JPH10148799A - Colored article and production of colored article - Google Patents

Abstract

PROBLEM TO BE SOLVED: To improve the appearance and optical characteristics of a half-coated colored article by including a process to atomize a dye or an org. resin coating material containing a pigment and to spray it on the surface of a base body to form a colored region and a process to spray a transparent org. resin coating material to coat a region except for the colored region. SOLUTION: The production method of a colored article includes a process to inject a dye or an org. resin coating material containing a pigment with a gas to atomize the dye or the org. resin coating material containing a pigment and to spray the atomized material on the surface of a base body to form a colored region, and a process to spray an transparent org. resin coating material on a region except for the colored region. As for the pigment, an org. pigment such as phthalocyanine, perylene, isoindolinone pigments are preferably used. The particle size of the pigment is 0.05 to 0.2μm, and preferably about 0.1μm.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は基材表面に着色領域
と非着色領域が存在するようなハーフコートされた着色物品及
びその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a half-coated colored article having a colored area and a non-colored area on the surface of a substrate, and a method for producing the same.

【０００２】[0002]

【従来の技術】従来、プラスチックやガラス等の基材を
着色する場合、着色方法としては、刷毛塗りや浸漬法、
スピナー法等が知られてた。また最近では、スプレーを
用い塗布するスプレー塗装法が試みられている。そして
スプレー塗装法を用いれば、従来の着色よりも塗装面の
平滑性が向上する利点があった。特開昭６４−１１１８
６号公報では、顔料等の色素材料を含んだ有機樹脂塗料
をスプレー塗装法により透明材料に塗布する開示がなさ
れている。また特開平６−４９２４８号公報には、有
色、透明で粒子径が1．0ミクロン以下の顔料をスプレー塗装
法等で塗布することが記載されている。2. Description of the Related Art Conventionally, when coloring a base material such as plastic or glass, the coloring method includes brushing or dipping,
The spinner method was known. In recent years, a spray coating method of applying using a spray has been attempted. When the spray coating method is used, there is an advantage that the smoothness of the coated surface is improved as compared with the conventional coloring. JP-A 64-1118
Japanese Patent Application Laid-Open No. 6-26139 discloses that an organic resin paint containing a pigment material such as a pigment is applied to a transparent material by a spray coating method. JP-A-6-49248 describes that a pigment having a particle size of 1.0 μm or less is coated by a spray coating method or the like.

【０００３】[0003]

【発明が解決しようとする課題】本発明者は、従来の方
法により製造されたハーフコートされた着色物品の表面を観察
した。その結果、色むらや面不良等が生じ、外観上の問
題が発生した。特に眼鏡プラスチックレンズなどの光学
物品を製造した場合には干渉縞が発生する問題点が生じ
た。The present inventors have observed the surface of a half-coated colored article manufactured by a conventional method. As a result, color unevenness, surface defects, and the like occurred, and a problem in appearance occurred. In particular, when optical articles such as spectacle plastic lenses are manufactured, there is a problem that interference fringes occur.

【０００４】[0004]

【課題を解決するための手段】本発明者は、顔料を含む
有機樹脂塗料を用いスプレー塗装法によりハーフコートを行
い、このハーフコートされた着色プラスチック物品の表面を詳
細に観察した。その結果、表面の面不良は、着色領域と
着色されていない領域との境界部分で顕著であることが
判った。また着色されていない領域の表面にはざらつき
が存在していることが判った。Means for Solving the Problems The present inventor performed half-coating by a spray coating method using an organic resin paint containing a pigment, and observed the surface of the half-coated colored plastic article in detail. As a result, it was found that the surface defect was remarkable at the boundary between the colored region and the uncolored region. It was also found that the surface of the uncolored area had roughness.

