JPH1060736A - Polyphenylene sulfide monofilament and woven fabric for industrial use - Google Patents
Polyphenylene sulfide monofilament and woven fabric for industrial useInfo
- Publication number
- JPH1060736A JPH1060736A JP21986896A JP21986896A JPH1060736A JP H1060736 A JPH1060736 A JP H1060736A JP 21986896 A JP21986896 A JP 21986896A JP 21986896 A JP21986896 A JP 21986896A JP H1060736 A JPH1060736 A JP H1060736A
- Authority
- JP
- Japan
- Prior art keywords
- polyphenylene sulfide
- monofilament
- woven fabric
- industrial
- sulfide monofilament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、織物用モノフィラ
メントとしての十分な強度および伸びを有すると共に、
耐屈曲摩耗性および耐屈曲疲労性にすぐれ、産業用途に
好適なポリフェニレンサルファイドモノフィラメントお
よびこのモノフィラメントからなる抄紙用ドライヤーカ
ンバス、搬送用ベルト、フィルター、サーマルボンド法
不織布接着工程用ネットコンベアまたは抄紙ワイヤーな
どの工業用織物に関するものである。TECHNICAL FIELD The present invention has sufficient strength and elongation as a woven monofilament,
Polyphenylene sulfide monofilament which is excellent in bending wear resistance and bending fatigue resistance, suitable for industrial use and papermaking dryer canvas, transport belt, filter, thermal bonding method nonwoven fabric bonding net conveyor or papermaking wire etc. It relates to industrial textiles.
【０００２】[0002]
【従来の技術】搬送ベルト用織物、抄紙カンバス用織物
およびフィルター用織物などの工業織物用途において
は、これらの織物がたとえば１３０℃以上の高温雰囲気
や、高濃度の酸、アルカリなどの薬品環境にさらされる
ことから、織物素材であるモノフィラメントには、高強
度、高伸度、高結節強度および高屈曲摩耗などの機械特
性と共に、耐熱性および耐薬品性が強く要求されてい
た。2. Description of the Related Art In industrial textile applications such as transport belt textiles, papermaking canvas textiles and filter textiles, these textiles are exposed to high-temperature atmospheres of, for example, 130 ° C. or higher, or chemical environments such as highly concentrated acids and alkalis. For this reason, monofilaments, which are woven fabric materials, have been required to have high heat resistance and chemical resistance as well as mechanical properties such as high strength, high elongation, high knot strength and high bending wear.
【０００３】従来、このような要求特性を満たす産業用
繊維としては、アラミド系繊維（商品名：ＮＯＭＥＸま
たはＫＥＶＬＡＲなど）およびポリテトラフルオロエチ
レン（商品名：ＴＥＦＬＯＮ）などが要求に応じて使用
されてきたが、これらの重合体はいずれも溶融押出成形
が不可能であることおよび高価であることから、その使
用範囲が著しく制限されていた。Conventionally, aramid fibers (trade name: NOMEX or KEVLAR) and polytetrafluoroethylene (trade name: TEFLON) have been used as industrial fibers satisfying such required characteristics as required. However, all of these polymers cannot be melt-extruded and are expensive, so that the range of use thereof has been significantly limited.
【０００４】一方、ポリフェニレンサルファイドはすぐ
れた耐熱性および抜群の耐薬品性を有する上に、溶融成
形が可能であることから、いわゆる成形品用途以外に
も、繊維やフィルムに応用する技術が従来から検討され
ており、繊維の製造については、たとえば米国特許第
３，８９５，０９１号明細書、同３，８９８，２０４号
明細書、同３，９１２，６９５号明細書、同４，０２
９，６３９号明細書、同４，０９８，７７６号明細書、
同４，１１５，５６２号明細書、特開昭４９−５４６１
７号公報、特公昭５２−１２２４０号公報、特公昭５２
−３０６０９号公報、特開昭５７−１４３５１８号公
報、特開昭５８−１８４０９号公報、特開昭５８−３１
１１２号公報および特開昭６１−７５８１２号公報など
により提案されている。[0004] On the other hand, polyphenylene sulfide has excellent heat resistance and outstanding chemical resistance, and can be melt-molded. Therefore, in addition to so-called molded article applications, techniques applied to fibers and films have been conventionally used. The production of fibers has been discussed, for example, in US Pat. Nos. 3,895,091, 3,898,204, 3,912,695, and 4,02.
