JPH10221566A - Optical connector ferrule - Google Patents
Optical connector ferruleInfo
- Publication number
- JPH10221566A JPH10221566A JP2643497A JP2643497A JPH10221566A JP H10221566 A JPH10221566 A JP H10221566A JP 2643497 A JP2643497 A JP 2643497A JP 2643497 A JP2643497 A JP 2643497A JP H10221566 A JPH10221566 A JP H10221566A
- Authority
- JP
- Japan
- Prior art keywords
- optical connector
- ferrule
- connector ferrule
- resin composition
- optical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、光ファイバを接続
するための光コネクタフェルールに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an optical connector ferrule for connecting an optical fiber.
【０００２】[0002]
【従来の技術】光通信や光測定等の分野において、光フ
ァイバの接続に用いられる光コネクタは、単心のものと
多心のものとがある。多心のものでは、複数本の単心の
光ファイバの接続に用いられるものと、テープ状光ファ
イバ心線に用いられるものがあるが、嵌合ピンを用いて
位置決めを行なう構造のものが一般的である。このよう
に、光コネクタの種類は、多種類に及んでいる。この光
コネクタを用いて光ファイバを接続する場所が、マンホ
ール内や、架線に取り付けられる接続函内などのよう
に、一度結合した後は、ほとんど着脱が行なわれない場
所に用いる光コネクタとしては、一対の多心コネクタを
クリップ等簡易な把持具を用いて結合する、いわゆるＭ
Ｔ（Ｍｅｃｈａｎｉｃａｌｌｙ Ｔｒａｎｓｆｅｒａｂ
ｌｅ）コネクタが使用されている。また、屋内の比較的
着脱回数の多い用途では、プッシュプル機構を持つハウ
ジングを有し、コネクタアダプタを介して結合する、い
わゆるＭＰＯ（Ｍｕｌｔｉ−ｐａｓｓ Ｐｕｓｈ Ｏ
ｎ）コネクタが使用される場合が多い。2. Description of the Related Art In the fields of optical communication, optical measurement, and the like, optical connectors used for connecting optical fibers include single-core and multi-core connectors. The multi-core type is used for connecting a plurality of single-core optical fibers, and the tape type optical fiber is used. It is a target. Thus, the types of optical connectors are many. As an optical connector used in a place where the optical fiber is connected using this optical connector, such as in a manhole or a connection box attached to an overhead wire, once it is connected, it is hardly detachable. A pair of multi-core connectors are connected using a simple gripping tool such as a clip, so-called M
T (Mechanically Transferferab)
le) Connectors are used. In applications where the number of times of attachment and detachment is relatively large indoors, a so-called MPO (Multi-pass Push O) is provided which has a housing having a push-pull mechanism and is connected via a connector adapter.
n) Connectors are often used.
【０００３】図１は、実用化されているＭＴコネクタの
説明図であり、図１（Ａ）はコネクタの結合前の斜視
図、図１（Ｂ）はコネクタ結合時の斜視図である。図
中、１０は光ファイバ、１１は光コネクタフェルール、
１１ａはガイドピン穴、１２はテープ状光ファイバ心
線、１３はガイドピン、１４はクリップである。FIG. 1 is an explanatory view of an MT connector that has been put into practical use. FIG. 1 (A) is a perspective view before the connector is connected, and FIG. 1 (B) is a perspective view when the connector is connected. In the figure, 10 is an optical fiber, 11 is an optical connector ferrule,
11a is a guide pin hole, 12 is a tape-shaped optical fiber core wire, 13 is a guide pin, and 14 is a clip.
【０００４】図１（Ａ）に示すように、一対の光コネク
タフェルール１１の結合端面には、ガイドピン１３と嵌
合する２つのガイドピン穴１１ａが開けられ、その間の
部分に複数本の光ファイバ１０を挿入する穴が設けられ
ている。この穴に多心のテープ状光ファイバ心線１２の
複数本の光ファイバ１０を、その端部が露出するようエ
ポキシ系接着剤等で固定した後、光コネクタフェルール
３１の端面が、光ファイバ１０の端面と共に研磨され
る。As shown in FIG. 1A, two guide pin holes 11a for fitting with the guide pins 13 are formed in the joint end faces of the pair of optical connector ferrules 11, and a plurality of optical pins are provided between the guide pin holes 11a. A hole for inserting the fiber 10 is provided. After fixing a plurality of optical fibers 10 of the multi-core optical fiber core 12 in this hole with an epoxy adhesive or the like so that the ends are exposed, the end face of the optical connector ferrule 31 is Is polished together with the end face.
