JPH10259114A - Oil-in-water type emulsified composition - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain an oil-in-water type emulsified composition, excellent in stability with time, having great humectant effects on prevention of drying of skin or hair and hardly causing a sense of incompatibility with the skin such as stickiness or oiliness. SOLUTION: This composition is obtained by including an oil in a solid or a semisolid state at 25 deg.C such as vaseline, microcrystalline wax, lanolin, cholesterol, phytosterol, a cholesterol derivative, a phytosterol derivative or a lanolin derivative, formulating >=1.0wt.% oily phase having >=25 deg.C softening temperature, water and a surface-active substance therein and regulating the emulsified particle diameter to <0.3μm.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、化粧料や医薬品基
剤として用いられる水中油型乳化組成物に関し、さらに
詳しくは、経時安定性に優れ、肌や毛髪の乾燥を防ぐ保
湿効果が大きく、かつべたつき、油っぽさ等の肌への違
和感の少ない水中油型乳化組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an oil-in-water emulsion composition used as a cosmetic or pharmaceutical base, and more specifically, has excellent stability over time and a large moisturizing effect for preventing drying of skin and hair. The present invention relates to an oil-in-water emulsified composition having less stickiness, oiliness and other uncomfortable feelings to the skin.

【０００２】[0002]

【従来の技術】化粧料においては、皮膚や毛髪からの水
分の揮散防止や外的刺激からの保護の目的から油分が配
合されている。油分を直接皮膚や毛髪に塗布した場合、
均一に塗布することが困難であったり、油のべたつきが
使用感触を損う等の理由から、油を化粧料に配合する際
には乳化技術を用いるのが一般的である。最近の消費者
は、油のべたつきを嫌い、水溶液状のさっぱりとした製
剤を嗜好することから、特に水中油型乳化組成物が広く
用いられている。炭化水素油の中でも分子量の高い油分
は、皮膚に対するオクルージョン効果（皮膚からの水分
の蒸散を皮膚上の油膜により抑制する効果）に優れ、皮
膚を健やかに保つ働きがあるが、油相に必要量配合しよ
うとすると、油相の粘度が上昇したり、あるいは油相が
常温で固化してしまう。このため、水中油型乳化組成物
に調製した場合であっても、皮膚へなじみくい、広げに
くい等、使用感触が損なわれたり、塗布後のべたつきや
油っぽさが問題となる。また、良好な保湿作用を発揮す
るには、皮膚上に均一な油相の被膜を形成する必要があ
るが、油相の増粘、固化は均一な被膜の形成を妨げてし
まう。このような課題を解決するために、使用性の良好
な低粘度油分やシリコーン油を組み合わせて配合する技
術や、揮散性油分で固形、半固形油分等を溶解させて塗
布時の粘度を低下させ、揮散性油分が蒸発した後、油性
被膜を形成する技術が開発されている。2. Description of the Related Art Oils are incorporated in cosmetics for the purpose of preventing evaporation of water from the skin and hair and protecting the skin from external stimuli. If the oil is applied directly to the skin or hair,
It is common to use an emulsification technique when blending oil into cosmetics, because it is difficult to apply it evenly, or the stickiness of oil impairs the feel of use. In recent years, oil-in-water emulsified compositions have been widely used, since recent consumers dislike the stickiness of oil and prefer a fresh solution in the form of an aqueous solution. Among the hydrocarbon oils, oils with high molecular weight have excellent occlusion effect on skin (effect of suppressing evaporation of water from skin by oil film on skin) and work to keep skin healthy, but necessary amount for oil phase Attempting to mix them will increase the viscosity of the oil phase or solidify the oil phase at room temperature. For this reason, even when it is prepared as an oil-in-water emulsion composition, the feel of use is impaired, such as the skin is difficult to spread and spread easily, and stickiness and oiliness after application become problems. Further, in order to exert a good moisturizing effect, it is necessary to form a uniform oil phase film on the skin. However, thickening and solidification of the oil phase hinders formation of a uniform film. In order to solve such problems, the technology of combining low-viscosity oils and silicone oils with good usability, and dissolving solid, semi-solid oils, etc. with volatile oils to lower the viscosity during application A technique for forming an oily film after the volatile oil evaporates has been developed.

【０００３】[0003]

【発明が解決しようとする課題】これらの技術は、使用
感触の点では改善されているものの、固形、半固形油分
を多量に配合することができず、充分な保湿効果が得ら
れにくい。本発明は、このような観点からなされたもの
であり、固形あるいは半固形状油分本来の効果であるオ
クルージョン効果や皮膚を健やかに保つ働きを損なうこ
となく、使用感触やべたつき等の肌への違和感をなくし
た水中油型乳化組成物を提供することを目的とする。Although these techniques are improved in terms of feeling of use, they do not allow a large amount of solid or semi-solid oil to be blended, making it difficult to obtain a sufficient moisturizing effect. The present invention has been made from such a viewpoint, and does not impair the occlusion effect, which is the original effect of solid or semi-solid oil, and the function of keeping the skin healthy, and gives a feeling of discomfort to the skin such as feeling of use and stickiness. It is an object of the present invention to provide an oil-in-water type emulsified composition which is free from the problem.

【０００４】[0004]

【課題を解決するための手段】前記目的を達成するため
に、本発明者等は鋭意検討を進めた結果、特定の性状を
有する油相を用い、かつ乳化粒子径を０．３μｍ未満に
調整することにより、使用時のべたつきや油っぽさがな
く、かつ油滴が均一に皮膚あるいは毛髪表面に付着し、
外相である水の揮散とともに均一な油性被膜を容易に形
成し得ることを見い出し、本発明を完成するに至った。Means for Solving the Problems In order to achieve the above object, the present inventors have conducted intensive studies and as a result, have adjusted the emulsified particle diameter to less than 0.3 μm by using an oil phase having a specific property. By doing so, there is no stickiness or oiliness at the time of use, and oil droplets uniformly adhere to the skin or hair surface,
The inventors have found that a uniform oily film can be easily formed together with the evaporation of water as an external phase, and have completed the present invention.

【０００５】即ち、本発明は、２５℃において固形また
は半固形状の油分を含有し、かつ２５℃以上に軟化温度
を有する油相と、水と、界面活性物質とを少なくとも含
み、乳化粒子径が０．３μｍ未満であることを特徴とす
る水中油型乳化組成物である。[0005] That is, the present invention comprises an oil phase containing a solid or semi-solid oil component at 25 ° C and having a softening temperature of 25 ° C or higher, at least water, and a surface active substance. Is less than 0.3 μm.

