JPH10155831A - Wound coating material and its production - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a process for producing a wound coating material which is capable of executing lamination working while preventing the formation of unshaped pinholes of various shapes in a polyurethane resin film which comes into contact with the skin in particular at the time of lamination working of a nonwoven fabric on the polyurethane resin film, and to obtain the wound coating material which obviates the peeling of execution lumps and the exertion of a mechanical damage on the lesion and is capable of relieving the pain at the time of replacing the wound coating material. SOLUTION: This process for producing the wound coating material 10 includes a stage for coating the surface on the side opposite to the surface to be come into contact with the skin, of the film 13 made of the synthetic resin so as to be formed as its surface into contact with the skin, with the synthetic resin and lamination working a sheet-like material maintaining absorption performance on the synthetic resin in a half-dry state before the synthetic resin dries completely. The pinholes are substantially not formed at the film 13 made of the synthetic resin to be formed as the surface which comes into contact with the skin.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は創傷被覆材に関する
ものであり、より詳しくは、皮膚に接する面とすべく合
成樹脂を製膜してなるフィルムに実質的にピンホール
（傷）のない創傷被覆材及びその製造方法に関するもの
である。すなわち、患部から漏出する及び／又は滲出す
る蛋白成分を含む滲出液、分泌物が、ピンホール中で乾
固して乾固塊となり、当該創傷被覆材の取り換えに際し
て、前記乾固塊が剥がし取られることで、患部に機械的
な損傷を与えたり、疼痛を与えたりすることを緩和する
ことができる創傷被覆材、及びその製造方法に関するも
のである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wound dressing, and more particularly, to a wound made of a synthetic resin film for forming a surface in contact with the skin. The present invention relates to a coating material and a method for manufacturing the same. That is, exudates and secretions containing protein components leaking and / or exuding from the affected area are dried in a pinhole into a dry mass, and when the wound dressing is replaced, the dry mass is peeled off. The present invention relates to a wound dressing capable of mitigating mechanical damage or pain to an affected part by being applied thereto, and a method for producing the same.

【０００２】[0002]

【従来の技術】熱傷、褥創、電撃傷、手術創、化学傷等
の創傷を治療するにあたっては、受傷部位、受傷面積の
大小、受傷深度等によってそれぞれ治療方法が異なるも
のの、創傷面や糜爛面を被覆固定することは、激烈な疼
痛を緩和させたり、創傷面や糜爛面を保護したり、ま
た、感染防止という観点からも、大きな意義がある。2. Description of the Related Art In treating wounds such as burns, pressure sores, electric shocks, surgical injuries, and chemical injuries, the treatment methods differ depending on the site of the injury, the size of the injured area, the depth of the injury, and the like. Covering and fixing the surface is of great significance from the viewpoint of alleviating severe pain, protecting the wound surface and erosion surface, and preventing infection.

【０００３】従来のかかる創傷や面を被覆する方法とし
ては、植皮術、又は凍結乾燥豚皮若しくは新鮮豚皮を
創傷面に貼り付け、疼痛緩和、体液漏出防止、表皮再生
促進等の効果を期待する所謂バイオロジカル ドレッシ
ング（biological dresssing）がある一方、抗生物質
や合成抗菌剤等の抗菌剤を含有するワセリン基剤を薄く
塗布した滅菌シリコン加工ガーゼや、キトサン若しくは
キトサン−コラーゲン複合材料からなる人工皮膚、ある
いは、創傷面や糜爛面に前記抗菌剤を配合したクリー
ム等を塗布し滅菌ガーゼでその全面を被覆した後に包帯
で固定する方法等が知られている。[0003] Conventional methods for covering such wounds and surfaces include skin grafting, or freeze-dried pig skin or fresh pig skin attached to the wound surface, and are expected to have effects such as pain relief, body fluid leakage prevention, and epidermal regeneration promotion. While there is a so-called biological dressing, a sterilized siliconized gauze thinly coated with a vaseline base containing an antibacterial agent such as an antibiotic or a synthetic antibacterial agent, or an artificial skin made of chitosan or chitosan-collagen composite material Alternatively, a method is known in which a cream or the like containing the above-mentioned antibacterial agent is applied to the wound surface or erosion surface, and the entire surface is covered with sterile gauze, and then fixed with a bandage.

【０００４】また、特開平４−３１７６５４号公報に
は、伸縮性を有し抗菌剤が含ませてある不織布と、ポリ
ウレタン樹脂とからなる積層体であって、少なくともポ
リウレタン樹脂フィルムに孔開が形成されている構造に
構成特徴をもつ創傷被覆材が開示されている。Japanese Patent Application Laid-Open No. 4-317654 discloses a laminate comprising a stretchable nonwoven fabric containing an antibacterial agent and a polyurethane resin, wherein at least a polyurethane resin film has perforations. A wound dressing having structural features in the described structure is disclosed.