9,639, 4,098,776,
No. 4,115,562, JP-A-49-5461.
No. 7, JP-B-52-12240, JP-B-52
-30609, JP-A-57-143518, JP-A-58-18409, and JP-A-58-31
112 and JP-A-61-75812.
【０００５】そして、ポリフェニレンサルファイドモノ
フィラメントの上述したすぐれた特性を利用して、これ
を抄紙カンバス用織物に利用することも、特開昭６１−
６３９０号公報により提案されている。Utilizing the above-mentioned excellent properties of polyphenylene sulfide monofilament, it is also possible to use the same for fabric for papermaking canvas.
No. 6390 has proposed this.
【０００６】しかしながら、ポリフェニレンサルファイ
ド繊維は、耐熱性および耐薬品性にすぐれる反面、糸自
体が硬いために脆さがあり、靭性が不足していることか
ら、耐屈曲耐摩耗性および耐屈曲疲労性などの特性が劣
るという欠点を有していた。[0006] However, polyphenylene sulfide fiber has excellent heat resistance and chemical resistance, but is brittle because the yarn itself is hard and has insufficient toughness. However, it has the disadvantage that the properties such as the properties are inferior.
【０００７】したがって、ポリフェニレンサルファイド
モノフィラメントを工業用織物に適用しようとする場合
には、製織時に糸切れ、糸割れなどの問題を生じるばか
りか、製織後の摩耗、屈曲特性が著しく劣ることから、
例えば抄紙用ドライヤーカンバスとしての使用中に織物
の屈曲部位などが破損しやすく、この面での耐久性が低
いという問題があった。[0007] Therefore, when polyphenylene sulfide monofilament is applied to industrial fabrics, not only problems such as yarn breakage and yarn breakage during weaving occur, but also wear and bending characteristics after weaving are extremely poor.
For example, there is a problem that the bent portion of the fabric is easily damaged during use as a papermaking dryer canvas, and the durability in this aspect is low.
【０００８】一方、ポリフェニレンサルファイドモノフ
ィラメントの耐摩耗性を改良する方法としては、ポリテ
トラフルオロエチレンに代表されるフッ素系ポリマを
０．５〜１０重量％ブレンド紡糸する方法（米国特許第
３，４８７，４５４号明細書）、およびエチレン／テト
ラフルオロエチレン共重合体に代表されるオレフィン系
共重合体を５〜５０重量％ブレンド紡糸する方法（米国
特許第４，６１０，９１６号明細書）などが知られてい
る。On the other hand, as a method for improving the abrasion resistance of polyphenylene sulfide monofilament, a method of blending and spinning 0.5 to 10% by weight of a fluorine-based polymer represented by polytetrafluoroethylene (US Pat. No. 3,487,387) 454), and a method of blending and spinning an olefin copolymer represented by an ethylene / tetrafluoroethylene copolymer by 5 to 50% by weight (U.S. Pat. No. 4,610,916). Have been.
【０００９】しかしながら、これらの従来法では、確か
にポリフェニレンサルファイドモノフィラメントの耐摩
耗性は向上するものの、逆にモノフィラメント本来の高
強伸度特性が著しく低下し、例えば抄紙用ドライヤーカ
ンバスなどの工業用織物の用途への適用が阻害されると
いう問題があった。However, in these conventional methods, although the abrasion resistance of polyphenylene sulfide monofilaments is certainly improved, the inherent high strength and elongation characteristics of monofilaments are remarkably reduced. There is a problem that application to the application is hindered.
【００１０】[0010]
【発明が解決しようとする課題】本発明は、上述した従
来のポリフェニレンサルファイドモノフィラメントが有
する問題点を解決するために検討した結果、達成された
ものである。SUMMARY OF THE INVENTION The present invention has been achieved as a result of study for solving the problems of the above-mentioned conventional polyphenylene sulfide monofilament.