【０００６】一般に、水中油型乳化組成物の塗布から、
油性被膜が塗布面に形成されていく過程は、以下のよう
に考えられている。まず、皮膚や毛髪に外相（水相）が
接触し表面を濡らす。次いで、塗布による剪断力や水分
の蒸発に伴い乳化粒子（油滴）の破壊が生じ、徐々に皮
膚や毛髪表面に油分が付着していく。さらに、塗布を続
けることにより油滴は完全に破壊され、皮膚上に塗擦し
ていくことで油性の薄膜が形成される。ここで、乳化粒
子を微細化した場合には、皮膚に付着した油滴を均一に
塗り広げる過程において、乳化粒子数が多いために油滴
が均一に皮膚上に被覆され、大きな油滴をつぶして皮膚
にのばす工程が容易となるという利点がある。このよう
に、油滴を微細化することは、粘性の高い油滴を破壊
し、皮膚や毛髪に広げるという工程を容易にし、より均
一で効率的な油性被膜の形成を可能とするものである。
また、使用時のべたつきや油っぽさも低減される。油膜
を皮膚や毛髪上に効率的に形成することは、より少量の
油分で効果を発揮することを意味し、使用感触、コス
ト、エコロジーの観点からもさらに有利である。In general, from the application of an oil-in-water emulsion composition,
The process in which the oily film is formed on the application surface is considered as follows. First, the external phase (aqueous phase) comes into contact with the skin and hair and wets the surface. Next, the emulsified particles (oil droplets) are destroyed due to the shearing force and the evaporation of water due to the application, and the oil gradually adheres to the skin and the hair surface. Furthermore, the oil droplets are completely destroyed by continuing the application, and an oily thin film is formed by rubbing on the skin. Here, when the emulsified particles are refined, in the process of uniformly spreading the oil droplets adhered to the skin, the oil droplets are uniformly coated on the skin due to the large number of emulsified particles, and the large oil droplets are crushed. This has the advantage of facilitating the process of extending the skin. In this way, making the oil droplets finer breaks the highly viscous oil droplets, facilitates the process of spreading the oil droplets on the skin and hair, and enables the formation of a more uniform and efficient oily film. .
In addition, stickiness and oiliness during use are reduced. Efficient formation of an oil film on the skin or hair means that the effect is exhibited with a smaller amount of oil, and is further advantageous from the viewpoint of feeling in use, cost and ecology.

【０００７】本発明に用いられる常温（２５℃）におい
て固形または半固形状の油分としては、具体的には、ワ
ックス類（例えばマイクロクリスタリンワックス、ビー
スワックス）、固形パラフィン、硬化油、牛脂、モクロ
ウ、ミツロウ、キャンデリラロウ、カルナバロウ、セレ
シン、ワセリン、ラノリン、ラノリン誘導体、コレステ
ロール、コレステロール誘導体、フィトステロール、フ
ィトステロール誘導体等が挙げられる。このうち、皮膚
に対する保湿効果の点で、ワセリンやマイクロクリスタ
リンワックスのように非晶質あるいは微結晶性の油分が
特に好ましい。また、皮膚に対する親和性の点で、ラノ
リン、コレステロール、フィトステロール、コレステロ
ール誘導体、フィトステロール誘導体、ラノリン誘導体
も好ましい。The solid or semi-solid oil at normal temperature (25 ° C.) used in the present invention includes, for example, waxes (eg, microcrystalline wax, beeswax), solid paraffin, hardened oil, beef tallow, mokurou , Beeswax, candelilla wax, carnauba wax, ceresin, petrolatum, lanolin, lanolin derivatives, cholesterol, cholesterol derivatives, phytosterols, phytosterol derivatives and the like. Among these, an amorphous or microcrystalline oil such as petrolatum or microcrystalline wax is particularly preferable from the viewpoint of a moisturizing effect on the skin. In addition, lanolin, cholesterol, phytosterol, cholesterol derivatives, phytosterol derivatives, and lanolin derivatives are also preferable in terms of affinity for skin.

【０００８】また、本発明の水中油型乳化組成物の油相
には、上記固形または半固形油分に加えて、他の液状油
分を配合することもできる。その他の油分として具体的
には、流動パラフィン、スクワラン等の炭化水素、オリ
ーブ油、マカデミアナッツ油、ホホバ油、液状ラノリン
等の動植物抽出油、シリコーン油、パーフルオロ化油、
脂肪酸および高級アルコールを反応させて得られるエス
テル油等が挙げられる。The oil phase of the oil-in-water emulsion composition of the present invention may contain another liquid oil component in addition to the solid or semi-solid oil component. Specific examples of other oil components include liquid paraffin, hydrocarbons such as squalane, olive oil, macadamia nut oil, jojoba oil, animal and plant extracted oils such as liquid lanolin, silicone oil, perfluorinated oil,
An ester oil obtained by reacting a fatty acid and a higher alcohol is exemplified.

【０００９】油相全体の物性としては、軟化温度が２５
℃以上であることが必要であり、好ましくは、３５℃以
上である。軟化温度が２５℃未満では、肌に対する保湿
効果が不十分となる。また軟化温度は５０℃以下である
ことが好ましい。軟化温度が５０℃を超えると皮膚上に
均一に塗布するのが困難となる場合がある。また、油相
全体の粘度は、常温（２５℃）で、１０００ｃｐｓ以上
であることが好ましい。The physical properties of the entire oil phase are as follows:
It is necessary that the temperature be at least 35 ° C, preferably at least 35 ° C. When the softening temperature is lower than 25 ° C., the moisturizing effect on the skin becomes insufficient. The softening temperature is preferably 50 ° C. or lower. If the softening temperature exceeds 50 ° C., it may be difficult to apply the composition uniformly on the skin. The viscosity of the entire oil phase is preferably 1000 cps or more at room temperature (25 ° C.).

【００１０】組成物全体に占める油相の配合量は１．０
重量％以上であり、さらに好ましくは５．０重量％以上
である。この配合量が１．０重量％未満では、充分な保
湿効果が得られない。また、油相の上限は特に限定され
ないが、４０．０重量％までであることが好ましい。４
０重量％を超えると、乳化の際に増粘し、乳化粒子の微
細化が困難になる場合がある。The amount of the oil phase in the whole composition is 1.0
% By weight or more, more preferably 5.0% by weight or more. If the amount is less than 1.0% by weight, a sufficient moisturizing effect cannot be obtained. The upper limit of the oil phase is not particularly limited, but is preferably up to 40.0% by weight. 4
If it exceeds 0% by weight, the viscosity increases during emulsification, and it may be difficult to make the emulsified particles fine.

【００１１】本発明に用いられる界面活性物質として
は、化粧料や医薬外用剤に用いることのできる非イオン
界面活性剤、アニオン界面活性剤、両イオン界面活性
剤、カチオン界面活性剤、両親媒性物質を用いることが
できる。The surfactants used in the present invention include nonionic surfactants, anionic surfactants, zwitterionic surfactants, cationic surfactants, amphiphilic surfactants which can be used in cosmetics and external preparations for medicines. Substances can be used.

