JPH108551A - Structure of beam-column joint - Google Patents
Structure of beam-column jointInfo
- Publication number
- JPH108551A JPH108551A JP16756296A JP16756296A JPH108551A JP H108551 A JPH108551 A JP H108551A JP 16756296 A JP16756296 A JP 16756296A JP 16756296 A JP16756296 A JP 16756296A JP H108551 A JPH108551 A JP H108551A
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- column
- fiber
- strength
- column joint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、鉄筋コンクリー
ト構造物等において、柱部材と梁部材とが接合される柱
梁仕口部構造に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a beam-column connection structure in which a column member and a beam member are joined in a reinforced concrete structure or the like.
【０００２】[0002]
【従来の技術】鉄筋コンクリート構造物において、柱部
材と梁部材とが接合される柱梁仕口部は、一般に、柱部
材と梁部材とが接合される部分において、各部材に配筋
される柱主筋や梁主筋を相互に連結するとともに、この
部分を補強するためのせん断補強筋を配筋した後、これ
ら主筋や補強筋を埋設するようにコンクリートを打設す
ることによって構築される。2. Description of the Related Art In a reinforced concrete structure, a beam-column connection portion at which a column member and a beam member are joined is generally provided at a portion where the column member and the beam member are joined, with columns arranged at the members. It is constructed by connecting the main reinforcing bars and beam reinforcing bars to each other, arranging shear reinforcing bars for reinforcing this portion, and then pouring concrete so as to bury these main reinforcing bars and reinforcing bars.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、一般
に、柱梁仕口部では、これに接合される柱部材や梁部材
を高強度化すると、仕口部の強度が柱や梁部材に対して
相対的に低くなる傾向がある。また、柱梁仕口部の強度
を向上させるべくここに配筋されるせん断補強筋の量を
増加すると、この仕口部で柱主筋や梁主筋及びせん断補
強筋等が複雑に交錯することとなり、仕口部に打設され
るコンクリートの量が他の部分と比較して少なくなりや
すいという問題がある。However, in general, when the strength of a column member or a beam member to be joined thereto is increased in the column-beam connection portion, the strength of the connection portion is relatively large with respect to the column or the beam member. Tends to be low. In addition, if the amount of shear reinforcing bars arranged here is increased in order to improve the strength of the beam-column connection, the main columns, beam main bars, shear reinforcing bars, etc. will be complicatedly mixed at this connection. However, there is a problem in that the amount of concrete poured into the connection tends to be smaller than in other parts.
【０００４】その一方で、柱梁仕口部には、各部材から
の軸力が作用する他、地震により各部材が相対的に変位
するような場合には曲げ応力等が作用する。そのため、
柱梁仕口部のコンクリート部分には、過大なせん断力等
の応力が作用することとなり、この部分の強度や靭性の
向上を図る必要がある。On the other hand, an axial force from each member acts on the beam-to-column connection, and a bending stress acts when each member is relatively displaced by an earthquake. for that reason,
Stress such as excessive shear force acts on the concrete portion of the beam-column connection, and it is necessary to improve the strength and toughness of this portion.
【０００５】本発明は上述したような問題に鑑みてなさ
れたものであり、柱梁仕口部に打設されるコンクリート
の強度や靭性を高めるとともに、鉄筋との付着強度を増
強することによって、柱梁仕口部の強度の向上を図るこ
とのできる柱梁仕口部構造を提供することを目的とす
る。[0005] The present invention has been made in view of the above-described problems, and by increasing the strength and toughness of concrete cast in a beam-column joint, and by increasing the bonding strength with a reinforcing bar, An object of the present invention is to provide a beam-column connection structure capable of improving the strength of the beam-column connection.
【０００６】[0006]
【課題を解決するための手段】この発明の柱梁仕口部構
造は、上記目的を達成するためになされたものであり、
その要旨は、鉄筋コンクリート構造物等の柱梁仕口部に
おいて、この仕口部に打設されるコンクリートに繊維補
強材を混入してなることを特徴とするものである（請求
項１）。このような柱梁仕口部構造によれば、ここに打
設されるコンクリートに繊維補強材を混入したので、こ
の繊維補強材によってコンクリートの強度や靭性が増大
すると共に、柱梁仕口部に配筋される柱主筋や梁主筋と
コンクリートとの付着強度が高くなるため、柱梁仕口部
の強度の向上を図ることができる。SUMMARY OF THE INVENTION A column-beam connection structure according to the present invention has been made to achieve the above object.