【００１１】したがって、本発明の目的は、織物用モノ
フィラメントとしての十分な強度および伸びを有すると
共に、耐屈曲摩耗性および耐屈曲疲労性にすぐれ、産業
用途に好適なポリフェニレンサルファイドモノフィラメ
ントおよびこのモノフィラメントからなる高機能性を有
する抄紙用ドライヤーカンバス、搬送用ベルトおよびフ
ィルターなどの工業用織物を提供することにある。Accordingly, an object of the present invention is to provide a polyphenylene sulfide monofilament having sufficient strength and elongation as a woven fabric monofilament, excellent flex wear resistance and flex fatigue resistance, and suitable for industrial use, and the monofilament. An object of the present invention is to provide industrial fabrics such as a papermaking dryer canvas, a conveyor belt and a filter having high functionality.
【００１２】[0012]
【課題を解決するための手段】上記の目的を達成するた
めに、本発明のポリフェニレンサルファイドモノフィラ
メントは、ポリフェニレンサルファイドに対し、フッ素
系樹脂を０．０５〜０．４０重量％配合した組成物を溶
融紡糸したことを特徴とする。Means for Solving the Problems To achieve the above object, the polyphenylene sulfide monofilament of the present invention is obtained by melting a composition containing 0.05 to 0.40% by weight of a fluorine resin with respect to polyphenylene sulfide. It is characterized by being spun.
【００１３】また、本発明の工業用織物は、上記ポリフ
ェニレンサルファイドモノフィラメントを経糸および／
または緯糸の少なくとも一部に用いて織成したことを特
徴とし、その具体的な用途としては、抄紙用ドライヤー
カンバス、搬送用ベルト、フィルター、サーマルボンド
法不織布接着工程用ネットコンベアまたは抄紙ワイヤー
などが挙げられる。[0013] Further, the industrial fabric of the present invention comprises the above polyphenylene sulfide monofilament in the form of warp and / or warp.
Or characterized by being woven using at least a part of the weft yarn, and specific uses thereof include a papermaking dryer canvas, a conveyor belt, a filter, a net conveyor or a papermaking wire for a thermal bonding nonwoven fabric bonding step, and the like. Can be
【００１４】[0014]
【発明の実施の形態】本発明で用いるポリフェニレンサ
ルファイドとは、構成単位の８５モル％以上がｐ−フェ
ニレンサルファイド単位からなるポリマであり、１５モ
ル％以下の範囲で他の共重合成分を含有することができ
る。なお、ｐ−フェニレンサルファイド単位が８５モル
％未満では耐熱性が損われるため好ましくない。BEST MODE FOR CARRYING OUT THE INVENTION The polyphenylene sulfide used in the present invention is a polymer in which at least 85 mol% of the constituent units are composed of p-phenylene sulfide units, and contains other copolymer components in the range of 15 mol% or less. be able to. In addition, when the p-phenylene sulfide unit is less than 85 mol%, heat resistance is unfavorably deteriorated.
【００１５】なお、本発明においては、従来公知のクエ
ンチ法およびフラッシュ法などで製造したポリフェニレ
ンサルファイドを使用することができ、特に低廉に製造
できて不純物含量の多いフラッシュ法ポリマに適用した
場合には、クエンチ法ポリマ並の高物性を確保できると
いう利点が得られる。In the present invention, polyphenylene sulfide produced by a conventionally known quench method or flash method can be used. Particularly, when applied to a flash method polymer which can be produced at a low cost and has a high impurity content, The advantage is that high physical properties comparable to those of the quenching method polymer can be ensured.
【００１６】さらに、使用するポリフェニレンサルファ
イドには、耐熱剤、耐候剤、耐光剤、帯電防止剤、染
料、顔料および少量のトリクロルベンゼンなどの架橋成
分を含有させることができる。Further, the polyphenylene sulfide used may contain a heat-resistant agent, a weathering agent, a light-proofing agent, an antistatic agent, a dye, a pigment and a small amount of a crosslinking component such as trichlorobenzene.
【００１７】また、本発明で用いるポリフェニレンサル
ファイドは、ＪＩＳ Ｋ−７２１０に準じ、押出形プラ
ストメータを用いて、オリフィス径：２．０９５mm、同
じく長さ：８．０mm、温度：３１６℃、荷重：５．０Kg
の条件で測定したポリマのメルトフローレートが２００
以下、とくに１６０以下の範囲にあることが、溶融紡糸
・延伸性、さらには得られるモノフィラメントの品質面
の点から好ましい。The polyphenylene sulfide used in the present invention is an extruded plastometer according to JIS K-7210, and has an orifice diameter of 2.095 mm, a length of 8.0 mm, a temperature of 316 ° C., and a load of 316 ° C. 5.0Kg
The melt flow rate of the polymer measured under the conditions
Below, it is particularly preferable that it is in the range of 160 or less from the viewpoint of melt spinning / drawing properties and the quality of the obtained monofilament.