【０００５】これらの原因を探ったところ、基材表面の
着色領域と着色されていない領域との境界部分では、着
色領域における境界付近の塗膜の膜厚が特に薄くなるた
め面不良や色むらが発生し易くなることが判った。また
着色領域と着色領域以外の領域との間で膜厚差が生じる
ために、干渉縞が発生し易くなることも判った。更に着
色されていない領域表面のざらつきの発生は、飛散した
顔料のミストが着色されていない領域の表面に付着する
ために発生することが判った。更に、スプレーを用い顔
料を含む有機樹脂塗料や染料を霧化する際、空気と共に
有機樹脂塗料を高圧にて噴出するために、塗膜の厚いと
ころではかえりが出易くなることが判った。さらに、塗
膜の薄いところでは高圧に噴射される空気が既に表面に
付着した顔料を含む有機樹脂塗料を乾燥させ、この乾燥
した表面に部分的に液状の顔料が付着することから着色
表面に凹凸が発生してしまうことが判った。[0005] When these causes were investigated, at the boundary between the colored region and the uncolored region on the surface of the base material, the thickness of the coating film near the boundary in the colored region was particularly thin, so that surface defects and color unevenness were observed. It has been found that liability is likely to occur. Further, it was also found that interference fringes tend to occur because a difference in film thickness occurs between the colored region and a region other than the colored region. Further, it has been found that the roughness of the surface of the non-colored area occurs because the mist of the scattered pigment adheres to the surface of the non-colored area. Further, it has been found that when atomizing an organic resin paint or dye containing a pigment using a spray, the organic resin paint is ejected at a high pressure together with air, so that burrs are likely to appear at a thick film. Furthermore, where the coating film is thin, air jetted at a high pressure dries the organic resin paint containing the pigment that has already adhered to the surface, and the liquid pigment partially adheres to the dried surface. Was found to occur.

【０００６】そこで本発明者は、基材表面の着色領域と
非着色領域の構成及び着色領域形成時の塗料の噴霧条件
を改善することにし、本発明を成すに至った。本発明
は、第一に「顔料を有する有機樹脂塗料又は染料を気体
と共に噴出させることにより前記顔料を有する有機樹脂
塗料又は染料を霧化させ、これを基材表面に噴霧し塗布
することで着色領域を形成する工程と、該着色領域以外
の領域に透明有機樹脂塗料を噴霧し塗布する工程を有す
ることを特徴とする着色物品の製造方法（請求項１）」
を提供する。第二に「前記着色領域を形成する場合にお
ける気体の噴出圧力が約２．５kg/cm２よりも低い圧力
であることを特徴とする請求項１記載の製造方法 （請求項２）」を提供する。第三に「基材表面に顔料を
有する有機樹脂塗料又は染料を含む有機物が噴霧された
着色領域と該着色領域以外の領域に透明有機樹脂塗料が
噴霧された非着色領域を有する着色物品（請求項
３）」。第四に「前記着色領域において、濃度が相対的
に濃い部分の膜厚が相対的に薄い部分の膜厚に比べて厚
いことを特徴とする請求項３記載の着色物品（請求項
４）」を提供する。Therefore, the present inventor has improved the structure of the colored region and the non-colored region on the surface of the base material and the spraying conditions of the paint at the time of forming the colored region, thereby completing the present invention. First, the present invention provides a method of spraying an organic resin paint or dye having a pigment by spraying an organic resin paint or a dye having a pigment together with a gas, and spraying and applying the sprayed paint onto the surface of a base material. A method for producing a colored article, comprising: a step of forming an area; and a step of spraying and applying a transparent organic resin paint to an area other than the colored area (claim 1).
I will provide a. Secondly, there is provided "the manufacturing method according to claim 1, wherein the jet pressure of gas when forming the colored region is a pressure lower than about 2.5 kg / cm <2>". . Thirdly, "a colored article having a colored region sprayed with an organic resin paint having a pigment or an organic material containing a dye on the surface of a substrate and a non-colored region sprayed with a transparent organic resin paint in a region other than the colored region (claim) Item 3). " Fourth, "the colored article according to claim 3 (claim 4), wherein in the colored region, the thickness of the portion where the density is relatively high is thicker than the thickness of the portion where the density is relatively thin. I will provide a.

【０００７】[0007]

【発明の実施の形態】本発明に関わる着色物品において
は、着色領域以外の領域にスプレー塗装法により透明性
に優れた有機樹脂塗料が塗布された非着色領域が形成さ
れたものである。更に着色領域は濃度の濃い部分から徐
々に薄い部分が存在するような濃度勾配を有するもので
ある。BEST MODE FOR CARRYING OUT THE INVENTION In a colored article according to the present invention, a non-colored area in which an organic resin paint having excellent transparency is applied by spray coating to an area other than the colored area. Further, the colored region has a density gradient such that a portion having a high density gradually decreases from a portion having a high density.