The gist of the invention is characterized in that a fiber reinforcing material is mixed into concrete cast at the joint in a beam-column joint of a reinforced concrete structure or the like (claim 1). According to such a beam-to-column connection structure, the fiber reinforcement is mixed into the concrete cast here, so that the fiber reinforcement increases the strength and toughness of the concrete, and the beam-to-column connection is Since the strength of adhesion between the column main bars or beam main bars to be arranged and the concrete is increased, the strength of the column-beam joint can be improved.
【０００７】また、上記柱梁仕口部構造において、前記
繊維補強材は炭素繊維であることが好ましい（請求項
２）。このような柱梁仕口部構造によれば、炭素繊維は
発錆しにくいため、コンクリート部分が時間と共に劣化
するのを防止することができ、柱梁仕口部の信頼性を向
上させることができる。In the above-mentioned beam-column connection structure, it is preferable that the fiber reinforcing material is carbon fiber. According to such a beam-to-column connection structure, since carbon fiber is unlikely to rust, it is possible to prevent the concrete portion from deteriorating with time, and to improve the reliability of the beam-to-column connection. it can.
【０００８】さらに、上記柱梁仕口部構造においては、
前記繊維補強材を合成樹脂製繊維とすることができる
（請求項３）。このような柱梁仕口部構造によれば、合
成樹脂製繊維は、発錆することがないうえに軽量である
ため、コンクリート部分の劣化を防ぐことができるとと
もに、コンクリートの単位重量あたりの強度を高めるこ
とができる。Further, in the above-mentioned beam-column connection structure,
The fiber reinforcement may be a synthetic resin fiber (claim 3). According to such a beam-to-column connection structure, the synthetic resin fiber does not rust and is lightweight, so that it is possible to prevent deterioration of the concrete portion and to increase the strength per unit weight of the concrete. Can be increased.
【０００９】[0009]
【発明の実施の形態】以下、この発明の好適な実施の形
態を図面を用いて詳細に説明する。図１は、本実施形態
にかかる柱梁仕口部構造１０を示すものである。本実施
形態において、仕口部３は、断面矩形状の鉄筋コンクリ
ート製柱１に対して４つの梁部材２が接合される部分で
あり、この仕口部３内において、柱部材１の柱主筋１ａ
や梁部材２の梁主筋２ａが相互に連結されているととも
に、せん断補強筋４が柱主筋１ａの外周を一括して囲む
ようにして配筋されている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the present invention will be described below in detail with reference to the drawings. FIG. 1 shows a beam-column connection structure 10 according to the present embodiment. In the present embodiment, the joint 3 is a portion where the four beam members 2 are joined to the reinforced concrete column 1 having a rectangular cross section. In the joint 3, the column main bar 1 a of the column member 1 is provided.
The beam reinforcing bars 2a of the beam members 2 are connected to each other, and the shear reinforcing bars 4 are arranged so as to collectively surround the outer periphery of the column main bar 1a.
【００１０】かかる仕口部３は、例えば、構築された柱
部材１の上部に梁部材２を構築する型枠を建込むことに
より構築される。すなわち、同図に示すように、プレキ
ャスト部材の建込み若しくはコンクリートの現場打ちに
より構築された柱部材１の上部において梁型枠２１を建
込み、各梁型枠２１内に梁主筋２ａを配筋するととも
に、これらの梁主筋２ａを仕口部３内において相互に連
結しつつ、仕口部３内にせん断補強筋４を配筋し、次い
で仕口部３を囲むように仕口部型枠３１を建込み、前記
各主筋やせん断補強筋を埋設するように、仕口部型枠３
１及び梁型枠２１内にコンクリートを打設する。The connection part 3 is constructed, for example, by laying a formwork for constructing the beam member 2 above the constructed column member 1. That is, as shown in the figure, the beam formwork 21 is erected at the upper part of the column member 1 constructed by laying a precast member or cast-in-place of concrete, and arranging the beam main reinforcement 2a in each beam formwork 21. At the same time, while connecting the beam main reinforcements 2a to each other in the connection part 3, the shear reinforcement 4 is arranged in the connection part 3, and then the connection part formwork is formed so as to surround the connection part 3. 31 so that the main bars and the shear reinforcing bars are buried.