【０００５】結合状態においては、２本のガイドピン１
３によって左右の光コネクタフェルール１１が位置決め
されて、突き合わされ、ガイドピン穴１１ａに対して精
密に配列固定された左右の光ファイバ１０同士が、屈折
率整合剤を介して結合され、図１（Ｂ）に示すようなク
リップ１４で固定される。In the coupled state, two guide pins 1
The right and left optical connector ferrules 11 are positioned and abutted by 3 and the right and left optical fibers 10 precisely aligned and fixed in the guide pin holes 11a are connected to each other via a refractive index matching agent, and are connected as shown in FIG. It is fixed with a clip 14 as shown in FIG.
【０００６】図２は、実用化されているＭＰＯコネクタ
の説明図であり、図２（Ａ）はコネクタプラグの斜視
図、図２（Ｂ）はコネクタアダプタの斜視図、図２
（Ｃ）は光コネクタフェルールの端面の拡大図である。
図中、図１と同様な部分には同じ符号を付して説明を省
略する。２１は光コネクタフェルール、２１ａはガイド
ピン穴、２２はコネクタプラグ、２３はコネクタハウジ
ング、２４はコネクタアダプタである。FIG. 2 is an explanatory view of an MPO connector that has been put into practical use. FIG. 2 (A) is a perspective view of a connector plug, FIG. 2 (B) is a perspective view of a connector adapter, FIG.
(C) is an enlarged view of the end face of the optical connector ferrule.
In the figure, the same parts as those in FIG. 21 is an optical connector ferrule, 21a is a guide pin hole, 22 is a connector plug, 23 is a connector housing, and 24 is a connector adapter.
【０００７】図２（Ａ）に示すように、コネクタプラグ
２２は、コネクタハウジング２３内に光コネクタフェル
ール２１が収容されたもので、テープ状光ファイバ心線
１２の多心の光ファイバ１０の端面が、図２（Ｃ）に示
すように、光コネクタフェルール２１の端面に露出して
いる。光ファイバ１０が光コネクタフェルール２１にエ
ポキシ系接着剤等で固定された後、光コネクタフェルー
ル２１の端面が、光ファイバ１０の端面と共に研磨され
る。なお、光コネクタフェルール２１にはガイドピンを
挿入するガイドピン穴２１ａが設けられている。As shown in FIG. 2A, the connector plug 22 is a connector housing 23 in which an optical connector ferrule 21 is accommodated, and the end face of the multi-core optical fiber 10 of the tape-shaped optical fiber core 12. However, as shown in FIG. 2C, it is exposed at the end face of the optical connector ferrule 21. After the optical fiber 10 is fixed to the optical connector ferrule 21 with an epoxy adhesive or the like, the end face of the optical connector ferrule 21 is polished together with the end face of the optical fiber 10. The optical connector ferrule 21 is provided with a guide pin hole 21a for inserting a guide pin.
【０００８】一対のコネクタプラグ２２を、図２（Ｂ）
に示すような角型形状のコネクタアダプタ２４の左右か
ら差し込んで、左右のコネクタフェルール２１同士を物
理的結合（Ｐｈｙｓｉｃａｌ Ｃｏｎｔａｃｔ、以下、
「ＰＣ結合」という。）により結合する。詳細構造につ
いては説明を省略するが、コネクタアダプタ２４の内部
にはコネクタ係止機構があり、コネクタハウジング２３
の先端の挿入ガイドをコネクタアダプタ内に係止するよ
うになっている。また、コネクタハウジング２３と光コ
ネクタフェルール２１との間隙がフローティング空間に
なっている。A pair of connector plugs 22 are connected to each other as shown in FIG.