【０００８】着色領域には顔料を含む有機樹脂塗料又は
染料が塗布される。顔料を含む有機樹脂塗料とは透明樹
脂中に顔料が分散されたものである。使用可能な顔料と
有機樹脂塗料を以下に例示する。顔料としては、フタロシアニ
ン系、ペリレン系、イソインドリノン系等の有機顔料が
好ましく使用される。顔料の粒径は、0.05ミクロン〜0.2ミクロ
ンであるが、0.1ミクロン程度が好ましい。0.05ミクロン以下であ
ると耐光性が低下する問題点が有り、0.2ミクロンより大き
くなると着色領域は不透明になってしまうことがある。An organic resin paint or dye containing a pigment is applied to the colored area. The organic resin paint containing a pigment is one in which a pigment is dispersed in a transparent resin. Examples of usable pigments and organic resin paints are shown below. As the pigment, an organic pigment such as a phthalocyanine-based, perylene-based or isoindolinone-based pigment is preferably used. The particle size of the pigment is from 0.05 micron to 0.2 micron, preferably about 0.1 micron. If it is less than 0.05 micron, there is a problem that light resistance is reduced, and if it is more than 0.2 micron, the colored region may become opaque.

【０００９】顔料を分散する有機樹脂塗料としてはアクリル
系樹脂、ポリエステル系樹脂、エポキシ系樹脂等を用い
ることが好ましい。また染料としては、カヤロンポリエステ
ルブルー、レッド、イエロー（日本化薬社製）やミケトンポ
リエステルイエロー、レッド、ブルー等一般に市販されてい
る染料を使用することができる。顔料が分散された樹脂
塗料には、塗布性の向上のためにシンナー等の稀釈剤を
添加することも可能である。非着色領域には顔料を含ま
ない透明性に優れた有機樹脂塗料が塗布される。この有
機樹脂塗料はクリヤーコートとも呼ばれ、エポキシ系樹
脂、アクリル系樹脂、ポリビニルブチラール系樹脂等が
用いられる。またこの有機樹脂塗料は、顔料の分散に用
いられるものと同じものが使用可能である。As the organic resin paint in which the pigment is dispersed, it is preferable to use an acrylic resin, a polyester resin, an epoxy resin or the like. As the dye, generally available dyes such as Kayaron polyester blue, red, and yellow (manufactured by Nippon Kayaku Co., Ltd.) and Miketone polyester yellow, red, and blue can be used. It is also possible to add a diluent such as thinner to the resin coating material in which the pigment is dispersed to improve coatability. The non-colored area is coated with an organic resin paint having no pigment and excellent transparency. The organic resin paint is also called a clear coat, and an epoxy resin, an acrylic resin, a polyvinyl butyral resin, or the like is used. The same organic resin paint as that used for dispersing the pigment can be used.

【００１０】本発明では前記の如く顔料を含む樹脂塗料
又は染料を用いて着色を行うが、顔料を用いた場合、耐
光性、色の再現性がより優れた着色物品が得られ、また
基材がプラスチックである場合、プラスチック材料の種
類によらず着色可能であることから顔料を用いることが
より好ましい。本発明における塗料の塗布は、スプレー
塗装法を用いるが、従来のスプレー塗装法のように高圧
（約2．5よりも大きな圧力、約４．０kg/cm２以下）で
塗料を霧化し基材に噴霧するのではなく、低圧（約0．5
〜2．5 kg/cm２)で噴霧する。これ以下であると、塗料
を霧化できなくなるため良好な着色面を得ることができ
なくなる。In the present invention, coloring is carried out using a resin coating or dye containing a pigment as described above. When a pigment is used, a colored article having more excellent light resistance and color reproducibility can be obtained. When is a plastic, it is more preferable to use a pigment because it can be colored regardless of the type of the plastic material. In the present invention, the paint is applied by a spray coating method. However, as in the conventional spray coating method, the paint is atomized at a high pressure (a pressure higher than about 2.5, about 4.0 kg / cm2 or less) and applied to the substrate. Instead of spraying, use low pressure (approximately 0.5
Spray at ~ 2.5 kg / cm2). If it is less than this, it becomes impossible to atomize the paint, so that a good colored surface cannot be obtained.

