JPH1024547A - Manufacture of planographic printing plate - Google Patents
Manufacture of planographic printing plateInfo
- Publication number
- JPH1024547A JPH1024547A JP18042596A JP18042596A JPH1024547A JP H1024547 A JPH1024547 A JP H1024547A JP 18042596 A JP18042596 A JP 18042596A JP 18042596 A JP18042596 A JP 18042596A JP H1024547 A JPH1024547 A JP H1024547A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- lithographic printing
- printing plate
- hydrophilic layer
- hydrophilic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、高い解像性を有す
る画像を得ることが可能で、かつ明室下での取り扱い及
び処理液を必要とせず、また特に製造コストが安価であ
る、平版印刷に用いられる印刷版の製版方法に関する。FIELD OF THE INVENTION The present invention relates to a lithographic plate capable of obtaining an image having high resolution, requiring no handling and processing solution in a bright room, and particularly having a low production cost. The present invention relates to a method of making a printing plate used for printing.
【０００２】[0002]
【従来の技術】平版印刷版は、油脂性のインキを受理す
る親油性の画像部分と、インキを受理しない撥油性の非
画像部分からなり、一般に非画像部分は水を受け付ける
親水性部分から構成されている。通常の平版印刷では、
水とインキの両方を版面に供給し、画像部はインキを、
非画像部は水を選択的に受け入れ、画像部上のインキを
例えば紙等の被印刷体に転写させることによって印刷が
なされる。2. Description of the Related Art A lithographic printing plate comprises an oleophilic image portion which receives oil-based ink and an oil-repellent non-image portion which does not receive ink. Generally, the non-image portion comprises a hydrophilic portion which receives water. Have been. In normal lithographic printing,
Both water and ink are supplied to the plate, and the image area
The non-image area selectively receives water, and printing is performed by transferring the ink on the image area to a printing medium such as paper.
【０００３】現在、平版印刷版は表面を親水化処理した
アルミニウム板、亜鉛板、紙等の基材上に親油性のイン
ク受理層を設けることにより製造される。これらの中で
は、ＰＳ版と呼ばれる表面を親水性処理した金属製支持
体上にジアゾ化合物やフォトポリマー等の感光材料を用
いたものや、紙やプラスチック支持体上にハロゲン化銀
を感光材料として銀錯塩拡散転写法（ＤＴＲ法）を利用
し画像形成するものなどが一般的である。At present, a lithographic printing plate is manufactured by providing a lipophilic ink-receiving layer on a base material such as an aluminum plate, a zinc plate, or paper having a hydrophilized surface. Among these, a photosensitive material such as a diazo compound or a photopolymer is used on a metal support having a hydrophilic surface on a PS plate, or silver halide is used as a photosensitive material on paper or a plastic support. An image forming apparatus using a silver complex salt diffusion transfer method (DTR method) is generally used.
【０００４】ジアゾ化合物やフォトポリマーによってイ
ンク受理層（以降画像層という）を形成する方法は、ま
ず金属板、紙、積層板、絶縁性基板等の基材上にジアゾ
化合物やフォトポリマー等の感光材料を塗布する。次い
で、光を照射して感光材料に化学変化を生じさせて、現
像液に対する溶解性を変化させる。感光材料は化学変化
の種類によって二つに分類される。光が照射された部分
が重合・硬化して、現像液に対して不溶性になるネガ型
と、逆に光が照射された部分の官能基が変化して、現像
液に対する溶解性を有するようになるポジ型である。何
れの場合にも、現像液による処理後に基材上に残存す
る、現像液に不溶の感光材料が画像層となる。A method of forming an ink receiving layer (hereinafter referred to as an image layer) by using a diazo compound or a photopolymer is as follows. First, a photosensitive material such as a diazo compound or a photopolymer is formed on a substrate such as a metal plate, paper, a laminate, or an insulating substrate. Apply material. Next, the photosensitive material is irradiated with light to cause a chemical change to change the solubility in a developing solution. Photosensitive materials are classified into two types according to the type of chemical change. The light-irradiated part polymerizes and cures, so that the negative type becomes insoluble in the developer, and conversely, the functional group of the light-irradiated part changes to have solubility in the developer. It is a positive type. In either case, the photosensitive material remaining on the base material after processing with the developer and insoluble in the developer becomes an image layer.
【０００５】一方、ＤＴＲ法を用いた平版印刷版、特に
ハロゲン化銀乳剤層の上に物理現像核層を有する平版印
刷版は、例えば、米国特許第３，７２８，１１４号、同
第４，１３４，７６９号、同第４，１６０，６７０号、
同第４，３３６，３２１号、同第４，５０１，８１１
号、同第４，５１０，２２８号、同第４，６２１，０４
１号明細書等に記載されており、露光されたハロゲン化
銀結晶は、ＤＴＲ現像により化学現像を生起し黒色の銀
となり親水性の非画像部を形成し、一方、未露光のハロ
ゲン化銀結晶は現像液中の錯化剤により銀塩錯体になっ
て表面の物理現像核層まで拡散し、核の存在により物理
現像を生起してインキ受容性の物理現像銀を主体とする
画像部を形成する。On the other hand, a lithographic printing plate using the DTR method, particularly a lithographic printing plate having a physical development nucleus layer on a silver halide emulsion layer, is disclosed, for example, in US Pat. No. 134,769, No. 4,160,670,
Nos. 4,336,321 and 4,501,811
No. 4,510,228 and 4,621,04
No. 1, etc., the exposed silver halide crystal undergoes chemical development by DTR development to become black silver, forming a hydrophilic non-image portion. The crystals are converted into a silver salt complex by the complexing agent in the developing solution and diffuse to the physical development nucleus layer on the surface, and physical development is caused by the presence of the nucleus to form an image portion mainly composed of ink-receptive physical development silver. Form.