Concrete is poured into the beam formwork 1 and the beam formwork 21.
【００１１】ここで、かかる仕口部３に打設されるコン
クリートには繊維補強材５が混入されている。この、繊
維補強材５は、コンクリートの強度や靭性を向上させる
ものであり、例えば、通常、繊維補強コンクリートに用
いられる鋼繊維やスチールファイバ等の短繊維の他、ポ
リエチレンやビニロン等の合成樹脂繊維、炭素繊維、ガ
ラス繊維などを用いることができる。Here, a fiber reinforcement 5 is mixed in the concrete cast into the connection portion 3. The fiber reinforcing material 5 improves the strength and toughness of the concrete. For example, in addition to short fibers such as steel fibers and steel fibers usually used for fiber reinforced concrete, synthetic resin fibers such as polyethylene and vinylon , Carbon fiber, glass fiber and the like can be used.
【００１２】かかる繊維補強材５として用いられる鋼繊
維は、通常の繊維補強コンクリートに配合される短繊維
を用いることができ、例えば、直径が０．３mmから０．
６mm程度の長さが２０mmから４０mm程度のものを使用す
ることが好ましい。そして、この短繊維としては、周知
のような、例えば、圧延、引き抜きされた鋼線をカッタ
ーで所定の長さに切断したカットワイヤーや、薄鋼板を
せん断することによって製造されたせん断ファイバー、
鋼製の厚板を回転するスライス平刃によって切削して得
られる切削ファイバーなどがあり、好ましくは、その形
状を異形としたり、表面に線条を形成するなどしてコン
クリートとの付着の向上を図る。As the steel fiber used as the fiber reinforcing material 5, short fibers mixed with ordinary fiber reinforced concrete can be used.
It is preferable to use one having a length of about 6 mm and a length of about 20 to 40 mm. And as the short fiber, as well-known, for example, rolled, cut wire or steel wire cut to a predetermined length with a cutter, a shear fiber manufactured by shearing a thin steel sheet,
There is a cutting fiber obtained by cutting a steel thick plate with a rotating slice flat blade, and preferably, the shape is modified, or a streak is formed on the surface to improve adhesion to concrete. Aim.
【００１３】一方、繊維補強材５として上記炭素繊維を
用いた場合には、炭素繊維は、発錆しにくいため、コン
クリート部分が時間と共に劣化するのを防止することが
できる。また、合成樹脂繊維を用いた場合には、合成樹
脂製繊維は軽量であるためコンクリートの単位重量あた
りの強度を高めることができる。On the other hand, when the carbon fiber is used as the fiber reinforcing material 5, the carbon fiber hardly rusts, so that the concrete portion can be prevented from deteriorating with time. When synthetic resin fibers are used, since the synthetic resin fibers are lightweight, the strength per unit weight of concrete can be increased.
【００１４】そして、この繊維補強材５の練り混ぜは、
コンクリートミキサー中に繊維補強材５を投入する際、
分散機を用いてコンクリート中に一様に分散せしめ、フ
ァイバーボールが生じるのを防ぎつつ混練する。その
後、繊維補強材５が混入されたコンクリートＣは、圧送
ポンプ等によって仕口部３に打設される。次いで、コン
クリートＣが硬化したら、梁型枠２１や仕口部型枠３１
を脱型し、柱梁仕口部構造の構築作業を終了する。な
お、型枠としてプレキャスト型枠を用いた場合には、前
記型枠を部材表面に残置するため、これらの型枠を撤去
する作業を行う必要はない。The kneading of the fiber reinforcing material 5 is as follows:
When putting the fiber reinforcement 5 into the concrete mixer,
The mixture is uniformly dispersed in concrete using a disperser, and kneaded while preventing the formation of fiber balls. Thereafter, the concrete C into which the fiber reinforcing material 5 is mixed is poured into the connection part 3 by a pressure pump or the like. Next, when the concrete C has hardened, the beam formwork 21 and the joint formwork 31 are formed.
And finish the construction work of the beam-column connection structure. When a precast formwork is used as the formwork, it is not necessary to remove the formwork because the formwork is left on the surface of the member.
