JPH10175274A - Fire-retardant precious wood decorative sheet and panel - Google Patents

Abstract

PROBLEM TO BE SOLVED: To impart high fire retardancy and to prevent the lowering of bonding force, the generation of corrosion or the reduction of flexibility by forming first and second adhesive resin layers from a resin layer composed of a resin selected from an ethylene/acrylic acid copolymer and an ionomer and adding a fire retardant to the respective layers in a specific wt. ratio. SOLUTION: Precious wood veneer 7, an adhesive layer 6, paper or a nonwoven fabric 5, a first adhesive resin layer 4, aluminum foil or a glass fiber sheet 3, a second adhesive resin layer 2 and paper or a nonwoven fabric 1 are successively laminated downwardly from the surface of a sheet. The first and second adhesive resin layers are independently formed from an ethylene/acrylic acid copolymer or ionomer resin layer and the wt. of them is 18-47g/m<2> and a fire, retardant is added to the first and second adhesive resin layers in a wt. ratio of 5-15%. That is, the content thereof is set to 90-270g/m<2> in a case of 18g/m<2> in the wt. of the adhesive resin layers and to 240-720g/m<2> in a case of 48g/m<2> .

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、化粧単板シートの
難燃化技術の改良に関し、より詳しくは、銘木単板を表
面層とする積層シートが準不燃性能を満たしうるよう
に、難燃化処理を該積層シートに施す技術に関する。従
って、本発明は、かかる難燃化技術が適用された防燃性
銘木化粧シート、および、該防燃性銘木化粧シートが基
材の上に貼着された防燃性銘木化粧板に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an improvement in flame-retarding technology for decorative veneer sheets, and more particularly, to a flame-retardant method in which a laminated sheet having a precious wood veneer as a surface layer can satisfy quasi-non-flammability performance. The present invention relates to a technique for performing a chemical conversion treatment on the laminated sheet. Therefore, the present invention relates to a decorative sheet for a flame-resistant precious wood to which such a flame-retardant technique is applied, and a decorative board for a decorative fire-resistant wood having the decorative sheet for a flame-resistant precious wood stuck on a base material.

【０００２】それゆえ、本発明は、以下に掲げる化粧単
板シートの一般的な用途に利用されうるものである。：
建築内装材例えば壁面材、天井表面材、柱被覆材および
可動間仕切り等の表面材：自動車、船舶の内装製品の表
面材：箪笥等の家具の外面化粧材：什器等の一般木製品
の外面化粧材：並びに電子機器および楽器の外面化粧材
など。Therefore, the present invention can be used for the following general applications of decorative veneer sheets. :
Architectural interior materials, such as wall materials, ceiling surface materials, column covering materials, and movable partitions: Surface materials for interior products of automobiles and ships: Exterior materials for furniture such as wardrobes: Exterior materials for general wood products such as furniture : Exterior decoration materials for electronic devices and musical instruments.

【０００３】[0003]

【従来の技術】天然木資源、特に銘木資源の枯渇によ
り、今日では、無垢木板に代えて、薄肉の突板を紙、不
織布等の繊維質シートで裏打ちした化粧単板シートが、
上記したような用途において、広く使用されている。而
して、出願人は、改良された化粧単板シートとして、特
開昭 61-47250 号公報に開示される製品、即ち銘木単
板；接着剤；クラフト紙、薄葉紙、含浸加工紙等の紙あ
るいは不織布；ポリエチレン層またはポリプロピレン
層；アルミニウム箔または鉄箔；ポリエチレン層または
ポリプロピレン層；クラフト紙、薄葉紙、含浸加工紙等
の紙あるいは不織布という積層構成を有する銘木化粧単
板シートを開発し、そして、これの製造、販売を行なっ
てきた。この銘木化粧単板シートの特徴は、その表面が
銘木単板であって無垢木板と同様の美的価値を維持する
だけでなく、その裏打ち材の積層体の中に一枚の金属箔
を介在させたことにより、曲げ容易な柔軟さを保有する
一方で、十分高い寸法安定性が得られるようにした点に
ある。2. Description of the Related Art Due to the depletion of natural wood resources, especially precious wood resources, decorative veneer sheets in which thin veneers are lined with fibrous sheets such as paper and nonwoven fabrics instead of solid wood boards are nowadays.
It is widely used in the applications described above. Thus, the applicant has proposed, as an improved decorative veneer sheet, a product disclosed in JP-A-61-47250, that is, a nameplate veneer; an adhesive; a paper such as kraft paper, tissue paper, impregnated paper and the like. Or a nonwoven fabric; a polyethylene layer or a polypropylene layer; an aluminum foil or an iron foil; a polyethylene layer or a polypropylene layer; a precious wood decorative veneer sheet having a laminated structure of paper or nonwoven fabric such as kraft paper, tissue paper, impregnated paper, and the like; It has been manufacturing and selling it. The characteristic of this decorative veneer veneer sheet is that the surface is a precious wood veneer and not only maintains the same aesthetic value as a solid wood veneer, but also a sheet of metal foil is interposed in the laminate of the backing material. As a result, while maintaining flexibility that can be easily bent, a sufficiently high dimensional stability is obtained.

【０００４】[0004]

【発明が解決しようとする課題】ところで、木材には火
炎により燃焼し易いという性質があり、この点が従来、
木材製品の欠点となっていた。この事情からか、最近、
化粧単板シートそれ自体について、適当な難燃化、不燃
化処理を施すことが要求され始めてきた。しかし、上述
の銘木化粧単板シートは、特別な難燃化処理が施されて
おらず、不燃性能の面で、改良すべき余地が残されてい
た。By the way, wood has a property that it is easily burned by a flame.
It was a drawback of wood products. From this situation, recently,
It has begun to require that the decorative veneer sheet itself be subjected to appropriate flame retarding and non-flammable treatments. However, the above-mentioned decorative veneer veneer sheet has not been subjected to a special flame-retardant treatment, leaving room for improvement in terms of non-combustibility.

【０００５】一般に、化粧単板シートの難燃化方法とし
ては、まず、突板を燐酸系の難燃剤の液中に含浸処理し
て、突板自体に難燃性を付与する方法が考えられる。し
かし、この方法によると、突板が含浸処理とこれに続く
熱圧接着によって濃褐色に変色する場合が多く、商品価
値のある程度の低下が避けられないという欠点がある。
また、難燃化のために考えられる別の方法としては、化
粧単板シートの内部層に使用される紙や不織布等を難燃
剤の添加により難燃化処理する方法がある。しかし、紙
や不織布等について燐酸系難燃剤等の添加により自消性
を付与せしめるには、該難燃剤を重量比で約４０〜５０
％の量添加する必要があり、このため、難燃化された紙
や不織布等は吸湿性が増大し、従って、化粧単板シート
の製造過程において、その紙、不織布等と突板または他
の層材料との接着性が悪くなり、特にホットメルト接着
剤を用いて圧着成形する過程で剥離が起きる等、製造不
良の発生を招くという問題があった。さらに、別の難燃
化方法としては、難燃剤を化粧単板シートの中の樹脂層
に配合するという方法が考えられる。この種の樹脂層は
普通、化粧単板シートそれ自体に可撓性や柔軟性等を付
与するために、あるいは、化粧単板シートを構成する各
要素（紙、アルミニウム箔など）間の接着一体化を図る
ために、積層要素の一つとされるものである。In general, as a method for making a decorative veneer sheet flame-retardant, first, a method of impregnating a veneer with a phosphoric acid-based flame retardant liquid to impart flame retardancy to the veneer itself can be considered. However, according to this method, the veneer often changes its color to dark brown due to the impregnation treatment and the subsequent hot-press bonding, so that there is a disadvantage that a certain reduction in commercial value cannot be avoided.
Further, as another method that can be considered for flame retardation, there is a method in which paper or nonwoven fabric used for the inner layer of the decorative veneer sheet is subjected to flame retardation treatment by adding a flame retardant. However, in order to impart self-extinguishing property to paper or nonwoven fabric by adding a phosphoric acid-based flame retardant, the flame retardant is added in a weight ratio of about 40 to 50.
%, The flame-retarded paper or nonwoven fabric has an increased hygroscopic property. Therefore, in the process of manufacturing a decorative veneer sheet, the paper, nonwoven fabric or the like and the veneer or other layer are added. There has been a problem in that the adhesiveness to the material is deteriorated, and in particular, peeling occurs in the process of pressure bonding using a hot-melt adhesive, thereby causing defective production. Further, as another flame retarding method, a method of blending a flame retardant into the resin layer in the decorative veneer sheet can be considered. This type of resin layer is usually used to provide flexibility and flexibility to the veneer veneer sheet itself, or to bond together the elements (paper, aluminum foil, etc.) that make up the veneer veneer sheet. It is considered as one of the laminated elements in order to achieve the realization.

【０００６】本発明者は、上記の方法について、表面層
が銘木単板であって一枚の金属箔が裏打ち材の中に介在
する構成の化粧単板シートを対象として、さらに研究を
進めたところ、難燃剤を化粧単板シート中の樹脂層に単
に添加しただけでは、難燃性は当然に改良されて、より
高まるが、その反面、化粧単板シートの各要素間の接着
力、特にアルミニウム箔と紙または不織布との間の接着
力が低下し、また化粧単板シート中の金属箔について腐
食の発生が起き、さらに化粧単板シート全体の柔軟性、
曲げ適性が悪くなる等、諸性能の問題となる低下がみら
れるという事実を見い出し、従って、難燃性以外の諸性
能も総じて良好なものにする観点より、添加される難燃
剤の配合量には、一定の限界が存在するという結果を得
た。さらに、本発明者は、上記の研究の中で、難燃剤が
配合された化粧単板シートが不燃・準不燃の性能を満た
しうるかどうかは、アルミニウム箔の重量（厚さ）だけ
でなく、難燃剤が添加される樹脂層の重量にも大きく関
係していること、並びに、難燃剤の配合に伴う化粧単板
シートの層間接着力の低下は、難燃剤が添加される樹脂
層の種類に依存することを確認した。また、上記の難燃
剤配合の化粧単板シートにおいて、不燃材としてアルミ
ニウム箔の代わりにガラス繊維不織布等を採用した構成
とすることも可能であると考えられる。The present inventor has further studied the above-mentioned method for a decorative veneer sheet in which the surface layer is a precious wood veneer and one metal foil is interposed in the backing material. However, by simply adding a flame retardant to the resin layer in the decorative veneer sheet, the flame retardancy is naturally improved and increased, but on the other hand, the adhesive force between the elements of the decorative veneer sheet, especially The adhesive force between the aluminum foil and the paper or nonwoven fabric is reduced, and corrosion occurs on the metal foil in the decorative veneer sheet, and further, the flexibility of the decorative veneer sheet as a whole,
It has been found that there is a decrease in performance that causes problems such as poor bending aptitude.Therefore, from the viewpoint of improving overall performance other than flame retardancy, the amount of the added flame retardant is reduced. Obtained that certain limits exist. Furthermore, the present inventor has determined that, in the above research, whether a decorative veneer sheet containing a flame retardant can satisfy non-combustible / quasi-incombustible performance not only depends on the weight (thickness) of the aluminum foil but also on the difficulty. The fact that the weight of the resin layer to which the flame retardant is added is greatly related to the weight of the resin layer to which the flame retardant is added. Make sure you do. Further, it is considered that the decorative veneer sheet containing the above-described flame retardant may have a configuration in which a glass fiber nonwoven fabric or the like is employed as the non-combustible material instead of the aluminum foil.

【０００７】従って、本発明の目的は、積層体の表面が
銘木単板であって一枚のアルミニウム箔等の不燃材が裏
打ち材の中に介在する構成の化粧単板シートについて、
高い難燃性を有し、防火材料における準不燃の性能を達
成することができるところの防燃性銘木化粧シートを提
供することにある。また、他の側面において、本発明の
目的は、難燃剤の含有による層間接着力の低下、腐食の
発生等の性能の悪化をひき起こさず、準不燃性能の他、
機械的性質（柔軟性、強度など）および耐腐食性等に関
して満足な性能を有し、建築材料として大変優れるとこ
ろの防燃性銘木化粧シートを提供することでもある。さ
らに、別の側面において、本発明の目的は、従来の難燃
化処理を施した化粧単板シートにおける種々の欠点が起
きないところの防燃性銘木化粧シートを提供することで
もある。また、本発明の他の目的は、かかる防燃性銘木
化粧シートを表面材とする化粧板であって、上記と同様
の性能を有する、防燃性銘木化粧板を提供することにあ
る。[0007] Accordingly, an object of the present invention is to provide a decorative veneer sheet having a structure in which the surface of the laminate is a precious wood veneer and a single non-combustible material such as aluminum foil is interposed in the backing material.
It is an object of the present invention to provide a flame-resistant precious wood decorative sheet having high flame retardancy and capable of achieving a quasi-incombustible performance of a fire protection material. In another aspect, the object of the present invention is to reduce the interlayer adhesion due to the inclusion of a flame retardant, without causing deterioration in performance such as occurrence of corrosion, in addition to quasi-nonflammability,
Another object of the present invention is to provide a fireproof precious wood decorative sheet having satisfactory performance in mechanical properties (flexibility, strength, etc.), corrosion resistance, and the like, and being very excellent as a building material. Further, in another aspect, an object of the present invention is to provide a flame-resistant precious wood decorative sheet which does not cause various disadvantages in a conventional veneer-treated decorative veneer sheet. Another object of the present invention is to provide a decorative board using the decorative sheet for a fireproof nameplate as a surface material and having the same performance as described above.