【０００６】上記のような感光材料を用いて画像層を形
成する場合に、露光方法が解像性を決定する重要な因子
の一つとなっている。従来は、露光用フィルムを作製
し、次いで紫外光または白色光を使用した密着露光方法
を行うのが主流であった。しかし、コンピュータの進歩
に伴って、コンピュータ情報からのディジタル信号を露
光装置へと送信（コンピュータ・ツゥ・プレート）し、
レーザを用いて直接感光材料を露光するレーザ直接描画
方法が行われるようになっている。レーザ直接描画方法
は、コストが安い、速度が速い、多品種少ロット品での
生産性が高い等の利点がある。When an image layer is formed using the above-described photosensitive material, the exposure method is one of the important factors that determines the resolution. Conventionally, the mainstream has been to prepare an exposure film and then perform a contact exposure method using ultraviolet light or white light. However, with the progress of computers, digital signals from computer information were transmitted to the exposure equipment (computer-to-plate),
A laser direct writing method of directly exposing a photosensitive material using a laser has been performed. The laser direct writing method has advantages such as low cost, high speed, and high productivity in a wide variety of small lot products.
【０００７】このレーザ直接描画方法に対応するために
は、感光材料の光学感度を高くしなければならない。ジ
アゾ化合物やフォトポリマーでは、光化学反応を伴うた
めに、光学感度は低く、数〜数百ｍＪ／ｃｍ2である。
そのため、レーザ出力装置が高出力でなければならず、
装置が大きくなったり、コストが高くなるなどの問題が
あった。In order to cope with this laser direct writing method, the optical sensitivity of the photosensitive material must be increased. Since diazo compounds and photopolymers involve a photochemical reaction, the optical sensitivity is low, and is several to several hundred mJ / cm 2 .
Therefore, the laser output device must be high output,
There have been problems such as an increase in the size of the device and an increase in cost.
【０００８】また、ハロゲン化銀を用いたＤＴＲ法によ
り画像形成するものでは、感度は数μＪ／ｃｍ2であり
簡便な半導体レーザなどでも十分露光可能であるが、逆
に、露光工程を行う前までの保存、基材への塗布工程等
を、暗中もしくはセーフティライト下で行わなければな
らないという、製造及び製版作業の効率を著しく悪くす
る欠点があった。また、ジアゾ化合物やフォトポリマー
においても、室内光や太陽光下でも反応が進行するし、
高温下でも反応性に変化が生じる。さらに、酸素が存在
すると、反応の阻害剤となる。したがって、露光及び現
像前までは同様に暗室処置や低酸素状態化での保存が必
要となっていた。In the case of forming an image by a DTR method using silver halide, the sensitivity is several μJ / cm 2 and a simple semiconductor laser or the like allows sufficient exposure. Storage and application steps to the substrate must be performed in the dark or under a safety light, which has the disadvantage of significantly reducing the efficiency of the production and plate making operations. In addition, in diazo compounds and photopolymers, the reaction proceeds even under room light or sunlight,
The reactivity changes even at high temperatures. In addition, the presence of oxygen becomes an inhibitor of the reaction. Therefore, before exposure and development, darkroom treatment and storage in a low oxygen state were similarly required.
【０００９】さらに、上述の画像形成方法では、現像液
を用いる等の液体処理を行うことが一般的であり、廃液
の処理が環境問題となっているという欠点があった。Further, in the above-described image forming method, liquid processing such as using a developing solution is generally performed, and there is a disadvantage that processing of waste liquid is an environmental problem.
【００１０】[0010]
【発明が解決しようとする課題】本発明の課題は、平版
印刷版の製版技術において、高解像性を有する画像を得
ることができ、かつレーザによる直接描画方法に対応
し、また特に明室下でも画像を得ることができ、廃液が
発生することがないという作業性に極めて優れた平版印
刷版の製版方法を提供することにある。SUMMARY OF THE INVENTION It is an object of the present invention to provide a plate-making technology for a lithographic printing plate, which can obtain an image having a high resolution and corresponds to a direct drawing method using a laser. An object of the present invention is to provide a method of making a lithographic printing plate which is extremely excellent in workability in which an image can be obtained even underneath and no waste liquid is generated.
【００１１】[0011]
【課題を解決するための手段】本発明者らは、上記課題
を解決するために鋭意検討した結果、以下の発明を見い
出した。Means for Solving the Problems The present inventors have made intensive studies to solve the above-mentioned problems, and as a result, have found the following invention.
【００１２】本発明の平版印刷版の製版方法は、疎水性
表面を有する支持体上に、少なくとも最表層として親水
性層を設けてなる平版印刷原版において、画像とする部
分の親水性層をレーザによって加熱することにより、前
記平版印刷原版支持体の疎水性表面を露出させるもので
ある。このため、この加熱の有無により平版印刷原版上
に疎水性部分と親水性部分と言う差異が生じることとな
る。即ち、本発明の平版印刷版の製版方法により製版
し、平版印刷機に装着して印刷を開始すると、加熱され
最表層の親水性層がなく疎水性層または支持体表面が露
出している部分はインキを受理し画像部となり、加熱さ
れていない部分では最表層である親水性層がそのまま残
存することでインキ非受理（水受理）の非画像部とな
り、平版印刷が可能となる。In the method of making a lithographic printing plate according to the present invention, in a lithographic printing original plate comprising a support having a hydrophobic surface and at least a hydrophilic layer as an outermost layer, a portion of an image forming hydrophilic layer is formed by a laser. The lithographic printing plate precursor is exposed to heat to expose the hydrophobic surface of the lithographic printing original plate support. For this reason, a difference between a hydrophobic portion and a hydrophilic portion occurs on the lithographic printing original plate depending on the presence or absence of the heating. That is, when a plate is made by the method of making a lithographic printing plate of the present invention, and the printing is started by mounting the plate on a lithographic printing machine, a portion where the surface of the substrate is heated and the hydrophobic layer or the surface of the support is exposed without the outermost hydrophilic layer. Receives an ink and becomes an image area, and in a part that is not heated, the hydrophilic layer, which is the outermost layer, remains as it is, so that it becomes a non-image area of ink non-reception (water reception), and lithographic printing becomes possible.
