JPH10315398A - Heat resistant sheet for electric insulation - Google Patents
Heat resistant sheet for electric insulationInfo
- Publication number
- JPH10315398A JPH10315398A JP12416197A JP12416197A JPH10315398A JP H10315398 A JPH10315398 A JP H10315398A JP 12416197 A JP12416197 A JP 12416197A JP 12416197 A JP12416197 A JP 12416197A JP H10315398 A JPH10315398 A JP H10315398A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- glass fiber
- para
- epoxy resin
- aromatic polyamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の属する技術分野】本発明は電気絶縁用耐熱シー
トに関する。さらに詳しくは、絶縁性に優れ、高温にお
いても強度、絶縁破壊電圧の熱劣化が小さい電気絶縁用
耐熱シートに関する。The present invention relates to a heat-resistant sheet for electrical insulation. More specifically, the present invention relates to a heat-resistant sheet for electrical insulation, which has excellent insulation properties, has low strength even at high temperatures, and has low thermal degradation of dielectric breakdown voltage.
【０００１】[0001]
【従来の技術】低電圧回転機のスロットライナ、層間絶
縁、ウエッジおよび小型静止機器のコイル層間絶縁に
は、電気絶縁用ポリエステルフィルムやその加工紙、例
えばポリエチレンテレフタレートフィルム（以下ＰＥＴ
フィルムとする）とプレスボードを貼り合わせた複合シ
ートなどが使用されている。この複合化の利点は、プレ
スボードがＰＥＴフィルムの表面を保護するため、圧縮
荷重を掛けたときの絶縁破壊電圧の低下が小さいことで
ある。また、複合シートの強度と破壊電圧はＰＥＴフィ
ルムが負担するため、絶縁紙単独の場合に比較して高い
破壊電圧レベルを実現できることなどが上げられる。2. Description of the Related Art A polyester film for electric insulation and its processed paper, for example, a polyethylene terephthalate film (hereinafter referred to as PET) are used for slot liner, interlayer insulation, wedge and coil interlayer insulation of a small stationary device for a low voltage rotating machine.
A composite sheet obtained by laminating a press board with a film is used. The advantage of this compounding is that the press board protects the surface of the PET film, so that the decrease in dielectric breakdown voltage when a compressive load is applied is small. In addition, since the PET film bears the strength and the breakdown voltage of the composite sheet, a higher breakdown voltage level can be realized as compared with the case where the insulating paper is used alone.
【０００２】近年の回転機の高性能化、小型化のために
耐熱性の高い複合シートが要求されている。これらの用
途には前記ＰＥＴフィルムやその加工紙では耐熱性が十
分ではなかった。なぜなら、要求される絶縁階級がＦ種
（１５５℃）〜Ｈ種（１８０℃）であるのに対して、Ｐ
ＥＴフィルム絶縁階級はＥ種（１２０℃）〜Ｂ種（１３
５℃）であり、しかもプレスボードはＡ種（１０５℃）
と耐熱性が低いためである。そこで耐熱性の高い絶縁紙
とＰＥＴフィルムを貼合した複合シートが使われてい
る。例えば、「電子デバイス・電子絶縁材料の新技術」
（（株）中日社出版）に、アラミド紙として代表的なノ
ーメックスとＰＥＴフィルムを貼合した複合シートが開
示されている。このノーメックスは、メタ系芳香族ポリ
アミドの短繊維とパルプ状のフィブリッドを湿式抄紙し
たアラミド紙である。In recent years, a composite sheet having high heat resistance has been demanded for higher performance and smaller size of a rotating machine. The heat resistance of the PET film or its processed paper was not sufficient for these uses. Because the required insulation class is class F (155 ° C) to class H (180 ° C),
ET film insulation class is class E (120 ° C)-class B (13
5 ° C), and press board type A (105 ° C)
And low heat resistance. Therefore, a composite sheet in which insulating paper having high heat resistance and a PET film are bonded is used. For example, "New technology for electronic devices and electronic insulating materials"
(Chunichisha Publishing Co., Ltd.) discloses a composite sheet obtained by laminating a typical Nomex and PET film as aramid paper. This Nomex is an aramid paper obtained by wet-making a short fiber of a meta-aromatic polyamide and a pulp-like fibrid.