【０００８】[0008]

【課題を解決するための手段】本発明は、積層体の表面
が銘木単板であって一枚の不燃材（アルミニウム箔また
はガラス繊維シート）が裏打ち材の中に介在する構成の
化粧単板シートについて、不燃材の上下両側の層として
特定の接着性樹脂層を採用し、かつ、一定量の難燃剤を
これら両層の接着性樹脂層にそれぞれ配合することによ
り、準不燃性能を満たす程に難燃性の著しい改良を図
り、併せて、機械的性質等との調和並びに最適化を図っ
たものである。より明確には、本発明は、銘木単板；接
着剤層；紙または不織布；第１の接着性樹脂層；アルミ
ニウム箔またはガラス繊維シート；第２の接着性樹脂
層；紙または不織布がシート表面より下方へ順に積層さ
れ、一体に圧着成形されてなる化粧単板シートであっ
て、前記第１の接着性樹脂層および第２の接着性樹脂層
は、エチレン−アクリル酸共重合体（ＥＡＡ）およびア
イオノマーからなる群より各々独立に選択された樹脂層
より成り、かつ、難燃剤が該第１の接着性樹脂層および
第２の接着性樹脂層の各層にそれぞれ、重量比で５％な
いし１５％の量含有されていることを特徴とする防燃性
銘木化粧シートに関する。また、本発明は、上記の防燃
性銘木化粧シートが、木質系、無機質系または金属系基
材の上に貼着されている防燃性銘木化粧板にも関する。SUMMARY OF THE INVENTION The present invention provides a decorative veneer in which the surface of a laminate is a precious wood veneer and one noncombustible material (aluminum foil or glass fiber sheet) is interposed in a backing material. For the sheet, a specific adhesive resin layer is used as the upper and lower layers of the non-combustible material, and a certain amount of flame retardant is blended into each of these adhesive resin layers to satisfy the quasi-noncombustible performance. In addition, the flame retardancy has been remarkably improved, and at the same time, harmony and optimization with mechanical properties and the like have been achieved. More specifically, the present invention relates to a veneer veneer; an adhesive layer; a paper or nonwoven fabric; a first adhesive resin layer; an aluminum foil or fiberglass sheet; a second adhesive resin layer; A decorative veneer sheet laminated in a lower order and integrally press-molded, wherein the first adhesive resin layer and the second adhesive resin layer are ethylene-acrylic acid copolymer (EAA) And a resin layer independently selected from the group consisting of an ionomer and a flame retardant added to each of the first adhesive resin layer and the second adhesive resin layer in a weight ratio of 5% to 15%. %. The present invention also relates to a decorative board made of a flame-resistant precious wood, in which the above-mentioned decorative sheet for a fire-proof precious wood is stuck on a wood-based, inorganic-based or metal-based substrate.

【０００９】本発明者は、上述の研究の中で、銘木単板
（重量４０ないし１５０ｇ／ｍ² ）を表面層とする化粧
単板シートの裏打ち材の中核として重量２７ないし８２
ｇ／ｍ² （厚さ１０ないし３０μｍ）のアルミニウム箔
または重量１０ないし４０ｇ／ｍ² のガラス繊維シート
を使用し、かつ、それら表裏両面に接着性樹脂層（エチ
レン−アクリル酸共重合体（ＥＡＡ）またはアイオノマ
ーよりなる）をそれぞれ１８ないし４７ｇ／ｍ² の重量
（２０ないし５０μｍの厚さ）で積層し、そして、難燃
剤を２層の該接着性樹脂層にそれぞれ、重量比で５％な
いし１５％の範囲で添加することにより、得られる防燃
性化粧単板シートは、大変高い難燃性を有し法定の準不
燃の性能を満たすのは勿論のこと、シートの層間接着力
も満足な高水準であり、化粧単板シートとして適度の可
撓性、柔軟性を有し、さらに、難燃剤の含有にも拘ら
ず、腐食の発生が抑制される等、種々の利点に優れたも
のとなり、従って、かかる条件では、それら性能諸々が
最適化されるという事実を見出した。したがって、本発
明の最も好ましい態様は、重量４０ないし１５０ｇ／ｍ
² の銘木単板；接着剤層；重量２０ないし５０ｇ／ｍ²
の紙または不織布；重量１８ないし４７ｇ／ｍ² の第１
の接着性樹脂層；重量２７ないし８２ｇ／ｍ² のアルミ
ニウム箔または重量１０ないし４０ｇ／ｍ² のガラス繊
維シート；重量１８ないし４７ｇ／ｍ² の第２の接着性
樹脂層；重量２０ないし５０ｇ／ｍ² の紙または不織布
がシート表面より下方へ順に積層され、一体に圧着成形
されてなる化粧単板シートであって、前記第１の接着性
樹脂層および第２の接着性樹脂層は各々独立してエチレ
ン−アクリル酸共重合体（ＥＡＡ）またはアイオノマー
の樹脂層より成り、かつ、難燃剤が該第１および第２の
接着性樹脂層の各層にそれぞれ重量比で５％ないし１５
％の量含有されているところの防燃性銘木化粧シート、
並びに、該防燃性銘木化粧シートが木質系、無機質系ま
たは金属系基材の上に貼着されている防燃性銘木化粧板
に関する。In the above-mentioned research, the inventor of the present invention has found that the core of the backing material for decorative veneer sheets having a surface layer of a veneer veneer (weight 40 to 150 g / m ² ) has a weight of 27 to 82.
g / m ² (thickness of 10 to 30 μm) or a glass fiber sheet weighing 10 to 40 g / m ² , and an adhesive resin layer (ethylene-acrylic acid copolymer (EAA) ) Or ionomer) at a weight of 18 to 47 g / m ² (thickness of 20 to 50 μm), respectively, and a flame retardant is added to each of the two adhesive resin layers in a weight ratio of 5% to 5%. By adding in the range of 15%, the resulting fire-resistant decorative veneer sheet has extremely high flame retardancy and satisfies the statutory quasi-nonflammability performance, and also satisfies the interlayer adhesion of the sheet. It has excellent flexibility and flexibility as a veneer veneer sheet, and is excellent in various advantages such as suppressing the occurrence of corrosion despite containing a flame retardant. And therefore In that condition, they performance various have found the fact that is optimized. Therefore, the most preferred embodiment of the present invention is that the weight is between 40 and 150 g / m2.
² precious wood veneer; adhesive layer; weight 20 to 50 g / m ²
Paper or non-woven fabric; first weight 18 to 47 g / m ²
Aluminum foil weighing 27 to 82 g / m ² or glass fiber sheet weighing 10 to 40 g / m ² ; second adhesive resin layer weighing 18 to 47 g / m ² ; weight 20 to 50 g / m ² of paper or non-woven fabric are laminated in this order downward from the sheet surface, a decorative veneer sheet formed by bonding formed integrally, the first adhesive resin layer and a second adhesive resin layer are each independently And a resin layer of ethylene-acrylic acid copolymer (EAA) or ionomer, and a flame retardant is added to each of the first and second adhesive resin layers in a weight ratio of 5% to 15%.
% Of flame-retardant precious wood decorative sheets,
In addition, the present invention relates to a decorative board made of a flame-retardant precious wood, wherein the decorative sheet of the fire-proof precious wood is adhered on a wood-based, inorganic-based or metal-based substrate.

【００１０】[0010]

【発明の実施の形態】本発明の特徴は、化粧単板シート
全体をより高く防燃化するために、難燃剤が配合された
二つの接着性樹脂層を不燃材のアルミニウム箔またはガ
ラス繊維シートの両側にそれぞれ介在させた積層物を、
銘木単板の裏打ち材として備えた構成としたことにあ
る。難燃剤は、二つの接着性樹脂層、つまり第１および
第２の接着性樹脂層の双方にそれぞれ、重量比で５％な
いし１５％の量含有される。本発明で用いうる難燃剤に
は、三酸化アンチモン、燐酸系、ハロゲン系のものが挙
げられる。本発明の化粧シートおよび化粧板は、かかる
構成により、昭和５９年９月２９日建設省告示第１３７
２号に基づく表面試験（加熱試験）において防火材料と
して準不燃の性能を満足することができる。さらに、本
発明では、難燃剤を銘木化粧シート内の接着性樹脂層の
中に配合したので、従来技術で見られた種々の不都合お
よび欠点が生じなくなる。すなわち、化粧シート表面の
銘木単板を難燃化処理する必要が無くなるので、その処
理によって従来生じる場合があった単板の変色という問
題が全く起きなくなる。また、化粧シート内で単板直下
の紙または不織布等を難燃化処理する必要も無くなるの
で、従来その処理によりみられた単板と紙等との間の接
着性不良という問題も生じなくなる。さらに、難燃剤に
は、燐酸系を含め、広範囲のものが適用し得るという利
点もある。DESCRIPTION OF THE PREFERRED EMBODIMENTS The feature of the present invention is that in order to make the whole decorative veneer sheet more highly flame-retardant, two adhesive resin layers containing a flame retardant are coated with a non-combustible aluminum foil or glass fiber sheet. The laminates interposed on both sides of the
This is due to the structure provided as a backing material for precious wood veneers. The flame retardant is contained in each of the two adhesive resin layers, that is, both the first and second adhesive resin layers, in an amount of 5% to 15% by weight. Examples of the flame retardant that can be used in the present invention include antimony trioxide, phosphoric acid type, and halogen type. The decorative sheet and the decorative plate of the present invention have the above-mentioned configuration, and are notified by the Ministry of Construction No. 137 of September 29, 1984.
In the surface test (heating test) based on No. 2, it can satisfy the quasi-nonflammable performance as a fireproof material. Furthermore, in the present invention, since the flame retardant is blended in the adhesive resin layer in the nameplate decorative sheet, various disadvantages and disadvantages found in the prior art are not caused. That is, since it is not necessary to perform the flame retarding treatment on the precious wood veneer on the surface of the decorative sheet, the problem of discoloration of the veneer which has conventionally occurred due to the treatment does not occur. Further, since it is not necessary to perform a flame-retardant treatment on the paper or non-woven fabric immediately below the veneer in the decorative sheet, the problem of poor adhesion between the veneer and the paper, which is conventionally observed by the treatment, does not occur. Further, there is an advantage that a wide range of flame retardants, including phosphoric acid-based ones, can be applied.

【００１１】本発明は、単に、難燃剤の配合によって化
粧単板シートの難燃化を図ったものではない。本発明
は、表面が銘木単板であって一枚の不燃材がその裏打ち
材の中に介在する構成の化粧単板シートを対象として、
その防燃化、具体的には、防火材料における準不燃性能
の達成を図ったものである。一般に、化粧単板シートの
難燃性をより一層高めるには、より多量の難燃剤を化粧
単板シートの積層要素、例えばその中の樹脂層に含有す
ればよいと考えられる。しかし、難燃剤の多量配合は、
化粧単板シートの各要素間の接着力を著しく弱め、ひど
いときには、同シートの各要素が容易に層間剥離しうる
ものにし、積層構造を維持できなくする。また、難燃剤
の多量配合は、化粧単板シート中のアルミニウム箔の腐
食をも促進する。ここで、特に考慮すべきことは、難燃
剤の配合に伴う化粧単板シートの各要素間の接着力の低
下は、難燃剤が添加される樹脂層の種類に依って著しく
異なるという点である。樹脂層がこの種の化粧単板シー
トで従来より慣用されているポリエチレン層またはポリ
プロピレン層である場合、化粧単板シートの各要素間の
接着力は、難燃剤の配合により、急激に低下する。難燃
剤を僅か５重量％配合しただけで、常態での接着力は難
燃剤未配合の場合と比べてほぼ半減し、さらに難燃剤を
配合すると、難燃剤配合の樹脂層と紙・不織布との間で
剥離が起きやすくなる。高温高湿の雰囲気下に放置する
と、その剥離はますます容易になり、場合によっては、
化粧単板シートは、何の力を加えずとも、積層構造それ
自体を維持することができなくなる。従って、難燃剤を
配合する樹脂層としてポリエチレン層あるいはポリプロ
ピレン層を採用したのでは、法定の準不燃性能を達成す
る以前に、化粧単板シートとしての物理的な構成それ自
体を満足に備えることが難しくなる。本発明は、化粧単
板シート中の樹脂層として、エチレン−アクリル酸共重
合体（ＥＡＡ）およびアイオノマーからなる群より各々
独立に選択された接着性樹脂を適用することにより、上
述の不都合を改善したものである。すなわち、本発明
は、これら特定の接着性樹脂の適用により、準不燃性能
を満たす程の大変高い難燃性を達成できるとともに、化
粧単板シートの層間接着力をも十分高い水準で維持でき
るようにしたものである。[0011] The present invention is not merely intended to make the decorative veneer sheet flame-retardant by adding a flame retardant. The present invention is directed to a decorative veneer sheet in which the surface is a precious wood veneer and one incombustible material is interposed in the backing material.
It is intended to achieve the flameproofing, specifically, the quasi-nonflammable performance of the fireproofing material. Generally, in order to further enhance the flame retardancy of a decorative veneer sheet, it is considered that a larger amount of a flame retardant should be contained in a laminated element of the decorative veneer sheet, for example, a resin layer therein. However, large amounts of flame retardants
The adhesive strength between the components of the decorative veneer sheet is significantly reduced, and in severe cases, the components of the sheet can be easily delaminated, and the laminated structure cannot be maintained. Also, the large amount of the flame retardant promotes the corrosion of the aluminum foil in the decorative veneer sheet. Here, what should be particularly considered is that the decrease in the adhesive force between the components of the decorative veneer sheet due to the blending of the flame retardant is significantly different depending on the type of the resin layer to which the flame retardant is added. . When the resin layer is a polyethylene veneer or a polypropylene layer conventionally used in this type of veneer veneer sheet, the adhesive strength between the components of the veneer veneer sheet rapidly decreases due to the incorporation of the flame retardant. Even when only 5% by weight of the flame retardant is blended, the adhesive strength in the normal state is almost halved compared to the case where the flame retardant is not blended. Separation easily occurs between them. When left in a high-temperature, high-humidity atmosphere, the peeling becomes even easier, and in some cases,
The decorative veneer sheet cannot maintain the laminated structure itself without any force. Therefore, if a polyethylene layer or a polypropylene layer is adopted as the resin layer containing the flame retardant, the physical configuration itself as a decorative veneer sheet must be satisfied before achieving the legal quasi-nonflammability performance. It becomes difficult. The present invention solves the above-mentioned disadvantages by applying, as a resin layer in a decorative veneer sheet, an adhesive resin independently selected from the group consisting of an ethylene-acrylic acid copolymer (EAA) and an ionomer. It was done. That is, according to the present invention, by applying these specific adhesive resins, it is possible to achieve a very high flame retardancy that satisfies the quasi-nonflammable performance, and to maintain the interlayer adhesive force of the decorative veneer sheet at a sufficiently high level. It was made.