【００１３】また、本発明の内、第２の発明である平版
印刷版の製版方法では、平版印刷原版の少なくとも一つ
の層に光吸収剤を含有させることであり、これによりレ
ーザによる熱、光等のエネルギーを効率よく吸収し、有
効に支持体の疎水性表面を露出させることができるの
で、より低出力のレーザを用いることが可能となる。こ
のため、装置コストの低減や作業効率の向上が図れる。
また光吸収剤は複数の層に含有させることもできる。In the plate making method of a lithographic printing plate according to a second aspect of the present invention, a light absorbing agent is contained in at least one layer of the lithographic printing plate precursor. Energy can be efficiently absorbed and the hydrophobic surface of the support can be effectively exposed, so that a lower output laser can be used. For this reason, reduction of apparatus cost and improvement of work efficiency can be achieved.
Further, the light absorbing agent can be contained in a plurality of layers.
【００１４】光吸収剤は、その吸光波長が用いるレーザ
の発光波長と略一致する染料あるいは顔料であれば良
い。例えばカーボンブラックのように広い波長帯で光吸
収可能な黒色のものを用いることが好ましい。The light absorbing agent may be a dye or pigment whose absorption wavelength substantially coincides with the emission wavelength of the laser used. For example, it is preferable to use a black material capable of absorbing light in a wide wavelength band such as carbon black.
【００１５】また、本発明の内、第３の発明の平版印刷
版の製版方法では、平版印刷原版の支持体に光吸収剤を
含有させることにより、さらににレーザのエネルギー吸
収効率を向上させることができる。さらに親水性層へ光
吸収剤を添加することによる親水性や支持体への接着性
への悪影響がある場合には、親水性層への光吸収剤の添
加を除いて、あるいは添加量を少なくして印刷版として
の能力を向上させることが出来る。In the plate making method of a lithographic printing plate according to a third aspect of the present invention, the light absorbing agent is added to the support of the lithographic printing plate precursor to further improve the energy absorption efficiency of the laser. Can be. If the addition of the light absorbing agent to the hydrophilic layer has a negative effect on the hydrophilicity and the adhesion to the support, the addition of the light absorbing agent to the hydrophilic layer is reduced or the amount of addition is reduced. Thus, the ability as a printing plate can be improved.
【００１６】さらに、本発明の内、第４の発明の平版印
刷版の製版方法では、平版印刷原版の親水性層に下記の
一般式１に示されるアクリルアミド系ポリマーを親水性
層に含有させることにより、さらに平版印刷中の水受理
性（親水性能）が印刷中長期に渡って保持されてインキ
を反撥し、非画像部の汚れ（地汚れ）のない良好な印刷
が行うことができる。また本発明に用いられる一般式１
のポリマーの含有量は、３００ｍｇ／ｍ2以下が好まし
く、より好ましくは２〜１５０ｍｇ／ｍ2の範囲であ
る。Further, in the plate making method of a lithographic printing plate according to a fourth aspect of the present invention, the hydrophilic layer of the lithographic printing plate precursor contains an acrylamide polymer represented by the following general formula 1 in the hydrophilic layer. Thereby, the water receptivity (hydrophilic performance) during lithographic printing is maintained for a long period of time during printing, repelling the ink, and good printing without stains (ground stains) in non-image areas can be performed. The general formula 1 used in the present invention
The content of the polymer is preferably 300 mg / m 2 or less, more preferably in the range of 2 to 150 mg / m 2 .
【００１７】[0017]
【化２】 Embedded image
【００１８】式中のＲ１は水素原子またはアルキル基を
表し、Ｒ２は水素原子またはアルカリ金属原子を表し、
ｎは１〜１００モル％、ｍは０〜５０モル％、ｌは０〜
５モル％である。そして平均分子量は２０００〜３０万
である。In the formula, R1 represents a hydrogen atom or an alkyl group, R2 represents a hydrogen atom or an alkali metal atom,
n is 1 to 100 mol%, m is 0 to 50 mol%, l is 0 to 100 mol%
5 mol%. And an average molecular weight is 2000-300,000.
【００１９】本発明によれば、所望する画像に従ってレ
ーザにより加熱することで、液体の現像剤やその処理を
行う装置類を用いることなく、簡便に平版印刷版を製版
することが可能となる。さらには、平版印刷用原版の製
造工程から製版工程、及び印刷工程に至るまで明室下で
の作業が可能であると共に、明室や酸素下での長期安定
保存が可能である。According to the present invention, by heating with a laser according to a desired image, a lithographic printing plate can be easily made without using a liquid developer or equipment for processing the liquid developer. Further, it is possible to work in a bright room from the manufacturing process of the lithographic printing plate precursor to the plate making process and the printing process, and also to perform long-term stable storage in the bright room or under oxygen.
【００２０】[0020]
【発明の実施の形態】以下、図面を使って、本発明の実
施の形態を説明する。Embodiments of the present invention will be described below with reference to the drawings.