【００１２】非イオン界面活性剤としては、例えば、Ｐ
ＯＥソルビタンモノステアレート、ＰＯＥソルビタンモ
ノオレエート等のＰＯＥソルビタン脂肪酸エステル類、
ＰＯＥソルビットモノラウレート、ＰＯＥソルビットモ
ノオレエート等のＰＯＥソルビット脂肪酸エステル類、
ＰＯＥグリセリンモノステアレート、ＰＯＥグリセリン
モノイソステアレート、ＰＯＥグリセリントリイソステ
アレート等のＰＯＥグリセリン脂肪酸エステル類、ＰＯ
Ｅモノオレエート、ＰＯＥジステアレート、ＰＯＥモノ
ジオレエート、システアリン酸エチレングリコール等の
ＰＯＥ脂肪酸エステル類、ＰＯＥオレイルエーテル、Ｐ
ＯＥステアリルエーテル、ＰＯＥベヘニルエーテル、Ｐ
ＯＥ２−オクチルドデシルエーテル、ＰＯＥコレスタノ
ールエーテル等のＰＯＥアルキルエーテル類、ＰＯＥオ
クチルフェニルエーテル等のＰＯＥアルキルフェニルエ
ーテル類、ブルロニック等のプルアロニック型類、ＰＯ
Ｅ・ＰＯＰセチルエーテル、ＰＯＥ・ＰＯＰ２−デシル
テトラデシルエーテル、ＰＯＥ・ＰＯＰ水添ラノリン、
ＰＯＥ・ＰＯＰグリセリンエーテル等のＰＯＥ・ＰＯＰ
アルキルエーテル類、ＰＯＥ硬化ヒマシ油、ＰＯＥ硬化
ヒマシ油モノイソステアレート等のＰＯＥ硬化ヒマシ油
誘導体、ＰＯＥソルビットミツロウ等のＰＯＥミツロウ
・ラノリン誘導体、ヤシ油脂肪酸ジエタノールアミド、
ラウリン酸モノエタノールアミド、脂肪酸イソプロパノ
ールアミド等のアルカノールアミド、ＰＯＥプロピレン
グリコール脂肪酸エステル、ＰＯＥアルキルアミン、Ｐ
ＯＥ脂肪酸アミド、ショ糖脂肪酸エステル等が挙げられ
る。As the nonionic surfactant, for example, P
POE sorbitan fatty acid esters such as OE sorbitan monostearate and POE sorbitan monooleate;
POE sorbit fatty acid esters such as POE sorbit monolaurate and POE sorbit monooleate;
POE glycerin fatty acid esters such as POE glycerin monostearate, POE glycerin monoisostearate, POE glycerin triisostearate, POE
POE fatty acid esters such as E monooleate, POE distearate, POE monodioleate, ethylene glycol cysteate, POE oleyl ether, P
OE stearyl ether, POE behenyl ether, P
POE alkyl ethers such as OE2-octyldodecyl ether and POE cholestanol ether; POE alkyl phenyl ethers such as POE octyl phenyl ether; pluronic type such as bruronic;
E-POP cetyl ether, POE-POP2-decyltetradecyl ether, POE-POP hydrogenated lanolin,
POE / POP POE / POP such as glycerin ether
Alkyl ethers, POE hydrogenated castor oil, POE hydrogenated castor oil derivatives such as POE hydrogenated castor oil monoisostearate, POE beeswax lanolin derivatives such as POE sorbit beeswax, coconut oil fatty acid diethanolamide,
Alkanolamides such as lauric acid monoethanolamide, fatty acid isopropanolamide, POE propylene glycol fatty acid ester, POE alkylamine, P
OE fatty acid amide, sucrose fatty acid ester and the like.

【００１３】アニオン界面活性剤としては、例えば、ス
テアリン酸カリウム、ベヘン酸ナトリウム等の脂肪酸セ
ッケン、ラウリル硫酸ナトリウム、セチル硫酸ナトリウ
ム等の高級アルキル硫酸エステル塩、Ｎ−パルミトイル
イルグルタミン酸モノナトリウム、Ｎ−ステアロイルグ
ルタミン酸ジナトリウム、Ｎ−ミリストイル−Ｌ−グル
タミン酸モノナトリウム等のＮ−アシルグルタミン酸塩
等が挙げられる。Examples of the anionic surfactant include fatty acid soaps such as potassium stearate and sodium behenate, higher alkyl sulfates such as sodium lauryl sulfate and sodium cetyl sulfate, monosodium N-palmitoylylglutamate, and N-stearoyl. Examples include N-acyl glutamates such as disodium glutamate and monosodium N-myristoyl-L-glutamate.

【００１４】両イオン界面活性剤としては、例えば、２
−ウンデシル−Ｎ，Ｎ，Ｎ−（ヒドロキシエチルカルボ
キシメチル）−２−イミダゾリンナトリウム、２−ココ
イル−２−イミタゾリニウムヒドロキサイド−１−カル
ボキシエチロキシ２ナトリウム塩等のイミダゾリン系両
性界面活性剤、２−ヘプタデシル−Ｎ−カルボキシメチ
ル−Ｎ−ヒドロキシエチルイミダゾリニウムベタイン、
ラウリルジメチルアミノ酢酸ベタイン、アルキルベタイ
ン、アミドベタイン、スルホベタイン等のベタイン系界
面活性剤等が挙げられる。As the amphoteric surfactant, for example, 2
-Imidazoline amphoteric surfactants such as -undecyl-N, N, N- (hydroxyethylcarboxymethyl) -2-imidazoline sodium and 2-cocoyl-2-imitazolinium hydroxide-1-carboxyethyloxy disodium salt 2-heptadecyl-N-carboxymethyl-N-hydroxyethylimidazolinium betaine,
Betaine-based surfactants such as betaine lauryldimethylaminoacetate, alkylbetaine, amidobetaine, and sulfobetaine are exemplified.

【００１５】カチオン界面活性剤としては、例えば、塩
化ステアリルトリメチルアンモニウ等のアルキルトリメ
チルアンモニウム塩、塩化ジステアリルジメチルアンモ
ニウムジアルキルジメチルアンモニウム塩、ステアリン
酸ジメチルアミノプロピルアミドＬ−グルタミン酸塩等
が挙げられる。Examples of the cationic surfactant include alkyltrimethylammonium salts such as stearyltrimethylammonium chloride, distearyldimethylammonium dialkyldimethylammonium chloride, and dimethylaminopropylamide L-glutamate stearate.

【００１６】両親媒性物質は、界面活性を有するが、そ
れ自体は疎水性が強く一般の界面活性剤ほど界面活性を
有さないものであり、例えばリン脂質、高級脂肪酸、高
級脂肪族アルコール、モノグリセリド、グリセロールモ
ノアルキルエーテル、モノアルキルアミン、およびステ
ロール骨格を有する化合物（コレステロール、フィトス
テロール）等がある。An amphiphilic substance has surface activity, but is itself highly hydrophobic and has less surface activity than a general surfactant. For example, a phospholipid, a higher fatty acid, a higher aliphatic alcohol, Examples include monoglycerides, glycerol monoalkyl ethers, monoalkylamines, and compounds having a sterol skeleton (cholesterol, phytosterol).

【００１７】界面活性物質の合計量は、油相の合計量の
１／１０以上（重量比）であることが好ましい。界面活
性物質の合計量が１／１０未満では、乳化粒子の微細化
が困難な場合がある。The total amount of the surface active substance is preferably at least 1/10 (weight ratio) of the total amount of the oil phase. If the total amount of the surfactant is less than 1/10, it may be difficult to make the emulsified particles fine.

【００１８】本発明で用いられる水は、４０．０重量％
以上、特に６０．０重量％以上配合するのが好ましい。
水の量が少ないと、みずみずしい感触が損なわれる傾向
があり、使用感触が損なわれることがある。The water used in the present invention is 40.0% by weight.
As described above, it is particularly preferable to add 60.0 wt% or more.
When the amount of water is small, the fresh feel tends to be impaired, and the use feeling may be impaired.