【００１２】上記の第１および第２の接着性樹脂層は、
それぞれ、次のような機能を果たすものである。 (a) 接着力が高い故、化粧単板シート中の不燃材と紙・
不織布との接着一体化を可能にする。 (b) 不燃材（アルミニウム箔）を含む積層構造におい
て、外気中の水分は表面層の紙・不織布より浸入し、次
いでアルミニウム箔にまで移行し、よってアルミニウム
箔の腐食が発生する。樹脂層がアルミニウム箔の両側を
被覆するように介在することにより、水分の移行が遮断
され、従ってアルミニウム箔の腐食の発生を防止するこ
とができる。 (c) 樹脂層は柔軟性が高いことから、これを化粧単板シ
ートの積層要素とすることにより、化粧単板シートに適
度の柔軟性を付与して施工時下地の凹凸を吸収するとと
もに、該シート自体に適度の可撓性および曲げ適性（曲
げたとき、単板が割れず、木目が拡張する性質）を付与
し、曲げ加工を容易にする。 (d) さらに、不燃材と一緒になって、突板のあばれ、反
りを抑える。一般に、上記(a) 〜(d) の性能は、接着性
樹脂層への難燃剤の配合により悪化し、特に接着力の低
下並びにアルミニウム箔の腐食発生は顕著になる。本発
明は、接着性樹脂層としてエチレン−アクリル酸共重合
体（ＥＡＡ）およびアイオノマーからなる群より各々独
立に選択された樹脂層を適用することにより、上記(a)
〜(d) の性能の悪化を極力抑止したものである。なお、
この限定事項は、従来より樹脂層として慣用されるポリ
エチレンまたはポリプロピレン層を使用した化粧単板シ
ートにおいては、上記の性能の悪化が著しいが、上記群
の接着性樹脂層を使用した化粧単板シートにおいては、
その悪化の進行が大変遅いという本発明者による新規な
知見に基づくものである。また、本発明で用いる第１お
よび第２の接着性樹脂層は、同種であっても異種であっ
ても、また各樹脂層は単層であっても複層であってもよ
い。[0012] The first and second adhesive resin layers are
Each performs the following functions. (a) Due to high adhesive strength, non-combustible material in decorative veneer sheet and paper /
Enables integrated bonding with non-woven fabric. (b) In a laminated structure including a non-combustible material (aluminum foil), moisture in the outside air penetrates from the paper or nonwoven fabric of the surface layer, and then migrates to the aluminum foil, thereby causing corrosion of the aluminum foil. By interposing the resin layer so as to cover both sides of the aluminum foil, the transfer of moisture is blocked, so that the occurrence of corrosion of the aluminum foil can be prevented. (c) Since the resin layer has high flexibility, by using this as a laminated element of the decorative veneer sheet, the decorative veneer sheet is given appropriate flexibility to absorb the unevenness of the base during construction, The sheet itself is provided with appropriate flexibility and bendability (the property that the veneer does not crack and the grain expands when bent), and facilitates bending. (d) Further, together with the non-combustible material, the vulcanized board is prevented from being warped or warped. In general, the above-mentioned properties (a) to (d) are deteriorated by the incorporation of a flame retardant into the adhesive resin layer, and in particular, the adhesive strength and the corrosion of the aluminum foil become remarkable. The present invention provides the above (a) by applying a resin layer independently selected from the group consisting of an ethylene-acrylic acid copolymer (EAA) and an ionomer as the adhesive resin layer.
(D) performance deterioration was suppressed as much as possible. In addition,
This limitation is that the decorative veneer sheet using a polyethylene or polypropylene layer conventionally used as a resin layer, the above-mentioned performance is significantly deteriorated, but the decorative veneer sheet using the adhesive resin layer of the above group. In
This is based on a novel finding by the present inventors that the progress of the deterioration is very slow. Further, the first and second adhesive resin layers used in the present invention may be the same or different, and each resin layer may be a single layer or a multilayer.

【００１３】不燃材のアルミニウム箔は、化粧単板シー
トに適度の剛性を持たせて突板の寸法変化、あばれ、反
りを抑えるために、また化粧単板シートに高い寸法安定
性を付与するために、積層要素とされるものである。な
お、本発明において、アルミニウム箔とは、アルミニウ
ムの純金属またはその合金の総てを指す。また、ガラス
繊維シートとは、例えばガラス繊維不織布よりなるシー
ト材である。ガラス繊維シートは、適度の強度を化粧単
板シートに与える他、銘木単板のあばれ、反りを抑え、
高い寸法安定性を化粧単板シートに付与せしめるため
に、その積層要素とされた不燃材である。従って、ガラ
ス繊維シートが介在する本発明の銘木化粧シートは、不
燃性に優れるだけでなく、強度、寸法安定性、電気絶縁
性、耐腐食性さらに耐薬品性の面でも良好なものにな
る。本発明で用いうるガラス繊維シートとしては、市販
のガラス繊維不織布、例えばグラスパー ＧＨＮ−２５
（王子製紙株式会社製、坪量２５ｇ／ｍ² ）、グラスパ
ー ＧＨＮ−２５ＧＳ（王子製紙株式会社製、坪量２５
ｇ／ｍ² ）およびグラベスト ＦＢＰ ０２５（オリベ
スト株式会社製、坪量２５ｇ／ｍ² ）が挙げられる。The non-combustible aluminum foil is used to give the decorative veneer sheet an appropriate rigidity to suppress the dimensional change, warping, and warpage of the veneer sheet, and to provide the decorative veneer sheet with high dimensional stability. , And a laminated element. In the present invention, the term “aluminum foil” refers to all pure metals or alloys of aluminum. Further, the glass fiber sheet is a sheet material made of, for example, a glass fiber nonwoven fabric. The glass fiber sheet gives moderate strength to the veneer veneer sheet, and also suppresses the unwinding and warping of the veneer veneer sheet.
It is a non-combustible material used as a laminated element in order to impart high dimensional stability to decorative veneer sheets. Therefore, the decorative wood decorative sheet of the present invention in which the glass fiber sheet is interposed has not only excellent nonflammability but also good strength, dimensional stability, electrical insulation, corrosion resistance and chemical resistance. As the glass fiber sheet that can be used in the present invention, a commercially available glass fiber nonwoven fabric, for example, Grasper GHN-25
(Oji Paper Co., Ltd., basis weight 25 g / m ² ), Grasper GHN-25GS (Oji Paper Co., Ltd., basis weight 25)
g / m ² ) and Gravest FBP 025 (manufactured by Olivet Co., Ltd., basis weight 25 g / m ² ).

【００１４】また、考慮すべきことは、上記の接着性樹
脂層を不燃材の両側に各々積層した構成の化粧単板シー
トが、難燃剤を配合したとき、昭和５９年９月２９日建
設省告示第１３７２号に基づく表面試験［加熱試験］に
おいて防火材料における準不燃性能を有するものになる
かどうかは、難燃剤が添加される接着性樹脂層の重量
（厚さ）並びに不燃材の重量（厚さ）とも密接に関係し
ている点である。難燃剤が二つの接着性樹脂層にそれぞ
れ配合された上記の化粧単板シートにおいて、接着性樹
脂層の重量をしだいに増加したとき、その重量が約３８
ｇ／ｍ²（つまり厚さ約４０μｍ）までは十分満足な難
燃性が確保されるが、それより増大すると、難燃剤の配
合量が相当に増えるにも拘らず、難燃性が低下し始め、
接着性樹脂層の重量が４７ｇ／ｍ² （厚さ５０μｍ）を
越すと、上記の準不燃の性能を確保できなくなる。他
方、接着性樹脂層の重量が約１８ｇ／ｍ² （厚さ約２０
μｍ）であっても、高い難燃性が得られ、上記の準不燃
性能を確保することができるが、それよりも減少する
と、添加される難燃剤の総量が減少して難燃性が低下す
るだけでなく、化粧単板シート全体に十分な柔軟性を付
与できなくなる。かかる観点より、本発明のより好まし
い態様は、第１の接着性樹脂層および第２の接着性樹脂
層の重量がそれぞれ１８ないし４７ｇ／ｍ² の範囲内
（厚さ２０ないし５０μｍの範囲内）であるときであ
る。また、不燃材のうち、アルミニウム箔の重量に関し
ては、その重量が２７ｇ／ｍ² （つまり厚さ１０μｍ）
もあれば、アルミニウム箔は上記の準不燃性能を達成で
きる程の高い不燃化作用を発揮することができる。しか
しながら、アルミニウム箔の重量が８２ｇ／ｍ² （厚さ
３０μｍ）を越すと、化粧単板シートは、可撓性が極度
に悪くなり、曲げ加工しにくい剛直なシートとなり、表
面化粧材として不向きな製品となる。そこで、本発明の
より好ましい態様は、アルミニウム箔の重量が２７ない
し８２ｇ／ｍ² の範囲内（厚さ１０μｍないし３０μｍ
の範囲内）であるときである。また、ガラス繊維シート
の重量に関しては、その重量がおよそ１０ｇ／ｍ² もあ
れば、ガラス繊維シートは上記の準不燃性能を達成でき
る程の高い不燃化作用を発揮することができる。しか
し、ガラス繊維シートの重量が４０ｇ／ｍ² を越すと、
化粧単板シートは、可撓性が極度に悪くなり、曲げ加工
しにくい剛直なシートとなり、表面化粧材として不向き
な製品となる。そこで、本発明のより好ましい態様は、
ガラス繊維シートの重量が１０ないし４０ｇ／ｍ² の範
囲内であるときである。本発明者は、各々上記の範囲の
厚さを有する、上記の特定の接着性樹脂層および不燃材
（アルミニウム箔）を採用した場合において、化粧単板
シートの各要素間の接着力およびアルミニウム箔の腐食
等が問題とならない条件の下、難燃剤は２つの接着性樹
脂層にそれぞれ１５重量％まで配合することができ、か
つ、そのような難燃剤の高配合により、防火材料におけ
る準不燃性能を満たす高い難燃性を達成できることを確
認したのである。而して、上述した本発明のより好まし
い態様は、本発明者によるこの新しい知見に基づき、完
成している。Also, what should be taken into consideration is that when a decorative veneer sheet having the above-mentioned adhesive resin layer laminated on both sides of a non-combustible material is blended with a flame retardant, on September 29, 1984, the Ministry of Construction In the surface test [heating test] based on the notification No. 1372, whether or not the fire-resistant material has the quasi-nonflammability performance depends on the weight (thickness) of the adhesive resin layer to which the flame retardant is added and the weight of the nonflammable material ( Thickness). In the decorative veneer sheet in which the flame retardant is blended into the two adhesive resin layers, when the weight of the adhesive resin layer is gradually increased, the weight becomes about 38.
g / m ² (i.e., a thickness of about 40 μm), a sufficiently satisfactory flame retardancy is ensured. However, when the flame retardancy is increased, the flame retardancy is reduced despite the considerable increase in the amount of the flame retardant. start,
If the weight of the adhesive resin layer exceeds 47 g / m ² (thickness: 50 μm), the above-mentioned quasi-noncombustibility cannot be secured. On the other hand, the weight of the adhesive resin layer is about 18 g / m ² (thickness of about 20 g / m ² ).
μm), high flame retardancy can be obtained and the above quasi-nonflammability can be ensured. However, when the flame retardancy is less than that, the total amount of the added flame retardant decreases and the flame retardancy decreases. In addition, sufficient flexibility cannot be imparted to the entire decorative veneer sheet. From this viewpoint, a more preferred embodiment of the present invention is that the first adhesive resin layer and the second adhesive resin layer each have a weight of 18 to 47 g / m ² (with a thickness of 20 to 50 μm). It is when. Among the non-combustible materials, the weight of the aluminum foil is 27 g / m ² (that is, the thickness is 10 μm).
If there is, the aluminum foil can exhibit a high non-combustible action enough to achieve the above quasi-noncombustible performance. However, if the weight of the aluminum foil exceeds 82 g / m ² (thickness: 30 μm), the decorative veneer sheet has extremely poor flexibility, becomes a rigid sheet that is difficult to bend, and is not suitable as a surface decorative material. Product. Therefore, a more preferred embodiment of the present invention is that the weight of the aluminum foil is in the range of 27 to 82 g / m ² (thickness of 10 μm to 30 μm
). Further, as for the weight of the glass fiber sheet, if the weight is about 10 g / m ² , the glass fiber sheet can exhibit a high non-combustibility effect capable of achieving the above-described quasi-noncombustibility performance. However, when the weight of the glass fiber sheet exceeds 40 g / m ² ,
The decorative veneer sheet has extremely poor flexibility, is a rigid sheet that is difficult to bend, and is not suitable as a surface decorative material. Therefore, a more preferred embodiment of the present invention is:
This is when the weight of the glass fiber sheet is in the range of 10 to 40 g / m ² . The inventor of the present invention, when employing the above-mentioned specific adhesive resin layer and non-combustible material (aluminum foil) each having a thickness in the above-mentioned range, has an adhesive force between each element of the decorative veneer sheet and an aluminum foil. The flame retardant can be added to each of the two adhesive resin layers in an amount of up to 15% by weight under conditions that do not cause a problem such as corrosion of the material. It has been confirmed that high flame retardancy satisfying the above can be achieved. Thus, the above-described more preferable aspects of the present invention have been completed based on this new finding by the present inventors.

