JPH10287352A - Heat-insulating lid for container - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain a lid which is free from cracks, whose fitness may not drop and which has high heat insulation by thermoforming a sheet comprising resin films laminated, specifying its thickness, density and a span value at specific values and also by specifying a buckling point load and flexion quantity in a pressing bend test at specific values. SOLUTION: An injection foaming sheet comprising styrene containing resin as base resin or a sheet comprising the injection foaming sheet and a resin film laminated thereon is thermoformed, and a heat-insulating lid 4 for a container with a thickness of 0.3 to 3.0 mm and a density of 0.05 to 0.80 g/cc has a buckling point load of 25 to 100 g/cm and a flexion quantity of 30 to 80 mm in a pressing bend test in a span of 100 mm. Therefore, it has both appropriate flexibility and strength, wherein even if a lid is mounted on the container by an automation line, the lid may not crack, or even if the containers filled with contents are stacked in stages, the lid may not deform to cause deterioration in fitness. Further, expansion of an entire heat-insulating lid is suppressed even at the time of using a closed lid at a high temperature or draining hot water.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、容器用断熱蓋に関
し、特に即席ラーメン、即席焼きそば等の食品容器の蓋
として好適に使用できる容器用断熱蓋に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a heat insulating cover for a container, and more particularly to a heat insulating cover for a container which can be suitably used as a lid for food containers such as instant noodles and instant noodles.

【０００２】[0002]

【従来の技術】従来、例えば、即席ラーメン、即席焼き
そば等の即席麺容器に対して用いる容器用蓋の場合、気
密性を重視して非発泡樹脂シートを成形した蓋が広く用
いられている。しかし、このような非発泡樹脂シートを
成形した蓋では、容器本体と蓋との嵌合気密性は維持で
きる反面、蓋そのものの断熱性が劣るため、容器内の内
容物を充分に保温できるようなものではなかった。特
に、即席焼きそばのように麺を熱湯でもどすため、いっ
たん容器に熱湯を注入した後、この熱湯を流し出してか
ら食する場合には、断熱性に劣る非発泡樹脂シートを成
形した蓋では火傷を負う危険があった。2. Description of the Related Art Conventionally, in the case of a container lid used for instant noodle containers such as instant noodles and instant yakisoba, a lid formed of a non-foamed resin sheet has been widely used with an emphasis on airtightness. However, in the lid formed of such a non-foamed resin sheet, while the fitting airtightness between the container body and the lid can be maintained, the heat insulation of the lid itself is poor, so that the contents in the container can be sufficiently kept warm. It was not something. In particular, in order to return noodles with boiling water like instant yakisoba, once pouring hot water into a container and then pouring out the hot water before eating, a lid made of a non-foamed resin sheet with poor heat insulating properties will cause burns. There was a danger of incurring.

【０００３】特開平８−２３０９１５号公報には、発泡
シートを基材樹脂として使用し、これを発泡成形した食
品容器用断熱蓋が開示されている。また、該公報には発
泡シートにスチレンーブタジエンブロック共重合体を含
有させた樹脂フィルムを積層することで、脆さを改善で
き、成形後に抜き加工してシートから蓋を分離する際に
蓋の周囲が割れたりすることを防止することができる
と、されている。[0003] Japanese Patent Application Laid-Open No. 8-230915 discloses a heat insulating lid for a food container in which a foamed sheet is used as a base resin and is foamed and formed. Further, the publication discloses that by laminating a resin film containing a styrene-butadiene block copolymer on a foamed sheet, the brittleness can be improved. It is said that the surroundings can be prevented from cracking.

【０００４】[0004]

【発明が解決しようとする課題】しかし、このような容
器用断熱蓋を、例えば食品容器の蓋として使用する場合
に、実際には、即席麺メーカーで麺充填容器へ蓋を被覆
する方法として、自動機にて高速で連続的に行われるこ
とが多く、この際、充分に嵌合させるために、いったん
蓋を湾曲させた後、被覆ロールを使用してしごきながら
容器本体に装着する方法が採用されているので、上記の
ような発泡シートにて成形された蓋は、蓋を湾曲させた
際に割れるという問題を生じた。このような割れを回避
するために、人手で蓋を装着することも可能であるが、
非効率的であるばかりか、このような蓋は輸送時、実食
時に、蓋の周辺嵌合部、あるいは湯切り用切り起こし部
が割れたり、切断する恐れがあり性能的に不充分であっ
た。また、内容物を充填した容器を段積みした際に、蓋
が変形し嵌合性が低下することが生じた。However, when such a heat insulating lid for a container is used, for example, as a lid for a food container, in practice, an instant noodle maker uses a method for coating the lid on a noodle filling container. It is often performed continuously at high speed with an automatic machine. In this case, in order to make a sufficient fit, a method is used in which the lid is once bent and then attached to the container body while squeezing using a coating roll. Therefore, there has been a problem that the lid formed of the foam sheet as described above breaks when the lid is bent. To avoid such cracking, it is possible to attach the lid manually,
In addition to inefficiency, such lids may be broken or cut at the time of transportation or eating, and the fitting portion around the lid or the cut-and-raised portion for hot water drainage may not be sufficient, resulting in insufficient performance. Was. In addition, when the containers filled with the contents were stacked, the lid was deformed and the fitting property was reduced.

【０００５】そこで、本発明者らは、上記の問題点を解
消することを目的として、自動機にて高速で連続的に容
器へ蓋を被覆する際に、いったん蓋を湾曲させて被覆ロ
ールにかける行程で割れが生じず、内容物を充填した容
器を段積みした際に、蓋が変形し嵌合性が低下すること
がない容器用断熱蓋であって、かつ高い断熱性を有し、
火傷や手を切る等のおそれがない蓋を提供せんとして鋭
意検討した結果、完成したものである。[0005] In order to solve the above-mentioned problems, the inventors of the present invention have been trying to cover a container with a cover at a high speed and continuously by an automatic machine. Cracking does not occur in the process of applying, when the containers filled with the contents are stacked, the lid is not deformed and the fitting property is not reduced, and has a high heat insulating property, and
It was completed as a result of intensive studies to provide a lid that would not cause burns or cut hands.

【０００６】[0006]

【課題を解決するための手段】本発明は、スチレン系樹
脂を基材樹脂とする押出発泡シート、または前記押出発
泡シートに樹脂フィルムを積層したシートを熱成形した
厚みが０．３〜３．０ｍｍ、密度が０．０５〜０．８０
ｇ／ｃｃの容器用断熱蓋であって、スパン１００ｍｍで
の押し曲げ試験における座屈点荷重が２５〜１００ｇ／
ｃｍ、かつ撓み量が３０〜８０ｍｍであることを特徴と
する容器用断熱蓋である。According to the present invention, an extruded foamed sheet using a styrene resin as a base resin, or a sheet obtained by laminating a resin film on the extruded foamed sheet, has a thickness of 0.3 to 3 mm. 0mm, density 0.05 ~ 0.80
g / cc container heat-insulating lid having a buckling point load of 25 to 100 g / cm in a push bending test at a span of 100 mm.
cm, and the amount of deflection is 30 to 80 mm.