【００１９】本発明の水中油型乳化組成物の乳化粒子径
は、０．３μｍ未満であり、特に好ましくは０．１５μ
ｍ以下である。０．３μｍ以上では、べたつきや、油っ
ぽさが顕著に感じられるようになる。ここで用いられる
エマルションの乳化粒子径は、動的光散乱法により測定
されたものであり、例えば、ＮＩＣＯＭＰ−２７０（Ｈ
ＹＡＣ／ＲＯＹＣＯ社製）により測定したものが挙げら
れる。The oil-in-water emulsion composition of the present invention has an emulsion particle size of less than 0.3 μm, particularly preferably 0.15 μm.
m or less. When the thickness is 0.3 μm or more, stickiness and oiliness become noticeable. The emulsion particle size of the emulsion used here is measured by a dynamic light scattering method. For example, NICOMP-270 (H
YAC / ROYCO).

【００２０】かかる乳化粒子径を有する乳化組成物は、
上記の必須成分を有する混合分散液をホモミキサーより
も強力な剪断力をかけられる乳化機、例えばマントンゴ
ーリン、フレンチプレス、コロイドミル、マイクロフル
イダイザー、超音波乳化機等の強力な剪断力で処理する
ことにより調製することができる。また、マントンゴー
リン、フレンチプレス、マイクロフルイダイザー等の高
圧ホモジナイザーを用いる場合には、１０００ｐｓｉ以
上の圧力下で乳化するのが好ましい。An emulsified composition having such an emulsified particle size is
The mixed dispersion having the above essential components is treated with an emulsifier capable of applying a stronger shearing force than a homomixer, for example, a strong shearing force such as a manton gaulin, a French press, a colloid mill, a microfluidizer, and an ultrasonic emulsifier. Can be prepared. When a high-pressure homogenizer such as Manton-Gaulin, French Press, or Microfluidizer is used, it is preferable to emulsify under a pressure of 1000 psi or more.

【００２１】本発明に係る乳化処理は、系全量を行って
もよいし、場合によっては一部を処理し、その後に水あ
るいは多価アルコール等の他の配合物により希釈しても
よい。また、乳化時の温度は、系中の油相が常温で固形
あるいは半固形の場合は油相が融解する温度以上で行う
ことが望ましい。In the emulsification treatment according to the present invention, the whole system may be used, or a part of the system may be treated in some cases, and thereafter, the mixture may be diluted with water or another compound such as a polyhydric alcohol. When the oil phase in the system is solid or semi-solid at room temperature, the emulsification is preferably carried out at a temperature higher than the temperature at which the oil phase melts.

【００２２】本発明の乳化組成物については、前記必須
成分の他に、化粧料や医薬品等の皮膚外用剤に一般的に
用いられる成分を、本発明の所望の効果を損なわない範
囲で配合することができる。かかる配合成分としては、
例えば、エチレングリコール、プロピレングリコール、
１，３−ブチレングリコール、ジプロピレングリコー
ル、グリセリン、ジグリセリン、エリスリトール、ソル
ビトール、ムコ多糖、ヒアルロン酸、コンドロイチン硫
酸、キトサン、グルコース、マルトース、マルチトー
ル、蔗糖、フルクトース、キシリトール、イノシトー
ル、ペンタエリスリトール、マルトトリオース等の保湿
剤、エタノール等の低級アルコール、安息香酸、サリチ
ル酸、パラオキシ安息香酸アルキルエステル、フェノキ
シエタノール、ソルビン酸、ヘキサクロロフェン等の抗
菌剤、パラアミノ安息香酸、オクチルメトキシシンナメ
ート、２，４−ジヒドロキシベンゾフェノン等の紫外線
吸収剤、グリシン、アラニン、バリン、ロイシン、トレ
オニン、フェニルアラニン、チロシン、アスパラギン
酸、アスパラギン、グルタミン酸、グルタミン、タウリ
ン、アルギニン、ヒスチジン等のアミノ酸及びこれらの
アルカリ金属塩と塩酸塩、アシルサルコシン酸、グルタ
チオン、クエン酸、リンゴ酸、酒石酸、乳酸等の有機
酸、ビタミンＡ及びその誘導体、ビタミンＢ6塩酸塩、
ビタミンＢ6トリパルミテート、ビタミンＢ6ジオクタノ
エート、ビタミンＢ2及びその誘導体、ビタミンＢ12、
ビタミンＢ15及びその誘導体等のビタミンＢ類、アスコ
ルビン酸、アスコルビン酸硫酸エステル（塩）、アスコ
ルビン酸リン酸エステル、アスコルビン酸ジパルミテー
ト等のビタミンＣ類、α−トコフェロール、β−トコフ
ェロール、γ−トコフェロール、ビタミンＥアセテート
等のビタミンＥ類、ビタミンＤ類、ビタミンＨ、パント
テン酸、パンテチン、ビオチン等のビタミン類、ニコチ
ン酸アミド、ニコチン酸ベンジル、γ−オリザノール、
アラントイン、グリチルリチン酸（塩）、グリチルレチ
ン酸及びその誘導体、ヒノキチオール、ビサボロール、
ユーカリプトール、チモール、イノシトール、サイコサ
ポニン、ニンジンサポニン等のサポニン類、パントテニ
ルエチルエーテル、エチニルエストラジオール、トラネ
キサム酸、アルブチン、セファランチン、プラセンタエ
キス等の薬剤、カラギーナン、キサンタンガム、カゼイ
ン、カルボキシメチルセルロース、ポリビニルアルコー
ル、カルボキシビニルポリマー、ポリアクリル酸ナトリ
ウム、ポリエチルアクリレート、ポリアクリルアミド、
ポリビニルピロリドン、Ｎ−ビニルピロリドン−Ｎ，Ｎ
−ジメチルアミノエチルメタクリル酸共重合体ジエチル
硫酸塩等の水溶性または水分散性高分子、さらに色素、
金属封鎖剤、酸化防止剤、香料、被膜剤、増粘剤、粉末
等がそれぞれ挙げられる。In the emulsion composition of the present invention, in addition to the above-mentioned essential components, components generally used in external preparations for skin such as cosmetics and pharmaceuticals are blended within a range not to impair the desired effects of the present invention. be able to. As such compounding components,
For example, ethylene glycol, propylene glycol,
1,3-butylene glycol, dipropylene glycol, glycerin, diglycerin, erythritol, sorbitol, mucopolysaccharide, hyaluronic acid, chondroitin sulfate, chitosan, glucose, maltose, maltitol, sucrose, fructose, xylitol, inositol, pentaerythritol, malt Moisturizers such as triose, lower alcohols such as ethanol, antibacterial agents such as benzoic acid, salicylic acid, alkyl esters of parahydroxybenzoic acid, phenoxyethanol, sorbic acid, hexachlorophene, etc., paraaminobenzoic acid, octyl methoxycinnamate, 2,4-dihydroxy UV absorbers such as benzophenone, glycine, alanine, valine, leucine, threonine, phenylalanine, tyrosine, aspartic acid, asparagine, gluta Acid, glutamine, taurine, arginine, histidine and other amino acids and their alkali metal salts and hydrochlorides, acyl sarcosine, glutathione, citric acid, malic acid, tartaric acid, organic acids such as lactic acid, vitamin A and its derivatives, vitamins B6 hydrochloride,
Vitamin B6 tripalmitate, vitamin B6 dioctanoate, vitamin B2 and its derivatives, vitamin B12,
Vitamin B such as vitamin B15 and derivatives thereof, ascorbic acid, ascorbic acid sulfate (salt), ascorbic acid phosphate, vitamin C such as ascorbic acid dipalmitate, α-tocopherol, β-tocopherol, γ-tocopherol, vitamin Vitamin E such as E-acetate, vitamin D, vitamin H, vitamins such as pantothenic acid, pantethine, biotin, nicotinamide, benzyl nicotinate, γ-oryzanol,
Allantoin, glycyrrhizic acid (salt), glycyrrhetinic acid and its derivatives, hinokitiol, bisabolol,
Saponins such as eucalyptol, thymol, inositol, saikosaponin, carrot saponin, drugs such as pantothenyl ethyl ether, ethinyl estradiol, tranexamic acid, arbutin, cepharanthin, placenta extract, carrageenan, xanthan gum, casein, carboxymethylcellulose, polyvinyl alcohol , Carboxyvinyl polymer, sodium polyacrylate, polyethyl acrylate, polyacrylamide,
Polyvinylpyrrolidone, N-vinylpyrrolidone-N, N
-Water-soluble or water-dispersible polymer such as dimethylaminoethyl methacrylic acid copolymer diethyl sulfate, and further a dye,
Examples thereof include a metal sequestering agent, an antioxidant, a fragrance, a coating agent, a thickener, and a powder.