【００１５】本発明において用いる紙または不織布は、
下地の凹凸を緩衝して化粧シートの浮き上がりを防止す
るために、また内側のアルミニウム箔およびガラス繊維
シートの輝きを隠蔽するために、積層要素とされるもの
である。本発明で用いる紙または不織布には、和紙、洋
紙（上質紙、中質紙等）、クラフト紙、薄葉紙または樹
脂含浸紙、並びに、ポリエチレン不織布、ポリエステル
／パルプ不織布等の各種不織布など、すべての繊維質シ
ートが包含される。紙または不織布の坪量は、１５〜１
００ g/m² 、好ましくは２０〜５０ g/m² である。ま
た、本発明において、銘木単板としては、各種の銘木よ
り、例えば０．０５ないし３．０mmの厚さに、好ましく
は０．１０ないし０．４mmの厚さに、切削加工された挽
板または突板を適用することができる。銘木単板の木理
は、特に限定されず、柾目、追柾、板目またはこぶ杢な
ど、いずれでもよい。また、銘木単板の樹種も特には、
限定されないが、好ましい樹種の例は、次の通りであ
る。：檜、楢、欅、桜、楡、黒柿、栃、桂、楓、槐、楠
木等：ローズウッド、チーク、マホガニー、コクタン
（黒壇）、シタン（紫檀）、バーズアイメープル、アメ
リカンブラックウォールナット、クラロウォールナッ
ト、ラテヌォールナット、クィンスランドウォールナッ
ト、ゼブラウッド、マンガシロ、ブラジリアンローズ、
カリン（花梨）、バーシモン、シルバーローズ、パル
マ、レッドウッド、パープルウッド、シルキーオーク、
タイワンクス、チェリー、マグノリヤ、黒レオ（ダ
オ）、白レオ、サベリ、ブビンカ、マコレ、マドローナ
ー、ミルトル、メープル、アッシン、インブイヤー等。
接着剤層は、銘木単板と紙または不織布とを接着するた
めに、積層要素とされる。単板と紙または不織布との接
着が比較的容易であるため、本発明において使用される
接着剤の種類は特に限定されないが、例えば、エチレン
酢酸ビニル樹脂（ＥＶＡ）接着剤、酢酸ビニル−アクリ
ル共重合体接着剤、水性ビニルウレタン系接着剤、また
はアクリル系粘着剤などが有利に利用することができ
る。また、本発明における防燃性銘木化粧板は、上述の
各要素より成る防燃性銘木化粧シートを表面材とし、こ
れを厚肉の基材の上に貼着してなるものであるが、かか
る基材としては、有利には、木質系の基材（例えば、合
板、ＭＤＦ、パーティクルボードハニカムボード等）、
無機質系の基材（例えば、石膏ボード、軽カル板、石綿
パーライト板等）または金属系の基材（例えば、アルミ
ニウム板、鉄板等）が適用される。The paper or nonwoven fabric used in the present invention is
It is a laminated element in order to buffer the unevenness of the base and prevent the decorative sheet from floating, and to conceal the brightness of the inner aluminum foil and glass fiber sheet. Examples of the paper or nonwoven fabric used in the present invention include all fibers such as Japanese paper, western paper (high quality paper, medium paper, etc.), kraft paper, tissue paper or resin impregnated paper, and various nonwoven fabrics such as polyethylene nonwoven fabric and polyester / pulp nonwoven fabric. A quality sheet is included. The basis weight of paper or non-woven fabric is 15 to 1
00 g / m ² , preferably 20 to 50 g / m ² . Further, in the present invention, as a precious wood veneer, a ground plate cut from various precious woods to a thickness of, for example, 0.05 to 3.0 mm, preferably to a thickness of 0.10 to 0.4 mm. Or a veneer can be applied. The grain of the precious wood veneer is not particularly limited, and may be any of a straight grain, an additional straight grain, a board grain, and a knob-like heather. In particular, the wood species of the precious wood veneer,
Non-limiting examples of preferred tree species are: : Hinoki, oak, zelkova, yu, black persimmon, tochi, katsura, maple, sophora, kusugi, etc .: rosewood, teak, mahogany, koktan (black dan), rosewood (rosewood), bird's eye maple, american black walnut, claro Walnut, Latino nut, Queensland walnut, zebrawood, mangashiro, Brazilian rose,
Karin (Karin), Versimon, Silver Rose, Palma, Redwood, Purplewood, Silky Oak,
Thai Wanks, Cherry, Magnolia, Black Leo (Dao), White Leo, Saberi, Bubinka, Makore, Madrone, Miltor, Maple, Assin, Inbuyer, etc.
The adhesive layer is a laminated element for adhering the veneer veneer and paper or nonwoven fabric. The type of adhesive used in the present invention is not particularly limited because the adhesion between veneer and paper or nonwoven fabric is relatively easy. For example, ethylene vinyl acetate resin (EVA) adhesive, vinyl acetate-acrylic A polymer adhesive, an aqueous vinyl urethane-based adhesive, an acrylic adhesive, or the like can be advantageously used. Further, the fire-resistant precious wood decorative board in the present invention is a fire-resistant precious wood decorative sheet composed of the above-described elements as a surface material, which is attached to a thick base material, As such a substrate, a wood-based substrate (eg, plywood, MDF, particle board honeycomb board, or the like) is advantageously used.
An inorganic base material (for example, gypsum board, light calcium plate, asbestos perlite plate, or the like) or a metal base material (for example, an aluminum plate, an iron plate, or the like) is used.

【００１６】また、本発明の防燃性銘木化粧シートおよ
び化粧板は、予め難燃剤がそれぞれ添加された２種の接
着性樹脂を用いて、一般的な押出しラミネート法および
熱圧締法に従って、難燃剤が含有された特定の接着性樹
脂層を不燃材の両側に積層した構成の化粧単板シートを
製造（特に量産）することができる。防燃性銘木化粧シ
ートは、難燃剤配合の段階と積層成形の段階との２段階
より製造することができる。前者の段階は、所定量（重
量比で５％ないし１５％）の難燃剤を第１の接着性樹脂
および第２の接着性樹脂の双方にそれぞれ添加する段階
である。また、後者の段階には、製造上有利な方法とし
て次の２通りの方法がある。一の方法は、(a) まず、押
出しラミネート法に従い、紙または不織布；第１の接着
性樹脂の層；不燃材（アルミニウム箔、ガラス繊維シー
ト）；第２の接着性樹脂の層；紙または不織布よりなる
積層体を成形し、次に、接着剤を該積層体の上側の紙ま
たは不織布の上に塗布し、続いて、銘木単板をその上に
オーバーレイし、そしてこれら全体を熱圧接着するとい
う方法である。また、別の方法は、(b) 一方で、押出し
ラミネート法に従い、第１の接着性樹脂の層；不燃材
（アルミニウム箔、ガラス繊維シート）；第２の接着性
樹脂の層；紙または不織布よりなる積層体を成形し、ま
た他方で、貼合わせにより、銘木単板；接着剤層；紙ま
たは不織布よりなる単板裏打ちシートを製造し、そし
て、前記積層体と単板裏打ちシートとを熱圧接着すると
いう方法である。また、本発明の防燃性銘木化粧板は、
さらに、上記の方法に従い製造された防燃性銘木化粧シ
ートを木質系、無機質系または金属系基材の上に貼着す
るという段階を経て製造される。Further, the decorative sheet and the decorative board of the flame retardant precious wood of the present invention are prepared by using two types of adhesive resins to which a flame retardant is previously added, respectively, according to a general extrusion laminating method and a hot pressing method. A decorative veneer sheet having a configuration in which a specific adhesive resin layer containing a flame retardant is laminated on both sides of a nonflammable material can be manufactured (particularly mass-produced). The flame retardant precious wood decorative sheet can be manufactured in two stages, that is, a stage of blending a flame retardant and a stage of lamination molding. In the former step, a predetermined amount (5% to 15% by weight) of a flame retardant is added to both the first adhesive resin and the second adhesive resin. In the latter stage, there are the following two methods which are advantageous in manufacturing. One method is as follows: (a) First, according to the extrusion lamination method, a paper or nonwoven fabric; a first adhesive resin layer; a non-combustible material (aluminum foil, glass fiber sheet); a second adhesive resin layer; A laminate of nonwoven is formed, then the adhesive is applied on the paper or nonwoven on top of the laminate, followed by overlaying a veneer veneer thereon and hot pressing together It is a method of doing. Another method is as follows: (b) On the other hand, a first adhesive resin layer; a non-combustible material (aluminum foil, glass fiber sheet); a second adhesive resin layer; A laminated sheet made of a nameplate veneer; an adhesive layer; paper or a nonwoven fabric is manufactured by laminating, and the laminate and the veneered sheet are heat-bonded. This is a method of pressure bonding. Further, the fireproof precious wood decorative board of the present invention,
Further, it is manufactured through a step of sticking the flame-resistant precious wood decorative sheet manufactured according to the above method on a wood-based, inorganic-based or metal-based substrate.

【００１７】[0017]

【実施例】以下、本発明の実施例を図面により説明す
る。Embodiments of the present invention will be described below with reference to the drawings.

【００１８】実施例１ この実施例は、防燃性銘木化粧シートに関する。これ
は、図１に示すように、紙または不織布１（坪量３０ｇ
／ｍ² の紙）；第２の接着性樹脂層２（重量３８ｇ／ｍ
² 、厚さ４０μｍのアイオノマー層）；アルミニウム箔
３（重量４１ｇ／ｍ² 、厚さ１５μｍ）；第１の接着性
樹脂層４（重量３８ｇ／ｍ² 、厚さ４０μｍのアイオノ
マー層）；紙または不織布５（坪量３０ｇ／ｍ² の中質
紙）；接着剤層６（酢酸ビニルアクリル共重合体接着
剤）；銘木単板７（厚さ０．２４ｍｍの楢突板）が最下
層より順に積層され、一体に圧着成形されてなる化粧シ
ートである。そして本実施例では、難燃剤として三酸化
アンチモンおよび臭素系難燃剤が第１の接着性樹脂層４
および第２の接着性樹脂層２の双方に含有されている。 Example 1 This example relates to a flameproof precious wood decorative sheet. This is, as shown in FIG. 1, paper or nonwoven fabric 1 (basis weight 30 g).
/ M ² paper); second adhesive resin layer 2 (weight: 38 g / m 2
² , an ionomer layer having a thickness of 40 μm); aluminum foil 3 (weight: 41 g / m ² , thickness: 15 μm); first adhesive resin layer 4 (weight: 38 g / m ² , ionomer layer having a thickness of 40 μm); paper or Non-woven fabric 5 (medium-weight paper of 30 g / m ² basis weight); adhesive layer 6 (vinyl acetate acrylic copolymer adhesive); precious wood veneer 7 (0.24 mm thick veneer) laminated in order from the bottom layer This is a decorative sheet that is integrally formed by pressure bonding. In the present embodiment, antimony trioxide and a bromine-based flame retardant are used as the flame retardant in the first adhesive resin layer 4.
And the second adhesive resin layer 2.

