Abstract

PROBLEM TO BE SOLVED: To discover illicit unsealing at the time of such action, to keep the data thereof recorded and to easily manufacture an unsealing preventive tape by forming conductive patterns which are easily disconnected in pulling and peeling in this unsealing preventive tape. SOLUTION: The unsealing preventive tape 1 has a laminated structure consisting of a primer layer 3 disposed on a stretchable base material sheet 2, the conductive patterns 4 disposed thereon, metallic pieces 5 for terminals connected to both ends thereof and an adhesive layer 6. The breaking elongation of the stretchable base material sheet 2 is specified to >=10%, more preferably >=30%. The spacings between the conductive particles of a conductive coating material constituting the conductive patterns 4 are sufficiently widened and the contact of the conductive particles with each other does not arise any more by increasing the elongating rate of the stretchable base materials sheet 2 and, therefore, the conductive patterns 4 are easily disconnected. The stretchable base material sheet 2 are peeled together with the conductive patterns 4 when the unsealing preventive tape 1 is pulled and peeled by the primer layer 3 and, therefore, the sure disconnection occurs.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、物品の不正開封を
防止する開封防止テープに関する。更に詳しくは、開封
を防止しようとする物品を被着体とし、これに貼着する
テープであって、このテープを被着体に貼着後、引き剥
がすと、テープ内に形成されていた回路が断線し、不正
開封が電気的に発見又は記録されるようにする開封防止
テープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an opening prevention tape for preventing unauthorized opening of articles. More specifically, a tape to be adhered to an article to be prevented from being unsealed and to be adhered to the article, wherein the tape is adhered to the adherend and peeled off to form a circuit formed in the tape. The present invention relates to an anti-opening tape that allows disconnection and unauthorized opening to be electrically detected or recorded.

【０００２】[0002]

【従来の技術】従来より、容器や箱等の封緘にあたり、
不正開封を防止して安全管理を行い、品質保証をするた
め、開封防止テープ、あるいは封印用テープ、封緘シー
ル、開封防止ラベル等とも称されている粘着テープが使
用されている。2. Description of the Related Art Conventionally, in sealing containers and boxes,
In order to prevent unauthorized opening, perform safety management, and assure quality, adhesive tapes, which are also called opening prevention tapes, sealing tapes, sealing seals, opening prevention labels, and the like, are used.

【０００３】この開封防止テープとしては、次のような
種類のものが知られている。The following types of opening prevention tapes are known.

【０００４】第１に、図３に示したように、開封防止テ
ープ３０を剥離紙３１、粘着剤層３２、脆質フィルム３
３の積層シートから形成し、脆質フィルム３３上に任意
に印刷を施したものがある。この開封防止テープ３０を
被着体に貼着するときにはその剥離紙３１を剥がして粘
着剤層３２を被着体に貼着する。この開封防止テープ３
０は、一旦被着体に貼着させた後に引き剥がそうとする
と、粘着剤層３２は被着体に対する十分な接着力を有し
ているので被着体に貼着したままとなるが、脆質フィル
ム３３はそれ自体に伸長性が乏しく、引張強度も低く、
切れやすいので、速やかに引きちぎられる。したがっ
て、この開封防止テープ３０によると、脆質フィルム３
３の破断により開封の痕跡が残されることとなり、不正
開封後に未開封状態に見せかけることができなくなり、
不正開封が防止される。First, as shown in FIG. 3, an opening prevention tape 30 is separated from a release paper 31, an adhesive layer 32, and a brittle film 3.
3 is formed from the laminated sheet and is arbitrarily printed on the brittle film 33. When sticking the opening prevention tape 30 to the adherend, the release paper 31 is peeled off, and the adhesive layer 32 is adhered to the adherend. This opening prevention tape 3
0, if it is to be peeled off after being once adhered to the adherend, the pressure-sensitive adhesive layer 32 has sufficient adhesive force to the adherend, so that it remains adhered to the adherend, The brittle film 33 itself has poor extensibility, low tensile strength,
As it is easy to cut, it can be torn quickly. Therefore, according to the opening prevention tape 30, the brittle film 3
3 will leave traces of opening due to the breakage of 3, making it impossible to imitate the unopened state after unauthorized opening,
Tampering is prevented.

【０００５】第２に、図４に示したように、開封防止テ
ープ４０を、伸び率が大きく、残留歪みの大きい伸長性
フィルム基材４１と粘着剤層４２との積層シートとした
ものも知られている。この開封防止テープ４０による
と、不正開封により伸長性フィルム基材４１が大きな伸
び変形を起こすので開封の痕跡が残され、不正開封が防
止される（特公昭６３−３２３８８号公報）。Second, as shown in FIG. 4, an unsealing prevention tape 40 is also known as a laminated sheet of an extensible film base material 41 having a large elongation rate and a large residual strain and an adhesive layer 42. Have been. According to the unsealing prevention tape 40, since the extensible film base material 41 undergoes significant elongation deformation due to unauthorized opening, a trace of opening is left, and unauthorized opening is prevented (Japanese Patent Publication No. 63-32388).