【０００７】本発明の容器用断熱蓋を構成する発泡樹脂
シートの基材樹脂であるスチレン系樹脂としては、スチ
レン、メチルスチレン、エチルスチレン、イソプロピル
スチレン、ジメチルスチレン、クロルスチレン、ブロモ
スチレン、ビニルトルエン、ビニルキシレン等のスチレ
ン単量体の単独重合体、又はアクリロニトリル、メタク
リロニトリル、アクリル酸、メタクリル酸、アクリル酸
エステル（例えばメチル、エチル等のエステル）、メタ
クリル酸（例えばメチル、エチル等のエステル）、無水
マレイン酸、ブタジエン等のビニル単量体との共重合体
が挙げられる。具体的には、ポリスチレン樹脂、スチレ
ン−無水マレイン酸共重合体、スチレン−アクリル酸共
重合体、スチレン−アクリル酸エステル共重合体、耐衝
撃性ポリスチレン樹脂（ＨＩＰＳ）、スチレン−アクリ
ロニトリル共重合体、アクリロニトリル−ブタジエン−
スチレン三元共重合体等の耐熱性、耐衝撃性に優れた樹
脂が挙げられる。The styrene resin which is the base resin of the foamed resin sheet constituting the heat insulating lid for the container of the present invention includes styrene, methylstyrene, ethylstyrene, isopropylstyrene, dimethylstyrene, chlorostyrene, bromostyrene, vinyltoluene. , Homopolymers of styrene monomers such as vinyl xylene, or acrylonitrile, methacrylonitrile, acrylic acid, methacrylic acid, acrylates (eg, esters such as methyl, ethyl, etc.), and methacrylic acids (eg, esters such as methyl, ethyl, etc.) ), And copolymers with vinyl monomers such as maleic anhydride and butadiene. Specifically, polystyrene resin, styrene-maleic anhydride copolymer, styrene-acrylic acid copolymer, styrene-acrylate copolymer, impact-resistant polystyrene resin (HIPS), styrene-acrylonitrile copolymer, Acrylonitrile-butadiene-
Resins having excellent heat resistance and impact resistance, such as styrene terpolymers, may be mentioned.

【０００８】上記基材樹脂には、脆性改善の観点から、
ゴム分が含まれるものが好ましく、また、ゴム分が含ま
れないものにはゴム分を添加することが好ましい。ここ
で、ゴム分としては、種々のものが用いられるが、ブレ
ンド成分とし用いる場合にはブタジエンゴム、エチレン
−プロピレンゴム、スチレン−ブタジエンゴム等を添加
して用いるのが好適であり、共重合成分として用いる場
合には、ブタジエン、イソプレン、クロロプレン等のモ
ノマー又はオリゴマーを所定のモル比で共重合してなる
ポリスチレン系樹脂を用いるのが好適である。[0008] From the viewpoint of brittleness improvement,
It is preferable to include a rubber component, and it is preferable to add a rubber component to a component not including a rubber component. Here, various rubber components are used, but when used as a blend component, it is preferable to add butadiene rubber, ethylene-propylene rubber, styrene-butadiene rubber, or the like, and to use a copolymer component. In the case of using a polystyrene resin, it is preferable to use a polystyrene resin obtained by copolymerizing a monomer or oligomer such as butadiene, isoprene, or chloroprene at a predetermined molar ratio.

【０００９】上記基材樹脂は、公知の押出発泡成形に付
されることにより押出発泡シートが得られる。押出発泡
法は、所望の密度となるように押出機に基材樹脂、発泡
剤及び添加剤を入れ、溶融及び混合した後、ダイから押
し出すことにより行われる。なお、予め他の押出機で基
材樹脂、発泡剤及び添加剤を均一に溶解し及び混合した
後、押出機に送ってもよい。The extruded foam sheet is obtained by subjecting the base resin to known extrusion foam molding. The extrusion foaming method is performed by putting a base resin, a foaming agent and an additive into an extruder so as to have a desired density, melting and mixing, and then extruding from a die. The base resin, the foaming agent and the additive may be uniformly dissolved and mixed in advance with another extruder, and then sent to the extruder.

【００１０】押出発泡成形に際して使用できる発泡剤
は、公知のものをいずれも使用できる。具体的には、分
解型発泡剤、気体又は揮発性の発泡剤が使用できる。分
解型発泡剤としては、例えば、炭酸アンモニウム、重炭
酸ナトリウム、重炭酸アンモニウム、亜硝酸アンモニウ
ム、カルシウムアジド、ナトリウムアジド、ホウ水素ナ
トリウム等の無機系分解性発泡剤、アゾジカルボンアミ
ド、アゾビススルホルムアミド、アゾビスイソブチロニ
トリル及びジアゾアミノベンゼン等のアゾ化合物、Ｎ，
Ｎ’−ジニトリソペンタンメチレンテトラミン及びＮ，
Ｎ’−ジメチル−Ｎ，Ｎ’−ジニトロソテレフタルアミ
ド等のニトロソ化合物、ベンゼンスルホニルヒドラジ
ド、ｐ−トルエンスルホニルヒドラジド及びｐ，ｐ’−
オキシビスベンゼンスルホニルセミカルバジド、ｐ−ト
ルエンスルホニルセミカルバジド、トリヒドラジノトリ
アジン、バリウムアゾジカルボキシレート、クエン酸等
が挙げられる。これら発泡剤は、単独でも組み合わせて
もよい。更に、分解温度、発生ガス量及び分解速度を調
節するために公知の発泡助剤を添加してもよい。Any known foaming agent can be used for extrusion foaming. Specifically, a decomposable foaming agent, a gaseous or volatile foaming agent can be used. Examples of the decomposable blowing agent include, for example, inorganic decomposable blowing agents such as ammonium carbonate, sodium bicarbonate, ammonium bicarbonate, ammonium nitrite, calcium azide, sodium azide, sodium borohydride, azodicarbonamide, azobissulfformamide, Azo compounds such as azobisisobutyronitrile and diazoaminobenzene;
N'-dinitrisopentamethylenetetramine and N,
Nitroso compounds such as N'-dimethyl-N, N'-dinitrosoterephthalamide, benzenesulfonylhydrazide, p-toluenesulfonylhydrazide and p, p'-
Oxybisbenzenesulfonyl semicarbazide, p-toluenesulfonyl semicarbazide, trihydrazinotriazine, barium azodicarboxylate, citric acid and the like can be mentioned. These blowing agents may be used alone or in combination. Further, a known foaming aid may be added to adjust the decomposition temperature, the amount of generated gas, and the decomposition rate.