【００１９】本実施例の化粧シートは、以下の手順に従
い、製造された。 難燃剤の配合 三酸化アンチモンおよび臭素系難燃剤を各々適量づつ、
アイオノマーの中に添加し、次いで、ロール練り等によ
って、これを均質になるまで十分に混和し、難燃剤の配
合された第１の接着性樹脂層４および第２の接着性樹脂
層２の双方を調製した。 積層成形 ｍｍ 一のプロセスとして、図３に示すように、最初に押出し
ラミネート法に従い、坪量３０ｇ／ｍ² の紙１；前記ア
イオノマーよりなる第２の接着性樹脂層２（厚さ４０μ
ｍ）；厚さ１５μｍのアルミニウム箔３；前記アイオノ
マーよりなる第１の接着性樹脂層４（厚さ４０μｍ）；
坪量３０ｇ／ｍ² の紙５よりなる積層体１０を成形し
（図３(A) ）、次に酢酸ビニルアクリル共重合体接着剤
６を積層体１０表面の紙５の上に適量塗布し（図３(B)
）、続いて厚さ０．２４ｍｍの楢突板７をその上にオ
ーバーレイし（図３(C) ）、そしてこれら全体を熱圧締
することにより、防燃性銘木化粧シートに仕上げた（図
３(D) ）。また、別の積層成形プロセスにより本実施例
の化粧シートを製作した。図４に示すように、まず一方
で、押出しラミネート法に従い、坪量３０ｇ／ｍ² の紙
１；前記アイオノマーよりなる第２の接着性樹脂層２
（厚さ４０μｍ）；厚さ１５μｍのアルミニウム箔３；
前記アイオノマーよりなる第１の接着性樹脂層４（厚さ
４０μｍ）よりなる積層体１１を成形し（図４(A) ）、
また他方で、貼合わせにより（ 110℃× 7kg/cm²× 3分
の条件による熱圧締）、厚さ０．２４ｍｍの楢突板７；
酢酸ビニルアクリル共重合体接着剤６；坪量３０ｇ／ｍ
² の紙５よりなる単板裏打ちシート１２を製造し（図４
(B) ）、そして、積層体１１と単板裏打ちシート１２と
をホット・コールド連続プレス機の中に入れ、これらを
125℃×7kg/cm²×15分の条件で熱圧締し、続いて同じ
プレス圧を維持したまま、強制冷却により常温に降温す
るまで圧締を続け（図４(C) ）、その後、必要により、
サンドペーパー＃ 240を用いて突板７の表面を研磨し続
いてその表面にポリウレタン樹脂塗料（固形分塗布量 1
0 g/m² ）を塗装することにより、防燃性銘木化粧シー
ト８を作り上げた（図４(C) ）。The decorative sheet of this example was manufactured according to the following procedure. Combination of flame retardant Antimony trioxide and bromine-based flame retardant, each in an appropriate amount,
It is added to the ionomer, and then sufficiently mixed until it becomes homogeneous by roll milling or the like, and both the first adhesive resin layer 4 and the second adhesive resin layer 2 containing the flame retardant are mixed. Was prepared. Lamination molding mm As one process, as shown in FIG. 3, first, according to the extrusion lamination method, paper 1 having a basis weight of 30 g / m ² ; second adhesive resin layer 2 composed of the ionomer (thickness of 40 μm)
m); an aluminum foil 3 having a thickness of 15 μm; a first adhesive resin layer 4 made of the ionomer (40 μm in thickness);
A laminate 10 made of paper 5 having a basis weight of 30 g / m ² is formed (FIG. 3 (A)), and then an appropriate amount of a vinyl acetate acrylic copolymer adhesive 6 is applied onto the paper 5 on the surface of the laminate 10. (Fig. 3 (B)
) Then, a 0.24 mm thick veneer 7 was overlaid thereon (FIG. 3 (C)), and the whole was hot-pressed to obtain a flameproof precious wood decorative sheet (FIG. 3). (D)). Further, the decorative sheet of the present example was manufactured by another lamination molding process. As shown in FIG. 4, on the one hand, according to the extrusion lamination method, paper 1 having a basis weight of 30 g / m ² ; a second adhesive resin layer 2 composed of the ionomer
(Thickness: 40 μm); aluminum foil 3 having a thickness of 15 μm;
A laminate 11 composed of the first adhesive resin layer 4 (thickness: 40 μm) composed of the ionomer was formed (FIG. 4A).
On the other hand, by laminating (hot pressing under the condition of 110 ° C. × 7 kg / cm ² × 3 minutes), a veneer plate 7 having a thickness of 0.24 mm;
Vinyl acetate acrylic copolymer adhesive 6; basis weight 30 g / m
² to produce a veneer backing sheet 12 made of paper 5 (FIG. 4).
(B)) Then, the laminate 11 and the veneer backing sheet 12 are put into a hot / cold continuous pressing machine, and these are put together.
Heat-pressing under the condition of 125 ° C. × 7 kg / cm ² × 15 minutes, and then, while maintaining the same pressing pressure, continuing pressing until the temperature is reduced to room temperature by forced cooling (FIG. 4 (C)). If necessary,
The surface of the veneer 7 is polished using sandpaper # 240, and then the surface of the veneer 7 is coated with a polyurethane resin paint (solid content 1
By coating with 0 g / m ² ), a flameproof precious wood decorative sheet 8 was produced (FIG. 4 (C)).

【００２０】実施例２ この実施例は、防燃性銘木化粧板に関する。これは、図
２に示すように、実施例１の防燃性銘木化粧シート８が
木質系基材９（合板、ＭＤＦ等）の上に貼着されてなる
化粧板である。従って、本実施例では、特徴的なこと
に、表面材たる化粧シートの内部層２、４それぞれに三
酸化アンチモンおよび臭素系難燃剤が配合されている。
この実施例の防燃性銘木化粧板は、図４(D) に示すよう
に、上記のプロセスに従い製造された防燃性銘木化粧シ
ート８を、木質系基材９の上に貼着することにより、作
り上げた。 Example 2 This example relates to a flame-resistant decorative wood veneer. As shown in FIG. 2, this is a decorative board in which the flame-resistant precious wood decorative sheet 8 of Example 1 is stuck on a wooden base material 9 (plywood, MDF, etc.). Therefore, in this embodiment, it is characteristic that antimony trioxide and a bromine-based flame retardant are blended in each of the inner layers 2 and 4 of the decorative sheet as the surface material.
As shown in FIG. 4 (D), the decorative board made of flame retardant wood of this embodiment is obtained by sticking a decorative sheet 8 of fire resistant wood produced according to the above process onto a wood-based substrate 9. By making it.

【００２１】実施例３ この実施例は、防燃性銘木化粧シートに関する。これ
は、図５に示すように、紙または不織布１（坪量３０ｇ
／ｍ² の紙）；第２の接着性樹脂層２（重量３８ｇ／ｍ
² 、厚さ４０μｍのエチレン−アクリル酸共重合体（Ｅ
ＡＡ）層）；ガラス繊維不織布１３（重量２５ｇ／ｍ
² ）；第１の接着性樹脂層４（重量３８ｇ／ｍ² 、厚さ
４０μｍのエチレン−アクリル酸共重合体（ＥＡＡ）
層）；紙または不織布５（坪量３０ｇ／ｍ² の中質
紙）；接着剤層６（酢酸ビニルアクリル共重合体接着
剤）；銘木単板７（厚さ０．２４ｍｍの楢突板）が最下
層より順に積層され、一体に圧着成形されてなる化粧シ
ートである。そして本実施例では、難燃剤として三酸化
アンチモンおよび臭素系難燃剤が第１の接着性樹脂層４
および第２の接着性樹脂層２の双方に含有されている。 Example 3 This example relates to a flameproof precious wood decorative sheet. This is, as shown in FIG. 5, paper or nonwoven fabric 1 (basis weight 30 g).
/ M ² paper); second adhesive resin layer 2 (weight: 38 g / m 2
^2. 40 μm thick ethylene-acrylic acid copolymer (E
AA) layer); glass fiber nonwoven fabric 13 (weight 25 g / m
² ); First adhesive resin layer 4 (weight 38 g / m ² , thickness 40 μm, ethylene-acrylic acid copolymer (EAA))
Layer); paper or non-woven fabric 5 (medium-weight paper of 30 g / m ² basis weight); adhesive layer 6 (vinyl acetate acrylic copolymer adhesive); precious wood veneer 7 (0.24 mm thick veneer). It is a decorative sheet that is laminated in order from the lowermost layer and integrally formed by pressure bonding. In the present embodiment, antimony trioxide and a bromine-based flame retardant are used as the flame retardant in the first adhesive resin layer 4.
And the second adhesive resin layer 2.

【００２２】而して、実施例１の化粧シートも、実施例
２の化粧板も、そして実施例３の化粧シートも、高い難
燃性を有し、満足な防火性能を発揮するものであった。
このことは、次の試験例の結果からも、確認することが
できる。Thus, the decorative sheet of Example 1, the decorative plate of Example 2, and the decorative sheet of Example 3 have high flame retardancy and exhibit satisfactory fire protection performance. Was.
This can be confirmed also from the results of the following test examples.

【００２３】試験例１：化粧シートの表面燃焼試験 実施例１の防燃性銘木化粧シートについて、防火材料の
建設省告示および JISA 1321 に従い、表面燃焼試験を
行なった。試験に供する基材として、法定不燃材料の石
綿パーライト板（１０ｍｍ厚）および法定準不燃材料の
石膏ボード（９ｍｍ厚）を採用し、そして各々その上に
実施例１の化粧シートを貼着して、試験体を作成した。
各基材につき２個の試験体を準備した。なお、化粧シー
トと基材との貼着には、酢酸ビニルエマルジョン接着剤
を塗布量（固形分）４０ｇ／ｍ²にて使用した。試験の
結果を次の表に示す。 この表より、化粧シートを不燃基材の上に貼着した試験
体も、またそれを準不燃基材の上に貼着した試験体も、
準不燃の性能を有することがわかる。したがって、実施
例１の化粧シートは、準不燃の性能を発揮する壁装材料
であると認められる。 Test Example 1 : Surface Burning Test of Decorative Sheet The surface burning test of the fireproof precious wood decorative sheet of Example 1 was carried out in accordance with the notification of the Ministry of Construction of Fire Protection Materials and JISA 1321. As a base material to be tested, an asbestos pearlite board (10 mm thick) of a legally incombustible material and a gypsum board (9 mm thick) of a legally quasi-incombustible material were used, and the decorative sheet of Example 1 was adhered thereon. , A specimen was prepared.
Two specimens were prepared for each substrate. Note that a vinyl acetate emulsion adhesive was used at a coating amount (solid content) of 40 g / m ² for sticking the decorative sheet to the base material. The test results are shown in the following table. From this table, both the test specimens in which the decorative sheet was adhered on the non-combustible base material and the test specimens in which the decorative sheet was adhered on the semi-combustible base material,
It can be seen that it has a semi-incombustible performance. Therefore, it is recognized that the decorative sheet of Example 1 is a wall covering material exhibiting semi-flammable performance.

【００２４】試験例２：化粧シートの表面燃焼について
の比較試験 各化粧シートについて、防火材料の建設省告示および J
IS A 1321 に従う表面燃焼試験を以下の通り行ない、そ
の防火性能を比較してみた。 −供試化粧シート 次の積層構成をなす化粧シートＡ、ＢおよびＣを夫々、
各シートにつき３枚づつ製作し、上記試験に供すること
とした。 化粧シートＡ； （最上層）突板／接着剤層／紙／無処理の接着性樹脂層
／アルミニウム箔／無処理の接着性樹脂層／紙（最下
層） 化粧シートＢ； （最上層）突板／接着剤層／紙／難燃剤含有の接着性樹
脂層／アルミニウム箔／無処理の接着性樹脂層／紙（最
下層） 化粧シートＣ； （最上層）突板／接着剤層／紙／難燃剤含有の接着性樹
脂層／アルミニウム箔／難燃剤含有の接着性樹脂層／紙
（最下層） −化粧シートの積層要素 上記各化粧シートに使用された材料は、次の通りであ
る。 突板：かば材 気乾重量 １０９ｇ／ｍ² 表面塗装無し 紙 ：坪量３０ｇ／ｍ² 接着剤層：酢酸ビニル系接着剤 塗布量（固形分） ２０ｇ／ｍ² 接着性樹脂層：エチレン−アクリル酸共重合体樹脂（ＥＡＡ）の接着性フィルム 厚さ４０μｍ 無処理の接着性樹脂層には、難燃剤が添加されて いない。難燃剤含有の接着性樹脂層には、三酸化アンチモンおよ びブロム系難燃剤が合計で重量比で１２％含有されている。 アルミニウム箔： 厚さ １５μｍ −表面燃焼試験 表面燃焼試験のための基材として、法定準不燃材料の石
膏ボード（９ｍｍ厚）を採用し、その上に上記の化粧シ
ートＡ、ＢおよびＣを夫々貼着し、供試シートを各種類
ごとに３個づつ作成した。なお、化粧シートと基材との
貼着には、酢酸ビニルエマルジョン接着剤を塗布量（固
形分）４０ｇ／ｍ² にて使用した。試験の結果を次の表
に示す。 なお、準不燃の性能の規格値は、温度時間面積 tdθ＜
１００、発煙係数 CA＜６０、残炎時間＝０である。こ
の表より、適量の難燃剤を接着性樹脂層に含有すること
により、化粧シートは、法定準不燃の性能を発揮し、し
かも上下２層の接着性樹脂層に含有すれば、防火性能が
ますます向上することがわかる。 Test Example 2 : Comparative test on surface burning of decorative sheet For each decorative sheet, notice of Ministry of Construction and J
A surface combustion test according to IS A 1321 was performed as follows, and the fire protection performance was compared. -Cosmetic sheet under test Cosmetic sheets A, B and C having the following laminated structure are respectively:
Three sheets were manufactured for each sheet and subjected to the above test. Decorative sheet A; (top layer) veneer / adhesive layer / paper / untreated adhesive resin layer / aluminum foil / untreated adhesive resin layer / paper (bottom layer) Decorative sheet B; (top layer) veneer / Adhesive layer / paper / adhesive resin layer containing flame retardant / aluminum foil / untreated adhesive resin layer / paper (bottom layer) Decorative sheet C; (top layer) veneer / adhesive layer / paper / containing flame retardant Adhesive resin layer / aluminum foil / Adhesive resin layer containing flame retardant / paper (bottom layer)-Laminate element of decorative sheet The materials used for each decorative sheet are as follows. Veneer: fog material Air-dry weight 109 g / m ² without surface coating Paper: basis weight 30 g / m ² Adhesive layer: vinyl acetate-based adhesive Application amount (solid content) 20 g / m ² Adhesive resin layer: ethylene-acryl Adhesive film of acid copolymer resin (EAA) Thickness 40 μm No flame retardant was added to the untreated adhesive resin layer. The adhesive resin layer containing a flame retardant contains antimony trioxide and a bromo-based flame retardant in a total weight ratio of 12%. Aluminum foil: Thickness 15 μm-Surface burning test A gypsum board (9 mm thick) of legally quasi-noncombustible material was used as a base material for the surface burning test, and the decorative sheets A, B and C were pasted thereon. Then, three test sheets were prepared for each type. Note that a vinyl acetate emulsion adhesive was used at a coating amount (solid content) of 40 g / m ² for sticking the decorative sheet to the base material. The test results are shown in the following table. In addition, the standard value of the performance of quasi-incombustibility is the temperature time area tdθ <
100, smoke emission coefficient CA <60, afterflame time = 0. According to this table, the decorative sheet exhibits the statutory non-flammable performance by containing an appropriate amount of flame retardant in the adhesive resin layer, and the fire protection performance is enhanced if it is contained in the upper and lower adhesive resin layers. It turns out that it improves more and more.