【０００５】[0005]

【発明が解決しようとする課題】しかしながら、上記
で述べた、創傷面に抗菌剤を配合したクリーム剤等を塗
布し、滅菌ガーゼでその全面を被覆し、包帯で固定する
方法にあっては、通常、滅菌ガーゼを頻繁に取り換える
ことが必要であるので、このガーゼ取り換え作業の煩雑
さに加えて、ガーゼ取り換え作業時に患者さんに苦痛を
与えることがあるとか、治療者にとっては極めて手間暇
のかかる作業になる等の問題があった。また、創傷部位
や糜爛面から漏出する及び／又は滲出する滲出液、分泌
物が、ガーゼに付着し、乾固してなる乾固塊、或いは焼
痂等が、ガーゼ取り換え作業時に、ガーゼとともに剥し
取られ、受傷部位から滲出液、分泌物が再び漏出及び／
又は滲出するようになる。そして、かかる過程は、繰り
返されるという問題があった。However, in the above-mentioned method of applying a cream or the like containing an antibacterial agent to the wound surface, covering the whole surface with sterile gauze, and fixing with a bandage, Usually, it is necessary to change sterilized gauze frequently, and in addition to the complexity of the gauze replacement work, the gauze replacement work may be painful to the patient or extremely time-consuming for the therapist. There were problems such as work. In addition, exudates and secretions leaking and / or exuding from a wound site or an erosion surface adhere to the gauze, and a dry mass or eschar, etc., which is dried and removed together with the gauze during the gauze replacement work. Exudate, secretions are again leaked from the wound site and / or
Or it begins to seep. And there was a problem that such a process was repeated.

【０００６】また、前記４の特開平４−３１７６５４号
公報に記載の創傷被覆材にあっては、皮膚と接するポリ
ウレタン樹脂フィルムに多数の孔開が形成されているた
め、創傷面や糜爛面からの剥離性や水分蒸発制御性にお
いて優れるものの、ポリウレタン樹脂フルムに不織布を
ラミネート加工する際に、不織布を構成する繊維の先端
によって穿孔されるためか、ポリウレタン樹脂フィルム
に大小様々な不定形のピンポール（傷）が形成される。
そのために、創傷部位や糜爛面から漏出及び／又は滲出
する滲出液、分泌物は、このピンホール（傷）内でも乾
固して乾固塊が形成されることとなり、不都合なこと
に、上述したように、この乾固塊は創傷被覆材を取り換
えする際に、被覆材の剥離とともに剥し取られる。した
がって、創傷部位や糜爛面から滲出液、分泌物が再び漏
出及び／又は滲出することになるという問題があった。In the wound dressing described in JP-A-4-317654, since a large number of holes are formed in the polyurethane resin film which is in contact with the skin, the wound dressing may be damaged from the wound surface or erosion surface. Despite its excellent exfoliation and moisture evaporation controllability, when laminating a non-woven fabric to a polyurethane resin film, it may be because the perforations are formed by the tips of the fibers that make up the non-woven fabric. Scratches) are formed.
Therefore, exudates and secretions leaking and / or exuding from the wound site or the erosion surface are dried even in this pinhole (wound) to form a dry solid mass. As described above, when the wound dressing is replaced, the dry mass is peeled off with the peeling of the dressing. Therefore, there is a problem that exudate and secretions leak and / or exude again from the wound site and the erosion surface.

【０００７】本発明はこのような事情に鑑み鋭意開発さ
れたものであって、その解決すべき課題は、従来の創傷
被覆材が具有する上述した問題点を解消することであ
る。そして、その目的とするところは、特には、皮膚と
接するポリウレタン樹脂フィルムに不織布をラミネート
加工する際、このポリウレタン樹脂フィルムに大小様々
な不定形のピンポールが形成されることを防止しつつ、
ラミネート加工できる創傷被覆材の製造方法を提供する
ことであり、また、特には、創傷被覆材の取り換えに際
して、前記乾固塊が剥がし取られることで、患部に機械
的な損傷を与えたり、疼痛を与えたりすることを緩和す
ることができる創傷被覆材を提供することにある。The present invention has been developed in light of the above circumstances, and an object of the present invention is to solve the above-mentioned problems of the conventional wound dressing. And, the purpose of the method is, in particular, when laminating a nonwoven fabric on a polyurethane resin film in contact with the skin, while preventing the formation of irregularly shaped pin poles of various sizes on this polyurethane resin film,
It is intended to provide a method for producing a wound dressing that can be laminated, and in particular, when the wound dressing is replaced, the dry mass is peeled off, thereby causing mechanical damage to the affected area or causing pain. It is an object of the present invention to provide a wound dressing capable of alleviating the application of a wound dressing.

【０００８】[0008]

【課題を解決するための手段】本発明者らは、上記課題
を解決すべく鋭意検討を行った結果、合成樹脂フィルム
のシート状物をラミネート加工する面に合成樹脂をコー
ティングし、該コーティング樹脂が半乾燥の状態で合成
樹脂と吸水性能を有するシート状物をラミネート加工す
ることにより、合成樹脂にピンホールが実質的に形成さ
れずにラミネート加工することができることを見い出
し、本発明を完成するに至った。Means for Solving the Problems The inventors of the present invention have made intensive studies to solve the above problems, and as a result, coated a synthetic resin on a surface of a synthetic resin film sheet to be laminated, and coated the resin with the coating resin. Found that by laminating a synthetic resin and a sheet-like material having a water absorbing property in a semi-dry state, the synthetic resin can be laminated without substantially forming pinholes, thereby completing the present invention. Reached.