【００２１】図１は本発明に係わる平版印刷原版の一例
を表す断面概略図である。本発明に係わる平版印刷原版
（ａ）は、支持体１の紙ベース１１の表裏面上に疎水性
である樹脂１２が被覆するように設けてあり、さらにそ
の上層（最表層）として親水性層３が設けられている。
本発明の平版印刷版の製版方法としては、まず、平版印
刷用原版（ａ）にレーザにより所望する画像様に照射を
行う。ここで、レーザが照射された部分の親水性層３が
熱溶融及び／または熱分解され、樹脂１２が露出される
ことで製版が完了する。この後に、平版印刷機に装着す
れば、疎水性である樹脂１２が露出した部分にインキ
が、また残存している親水性層３には水がそれぞれ受理
され、印刷が可能となる。FIG. 1 is a schematic sectional view showing an example of a lithographic printing original plate according to the present invention. The lithographic printing plate precursor (a) according to the present invention is provided so that a hydrophobic resin 12 is coated on the front and back surfaces of a paper base 11 of a support 1, and a hydrophilic layer as an upper layer (outermost layer). 3 are provided.
In the method of making a lithographic printing plate according to the present invention, first, a lithographic printing original plate (a) is irradiated with a laser to obtain a desired image. Here, the plate making is completed when the portion of the hydrophilic layer 3 irradiated with the laser is thermally melted and / or thermally decomposed and the resin 12 is exposed. Thereafter, when the apparatus is mounted on a lithographic printing press, ink is received in a portion where the hydrophobic resin 12 is exposed, and water is received in the remaining hydrophilic layer 3, thereby enabling printing.
【００２２】本発明に係わる平版印刷原版の親水性層
は、皮膜形成能を有する親水性ポリマーを主体としてな
り、少なくとも最表層が親水性層となるように塗設され
る。この親水性層は複数あっても差し支えない。また親
水性層を構成する親水性ポリマーの量としては一層あた
り０．５〜１０ｇ／ｍ2の範囲であれば良い。The hydrophilic layer of the lithographic printing plate precursor according to the present invention mainly comprises a hydrophilic polymer having a film-forming ability, and is applied so that at least the outermost layer is a hydrophilic layer. There may be more than one hydrophilic layer. The amount of the hydrophilic polymer constituting the hydrophilic layer may be in the range of 0.5 to 10 g / m 2 per layer.
【００２３】このような親水性層を形成する親水性ポリ
マーとしては、以下の例が挙げられ、これらは地汚れ性
や耐刷性など印刷性能を鑑みて２種以上混合して用いる
ことができる。Examples of the hydrophilic polymer forming the hydrophilic layer include the following examples. These can be used as a mixture of two or more kinds in view of printing performance such as background stain and printing durability. .
【００２４】天然物では、澱粉類、海藻マンナン、寒天
およびアルギン酸ナトリウム等の藻類から得られるも
の、マンナン、ペクチン、トラガントガム、カラヤガ
ム、キサンチンガム、グアービンガム、ローカストビン
ガム、アラビアガム等の植物性粘質物、デキストラン、
グルカン、キサンタンガム、およびレバンなどのホモ多
糖類、サクシノグルカン、プルラン、カードラン、およ
びザンタンガムなどのヘテロ多糖等の微生物粘質物、に
かわ、ゼラチン、カゼインおよびコラーゲン等のタンパ
ク質、キチンおよびその誘導体等が挙げられる。Examples of natural products include those obtained from algae such as starches, seaweed mannan, agar and sodium alginate; vegetable mucilage such as mannan, pectin, tragacanth gum, karaya gum, xanthin gum, guaringham, locust bingham, gum arabic; Dextran,
Glucan, xanthan gum, and homopolysaccharides such as levan, succinoglucan, pullulan, curdlan, and microbial mucilage such as heteropolysaccharides such as xanthan gum, glue, gelatin, proteins such as casein and collagen, chitin and its derivatives and the like. No.
【００２５】また、半天然物（半合成物）類としては、
セルロース誘導体、カルボキシメチルグアーガム等の変
性ガム、並びにデキストリン等の培焼澱粉類、酸化澱粉
類、エステル化澱粉類等の加工澱粉等が挙げられる。Also, as a semi-natural product (semi-synthetic product),
Examples include cellulose derivatives, modified gums such as carboxymethyl guar gum, and modified starches such as baked starches such as dextrin, oxidized starches, and esterified starches.
【００２６】合成品には、ポリビニルアルコール、部分
アセタール化ポリビニルアルコール、アリル変性ポリビ
ニルアルコール、ポリビニルメチルエーテル、ポリビニ
ルエチルエーテル、ポリビニルイソブチルエーテル等の
変性ポリビニルアルコール、ポリアクリル酸塩、ポリア
クリル酸エステル部分けん化物、ポリメタクリル酸塩、
及びポリアクリルアマイド等のポリアクリル酸誘導体及
びポリメタクリル酸誘導体、ポリエチレングリコール、
ポリエチレンオキサイド、ポリビニルピロリドン、ビニ
ルピロリドン／酢酸ビニル共重合物、カルボキシビニル
重合物、スチレン／マレイン酸共重合物、スチレン／ク
ロトン酸共重合物等が挙げられる。The synthetic products include polyvinyl alcohol, partially acetalized polyvinyl alcohol, allyl-modified polyvinyl alcohol, modified polyvinyl alcohol such as polyvinyl methyl ether, polyvinyl ethyl ether and polyvinyl isobutyl ether, polyacrylate, and polyacrylate. Compound, polymethacrylate,
And polyacrylic acid derivatives such as polyacrylamide and polymethacrylic acid derivatives, polyethylene glycol,
Examples include polyethylene oxide, polyvinylpyrrolidone, vinylpyrrolidone / vinyl acetate copolymer, carboxyvinyl polymer, styrene / maleic acid copolymer, and styrene / crotonic acid copolymer.
【００２７】これらの中でも、特にゼラチン、変性及び
無変性のポリビニルアルコール、及びセルロース誘導体
が有利に使用できる。Of these, gelatin, modified and unmodified polyvinyl alcohol, and cellulose derivatives can be advantageously used.