【０００３】しかし、これらＰＥＴフィルムとアラミド
紙の複合シートは、アラミド紙が高価であることから、
市場に受け入れられにくい側面があった。However, these composite sheets of PET film and aramid paper are expensive because aramid paper is expensive.
There were aspects that were hard to accept in the market.
【０００４】[0004]
【発明が解決しようとする課題】本発明は電気絶縁性、
耐熱性に優れ、経済的に市場に受け入れられやすい電気
絶縁用耐熱シートを提供するものである。SUMMARY OF THE INVENTION The present invention relates to an electric insulating material,
An object of the present invention is to provide a heat-resistant sheet for electric insulation which has excellent heat resistance and is easily accepted in the market economically.
【０００５】[0005]
【課題を解決するための手段】本発明者らは、かかる現
状に鑑み鋭意研究を行った結果、ポリエチレンテレフタ
レートフィルムに、接着剤層を介して、パラ系芳香族ポ
リアミドフィブリッドとガラス繊維を、エポキシ樹脂を
バインダーとして用いて結合した耐熱絶縁シートを貼合
することにより、安価な耐熱絶縁紙を提供する手段をみ
いだした。Means for Solving the Problems The inventors of the present invention have conducted intensive studies in view of the present situation, and as a result, a para-aromatic polyamide fibrid and glass fiber have been applied to a polyethylene terephthalate film via an adhesive layer. By bonding a heat-resistant insulating sheet bonded using an epoxy resin as a binder, a means for providing an inexpensive heat-resistant insulating paper has been found.
【０００６】即ち、本発明は、ポリエチレンテレフタレ
ートフィルムの片面または両面に、接着剤層を介してパ
ラ系芳香族ポリアミドフィブリッドとガラス繊維からな
り、エポキシ樹脂を含有するシートを貼合して構成され
たことを特徴とする電気絶縁用耐熱シートである。That is, the present invention comprises a polyethylene terephthalate film having one or both surfaces bonded to a sheet made of para-aromatic polyamide fibrid and glass fiber via an adhesive layer and containing an epoxy resin. A heat-resistant sheet for electrical insulation, characterized in that:
【０００７】[0007]
【発明の実施の形態】本発明に用いるＰＥＴフィルムは
電気絶縁用として一般に用いられるものでよい。フィル
ムの厚さは任意に決定することができる。DESCRIPTION OF THE PREFERRED EMBODIMENTS The PET film used in the present invention may be a film generally used for electrical insulation. The thickness of the film can be arbitrarily determined.
【０００８】本発明において使用するパラ系芳香族ポリ
アミドフィブリッドは、種々のものがあるが、好ましく
はポリパラフェニレンテレフタルアミドである。更に具
体的には例えば、トワロン（登録商標、アクゾ社製）や
ケブラー（登録商標、デュポン社製）のフィブリッドが
ある。The para-aromatic polyamide fibrid used in the present invention is of various types, but is preferably polyparaphenylene terephthalamide. More specifically, for example, there are fibrids of Twaron (registered trademark, manufactured by Akzo) and Kevlar (registered trademark, manufactured by DuPont).
【０００９】ガラス繊維は、直径１５μｍ以下、好まし
くは１０μｍ以下で、長さ２〜１０ｍｍ、好ましくは３
〜８ｍｍのものを用いる。The glass fiber has a diameter of 15 μm or less, preferably 10 μm or less, and a length of 2 to 10 mm, preferably 3 μm.
の も の 8 mm is used.
【００１０】パラ系芳香族ポリアミドフィブリッドとガ
ラス繊維の混抄シートは、一般の抄紙機、例えば、円
網、傾斜ワイヤー、長網抄紙機などを用いて抄造され
る。The mixed sheet of para-aromatic polyamide fibrid and glass fiber is formed using a general paper machine, for example, a circular net, inclined wire, fourdrinier paper machine, or the like.