【０００９】すなわち、本発明の要旨は、皮膚に接する
面とすべき合成樹脂を製膜してなるフィルムと吸水性能
を保持したシート状物とをラミネート加工して得られる
創傷被覆材であって、該合成樹脂フィルムに実質的にピ
ンホールが形成されていないことを特徴とする創傷被覆
材及びその製造方法に存する。That is, the gist of the present invention is a wound dressing obtained by laminating a film formed of a synthetic resin to be brought into contact with the skin and a sheet-like material having a water absorbing property. And a method for producing the wound dressing, wherein substantially no pinholes are formed in the synthetic resin film.

【００１０】[0010]

【発明の実施の形態】本発明に係る方法を実施するにあ
たり、皮膚に接する面とすべくフィルム状に製膜される
合成樹脂は、密着性、柔軟性、患部からの剥離性、水分
蒸発制御性に優れているものであればどんな合成樹脂で
あっても構わない。かかる合成樹脂としては、ポリビニ
ールアルコール樹脂、アセテート樹脂、ポリエステル樹
脂、ポリアミド樹脂、又はポリウレタン樹脂等が例示で
きる。DESCRIPTION OF THE PREFERRED EMBODIMENTS In carrying out the method according to the present invention, a synthetic resin formed into a film so as to be in contact with the skin has an adhesive property, a flexibility, a releasability from an affected part, and a moisture evaporation control. Any synthetic resin may be used as long as it has excellent properties. Examples of such a synthetic resin include a polyvinyl alcohol resin, an acetate resin, a polyester resin, a polyamide resin, and a polyurethane resin.

【００１１】皮膚に接する面と反対側の面に製膜される
合成樹脂層もまた、上記と同様に、密着性、柔軟性、患
部からの剥離性、水分蒸発制御性に優れているものであ
ればどんな合成樹脂であっても良く、かかる合成樹脂と
しては、ポリビニールアルコール樹脂、アセテート樹
脂、ポリエステル樹脂、ポリアミド樹脂、又はポリウレ
タン樹脂等が例示できる。このうち好ましくはポリウレ
タン樹脂である。The synthetic resin layer formed on the surface opposite to the surface in contact with the skin is also excellent in adhesion, flexibility, releasability from the affected part, and water evaporation control, as described above. Any synthetic resin may be used as long as it is a polyvinyl alcohol resin, an acetate resin, a polyester resin, a polyamide resin, a polyurethane resin, or the like. Of these, a polyurethane resin is preferred.

【００１２】なお、前記各合成樹脂の製造方法、及び透
湿性の高いフィルムの製膜方法はいずれも公知であり、
例えば、特開平４−３１７６５４号公報にかかるポリウ
レタン膜の製造方法が記載されており、これらのことは
いずれも、所謂当業者周知のことである。It is to be noted that a method for producing each of the synthetic resins and a method for producing a film having high moisture permeability are both known.
For example, Japanese Patent Application Laid-Open No. 4-317654 describes a method for producing a polyurethane film, all of which are well known to those skilled in the art.

【００１３】つぎに、本発明の創傷被覆材の製造方法に
ついて、合成樹脂がポリウレタンの場合を例に挙げて説
明する。Next, the method for producing a wound dressing according to the present invention will be described with reference to a case where the synthetic resin is polyurethane.

【００１４】まず、ポリウレタン樹脂を製膜して、透湿
性の高いポリウレタン膜を得る方法として、(1) 基材上
にポリウレタン樹脂溶液を塗布し、凝固槽内で溶媒その
他の共存物を抽出除去する湿式製膜法と、(2) 基材上に
油中水型ポリウレタン樹脂エマルジョンを塗布し、加熱
乾燥することにより多孔質膜とする乾式膜方法、等があ
り、いずれも、本発明の創傷被覆材を製造する方法とし
て活用できるが、前記乾式製膜法、すなわち、ポリウレ
タン樹脂溶液を基材に塗布し、加熱乾燥する方法による
と、安定した透湿性を再現性良く得ることができ、単独
膜でも実用上充分な強度、伸縮性、耐久性のあるものが
得られるため、好ましい。First, a polyurethane resin is formed into a film to obtain a highly permeable polyurethane film. (1) A polyurethane resin solution is applied on a substrate, and a solvent and other coexisting substances are extracted and removed in a coagulation tank. And (2) a water-in-oil type polyurethane resin emulsion is coated on a substrate and dried by heating to form a porous film, and the like. Although it can be used as a method for producing a coating material, the dry film forming method, that is, a method in which a polyurethane resin solution is applied to a substrate and dried by heating, can provide stable moisture permeability with good reproducibility, and can be used alone. It is preferable that the film has sufficient strength, elasticity and durability for practical use.

【００１５】乾式製膜法に使用する基材を特に限定する
ものではないが、ポリエチレン若しくはポリプロピレン
フィルム、ふっ素系若しくはシリコン系のフィルム等が
例示できる。The substrate used in the dry film forming method is not particularly limited, and examples thereof include a polyethylene or polypropylene film, a fluorine-based or silicon-based film, and the like.