The connector ferrules 21 are inserted from the left and right sides of a rectangular connector adapter 24 as shown in FIG.
It is called "PC connection". ). Although a detailed description is omitted, a connector locking mechanism is provided inside the connector adapter 24 and the connector housing 23 is provided.
The insertion guide at the tip of the connector is locked in the connector adapter. The gap between the connector housing 23 and the optical connector ferrule 21 is a floating space.
【０００９】このＭＰＯコネクタは、通常、光コネクタ
フェルール同士を屈折率整合剤を使用せずに接触させる
ＰＣ結合の方式で結合するので、結合面における反射光
が、光ファイバ内に戻らないようにするため、光コネク
タフェルール２１の端面を斜めに、例えば、８度の角度
となるように研磨する。In this MPO connector, the optical connector ferrules are usually connected by a PC coupling method in which the optical connector ferrules are brought into contact with each other without using a refractive index matching agent. To this end, the end face of the optical connector ferrule 21 is polished obliquely, for example, at an angle of 8 degrees.
【００１０】このような光コネクタフェルールは、従来
は熱硬化型のエポキシ樹脂を用いて、トランスファ成形
して製造されていたが、熱硬化型のエポキシ樹脂は硬化
に時間がかかるため、成形のサイクルタイムを早くでき
ないという問題があった。Conventionally, such an optical connector ferrule has been manufactured by transfer molding using a thermosetting epoxy resin, but the thermosetting epoxy resin takes a long time to cure. There was a problem that time could not be shortened.
【００１１】これに対して、熱可塑性樹脂を用いて射出
成形で光コネクタフェルールを製造することが提案され
ている。特開平８−１５５６８号公報に記載された光コ
ネクタフェルールは、少なくともサーモトロピック液晶
性全芳香族ポリエステルと炭素繊維を含む樹脂組成物を
用いて、射出成形で製造されるものである。しかしなが
ら、サーモトロピック液晶性全芳香族ポリエステルの場
合は、樹脂が配向しているために、成型時において、樹
脂が流動方向に配向してしまう。そうすると、樹脂の流
動方向とその直角方向とで異方性が生じる。このような
状態で成形が行なわれるから、成形後において、温度を
かけると、経時的に反りが生じやすく、充分な寸法精度
が保証されないという問題がある。On the other hand, it has been proposed to manufacture an optical connector ferrule by injection molding using a thermoplastic resin. The optical connector ferrule described in JP-A-8-15568 is manufactured by injection molding using a resin composition containing at least a thermotropic liquid crystalline wholly aromatic polyester and carbon fibers. However, in the case of a thermotropic liquid crystalline wholly aromatic polyester, the resin is oriented in the flow direction during molding because the resin is oriented. Then, anisotropy occurs in the flow direction of the resin and in the direction perpendicular to the resin flow direction. Since molding is performed in such a state, if a temperature is applied after molding, there is a problem that warping tends to occur with time, and sufficient dimensional accuracy cannot be guaranteed.
【００１２】[0012]
【発明が解決しようとする課題】本発明は、上述した問
題点を解決するためになされたもので、成形後に反りが
生じにくい樹脂成型物を用いた光コネクタフェルールを
提供することを目的とするものである。SUMMARY OF THE INVENTION The present invention has been made in order to solve the above-mentioned problems, and an object of the present invention is to provide an optical connector ferrule using a resin molded product which does not easily warp after molding. Things.
【００１３】[0013]
【課題を解決するための手段】請求項１に記載の発明
は、光ファイバを位置決め固定し、接続するための光コ
ネクタフェルールにおいて、該フェルールが、少なくと
も半芳香族型の液晶ポリマーと充填材を含む樹脂組成物
からなることを特徴とするものである。According to a first aspect of the present invention, there is provided an optical connector ferrule for positioning and fixing and connecting an optical fiber, wherein the ferrule comprises at least a semi-aromatic liquid crystal polymer and a filler. Characterized by comprising a resin composition containing:
【００１４】請求項２に記載の発明は、請求項１に記載
の光コネクタフェルールにおいて、前記樹脂組成物が、
無機充填材を６０重量％以上８５重量％以下含有するこ
とを特徴とするものである。According to a second aspect of the present invention, in the optical connector ferrule according to the first aspect, the resin composition comprises:
It is characterized by containing an inorganic filler in an amount of 60% by weight or more and 85% by weight or less.