【００１８】一方、本発明で用いるフッ素系樹脂として
は、エチレン／テトラフルオロエチレン共重合体、エチ
レン−クロロトリフルオロエチレン共重合体、フッ化ビ
ニリデン−テトラフルオロエチレン−ヘキサフルオロプ
ロピレン共重合体、ポリテトラフルオロエチレン、ポリ
フッ化ビニリデン、ポリクロロトリフルオロエチレンお
よびポリフッ化ビニルなどが挙げられ、なかでもエチレ
ン／テトラフルオロエチレン共重合体を使用した場合に
すぐれた効果を得ることができる。On the other hand, the fluororesin used in the present invention includes ethylene / tetrafluoroethylene copolymer, ethylene-chlorotrifluoroethylene copolymer, vinylidene fluoride-tetrafluoroethylene-hexafluoropropylene copolymer, Examples include tetrafluoroethylene, polyvinylidene fluoride, polychlorotrifluoroethylene, and polyvinyl fluoride. Among them, an excellent effect can be obtained when an ethylene / tetrafluoroethylene copolymer is used.
【００１９】上記フッ素系樹脂のポリフェニレンサルフ
ァイドに対する配合量は、０．０５〜０．４０重量％、
とくに０．１０〜０．３０重量％の範囲が好適であり、
０．０５重量％未満では耐屈曲摩耗性および耐屈曲疲労
性の向上効果が不十分であり、０．４０重量％を越える
とポリフェニレンサルファイドモノフィラメント本来の
強伸度特性が低下するため好ましくない。The amount of the fluorine-based resin to be added to polyphenylene sulfide is 0.05 to 0.40% by weight,
In particular, the range of 0.10 to 0.30% by weight is preferable,
If it is less than 0.05% by weight, the effect of improving flex wear resistance and flex fatigue resistance is insufficient, and if it exceeds 0.40% by weight, the inherent high elongation characteristic of polyphenylene sulfide monofilament is undesirably reduced.
【００２０】なお、本発明においては、上記フッ素系樹
脂をポリフェニレンサルファイドに対し０．０５〜０．
４０重量％という微少量配合することによって、ポリフ
ェニレンサルファイドモノフィラメントの耐屈曲摩耗性
および耐屈曲疲労性の向上を図ると共に、強伸度特性を
高水準で確保することができ、このことは従来の知見か
らは想像だにし得ない新規な発見であるといえる。In the present invention, the above-mentioned fluororesin is used in an amount of from 0.05 to 0.5% based on polyphenylene sulfide.
By blending the polyphenylene sulfide monofilament in a very small amount of 40% by weight, it is possible to improve the bending wear resistance and the bending fatigue resistance of the polyphenylene sulfide monofilament and to secure the high elongation characteristics at a high level. This is a new discovery that cannot be imagined.
【００２１】ポリフェニレンサルファイドとフッ素系樹
脂とからなる組成物を得る手段としては、ペレット同志
を混合する方法、ドライブレンド−再ペレタイズする方
法およびエクストルーダーへ別々に供給して溶融混合す
る方法などの慣用の手段を採用することができる。Means for obtaining a composition comprising polyphenylene sulfide and a fluorine-based resin include conventional methods such as a method of mixing pellets, a method of dry blending and re-pelletizing, and a method of separately supplying to an extruder and melt-mixing. Means can be adopted.
【００２２】ポリフェニレンサルファイドとフッ素系樹
脂とからなる組成物を溶融紡糸し、モノフィラメント化
する方法にもとくに制限はないが、溶融押出温度は、通
常ポリマの融点よりも２０〜６０℃、とくに３０〜５０
℃高い温度が好適である。そして、溶融紡出された糸条
は、通常６０℃以上の温水中で冷却固化される。The method of melt-spinning a composition comprising polyphenylene sulfide and a fluororesin to form a monofilament is not particularly limited. The melt extrusion temperature is usually 20 to 60 ° C., more preferably 30 to 60 ° C., than the melting point of the polymer. 50
C. higher temperatures are preferred. The melt-spun yarn is usually cooled and solidified in warm water of 60 ° C. or higher.