【００１６】前記基材上に合成樹脂層を塗布する方法と
しては、特に限定するものではないが、ナイフコータ
ー、ロールコーターの何れもが活用でき、乾燥温度は使
用する乾燥機の性能により適宜設定される。但し、乾燥
不十分とか、急激な脱溶媒が起きない温度範囲である必
要がある。乾燥温度としては、通常、５０〜１８０℃で
あり、好ましくは、６０〜１３０℃である。The method for applying the synthetic resin layer on the substrate is not particularly limited, but any of a knife coater and a roll coater can be used, and the drying temperature is appropriately set according to the performance of the dryer used. Is done. However, the temperature must be within a temperature range in which insufficient drying or rapid desolvation does not occur. The drying temperature is usually from 50 to 180 ° C, preferably from 60 to 130 ° C.

【００１７】本発明において、基材に塗布されてなるポ
リウレタン樹脂のフィルム及び該ポリウレタンフィルム
にコーティングされてなる合成樹脂膜の厚さとして、３
〜１５０μｍ、好ましくは５〜２５μｍである。３μｍ
以下では塗布の際にピンホールができ易く、１５０μｍ
以上であると充分な透湿機能を得難い。In the present invention, the thickness of the polyurethane resin film applied to the substrate and the thickness of the synthetic resin film coated on the polyurethane film are 3
To 150 μm, preferably 5 to 25 μm. 3 μm
In the following, pinholes are easily formed at the time of application, and 150 μm
If it is above, it is difficult to obtain a sufficient moisture permeability function.

【００１８】ポリウレタン樹脂を溶解するための溶媒と
しては、ジメチルホルムアミド（ＤＭＦ）、ジメチルア
セトアミド、ジメチルスルホキシド等の溶解活性の大き
い溶媒が適するものの、これら単独使用の他、トルエ
ン、キシレン等に代表される芳香族系有機溶媒、メチル
エチルケトン、アセトン、シクロヘキサン等に代表され
るケトン系溶媒、酢酸エチル、酢酸ブチル等に代表され
る酢酸エステル系溶媒、ジクロロエタン等に代表される
塩素系溶媒、テトラヒドロフラン（ＴＨＦ）、ジオキサ
ン等に代表されるエーテル系溶媒、メチルアルコール、
エチルアルコール、イソプロピルアルコール等に代表さ
れるアルコール系溶媒からなる群から選ばれた単独の溶
媒若しくは同じ群から選ばれた複数の混合溶媒、又は、
前記群を異にする２種以上の混合溶媒が使用できる。な
お、基材上にコーテイングされるポリウレタン樹脂を溶
解するための溶媒と、ついで、基材上に製膜されたポリ
ウレタンフィルムの、基材が備えられた面と反対側の全
面にコーテイングされるポリウレタン樹脂の溶液を溶解
するための溶媒とは、両者が共に同一の溶媒（混合溶媒
を含む）であっても、両者が互いに相違する前記群から
選択された溶媒であっても、或いは、同一の群に属する
異なる溶媒（化学分子）であってよい。該ポリウレタン
溶液は、通常、５〜３０重量％の濃度で用いられ、好ま
しくは１０〜２５重量％である。As a solvent for dissolving the polyurethane resin, a solvent having high dissolving activity such as dimethylformamide (DMF), dimethylacetamide, dimethylsulfoxide and the like is suitable, but in addition to these alone, toluene, xylene and the like are used. Aromatic organic solvents, ketone solvents represented by methyl ethyl ketone, acetone, cyclohexane, etc .; acetate solvents represented by ethyl acetate, butyl acetate, etc .; chlorine solvents represented by dichloroethane, etc .; tetrahydrofuran (THF); Ether solvents such as dioxane, methyl alcohol,
Ethyl alcohol, a single solvent selected from the group consisting of alcohol solvents represented by isopropyl alcohol, or a plurality of mixed solvents selected from the same group, or
Two or more kinds of mixed solvents belonging to different groups can be used. In addition, a solvent for dissolving the polyurethane resin coated on the substrate, and then the polyurethane coated on the entire surface of the polyurethane film formed on the substrate opposite to the surface on which the substrate is provided. The solvent for dissolving the resin solution may be either the same solvent (including a mixed solvent), a solvent selected from the above-mentioned group different from each other, or the same solvent. It may be a different solvent (chemical molecule) belonging to the group. The polyurethane solution is usually used at a concentration of 5 to 30% by weight, preferably 10 to 25% by weight.

【００１９】つぎに、基材上に剥離剤を介して製膜され
たポリウレタンフィルムの上に、例えば不織布のごとき
シート状物を積層した状態となるよう固着する方法につ
いて説明する。Next, a method will be described in which a sheet-like material such as a nonwoven fabric is laminated on a polyurethane film formed on a base material via a release agent, for example.

【００２０】まず、基材上に剥離剤を介して製膜された
ポリウレタンフィルムの、基材が備えられた面と反対側
の全面に、ポリウレタン樹脂溶液を塗布し、該ポリウレ
タン樹脂溶液が半乾燥状態となった時点で不織布を重ね
合わせ、押圧して添着したまままの状態で加熱乾燥す
る。ここで、半乾燥状態とは、該合成樹脂溶液の濃度
が、５０〜９０重量％である場合をいい、使用する合成
樹脂によって異なるが、乾燥温度又は乾燥時間を調整す
ることによって製造する。First, a polyurethane resin solution is applied to the entire surface of a polyurethane film formed on a base material via a release agent, on the side opposite to the surface provided with the base material, and the polyurethane resin solution is semi-dried. When the state is reached, the nonwoven fabrics are overlaid, pressed and heated and dried while they are still attached. Here, the semi-dry state refers to the case where the concentration of the synthetic resin solution is 50 to 90% by weight, which varies depending on the synthetic resin used, but is produced by adjusting the drying temperature or the drying time.