【００２３】[0023]

【実施例】以下、具体的な実施例を挙げつつ、本発明を
更に詳細に説明する。なお、本発明は以下の実施例に限
定されるものではない。配合量は重量％である。Hereinafter, the present invention will be described in more detail with reference to specific examples. Note that the present invention is not limited to the following embodiments. The compounding amount is% by weight.

【００２４】(1) 乳化粒子径による使用感触、保湿作用
の変化 本発明者らは水中油型乳化組成物における油相の乳化粒
子径と使用感触、保湿作用について検討を行った。すな
わち、次の表１の処方に基づき、種々の乳化粒子径の水
中油型乳化組成物を調製し、乳化粒子径と使用感触の関
係について検討した。油相としては、ワセリン、マイク
ロクリスタリンワックス、流動パラフィンを１：１：１
に混合したものを用いた。この油相の軟化点は約４５℃
であった。(1) Change in feeling of use and moisturizing effect depending on the emulsified particle size The present inventors have studied the emulsified particle size of the oil phase in the oil-in-water emulsion composition, the feeling of use, and the moisturizing effect. That is, oil-in-water emulsified compositions having various emulsified particle diameters were prepared based on the formulation shown in Table 1 below, and the relationship between the emulsified particle diameter and the feel in use was examined. As the oil phase, petrolatum, microcrystalline wax and liquid paraffin were used in a ratio of 1: 1: 1.
Was used. The softening point of this oil phase is about 45 ° C
Met.

【００２５】調製した試料の乳化粒子径をＮＩＣＯＭＰ
−２７０（ＨＹＡＣ／ＲＯＹＣＯ社製）により測定する
と共に、４０℃で１カ月間放置してその安定性を調べ
た。また、調製した試料の塗りやすさ、べたつき、保湿
効果について評価した。それぞれの評価は、専門パネル
１０名により調製した試料を実際に使用し、下記基準に
より評価した。それらの結果を表１に示す。The emulsified particle size of the prepared sample was determined by NICOMP
-270 (manufactured by HYAC / ROYCO), and left at 40 ° C. for one month to examine its stability. The prepared samples were evaluated for ease of application, stickiness, and moisturizing effect. In each evaluation, samples prepared by 10 professional panels were actually used, and evaluated according to the following criteria. Table 1 shows the results.

【００２６】（安定性評価） ○：良好。 ×：クリーミングを起こした。(Evaluation of stability) ：: good. X: Creaming occurred.

【００２７】（官能評価）評価点 塗りやすさ 非常に塗り易い。・・・・４ やや塗り易い。・・・・・３ 塗り難い。・・・・・・・２ 非常に塗り難い。・・・・１ べたつき べたつかない。・・・・・４ ややべたつく。・・・・・３ べたつく。・・・・・・・２ 非常にべたつく。・・・・１ 保湿効果 保湿効果が感じられる。・・・・・・４ 保湿効果がやや感じられる。・・・・３ 保湿効果がほとんど感じられない。・２ 保湿効果が感じられない。・・・・・１(Sensory evaluation) Ease of application at evaluation points Very easy to apply. ... 4 Slightly easy to apply. ... 3 It is difficult to apply. ... 2 Very difficult to apply.・ ・ ・ ・ 1 Sticky Not sticky. ... 4 Slightly sticky.・ ・ ・ ・ ・ 3 Sticky.・ ・ ・ ・ ・ ・ ・ 2 Very sticky.・ ・ ・ ・ 1 Moisturizing effect Moisturizing effect is felt. ... 4 A slight moisturizing effect is felt. .... 3 Moisturizing effect is hardly felt.・ 2 No moisturizing effect is felt. ..... 1

【００２８】評価基準 ◎：評価点平均３．５点以上 ○：評価点平均２．５点以上，３．５点未満 △：評価点平均１．５点以上，２．５点未満 ×：評価点平均１．５点未満 Evaluation criteria ◎: Average of evaluation points 3.5 or more 評 価: Average of evaluation points 2.5 or more and less than 3.5 points Δ: Average of evaluation points 1.5 or more and less than 2.5 points ×: Evaluation Point average less than 1.5 points

【００２９】[0029]

【表１】 ───────────────────────────────── 比較例 実施例 比較例 実施例 ──── ──── ──── ───── １ ２ １ ２ ３ ４ ３ ４ ───────────────────────────────── (1)ベヘニルアルコール 1.5 1.5 1.5 1.5 1.0 1.0 1.0 1.0 (2)ステアリン酸カリウム 2.0 2.0 2.0 2.0 0.5 0.5 0.5 0.5 (3)油相 20.0 20.0 20.0 20.0 3.0 3.0 3.0 3.0 (4)ジプロピレングリコール 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 (5)イオン交換水 残量 残量 残量 残量 残量 残量 残量 残量 ───────────────────────────────── 乳化粒子径（μｍ） 5.0 0.5 0.25 0.13 1.0 0.3 0.15 0.07 ４０℃１カ月後安定性 × × ○ ○ × △ ○ ○ ───────────────────────────────── 塗りやすさ × △ ○ ◎ × △ ○ ◎ べたつき × △ ○ ◎ × △ ○ ◎ 保湿作用 ◎ ◎ ◎ ◎ ○ ◎ ◎ ◎ ─────────────────────────────────[Table 1] ───────────────────────────────── Comparative Example Example Comparative Example Example ──── ─ ─── ──── ───── 1 2 1 2 3 4 3 4 4 ─── (1) Behenyl alcohol 1.5 1.5 1.5 1.5 1.0 1.0 1.0 1.0 (2) Potassium stearate 2.0 2.0 2.0 2.0 0.5 0.5 0.5 0.5 (3) Oil phase 20.0 20.0 20.0 20.0 3.0 3.0 3.0 3.0 (4) Dipropylene glycol 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 (5) Ion exchange water Remaining Remaining Remaining Remaining Remaining Remaining Remaining Remaining Remaining Remaining ──────────────────────径 Emulsion particle size (μm) 5.0 0.5 0.25 0.13 1.0 0.3 0.15 0.07 Stability after 1 month at 40 ° C × × ○ ○ × △ ○ ○ ────────── ─────────────────────── paint Sustainability × △ ○ ◎ × △ ○ ◎ Sticky × △ ○ ◎ × △ ○ ◎ Moisturizing ◎ ◎ ◎ ◎ ○ ◎ ◎ ◎ ────────────────────── ───────────

【００３０】（製法）(1)，(2)，(4)，(5)を８０℃で攪
拌混合する。これに、８０℃で融解した(3)を攪拌しな
がら混合し、８０℃において、ホモミキサーおよび高圧
ホモジナイザー（１０００〜８０００ｐｓｉ）を用い、
乳化した後冷却し、試料を得た。(Preparation method) (1), (2), (4) and (5) are stirred and mixed at 80 ° C. To this, (3) melted at 80 ° C was mixed with stirring, and at 80 ° C, using a homomixer and a high-pressure homogenizer (1000 to 8000 psi),
After emulsification, the mixture was cooled to obtain a sample.