【００１１】気体の発泡剤としては、窒素、炭酸ガス、
プロパン、ｎ−ブタン、ｉ−ブタン、ｔｅｒｔ−ブタ
ン、メチルエーテル等が挙げられる。一方、揮発性の発
泡剤としては、エーテル、石油エーテル、アセトン、ペ
ンタン、イソペンタン、ヘキサン、イソヘキサン、ヘプ
タン、イソヘプタン、ベンゼン、トルエン等が挙げられ
る。また、上記以外にも水を使用することができる。上
記発泡剤のうち、ｎ−ブタン、ｉ−ブタン、窒素、炭酸
ガスが好ましい。As gaseous foaming agents, nitrogen, carbon dioxide,
Examples include propane, n-butane, i-butane, tert-butane, methyl ether and the like. On the other hand, examples of the volatile foaming agent include ether, petroleum ether, acetone, pentane, isopentane, hexane, isohexane, heptane, isoheptane, benzene, and toluene. In addition to the above, water can be used. Among the above foaming agents, n-butane, i-butane, nitrogen and carbon dioxide are preferred.

【００１２】添加剤としては、例えば、フィラー、核剤
（タルク、炭酸水素ナトリウム、炭酸水素アンモニウ
ム、炭酸カルシウム、クレー、クエン酸等）、着色剤、
難燃剤、滑剤（炭化水素、脂肪酸系、脂肪酸アミド系、
エステル系、アルコール系、金属石鹸シリコン油、低分
子ポリエチレン等のワックスなど）、展着剤（流動パラ
フィン、ポリエチレングリコール、ポリブテン等）、分
散剤等が挙げられる。これら添加剤は、所望の性質を有
する熱可塑性樹脂の発泡体を得るのに、及び容器用断熱
蓋としての性能を損なわない範囲で添加することが好ま
しい。フィラーの含有量は、基材樹脂に対して０．５〜
１０重量％であることがより好ましい。フィラーの含有
量が０．５重量％未満の場合、気泡が細かくならず、成
形品の表面平滑性が悪くなるので好ましくない。一方、
１０重量％を超える場合、実用時に水蒸気が蓋にしみこ
み易くなり、湯切り時に手が熱く、容器を支えられなく
なるので好ましくない。Examples of additives include fillers, nucleating agents (talc, sodium hydrogen carbonate, ammonium hydrogen carbonate, calcium carbonate, clay, citric acid, etc.), coloring agents,
Flame retardants, lubricants (hydrocarbons, fatty acids, fatty amides,
Esters, alcohols, metal soaps, silicone oils, waxes such as low molecular weight polyethylene, etc.), spreading agents (liquid paraffin, polyethylene glycol, polybutene, etc.), dispersants and the like. These additives are preferably added in order to obtain a thermoplastic resin foam having desired properties and within a range that does not impair the performance as a heat insulating lid for a container. The content of the filler is 0.5 to the base resin.
More preferably, it is 10% by weight. If the content of the filler is less than 0.5% by weight, bubbles are not fine and the surface smoothness of the molded article is deteriorated, which is not preferable. on the other hand,
If it exceeds 10% by weight, steam is likely to permeate into the lid during practical use, and hands become hot when draining the hot water, and the container cannot be supported.

【００１３】本発明のスチレン系樹脂を基材樹脂とする
押出発泡シートに積層する樹脂フィルムとしては、スチ
レン系樹脂、ポリエチレン系樹脂、ポリプロピレン系樹
脂、アクリル系樹脂、ポリエステル系樹脂等の樹脂のフ
ィルムが使用できるが、特に、スチレン系樹脂フィルム
を使用して、このフィルム樹脂にゴム分を含有させると
更なる脆性改良効果が得られるから好ましい。更に、裏
面に印刷がほどこされたフィルムの場合には、ゴム含有
樹脂として、スチレン−ブタジエンブロック共重合樹脂
を用いると、フィルムの透明性を損なわず印刷柄が鮮明
になり好ましい。The resin film to be laminated on the extruded foamed sheet of the present invention using a styrene resin as a base resin is a resin film of a styrene resin, a polyethylene resin, a polypropylene resin, an acrylic resin, a polyester resin or the like. However, it is particularly preferable to use a styrene-based resin film and to add a rubber component to the film resin since a further brittleness improving effect can be obtained. Further, in the case of a film having a back side printed thereon, it is preferable to use a styrene-butadiene block copolymer resin as the rubber-containing resin because the printed pattern becomes clear without impairing the transparency of the film.

【００１４】本発明のスチレン系樹脂を基材樹脂とする
押出発泡シート、または前記押出発泡シートに樹脂フィ
ルムを積層したシートを熱成形した容器用断熱蓋の厚み
は０．３〜３．０ｍｍである必要があり、厚みが０．３
ｍｍ未満では、蓋としての強度が弱くなり、断熱性も悪
くなる。厚みが３．０ｍｍを越えると成形時の型との精
度が悪くなり、嵌合機密性の低い蓋となる。密度が０．
０５ｇ／ｃｃ未満では、成形品としての蓋自体の樹脂量
が少なくなり、強度が弱くなる。密度が０．８ｇ／ｃｃ
を越えると厚みを厚くしても断熱性が悪く、また材質が
硬くなりすぎるので、手切りとか割れが発生しやすくな
る。The thickness of the heat-insulating lid for a container obtained by thermoforming an extruded foamed sheet of the present invention using a styrene resin as a base resin or a sheet obtained by laminating a resin film on the extruded foamed sheet is 0.3 to 3.0 mm. Must have a thickness of 0.3
If it is less than mm, the strength as a lid is weakened, and the heat insulation is also poor. If the thickness exceeds 3.0 mm, the precision with the mold at the time of molding is deteriorated, and a lid with low fitting airtightness is obtained. Density is 0.
If it is less than 05 g / cc, the resin amount of the lid itself as a molded product will be small, and the strength will be weak. 0.8g / cc density
If the thickness exceeds, even if the thickness is increased, the heat insulating property is poor, and the material is too hard, so that hand cutting or cracking is likely to occur.

【００１５】本発明のスチレン系樹脂を基材樹脂とする
押出発泡シート、または前記押出発泡シートに樹脂フィ
ルムを積層したシートを熱成形した容器用断熱蓋の押し
曲げ試験における座屈点荷重は２５〜１００ｇ／ｃｍで
ある必要があり、押し曲げ試験における座屈点荷重が２
５ｇ／ｃｍ未満では、蓋自体が柔らかすぎるため、僅か
の外力で変形したり、容器本体との嵌合が弱くなる。ま
た、座屈点荷重が１００ｇ／ｃｍを越えると、蓋自体が
硬すぎるため、容器本体に蓋を被覆し難くなる。The buckling point load in the push-bending test of the extruded foamed sheet using the styrene-based resin of the present invention as a base resin or the heat-insulated lid for a container obtained by thermoforming a sheet obtained by laminating a resin film on the extruded foamed sheet is 25. １００100 g / cm, and the buckling point load in the push bending test is 2
If it is less than 5 g / cm, the lid itself is too soft, so that the lid is deformed by a slight external force and the fitting with the container body is weak. On the other hand, when the buckling point load exceeds 100 g / cm, the lid itself is too hard, so that it is difficult to cover the container body with the lid.

