフイルムに、乾燥膜厚
が１μｍになるように塗布及び乾燥して本発明の熱転写
シートを得た。 （熱転写層用インキ） Ｃ．Ｉ．ソルベントイエロー１８６ ４．０部 フェノキシ樹脂 ５．０部 メチルエチルケトン ６０．０部 トルエン ３１．０部 次に、基材シートとして発泡ポリプロピレンフィルム
（厚さ５０μ）／接着樹脂層／コート紙（１０８ｇ／ｍ
²）／接着樹脂層／発泡ポリプロピレンフィルム（厚さ
５０μ）を用い、この片方の面に下記の染料受容層用イ
ンキを乾燥膜厚が４μｍとなるように塗布、乾燥を行
い、その後４５℃１週間エージング行い、被転写体を得
た。 （染料受容層用インキ） アセタール樹脂 １０．０部 塩化ビニル−酢酸ビニル共重合樹脂 １０．０部 シリコンオイル ２．０部 イソシアネート樹脂 ３．０部 メチルエチルケトン ５０．０部 トルエン ２５．０部 得られた熱転写シートの熱転写層面と被転写体の染料受
容層面とを重ね、サーマルヘッドを用いて、下記の条件
で染料を転写させ、画像形成を行った。 （印字条件） 印字機 ：ＳＩＰ社製シミュレーター ３００ｄ
ｏｔ／ｍｍヘッド使用 印字パターン ：１６階調パターン 印字エネルギー：１６階調目で０．６ｍＪ／ｄｏｔ 印字スピード：８ｍｓ／ｌｉｎｅ ＤＵＴＹ ：６５％ 印可電圧 ：１８Ｖ 次いで、得られた画像に対して以下の評価を行った。Example 1 An ink composition for a thermal transfer layer having the following composition was prepared and heat-treated on the back surface to a thickness of 5.4 μm.
m of a polyethylene terephthalate film and dried so as to have a dry film thickness of 1 μm to obtain a thermal transfer sheet of the present invention. (Ink for thermal transfer layer) C.I. I. Solvent Yellow 186 4.0 parts Phenoxy resin 5.0 parts Methyl ethyl ketone 60.0 parts Toluene 31.0 parts Next, as a base sheet, a foamed polypropylene film (thickness 50 μ) / adhesive resin layer / coated paper (108 g / m 2)
² ) / adhesive resin layer / foamed polypropylene film (thickness: 50 μm), the following dye-receiving layer ink was applied to one surface to a dry film thickness of 4 μm, and dried at 45 ° C. Aging was performed for a week to obtain a transfer-receiving body. (Dye receiving layer ink) Acetal resin 10.0 parts Vinyl chloride-vinyl acetate copolymer resin 10.0 parts Silicon oil 2.0 parts Isocyanate resin 3.0 parts Methyl ethyl ketone 50.0 parts Toluene 25.0 parts obtained The thermal transfer layer surface of the thermal transfer sheet was superimposed on the dye receiving layer surface of the transfer object, and the dye was transferred under the following conditions using a thermal head to form an image. (Printing conditions) Printing machine: Simulator made by SIP 300d
ot / mm head use Print pattern: 16 gradation pattern Printing energy: 0.6 mJ / dot at 16th gradation Print speed: 8 ms / line DUTY: 65% Applied voltage: 18 V Then, the following image was obtained. An evaluation was performed.

【００１４】（評価項目） 発色濃度 ：１６階調目の反射濃度をマクベスＲＤ−９
１８にて測定 耐熱移行性：７０℃８時間後の１６階調目の濃度減衰率 耐光性 ：キセノンフェードメーター１０時間照射後
の１６階調目の濃度減衰率 上記項目に対して評価を行った結果、以下の通り良好な
結果が得られた。イエロー色としての色再現性が非常に
良好であった。 発色濃度 ：３．５ 耐熱移行性：７％以下 耐光性 ：５％以下(Evaluation items) Coloring density: The reflection density of the 16th gradation was determined by Macbeth RD-9.
Measured at 18 Heat transferability: Density decay rate at 16th gradation after 70 hours at 8 hours at 70 ° C. Light resistance: Density decay rate at 16th gradation after irradiation with xenon fade meter for 10 hours The above items were evaluated. As a result, good results were obtained as follows. The color reproducibility as a yellow color was very good. Coloring density: 3.5 Heat transfer resistance: 7% or less Light resistance: 5% or less