【００１１】図２は本発明に用いるスプレーガンの先端
部に装着するキャップの概略を示す断面図である。顔料
分散樹脂塗料の塗料噴出口５は円筒形状を成しており、
その内壁に沿って塗料が噴出する。塗料噴出口５の周囲
には圧縮空気噴出口４が設けられている。更に圧縮空気
噴出口４に位置する塗料噴出口５の外壁にはスパイラル
状に突起７が形成されている。圧縮空気は、突起７によ
り形成された空隙に沿って流れてくる。この空気は、圧
縮空気噴出口４の中心軸を軸とした回転を伴ったもので
ある。そのため圧縮空気噴出口４の出口においても噴出
する空気は回転を伴ったものとなる。この回転により、
噴出する空気の速度は高速度となる。そのため空気の噴
出圧力を低圧に抑えても塗料の霧化が可能な圧力の空気
の噴出を行うことが可能となる。つまり従来のスプレー
ガンを用いたときに使用する場合と同じ空気量で、より
高速の空気の噴出が可能となる。なおキャップの材質は
金属製、プラスチック製などが使用可能であり特に限定
されるものではない。またスパイラル状の突起７の形
状、寸法を調製することにより、噴出させる空気の噴出
速度を調整することも可能である 塗料噴出口５から噴出された塗料は、この回転を伴った
空気と混ざり合い、塗料も回転を伴い直進する。この状
態において塗料は霧化される。FIG. 2 is a sectional view schematically showing a cap to be attached to the tip of the spray gun used in the present invention. The paint ejection port 5 of the pigment-dispersed resin paint has a cylindrical shape,
The paint squirts along the inner wall. A compressed air outlet 4 is provided around the paint outlet 5. Further, a projection 7 is formed in a spiral shape on the outer wall of the paint outlet 5 located at the compressed air outlet 4. The compressed air flows along the gap formed by the projection 7. This air is accompanied by rotation about the central axis of the compressed air jet port 4. Therefore, the air ejected at the outlet of the compressed air ejection port 4 is accompanied by rotation. With this rotation,
The velocity of the jetting air becomes high. Therefore, it is possible to eject air at a pressure that allows the paint to be atomized even when the ejection pressure of the air is kept low. That is, it is possible to jet air at a higher speed with the same amount of air as when using a conventional spray gun. The cap can be made of metal, plastic, or the like, and is not particularly limited. By adjusting the shape and dimensions of the spiral projections 7, it is also possible to adjust the jetting speed of the air to be jetted. , And paint goes straight with rotation. In this state, the paint is atomized.

【００１２】非着色領域形成用のスプレーガンは従来か
ら用いてられているものでよい。またスプレーガンは、
着色領域形成用と非着色領域形成用のものを別個に用意
し、それぞれの領域を別個に形成することが好ましい
が、塗料の噴出口が複数設けられた双頭ガンを用いるこ
とも可能である。双頭ガンを用いる場合、一方の噴出口
から着色領域形成のための染料や顔料を含む有機樹脂塗
料を噴出させ、他方の噴出口から透明有機樹脂塗料を噴
出してもよい。The spray gun for forming the non-colored area may be a conventionally used spray gun. The spray gun is
It is preferable to separately prepare one for forming a colored region and one for forming a non-colored region and form each region separately, but it is also possible to use a double-headed gun provided with a plurality of paint ejection ports. When a double-headed gun is used, an organic resin paint containing a dye or pigment for forming a colored area may be ejected from one jet port, and a transparent organic resin paint may be jetted from the other jet port.