【００１５】このようにして構築される柱梁仕口部構造
１０によれば、仕口部３に打設されるコンクリートＣ中
に混入された繊維補強材５の応力伝達作用によって、コ
ンクリート部分の変形能やひび割れに対する抵抗性が増
大するとともに、仕口部３に配筋される柱主筋１ａや梁
主筋２ａとコンクリートＣとの付着強度が高くすること
ができ、その結果仕口部３の強度や靭性を増大すること
ができる。According to the beam-column connection structure 10 constructed in this way, the concrete portion is cast by the stress transmitting action of the fiber reinforcing material 5 mixed in the concrete C cast into the connection portion 3. The deformability and resistance to cracks are increased, and the adhesion strength between the column main reinforcement 1a and the beam main reinforcement 2a arranged in the joint 3 and the concrete C can be increased. As a result, the strength of the joint 3 And toughness can be increased.
【００１６】[0016]
【発明の効果】以上、詳細に説明したように本発明の柱
梁仕口部構造によれば、仕口部に打設されるコンクリー
トに繊維補強材を混入することにより、繊維補強材によ
ってコンクリートの強度や靭性が増大すると共に、柱梁
仕口部に配筋される柱主筋や梁主筋とコンクリートとの
付着強度が高くなるため、柱梁仕口部の強度の向上を図
ることができる。As described above in detail, according to the beam-column connection structure of the present invention, the fiber reinforcing material is mixed with the concrete cast in the connection portion, whereby the concrete is strengthened by the fiber reinforcing material. In addition to the increase in strength and toughness of the joints, the strength of the connection between the column main bars and the beam main bars arranged in the beam-column joints and the concrete is increased, so that the strength of the beam-column joints can be improved.
【００１７】また、上記柱梁仕口部構造において、前記
繊維補強材として炭素繊維を用いれば、炭素繊維は発錆
しにくいため、コンクリート部分が時間と共に劣化する
のを防止することができ、柱梁仕口部の信頼性を向上さ
せることができる。Further, in the above-mentioned beam-column connection structure, if carbon fiber is used as the fiber reinforcing material, the carbon fiber hardly rusts, so that the concrete portion can be prevented from deteriorating with time. The reliability of the beam connection can be improved.
【００１８】さらに、上記柱梁仕口部構造においては、
前記繊維補強材を合成樹脂製繊維とすることにより、合
成樹脂製繊維は、発錆することがないうえに軽量である
ため、コンクリート部分の劣化を防ぐことができるとと
もに、コンクリートの単位重量あたりの強度を高めるこ
とができる。Further, in the above-mentioned beam-column connection structure,
By using a synthetic resin fiber as the fiber reinforcing material, the synthetic resin fiber does not rust and is lightweight, so that it is possible to prevent deterioration of the concrete portion and to reduce the weight per unit weight of the concrete. Strength can be increased.
【図１】この発明の実施形態にかかる柱梁仕口部構造を
示す水平断面図である。FIG. 1 is a horizontal sectional view showing a beam-column connection structure according to an embodiment of the present invention.
１ 柱部材 ２ 梁部材 ３ 仕口部 ４ せん断補強筋 ５ 繊維補強材 １０ 柱梁仕口部構造 Ｃ コンクリート DESCRIPTION OF SYMBOLS 1 Column member 2 Beam member 3 Connection part 4 Shear reinforcement 5 Fiber reinforcement 10 Column beam connection structure C Concrete
フロントページの続き (72)発明者 高見 信嗣 東京都清瀬市下清戸４丁目640番地 株式 会社大林組技術研究所内Continued on the front page (72) Inventor Shinji Takami 4-640 Shimoseito, Kiyose-shi, Tokyo Inside Obayashi Corporation Technical Research Institute
Claims (3)
て、この仕口部に打設されるコンクリートに繊維補強材
を混入してなることを特徴とする柱梁仕口部の補強構
造。1. A reinforcing structure for a beam-column joint of a concrete structure, wherein a fiber reinforcing material is mixed into concrete cast in the port.
特徴とする請求項１に記載の柱梁仕口部構造。2. The beam-column connection structure according to claim 1, wherein the fiber reinforcing material is carbon fiber.
ことを特徴とする請求項１に記載の柱梁仕口部構造。3. The beam-column connection structure according to claim 1, wherein the fiber reinforcement is a synthetic resin fiber.