【００２３】得られた未延伸モノフィラメントは、引続
いてそのガラス転移温度よりも高い温度で延伸される。
この延伸段階においては、二段以上の多段延伸を行な
い、全延伸倍率を４．４〜５．２倍に設定することが望
ましい。なお、延伸雰囲気としては、温水浴、空気浴お
よび水蒸気浴などが好適に用いられる。The undrawn monofilament obtained is subsequently drawn at a temperature above its glass transition temperature.
In this stretching step, it is desirable to perform two or more stages of multi-stage stretching and set the total stretching ratio to 4.4 to 5.2 times. As the stretching atmosphere, a warm water bath, an air bath, a steam bath, or the like is suitably used.
【００２４】延伸されたポリフェニレンサルファイドモ
ノフィラメントは、残留収縮率などを合わせる目的で、
引続き熱処理に供されるが、この熱処理は１３５〜１９
０℃、とくに１４０〜１７０℃の空気浴中で、定長状態
で行なうのが好適である。The drawn polyphenylene sulfide monofilament is used for adjusting the residual shrinkage and the like.
It is subsequently subjected to a heat treatment, which is between 135 and 19
It is preferable to carry out the reaction in an air bath at 0 ° C., particularly 140 to 170 ° C., in a constant length state.
【００２５】本発明のポリフェニレンサルファイドモノ
フィラメントの断面形状は、円形、楕円形、三角形、正
方形、半月形、五角形以上の多角形、多葉形、ドックボ
ーン形および繭形などのいかなる形状であってもよい
が、工業用織物の構成素材として用いる場合は、円また
は楕円（扁平）形状であることが好ましい。The cross-sectional shape of the polyphenylene sulfide monofilament of the present invention may be any shape such as a circle, an ellipse, a triangle, a square, a half-moon, a polygon having five or more pentagons, a multilobe, a dockbone and a cocoon. Good, but when used as a constituent material of industrial textiles, it is preferable to be circular or elliptical (flat).
【００２６】このようにして得られる本発明のポリフェ
ニレンサルファイドモノフィラメントは、ポリフェニレ
ンサルファイド自体のすぐれた耐熱性および耐薬品性を
具備し、しかも引張強伸度および結節強伸度が均衡にす
ぐれ、十分な強靭性を発揮するばかりか、耐屈曲摩耗性
および耐屈曲疲労性がきわめてすぐれている。The polyphenylene sulfide monofilament of the present invention thus obtained has the excellent heat resistance and chemical resistance of polyphenylene sulfide itself, and furthermore, the tensile strength and the knot strength / elongation are well-balanced and sufficient. Not only exhibits toughness, but also extremely excellent flex wear resistance and flex fatigue resistance.
【００２７】したがって、本発明のポリフェニレンサル
ファイドモノフィラメントは、各種の産業用途に対し好
適な性能を有しており、特にこのポリフェニレンサルフ
ァイドモノフィラメントを経糸および／または緯糸の少
なくとも一部に用いて織成した織物は、工業用としての
理想的な性能を発揮する。Therefore, the polyphenylene sulfide monofilament of the present invention has a suitable performance for various industrial uses. In particular, the woven fabric woven by using the polyphenylene sulfide monofilament for at least a part of a warp and / or a weft is Demonstrates the ideal performance for industrial use.
【００２８】本発明でいう工業用織物とは、主として第
二次産業の搬送、篩分け、乾燥、プレスおよび熱処理な
どの工程において、製品または中間製品への加工もしく
はこれらの生産の用具として使用することを目的とした
織物であり、異物の混入や環境への排出防止に使用する
布帛などをも含む。The industrial fabric referred to in the present invention is mainly used as a tool for processing into a product or an intermediate product or as a tool for producing these in processes such as transport, sieving, drying, pressing and heat treatment in the secondary industry. It is a woven fabric for the purpose, and also includes a fabric used for preventing foreign substances from being mixed or discharged into the environment.