【００１３】着色領域の膜厚は５ミクロン以下であることが
好ましいが、着色する色の種類によって調整するのが好
ましく、これに限定されるものではない。本発明におい
て用いられる基材は、例えばポリカーボネート系、ウレ
タン系、スチレン系、ＣＲ−３９の重合体、ポリエステル
系、不飽和ポリエステル系、塩化ビニル系、エポキシ系
樹脂などのプラスチックやガラス、金属を用いることが
可能である。。The thickness of the colored region is preferably 5 μm or less, but is preferably adjusted according to the type of color to be colored, and is not limited to this. The base material used in the present invention is, for example, a plastic, glass, or metal such as a polycarbonate-based, urethane-based, styrene-based, CR-39 polymer, polyester-based, unsaturated polyester-based, vinyl chloride-based, or epoxy-based resin. It is possible. .

【００１４】塗膜表面には基材の耐衝撃性を向上させる
プライマー層を形成することも可能である。プライマー
層に用いる材料としてはアクリルポリオールやポリエステル
ポリオール、イソシアネートを原料としたウレタン系樹脂やポリ
ビニルアセタール系樹脂を原料としたものが用いられ
る。具体的にはアルキレングリコール類、ポリアルキレ
ングリコール類、ポリ（アルキレンアジぺート）類、ポ
リ−ε−カプロラクトン、ポリブタジエングリコール類
ポリ（アルキレンカーボネート）類又はシリコーンポリオー
ルから選ばれる活性水素含有化合物とポリイソシアネートとか
ら得られるものが好ましい。A primer layer for improving the impact resistance of the substrate can be formed on the surface of the coating film. As a material used for the primer layer, a material obtained from a urethane-based resin or a polyvinyl acetal-based resin from acrylic polyol, polyester polyol, or isocyanate is used. Specifically, an active hydrogen-containing compound selected from an alkylene glycol, a polyalkylene glycol, a poly (alkylene adipate), a poly-ε-caprolactone, a polybutadiene glycol, a poly (alkylene carbonate) or a silicone polyol, and a polyisocyanate Are preferred.

【００１５】プライマー層上には、耐擦傷性を向上させ
るためにハードコート層を形成してもよい。特に本発明
の着色物品は、基材表面に着色塗膜が形成されているこ
とからハードコート層を形成し耐擦傷性を向上させるこ
とは有効である。ハードコート層を形成する材料として
は、下記の一般式で表される有機ケイ素化合物が用いら
れる。A hard coat layer may be formed on the primer layer in order to improve the scratch resistance. In particular, since the colored article of the present invention has a colored coating film formed on the surface of the substrate, it is effective to form a hard coat layer to improve the scratch resistance. As a material for forming the hard coat layer, an organosilicon compound represented by the following general formula is used.

【００１６】Ｒ１ａR２ｂSｉ（ＯＲ３)４−（ａ＋ｂ） （Ｒ１、 Ｒ２は、Ｃ１〜Ｃ１０のアルキル、アリー
ル、ハロゲン化アルキル、ハロゲン化アリール、アルケ
ニルまたはエポキシ基、（メタ）アクリルオキシ基、メ
ルカプト基、アミノ基、もしくはシアノ基を有する有機
基でＳｉ−Ｃ結合によりケイ素と結合されているもので
あり、Ｒ３は、Ｃ１〜Ｃ６のアルキル基、アルコキシア
ルキル基またはアシル基であり、ａ及びｂは、０、１ま
たは２であり、ａ＋ｂが１または２である。）で示され
る化合物およびその加水分解物からなる群から選ばれた
化合物からなるケイ素系高分子化合物を主成分として含
むものである。この中でもエポキシシランは有効なもの
である。R1aR2bSi (OR3) 4- (a + b) (R1, R2 are C1 to C10 alkyl, aryl, halogenated alkyl, halogenated aryl, alkenyl or epoxy group, (meth) acryloxy group, mercapto group, amino group R3 is a C1-C6 alkyl group, alkoxyalkyl group or acyl group, and a and b are 0 or , 1 or 2, and a + b is 1 or 2.) and a silicon-based polymer compound composed of a compound selected from the group consisting of hydrolysates thereof. Among them, epoxysilane is effective.