【００１１】本発明において使用するエポキシ樹脂とし
てはポリエチレンイミンーエピクロルヒドリン縮合体、
ポリアミドアミンエピクロルヒドリン樹脂、ジメチルア
ミンエピクロルヒドリン樹脂、各種ビスフェノールＡ型
樹脂およびこれら誘導体の溶液またはエマルジョン等で
あって、単独でも２種類以上併用してもよい。エポキシ
樹脂は、抄紙の際に内添、スプレー含浸、サイズプレス
含浸、含浸機での含浸などによってパラ系芳香族ポリア
ミドフィブリッドとガラス繊維の混抄シートに含有させ
ることができる。エポキシ樹脂の含有量は混抄シート重
量に対して、固形分で２％以上が好ましい。これより含
有量が少ないとシートの毛羽立ちなどが起きる。エポキ
シ樹脂の含有量を多くすると、毛羽立ちは無くなるが、
シートの柔軟性が失われて硬くなる。したがって、用途
に合わせて適宜含有量を決定すればよい。The epoxy resin used in the present invention includes polyethyleneimine-epichlorohydrin condensate,
Polyamideamine epichlorohydrin resin, dimethylamine epichlorohydrin resin, various bisphenol A-type resins, and solutions or emulsions of these derivatives may be used alone or in combination of two or more. The epoxy resin can be contained in the mixed sheet of para-aromatic polyamide fibrid and glass fiber by internal addition, spray impregnation, size press impregnation, impregnation with an impregnating machine, or the like during papermaking. The content of the epoxy resin is preferably 2% or more in terms of solid content based on the weight of the mixed sheet. If the content is less than this, fluffing of the sheet occurs. When the content of the epoxy resin is increased, fluffing is eliminated,
The sheet loses its flexibility and becomes hard. Therefore, the content may be appropriately determined according to the use.
【００１２】貼合に用いられる接着剤は、ポリウレタン
樹脂、エポキシエステル系、ポリエステル系、エポキシ
樹脂、シリコーン樹脂などがある。塗布量は１０〜２０
ｇ／ｍ2が好ましい。これに満たない塗布量では、貼合
相手の紙に凹凸があるために充分な接着強度が得られ
ず、これを越す塗布量では接着力の向上がなく、無駄で
ある。The adhesive used for bonding includes polyurethane resin, epoxy ester type, polyester type, epoxy resin, silicone resin and the like. Coating amount is 10-20
g / m 2 is preferred. If the amount of application is less than this, sufficient adhesion strength cannot be obtained due to the unevenness of the paper of the bonding partner. If the amount of application exceeds this, there is no improvement in the adhesive strength and it is useless.
【００１３】本発明はポリエチレンテレフタレートフィ
ルムにパラ系芳香族ポリアミドフィブリッドとガラス繊
維からなるシートにエポキシ樹脂を含有せしめた耐熱絶
縁紙を貼合し、耐熱性と電気絶縁性を向上させたもので
ある。すなわち、ＰＥＴフィルム単独の絶縁階級はＥ種
（１２０℃）であるが、耐熱絶縁紙によってＰＥＴフィ
ルムが被覆され、空気に触れにくくなるために、熱劣化
速度が低下し、耐熱特性が向上する。また、耐熱絶縁紙
の側からみれば、紙より絶縁性に優れたＰＥＴフィルム
と貼合されたことにより、絶縁性が向上することにな
る。さらに、本発明では原料にガラス繊維を配合するた
め、従来のメタ系芳香族ポリアミド紙とＰＥＴフィルム
の貼合シートよりも、安価にシートを得ることができ
る。According to the present invention, a polyethylene terephthalate film is bonded to a sheet made of para-aromatic polyamide fibrid and glass fiber with heat-resistant insulating paper containing an epoxy resin to improve heat resistance and electrical insulation. is there. In other words, the insulation class of the PET film alone is class E (120 ° C.), but since the PET film is covered with the heat-resistant insulating paper and is less likely to come into contact with air, the heat deterioration rate is reduced and the heat resistance is improved. In addition, when viewed from the heat-resistant insulating paper side, the insulating property is improved by being bonded to the PET film having better insulating property than the paper. Furthermore, in the present invention, since glass fiber is blended into the raw material, a sheet can be obtained at a lower cost than a conventional laminated sheet of a meta-aromatic polyamide paper and a PET film.
【００１４】[0014]
【実施例】本発明を下記実施例によりさらに具体的に説
明するが、本発明はこれらに限定されるものではない。
なお、実施例および比較例において表示する「％」は、
特記のないかぎり「固形分重量％」を示す。The present invention will be described in more detail with reference to the following Examples, but it should not be construed that the invention is limited thereto.