【００１６】また、押し曲げ試験における撓み量が３０
ｍｍ未満では、自動機ラインあるいは輸送中に蓋が割れ
る恐れがあり、撓み量が８０ｍｍを越えると、蓋付き容
器を段積みした際に蓋の形状変形が大きく、嵌合機密性
の低下を招来するので、本発明の断熱蓋では３０〜８０
ｍｍの撓み量が必要であるが、特に好ましい撓み量とし
ては、４０〜６０ｍｍである。The amount of deflection in the push bending test is 30.
If it is less than 80 mm, the lid may be broken during the automatic machine line or transportation, and if the amount of bending exceeds 80 mm, the shape of the lid will be greatly deformed when stacking containers with lids, leading to a decrease in fitting confidentiality. Therefore, in the heat insulating lid of the present invention, 30 to 80
Although a bending amount of mm is required, a particularly preferable bending amount is 40 to 60 mm.

【００１７】さらに、本発明の断熱蓋として、実食時に
熱湯を注いだ後、蓋を装着したまま湯切りをするような
用途、例えば即席焼きそば容器用の蓋では、特に高温時
の寸法安定性が必要であるので、温度１００℃で１５０
秒間加熱した後の寸法を加熱前の寸法で除した加熱寸法
変化率が、ＭＤ方向、ＴＤ方向ともに０．８〜１．１で
あり、かつ厚み方向には０．９〜１．３であることが好
ましい。ここで、ＭＤ方向とは、発泡シートの押出方向
であり、ＴＤ方向とは発泡シートの押出方向と直角する
方向をいう。このＭＤ方向及びＴＤ方向への加熱寸法変
化率が０．８未満では、熱により収縮変形を起こし、蓋
がよじれたり、外れたりし易くなる。また、前記変化率
が１．１を越えると、熱により膨張変形を起こし、蓋と
しての嵌合機密性が悪くなり、保温効果を損なったり、
湯切り時に湯切り口以外から湯が洩れやすくなる。さら
に、厚み方向の加熱寸法変化率についても、０．９未満
では収縮変形を起こし、１．３を越えると膨張変形を起
こし、いずれの点からも高温時の形状変形や嵌合機密性
の低下を招来する。Further, in the heat-insulating lid of the present invention, in which the hot water is poured at the time of actual eating and then the hot water is drained with the lid attached, for example, the lid for an instant fried noodles container, the dimensional stability especially at high temperatures Is required, so that the temperature is
The heating dimensional change rate obtained by dividing the dimension after heating for two seconds by the dimension before heating is 0.8 to 1.1 in both the MD and TD directions, and 0.9 to 1.3 in the thickness direction. Is preferred. Here, the MD direction is the extrusion direction of the foamed sheet, and the TD direction is a direction perpendicular to the extrusion direction of the foamed sheet. When the heating dimensional change rate in the MD direction and the TD direction is less than 0.8, shrinkage deformation occurs due to heat, and the lid is easily kinked or detached. On the other hand, when the rate of change exceeds 1.1, heat causes expansion and deformation, and the tightness of the fitting as the lid deteriorates, and the heat retention effect is impaired,
Hot water is easily leaked from the opening other than the hot water drain. Further, as for the heating dimensional change rate in the thickness direction, when it is less than 0.9, shrinkage deformation occurs, and when it exceeds 1.3, expansion deformation occurs. Invite.

【００１８】本発明の断熱蓋を構成する押出発泡シート
の基材樹脂中には、４〜４０重量％のゴム分を含有して
いることが好ましい。ゴム分を含有した物は蓋の脆性改
良に効果があるが、含有量が４重量％未満では、効果が
不充分で麺充填ラインでの割れを完全に防止できない。
また、含有量が４０重量％を越えると、樹脂の発泡効率
が低下するとともに、発泡シートの表面が荒れ、表面平
滑性が悪くなる。The base resin of the extruded foam sheet constituting the heat insulating lid of the present invention preferably contains a rubber content of 4 to 40% by weight. A rubber-containing material is effective in improving the brittleness of the lid, but if the content is less than 4% by weight, the effect is insufficient and cracking in the noodle filling line cannot be completely prevented.
On the other hand, when the content exceeds 40% by weight, the foaming efficiency of the resin is reduced, and the surface of the foamed sheet is roughened, and the surface smoothness is deteriorated.

【００１９】本発明のスチレン系樹脂を基材樹脂とする
押出発泡シートに樹脂フィルムを積層するには、前記発
泡シートに樹脂フィルムを共押出により積層する方法
や、後から加熱ロールや接着剤等を使用して積層する方
法等いずれの方法も使用できる。特に、裏面に印刷がほ
どこされたフィルムを積層すると美麗な蓋が成形でき
る。また、ポリスチレン系樹脂を基材樹脂とする押出発
泡シートに積層する樹脂フィルムは、前記押出発泡シー
トの片面に設けても良く、両面に設けても良い。In order to laminate a resin film on an extruded foamed sheet using the styrene-based resin of the present invention as a base resin, a method of laminating a resin film on the foamed sheet by coextrusion, a heating roll, an adhesive, etc. Any method can be used, such as a method of laminating by using a method. In particular, a beautiful lid can be formed by laminating a printed film on the back surface. Further, a resin film to be laminated on an extruded foamed sheet using a polystyrene-based resin as a base resin may be provided on one side of the extruded foamed sheet or on both sides.

【００２０】具体的な非発泡フィルムの積層方法として
は、（１）インライン又はアウトラインで、押出機より
押出された熱可塑性樹脂からなる非発泡フィルムを冷却
しきらないうちに、直接、押出発泡シートに積層する方
法、（２）インライン又はアウトラインで、押出機より
押出された熱可塑性樹脂をバインダーとして、あらかじ
め準備された熱可塑性樹脂の非発泡フィルム（あらかじ
め印刷を施してあるものでも、無地のものでも良い）を
押出発泡シート又は挟圧処理シートに積層する方法、
（３）あらかじめ準備された熱可塑性樹脂の非発泡フィ
ルム（無地又は印刷品）を加熱ロールで加熱しながら、
押出発泡シート又は挟圧処理シートに圧着して積層する
方法、（４）押出発泡シートと非発泡フィルムを合流・
積層させてから、ダイから押出して、積層発泡シートを
得る共押出と呼ばれる方法等が採用できる。Specific methods for laminating a non-foamed film are as follows: (1) In-line or out-line, the extruded foamed sheet made of a thermoplastic resin extruded from an extruder is directly cooled before it can be completely cooled. (2) A non-foamed film of a thermoplastic resin prepared in advance using a thermoplastic resin extruded from an extruder as a binder in-line or out-line (whether pre-printed or uncoated) May be laminated to an extruded foam sheet or a pressure-treated sheet,
(3) While heating a non-foamed film (plain or printed) of a thermoplastic resin prepared in advance with a heating roll,
(4) Combining the extruded foam sheet and the non-foamed film
A method called co-extrusion to obtain a laminated foamed sheet by extruding from a die after lamination can be adopted.