【００２９】そして、この工業用織物の具体的な実例と
しては、抄紙用ドライヤーカンバス、搬送用ベルト、フ
ィルター、サーマルボンド法不織布接着工程用ネットコ
ンベアおよび抄紙ワイヤーなどが挙げられる。Specific examples of the industrial fabric include a papermaking dryer canvas, a conveyor belt, a filter, a net conveyor for a non-woven fabric bonding step by a thermal bonding method, and a papermaking wire.
【００３０】[0030]
【実施例】以下に実施例を挙げて、本発明の構成および
効果についてさらに説明する。The configuration and effects of the present invention will be further described with reference to examples.
【００３１】［実施例１〜４，比較例１〜４］ＭＦＲが
１３０、ガラス転移温度が９０．５℃のポリフェニレン
サルファイド（東レ社製“Ｅ２１８０”）に対し、エチ
レン／テトラフルオロエチレン共重合体（ダイキン工業
社製ＥＴＦＥ、“ネオフロンＥＰ−５２０）を表１に示
した割合で配合した組成物を、４０mm直径のエクストル
ーダー紡糸機により、３２０℃で溶融し、孔径１．０mm
の口金から溶融押出した。[Examples 1 to 4 and Comparative Examples 1 to 4] An ethylene / tetrafluoroethylene copolymer was used for polyphenylene sulfide (“E2180” manufactured by Toray Industries, Ltd.) having an MFR of 130 and a glass transition temperature of 90.5 ° C. A composition prepared by blending (Etflon EP-520, manufactured by Daikin Industries, Ltd., "Neoflon EP-520") at the ratio shown in Table 1 was melted at 320 ° C. by an extruder spinning machine having a diameter of 40 mm, and the pore diameter was 1.0 mm.
Was melt extruded from a die.
【００３２】紡出糸条をただちに８０℃の冷却温水浴中
に導き、冷却した後、９６℃の温水中で３．７倍に一次
延伸し、さらに引続いて１６０℃の空気浴中で１．２４
倍に二次延伸した。The spun yarn was immediately introduced into a cooling hot water bath at 80 ° C., cooled, and then primary-drawn 3.7 times in hot water at 96 ° C., followed by 1 hour drawing in a 160 ° C. air bath. .24
Secondary stretching was performed twice.
【００３３】なお、延伸されたモノフィラメントを、引
続いて１５５℃の空気浴中で１．０倍の定長熱処理後巻
き取った。The stretched monofilament was subsequently wound in a 155 ° C. air bath after a 1.0-fold constant-length heat treatment.
【００３４】得られたポリフェニレンサルファイドモノ
フィラメントの直径はそれぞれ０．４０mmであった。The diameter of each of the obtained polyphenylene sulfide monofilaments was 0.40 mm.
【００３５】これらのポリフェニレンサルファイドモノ
フィラメントについて、耐屈曲摩耗性、耐屈曲疲労性、
引張強度、引張伸度、結節強度および結節伸度を評価し
た結果を表１に併せて示す。With respect to these polyphenylene sulfide monofilaments, bending wear resistance, bending fatigue resistance,
Table 1 also shows the results of evaluation of tensile strength, tensile elongation, knot strength and knot elongation.
【００３６】なお、モノフィラメントの物性評価は次の
方法により行なった。The physical properties of the monofilament were evaluated by the following methods.
【００３７】耐屈曲摩耗性 糸摩耗試験機を用いて測定した、すなわち、試長：２０
ｃｍのモノフィラメントを３個のローラ間に水平に配置
し、一端側に２ｇｆ／ｔｅｘの荷重をかけてこの部分を
ローラからを垂下させ、他の２個のローラ間に１．０ｍ
ｍφ硬質鋼からなる摩擦子を摩擦角度：１１０°で配置
し、この摩擦子の部分でモノフィラメントを摩擦速度：
６０回／分、往復距離：２．５ｃｍの条件で往復運動さ
せた場合に、モノフィラメントが切断するまでの運動回
数を測定した。試験回数は５回とし、その平均値で示し
た。回数が大きいほど耐屈曲摩耗性がすぐれている。[0037] was measured using a flex abrasion resistance yarn abrasion tester, i.e., sample length: 20
cm monofilament is placed horizontally between the three rollers, a load of 2 gf / tex is applied to one end of the monofilament, and this part is hung from the roller.