Note that “%” displayed in Examples and Comparative Examples is
Unless otherwise specified, "solid content weight%" is indicated.
【００１５】実施例１ ポリパラフェニレンテレフタルアミドフィブリッド（ト
ワロン１０９４）をリファイナーによって、カナディア
ンスタンダードフリーネス（Ｃ．Ｓ．Ｆ）８０ｍｌに叩
解してスラリーとした。このスラリーに、直径６μｍ、
長さ３ｍｍのガラス繊維（ＲＥＳ０３ＧＰ１１Ｗ、日本
板ガラス社製）を固形分重量で５０対５０の割合になる
ように混合して原料スラリーを調成した。これにポリア
ミドエピクロルヒドリン（ＷＳー５７０、日本ＰＭＣ社
製）を１％添加して撹拌した後、ポリアクリルアミド系
の紙力剤（ポリストロン１９４、荒川化学社製）を１％
添加し、傾斜ワイヤーで抄き上げ、毛布に移したウエッ
トシートに水分散エポキシ樹脂（ＥＮ−０２７０、大日
本インキ化学工業社製）を塗布量が完成シートに対して
２％になるようにスプレーし、プレス後、ヤンキードラ
イヤー、アフタードライヤーで乾燥して、ポリパラフェ
ニレンテレフタルアミドフィブリッドとガラス繊維の混
抄紙（以下アラミドフィブリッド／ガラス繊維混抄絶縁
紙と称す）を得た。このアラミドフィブリッド／ガラス
繊維混抄絶縁紙は坪量が２０．４ｇ／ｍ2、（エポキシ
樹脂の総含有量は対シート３％）、厚さが６０μｍであ
った。Example 1 Polyparaphenylene terephthalamide fibrid (Twaron 1094) was beaten with a refiner to 80 ml of Canadian Standard Freeness (CSF) to form a slurry. This slurry has a diameter of 6 μm,
A raw material slurry was prepared by mixing glass fibers having a length of 3 mm (RES03GP11W, manufactured by Nippon Sheet Glass Co., Ltd.) so as to have a solid content ratio of 50:50. To this, 1% of polyamide epichlorohydrin (WS-570, manufactured by Nippon PMC) was added and stirred, and then a polyacrylamide-based paper strength agent (Polystron 194, manufactured by Arakawa Chemical Co., Ltd.) was added to 1%.
A water-dispersed epoxy resin (EN-0270, manufactured by Dainippon Ink and Chemicals, Inc.) is sprayed onto the wet sheet that has been added, made up with an inclined wire, and transferred to a blanket so that the coating amount is 2% of the finished sheet. After pressing, the mixture was dried with a Yankee dryer and an after-dryer to obtain a mixed paper of polyparaphenylene terephthalamide fibrid and glass fiber (hereinafter referred to as aramid fibrid / glass fiber mixed insulating paper). This aramid fibrid / glass fiber mixed insulating paper had a basis weight of 20.4 g / m 2 (the total content of epoxy resin was 3% of the sheet) and a thickness of 60 μm.
【００１６】次にポリウレタン系接着剤(ＧＡ−７２
１、住友ベークライト社製）をトルエンで希釈して、Ｐ
ＥＴフィルム（厚さ１ミル＝２５μｍ、３５．４ｇ／ｃ
ｍ2、ダイヤホイルヘキスト社製）に固形分塗布量１５
ｇ／ｍ2になるように塗布した後、熱風ドライヤーで接
着剤を予備乾燥して前記アラミドフィブリッド／ガラス
繊維混抄絶縁紙と貼合し、接着剤のキュアのために３日
間養生して電気絶縁用耐熱シートを得た。Next, a polyurethane adhesive (GA-72)
1. Sumitomo Bakelite Co., Ltd.) diluted with toluene
ET film (1 mil thickness = 25 μm, 35.4 g / c
m 2 , manufactured by Diafoil Hoechst)
g / m 2 , and then pre-dry the adhesive with a hot-air drier and paste it on the aramid fibrid / glass fiber mixed insulating paper, and cure for 3 days to cure the adhesive. A heat-resistant sheet for insulation was obtained.
【００１７】実施例２ 実施例１と同様にして電気絶縁用耐熱シートを得たが、
アラミドフィブリッド／ガラス繊維混抄絶縁紙の坪量を
４０．２ｇ／ｍ2（エポキシ樹脂含有量は対シート３
％）、厚さを１１５μｍとした。Example 2 A heat-resistant sheet for electrical insulation was obtained in the same manner as in Example 1.