【００３１】前記表１より明らかなように、乳化粒子径
が０．２５μｍまでは安定性は極めて良好であるが、
０．３μｍを境としてべたつきが生じ、かつ塗りにくく
なって油相を均一に皮膚になじませることが困難とな
り、使用感触が著しく損なわれることがわかる。As is clear from Table 1, the stability is extremely good up to an emulsion particle size of 0.25 μm.
It can be seen that stickiness occurs at a boundary of 0.3 μm, and it becomes difficult to apply, and it becomes difficult to uniformly apply the oil phase to the skin, and the feel in use is significantly impaired.

【００３２】(2) 油相の配合量 次に本発明者らは、油の配合量について検討を行った。
すなわち、表２の処方に基づき水中油型乳化組成物を製
造し、それぞれの油相の配合量と乳化粒子径の微細化に
ついて検討を行った。(2) Amount of Oil Phase Next, the present inventors have studied the amount of oil.
That is, an oil-in-water emulsion composition was produced based on the formulation in Table 2, and the blending amount of each oil phase and the miniaturization of the emulsified particle diameter were examined.

【００３３】[0033]

【表２】 ─────────────────────────── 実施例 比較例 ──────── ──── ５ ６ ７ ５ ─────────────────────────── (1)POE(15)オレイルエーテル 1.0 1.5 2.0 2.5 (2)セトステアリルアルコール 1.5 2.25 3.0 3.75 (3)油相 20.0 30.0 40.0 50.0 (4)グリセリン 15.0 15.0 15.0 15.0 (5)イオン交換水 残量 残量 残量 残量 ─────────────────────────── 乳化粒子径（μｍ） 0.18 0.18 0.26 0.52 塗りやすさ ◎ ◎ ○ × べたつき ◎ ◎ ○ × ───────────────────────────[Table 2] ─────────────────────────── Example Comparative Example ──────── ５ 5 6 7 5 ─────────────────────────── (1) POE (15) Oleyl ether 1.0 1.5 2.0 2.5 (2) Cetostearyl alcohol 1.5 2.25 3.0 3.75 (3) Oil phase 20.0 30.0 40.0 50.0 (4) Glycerin 15.0 15.0 15.0 15.0 (5) Deionized water Remaining Remaining Remaining Remaining ──────────────────径 Emulsion particle size (μm) 0.18 0.18 0.26 0.52 Ease of application ◎ ◎ ○ × Sticky ◎ ◎ ○ × ─────────────────── ────────

【００３４】（製法）(1)，(2)，(4)，(5)を８０℃で攪
拌混合する。これに、８０℃で融解した(3)を攪拌しな
がら混合し、８０℃において、高圧ホモジナイザーを用
い１０００〜８０００ｐｓｉの圧力で乳化したのち冷却
し、試料を得た。(Preparation method) (1), (2), (4) and (5) are stirred and mixed at 80 ° C. To this, (3) melted at 80 ° C. was mixed with stirring, emulsified at 80 ° C. using a high-pressure homogenizer at a pressure of 1000 to 8000 psi, and then cooled to obtain a sample.

【００３５】前記表２より明らかなように、油相の配合
量が４０重量％までは目標とする乳化粒子径が得られた
が、４０重量％を超えると乳化粒子の微細化が困難とな
り、べたつきが生じ、使用感触が著しく損なわれる。こ
のように、油の配合量が大きな系では、乳化粒子径を微
細化するにつれて系全体の粘性が増大し、さらなる乳化
粒子の微細化が妨げられる。As is clear from Table 2, the target emulsified particle diameter was obtained up to the blending amount of the oil phase of up to 40% by weight, but if it exceeded 40% by weight, it became difficult to make the emulsified particles finer. Stickiness occurs and the feeling of use is significantly impaired. As described above, in a system having a large amount of oil, as the emulsion particle size is reduced, the viscosity of the entire system increases, and further reduction in the size of the emulsion particles is prevented.

【００３６】さらに、表３の処方に基づいて水中油型乳
化組成物を製造し、油相の配合量と保湿効果に関して検
討を行った。Further, an oil-in-water emulsion composition was produced based on the formulation shown in Table 3, and the amount of the oil phase and the moisturizing effect were examined.

【００３７】[0037]

【表３】 ───────────────────────────── 実施例 比較例 ───────────────── ８ ９ 10 11 ６ ───────────────────────────── (1)POE(60)硬化ヒマシ油 2.0 2.0 2.0 2.0 2.0 (2)油相 20.0 10.0 5.0 1.0 0.7 (3)グリセリン 10.0 10.0 10.0 10.0 10.0 (4)イオン交換水 残量 残量 残量 残量 残量 ───────────────────────────── 乳化粒子径（μｍ） 0.19 0.18 0.10 0.03 0.03 塗りやすさ ○ ○ ◎ ◎ ◎ べたつき ○ ○ ◎ ◎ ◎ 保湿作用 ◎ ◎ ○ △ × ─────────────────────────────[Table 3] ───────────────────────────── Example Comparative example ───────────── ──── 8 9 10 11 6 ───────────────────────────── (1) POE (60) hydrogenated castor oil 2.0 2.0 2.0 2.0 2.0 (2) Oil phase 20.0 10.0 5.0 1.0 0.7 (3) Glycerin 10.0 10.0 10.0 10.0 10.0 (4) Remaining amount of deionized water Remaining remaining amount Remaining amount ────────────径 Emulsion particle size (μm) 0.19 0.18 0.10 0.03 0.03 Ease of application ○ ○ ◎ ◎ ◎ Sticky ○ ○ ◎ ◎ ◎ Moisturizing ◎ ◎ ○ △ × ─ ────────────────────────────

【００３８】（製法）(1)，(3)，(4)を８０℃で攪拌混
合する。これに、８０℃で融解した(2)を攪拌しながら
混合し、８０℃において、高圧ホモジナイザーを用い８
０００ｐｓｉの圧力で乳化したのち冷却し、試料を得
た。(Preparation method) (1), (3) and (4) are stirred and mixed at 80 ° C. To this, (2) melted at 80 ° C. was mixed with stirring, and the mixture was stirred at 80 ° C. using a high-pressure homogenizer.
After emulsification at a pressure of 000 psi, the mixture was cooled to obtain a sample.