【００１７】プライマー層とハードコート層には例えば
酸化チタン、酸化スズ、酸化ケイ素、酸化タングステ
ン、酸化亜鉛、酸化鉄、酸化アルミニウム、酸化インジ
ウム、酸化タンタルなどの酸化物無機微粒子を単体また
は混合状態、複合状態で添加し、屈折率、硬度の調整や
帯電防止等の効果の付与を行うことも可能である。ま
た、ハードコート層は、ＣＶＤ法や真空蒸着法により形
成することも可能である。この場合使用する材料は、Ｔ
ｉ系、Ｓｉ系のアルコキシ基含有有機化合物が好まし
い。For the primer layer and the hard coat layer, for example, oxide inorganic fine particles such as titanium oxide, tin oxide, silicon oxide, tungsten oxide, zinc oxide, iron oxide, aluminum oxide, indium oxide and tantalum oxide are used alone or in a mixed state. It can be added in a composite state to adjust the refractive index and hardness and to impart effects such as antistatic. Further, the hard coat layer can be formed by a CVD method or a vacuum evaporation method. The material used in this case is T
Preferred are i-type and Si-type organic compounds containing an alkoxy group.

【００１８】更にハードコート層表面に酸化ケイ素、酸
化アルミニウム、酸化亜鉛、酸化チタン等の酸化物によ
り反射防止層を形成してもよい。更に反射防止層上に水
やけ防止層を形成することも可能である。水やけ防止層
の材料としては、有機ポリシロキサン系重合物またはパーフ
ルオロ基含有有機化合物を重合してなる重合物からなる
有機物含有硬化物層を有するものが好ましく使用され
る。Further, an antireflection layer may be formed on the surface of the hard coat layer using an oxide such as silicon oxide, aluminum oxide, zinc oxide, or titanium oxide. Furthermore, it is also possible to form a drainage preventing layer on the antireflection layer. As the material for the drainage preventing layer, those having an organic-containing cured material layer made of an organic polysiloxane polymer or a polymer obtained by polymerizing a perfluoro group-containing organic compound are preferably used.

【００１９】そして本発明のプラスチック物品は、装飾
品、フィルター、眼鏡等の用途に用いることができる。The plastic article of the present invention can be used for decorative articles, filters, glasses and the like.

【００２０】[0020]

【実施例１】本実施例では、基材としてポリカーボネー
トからなるプラスチックレンズ基材を用いた。 （１）顔料分散樹脂塗料の調製 着色領域を形成するためにフタロシアニン系の顔料を用い、こ
れを１５ｇとり一液性ウレタン樹脂５０ｇに分散させ
た。Example 1 In this example, a plastic lens substrate made of polycarbonate was used as a substrate. (1) Preparation of Pigment-Dispersed Resin Paint A phthalocyanine-based pigment was used to form a colored region, and 15 g of the pigment was dispersed in 50 g of a one-part urethane resin.

【００２１】（２）稀釈 顔料分散樹脂塗料をシンナーで稀釈した。本実施例にお
いて稀釈は、重量比で顔料分散樹脂塗料：シンナー＝１
０：１０で調製した。 （３）クリヤー塗料の調製 非着色領域形成のためのクリヤー塗料は、重量比でクリ
ヤー塗料：シンナー＝１０：１２で稀釈し調製した。(2) Dilution The pigment-dispersed resin coating was diluted with a thinner. In the present embodiment, the dilution is a pigment-dispersed resin paint: thinner = 1 by weight ratio.
Prepared at 0:10. (3) Preparation of clear paint The clear paint for forming the non-colored area was prepared by diluting the clear paint: thinner = 10: 12 by weight ratio.

【００２２】（４）着色領域の形成 本実施例においては、上記条件で顔料分散樹脂塗料をシ
ンナーで稀釈した塗料を用いて着色領域を形成する。ま
た着色領域は、非着色領域を形成する前に形成した。本
実施例の着色領域は、濃度勾配を有するものである。図
１は、本実施例により形成されるハーフコートされたプラスチ
ックレンズ３の概略を示す平面図である。図中２ａは、
最も濃度の濃い領域であり、２ｂは、次に濃度の濃い部
分である。また１の領域は非着色領域である。(4) Formation of Colored Region In this embodiment, a colored region is formed by using a paint obtained by diluting a pigment-dispersed resin paint with a thinner under the above conditions. The colored region was formed before forming the non-colored region. The colored region of this embodiment has a density gradient. FIG. 1 is a plan view schematically showing a half-coated plastic lens 3 formed according to the present embodiment. 2a in the figure is
This is the region with the highest density, and 2b is the portion with the next highest density. The area 1 is a non-colored area.