The basis weight of aramid fibrid / glass fiber mixed insulating paper is 40.2 g / m 2 (the epoxy resin content is
%), And the thickness was 115 μm.
【００１８】実施例３ 実施例１と同様にして電気絶縁用耐熱シートを得、厚さ
５０μｍ（７０．８ｇ／ｍ2）のＰＥＴフィルムと貼合
した。Example 3 A heat-resistant sheet for electrical insulation was obtained in the same manner as in Example 1, and was bonded to a PET film having a thickness of 50 μm (70.8 g / m 2 ).
【００１９】実施例４ 実施例２と同様にして電気絶縁用耐熱シートを得たが、
内添するポリアミドエピクロルヒドリンの添加量を対原
料固形分２％とし、ポリアクリルアミド系の紙力剤（ポ
リストロン１９４、荒川化学社製）の添加量を対原料固
形分１．５％とし、スプレーによるエポキシ樹脂の含浸
はしなかった。アラミドフィブリッド／ガラス繊維混抄
絶縁紙の坪量は４０．４ｇ／ｍ2、厚さは１１５μｍで
あり、厚さ５０μｍ（７０．８ｇ／ｍ2）のＰＥＴフィ
ルムと貼合した。Example 4 A heat-resistant sheet for electrical insulation was obtained in the same manner as in Example 2.
The addition amount of the polyamide epichlorohydrin to be added was set to 2% based on the solid content of the raw material, and the addition amount of the polyacrylamide-based paper strength agent (Polystron 194, manufactured by Arakawa Chemical Co.) was set to 1.5% based on the solid content of the raw material. No epoxy resin impregnation was performed. The aramid fibrid / glass fiber mixed insulating paper had a basis weight of 40.4 g / m 2 and a thickness of 115 μm, and was bonded to a PET film having a thickness of 50 μm (70.8 g / m 2 ).
【００２０】実施例５ 厚さ２５μｍのＰＥＴフィルムの両面にポリウレタン系
接着剤をそれぞれ１５ｇ／ｍ2になるように塗布し、実
施例１で得られたＰＥＴフィルムを貼合する前のアラミ
ドフィブリッド／ガラス繊維混抄絶縁紙を貼合した電気
絶縁用耐熱シートを得た。Example 5 Aramid fibrid before applying the PET film obtained in Example 1 by applying a polyurethane-based adhesive to both sides of a PET film having a thickness of 25 μm at a rate of 15 g / m 2. / A heat-resistant sheet for electrical insulation laminated with a glass fiber mixed insulating paper was obtained.
【００２１】実施例６ 実施例５と同様にして電気絶縁用耐熱シートを得たが、
ＰＥＴフィルムの両面に貼合したアラミドフィブリッド
／ガラス繊維混抄絶縁紙は実施例２と同じものとした。Example 6 A heat-resistant sheet for electrical insulation was obtained in the same manner as in Example 5.
The aramid fibrid / glass fiber mixed insulating paper bonded to both sides of the PET film was the same as in Example 2.
【００２２】比較例１ ＰＥＴフィルム（厚さ１ミル＝２５μｍ、３５．４ｇ／
ｃｍ2、ダイヤホイルヘキスト）を用いて試験に供し
た。Comparative Example 1 PET film (1 mil thickness = 25 μm, 35.4 g /
cm 2 , Diafoil Hoechst).
【００２３】比較例２ 実施例１のアラミドフィブリッド／ガラス繊維混抄絶縁
紙を試験に供した。Comparative Example 2 The aramid fibrid / glass fiber mixed insulating paper of Example 1 was subjected to a test.
【００２４】比較例３ ＮＵＫＰをリファイナーによって、Ｃ．Ｓ．Ｆ４５０ｍ
ｌに叩解し、パルプスラリーを得た。このスラリーを用
いて、坪量が８０ｇ／ｍ2になるように円網とヤンキー
ドライヤーを備える抄紙機にて抄紙し、さらにカレンダ
ーで処理して、厚さが８０μｍのプレスボードを得た。
得られたプレスボードを実施例１と同様にして接着剤を
介して、ＰＥＴフィルムに貼合して、厚さ１２０μｍの
電気絶縁シートを得た。Comparative Example 3 NUKP was subjected to C.I. S. F450m
to obtain a pulp slurry. Using this slurry, paper was made with a paper machine equipped with a circular net and a Yankee dryer so that the basis weight became 80 g / m 2 , and further processed with a calender to obtain a press board having a thickness of 80 μm.