【００１５】請求項３に記載の発明は、請求項２に記載
の光コネクタフェルールにおいて、前記無機充填材が、
少なくとも、ワラストナイト，タルク，マイカのいずれ
かを含んでいることを特徴とするものである。According to a third aspect of the present invention, in the optical connector ferrule according to the second aspect, the inorganic filler is:
It is characterized by containing at least one of wollastonite, talc, and mica.
【００１６】[0016]
【発明の実施の形態】本発明の光コネクタフェルールの
実施の形態は、光コネクタフェルールを成形するにあた
り、成形材料が、少なくとも半芳香族型の液晶ポリマー
をベースとする樹脂組成物からなるものである。この樹
脂組成物は、配向性は強くなく、成形後に温度をかけて
も、反りが生じにくいものであることが分かった。半芳
香族の液晶ポリマーの具体例としては、パラヒドロキシ
安息香酸の残基とテレフタル酸の残基、パラヒドロキシ
安息香酸の残基とエチレンプリコールの残基、あるい
は、パラヒドロキシ安息香酸の残基とテレフタル酸の残
基とエチレンプリコールの残基等からなる液晶性ポリエ
ステル共重合体などがある。BEST MODE FOR CARRYING OUT THE INVENTION In an embodiment of the optical connector ferrule of the present invention, when molding the optical connector ferrule, the molding material comprises at least a resin composition based on a semi-aromatic liquid crystal polymer. is there. It was found that this resin composition was not strong in orientation, and was not likely to be warped even when a temperature was applied after molding. Specific examples of the semi-aromatic liquid crystal polymer include a residue of parahydroxybenzoic acid and a residue of terephthalic acid, a residue of parahydroxybenzoic acid and a residue of ethylene prechol, or a residue of parahydroxybenzoic acid. And a liquid crystalline polyester copolymer comprising a residue of terephthalic acid and a residue of ethylene prechol.
【００１７】樹脂組成物における充填材としては、寸法
精度を上げるために、可能な限り高充填とすることが好
ましい。しかし、８５重量％を超える充填度では、材料
の粘度が極端に高くなり、樹脂組成物を金型内の細部ま
で充分に充填を行なうことが困難となり、ショートショ
ット等の問題が生じるから、これを避けるために、８５
重量％以下が望ましい。より好適には、８０重量％以下
が好ましい。充填材の充填度の下限値は、従来の通常の
成形では５０重量％が一般的であるが、６０重量％に満
たない充填量では、寸法精度の保証が難しく、６０重量
％以上が望ましい。より充分な寸法精度の要求に対して
は、７０重量％以上が望ましい。したがって、充填材の
充填度の範囲は、６０重量％以上８５重量％以下が好ま
しく、より好適な範囲としては、７０重量％以上８０重
量％以下が好適であるといえる。The filler in the resin composition is preferably as high as possible in order to increase the dimensional accuracy. However, if the filling degree exceeds 85% by weight, the viscosity of the material becomes extremely high, and it becomes difficult to sufficiently fill the resin composition into the details in the mold, and problems such as short shots occur. 85 to avoid
% By weight or less is desirable. More preferably, the content is 80% by weight or less. The lower limit of the filling degree of the filler is generally 50% by weight in conventional ordinary molding. However, if the filling amount is less than 60% by weight, it is difficult to guarantee the dimensional accuracy, and the lower limit is preferably 60% by weight or more. For the requirement of more sufficient dimensional accuracy, 70% by weight or more is desirable. Therefore, the range of the degree of filling of the filler is preferably from 60% by weight to 85% by weight, and more preferably, from 70% by weight to 80% by weight.
【００１８】充填材としては、ガラス繊維や炭素繊維が
一般的であるが、樹脂の配向を乱す目的を考慮すると、
ガラスビーズや、ワラストナイト，タルク，マイカ等の
ミネラルや、あるいは、ウィスカー等を用いるのが効果
的である。これら充填材を複数種類用いてもよい。As the filler, glass fiber or carbon fiber is generally used, but considering the purpose of disturbing the orientation of the resin,
It is effective to use glass beads, minerals such as wollastonite, talc and mica, or whiskers. A plurality of these fillers may be used.