A friction element made of mφ hard steel is arranged at a friction angle of 110 °, and a monofilament is rubbed at the friction element at a friction speed of:
When the reciprocating motion was performed under the conditions of 60 times / min and reciprocating distance: 2.5 cm, the number of motions until the monofilament was cut was measured. The number of tests was five, and the average value was shown. The greater the number, the better the flex wear resistance.
【００３８】耐屈曲疲労性 屈曲疲労試験機（ＴＯＹＯＳＥＩＫＩ社製）を用いて測
定した。すなわち、試長：８ｃｍのモノフィラメントの
一端側に５００ｇの荷重をかけ、他端側にチャックを接
続し、チャックを振角度：２２０°、回転数：１８０回
／分の条件で振子運動させた場合に、モノフィラメント
が切断するまでの運動回数を測定した。試験回数は５回
とし、その平均値で示した。回数が大きいほど耐屈曲疲
労性がすぐれている。Bending fatigue resistance The bending fatigue resistance was measured using a bending fatigue tester (manufactured by TOYOSEIKI). That is, when a load of 500 g is applied to one end of a monofilament having a test length of 8 cm, a chuck is connected to the other end, and the chuck is pendulum-moved at a swing angle of 220 ° and a rotation speed of 180 times / min. Next, the number of movements until the monofilament was cut was measured. The number of tests was five, and the average value was shown. The greater the number of times, the better the bending fatigue resistance.
【００３９】引張強度、引張伸度および結節強伸度 いずれもＪＩＳＬ１０１３−１９８１の規定に準じて測
定した。The tensile strength, tensile elongation and knotty elongation were all measured in accordance with JISL1013-1981.
【００４０】[0040]
【表１】 表１の結果から明らかなように、本発明のポリフェニレ
ンサルファイドモノフィラメント（実施例１〜４）は、
いずれも織物用モノフィラメントとして必要な引張強
度、引張伸度および結節強度・伸度を十分に保持しつ
つ、耐屈曲摩耗性および耐屈曲疲労性が改良されてお
り、物性バランスがきわめてすぐれたモノフィラメント
である。[Table 1] As is clear from the results in Table 1, the polyphenylene sulfide monofilaments of the present invention (Examples 1 to 4)
All of them are monofilaments that have excellent flexural wear resistance and flex fatigue resistance while maintaining sufficient tensile strength, tensile elongation and knot strength / elongation required for textile monofilaments, and have an extremely excellent balance of physical properties. is there.
【００４１】一方、フッ素系樹脂の添加量が０．０５重
量％未満の場合（比較例１，２）は、耐屈曲摩耗性およ
び耐屈曲疲労性の向上効果が得られず、０．４重量％を
越える場合には、耐屈曲摩耗性の改善効果が小さく、し
かも強伸度特性および結節特性の低下が著しくなる。On the other hand, when the addition amount of the fluororesin is less than 0.05% by weight (Comparative Examples 1 and 2), the effect of improving the bending wear resistance and the bending fatigue resistance is not obtained, and 0.4% by weight is not obtained. %, The effect of improving the bending wear resistance is small, and the strength and elongation properties and the nodular properties are significantly reduced.
【００４２】［実施例５〜７］実施例１〜４で用いたポ
リフェニレンサルファイドに対し、ポリフッ化ビニリデ
ン（ダイキン工業社製ＰＶＤＦ“ＶＰ８１０”）、エチ
レン−クロロトリフルオロエチレン共重合体（アウジモ
ント社社製ＥＣＴＦＥ、“ＨＡＬＡＲ５００”）、およ
びポリテトラフルオロエチレン（ダイキン工業社製、Ｐ
ＴＦＥ“Ｍ３００Ｐ”）を、各々０．２０重量％配合
し、他は実施例１〜４と同一の条件で溶融紡糸、二段延
伸および定長熱処理して得られたポリフェニレンサルフ
ァイドモノフィラメントについて、各物性を評価した結
果、表２に示したとおりいずれも物性バランスのすぐれ
るものであった。[Examples 5 to 7] The polyphenylene sulfide used in Examples 1 to 4 was replaced with polyvinylidene fluoride (PVDF “VP810” manufactured by Daikin Industries, Ltd.) and an ethylene-chlorotrifluoroethylene copolymer (Audimont Co., Ltd.). ECTFE, “HALAR500”), and polytetrafluoroethylene (manufactured by Daikin Industries, Ltd., P
TFE "M300P") was blended in an amount of 0.20% by weight, and the other properties of polyphenylene sulfide monofilaments obtained by melt spinning, two-stage drawing and constant length heat treatment under the same conditions as in Examples 1 to 4 were used. As a result, as shown in Table 2, all of them were excellent in physical property balance.