【００２１】ポリウレタン樹脂溶液を塗布する方法や、
ポリウレタン樹脂を溶解するための溶媒を特に限定する
ものではないことは、上述したとおりである。A method of applying a polyurethane resin solution,
As described above, the solvent for dissolving the polyurethane resin is not particularly limited.

【００２２】本発明に使用される例えば不織布は伸長性
をもつものが使用される。一般に、不織布は平滑な面に
細い繊維を吹き付け、この繊維を相互に絡ませたり、溶
着若しくは接着して製造することができる。本発明を実
施する場合は、特に伸張度の大きい不織布を使用するこ
とが好ましい。For example, the nonwoven fabric used in the present invention has elongation. In general, a nonwoven fabric can be manufactured by spraying fine fibers on a smooth surface, and tangling, welding or bonding the fibers together. When carrying out the present invention, it is preferable to use a nonwoven fabric having a particularly high degree of elongation.

【００２３】また、不織布の厚さを特に制限するもので
はないが、柔軟性、耐久性、作業性、吸水性等を考慮す
ることが必要であり、０．５〜５．０ｍｍ程度、好まし
くは０．５〜３ｍｍのものが望ましい。The thickness of the nonwoven fabric is not particularly limited, but it is necessary to consider flexibility, durability, workability, water absorption and the like, and it is about 0.5 to 5.0 mm, preferably about 0.5 to 5.0 mm. 0.5 to 3 mm is desirable.

【００２４】不織布の素材としては、柔軟性、耐久性、
作業性、吸水性等を考慮すると、木材パルプや木綿に代
表される天然繊維、レーヨン、キュプラに代表される再
生繊維、アセテート等に代表される半合成繊維、ナイロ
ン、ポリエステル、アクリル等に代表される合成繊維等
が好ましい。As the material of the nonwoven fabric, flexibility, durability,
Considering workability, water absorption, etc., natural fibers represented by wood pulp and cotton, regenerated fibers represented by rayon, cupra, semi-synthetic fibers represented by acetate, nylon, polyester, acrylic, etc. Synthetic fibers are preferred.

【００２５】本発明の創傷被覆材では、前記合成樹脂フ
ィルム及び吸水性能を保持したシート状物の一方又は両
方に、ぶどう球菌やレンサ球菌に代表されるグラム陽性
菌、緑膿菌や枯草菌に代表されるグラム陰性桿菌等、様
々な病原性細菌、特には、化膿菌に対して感受性が期待
される抗生物質や半合成抗生物質、あるいは合成抗菌剤
等の抗菌剤を含有させることができ、該抗菌剤として
は、ナリジキシン酸系やニトロフラゾン系、或いはサル
ファ剤等の化学抗菌剤の他に、ペニシリン系、マクロラ
イド系、アミノグリコシド系、セファロスポリン系、ク
ロラムフェニコール系、テトラサイクリン系、ポリペプ
チド系、リンコマイシン系、或いは、ポリエン系の抗生
物質等が例示できる。[0025] In the wound dressing of the present invention, one or both of the synthetic resin film and the sheet-like material having a water-absorbing property can be used for gram-positive bacteria represented by staphylococci and streptococci, Pseudomonas aeruginosa and Bacillus subtilis. Various pathogenic bacteria such as gram-negative bacilli represented, in particular, can contain antibacterial agents such as antibiotics and semi-synthetic antibiotics expected to be susceptible to S. pyogenes, or synthetic antibacterial agents, Examples of the antibacterial agent include nalidixic acid, nitrofurazone, and chemical antibacterial agents such as sulfa drugs, penicillin, macrolide, aminoglycoside, cephalosporin, chloramphenicol, tetracycline, and polypeptide. , Lincomycin or polyene antibiotics.

【００２６】これら抗菌剤を含有させる方法としては、
合成樹脂原料若しくは前記シート状物に配合するとか、
前記シート状物に含浸させるとか、前記シート状物に抗
菌剤を含有させたポリマー溶液を吹き付けて担持させる
とかすればよく、抗菌剤の含有量は抗菌剤の種類、使用
目的によりそれぞれ相違するから、場合に応じて適宜決
定される。As a method for containing these antibacterial agents,
To be mixed with synthetic resin raw material or the sheet-like material,
The sheet-like material may be impregnated or the sheet-like material may be supported by spraying a polymer solution containing an antibacterial agent, since the content of the antibacterial agent differs depending on the type of the antibacterial agent and the purpose of use. Is appropriately determined according to the case.

【００２７】本発明においては、コーティングされた樹
脂が半乾燥状態である合成樹脂フィルムと、吸水性を有
するシート状物とをロール機等を用いて押圧することに
より、積層することができる。その後、得られた積層物
を完全に乾燥させることで、本発明の創傷被覆材を得る
ことができる。In the present invention, a synthetic resin film in which the coated resin is in a semi-dry state and a water-absorbing sheet-like material can be laminated by pressing with a roll machine or the like. Thereafter, the wound dressing of the present invention can be obtained by completely drying the obtained laminate.