【０００６】第３に、図５に示したように、開封防止テ
ープ５０をテープ状シート５１、内部接着剤層５２、模
様インキ層５３、被着体に対する直接的な貼着層となる
外部接着剤層５４の積層シートとし、内部接着剤層５２
と模様インキ層５３との間に部分的に撥インキ部分５５
を設けたものも知られている。この開封防止テープ５０
では、撥インキ部分５５の形成の有無により、模様イン
キ層５３の内部接着剤層５２あるいは外部接着剤層５４
に対する接着力に差が生じるので、開封防止テープ５０
をその外部接着剤層５４を貼着面として被着体に貼着し
た後、これを引き剥がそうとすると、撥インキ部分５５
の形成されている部分では模様インキ層５３が被着体側
に残存するが、撥インキ部分５５の形成されていない部
分ではテープ状シート５１側に剥がしとられやすく、模
様インキ層５３の模様が大きく崩れる。したがって、こ
れにより不正開封の痕跡が残り、不正開封が防止される
（特公平５−３３３９８号公報）。Third, as shown in FIG. 5, the tape 50 for opening prevention is externally bonded to a tape-like sheet 51, an internal adhesive layer 52, a pattern ink layer 53, and a direct adhesive layer to an adherend. The internal adhesive layer 52
Between the ink layer 53 and the pattern ink layer 53
Also known are those provided with. This opening prevention tape 50
Then, depending on whether or not the ink-repellent portion 55 is formed, the internal adhesive layer 52 or the external adhesive layer 54 of the pattern ink layer 53 is determined.
Since there is a difference in adhesive strength with respect to the opening prevention tape 50,
Is adhered to an adherend using the external adhesive layer 54 as an adhering surface, and when this is to be peeled off, the ink repellent portion 55
The pattern ink layer 53 remains on the adherend side in the portion where is formed, but is easily peeled off on the tape-like sheet 51 side in the portion where the ink-repellent portion 55 is not formed, and the pattern of the pattern ink layer 53 is large. Crumble. Accordingly, this leaves traces of unauthorized opening, and prevents unauthorized opening (Japanese Patent Publication No. 5-33398).

【０００７】第４に、図６（ａ）に示したように、封印
シール６０を、被封印物への貼着面をなす粘着材６１、
線状の導電部材６２、粘着材６１及び帯状のシール基体
６３の積層構造とし、かつ、導電部材６２を挟む一対の
粘着材６１の該導電部材６２に対する粘着力の相対的強
さを隣接する領域ごとに逆転させたものが知られてい
る。即ち、領域Ａにおいては被封印物側を粘着力が強い
粘着材６１ｓとし、シール基体６３側を粘着力が弱い粘
着材６１ｗとする。そしてこの領域Ａに隣接する領域Ｂ
では、被封印物側を粘着力が弱い粘着材６１ｗとし、シ
ール基体６３側を粘着力が強い粘着剤６１ｓとし、さら
に、領域Ｂに隣接する領域Ｃでは、被封印物側を粘着力
が強い粘着材６１ｓとし、シール基体６３側を粘着力が
弱い粘着材６１ｗとする。こうして対向する粘着材の粘
着力の強弱の相対的関係が、隣接する領域で互いに反対
になるようにする。[0007] Fourth, as shown in FIG. 6A, the sealing seal 60 is made of an adhesive material 61 which forms a surface to be adhered to an object to be sealed.
A region having a laminated structure of the linear conductive member 62, the adhesive 61, and the band-shaped seal base 63, and the adjacent strength of the pair of adhesives 61 sandwiching the conductive member 62, relative to the conductive member 62. What is reversed every time is known. That is, in the region A, the sealed object side is made of the adhesive material 61s having strong adhesive force, and the seal base 63 side is made of the adhesive material 61w having weak adhesive force. And a region B adjacent to this region A
Then, the sealed object side is made of an adhesive material 61w having a low adhesive strength, the seal base 63 side is made of an adhesive 61s having a strong adhesive force, and further, in a region C adjacent to the region B, the sealed object side has a strong adhesive force. The adhesive material 61s is used, and the seal substrate 63 side is used as an adhesive material 61w having a low adhesive strength. In this way, the relative strength of the adhesive forces of the opposing adhesive materials is made opposite to each other in adjacent regions.