【００１５】（実施例２）実施例１において熱転写層用
インキ組成を下記組成に変更した以外は、実施例１と同
様にして熱転写シートを得た。 （熱転写層用インキ） Ｃ．Ｉ．ソルベントイエロー１８６ ２．０部 Ｃ．Ｉ．ソルベントイエロー９３ ２．０部 フェノキシ樹脂 ５．０部 メチルエチルケトン ６０．０部 トルエン ３１．０部 実施例１と同様にして得た被転写体と上記熱転写シート
を重ね、実施例１と同様に画像形成、評価を行った。評
価結果は、以下の通りである。 発色濃度 ：３．０ 耐熱移行性：５％以下 耐光性 ：３％以下 イエロー色としての色再現性は非常に良好な状態であり
ながら、諸耐性ではさらに良好な結果が得られた。Example 2 A thermal transfer sheet was obtained in the same manner as in Example 1, except that the ink composition for the thermal transfer layer was changed to the following composition. (Ink for thermal transfer layer) C.I. I. Solvent Yellow 186 2.0 parts C.I. I. Solvent Yellow 93 2.0 parts Phenoxy resin 5.0 parts Methyl ethyl ketone 60.0 parts Toluene 31.0 parts The transfer-receiving body obtained in the same manner as in Example 1 and the above-mentioned thermal transfer sheet are overlapped to form an image in the same manner as in Example 1. , Was evaluated. The evaluation results are as follows. Coloring density: 3.0 Heat transfer resistance: 5% or less Light fastness: 3% or less Although color reproducibility as a yellow color was in a very good state, even better results were obtained in various resistances.

【００１６】（実施例３）実施例１において熱転写層用
インキ組成を下記組成に変更した以外は、実施例１と同
様にして熱転写シートを得た。 （熱転写層用インキ） Ｃ．Ｉ．ソルベントイエロー１８６ ２．０部 Ｃ．Ｉ．ソルベントイエロー９３ ２．０部 フェノキシ樹脂 ３．０部 ブチラール樹脂 ２．０部 メチルエチルケトン ６０．０部 トルエン ３１．０部 実施例１と同様にして得た被転写体と上記熱転写シート
を重ね、実施例１と同様に画像形成、評価を行った。評
価結果は、以下の通りである。 発色濃度 ：３．０ 耐熱移行性：５％以下 耐光性 ：３％以下 イエロー色としての色再現性も非常に良好でありなが
ら、諸耐性でも良好な結果が得られた。Example 3 A thermal transfer sheet was obtained in the same manner as in Example 1 except that the ink composition for the thermal transfer layer was changed to the following composition. (Ink for thermal transfer layer) C.I. I. Solvent Yellow 186 2.0 parts C.I. I. Solvent Yellow 93 2.0 parts Phenoxy resin 3.0 parts Butyral resin 2.0 parts Methyl ethyl ketone 60.0 parts Toluene 31.0 parts The object to be transferred obtained in the same manner as in Example 1 and the above-mentioned thermal transfer sheet are overlapped. Image formation and evaluation were performed in the same manner as in Example 1. The evaluation results are as follows. Coloring density: 3.0 Heat transfer resistance: 5% or less Light fastness: 3% or less Although the color reproducibility as a yellow color was very good, good results were obtained in various resistances.

【００１７】（実施例４）実施例１において熱転写層用
インキ組成を下記組成に変更した以外は、実施例１と同
様にして熱転写シートを得た。 （熱転写層用インキ） Ｃ．Ｉ．ソルベントイエロー１８６ ２．０部 Ｃ．Ｉ．ソルベントイエロー９３ ２．０部 フェノキシ樹脂 ３．０部 ブチラール樹脂 ２．０部 シリコン変性樹脂 ０．０５部 メチルエチルケトン ６０．０部 トルエン ３１．０部 実施例１と同様にして得た被転写体と上記熱転写シート
を重ね、実施例１と同様に画像形成、評価を行った。評
価結果は、以下の通りである。 発色濃度 ：３．０ 耐熱移行性：５％以下 耐光性 ：３％以下 イエロー色としての色再現性も非常に良好でありなが
ら、諸耐性でも良好な結果が得られた。Example 4 A thermal transfer sheet was obtained in the same manner as in Example 1, except that the ink composition for the thermal transfer layer was changed to the following composition. (Ink for thermal transfer layer) C.I. I. Solvent Yellow 186 2.0 parts C.I. I. Solvent Yellow 93 2.0 parts Phenoxy resin 3.0 parts Butyral resin 2.0 parts Silicone-modified resin 0.05 parts Methyl ethyl ketone 60.0 parts Toluene 31.0 parts Transfer receiving body obtained in the same manner as in Example 1 and the above The thermal transfer sheets were stacked, and image formation and evaluation were performed in the same manner as in Example 1. The evaluation results are as follows. Coloring density: 3.0 Heat transfer resistance: 5% or less Light fastness: 3% or less Although the color reproducibility as a yellow color was very good, good results were obtained in various resistances.