【００２１】本発明の容器用断熱蓋は、蓋としての実用
強度と、割れない柔軟性を兼備した断熱蓋である点が重
要な特徴である。この特徴は、蓋の押し曲げ試験におけ
る座屈点荷重と撓み量にて定量的に表すことができる。
具体的には、Ｏｒｉｅｎｔｉｃ Ｃｏｒｐｏｒａｔｉｏ
ｎ製のテンシロンＵＣＴ−１０Ｔを使用し、図１に示す
ように、容器用断熱蓋１をスパン１００ｍｍにて設置し
た支持具２の上に、蓋表面側を上にして、蓋中心が支持
スパン２，２’の中央になるようにセットした後、支持
具と平行に、蓋の中心線上を横断して線圧縮できる押し
曲げ治具３にて、毎分２００ｍｍの圧縮速度で押し曲
げ、蓋が座屈するまでの荷重と撓み量をチャート紙に記
録し、座屈した時点での、単位長さ当たりの荷重及び撓
み量を読みとることにより数値化できる。上記測定に
て、座屈点荷重が２５〜１００ｇ／ｃｍの範囲にあり、
且つ撓み量が３０〜８０ｍｍの範囲にあるものが本発明
の容器用断熱蓋である。An important feature of the heat-insulating lid for containers of the present invention is that it is a heat-insulating lid having both practical strength as a lid and flexibility not to be broken. This feature can be quantitatively represented by the buckling point load and the amount of deflection in the push bending test of the lid.
Specifically, Orientic Corporation
As shown in FIG. 1, using a Tensilon UCT-10T made of n, a heat insulating lid 1 for a container was placed on a support 2 provided with a span of 100 mm, with the lid surface side up and the center of the lid was a support span. After being set to the center of 2, 2 ', the plate is pressed and bent at a compression speed of 200 mm / min with a pressing / bending jig 3 capable of linearly compressing the center line of the lid in parallel with the support. The load and the amount of bending until the buckling occurs are recorded on a chart paper, and the load and the amount of bending per unit length at the time of buckling can be read to be numerically expressed. In the above measurement, the buckling point load is in the range of 25 to 100 g / cm,
The heat-insulating lid of the present invention has a bending amount in the range of 30 to 80 mm.

【００２２】座屈点荷重と撓み量を上記範囲にコントロ
ールする手段としては、基材樹脂にゴム成分を含有さ
せ、更に含有量を基材樹脂に対して、４〜４０重量部の
範囲とするのが有効である。また、発泡シートの気泡の
大きさもシートの柔軟性に影響するので、平均気泡径は
０．１〜０．２ｍｍの範囲とするのが好ましい。そのた
めには、容器用断熱蓋を構成する押出発泡シートの基材
樹脂に気泡調整剤としてタルク、炭酸カルシウム、シリ
カ等の無機微粉末を１〜５重量部添加すると効果的であ
る。As means for controlling the buckling point load and the amount of deflection within the above ranges, a rubber component is contained in the base resin, and the content is set in the range of 4 to 40 parts by weight based on the base resin. Is effective. Since the size of the cells in the foam sheet also affects the flexibility of the sheet, the average cell diameter is preferably in the range of 0.1 to 0.2 mm. For this purpose, it is effective to add 1 to 5 parts by weight of an inorganic fine powder such as talc, calcium carbonate, silica or the like as a cell regulator to the base resin of the extruded foam sheet constituting the heat insulating lid for the container.

【００２３】さらに、本発明の容器用断熱蓋は、ＭＤ方
向、、ＴＤ方向、および厚み方向の加熱寸方変化率を調
整することにより、高温時の寸法安定性に優れた蓋とす
ることができる。上記変化率は、容器用断熱蓋の平坦な
部分より５０ｍｍ×５０ｍｍ角に切り取った切片を、１
００℃のギアオーブンで１５０秒間加熱した後の切片の
寸法変化を測定したものであり、ＭＤ方向、ＴＤ方向は
切片全体、厚みは切片中央部の寸法変化を測定したもの
である。具体的には、加熱後の寸法を加熱前の寸法で除
した数値であって、ＭＤ方向、ＴＤ方向の加熱寸法変化
率がともに０．８〜１．１であり、厚み方向の変化率が
０．９〜１．３の範囲にあるものが本発明の容器用断熱
蓋である。Further, the heat-insulating lid for a container of the present invention can be made a lid having excellent dimensional stability at high temperatures by adjusting the heating dimensional change rate in the MD direction, the TD direction, and the thickness direction. it can. The rate of change was determined by dividing a section cut out from a flat part of the heat insulating lid for a container into a square of 50 mm × 50 mm by 1 mm.
The dimensional change of the section was measured after heating in a gear oven at 00 ° C. for 150 seconds, and the MD and TD directions measured the entire section and the thickness measured the dimensional change at the center of the section. Specifically, it is a numerical value obtained by dividing the dimension after heating by the dimension before heating, the rate of change in the dimension of heating in the MD and TD directions is both 0.8 to 1.1, and the rate of change in the thickness direction is What is in the range of 0.9 to 1.3 is the heat insulating lid for a container of the present invention.

【００２４】ＭＤ方向、ＴＤ方向、及び厚み方向の加熱
寸法変化率を上記範囲にコントロールする手段として
は、発泡シートの気泡を連続気泡化するのが有効であ
る。発泡シートの連続気泡率が高ければ高い程、加熱時
の寸安定性は向上するが、強度は逆に低下する。従っ
て、好ましい連続気泡率としては３０〜８０％の範囲で
ある。発泡体の気泡構造が独立気泡となるか、連続気泡
となるかは、発泡性樹脂組成物の押し出し樹脂温度に特
に左右される。発泡適性温度領域内で比較的樹脂温度が
高い場合は、押し出された後の気泡形成時に気泡膜が破
れ、連続気泡になりやすい。逆に樹脂温度が低い場合は
樹脂の伸長強度があるため、気泡形成時に気泡破れがな
く、独立気泡になりやすい。従って、樹脂温度は発泡適
性領域内でできるだけ高く保持することが好ましい。As a means for controlling the heating dimensional change rate in the MD, TD, and thickness directions within the above ranges, it is effective to make the cells of the foamed sheet open cells. The higher the open cell ratio of the foamed sheet, the higher the dimensional stability during heating but the lower the strength. Therefore, the preferable open cell ratio is in the range of 30 to 80%. Whether the cell structure of the foam becomes closed cells or open cells depends particularly on the temperature of the extruded resin of the foamable resin composition. If the resin temperature is relatively high within the suitable temperature range for foaming, the foam film is broken at the time of foam formation after the extrusion, and the foam tends to become open cells. Conversely, when the resin temperature is low, the resin has elongation strength, so that the bubbles are not broken at the time of bubble formation, and are likely to become closed cells. Therefore, it is preferable to keep the resin temperature as high as possible in the foaming suitable region.