【００４３】[0043]
【表２】 [Table 2]
【００４４】[0044]
【発明の効果】以上詳細に説明したように、本発明のポ
リフェニレンサルファイドモノフィラメントは、ポリフ
ェニレンサルファイド自体のすぐれた耐熱性および耐薬
品性を具備し、しかも引張強度・伸度および結節強度・
伸度が均衡にすぐれ、十分な強靭性を発揮するばかり
か、耐屈曲摩耗性および耐屈曲疲労性にもすぐれるもの
である。As described in detail above, the polyphenylene sulfide monofilament of the present invention has excellent heat resistance and chemical resistance of polyphenylene sulfide itself, and has a tensile strength, an elongation and a knot strength.
It has excellent elongation and good toughness as well as excellent flex wear resistance and flex fatigue resistance.
【００４５】したがって、本発明のポリフェニレンサル
ファイドモノフィラメントは、産業用途に対し好適な性
能を有しており、特にこのポリフェニレンサルファイド
モノフィラメントを経糸および／または緯糸の少なくと
も一部に用いて織成した抄紙用ドライヤーカンバス、搬
送用ベルト、フィルター、サーマルボンド法不織布接着
工程用ネットコンベアおよび抄紙ワイヤーなどの工業用
織物は、産業用としての理想的な性能を発揮する。Therefore, the polyphenylene sulfide monofilament of the present invention has a suitable performance for industrial use, and in particular, a papermaking dryer canvas woven by using the polyphenylene sulfide monofilament for at least a part of a warp and / or a weft. Industrial fabrics such as conveyor belts, filters, net conveyors for the non-bonding process of the thermal bond nonwoven fabric, and papermaking wires exhibit ideal performance for industrial use.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ２１Ｆ 1/10 Ｄ２１Ｆ 1/10 7/08 7/08 Ａ // Ｄ０１Ｆ 6/94 Ｄ０１Ｆ 6/94 Ｚ ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification number Agency reference number FI Technical display location D21F 1/10 D21F 1/10 7/08 7/08 A // D01F 6/94 D01F 6/94 Z
Claims (4)
ッ素系樹脂を０．０５〜０．４０重量％配合した組成物
を溶融紡糸してなるポリフェニレンサルファイドモノフ
ィラメント。1. A polyphenylene sulfide monofilament obtained by melt-spinning a composition obtained by blending 0.05 to 0.40% by weight of a fluororesin with polyphenylene sulfide.
ロエチレン共重合体、エチレン−クロロトリフルオロエ
チレン共重合体、フッ化ビニリデン−テトラフルオロエ
チレン−ヘキサフルオロプロピレン共重合体、ポリテト
ラフルオロエチレン、ポリフッ化ビニリデン、ポリクロ
ロトリフルオロエチレンおよびポリフッ化ビニルから選
ばれた少なくとも１種である請求項１に記載のポリフェ
ニレンサルファイドモノフィラメント。2. The fluororesin is ethylene / tetrafluoroethylene copolymer, ethylene-chlorotrifluoroethylene copolymer, vinylidene fluoride-tetrafluoroethylene-hexafluoropropylene copolymer, polytetrafluoroethylene, polyfluorinated The polyphenylene sulfide monofilament according to claim 1, which is at least one selected from vinylidene, polychlorotrifluoroethylene, and polyvinyl fluoride.
ンサルファイドモノフィラメントを経糸および／または
緯糸の少なくとも一部に用いて織成してなる工業用織
物。3. An industrial woven fabric obtained by weaving the polyphenylene sulfide monofilament according to claim 1 or 2 for at least a part of a warp and / or a weft.
ト、フィルター、サーマルボンド法不織布接着工程用ネ
ットコンベアまたは抄紙ワイヤーである請求項３に記載
の工業用織物。4. The industrial fabric according to claim 3, which is a papermaking dryer canvas, a conveyor belt, a filter, a net conveyor for a nonwoven fabric bonding step of a thermal bonding method, or a papermaking wire.