【００１８】[0018]

【発明の効果】染料として、Ｃ．Ｉ．ソルベントイエロ
ー１８６と適当な染料を適当な比率で混合した染料、ま
たはＣ．Ｉ．ソルベントイエロー１８６を染料として単
体で使用することにより、従来からあるイエロー熱転写
シートに諸性能で劣ることなく、高耐性に重点を置くも
の、色再現性、感度、発色濃度に重点を置くものなど、
用途に応じたイエロー熱転写シートを提供することが出
来る。As a dye, C.I. I. A dye obtained by mixing Solvent Yellow 186 with an appropriate dye in an appropriate ratio, or C.I. I. By using Solvent Yellow 186 alone as a dye, it is possible to focus on high resistance, color reproducibility, sensitivity, color density, etc., without inferior in various performances to a conventional yellow thermal transfer sheet.
It is possible to provide a yellow thermal transfer sheet according to the application.

【００１９】また、Ｃ．Ｉ．ソルベントイエロー１８６
とＣ．Ｉ．ソルベントイエロー９３との混合物を使用す
ることで、元の画像に対する忠実な色再現性、低エネル
ギーの熱での十分な発色性、高発色濃度、得られた画像
の高堅牢性を実現することが出来るイエロー熱転写シー
トを得ることが出来る。In addition, C.I. I. Solvent Yellow 186
And C. I. By using a mixture with Solvent Yellow 93, it is possible to realize faithful color reproducibility with respect to the original image, sufficient color development with low energy heat, high color density, and high robustness of the obtained image. A possible yellow thermal transfer sheet can be obtained.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明に関わる熱転写シートの一実施例を、断
面図を用いて模式的に示す説明図である。FIG. 1 is an explanatory view schematically showing one embodiment of a thermal transfer sheet according to the present invention using a cross-sectional view.

【図２】本発明に関わる熱転写シートの別の一実施例
を、断面図を用いて模式的に示す説明図である。FIG. 2 is an explanatory view schematically showing another embodiment of the thermal transfer sheet according to the present invention using a cross-sectional view.

【符号の説明】[Explanation of symbols]

１‥‥‥熱転写シート ２‥‥‥基材シート ３‥‥‥熱転写層 ４‥‥‥バックコート層 1. Thermal transfer sheet 2. Base sheet 3. Thermal transfer layer 4. Back coat layer

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】基材シート上に、バインダー樹脂及び加熱
により移行し被転写体上に転写する染料からなる熱転写
層を設けた熱転写シートにおいて、該染料がＣ．Ｉ．ソ
ルベントイエロー１８６を含有することを特徴とする熱
転写シート。1. A thermal transfer sheet comprising a substrate sheet provided with a thermal transfer layer comprising a binder resin and a dye which is transferred by heating and is transferred onto a transfer-receiving member. I. A thermal transfer sheet containing Solvent Yellow 186. 【請求項２】基材シート上に、バインダー樹脂及び加熱
により移行し被転写体上に転写する染料からなる熱転写
層を設けた熱転写シートにおいて、該染料がＣ．Ｉ．ソ
ルベントイエロー１８６とＣ．Ｉ．ソルベントイエロー
９３との混合物であることを特徴とする熱転写シート。2. A thermal transfer sheet comprising a base sheet provided with a thermal transfer layer comprising a binder resin and a dye which is transferred by heating and transferred onto a transfer-receiving member. I. Solvent Yellow 186 and C.I. I. A thermal transfer sheet, which is a mixture with Solvent Yellow 93. 【請求項３】熱転写層中にシリコンオイルもしくはシリ
コン樹脂が含有されていることを特徴とする請求項１又
は請求項２記載の熱転写シート。3. The thermal transfer sheet according to claim 1, wherein the thermal transfer layer contains silicone oil or silicone resin.