【００２８】本発明の創傷被覆材は、孔開が形成されて
いると好適である。孔開は多数のカッター刃の埋め込ま
れたローラー（彫刻ローラーを含む）等を積層体のフィ
ルム面にころがし、孔開を形成するような方法で良い。
孔開の形は針穴状、パンチ穴状、十文字状や一文字状の
スリット状が考えられるが、とくに一文字状のスリット
状が良い。スリットの長さは２ｍｍ〜７ｍｍ程度が好ま
しく、スリットは並列状、千鳥状等、任意に配列され
る。The wound dressing of the present invention is preferably provided with perforations. The holes may be formed by rolling a roller (including an engraving roller) having a large number of cutter blades on the film surface of the laminate to form the holes.
The shape of the hole may be a needle hole, a punch hole, a cross-shaped or a single-letter slit, and a single-letter slit is particularly preferable. The length of the slit is preferably about 2 mm to 7 mm, and the slits are arranged arbitrarily, such as in a side-by-side or staggered manner.

【００２９】この孔開の役割は、創傷被覆材使用初期に
は、漏出、滲出する体液の発生が多いので、ドレナージ
を良くするためのものであり、複合シートに機械的に小
さな穴を開け、漏出、滲出する体液の貯留を防止する。
創傷被覆材使用後、しばらくすると漏出、滲出する体液
の発生が少なくなり、この液の乾化により、穴は閉ざさ
れる。このため、それ以降は複合シート自体に高い透湿
性が要求される。従って、ポリウレタンフィルムには高
い透湿性が必要となるのである。The role of the perforation is to improve drainage since a large amount of body fluid leaks and exudes at the initial stage of use of the wound dressing, so that a small hole is mechanically formed in the composite sheet. Prevents leakage and exudation of bodily fluids.
Shortly after the use of the wound dressing, the generation of leaking and exuding bodily fluids is reduced, and the holes are closed due to drying of the fluid. Therefore, thereafter, the composite sheet itself is required to have high moisture permeability. Therefore, high moisture permeability is required for the polyurethane film.

【００３０】本発明の創傷被覆材は、使用時に合成樹脂
フィル側についている基材を剥し、合成樹脂フィルムが
創傷部に接するようにして使用する。使用形態として
は、包帯状や数ｃｍから数十ｃｍのパット状等任意であ
る。傷の程度、大きさに応じ選択して用いられる。パッ
ト状の創傷被覆材の場合、テープや包帯等で固定する必
要が生ずるので使い勝手から包帯状とするのが良い。The wound dressing of the present invention is used in such a manner that the base material on the synthetic resin fill side is peeled off at the time of use so that the synthetic resin film is in contact with the wound. The mode of use is arbitrary such as a bandage shape, a pad shape of several cm to several tens cm, and the like. Select and use according to the degree and size of the scratch. In the case of a pad-shaped wound dressing, it is necessary to fix the wound dressing with a tape, a bandage, or the like.

【００３１】[0031]

【実施例】以下、本発明を具体化した実施例に基づいて
詳細に説明するが、本発明は以下の実施例の内容に限定
されるものではない。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in detail below with reference to embodiments that embody the present invention, but the present invention is not limited to the following embodiments.

【００３２】製造例 ポリプロピレン系剥離剤を塗布した剥離紙上に、０．５
重量％シルバースルファジアジンを含有する２０重量％
ポリウレタン樹脂エタノール溶液を塗布し、ナイフコー
ターを用いて、乾燥温度８０℃で、加熱乾燥することに
より、厚さが８μｍの多孔質ポリウレタンフィルムを製
膜した。ついで、前記剥離紙上に製膜させたポリウレタ
ンフィルム１３の、剥離紙が備えられた面と反対側の全
面に、０．５重量％シリバースルファジアジンを含有す
る２０重量％ポリウレタン樹脂エタノール溶液を塗布
し、該ポリウレタン樹脂溶液の濃度が５０重量％程度と
なった所謂半乾燥状態の時点で、ポリエステル繊維から
なる厚さが１．０ｍｍの不織布を重ね合わせ、ついで、
押圧して添着させたままの状態で、乾燥温度８０℃にて
加熱乾燥した。このようにして得られた創傷被覆材１０
のうち、ポリウレタン樹脂膜の全厚は、１５μｍであ
る。Production Example On a release paper coated with a polypropylene-based release agent,
20% by weight containing silver by weight sulfadiazine
An ethanol solution of a polyurethane resin was applied and heated and dried at a drying temperature of 80 ° C. using a knife coater to form a porous polyurethane film having a thickness of 8 μm. Then, an ethanol solution of 20% by weight polyurethane resin containing 0.5% by weight of silver sulfadiazine was applied to the entire surface of the polyurethane film 13 formed on the release paper opposite to the surface provided with the release paper. At the time of the so-called semi-dry state in which the concentration of the polyurethane resin solution became about 50% by weight, a 1.0 mm-thick non-woven fabric made of polyester fibers was overlapped.
It was heated and dried at a drying temperature of 80 ° C. while being pressed and attached. Wound dressing material 10 thus obtained
Among them, the total thickness of the polyurethane resin film is 15 μm.