【００２５】試験例３：防燃性銘木化粧シートの表面燃
焼試験 各防燃性銘木化粧シートについて、防火材料の建設省告
示および JIS A 1321に従う表面燃焼試験を以下の通り
行ない、その防火性能を比較してみた。 −供試化粧シート 次の積層構成をなす化粧シートＣ^* 、ＤおよびＥを夫
々、各シートにつき３枚づつ製作し、上記試験に供する
こととした。 化粧シートＣ^* ；（最上層）単板／接着剤層／紙／難燃
剤１２％含有の接着性樹脂層／アルミニウム箔／難燃剤
１２％含有の接着性樹脂層／紙（最下層） 化粧シートＤ ；（最上層）単板／接着剤層／紙／難燃
剤１２％含有の接着性樹脂層 ^*／紙（最下層） 化粧シートＥ；（最上層）単板／接着剤層／紙／無処理
の接着性樹脂層／アルミニウム箔／ブロム系難燃剤２４
％含有の接着性樹脂層／紙（最下層） −化粧シートの積層要素 上記各化粧シートに使用された材料は、次の通りであ
る。 単板：かば材 気乾重量 １１２ｇ／ｍ² 表面塗装無し 紙 ：坪量３０ｇ／ｍ² 接着剤層：酢酸ビニル系接着剤 塗布量（固形分） ２０ｇ／ｍ² アルミニウム箔： 厚さ １５μｍ 難燃剤１２％含有の接着性樹脂層：ブロム系難燃剤が重
量比で１２％含有されている、４０μ厚のＥＡＡ樹脂の
接着性フィルム 難燃剤１２％含有の接着性樹脂層 ^*：ブロム系難燃剤が
重量比で１２％含有されている、８０μ厚のＥＡＡ樹脂
の接着性フィルム 無処理の接着性樹脂層：難燃剤が添加されていない、４
０μ厚のＥＡＡ樹脂の接着性フィルム 難燃剤２４％含有の接着性樹脂層：ブロム系難燃剤が重
量比で２４％含有されている、４０μ厚のＥＡＡ樹脂の
接着性フィルム −表面燃焼試験 表面燃焼試験のための基材として、法定準不燃材料の石
膏ボード（９ｍｍ厚）を採用し、その上に上記の化粧シ
ートＣ^* 、ＤおよびＥを夫々貼着し、供試シートを各種
類ごとに３個づつ作成した。なお、化粧シートと基材と
の貼着には、酢酸ビニルエマルジョン接着剤を塗布量
（固形分）４０ｇ／ｍ² にて使用した。試験の結果を次
の表に示す。 なお、準不燃の性能の規格値は、温度時間面積 tdθ＜
１００、発煙係数 CA＜６０、残炎時間＝０である。こ
の表より、次のことが理解される。防燃性銘木化粧シー
トＣ^* は、難燃剤含有の接着性樹脂層／アルミニウム箔
／難燃剤含有の接着性樹脂層の３層構造を有する化粧シ
ートであり、測定３点いずれについても、準不燃の性能
の規格を満たす。これに対し、防燃性銘木化粧シートＤ
は、難燃剤含有の接着性樹脂層のみでアルミニウム箔が
介在していない構造を有する化粧シート（化粧シートＣ
^* のような３層構造を形成しておらず、すなわち、接着
性樹脂層の厚さは化粧シートＣ^*における該樹脂層の厚
さの２倍の厚さであって、化粧シートＣ^* よりアルミニ
ウム箔を取り除いた材料構成をなす。）であり、燃焼試
験において石膏ボードの特に表層の紙の燃焼が激しく、
測定３点いずれもtdθ＞１００であり、準不燃性能の規
格を満たさない。また、防燃性銘木化粧シートＥは、無
処理の接着性樹脂層／アルミニウム箔／難燃剤含有の接
着性樹脂層の３層構造を有する化粧シート（化粧シート
Ｃ^* のような３層構造を形成するが、難燃剤は一方の接
着性樹脂層のみに含有され、その含有量は化粧シートＣ
^* における含有量の２倍の量である。）であり、測定３
点のうち２点についてtdθ＞１００であるので、準不燃
の性能試験について、化粧シートＤと同様、不合格とな
る。なお、防燃性銘木化粧シートＣ^* において準不燃の
性能が発揮されるのは、第２の接着性樹脂層（難燃剤含
有されている）およびアルミニウム箔がシート裏側の紙
・不織布および石膏ボードの表面紙への炎の侵入を遅延
させ、かつ、第１の接着性樹脂層（難燃剤含有されてい
る）がシート表側の単板、接着剤層、および紙・不織布
の燃焼を遅延させ、炭化を促進して、断熱層を形成する
という機構によるものと推量される。したがって、接着
性樹脂層／アルミニウム箔／接着性樹脂層という３層の
積層構造を備えかつ難燃剤を双方の接着性樹脂層に各々
含有せしめることにより、アルミニウム箔が接着性樹脂
層の中に介在されていない構造の化粧シートと比較し
て、また、３層の積層構造を有するが難燃剤が一方の接
着性樹脂層のみに含有されている構造の化粧シートと比
較して、防火性能が著しく向上し、よって、本発明の防
燃性銘木化粧シートは、法定準不燃の性能を満足に発揮
することができるものである。 Test Example 3 Surface Burning Test of Flame-Retardant Precious Wood Decorative Sheets For each of the flame-retardant precious wood decorative sheets, a surface burning test according to the notification of the Ministry of Construction of Fire Protection Materials and JIS A 1321 was carried out as follows, and the fire protection performance was evaluated. I tried to compare. -Decorative Cosmetic Sheets Decorative sheets C ^* , D, and E each having the following laminated structure were manufactured three by one for each sheet, and subjected to the above test. Decorative sheet C ^* ; (top layer) Veneer / adhesive layer / paper / adhesive resin layer containing 12% flame retardant / aluminum foil / adhesive resin layer containing 12% flame retardant / paper (bottom layer) Decorative sheet D: (top layer) veneer / adhesive layer / paper / adhesive resin layer containing 12% flame retardant ^* / paper (bottom layer) decorative sheet E; (top layer) veneer / adhesive layer / paper / none Adhesive resin layer of treatment / Aluminum foil / Brom-based flame retardant 24
% Adhesive resin layer / paper (bottom layer)-Laminate element of decorative sheet The materials used for each decorative sheet are as follows. Veneer: birch material Air-dry weight 112 g / m ² without surface coating Paper: basis weight 30 g / m ² Adhesive layer: vinyl acetate adhesive applied amount (solid content) 20 g / m ² Aluminum foil: thickness 15 μm difficult Adhesive resin layer containing 12% flame retardant: Adhesive film of 40 μm thick EAA resin containing 12% by weight of bromo flame retardant Adhesive resin layer containing 12% flame retardant ^* : Brom flame retardant 80% thick EAA resin adhesive film containing 12% by weight of untreated adhesive resin layer: no flame retardant added
0 μm thick EAA resin adhesive film Adhesive resin layer containing 24% flame retardant: 40 μm thick EAA resin adhesive film containing 24% by weight of bromo-based flame retardant-Surface burning test Surface burning A gypsum board (9 mm thick) of legally quasi-noncombustible material was used as a base material for the test, and the decorative sheets C ^* , D, and E were stuck thereon, and the test sheets were prepared for each type. Created three by three. Note that a vinyl acetate emulsion adhesive was used at a coating amount (solid content) of 40 g / m ² for sticking the decorative sheet to the base material. The test results are shown in the following table. In addition, the standard value of the performance of quasi-incombustibility is the temperature time area tdθ
100, smoke emission coefficient CA <60, afterflame time = 0. From this table, the following is understood. The flameproof precious wood decorative sheet C ^* is a decorative sheet having a three-layer structure of an adhesive resin layer containing a flame retardant / aluminum foil / an adhesive resin layer containing a flame retardant. Meet the performance standards. On the other hand, the flameproof precious wood decorative sheet D
Is a decorative sheet having a structure in which only an adhesive resin layer containing a flame retardant and no aluminum foil is interposed (decorative sheet C
^* 3-layer structure does not form a like, that is, the thickness of the adhesive resin layer is a 2 times the thickness of the thickness of the resin layer in the decorative sheet C ^*, from the decorative sheet C ^* It has a material composition with the aluminum foil removed. ), And in the combustion test, the paper on the gypsum board, especially the surface layer, burned strongly,
At all three measurement points, tdθ> 100, which does not satisfy the quasi-noncombustibility standard. In addition, the decorative sheet E having a flame-resistant precious wood is a decorative sheet having a three-layer structure of an untreated adhesive resin layer / aluminum foil / an adhesive resin layer containing a flame retardant (a three-layer structure like a decorative sheet C ^* ). The flame retardant is contained in only one of the adhesive resin layers, and the content thereof is
^* Twice the content of ^* . ) And measurement 3
Since tdθ> 100 for two of the points, the semi-inflammable performance test is rejected as in the case of the decorative sheet D. The quasi-incombustible performance of the fireproof precious wood decorative sheet C ^* is due to the fact that the second adhesive resin layer (containing a flame retardant) and the aluminum foil are the paper / nonwoven fabric and the gypsum board on the back side of the sheet. The first adhesive resin layer (containing a flame retardant) delays the burning of the veneer, adhesive layer, and paper / nonwoven fabric on the front side of the sheet, It is presumed that this is due to the mechanism of promoting carbonization and forming a heat insulating layer. Therefore, by providing a three-layer structure of an adhesive resin layer / aluminum foil / adhesive resin layer and including a flame retardant in each of the adhesive resin layers, the aluminum foil is interposed in the adhesive resin layer. Compared to a decorative sheet having no laminated structure and a decorative sheet having a three-layer laminated structure, but having a flame retardant contained in only one of the adhesive resin layers, the fire protection performance is remarkable. Accordingly, the decorative sheet for fireproof precious wood of the present invention is capable of satisfactorily exhibiting the statutory non-combustibility performance.