【００２５】本発明である容器用断熱蓋をポリスチレン
系樹脂を基材樹脂とする押出発泡シート、または前記押
出発泡シートに樹脂フィルムを積層したシートから熱成
形する方法について説明する。熱成形の方法としては、
厚みの薄い成形品を成形するのに好適な接触加熱成形と
称されているものが好適である。即ち、所定温度に加熱
された熱板と雌型を用い、両者間に成形するシートを挟
み、シートを熱板に密着させて加熱後、熱板に多数形成
してある小孔から圧縮空気を送給して、反対側の雌型に
押し付ける。この時、雌型に多数形成してある小孔から
吸引して、雌型内の形状にシートを沿わせて成形する方
法である。A method of thermoforming a heat-insulated lid for a container from an extruded foam sheet using a polystyrene resin as a base resin or a sheet in which a resin film is laminated on the extruded foam sheet will be described. As a method of thermoforming,
What is called contact heating molding suitable for molding a molded article having a small thickness is preferable. That is, using a hot plate heated to a predetermined temperature and a female mold, sandwiching a sheet to be molded between the two, heating the sheet in close contact with the hot plate, and then compressing air from a number of small holes formed in the hot plate. Feed and press against opposite female mold. At this time, a method is used in which the sheet is sucked through a number of small holes formed in the female mold and the sheet is formed along the shape in the female mold.

【００２６】また、他の成形方法としては、発泡シート
の成形で主に用いられ成型方法（厚みの厚い成形品に適
している）がいずれも使用できる。例えば、シートを加
熱ゾーンに通して、両側から加熱して、軟化させ、成形
ゾーンにて、成形する方法が挙げられ、これら方法には
大きく分けて、片面真空成形、両面真空成形、マッチモ
ールド成形などが該当する。As other molding methods, any molding method mainly used for molding a foamed sheet (suitable for a thick molded article) can be used. For example, there is a method in which a sheet is passed through a heating zone, heated from both sides to be softened, and molded in a molding zone. These methods are roughly divided into one-side vacuum forming, two-side vacuum forming, and match mold forming. And so on.

【００２７】[0027]

【発明の実施の形態】本発明の容器用断熱蓋の例を図
２、図３に示す。図２は角形断熱蓋の平面図であり、図
３は図２に示した断熱蓋の底面図である。図２、図３に
おいて、符号４は容器用断熱蓋、符号５は周辺嵌合溝、
符号６，６′は空気用又は湯切り用の切り起し部、７は
周辺嵌合溝５の内側に突出した細突条、８は印刷部分を
示している。上記周辺嵌合溝５や細突条７は、図４に部
分断面図として示すように容器本体１０との嵌合性をよ
くしているものである。DESCRIPTION OF THE PREFERRED EMBODIMENTS FIGS. 2 and 3 show an example of a heat insulating lid for a container according to the present invention. FIG. 2 is a plan view of the rectangular heat insulating lid, and FIG. 3 is a bottom view of the heat insulating lid shown in FIG. 2 and 3, reference numeral 4 denotes a heat insulating lid for a container, reference numeral 5 denotes a peripheral fitting groove,
Reference numerals 6, 6 'denote cut-and-raised portions for air or hot water, 7 denotes a narrow ridge protruding inside the peripheral fitting groove 5, and 8 denotes a printed portion. The peripheral fitting groove 5 and the narrow protrusion 7 improve the fitting property with the container body 10 as shown in a partial sectional view in FIG.

【００２８】また、容器用断熱蓋の形状構造としても上
記角形のほか種々実施できる。例えば、図５および図６
には形状の異なる円形の場合の容器用断熱蓋の平面図と
底面図とを示してあり、切り起し部６，６′や細突条７
を有している点は先の角型断熱蓋の例と同様である。な
お、上記では円形及び角形の容器用断熱蓋を例として挙
げたが、これらに限定されるものではなく、対応する容
器の形状に合わせて適宜変更することができる。The shape and structure of the heat insulating lid for a container can be variously implemented in addition to the above-mentioned square shape. For example, FIGS.
Shows a plan view and a bottom view of the heat insulating lid for a container in the case of circular shapes having different shapes.
Is similar to the above-described example of the square heat-insulating lid. In the above, circular and square heat insulating lids for containers have been described as examples, but the present invention is not limited to these, and can be appropriately changed according to the shape of the corresponding container.

【００２９】また、本発明の方法により製造された容器
用断熱蓋を利用できる容器本体は、その形状、素材等を
特に限定されるものではない。例えば、合成樹脂、金
属、木材等いずれの素材からなる容器であっても、本発
明の容器用断熱蓋を使用することができる。しかしなが
ら、容器用断熱蓋と同種の発泡樹脂からなっていること
が好ましい。また、本発明の容器用断熱蓋は、即席麺
（特に、焼きそば等のいったん湯を捨てる必要があるも
の）の蓋として特に好適に使用することできる。The shape, material and the like of the container main body in which the heat insulating lid for a container manufactured by the method of the present invention can be used are not particularly limited. For example, even if the container is made of any material such as synthetic resin, metal, and wood, the heat insulating lid of the present invention can be used. However, it is preferable that it is made of the same type of foamed resin as the heat insulating lid for the container. Further, the heat insulating lid for a container of the present invention can be particularly suitably used as a lid for instant noodles (especially those for which it is necessary to once dispose of hot water such as fried noodles).

【００３０】[0030]

【実施例】以下、実施例、比較例をもって具体的に本発
明を詳細に説明する。 （実施例１〜７）スチレン系樹脂の混合樹脂を使用し
た。具体的に使用した樹脂名、その配合を表１に示し
た。The present invention will be described below in detail with reference to examples and comparative examples. (Examples 1 to 7) A mixed resin of a styrene resin was used. Table 1 shows the specific names of the resins used and their formulations.