【００１９】実施例について、比較例と共に説明する。
図３は、図１で説明したものと同様の光コネクタフェル
ールについて、樹脂組成物を変えて試作した成型品を１
００℃の恒温槽中で７日間放置した後の反り量で評価し
た実験結果を示したものである。試作Ｎｏ．１は、サー
モトロピック液晶性全芳香族ポリエステルとガラス繊維
を含む樹脂組成物を用いて試作した成型品で、比較例で
ある。試作Ｎｏ．２〜１０は、半芳香族型の液晶ポリマ
ーを含む樹脂組成物であるが、充填材としてガラス繊維
を用いた試作Ｎｏ．２〜５では、試作Ｎｏ．２，３が比
較例、試作Ｎｏ．４，５が本発明の実施例である。ま
た、充填材としてガラス繊維およびマイカを用いた試作
Ｎｏ．６〜１０では、試作Ｎｏ．６と１０が比較例、試
作Ｎｏ．７〜９が本発明の実施例である。なお、反り量
は、図４に示すように、光コネクタフェルールの端面を
正面から見て、反りによって生じた中央部と端部との高
さの差ｄをもって表わしたものである。Examples will be described together with comparative examples.
FIG. 3 shows a prototype of an optical connector ferrule similar to that described with reference to FIG.
FIG. 8 shows the results of an experiment evaluated on the amount of warpage after being left in a thermostat at 00 ° C. for 7 days. Prototype No. Reference numeral 1 is a comparative example, which was a trial product manufactured using a resin composition containing a thermotropic liquid crystalline wholly aromatic polyester and glass fiber. Prototype No. Nos. 2 to 10 are resin compositions containing a semi-aromatic type liquid crystal polymer. In Nos. 2 to 5, the prototype Nos. Nos. 2 and 3 are comparative examples and prototype Nos. 4 and 5 are examples of the present invention. In addition, a prototype No. using glass fiber and mica as a filler was manufactured. In Nos. 6 to 10, the prototype Nos. 6 and 10 are comparative examples, and prototype Nos. 7 to 9 are examples of the present invention. As shown in FIG. 4, the amount of warpage is represented by a height difference d between a center portion and an end portion caused by warpage when the end face of the optical connector ferrule is viewed from the front.
【００２０】比較例である試作Ｎｏ．１は、反り量が大
きいことが分かる。また、本発明の半芳香族型の液晶ポ
リマーを含む樹脂組成物でも、充填材の充填量が６０重
量％に達しない試作Ｎｏ．２，３，６では、反り量が大
きい。また、マイカを６０重量％とし、充填材の充填量
がガラス繊維と合計して９０重量％である試作Ｎｏ．８
では、粘度が大きくなり、成形ができなかった。これに
対して、充填材の充填量が６０〜８５重量％の範囲で
は、反り量が小さく、実用上十分であることが分かる。
特に、充填材の充填量が７０〜８５重量％の範囲では、
反り量が１μｍ以下である。しかし、充填材の充填量が
８５重量％である試作Ｎｏ．９では、粘度がやや大きか
ったことを考慮すると、充填材の充填量が７０重量％以
上８０重量％以下であれば、成形の際の粘度もさほど大
きくはなく、細かい成形にも十分の流動性があり、反り
も１μｍ以下という良好な光コネクタフェルールを製造
することができ、より好ましいと充填量といえる。The prototype No. which is a comparative example. 1 indicates that the amount of warpage is large. In addition, even in the resin composition containing the semi-aromatic liquid crystal polymer of the present invention, the trial product No. whose filling amount of the filler does not reach 60% by weight. In 2, 3, and 6, the amount of warpage is large. In addition, mica was 60% by weight, and the filling amount of the filler was 90% by weight in total with the glass fiber. 8
In this case, the viscosity increased and molding was not possible. On the other hand, when the filling amount of the filler is in the range of 60 to 85% by weight, the amount of warpage is small, and it can be seen that it is sufficient for practical use.