【００２６】試験例４：接着性樹脂層および不燃材の重
量による、防燃性銘木化粧シートの防火性能への影響に
ついて 接着性樹脂層の重量が種々異なる各防燃性銘木化粧シー
トについて、また、不燃材（アルミニウム箔、ガラス繊
維シート）の重量が種々異なる各防燃性銘木化粧シート
について、防火材料の建設省告示および JIS A 1321 に
従う表面燃焼試験を以下の通り行ない、その防火性能を
比較してみた。 −供試化粧シート 試験に用いられた防燃性銘木化粧シートは、いずれも次
の積層構成をなす。 （最上層）単板／接着剤層／紙／難燃剤含有の接着性樹
脂層／アルミニウム箔またはガラス繊維シート／難燃剤
含有の接着性樹脂層／紙（最下層） 接着性樹脂層の重量が１９、２８、３８、４７、５７ｇ
／ｍ² （つまり厚さが２０、３０、４０、５０、６０μ
ｍ）である５種類の防燃性銘木化粧シートをそれぞれ、
各種類のシートにつき３枚づつ製作し、上記試験に供す
ることとした。いずれの化粧シートも、重量４１ｇ／ｍ
² （厚さ１５μｍ）のアルミニウム箔を含む。また、ア
ルミニウム箔の重量が０、２７、４１、５４、８２ｇ／
ｍ² （つまり厚さが０、１０、１５、２０、３０μｍ）
である５種類の防燃性銘木化粧シートをそれぞれ、各種
類のシートにつき３枚づつ製作し、上記試験に供するこ
ととした。いずれの化粧シートも、重量３８ｇ／ｍ²
（厚さ４０μｍ）の接着性樹脂層をアルミニウム箔の両
側に備える。さらに、ガラス繊維シートの重量が０、１
０、２０、２５、３０、４０、５０ｇ／ｍ² である７種
類の防燃性銘木化粧シートをそれぞれ、各種類のシート
につき３枚づつ製作し、上記の試験に供することとし
た。いずれの化粧シートも、重量３８ｇ／ｍ² （厚さ４
０μｍ）の接着性樹脂層をアルミニウム箔の両側に備え
る。 −化粧シートの積層要素 上記の化粧シートに使用された材料は、次の通りであ
る。 単板：かば材 気乾重量 １０５ｇ／ｍ² 表面塗装無し 紙 ：薄葉紙 坪量３０ｇ／ｍ² 接着剤層：酢酸ビニル系接着剤 塗布量（固形分） ２０ｇ／ｍ² 難燃剤含有の接着性樹脂層： ブロム系難燃剤が重量比で１２％含有されているＥＡＡ樹脂の接着性フィルム ガラス繊維シート：ガラス繊維不織布 グラスパー ＧＨＮ−２５ （王子製紙株式会社製、坪量２５ｇ／ｍ² ） −表面燃焼試験 表面燃焼試験のための基材として、法定準不燃材料の石
膏ボード（９ｍｍ厚）を採用し、その上に上記の防燃性
銘木化粧シートを夫々貼着し、供試体を各種類ごとに３
個づつ作成した。なお、化粧シートと基材との貼着に
は、酢酸ビニルエマルジョン接着剤を塗布量（固形分）
４０ｇ／ｍ² にて使用した。試験の結果を次の二つの表
に示す。 また、図６は、接着性樹脂層の重量が種々異なる各防燃
性銘木化粧シートについての結果を表わすグラフであ
り、図７は、アルミニウム箔の重量が種々異なる各防燃
性銘木化粧シートについての結果を表わすグラフであ
る。これらの表およびグラフより、次のことが理解され
る。試験された防燃性銘木化粧シートは、接着性樹脂層
の重量が約３８ｇ／ｍ² （厚さ約４０μｍ）以下である
とき、ほぼ同程度の高い防火性能を示し、準不燃の基準
に適合するが、その重量が約３８ｇ／ｍ² を越えると、
防火性能は悪化し、準不燃の性能に達しなくなる。ま
た、アルミニウム箔の重量が２７ｇ／ｍ² ないし８２ｇ
／ｍ² （つまり厚さが１０μｍないし３０μｍ）の範囲
内であるとき、準不燃の基準を満たす大変高い防火性能
を示す。さらに、ガラス繊維シートの重量が１０ｇ／ｍ
² ないし４０ｇ／ｍ² の範囲内であるとき、準不燃の基
準を満たす大変高い防火性能を示す。 Test Example 4 : Influence of the Weight of the Adhesive Resin Layer and the Incombustible Material on the Fire-Proofing Performance of the Flame-Retardant Precious Wood Decorative Sheet For each of the fire-resistant precious wood decorative sheets having various weights of the adhesive resin layer, For each fireproof precious wood decorative sheet with various weights of non-combustible materials (aluminum foil and glass fiber sheet), the fire prevention materials were notified as follows and the surface fire test according to JIS A 1321 was conducted as follows, and their fire protection performances were compared. I tried to. -Cosmetic sheet for test All of the flameproof precious wood decorative sheets used in the test have the following laminated structure. (Top layer) Veneer / adhesive layer / paper / adhesive resin layer containing flame retardant / aluminum foil or glass fiber sheet / adhesive resin layer containing flame retardant / paper (bottom layer) Weight of adhesive resin layer 19, 28, 38, 47, 57 g
/ M ² (that is, the thickness is 20, 30, 40, 50, 60 μm).
m) each of the five types of flameproof precious wood decorative sheets,
Three sheets of each type were manufactured and subjected to the above test. Each decorative sheet weighs 41 g / m.
Includes ² (15 μm thick) aluminum foil. The weight of the aluminum foil is 0, 27, 41, 54, 82 g /
m ² (that is, 0, 10, 15, 20, 30 μm in thickness)
The five types of flame-resistant precious wood decorative sheets were manufactured for each type of sheet, and were subjected to the above test. Both decorative sheets weigh 38 g / m ^2.
An adhesive resin layer (thickness: 40 μm) is provided on both sides of the aluminum foil. Furthermore, the weight of the glass fiber sheet is 0, 1,
Three types of decorative sheets of fireproof precious wood, each having 0, ²⁰ , 25, 30, 40, and 50 g / m ² , were manufactured for each type of sheet, and were subjected to the above test. Both decorative sheets weigh 38 g / m ² (thickness 4
0 μm) is provided on both sides of the aluminum foil. -Laminated element of decorative sheet The materials used for the decorative sheet are as follows. Veneer: birch material Air-dried weight 105 g / m ² without surface coating Paper: tissue paper Basis weight 30 g / m ² Adhesive layer: vinyl acetate-based adhesive Application amount (solid content) 20 g / m ² Adhesive properties containing flame retardant Resin layer: Adhesive film of EAA resin containing 12% by weight of a bromo-based flame retardant Glass fiber sheet: Glass fiber non-woven fabric Graspar GHN-25 (Oji Paper Co., Ltd., basis weight 25 g / m ² ) Surface Combustion test Gypsum board (9 mm thick) of legally quasi-noncombustible material is used as a base material for surface combustion test, and the above-mentioned flame-resistant precious wood decorative sheets are adhered on each, and the specimens are prepared for each type. To 3
Created one by one. In addition, when applying the decorative sheet and the base material, a vinyl acetate emulsion adhesive is applied (solid content).
Used at 40 g / m ² . The results of the test are shown in the following two tables. FIG. 6 is a graph showing the results of the respective decorative sheets with different weights of the adhesive resin layer, and FIG. 7 is the graph of the respective decorative sheets with different weights of the aluminum foil. 6 is a graph showing the result of the above. The following can be understood from these tables and graphs. The tested fireproof precious wood decorative sheet shows almost the same high fire protection performance when the weight of the adhesive resin layer is about 38 g / m ² (thickness about 40 μm) or less, and meets the quasi-nonflammable standard. However, if the weight exceeds about 38 g / m ² ,
The fire protection performance deteriorates and the quasi-noncombustible performance is not reached. The aluminum foil weighs 27 g / m ² to 82 g.
/ M ² (that is, when the thickness is in the range of 10 μm to 30 μm), it shows a very high fire protection performance that satisfies the criterion of quasi-incombustibility. Further, the weight of the glass fiber sheet is 10 g / m.
² to time in the range of 40 g / m ^2, shows a very high fire performance that meets the criteria of the quasi-incombustible.

【００２７】試験例５：接着性樹脂層の接着力と難燃剤
含有量との関係 防燃性銘木化粧シートにおける接着力の低下は、同シー
トの強度、柔軟性を減少し、その可撓性および曲げ適性
を悪化せしめる。曲げ適性が悪いと、曲げたときに単板
の木目が追従して拡張せず、割れが生じ、よって、とり
わけ曲面部への曲げ貼着を困難なものにする。従って、
接着力と難燃剤含有量との関係を知ることは重要であ
り、本試験例はこの関係を調べたものである。 1)供試防燃性銘木化粧シート 構成 最上層より、銘木単板（樺柾目単板、厚さ０．２５ｍ
ｍ）／接着剤層（酢酸ビニル系接着剤、塗布量（乾燥
時）２０ｇ／ｍ² ）／薄葉紙（坪量３０ｇ／ｍ² ）／第
１の接着性樹脂層（重量 約３８ｇ／ｍ² 、厚さ４０μ
ｍ）／アルミニウム箔（重量４１ｇ／ｍ² 、厚さ１５μ
ｍ）／第２の接着性樹脂層（重量 約３８ｇ／ｍ² 、厚
さ４０μｍ）／薄葉紙（坪量３０ｇ／ｍ² ）よりなる積
層構造を有する。第１および第２の接着性樹脂層とし
て、エチレン−アクリル酸共重合体（ＥＡＡ）より成る
防燃性銘木化粧シート、および、低密度ポリエチレン
（ＬＤＰＥ）より成る防燃性銘木化粧シートの２種類を
作製し、これらを本試験に供することとした。そして、
これら接着性樹脂層には、下記の表に示す量のブロム系
難燃剤が各層に等量づつ配合されている。 製造法 本発明の方法に従い製造したが、その熱圧接着は、次の
手順により行なった。得られた積層体をホットコールド
連続プレス機の中に収め入れ、これを１２５℃×７ kg/
cm² ×１５分の条件で熱圧締し、続いて、プレス圧力を
同じに維持したまま、強制冷却し、それが常温に降温す
るまで圧締を続ける。 2)接着力の測定 ２種類の供試防燃性銘木化粧シートより、打ち抜きも
しくは切断等により、それぞれ１５ｍｍ幅のストリップ
（ストリップの長さ方向は単板の木目方向と平行であ
る。）を作製し、そしてナイフを用いて、該ストリップ
の先端部において第１の接着性樹脂層とその上層側の紙
との間に裂け目をいれ、そこより強制的にストリップの
約１／２の長さの部位まで引き剥して、１８０度ピーリ
ング強度測定用の試験体（一端側にて２つの片に分かれ
ている。）を作製した。 −測定１．− 作製された２種類の試験体（各種類に付き３個の試験
体）をそれぞれ、常温の室内に２４時間の間静置し、そ
してその後、取り出した各試験体について、一般の試験
規格に従って常態１８０°ピーリング強度（ｇ／１５ｍ
ｍ）を測定した。なお、供試防燃性銘木化粧シートに用
いられた紙それ自体の層内剥離強度（紙間剥離強度）は
平均で、１８００ｇ／１５ｍｍである。 −測定２．− また、作製された２種類の試験体（各種類に付き３個の
試験体）をそれぞれ、４０℃、相対湿度９５％の雰囲気
に調整されたチャンバ内に７日間置き、続いて２５℃、
相対湿度５５％の雰囲気下に３日間放置し、そしてその
後、取り出した各試験体について、測定１．と同様の方
法で常態１８０°ピーリング強度（ｇ／１５ｍｍ）を測
定した。 3)結果 上記測定１．および測定２．の結果を以下の表に示す。
この表中、ピーリング強度は、３回の試験における常態
１８０°ピーリング強度の平均値を表わす。また、図８
は、測定１．の結果を表わすグラフであり、図９は、測
定２．の結果を表わすグラフである。 この表およびグラフより、次のことが理解される。接着
性樹脂層としてＬＤＰＥ層より成る防燃性銘木化粧シー
トにあっては、接着性樹脂層とこれに隣接する紙との間
の接着力は、難燃剤の添加により急激に低下し、難燃剤
を僅か５重量％配合しただけで、その接着力は難燃剤未
配合の場合と比べてほぼ半減し、さらに難燃剤の配合量
を増加すると、層間接着力は格段に低下し、接着性樹脂
層と紙との間で剥離が起きやすくなる。特に、化粧シー
トを高温高湿の雰囲気下に曝した場合には、その後それ
を常温中湿度の雰囲気下に戻して乾燥させたとしても、
層間接着力の低下は著しく、接着性樹脂層と紙との間で
容易に剥離が生じるようになり、とりわけ難燃剤の配合
量が多いときには、化粧シートは積層構造を維持できな
くなる。これに対して、接着性樹脂層としてＥＡＡ樹脂
より成る防燃性銘木化粧シートにあっては、接着性樹脂
層とこれに隣接する紙との間の接着力は、難燃剤の少量
（５重量％ぐらい）添加の場合ではほとんど低下せず、
さらに難燃剤の配合量をより多くしても、層間接着力の
低下の進行はいたって緩やかであり、そして、難燃剤を
２０重量％配合したとき、接着力の低下が目立ちはじ
め、接着性樹脂層と紙との間で剥離が起きるようにな
る。従って、接着性樹脂層としては、ＥＡＡ樹脂層を適
用すべきであり、かつ、その場合において、それへの難
燃剤の配合量は最大で、およそ１５％に制限すべきであ
るとの結論が導かれる。 Test Example 5 : Relationship between Adhesive Strength of Adhesive Resin Layer and Flame Retardant Content A decrease in the adhesive strength of a flame-retardant precious wood decorative sheet decreases the strength and flexibility of the sheet, and its flexibility. In addition, it deteriorates bending aptitude. Poor bending aptitude does not allow the grain of the veneer to follow and expand when bent, resulting in cracks, thus making it especially difficult to bend and adhere to curved surfaces. Therefore,
It is important to know the relationship between the adhesive strength and the content of the flame retardant, and this test example examined this relationship. 1) Specimen flameproof precious wood decorative sheet Composition From the top layer, precious wood veneer (birch straight grain veneer, thickness 0.25m)
m) / adhesive layer (vinyl acetate-based adhesive, coated amount (dry) 20 g / m ² ) / tissue paper (basis weight 30 g / m ² ) / first adhesive resin layer (weight about 38 g / m ² , Thickness 40μ
m) / aluminum foil (weight 41 g / m ² , thickness 15μ)
m) / second adhesive resin layer (weight about 38 g / m ² , thickness 40 μm) / thin paper (basis weight 30 g / m ² ). As the first and second adhesive resin layers, two types of a flame-resistant nameplate decorative sheet made of ethylene-acrylic acid copolymer (EAA) and a flame-resistant nameplate decorative sheet made of low density polyethylene (LDPE) Were prepared and subjected to the present test. And
In these adhesive resin layers, an equal amount of a bromo-based flame retardant shown in the following table is blended in each layer. Production method The composition was produced according to the method of the present invention, and the hot-press bonding was performed according to the following procedure. The obtained laminate was placed in a hot-cold continuous press machine, and this was placed at 125 ° C. × 7 kg /
Heat-pressing is performed under the condition of cm ² × 15 minutes, followed by forcible cooling while maintaining the same press pressure, and then pressing is continued until it cools to room temperature. 2) Measurement of Adhesive Strength Strips each having a width of 15 mm (the length direction of the strip is parallel to the grain direction of the veneer) are prepared from the two kinds of decorative fire-resistant precious wood decorative sheets by punching or cutting. And using a knife to make a tear at the leading end of the strip between the first adhesive resin layer and the paper above it, forcing about half the length of the strip therefrom. The test piece was peeled off to the site to prepare a 180-degree peel strength measurement specimen (divided into two pieces at one end). -Measurement 1. -Each of the two specimens produced (three specimens of each kind) is allowed to stand in a room at room temperature for 24 hours, and then, for each specimen taken out, in accordance with general test standards; Normal 180 degree peeling strength (g / 15m
m) was measured. The in-layer peel strength (paper-to-paper peel strength) of the paper itself used for the test flame-resistant precious wood decorative sheet is 1800 g / 15 mm on average. Measurement 2. -Each of the two types of test specimens (three test specimens of each type) was placed in a chamber adjusted to an atmosphere of 40 ° C and a relative humidity of 95% for 7 days.
The sample was left for 3 days in an atmosphere with a relative humidity of 55%, and thereafter, each of the test pieces taken out was measured. The normal 180 ° peeling strength (g / 15 mm) was measured in the same manner as described above. 3) Results The above measurements 1. And measurement 2. The results are shown in the following table.
In this table, the peeling strength represents the average value of the normal 180 ° peeling strength in three tests. FIG.
Is the measurement 1. FIG. 9 is a graph showing the results of measurement 2. 6 is a graph showing the result of the above. The following can be understood from the table and the graph. In a decorative sheet made of a flame-retardant precious wood comprising an LDPE layer as an adhesive resin layer, the adhesive force between the adhesive resin layer and the paper adjacent thereto is rapidly reduced by the addition of the flame retardant, and the flame retardant When only 5% by weight of the compound is blended, the adhesive strength is almost halved as compared with the case where no flame retardant is blended. When the blending amount of the flame retardant is further increased, the interlayer adhesive strength is remarkably reduced, and the adhesive resin layer is formed. Separation easily occurs between the paper and the paper. In particular, when the decorative sheet is exposed to a high-temperature and high-humidity atmosphere, even if it is then returned to a normal-temperature and medium-humidity atmosphere and dried,
The decrease in interlayer adhesion is remarkable, and peeling easily occurs between the adhesive resin layer and the paper. Especially when the amount of the flame retardant is large, the decorative sheet cannot maintain the laminated structure. On the other hand, in the case of a fireproof precious wood decorative sheet made of EAA resin as the adhesive resin layer, the adhesive strength between the adhesive resin layer and the paper adjacent thereto is a small amount (5 wt. %) In the case of addition, it hardly decreases,
Even when the blending amount of the flame retardant is further increased, the progress of the decrease in the interlayer adhesive strength is extremely slow, and when the flame retardant is blended at 20% by weight, the decrease in the adhesive strength starts to be noticeable. Peeling occurs between the paper and the paper. Therefore, it was concluded that an EAA resin layer should be used as the adhesive resin layer, and in that case, the amount of the flame retardant added thereto should be limited to a maximum of about 15%. Be guided.