【００３３】図１は、剥離紙上に最初に製膜されたポリ
ウレタンフィルムの剥離紙を剥離した時の走査型電子顕
微鏡写真であり、図２はその概略を図示した説明図であ
る。図より、皮膚に接する面には、ピンホール１５が形
成されていないことが解る。FIG. 1 is a scanning electron microscope photograph when the release paper of the polyurethane film formed first on the release paper is peeled off, and FIG. 2 is an explanatory view schematically showing the same. From the figure, it can be seen that the pinhole 15 is not formed on the surface in contact with the skin.

【００３４】従来例 ポリプロピレン系剥離剤を塗布した剥離紙上に、０．５
重量％シルバースルファジアジンを含有する２０重量％
ポリウレタン樹脂エタノール溶液を塗布し、該ポリウレ
タン樹脂溶液の濃度が５０重量％程度となった所謂半乾
燥状態の時点で、ポリエステル繊維からなる厚さが１．
０ｍｍの不織布を重ね合わせ、ついで、押圧して添着さ
せたままの状態で、乾燥温度８０℃にて加熱乾燥した。
このようにして得られた従来例の創傷被覆材２０におい
て、ポリウレタン樹脂膜２３の全厚は、１８μｍであ
る。Conventional Example 0.5 μm on a release paper coated with a polypropylene release agent.
20% by weight containing silver by weight sulfadiazine
A polyurethane resin ethanol solution is applied, and when the concentration of the polyurethane resin solution becomes about 50% by weight, in a so-called semi-dry state, the thickness of the polyester fiber becomes 1.
A non-woven fabric of 0 mm was overlapped, and then heated and dried at a drying temperature of 80 ° C. in a state where it was pressed and adhered.
In the wound dressing material 20 of the conventional example thus obtained, the total thickness of the polyurethane resin film 23 is 18 μm.

【００３５】図３は、剥離紙上に最初に製膜されたポリ
ウレタンフィルムの剥離紙を剥離した時の走査型電子顕
微鏡写真であり、図４はその概略を図示した説明図であ
る。図より、皮膚に接する面には、大小様々で不定形の
ピンホール２５が多数形成されていることが解る。FIG. 3 is a scanning electron microscope photograph when the release paper of the polyurethane film formed first on the release paper is peeled off, and FIG. 4 is an explanatory view schematically showing the same. It can be seen from the figure that a large number of irregularly shaped pinholes 25 are formed on the surface in contact with the skin.

【００３６】ところで、上述した上述した製造例の創傷
被覆材の製造方法及び該製造方法によって作成された創
傷被覆材は、本発明の代表的な実施態様として述べたも
のであり、本発明は前記製造例に限定されるものではな
く、本発明を実施する場合には、例えばポリウレタンフ
ィルを叙上の他の合成樹脂フィルムに変更するとか等、
この発明の趣旨から逸脱しない範囲で適宜変更して実施
できる。By the way, the method of manufacturing the wound dressing of the above-mentioned manufacturing example and the wound dressing prepared by the manufacturing method have been described as typical embodiments of the present invention. The present invention is not limited to the production examples, and when practicing the present invention, for example, changing the polyurethane fill to another synthetic resin film described above,
The present invention can be appropriately modified and implemented without departing from the spirit of the present invention.

【００３７】[0037]

【発明の効果】本発明の創傷被覆材によれば、合成樹脂
層に実質的にピンホールがないため、患部から漏出及び
／又は滲出する分泌物が創傷被覆材の内部で乾固して乾
固塊となることで、創傷被覆材の取り換え時に、患部に
機械的な損傷を与えたり、疼痛を与えたりする、という
ことを緩和できる。According to the wound dressing of the present invention, since there is substantially no pinhole in the synthetic resin layer, secretions leaking and / or exuding from the affected part are dried and dried inside the wound dressing. By forming a solid mass, it is possible to reduce mechanical damage or pain to the affected area when the wound dressing is replaced.

【図面の簡単な説明】[Brief description of the drawings]

【図１】図１は、剥離紙上に最初に製膜されたポリウレ
タンフィルムの剥離紙を剥離した時の走査型電子顕微鏡
写真である。BRIEF DESCRIPTION OF DRAWINGS FIG. 1 is a scanning electron microscope photograph of a polyurethane film release film first formed on a release paper.

【図２】図２は図１の概略を図示した説明図である。FIG. 2 is an explanatory view schematically showing FIG. 1;

【図３】図３は、剥離紙上に最初に製膜されたポリウレ
タンフィルムの剥離紙を剥離した時の走査型電子顕微鏡
写真である。FIG. 3 is a scanning electron micrograph when a release film of a polyurethane film formed first on a release paper is peeled off.

【図４】図４は図３の概略を図示した説明図である。FIG. 4 is an explanatory view schematically showing FIG. 3;

【付号の説明】[Description of numbering]

１０…本発明の創傷被覆材 １３…ポリウレタン膜 １５…ピンホール ２０…本発明の創傷被覆材 ２３…ポリウレタン膜 ２５…ピンホール DESCRIPTION OF SYMBOLS 10 ... Wound dressing material of this invention 13 ... Polyurethane film 15 ... Pinhole 20 ... Wound dressing material of this invention 23 ... Polyurethane film 25 ... Pinhole

───────────────────────────────────────────────────── フロントページの続き (72)発明者 横塚 征一郎 東京都千代田区丸の内２丁目５番２号 三 菱化学株式会社内 (72)発明者 太田 隆之 東京都千代田区丸の内２丁目５番２号 三 菱化学株式会社内 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Seiichiro Yokozuka 2-5-2-2 Marunouchi, Chiyoda-ku, Tokyo Sankyo Chemical Co., Ltd. (72) Inventor Takayuki Ota 2-5-2-2, Marunouchi, Chiyoda-ku, Tokyo 3 Ryo Chemical Co., Ltd.