【００３１】[0031]

【表１】 [Table 1]

【００３２】上記の配合のスチレン系樹脂の混合樹脂を
押出機に通して、サーキュラーダイより円筒状の押出発
泡シート状に押出し、ついで円筒状の押出発泡シートを
カッターにて切開しフラットなシートとし、捲き取り機
でロール状に捲き取り、容器用断熱蓋の基材となる発泡
シートを得た。実施例１で得られた発泡シートの厚みは
０．９ｍｍであった。実施例４以外は、得られた発泡シ
ートの片面に各種非発泡樹脂フィルムを積層してから、
一般的な接触加熱成型機にて熱成形し、図２及び図３に
示したような外寸１７５ｍｍ、外周の高さ７ｍｍ、容器
との嵌合溝の幅１０ｍｍ、天板との段差５ｍｍの角形容
器用断熱蓋を試作し性能評価を行った。その結果を表２
に示す。ここで、容器用断熱蓋の厚みは、天板の中央部
の数値である。表２から明らかな通り、本発明の製造方
法により得られる容器用断熱蓋は、割れ、強度、断熱
性、熱湯変形のいずれの観点においても優れていること
が判る。The mixed resin of the styrene resin having the above composition is passed through an extruder, extruded from a circular die into a cylindrical extruded foam sheet, and then the cylindrical extruded foam sheet is cut with a cutter to form a flat sheet. Then, it was wound up in a roll shape by a winder to obtain a foamed sheet to be a base material of a heat insulating lid for a container. The thickness of the foamed sheet obtained in Example 1 was 0.9 mm. Except for Example 4, after laminating various non-foamed resin films on one side of the obtained foamed sheet,
It is thermoformed by a general contact heating molding machine, and has an outer dimension of 175 mm, an outer height of 7 mm, a width of a fitting groove for a container of 10 mm, and a step of 5 mm from a top plate as shown in FIGS. A prototype of a thermal insulation lid for a rectangular container was manufactured and its performance was evaluated. Table 2 shows the results.
Shown in Here, the thickness of the heat insulating lid for a container is a numerical value at the center of the top plate. As is clear from Table 2, it can be seen that the heat insulating lid for a container obtained by the production method of the present invention is excellent in all aspects of cracking, strength, heat insulating properties, and hot water deformation.

【００３３】[0033]

【表２】 [Table 2]

【００３４】（比較例１〜４）表１に示した基材配合処
方で実施例と同様に蓋を成形し、性能評価した。その結
果を表２に示す。比較例１では発泡シート基材樹脂にゴ
ム分を全く含ませなかった。比較例２では発泡シート基
材樹脂中に２．５重量％のゴム分を含ませた。比較例３
では発泡シート基材樹脂中に６０重量％のゴム分を含ま
せた。比較例４は非発泡シートからなる蓋の例である。
表２から明らかな通り、比較例１，２の蓋は割れが発生
し、比較例３の蓋は強度が不十分であり、比較例４の蓋
は断熱性が劣っており、いずれも実用に耐えないことが
判る。(Comparative Examples 1 to 4) Lids were molded in the same manner as in the examples with the base material blending recipe shown in Table 1, and the performance was evaluated. Table 2 shows the results. In Comparative Example 1, no rubber component was contained in the foamed sheet base resin. In Comparative Example 2, a rubber content of 2.5% by weight was contained in the foamed sheet base resin. Comparative Example 3
In this example, 60% by weight of rubber was contained in the foamed sheet base resin. Comparative Example 4 is an example of a lid made of a non-foamed sheet.
As is clear from Table 2, the lids of Comparative Examples 1 and 2 were cracked, the lid of Comparative Example 3 was insufficient in strength, and the lid of Comparative Example 4 was inferior in heat insulation. It turns out that it cannot stand.

【００３５】連続気泡率は東京サイエンス株式会社社製
エアーコンパリソンピクノメーターＤＥＬ１０００を使
用して、ＡＳＴＭＤ２８５６に基づいて測定した。な
お、表２に記載された容器用断熱蓋の性能の評価は、以
下の基準に従って評価したものである。 （１）割れ評価 自動機ラインで容器本体に蓋を装着する際の評価で、以
下の基準に従って評価した。 ・割れの発生が蓋のどの部位にも全くない…◎ ・部分的に若干割れが発生するが、実用に耐える程度で
ある…○ ・ほとんどの蓋に割れが発生し、実用に耐えない…×The open cell ratio was measured based on ASTM D2856 using an air comparison pycnometer DEL1000 manufactured by Tokyo Science Co., Ltd. In addition, the evaluation of the performance of the heat insulating lid for containers described in Table 2 was based on the following criteria. (1) Cracking evaluation This was evaluated when the lid was attached to the container body in an automatic machine line, and evaluated according to the following criteria.・ No cracks are generated at any part of the lid ... ◎ ・ Some cracks are generated partially, but only to the extent that they can be used practically. ○ ・ Most of the lids are cracked and they cannot be used practically. ×

【００３６】（２）強度評価 麺を充填した容器を三段に積んだ際の、最下段の蓋の状
態を以下の基準に従って評価した。 ・変形が見られず、元の形状を維持している…◎ ・蓋の中央部に若干の凹みが見られるが実用に耐える程
度である…○ ・蓋の中央部が大きく凹み嵌合部に隙間ができている…
×(2) Evaluation of Strength The state of the lowermost lid when the noodle-filled containers were stacked in three tiers was evaluated according to the following criteria. -No deformation is observed and the original shape is maintained ... ◎-A slight dent is seen in the center of the lid, but it is practically acceptable ... ○-The central part of the lid is greatly recessed and fits into the fitting part There is a gap ...
×

【００３７】（３）断熱性評価 容器本体に熱湯（９５℃）を入れて、蓋をして、湯切り
時に蓋を手で押さえて以下の基準に従って評価した。 ・熱くない…◎ ・熱いが何とか押さえていることができる…○ ・熱くて押さえることができない…×(3) Evaluation of Heat Insulating Property Hot water (95 ° C.) was put into the container body, the lid was closed, and the lid was pressed by hand when the hot water was drained, and evaluated according to the following criteria.・ It's not hot ... ◎ ・ It's hot but you can manage it ... ○ ・ It's hot and you can't hold it ... ×

【００３８】（４）熱湯変形評価 容器本体に内容物を入れ、熱湯（９５℃）を入れて蓋を
し、５分後に湯切りをした後、以下の基準に従って評価
した。 ・変形が見られない…◎ ・多少変形しているが実用上問題がない…○ ・変形し、内容物がこぼれたり、蓋がはずれる…×(4) Evaluation of Hot Water Deformation The contents were put in a container body, hot water (95 ° C.) was put, a lid was placed, and after 5 minutes, hot water was drained, and evaluated according to the following criteria.・ No deformation is observed… ◎ ・ Deformed slightly, but there is no problem in practical use… ○ ・ Deformed, contents spill out, or lid comes off… ×

【００３９】[0039]