【００２８】本発明の平版印刷用原版に係わる親水性層
に用いるゼラチンとしては、動物のコラーゲンを原料と
したゼラチンであれば全て使用できるが、豚皮、牛皮、
及び牛骨から得られるコラーゲンを原料としたゼラチン
が好ましい。また、ゼラチンの種類も特に制限はない
が、石灰処理ゼラチン及び酸処理ゼラチンの他、特公昭
３８−４８５４号、同３９−５５１４号、同４０−１２
２３７号、及び同４２−２６３４５号公報、米国特許第
２,５２５,７５３号、同第２,５９４,２９３号、同第
２,６１４,９２８号、同第２,７６３,６３９号、同第
３,１１８,７６６号、同第３,１３２,９４５号、同第
３,１８６,８４６号、同第３,３１２,５５３号明細書、
英国特許第１,０３３,１８９号明細書等に記載のゼラチ
ン誘導体等が挙げられ、これらは１種または２種以上を
組合わせて用いることができる。As the gelatin used for the hydrophilic layer of the lithographic printing plate precursor according to the present invention, any gelatin derived from animal collagen can be used.
Gelatin using collagen obtained from bovine bone as a raw material is preferable. There is no particular limitation on the kind of gelatin, but in addition to lime-treated gelatin and acid-treated gelatin, Japanese Patent Publication Nos. 38-4854, 39-5514, and 40-12.
Nos. 237 and 42-26345; U.S. Pat. Nos. 2,525,753, 2,594,293, 2,614,928, 2,763,639, and 3,118,766, 3,132,945, 3,186,846, 3,312,553,
Gelatin derivatives described in British Patent No. 1,033,189 and the like can be mentioned, and these can be used alone or in combination of two or more.
【００２９】ゼラチンを親水性層に用いる場合には、ゼ
ラチン硬膜剤で硬化することができる。ゼラチン硬膜剤
としては、例えば、クロム明ばんのような無機化合物、
ホルマリン、グリオキサール、マレアルデヒド、グルタ
ルアルデヒドのようなアルデヒド類、尿素やエチレン尿
素等のＮ−メチラール化合物、ムコクロル酸、２，３−
ジヒドロキシ−１，４−ジオキサンのようなアルデヒド
類縁化合物、２，４−ジクロロ−６−ヒドロキシ−Ｓ−
トリアジン塩や、２，４−ジヒドロキシ−６−クロロ−
Ｓ−トリアジン塩のような活性ハロゲンを有する化合
物、ジビニルスルホン、ジビニルケトンやＮ，Ｎ，Ｎ−
トリアクリロイルヘキサヒドロトリアジン、活性な三員
環であるエチレンイミノ基やエポキシ基を分子中に二個
以上有する化合物類、高分子硬膜剤としてのジアルデヒ
ド澱粉等の種々の化合物の１種もしくは２種以上を用い
ることができる。When gelatin is used for the hydrophilic layer, it can be cured with a gelatin hardener. Gelatin hardeners include, for example, inorganic compounds such as chrome alum,
Aldehydes such as formalin, glyoxal, malealdehyde and glutaraldehyde, N-methylal compounds such as urea and ethylene urea, mucochloric acid, 2,3-
Aldehyde analogs such as dihydroxy-1,4-dioxane, 2,4-dichloro-6-hydroxy-S-
Triazine salts, 2,4-dihydroxy-6-chloro-
Compounds having an active halogen such as S-triazine salt, divinyl sulfone, divinyl ketone, N, N, N-
One or two of various compounds such as triacryloylhexahydrotriazine, compounds having two or more active three-membered ethyleneimino groups or epoxy groups in a molecule, and dialdehyde starch as a polymer hardener. More than one species can be used.
【００３０】また一般式１に示したアクリルアミド系の
ポリマーの含有量は、３００ｍｇ／ｍ2以下が好まし
く、より好ましくは２〜１５０ｍｇ／ｍ2の範囲であ
り、分子量としては塗液安定性や塗布性を考えて、１万
〜５０万、より好ましくは５万〜３０万の範囲のもので
ある。The content of the acrylamide polymer represented by the general formula 1 is preferably 300 mg / m 2 or less, more preferably in the range of 2 to 150 mg / m 2. Considering the properties, it is in the range of 10,000 to 500,000, more preferably 50,000 to 300,000.
【００３１】本発明に係わる平版印刷原版の親水性層に
は、印刷地汚れ性を防止する目的で酸化チタン、二酸化
ケイ素、酸化アルミニウム等の無機物を含有させること
ができる。含有させる割合は、印刷に用いる印刷インキ
や湿し水等や印刷速度や印刷圧など各種条件により適宜
所望の範囲で決められる。The hydrophilic layer of the lithographic printing plate precursor according to the present invention may contain an inorganic substance such as titanium oxide, silicon dioxide, aluminum oxide or the like for the purpose of preventing printing soiling. The proportion to be contained is appropriately determined in a desired range depending on various conditions such as printing ink and fountain solution used for printing, printing speed and printing pressure.
【００３２】また、本発明に係わる平版印刷原版の親水
性層を塗設するために、助剤としてアニオン系、カチオ
ン系もしくはノニオン系界面活性剤のいくつかを用いて
も良いし、マット剤、増粘剤、帯電防止剤等を用いるこ
ともできる。In order to coat the hydrophilic layer of the lithographic printing plate precursor according to the present invention, some of anionic, cationic or nonionic surfactants may be used as an auxiliary, and a matting agent, Thickeners, antistatic agents and the like can also be used.