【００３９】前記表３より明らかなように、油の配合量
が１重量％未満では目標とする保湿作用が得られないこ
とが分かる。以下に、本発明に係る組成物の具体例を示
す。As is evident from Table 3, if the amount of the oil is less than 1% by weight, the desired moisturizing effect cannot be obtained. Hereinafter, specific examples of the composition according to the present invention will be described.

【００４０】実施例１２ エモリエントローション (1) セチルアルコール １．５ 重量％ (2) ミツロウ ０．５ (3) ワセリン １２．０ (4) スクワラン ５．０ (5) ジメチルポリシロキサン １．０ (6) エタノール ５．０ (7) グリセリン ４．０ (8) １，３−ブチレングリコール ４．０ (9) ＰＯＥ（１０）オレイルエーテル ２．０ (10)モノステアリン酸グリセリル １．０ (11)カルボキシビニルポリマー ０．１ (12)防腐剤 適量 (13)香料 適量 (14)水 残量 （製法）(6)、(7)〜(9)、(12)、(14)を７０℃で攪拌混合す
る。これに、７０℃で融解混合した(1)〜(5)、(10)、(13)
を攪拌しながら混合し、７０℃において、高圧ホモジナ
イザーを用い３０００ｐｓｉの圧力で乳化したのち冷却
し、乳化して得た乳化部に、(11)を一部の(14)に分散さ
せた水相部を混合してエモリエントローションを得た。
乳化粒子径は０．１５μｍであった。実際に皮膚に塗布
すると、塗布時にはみずみずしい感触で塗布しやすく、
その後しっとりとした保湿感が感じられた。Example 12 Emollient lotion (1) Cetyl alcohol 1.5% by weight (2) Beeswax 0.5 (3) Vaseline 12.0 (4) Squalane 5.0 (5) Dimethylpolysiloxane 1.0 (6) ) Ethanol 5.0 (7) glycerin 4.0 (8) 1,3-butylene glycol 4.0 (9) POE (10) oleyl ether 2.0 (10) glyceryl monostearate 1.0 (11) carboxy Vinyl polymer 0.1 (12) Preservative proper amount (13) Flavor proper amount (14) Water remaining amount (Preparation method) (6), (7)-(9), (12) and (14) are stirred and mixed at 70 ° C. I do. (1)-(5), (10), (13)
The mixture was stirred at 70 ° C., emulsified at 3000 psi using a high-pressure homogenizer, cooled, and then emulsified. An aqueous phase in which (11) was dispersed in a part of (14) was obtained by emulsification. The parts were mixed to obtain an emollient lotion.
The emulsion particle size was 0.15 μm. When actually applied to the skin, it is easy to apply with a fresh feeling at the time of application,
After that, a moist feeling was felt.

【００４１】 実施例１３ エモリエントローション (1) ベヘニルアルコール １．５ 重量％ (2) ワセリン ２０．０ (3) ジメチルポリシロキサン １．０ (4) グリセリン ８．０ (5) １，３−ブチレングリコール ４．０ (6) ベヘン酸 １．５ (7) ＫＯＨ ０．１ (8) 防腐剤 適量 (9) 香料 適量 (10)水 残量 （製法）(4)、(5)、(7)、(8)、(10)を８０℃で攪拌混合す
る。これに、８０℃で融解混合した(1)〜(3)、(6)を攪拌
しながら混合し、８０℃において、高圧ホモジナイザー
を用い３０００ｐｓｉの圧力で乳化したのち冷却し、ロ
ーションを得た。乳化粒子径は０．１３μｍであった。
実際に皮膚に塗布すると、塗布時にはみずみずしい感触
で塗布しやすく、その後しっとりとした保湿感が感じら
れた。Example 13 Emollient lotion (1) Behenyl alcohol 1.5% by weight (2) Vaseline 20.0 (3) Dimethyl polysiloxane 1.0 (4) Glycerin 8.0 (5) 1,3-butylene glycol 4 0.0 (6) Behenic acid 1.5 (7) KOH 0.1 (8) Preservative appropriate amount (9) Flavor appropriate amount (10) Water balance (Preparation method) (4), (5), (7), ( 8) and (10) are stirred and mixed at 80 ° C. To this, (1) to (3) and (6) melt-mixed at 80 ° C. were mixed with stirring, emulsified at 80 ° C. using a high-pressure homogenizer at a pressure of 3000 psi, and then cooled to obtain a lotion. The emulsion particle size was 0.13 μm.
When actually applied to the skin, the application was easy to apply with a fresh feel at the time of application, and thereafter a moist feeling was felt.

【００４２】 実施例１４ エモリエントローション (1) ベヘニルアルコール ２．０ 重量％ (2) 水添ラノリン ５．０ (3) ワセリン ５．０ (4) コレステロール ０．１ (5) グリセリン ８．０ (6) １，３−ブチレングリコール ４．０ (7) ショ糖ステアリン酸ジエステル １．５ (8) 防腐剤 適量 (9) 香料 適量 (10)水 残量 （製法）(5)〜(8)、(10)を８０℃で攪拌混合する。これ
に、８０℃で融解混合した(1)〜(4)、(9)を攪拌しながら
混合し、８０℃において、高圧ホモジナイザーを用い８
０００ｐｓｉの圧力で乳化したのち冷却し、ローション
を得た。乳化粒子径は０．０７μｍであった。実際に皮
膚に塗布すると、塗布時にはみずみずしい感触で塗布し
やすく、その後しっとりとした保湿感が感じられた。Example 14 Emollient lotion (1) Behenyl alcohol 2.0% by weight (2) Hydrogenated lanolin 5.0 (3) Vaseline 5.0 (4) Cholesterol 0.1 (5) Glycerin 8.0 (6) 1,3-butylene glycol 4.0 (7) Sucrose stearic acid diester 1.5 (8) Preservatives appropriate amount (9) Flavor appropriate amount (10) Water remaining amount (production method) (5)-(8), (10) ) At 80 ° C. with stirring. (1) to (4) and (9), which were melted and mixed at 80 ° C., were mixed with the resulting mixture at 80 ° C. using a high-pressure homogenizer.
After emulsification at a pressure of 000 psi, the mixture was cooled to obtain a lotion. The emulsion particle size was 0.07 μm. When actually applied to the skin, the application was easy to apply with a fresh feel at the time of application, and thereafter a moist feeling was felt.