The obtained press board was bonded to a PET film via an adhesive in the same manner as in Example 1 to obtain an electric insulating sheet having a thickness of 120 µm.
【００２５】実施例１〜６および比較例１〜３にて得た
電気絶縁性耐熱シートの電気絶縁性および耐熱性を評価
した。評価法は以下の試験法に従った。The electrical insulation and heat resistance of the electrically insulating heat-resistant sheets obtained in Examples 1 to 6 and Comparative Examples 1 to 3 were evaluated. The evaluation method followed the following test methods.
【００２６】（電気絶縁性評価）ＪＩＳ Ｃ−２１１１
にしたがって、絶縁破壊電圧を評価した。値が大きい方
が良好である。(Evaluation of electrical insulation) JIS C-2111
According to the above, the dielectric breakdown voltage was evaluated. The larger the value, the better.
【００２７】（耐熱性評価）ＪＥＣー６１５１「電気絶
縁材料の耐熱性試験方法通則」（電気学会 電気規格調
査会標準規格）にしたがって、引張強度の５０％劣化時
間を終点判定基準として評価した。実施例および比較例
で得られた電気絶縁用耐熱シートの電気絶縁性および耐
熱性の評価結果を表１に示す。(Evaluation of Heat Resistance) In accordance with JEC-6151 “General rules for heat resistance test method for electrical insulating materials” (standards of the Institute of Electrical Engineers of Japan), 50% degradation time of tensile strength was evaluated as an end point judgment standard. Table 1 shows the evaluation results of the electrical insulation and heat resistance of the heat-insulating sheets for electrical insulation obtained in the examples and comparative examples.
【００２８】[0028]
【表１】 [Table 1]
【００２９】（評価）表１から明らかなように、実施例
１〜６で得られる電気絶縁用耐熱シートは比較例１に示
すＰＥＴフィルムおよび比較例３に示すＰＥＴフィルム
をプレスボードに貼合したシートに比較して耐熱性が高
く、耐熱シートによってＰＥＴフィルムの耐熱性の低さ
を補い、耐熱性が向上していることがわかる。また、実
施例１〜６で得られる電気絶縁用耐熱シートは比較例２
に比べ、電気絶縁性に優れていることがわかる。(Evaluation) As is clear from Table 1, the heat-resistant sheets for electrical insulation obtained in Examples 1 to 6 were obtained by bonding a PET film shown in Comparative Example 1 and a PET film shown in Comparative Example 3 to a press board. It can be seen that the heat resistance is higher than that of the sheet, and the heat resistance sheet compensates for the low heat resistance of the PET film, and the heat resistance is improved. The heat-resistant sheet for electrical insulation obtained in Examples 1 to 6 is Comparative Example 2.
It can be seen that the electrical insulation is superior to that of
【００３０】[0030]
【発明の効果】本発明は、ＰＥＴフィルムの片面または
両面に接着剤を介して、エポキシ樹脂を含有する、パラ
系芳香族ポリアミドフィブリッドとガラス繊維混抄紙を
貼合してなる耐熱絶縁シートであり、絶縁性、耐熱性、
経済的に優れる。The present invention relates to a heat-resistant insulating sheet obtained by laminating a para-aromatic polyamide fibrid containing epoxy resin and a glass fiber mixed paper on one or both sides of a PET film via an adhesive. Yes, insulation, heat resistance,
Excellent economical.
Claims (1)
面または両面に接着剤層を介して、パラ系芳香族ポリア
ミドフィブリッドとガラス繊維からなり、エポキシ樹脂
を含有するシートを貼合して構成されたことを特徴とす
る電気絶縁用耐熱シート。 【０００１】1. A polyethylene terephthalate film comprising a para-aromatic polyamide fibrid and a glass fiber bonded on one or both sides of an adhesive layer on one or both sides thereof, and a sheet containing an epoxy resin is bonded. Heat-resistant sheet for electrical insulation. [0001]