【発明の効果】以上述べたように、本発明の容器用断熱
蓋は、スパン１００ｍｍでの押し曲げ試験における座屈
点荷重が２５〜１００ｇ／ｃｍ，撓み量が３０〜８０ｍ
ｍであるか、適度な柔軟性と強度を兼ね備えており、容
器への蓋装着を自動機ラインで実施しても蓋が割れるこ
とがなく、また内容物を充填した容器を段積みした際に
も、蓋が変形し嵌合性が低下することがない。また、本
発明の容器用断熱蓋は、ＭＤ方向及びＴＤ方向の変化率
が０．８〜１．１であり、厚み方向の変化率が０．８〜
１．３であるので高温時の寸法安定性に優れ、高温で閉
蓋使用時や湯切り時にも断熱蓋全体が膨張することが抑
制され、容器本体と蓋との嵌合部に隙間が空くという問
題を生じない。As described above, the heat insulating lid for a container according to the present invention has a buckling point load of 25 to 100 g / cm and a bending amount of 30 to 80 m in a push bending test at a span of 100 mm.
m, or has both the appropriate flexibility and strength, so that the lid does not break even when the lid is attached to the container with an automatic machine line, and when the containers filled with the contents are stacked Also, the lid is not deformed and the fitting property is not reduced. Further, the heat insulating lid for a container of the present invention has a rate of change in the MD and TD directions of 0.8 to 1.1, and a rate of change in the thickness direction of 0.8 to 1.1.
Since it is 1.3, it has excellent dimensional stability at high temperatures, suppresses expansion of the entire heat-insulating lid even when the lid is used at the high temperature or when the hot water is drained, and a gap is formed in a fitting portion between the container body and the lid. Problem does not occur.

【００４０】特に、ポリスチレン系基材樹脂に、４〜４
０重量％のゴム分を含有させることにより、上記の脆
性、強度、熱安定性を改善することが可能になる。ま
た、発泡シートの表面に非発泡フィルムを積層すると強
度ならびに印刷性を向上させることができ、この場合、
フィルム層にもゴム分を含有させると、更に割れにくい
蓋が得られる。加えて、本発明の容器用断熱蓋は発泡樹
脂製であるため、断熱性が高く、熱湯を入れた容器本体
に対して、被蓋して使用した際、湯切り時に蓋を手で押
さえても熱くなく、把持し易いという特徴を有してい
る。In particular, the polystyrene-based base resin has
By including 0% by weight of the rubber component, the above-mentioned brittleness, strength, and thermal stability can be improved. In addition, when a non-foamed film is laminated on the surface of the foamed sheet, strength and printability can be improved. In this case,
When a rubber component is also contained in the film layer, a lid that is more resistant to cracking can be obtained. In addition, since the heat-insulating lid for a container of the present invention is made of a foamed resin, the heat-insulating property is high, and when used with the container body covered with hot water covered, when the hot-water drainage is performed, the lid is pressed by hand. It is also not hot and easy to grasp.

【図面の簡単な説明】[Brief description of the drawings]

【図１】 本発明の蓋押し曲げ試験方法を示す概略図。FIG. 1 is a schematic view showing a lid pressing bending test method of the present invention.

【図２】 本発明の容器用断熱蓋の一態様である角形断
熱蓋の平面図。FIG. 2 is a plan view of a rectangular heat-insulating lid which is one embodiment of the heat-insulating lid for a container of the present invention.

【図３】 図２の角形断熱蓋の底面図。FIG. 3 is a bottom view of the rectangular heat-insulating lid of FIG. 2;

【図４】 容器本体への閉蓋時の部分断面図である。FIG. 4 is a partial sectional view when the container body is closed.

【図５】 本発明の容器用断熱蓋の一態様である円形断
熱蓋の平面図である。FIG. 5 is a plan view of a circular heat-insulating lid which is an embodiment of the heat-insulating lid for a container of the present invention.

【図６】 図５の円形断熱蓋の底面図である。FIG. 6 is a bottom view of the circular heat-insulating lid of FIG. 5;

【符号の説明】[Explanation of symbols]

１：測定用蓋成型品、２、２’：蓋支持具、３：押し曲
げ治具、４：容器用断熱蓋、５：周辺嵌合溝、６、
６′：空気用および湯切り用の切り起し部、７：細突
条、８：印刷部分、１０：容器本体1: Molded lid for measurement, 2, 2 ': Lid support, 3: Bending jig, 4: Insulated lid for container, 5: Groove fitting around 6,
6 ': cut and raised portion for air and hot water, 7: narrow ridge, 8: printed portion, 10: container body

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 スチレン系樹脂を基材樹脂とする押出発
泡シート、または前記押出発泡シートに樹脂フィルムを
積層したシートを熱成形した厚みが０．３〜３．０ｍ
ｍ、密度が０．０５〜０．８０ｇ／ｃｃの容器用断熱蓋
であって、スパン１００ｍｍでの押し曲げ試験における
座屈点荷重が２５〜１００ｇ／ｃｍ、かつ撓み量が３０
〜８０ｍｍであることを特徴とする容器用断熱蓋。An extruded foamed sheet comprising a styrene-based resin as a base resin, or a sheet obtained by laminating a resin film on the extruded foamed sheet, has a thickness of 0.3 to 3.0 m.
m, a heat-insulating lid for a container having a density of 0.05 to 0.80 g / cc, having a buckling point load of 25 to 100 g / cm and a deflection of 30 in a push bending test at a span of 100 mm.
A heat-insulating lid for a container, which is 80 mm in length. 【請求項２】 容器用断熱蓋を温度１００℃で１５０秒
間加熱した後の寸法を加熱前の寸法で除した加熱寸法変
化率が、ＭＤ方向、ＴＤ方向ともに０．８〜１．１であ
り、かつ厚み方向には０．９〜１．３であることを特徴
とする請求項１に記載の容器用断熱蓋。2. The heating dimensional change rate obtained by dividing the dimension after heating the heat insulating lid for a container at a temperature of 100 ° C. for 150 seconds by the dimension before heating is 0.8 to 1.1 in both the MD and TD directions. 2. The heat insulating lid for a container according to claim 1, wherein the thickness is 0.9 to 1.3. 【請求項３】 押出発泡シートの基材樹脂中に４〜４０
重量％のゴム分を含有していることを特徴とする請求項
１，２に記載の容器用断熱蓋。3. The extruded foamed sheet contains 4 to 40 base resins.
The heat insulating lid for a container according to claim 1 or 2, wherein the heat insulating lid contains a rubber component by weight. 【請求項４】 押出発泡シートに積層する樹脂フィルム
がゴム分を含有するスチレン系樹脂であることを特徴と
する請求項１〜３に記載の容器用断熱蓋。4. The heat insulating lid for a container according to claim 1, wherein the resin film laminated on the extruded foam sheet is a styrene resin containing a rubber component.