【００４３】 実施例１５ エモリエントローション (1) ステアリルアルコール １．５ 重量％ (2) ワセリン ９．０ (3) スクワラン ４．０ (4) マカデミアナッツ油 １．０ (5) エタノール ５．０ (6) グリセリン ５．０ (7) １，３−ブチレングリコール ４．０ (8) Ｎ−ステアロイルグルタミン酸ナトリウム １．０ (9) 防腐剤 適量 (10)香料 適量 (11)水 残量 （製法）(5)〜(9)、(11)を７０℃で攪拌混合する。これ
に、７０℃で融解混合した(1)〜(4)、(10)を攪拌しなが
ら混合し、７０℃において、高圧ホモジナイザーを用い
３０００ｐｓｉの圧力で乳化したのち冷却し、ローショ
ンを得た。乳化粒子径は０．１９μｍであった。実際に
皮膚に塗布すると、塗布時にはみずみずしい感触で塗布
しやすく、その後しっとりとした保湿感が感じられた。Example 15 Emollient lotion (1) Stearyl alcohol 1.5% by weight (2) Vaseline 9.0 (3) Squalane 4.0 (4) Macadamia nut oil 1.0 (5) Ethanol 5.0 (6) Glycerin 5.0 (7) 1,3-butylene glycol 4.0 (8) Sodium N-stearoylglutamate 1.0 (9) Preservatives appropriate amount (10) Fragrance appropriate amount (11) Water balance (production method) (5) (9) and (11) are stirred and mixed at 70 ° C. To this, (1) to (4) and (10) melt-mixed at 70 ° C. were mixed with stirring, emulsified at 70 ° C. at a pressure of 3000 psi using a high-pressure homogenizer, and then cooled to obtain a lotion. The emulsion particle size was 0.19 μm. When actually applied to the skin, the application was easy to apply with a fresh feel at the time of application, and thereafter a moist feeling was felt.

【００４４】 実施例１６ ヘアトリートメント (1) ステアリルアルコール １．０ 重量％ (2) ステアリン酸 １．０ (3) ミツロウ ２．０ (4) マイクロクリスタリンワックス ３．０ (5) ワセリン ５．０ (6) 流動パラフィン ５．０ (7) グリセリン ４．０ (8) １，３−ブチレングリコール ４．０ (9) 塩化ステアリルトリメチルアンモニウム １．０ (10)キサンタンガム ０．１ (11)防腐剤 適量 (12)香料 適量 (13)水 残量 （製法）(7)〜(11)、(13)を７０℃で攪拌混合する。これ
に、７０℃で融解混合した(1)〜(6)、(12)を攪拌しなが
ら混合し、７０℃において、高圧ホモジナイザーを用い
３０００ｐｓｉの圧力で乳化したのち冷却し、ヘアトリ
ートメントを得た。乳化粒子径は０．１９μｍであっ
た。実際に毛髪に塗布すると、塗布時にはみずみずしい
感触で塗布しやすく、その後しっとりとした保湿感が長
時間維持された。Example 16 Hair Treatment (1) Stearyl alcohol 1.0% by weight (2) Stearic acid 1.0 (3) Beeswax 2.0 (4) Microcrystalline wax 3.0 (5) Vaseline 5.0 ( 6) Liquid paraffin 5.0 (7) Glycerin 4.0 (8) 1,3-butylene glycol 4.0 (9) Stearyltrimethylammonium chloride 1.0 (10) Xanthan gum 0.1 (11) Preservative 12) Appropriate amount of fragrance (13) Remaining amount of water (Preparation method) Stir and mix (7) to (11) and (13) at 70 ° C. (1) to (6) and (12), which were melt-mixed at 70 ° C., were mixed with stirring, emulsified at 3000 ° C. using a high-pressure homogenizer at 70 ° C., and then cooled to obtain a hair treatment. . The emulsion particle size was 0.19 μm. When actually applied to the hair, it was easy to apply with a fresh feel at the time of application, and then a moisturizing feeling was maintained for a long time.

【００４５】実施例１７ エモリエントローション (1) ベヘニルアルコール １．５ 重量％ (2) ワセリン １５．０ (3) フィトステロール ４．５ (4) コレステロール誘導体 ０．５ (5) ジメチルポリシロキサン １．０ (6) グリセリン ８．０ (7) １，３−ブチレングリコール ４．０ (8) ベヘン酸 １．５ (9) ＫＯＨ ０．５ (10)防腐剤 適量 (11)香料 適量 (12)水 残量 （製法）(6)、(7)、(9)、(10)、(12)を８０℃で攪拌混合す
る。これに、８０℃で融解混合した(1)〜(5)、(8)を攪拌
しながら混合し、８０℃において、高圧ホモジナイザー
を用い３０００ｐｓｉの圧力で乳化したのち冷却し、ロ
ーションを得た。乳化粒子径は０．１０μｍであった。
実際に皮膚に塗布すると、塗布時にはみずみずしい感触
で塗布しやすく、その後しっとりとした保湿感が感じら
れた。Example 17 Emollient lotion (1) 1.5% by weight of behenyl alcohol (2) Vaseline 15.0 (3) Phytosterol 4.5 (4) Cholesterol derivative 0.5 (5) Dimethyl polysiloxane 1.0 (6) ) Glycerin 8.0 (7) 1,3-butylene glycol 4.0 (8) Behenic acid 1.5 (9) KOH 0.5 (10) Preservative appropriate amount (11) Perfume appropriate amount (12) Water remaining amount ( Production method) (6), (7), (9), (10), and (12) are stirred and mixed at 80 ° C. To this, (1) to (5) and (8) melt-mixed at 80 ° C. were mixed with stirring, emulsified at 80 ° C. using a high-pressure homogenizer at a pressure of 3000 psi, and then cooled to obtain a lotion. The emulsion particle size was 0.10 μm.
When actually applied to the skin, the application was easy to apply with a fresh feel at the time of application, and thereafter a moist feeling was felt.

【００４６】[0046]

【発明の効果】以上説明したように、本発明の水中油型
乳化組成物は、固形、半固形油分の配合により生じるべ
たつきや肌への違和感がなく、固形、半固形油分配合に
よる皮膚や毛髪の水分を保持する保湿効果を充分に発揮
できるものである。As described above, the oil-in-water emulsified composition of the present invention has no stickiness or a sense of incongruity to the skin caused by the blending of solid or semi-solid oil, and the skin or hair blended with the solid or semi-solid oil. Can sufficiently exhibit a moisturizing effect of retaining moisture.

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 ２５℃において固形または半固形状の油
分を含有し、かつ２５℃以上に軟化温度を有する油相を
１．０重量％以上と、水と、界面活性物質とを含み、乳
化粒子径が０．３μｍ未満であることを特徴とする水中
油型乳化組成物。1. An emulsifying agent containing at least 1.0% by weight of an oil phase containing a solid or semi-solid oil component at 25 ° C. and having a softening temperature of at least 25 ° C., water, and a surfactant, An oil-in-water emulsion composition having a particle diameter of less than 0.3 μm. 【請求項２】 油相の軟化温度が２５℃以上，５０℃以
下である請求項１記載の水中油型乳化組成物。2. The oil-in-water emulsion composition according to claim 1, wherein the oil phase has a softening temperature of 25 ° C. or more and 50 ° C. or less. 【請求項３】 界面活性物質の合計量が油相の合計量の
１／１０以上（重量比）配合されている請求項１または
２記載の水中油型乳化組成物。3. The oil-in-water emulsion composition according to claim 1, wherein the total amount of the surfactant is 1/10 or more (weight ratio) of the total amount of the oil phase. 【請求項４】 ２５℃において固形または半固形状の油
分がワセリン、マイクロクリスタリンワックス、ラノリ
ン、コレステロール、フィトステロール、コレステロー
ル誘導体、フィトステロール誘導体またはラノリン誘導
体である請求項１〜３のいずれかに記載の水中油型乳化
組成物。4. The water according to claim 1, wherein the solid or semi-solid oil at 25 ° C. is petrolatum, microcrystalline wax, lanolin, cholesterol, phytosterol, a cholesterol derivative, a phytosterol derivative or a lanolin derivative. Oil type emulsified composition.