【００３３】本発明に係わる平版印刷用原版の疎水性表
面を有する支持体としては、樹脂被覆紙、合成紙、ポリ
エチレンテレフタレートなどの合成もしくは半合成高分
子フィルム、アルミニウムや鉄等の金属板で、少なくと
もその表面が、インキと水を両方与えた場合にインキを
受理する程度の疎水性表面を有しており、平版印刷に耐
えるものであれば良い。また、これらの支持体の表面
は、上層として塗設される層との接着を良くするために
表面処理を行うことや、レーザ光吸収性を向上させるた
め染色処理をすることも可能である。Examples of the support having a hydrophobic surface of the lithographic printing plate precursor according to the present invention include resin-coated paper, synthetic paper, synthetic or semi-synthetic polymer films such as polyethylene terephthalate, and metal plates such as aluminum and iron. It is sufficient that at least the surface has a hydrophobic surface enough to accept the ink when both the ink and the water are applied and that it can withstand lithographic printing. Further, the surface of these supports can be subjected to a surface treatment in order to improve the adhesion to a layer to be coated as an upper layer, or can be subjected to a dyeing treatment in order to improve laser light absorption.
【００３４】本発明に係わる平版印刷原版は、耐刷性や
インキ乗り性など印刷性能の改善の目的で、支持体表面
上にさらに疎水性層を設けることもできる。この疎水性
層は、インキ受理性能と支持体表面との接着性および親
水性層との接着性が良く、かつ皮膜形成が良好な合成樹
脂（ポリマー）により形成するのが好ましく、例えば
（メタ）アクリル樹脂、酢酸ビニル樹脂、ポリエチレン
樹脂、ポリプロピレン樹脂、ポリブタジエン樹脂、塩化
ビニル樹脂、ビニルアセタール樹脂、塩化ビニリデン樹
脂、スチレン樹脂、ポリエステル樹脂、ポリアミド樹
脂、フェノール樹脂、キシレン樹脂、アルキッド樹脂、
等を挙げることができる。これらの樹脂は必要に応じて
２種以上混合して使用することができるし、また複数の
層としても良い。In the lithographic printing plate precursor according to the present invention, a hydrophobic layer may be further provided on the surface of the support for the purpose of improving printing performance such as printing durability and ink running property. The hydrophobic layer is preferably formed of a synthetic resin (polymer) having good ink receiving performance, good adhesion to the support surface, good adhesion to the hydrophilic layer, and good film formation. Acrylic resin, vinyl acetate resin, polyethylene resin, polypropylene resin, polybutadiene resin, vinyl chloride resin, vinyl acetal resin, vinylidene chloride resin, styrene resin, polyester resin, polyamide resin, phenol resin, xylene resin, alkyd resin,
And the like. These resins can be used as a mixture of two or more kinds, if necessary, or may be a plurality of layers.
【００３５】本発明の平版印刷版の製版方法において、
親水性層を加熱し支持体の疎水性表面を露出させるため
に用いられるレーザとしては、炭酸ガスレーザ、窒素レ
ーザ、Ａｒレーザ、Ｈｅ／Ｎｅレーザ、Ｈｅ／Ｃｄレー
ザ、Ｋｒレーザ等の気体レーザ、液体（色素）レーザ、
ルビーレーザ、Ｎｄ／ＹＡＧレーザ等の固体レーザ、Ｇ
ａＡｓ／ＧａＡｌＡｓ、ＩｎＧａＡｓレーザ等の半導体
レーザ、ＫｒＦレーザ、ＸｅＣｌレーザ、ＸｅＦレー
ザ、Ａｒ2等のエキシマレーザ等を挙げることができ
る。In the method of making a lithographic printing plate according to the present invention,
Lasers used for heating the hydrophilic layer to expose the hydrophobic surface of the support include gas lasers such as carbon dioxide laser, nitrogen laser, Ar laser, He / Ne laser, He / Cd laser, and Kr laser, and liquid lasers. (Dye) laser,
Solid-state laser such as ruby laser, Nd / YAG laser, G
Examples thereof include semiconductor lasers such as aAs / GaAlAs and InGaAs lasers, and excimer lasers such as a KrF laser, a XeCl laser, a XeF laser, and Ar 2 .
【００３６】本発明の平版印刷版の製版方法において、
本発明に係わる平版印刷原版の親水性層の熱溶融及び／
または熱分解を促進させ支持体表面を露出させる効率
（即ち本発明の方法における平版印刷原版の感度と言え
る）を向上させるために、親水性層、支持体、もしくは
平版印刷原版が複数の層からなる場合には親水性層以外
の層、の何れかに光吸収剤を含有させる。In the method of making a lithographic printing plate according to the present invention,
Thermal melting of the hydrophilic layer of the lithographic printing plate precursor according to the present invention and / or
Alternatively, in order to enhance the efficiency of exposing the support surface by promoting thermal decomposition (that is, the sensitivity of the lithographic printing original plate in the method of the present invention), the hydrophilic layer, the support, or the lithographic printing original plate may be formed from a plurality of layers. In such a case, a light absorbing agent is contained in any of the layers other than the hydrophilic layer.
【００３７】光吸収剤としては一般的に染料または顔料
であれば良く、例えばカーボンブラック、シアニン、無
金属または金属フタロシアニン、金属ジチオレン、アン
トラキノン等を挙げることができる。The light absorber may be any dye or pigment, and examples thereof include carbon black, cyanine, metal-free or metal phthalocyanine, metal dithiolene, and anthraquinone.
【００３８】また金属製支持体に光吸収剤を含有させる
場合においては、一般的に黒染と呼ばれる、化学的ある
いは電気化学的な金属着色法を用いることができる。特
にアルミニウム支持体の場合には、予め陽極酸化処理を
行った支持体に有機もしくは無機の染料を浸漬染色によ
り、陽極酸化膜が有する微細な多孔に染料を導入し、後
に封孔処理を行い染色することができる。When the light absorbing agent is contained in the metal support, a chemical or electrochemical metal coloring method generally called black dyeing can be used. Especially in the case of an aluminum support, an organic or inorganic dye is introduced into the fine pores of the anodized film by dipping and dyeing the support which has been previously subjected to anodizing treatment, and then the pores are sealed and dyed. can do.