【００２３】濃度勾配を形成するために本実施例では、
最も濃度の濃い部分２ａから着色を開始し、徐々に薄い
部分２ｂを形成するようにし濃度勾配を施した。まず濃
度の濃い部分２ａを形成するにあたり、塗装幅を約10ｍ
ｍに設定した。塗装幅とは、基材表面に対して塗料が噴
霧される幅を称する。塗装は、前記塗装幅の領域を３回
往復するように噴霧して行った。次に２ａよりのやや色
の薄い部分２ｂを形成する。２ｂを形成する場合には２
ａの部分との間に隙間が生じないように噴霧領域が少し
重なるように塗布領域を制御した。塗装幅は約10ｍｍに
設定した。更に塗布は、同一領域を２回往復するように
噴霧することにより行った。つまり、濃度勾配は、同一
領域への噴霧回数を制御することで行った。In this embodiment, in order to form a concentration gradient,
Coloring was started from the darkest part 2a, and a density gradient was applied so as to gradually form the lighter part 2b. First, when forming the dense part 2a, the coating width should be about 10m.
m. The coating width refers to the width at which the paint is sprayed on the substrate surface. The coating was performed by spraying the coating width in the range of three times. Next, a slightly lighter portion 2b than 2a is formed. When forming 2b, 2
The application area was controlled so that the spray areas slightly overlapped with each other so that no gap was formed between the areas. The coating width was set to about 10 mm. Further, the coating was performed by spraying the same area twice back and forth. That is, the concentration gradient was performed by controlling the number of sprays to the same area.

【００２４】次にクリヤー塗料を用いこれを着色領域以
外の領域に噴霧して非着色領域１を形成した。このよう
に着色領域と非着色領域が形成されたレンズは、塗装面
の安定性のために、空気中において約10分間放置した。
その後、80度に設定された乾燥炉中で約60分間乾燥させ
た。Next, a non-colored area 1 was formed by spraying a clear paint onto areas other than the colored areas. The lens in which the colored region and the non-colored region were formed was left in the air for about 10 minutes for the stability of the painted surface.
Then, it was dried in a drying oven set at 80 degrees for about 60 minutes.

【００２５】このような方法で製造されたプラスチック
レンズのプラスチック表面を観察したところ、色、色む
ら、へこみ、はじき、つぶ、レモンピオールなどの評価
項目において、従来のものよりも優れたプラスチックレ
ンズが得られた。Observation of the plastic surface of the plastic lens manufactured by such a method revealed that a plastic lens superior to the conventional one was obtained in the evaluation items such as color, uneven color, dent, repellency, crush, and lemon piol. Was done.

【００２６】[0026]

【実施例２】プラスチック基材材料、塗装方法、塗装条
件、顔料の種類は実施例１と同じ条件に設定し、顔料を
分散させる透明樹脂をエポキシ樹脂にしプラスチック基
材表面に噴霧した。レンズ表面を観察したところ、色、
色むら、へこみ、はじき、ぶつ、レモンピオールなどの
評価項目において、従来のものよりも優れたプラスチッ
クレンズが得られた。評価結果を表1に示す。Example 2 The plastic substrate material, coating method, coating conditions, and pigment type were set to the same conditions as in Example 1, and the transparent resin for dispersing the pigment was changed to an epoxy resin and sprayed onto the surface of the plastic substrate. Observing the lens surface, the color,
In the evaluation items such as color unevenness, dent, repelling, bump, lemon piol, etc., a plastic lens superior to the conventional one was obtained. Table 1 shows the evaluation results.

【００２７】[0027]

【表1】 【table 1】

【００２８】なお本実施例においては着色領域を形成し
た後に非着色領域を形成したが、非非着色領域を先に形
成してもよい。Although the non-colored area is formed after the colored area is formed in this embodiment, the non-colored area may be formed first.