Claims (10)

【特許請求の範囲】[Claims] 【請求項１】 皮膚に接する面とすべき合成樹脂を製膜
してなるフィルムと吸水性能を保持したシート状物とを
ラミネート加工して得られる創傷被覆材の製造方法であ
って、 該合成樹脂フィルム面のうちシート状物をラミネート加
工する面に合成樹脂がコーティングされ、該コーティン
グされた樹脂が半乾燥の状態で該合成樹脂フィルムと吸
水性能を保持したシート状物とをラミネート加工する工
程を含むことを特徴とする創傷被覆材の製造方法。1. A method for producing a wound dressing obtained by laminating a film formed of a synthetic resin to be brought into contact with the skin and a sheet-like material having a water absorbing property, A step of laminating the synthetic resin film with a sheet-like material having a water-absorbing property in a state where the surface of the resin film on which the sheet-like material is to be laminated is coated with a synthetic resin, and the coated resin is in a semi-dry state; A method for producing a wound dressing, comprising: 【請求項２】 前記創傷被覆材の製造方法において、 コーティング樹脂層を含む合成樹脂層若しくは前記シー
ト状物層のいずれか一方又は両方に抗菌剤が含まれてい
ることを特徴とする請求項１記載の創傷被覆材の製造方
法。2. The method for producing a wound dressing according to claim 1, wherein one or both of the synthetic resin layer including the coating resin layer and the sheet-like material layer contains an antimicrobial agent. A method for producing the wound dressing described above. 【請求項３】 前記創傷被覆材の製造方法において、 前記シート状物が不織布であることを特徴とする請求項
１又は２記載の創傷被覆材の製造方法。3. The method for producing a wound dressing according to claim 1, wherein the sheet-like material is a nonwoven fabric. 【請求項４】 前記創傷被覆材の製造方法において、 前記シート状物にラミネートされた合成樹脂フィルム層
の全厚が、２００μｍ以下であることを特徴とする請求
項１〜３のいずれか記載の創傷被覆材の製造方法。4. The method for producing a wound dressing according to claim 1, wherein a total thickness of the synthetic resin film layer laminated on the sheet-like material is 200 μm or less. A method for producing a wound dressing. 【請求項５】 皮膚に接する面とすべき合成樹脂を製膜
してなるフィルムと吸水性能を保持したシート状物とを
ラミネート加工して得られる創傷被覆材であって、 該合成樹脂フィルムに実質的にピンホールが形成されて
いないことを特徴とする創傷被覆材。5. A wound dressing obtained by laminating a film formed of a synthetic resin to be brought into contact with the skin and a sheet-like material having water absorption performance, wherein the synthetic resin film A wound dressing, wherein substantially no pinhole is formed. 【請求項６】 前記創傷被覆材において、 皮膚に接する面とすべき合成樹脂を製膜してなるフィル
ムの前記シート状物をラミネート加工する面に、合成樹
脂をコーティングし、該コーティングされた合成樹脂が
半乾燥の状態で、吸収性能を保持したシート状物をラミ
ネート加工してなる積層体構造を有することを特徴とす
る請求項５記載の創傷被覆材。6. The wound dressing, wherein a synthetic resin is coated on a surface of a film formed of a synthetic resin to be in contact with the skin, on which the sheet is laminated, and the coated synthetic resin is coated. The wound dressing according to claim 5, wherein the resin has a laminated structure obtained by laminating a sheet-like material having absorption performance in a semi-dry state. 【請求項７】 前記コーティング樹脂層を含む合成樹脂
層、若しくは前記吸収性能を保持したシート状物のいず
れか一方又は両方に、抗菌剤が含まれていることを特徴
とする請求項５又は６記載の創傷被覆材。7. An antibacterial agent is contained in one or both of the synthetic resin layer including the coating resin layer and the sheet-like material having the absorption performance. The wound dressing according to any one of the preceding claims. 【請求項８】 前記シート状物は、不織布であることを
特徴とする請求項５〜７のいずれかに記載の創傷被覆
材。8. The wound dressing according to claim 5, wherein the sheet is a nonwoven fabric. 【請求項９】 前記創傷被覆材において、 直径１０μｍ以上１ｍｍ以下のピンホールが１００箇所
／ｃｍ²以下であることを特徴とする請求項５〜７のい
ずれか記載の創傷被覆材。9. The wound dressing according to claim 5, wherein in the wound dressing, pinholes having a diameter of 10 μm or more and 1 mm or less are provided at 100 points / cm ² or less. 【請求項１０】 前記創傷被覆材において、 前記シート状物にラミネートされた合成樹脂フィルム層
の全厚が、２００μｍ以下であることを特徴とする請求
項６〜９のいずれか記載の創傷被覆材。10. The wound dressing according to claim 6, wherein the total thickness of the synthetic resin film layer laminated on the sheet-like material is 200 μm or less. .