【００３９】[0039]
【実施例】以下本発明を実施例により詳説するが、本発
明はその主旨を超えない限り、下記実施例に限定される
ものではない。EXAMPLES The present invention will be described in detail below with reference to examples, but the present invention is not limited to the following examples unless it exceeds the gist of the invention.
【００４０】実施例１ １３５ｇ／ｍ2の両面ポリエチレン被覆紙（ＲＣ紙）の
片面に平均粒子サイズ５μｍの二酸化ケイ素粒子を含有
するマット化層を設け、反対側の面にカーボンブラッ
ク、平均粒径７μｍの二酸化ケイ素粒子、硬膜剤として
の２，４−ジクロロ−６−ヒドロキシ−Ｓ−トリアジン
ナトリウム、及びゼラチン（３．５ｇ／ｍ2となるよう
に添加）からなる塗液を塗設し親水性層Ａを設けた。さ
らにその上に一般式１のポリマー（式中のＲ１、Ｒ２は
水素原子を表し、ｎ＝７８モル％、ｍ＝１０モル％、ｌ
＝２モル％である。平均分子量は１０万である。）塗液
を作成し、前記ポリマーが２０ｍｇ／ｍ2となるように
塗布、乾燥させ、親水性層Ｂとし、２層の親水性層を有
する平版印刷用原版を作製した。Example 1 A matte layer containing silicon dioxide particles having an average particle size of 5 μm was provided on one side of 135 g / m 2 double-sided polyethylene coated paper (RC paper), and carbon black and an average particle size were provided on the other side. A coating liquid comprising 7 μm silicon dioxide particles, sodium 2,4-dichloro-6-hydroxy-S-triazine as a hardener, and gelatin (added to 3.5 g / m 2 ) is applied and hydrophilic. An active layer A was provided. Further, a polymer of the general formula 1 (wherein R1 and R2 represent hydrogen atoms, n = 78 mol%, m = 10 mol%, l
= 2 mol%. The average molecular weight is 100,000. A) A coating solution was prepared, the polymer was applied so as to have a concentration of 20 mg / m 2, and dried to prepare a hydrophilic layer B, thereby preparing a lithographic printing original plate having two hydrophilic layers.
【００４１】次いで、半導体レーザ照射装置（８３０ｎ
ｍ）で画像部に相当する部分のレーザ照射を上記原版
（親水性層Ｂを最表層とする面）に行い、支持体表面を
露出させて、印刷版を得た。この印刷版を用いて、オフ
セット印刷機（リョービイマジクス（株）製 ３２００
ＭＣＤ）にて印刷を行ったところ、印刷の初段階から、
支持体表面が露出した部分にインキが着肉しており、５
千枚まで非画像部汚れ等が生じない良好な印刷物を得る
ことができた。Next, a semiconductor laser irradiation device (830n)
In m), laser irradiation of the portion corresponding to the image portion was performed on the original plate (the surface having the hydrophilic layer B as the outermost layer) to expose the surface of the support to obtain a printing plate. Using this printing plate, an offset printing machine (Ryobi Magics 3200)
MCD), and from the beginning of printing,
Ink is deposited on the part where the surface of the support is exposed.
A good printed matter free of non-image area stains and the like was obtained up to 1,000 sheets.
【００４２】保存性試験 上記と同様に作製した平版印刷用原版を３０℃の明室下
で６ヶ月保存した後に、上記と同様の方法で、印刷版の
製版を試みたところ、上記保存前と遜色のない印刷版を
得ることができた。 Preservation test The lithographic printing plate precursor prepared as described above was stored for 6 months in a light room at 30 ° C., and then a printing plate was prepared in the same manner as described above. A printing plate of comparable quality was obtained.
【００４３】実施例２ 厚さ１７５μｍのＰＥＴ（ポリエチレンテレフタレー
ト）フィルムの片面に平均粒子サイズ５μｍの二酸化ケ
イ素粒子を含有するマット化層を設け、反対側の面に、
無金属フタロシアニン顔料、ポリメタクリル酸メチル
（平均分子量３万）をキシレンを溶媒として塗布液を作
製し、塗布、乾燥させて、疎水性層（膜厚２μｍ）を形
成した。Example 2 A matting layer containing silicon dioxide particles having an average particle size of 5 μm was provided on one side of a PET (polyethylene terephthalate) film having a thickness of 175 μm, and on the opposite side,
A coating liquid was prepared by using a metal-free phthalocyanine pigment and polymethyl methacrylate (average molecular weight: 30,000) in xylene as a solvent, applied and dried to form a hydrophobic layer (film thickness: 2 μm).
【００４４】次いで、カーボンブラック、平均粒径７μ
ｍの二酸化ケイ素粒子、硬膜剤としてのＮ−メチロール
エチレン尿素、及びゼラチン（２．５ｇ／ｍ2となるよ
うに添加）、さらに一般式１のポリマー（式中Ｒ１、Ｒ
２は水素原子を表し、ｎ＝８０モル％、ｍ＝０モル％、
ｌ＝０モル％である。平均分子量は３万である。）を１
００ｍｇ／ｍ2となるように添加した塗液を作成し、親
水性層Ｃとして塗設し平版印刷原版を作製した。Then, carbon black, average particle size 7 μm
m of silicon dioxide particles, N-methylol ethylene urea as a hardener, and gelatin (added to 2.5 g / m 2 ), and a polymer of the general formula 1 (wherein R1, R
2 represents a hydrogen atom, n = 80 mol%, m = 0 mol%,
1 = 0 mol%. The average molecular weight is 30,000. ) To 1
A coating solution was added at a concentration of 00 mg / m 2 and applied as a hydrophilic layer C to prepare a lithographic printing original plate.