【００２９】[0029]

【発明の効果】本発明の着色物品は、着色領域と非着色
領域との境界部分の面不良を有さないので、着色物品表
面全体の平滑性に優れ、色むらのない表面を有するハーフコ
ートされた着色物品となり、外観の優れたプラスチック物
品が得られる。特に光学物品においては、干渉縞の生じ
ない光学特性に優れたものとなる。Since the colored article of the present invention has no surface defects at the boundary between the colored area and the non-colored area, the half-coat having excellent smoothness on the entire surface of the colored article and having no uneven color is provided. Thus, a plastic article having an excellent appearance can be obtained. In particular, optical articles have excellent optical characteristics free of interference fringes.

【００３０】更に着色領域を形成する場合、塗料の霧化
を低圧により行い、これにより塗布を行うため、平滑性
に優れたハーフコートされた着色物品を効率よく製造すること
ができる。また、製品ごとの着色状態にばらつきが少な
くなり再現性も向上する。Further, in the case of forming a colored region, since the paint is atomized at a low pressure and the application is performed by this, a half-coated colored article having excellent smoothness can be efficiently produced. Further, the variation in the coloring state of each product is reduced, and the reproducibility is improved.

【図面の簡単な説明】[Brief description of the drawings]

【図１】は、本発明に関わる着色物品の概略を示す平面
図である。FIG. 1 is a plan view schematically showing a colored article according to the present invention.

【図２】は、本発明に関わる着色物品を製造する場合に
用いるスプレーガンの先端に装着するキャップの一実施
例の概略を示す断面図である。FIG. 2 is a cross-sectional view schematically showing one embodiment of a cap to be attached to the tip of a spray gun used for producing a colored article according to the present invention.

【符号の説明】[Explanation of symbols]

１・・・非着色領域 ２ａ・・最も濃度の濃い着色領域 ２ｂ・・２ａよりも濃度の薄い着色領域 ３・・・プラスチックレンズ ４・・・圧縮空気噴出口 ５・・・塗料噴出口 ６・・・キャップ ７・・・スパイラル状の突起 以上 DESCRIPTION OF SYMBOLS 1 ... Non-colored area 2a ... The darkest colored area 2b ... The colored area lighter than 2a 3 ... Plastic lens 4 ... Compressed air jet 5 ... Paint jet 6 ... ..Cap 7: Spiral projection

Claims (4)

【明細書】 【特許請求の範囲】[Specifications] [Claims] 【請求項１】 顔料を有する有機樹脂塗料又は染料を気
体と共に噴出させることにより前記顔料を有する有機樹
脂塗料又は染料を霧化させ、これを基材表面に噴霧し塗
布することで着色領域を形成する工程と、該着色領域以
外の領域に透明有機樹脂塗料を噴霧し塗布する工程を有
することを特徴とする着色物品の製造方法。An organic resin paint or dye having a pigment is jetted out together with a gas to atomize the organic resin paint or dye having a pigment, and a colored region is formed by spraying and applying the spray to the surface of a substrate. And a step of spraying and applying a transparent organic resin paint to an area other than the colored area. 【請求項２】 前記着色領域を形成する場合における気
体の噴出圧力が約２．５kg/cm２よりも低い圧力である
ことを特徴とする請求項１記載の製造方法。2. The manufacturing method according to claim 1, wherein the gas ejection pressure for forming the colored region is lower than about 2.5 kg / cm 2. 【請求項３】 基材表面に顔料を有する有機樹脂塗料又
は染料が噴霧された着色領域と該着色領域以外の領域に
透明有機樹脂塗料が噴霧された非着色領域を有する着色
物品。3. A colored article having a colored region sprayed with an organic resin paint or dye having a pigment on the surface of a base material and a non-colored region sprayed with a transparent organic resin paint in a region other than the colored region. 【請求項４】 前記着色領域において、濃度が相対的に
濃い部分の膜厚が相対的に薄い部分の膜厚に比べて厚い
ことを特徴とする請求項３記載の着色物品。4. The colored article according to claim 3, wherein, in the colored region, the thickness of a portion having a relatively high density is thicker than the thickness of a portion having a relatively low density.