【０００８】この封印シール６０は、封印シール６０を
被封印物に貼着した後、引き剥がすと、各領域におい
て、粘着力の弱い粘着材６１ｗが引き剥がされ、図６
（ｂ）に示したように、導電部材６２がシール基体側と
被封印物側とに交互に分離し、分断されることとなる。
したがって、封印シール６０の開封を電気的に検出する
ことが可能となる（特開平８−２２１６７６号公報）。When the seal 60 is peeled off after the seal 60 is adhered to an object to be sealed, the adhesive material 61w having a low adhesive strength is peeled off in each region, and FIG.
As shown in (b), the conductive member 62 is alternately separated and separated into the seal base side and the sealed object side.
Therefore, it is possible to electrically detect the opening of the sealing seal 60 (Japanese Patent Laid-Open No. Hei 8-221676).

【０００９】[0009]

【発明が解決しようとする課題】しかしながら、図３〜
図５に示した従来の開封防止テープでは、不正開封の事
実を不正開封後に発見することはできても、不正開封の
行為時に発見して対処することはできず、また不正開封
行為の日時を記録しておくこともできない。However, FIGS.
In the conventional anti-opening tape shown in FIG. 5, although the fact of unauthorized opening can be found after the unauthorized opening, it cannot be found and dealt with at the time of the unauthorized opening, and the date and time of the unauthorized opening is set. I can't keep a record.

【００１０】そのため、不正開封を実際上阻止すること
はできず、社会的問題がひきおこされている。[0010] For this reason, unauthorized opening cannot be practically prevented, and social problems are caused.

【００１１】例えば、パチンコや、一般にパチスロと呼
ばれている機器には、その出玉の確率を決めるＲＯＭや
それに付随するＩＣを収めたボックスが備えられてい
る。このＲＯＭがパチンコ店や顧客によって不正に交換
され、出玉の確率が勝手に調整されることは犯罪につな
がる。そこで、このボックスの開口部には、ＲＯＭの不
正交換を防止するために、不正開封を防止する封緘シー
ルが貼られている。しかしながらこの封緘シールは比較
的容易に剥がすことができるので、不正なＲＯＭの交換
を確実に防止することができなくなっているのが実情で
ある。For example, a pachinko machine or a device generally called a pachislot is provided with a box for storing a ROM for determining the probability of a ball coming out and an accompanying IC. If this ROM is illegally exchanged by pachinko parlors and customers and the probability of winning is adjusted without permission, it leads to a crime. Therefore, in order to prevent unauthorized replacement of the ROM, a seal for preventing unauthorized opening is attached to the opening of the box. However, since the sealing seal can be peeled off relatively easily, the fact is that it is no longer possible to reliably prevent unauthorized ROM replacement.

【００１２】これに対して図６に示した従来の封印シー
ルでは、不正開封を電気的に検知し、記録することが可
能となるが、導電部材６２を挟む一対の粘着材の該導電
部材６２に対する粘着力の大小を、隣接する領域ごとに
逆転させなくてはならないので、粘着材６１の構成が複
雑となり、粘着材６１の設計や形成作業に手間がかかる
という問題がある。また、開封防止テープの開封時に、
被封印物に粘着している粘着材６１とその被封印物との
接着界面で剥離が生じるように、あるいはその被封印物
に粘着している粘着材の層中で破断が生じるように開封
防止テープを剥がすと、導電部材６２は分断されず、開
封が検知されないという問題もある。On the other hand, in the conventional sealing seal shown in FIG. 6, unauthorized opening can be electrically detected and recorded, but the conductive member 62 made of a pair of adhesives sandwiching the conductive member 62 is used. Since the magnitude of the adhesive force to the adhesive must be reversed for each adjacent region, the configuration of the adhesive 61 becomes complicated, and there is a problem in that the design and forming work of the adhesive 61 is troublesome. Also, when opening the opening prevention tape,
Opening prevention so that peeling occurs at the adhesive interface between the pressure-sensitive adhesive material 61 adhered to the sealed object and the sealed object, or breakage occurs in the layer of the adhesive material adhered to the sealed object. When the tape is peeled off, there is also a problem that the conductive member 62 is not divided and the opening is not detected.

【００１３】本発明は以上のような従来技術の問題点を
解決しようとするものであり、不正開封をその不正開封
の行為時に確実に発見することができ、また不正開封行
為の日時を記録しておくことができ、かつ容易に作製す
ることのできる開封防止テープを提供することを目的と
している。An object of the present invention is to solve the above-mentioned problems of the prior art, and it is possible to reliably detect an unauthorized opening at the time of the unauthorized opening, and to record the date and time of the unauthorized opening. An object of the present invention is to provide an unsealing prevention tape which can be kept and can be easily manufactured.

【００１４】[0014]

【課題を解決するための手段】本発明者らは、開封防止
テープ内に、このテープを引き剥がすときに容易に断線
する導電パターンを形成しておくことにより上記の目的
を達成できることを見出し、本発明を完成させるに至っ
た。Means for Solving the Problems The present inventors have found that the above object can be achieved by forming a conductive pattern in an opening prevention tape which is easily disconnected when the tape is peeled off. The present invention has been completed.