【００４５】半導体レーザ照射装置（８３０ｎｍ）で画
像部に相当する親水性層を照射し疎水性層を露出させ
て、印刷版を得た。この印刷版を用いて、実施例１と同
様に印刷を行ったところ、印刷の初段階から、４万枚ま
で非画像部汚れ等が生じず、インキ乗りの良い印刷物を
得ることができた。The printing plate was obtained by irradiating the hydrophilic layer corresponding to the image area with a semiconductor laser irradiation device (830 nm) to expose the hydrophobic layer. When printing was performed using this printing plate in the same manner as in Example 1, no non-image area stains were generated from the initial stage of printing up to 40,000 sheets, and a printed material with good ink coverage could be obtained.
【００４６】実施例３ 砂目立て及び陽極酸化された厚み０．２４ｍｍのアルミ
ニウム板を、アルミニウム用染料（サンド社製 Ｓａｎ
ｏｄａｌ Ｄｅｅｐ Ｂｌａｃｋ ＭＬＷ）を用いて常
法に従い黒色に染色した。Example 3 A grained and anodically oxidized aluminum plate having a thickness of 0.24 mm was coated with a dye for aluminum (San Co., Ltd.
odeep Deep Black MLW) in accordance with a conventional method.
【００４７】次に、上記支持体に、実施例１で用いた親
水性層Ａ及び親水性層Ｂの２層の親水性層塗設し平版印
刷用原版を作製した。Next, two hydrophilic layers of the hydrophilic layer A and the hydrophilic layer B used in Example 1 were coated on the above support to prepare a lithographic printing original plate.
【００４８】実施例１と同じ半導体レーザ照射装置を用
い、描画速度を実施例１の１．３倍として画像部に相当
する親水性層にレーザを照射し疎水性層を露出させて、
印刷版を得た。この印刷版を用いて、実施例１と同様に
印刷を行ったところ、印刷の初段階から、１０万枚まで
非画像部汚れ等が生じず、インキ乗りの良い印刷物を得
ることができた。Using the same semiconductor laser irradiation apparatus as in the first embodiment, the drawing speed was set to 1.3 times that of the first embodiment, and the hydrophilic layer corresponding to the image area was irradiated with laser to expose the hydrophobic layer.
A printing plate was obtained. When printing was performed using this printing plate in the same manner as in Example 1, non-image area stains and the like did not occur from the initial stage of printing up to 100,000 sheets, and a printed material with good ink coverage could be obtained.
【００４９】[0049]
【発明の効果】以上説明したごとく、本発明の平版印刷
版の製版方法及び平版印刷用原版は従来のジアゾ化合物
やフォトポリマーを用いた平版印刷版の製版方法と異な
り、明室下でも作業が行え、かつ現像液を使用すること
がないので作業環境が非常に良好である。また、低出力
のレーザを用いての直接描画方法に対応することがで
き、高解像性を有する画像を低コストで得ることができ
るという秀逸な効果をもたらす。As described above, the lithographic printing plate making method and the lithographic printing plate precursor of the present invention are different from the conventional lithographic printing plate making methods using a diazo compound or a photopolymer in that the work can be performed even in a bright room. The working environment is very good because it can be performed and no developer is used. In addition, it is possible to cope with a direct writing method using a low-output laser, which brings about an excellent effect that an image having high resolution can be obtained at low cost.
【図１】本発明の平版印刷用原版を表す概念図である。FIG. 1 is a conceptual diagram illustrating a lithographic printing original plate of the present invention.
１ 支持体 １１ 紙ベース １２ 樹脂 ３ 親水性層 DESCRIPTION OF SYMBOLS 1 Support 11 Paper base 12 Resin 3 Hydrophilic layer
Claims (4)
とも最表層として親水性層を設けてなる平版印刷原版に
おいて、画像とする部分の親水性層をレーザによって加
熱することにより、前記平版印刷原版支持体の疎水性表
面を露出させることを特徴とする平版印刷版の製版方
法。1. A lithographic printing original plate comprising a support having a hydrophobic surface and at least a hydrophilic layer provided as an outermost layer, wherein the lithographic printing is performed by heating the hydrophilic layer of an image portion with a laser. A method for making a lithographic printing plate, comprising exposing a hydrophobic surface of an original plate support.
に光吸収剤を含有することを特徴とする請求項１記載の
平版印刷版の製版方法。2. The method according to claim 1, wherein at least one layer of the lithographic printing plate precursor contains a light absorbing agent.
含有することを特徴とする請求項１または２に記載の平
版印刷版の製版方法。3. The method of making a lithographic printing plate according to claim 1, wherein the support of the lithographic printing original plate contains a light absorbing agent.
るポリマーを含有することを特徴とする請求項１〜３の
何れかに記載の平版印刷版の製版方法。 【化１】 （式中のＲ１は水素原子またはアルキル基を表し、Ｒ２
は水素原子またはアルカリ金属原子を表し、ｎは１〜１
００モル％、ｍは０〜５０モル％、ｌは０〜５モル％で
ある。そして、平均分子量は２０００〜３０万であ
る。）4. The method for making a lithographic printing plate according to claim 1, wherein the hydrophilic layer contains a polymer represented by the following general formula 1. Embedded image (Wherein R1 represents a hydrogen atom or an alkyl group;
Represents a hydrogen atom or an alkali metal atom, and n represents 1 to 1
00 mol%, m is 0 to 50 mol%, and l is 0 to 5 mol%. And an average molecular weight is 2000-300,000. )