In particular, when the filling amount of the filler is in the range of 70 to 85% by weight,
The amount of warpage is 1 μm or less. However, when the filling amount of the filler was 85% by weight, the prototype No. In the case of No. 9, considering that the viscosity was rather large, if the filling amount of the filler is 70% by weight or more and 80% by weight or less, the viscosity at the time of molding is not so large, and the fluidity is sufficient for fine molding. A good optical connector ferrule having a warp of 1 μm or less can be manufactured, and more preferable is a filling amount.
【００２１】[0021]
【発明の効果】以上の説明から明らかなように、本発明
によれば、光コネクタフェルールの成形に用いる成形用
樹脂組成物として、少なくとも半芳香族型の液晶ポリマ
ーと充填材を含む樹脂組成物を用いることにより、反り
量が少なく、寸法精度に優れた光コネクタフェルールを
提供することができる。As is apparent from the above description, according to the present invention, a resin composition containing at least a semi-aromatic liquid crystal polymer and a filler is used as a resin composition for molding an optical connector ferrule. By using the optical connector, it is possible to provide an optical connector ferrule with a small amount of warpage and excellent dimensional accuracy.
【００２２】前記樹脂組成物として、無機充填材を６０
重量％以上８５重量％以下含有するものを用いること、
また、無機充填材として、少なくとも、ワラストナイ
ト，タルク，マイカのいずれかを含んでいるものを用い
ることによって、細部の成形もでき、反り量が少なく寸
法精度に優れ、接続損失が充分に小さい光コネクタフェ
ルールを提供することができる。As the resin composition, an inorganic filler is used in an amount of 60.
Using at least 85% by weight or less,
In addition, by using at least one of wollastonite, talc, and mica as the inorganic filler, it is possible to form details, to reduce the amount of warpage, to have excellent dimensional accuracy, and to have a sufficiently small connection loss. An optical connector ferrule can be provided.
【図１】実用化されているＭＴコネクタの説明図であ
る。FIG. 1 is an explanatory diagram of an MT connector that has been put into practical use.
【図２】実用化されているＭＰＯコネクタの説明図であ
る。FIG. 2 is an explanatory view of an MPO connector that is put into practical use.
【図３】試作した光コネクタフェルールの反り量を測定
した結果の説明図である。FIG. 3 is an explanatory diagram of the result of measuring the amount of warpage of a prototype optical connector ferrule.
【図４】反り量の説明図である。FIG. 4 is an explanatory diagram of the amount of warpage.
１０…光ファイバ、１１…光コネクタフェルール、１１
ａ…ガイドピン穴、１２…テープ状光ファイバ心線、１
３…ガイドピン、１４…クリップ、２１…光コネクタフ
ェルール、２１ａ…ガイドピン穴、２２…コネクタプラ
グ、２３…コネクタハウジング、２４…コネクタアダプ
タ。10 optical fiber, 11 optical connector ferrule, 11
a: guide pin hole, 12: tape-shaped optical fiber core, 1
3 ... guide pin, 14 ... clip, 21 ... optical connector ferrule, 21a ... guide pin hole, 22 ... connector plug, 23 ... connector housing, 24 ... connector adapter.
Claims (3)
ための光コネクタフェルールにおいて、該フェルール
が、少なくとも半芳香族型の液晶ポリマーと充填材を含
む樹脂組成物からなることを特徴とする光コネクタフェ
ルール。1. An optical connector ferrule for positioning, fixing and connecting an optical fiber, wherein the ferrule is made of a resin composition containing at least a semi-aromatic liquid crystal polymer and a filler. Ferrule.
量％以上８５重量％以下含有することを特徴とする請求
項１に記載の光コネクタフェルール。2. The optical connector ferrule according to claim 1, wherein the resin composition contains an inorganic filler in an amount of 60% by weight or more and 85% by weight or less.
トナイト，タルク，マイカのいずれかを含んでいること
を特徴とする請求項２に記載の光コネクタフェルール。3. The optical connector ferrule according to claim 2, wherein the inorganic filler contains at least one of wollastonite, talc, and mica.