【００２８】試験例６：接着性樹脂層の水分遮断性能と
難燃剤含有量との関係 1)ＥＡＡ樹脂よりなりかつブロム系難燃剤が以下の表に
示す添加量にて配合された種々の接着性樹脂を調製し、
そして、各々の該樹脂を押出しラミネート法に従って、
紙（坪量３０ｇ／ｍ³ ）とアルミニウム箔（厚さ１５μ
ｍ）との間に押し出し、紙／難燃剤含有の接着性樹脂層
／アルミニウム箔の積層体を製造した。 2)試験法 炭酸ナトリウム１％水溶液を含浸させた脱脂綿の塊を上
記の積層体の紙表面に置き、続いて時計皿で脱脂綿の塊
を覆って水分の揮発を抑える。そして、これをその状態
のまま室温にて１２時間の間放置した。その後、時計皿
を取り外し、積層体を水で洗浄し、室温で乾燥させた。 3)評価 しかる後、得られた積層体のアルミニウム箔の表面を観
察し、腐食痕の発生の有無により、各積層体の接着性樹
脂層は水分遮断性能が良好であるかそれとも不良である
かを判定することとした。腐食痕の発生有りは水分遮断
の性能が不十分であることを意味し、一方、腐食痕の発
生無しは水分遮断の性能が十分良好であることを意味す
る。結果は以下の表に示す。 この表より、難燃剤の配合量が約２０％以上になると、
接着性樹脂層の本来具える水分遮断性能（外部から浸入
した水がさらに内部に浸透するのを妨げ、隣接するアル
ミニウム箔の腐食の発生を防止する性質）が著しく低下
し、アルミニウム箔の腐食の発生が観察されるようにな
ることがわかる。従って、接着性樹脂層への難燃剤の配
合量は最大で、およそ１５％に制限すべきであるとの結
論が導かれる。 Test Example 6 : Relationship between moisture barrier performance of adhesive resin layer and flame retardant content 1) Various adhesives composed of EAA resin and blended with bromo-based flame retardants in the amounts shown in the following table Prepare a functional resin,
And, according to the extrusion lamination method of each of the resins,
Paper (basis weight 30g / m ³ ) and aluminum foil (thickness 15μ)
m) to produce a laminate of paper / adhesive resin layer containing flame retardant / aluminum foil. 2) Test method A lump of absorbent cotton impregnated with a 1% aqueous solution of sodium carbonate is placed on the paper surface of the above-mentioned laminate, and subsequently the lump of absorbent cotton is covered with a watch glass to suppress volatilization of water. This was left as it was at room temperature for 12 hours. Thereafter, the watch glass was removed, and the laminate was washed with water and dried at room temperature. 3) Evaluation After that, the surface of the aluminum foil of the obtained laminate was observed, and whether or not the adhesive resin layer of each laminate had good or poor moisture barrier performance was determined by the presence or absence of corrosion marks. Was determined. The occurrence of corrosion marks means that the performance of moisture barrier is insufficient, while the absence of corrosion marks means that the performance of moisture barrier is sufficiently good. The results are shown in the table below. From this table, when the blending amount of the flame retardant is about 20% or more,
The inherent moisture barrier performance of the adhesive resin layer (the property of preventing the intrusion of water from the outside from penetrating into the inside and preventing the occurrence of corrosion of the adjacent aluminum foil) is significantly reduced, and the corrosion of the aluminum foil is greatly reduced. It can be seen that the occurrence is observed. Therefore, it is concluded that the blending amount of the flame retardant in the adhesive resin layer should be limited to a maximum of about 15%.

【００２９】[0029]

【発明の効果】以上説明したように、本発明によれば、
高い難燃性を有し、建設省告示およびJIS A 1321 に従
う表面燃焼試験において準不燃の性能を満足に発揮する
ことができ、防火材料として優れた製品（防燃性銘木化
粧シート、防燃性銘木化粧板）が提供される。その上、
本発明によれば、突板の変色による製品価値の低下や製
造不良の発生など、従来見られた種々の欠点、問題が起
きないだけでなく、難燃剤の含有による接着力の低下、
腐食の発生、可撓性の低減等、諸性能の悪化をもひき起
こさないという効果が得られる。As described above, according to the present invention,
Highly flame-retardant, satisfactorily exhibits quasi-incombustibility in surface combustion tests in accordance with the notification of the Ministry of Construction and JIS A 1321, and is an excellent product as a fire-resistant material (flame-resistant precious wood decorative sheet, Nameplate). Moreover,
According to the present invention, such as the reduction in product value due to discoloration of the veneer and the occurrence of manufacturing defects, such as the various disadvantages conventionally seen, not only the problem does not occur, but also the decrease in adhesion due to the inclusion of a flame retardant,
The effect of not causing deterioration of various performances such as generation of corrosion and reduction of flexibility can be obtained.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の実施例１の防燃性銘木化粧シートを示
す断面図である。FIG. 1 is a cross-sectional view showing a flameproof precious wood decorative sheet according to Example 1 of the present invention.

【図２】本発明の実施例２の防燃性銘木化粧板を示す断
面図である。FIG. 2 is a cross-sectional view showing a flame-resistant nameplate according to a second embodiment of the present invention.

【図３】図３(A) ないし図３(D) は、図１の防燃性銘木
化粧シートの製造工程を示す図である。FIGS. 3 (A) to 3 (D) are views showing a process of manufacturing the flameproof precious wood decorative sheet of FIG. 1.

【図４】図４(A) ないし図４(D) は、図１の防燃性銘木
化粧シート並びに図２の防燃性銘木化粧板の製造工程を
示す図である。FIGS. 4 (A) to 4 (D) are views showing the steps of manufacturing the flameproof precious wood decorative sheet of FIG. 1 and the flameproof precious wood decorative board of FIG. 2;

【図５】実施例３の防燃性銘木化粧シートを示す断面図
である。FIG. 5 is a cross-sectional view illustrating a flameproof precious wood decorative sheet of Example 3.

【図６】図６は、難燃剤含有の接着性樹脂層の重量と温
度時間面積の関係を示すグラフである。FIG. 6 is a graph showing the relationship between the weight of the adhesive resin layer containing a flame retardant and the temperature time area.

【図７】図７は、アルミニウム箔の重量と温度時間面積
の関係を示すグラフである。FIG. 7 is a graph showing the relationship between the weight of the aluminum foil and the temperature time area.

【図８】図８は、室内静置２４時間後のピーリング強度
と難燃剤の含有量との関係を示すグラフである。FIG. 8 is a graph showing the relationship between the peeling strength and the content of a flame retardant 24 hours after standing indoors.

【図９】図９は、４０℃×９５％ＲＨ中７日間→２５℃
×５５％ＲＨ中３日間後のピーリング強度と難燃剤の含
有量との関係を示すグラフである。FIG. 9: 7 days in 40 ° C. × 95% RH → 25 ° C.
It is a graph which shows the relationship between the peeling strength after 3 days in x55% RH, and the content of a flame retardant.

【符号の説明】[Explanation of symbols]

１ 紙または不織布 ２ 第２の接着性樹脂層 ３ アルミニウム箔 ４ 第１の接着性樹脂層 ５ 紙または不織布 ６ 接着剤層 ７ 銘木単板 ８ 防燃性銘木化粧シート ９ 木質系基材 １３ ガラス繊維シート DESCRIPTION OF SYMBOLS 1 Paper or nonwoven fabric 2 Second adhesive resin layer 3 Aluminum foil 4 First adhesive resin layer 5 Paper or nonwoven fabric 6 Adhesive layer 7 Precious wood veneer 8 Flameproof precious wood decorative sheet 9 Woody base material 13 Glass fiber Sheet

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.⁶ 識別記号 ＦＩ Ｂ３２Ｂ 21/10 Ｂ３２Ｂ 21/10 31/30 31/30 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. ⁶ Identification code FI B32B 21/10 B32B 21/10 31/30 31/30

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】 銘木単板；接着剤層；紙または不織布；
第１の接着性樹脂層；アルミニウム箔またはガラス繊維
シート；第２の接着性樹脂層；紙または不織布がシート
表面より下方へ順に積層され、一体に圧着成形されてな
る化粧単板シートであって、前記第１の接着性樹脂層お
よび第２の接着性樹脂層は、エチレン−アクリル酸共重
合体およびアイオノマーからなる群より各々独立に選択
された樹脂層より成り、かつ、難燃剤が該第１の接着性
樹脂層および第２の接着性樹脂層の各層にそれぞれ、重
量比で５％ないし１５％の量含有されていることを特徴
とする防燃性銘木化粧シート。1. Precious wood veneer; adhesive layer; paper or nonwoven fabric;
A first adhesive resin layer; an aluminum foil or a glass fiber sheet; a second adhesive resin layer; a decorative veneer sheet formed by laminating paper or nonwoven fabric in order from the sheet surface downward and integrally pressing them together. The first adhesive resin layer and the second adhesive resin layer each include a resin layer independently selected from the group consisting of an ethylene-acrylic acid copolymer and an ionomer; A decorative sheet for flame-resistant wood, characterized in that each of the adhesive resin layer (1) and the second adhesive resin layer contains 5 to 15% by weight, respectively. 【請求項２】 請求項１記載の防燃性銘木化粧シート
が、木質系、無機質系または金属系基材の上に貼着され
ていることを特徴とする防燃性銘木化粧板。2. A decorative board made of flame-retardant precious wood, characterized in that the decorative sheet of fire-preventive precious wood according to claim 1 is stuck on a wood-based, inorganic-based or metal-based substrate.