【００１５】すなわち、本発明は、破断伸び率が１０％
以上の伸長性基材シート、導電性塗料から形成された導
電パターン及び接着剤層からなる積層構造を有すること
を特徴とする開封防止テープを提供する。特に、好まし
い態様として、伸長性基材シートの破断伸び率が３００
％以上である態様や、伸長性基材シートと導電パターン
との間にこれらの接着力を高めるプライマー層を有する
態様を提供する。That is, according to the present invention, the elongation at break is 10%.
An anti-opening tape having a laminated structure including the above-described extensible base sheet, a conductive pattern formed from a conductive paint, and an adhesive layer is provided. In particular, as a preferred embodiment, the elongation at break of the extensible base sheet is 300
% Or more and an embodiment having a primer layer between the extensible base sheet and the conductive pattern, which enhances the adhesive strength between them.

【００１６】本発明の開封防止テープによると、伸長性
基材シート上に導電パターンが形成されているので、こ
の開封防止テープを接着剤層側から被着体に貼着し、そ
の後引き剥がそうとすると、伸長性基材シートが伸び、
それにより導電パターンを構成している導電性塗料の導
電性粒子相互の接触が維持されなくなり、又は粒子相互
間の距離が大きくなって、導電パターンが確実に断線状
態となる。したがって、導電パターンを警報装置や監視
システムと接続しておくことにより、不正開封時に不正
開封行為に対処することができ、また、導電パターンを
記録装置と接続しておくことにより不正開封行為の行わ
れた日時を記録することも可能となる。According to the anti-opening tape of the present invention, since the conductive pattern is formed on the extensible base sheet, the anti-opening tape is adhered to the adherend from the adhesive layer side and then peeled off. Then, the extensible base sheet elongates,
As a result, contact between the conductive particles of the conductive paint constituting the conductive pattern is not maintained, or the distance between the particles is increased, and the conductive pattern is reliably disconnected. Therefore, by connecting the conductive pattern to an alarm device or a monitoring system, it is possible to cope with unauthorized opening at the time of unauthorized opening, and by connecting the conductive pattern to a recording device, the unauthorized opening operation can be performed. It is also possible to record the date and time when the message was sent.

【００１７】[0017]

【発明の実施の態様】以下、本発明を図面に基づいて詳
細に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with reference to the drawings.

【００１８】図１は、本発明の開封防止テープの一態様
の平面図（同図（ａ））及び断面図（同図（ｂ））であ
る。FIG. 1 is a plan view (FIG. 1 (a)) and a cross-sectional view (FIG. 1 (b)) of one embodiment of the unsealing prevention tape of the present invention.

【００１９】この開封防止テープ１は、伸長性基材シー
ト２、伸長性基材シート２上に設けられたプライマー層
３、その上に設けられた導電パターン４、導電パターン
４の両端に接続された端子用金属片５、被着体に接着す
る接着剤層６の積層構造を有している。The opening prevention tape 1 is connected to an extensible base sheet 2, a primer layer 3 provided on the extensible base sheet 2, a conductive pattern 4 provided thereon, and both ends of the conductive pattern 4. And a laminated structure of a terminal metal piece 5 and an adhesive layer 6 that adheres to an adherend.

【００２０】ここで、伸長性基材シート２は導電パター
ン４に対して伸び率の高いシートから構成する。伸長性
基材シート２の伸び率が低いと、被着体に貼着された開
封防止テープ１が引き剥がされるときに、導電パターン
４を構成している導電性塗料の導電性粒子相互の間隔が
十分に広がらないので、導電パターン４は断線しにくく
なるが、伸長性基材シート２の伸び率を大きくすること
により、導電パターン４を構成している導電性塗料の導
電性粒子相互の間隔が十分に広がり、導電性粒子が相互
に接触しなくなるので、導電パターン４は容易に断線す
るものとなる。Here, the extensible base sheet 2 is composed of a sheet having a high elongation ratio with respect to the conductive pattern 4. When the elongation percentage of the extensible base sheet 2 is low, when the opening prevention tape 1 attached to the adherend is peeled off, the distance between the conductive particles of the conductive paint constituting the conductive pattern 4 is reduced. Does not spread sufficiently, so that the conductive pattern 4 is hardly broken. However, by increasing the elongation rate of the extensible base sheet 2, the distance between the conductive particles of the conductive paint constituting the conductive pattern 4 is reduced. Are sufficiently spread, and the conductive particles do not contact each other, so that the conductive pattern 4 is easily broken.

【００２１】伸長性基材シート２の伸び率の具体的数値
としては、破断伸び率（ＡＳＴＭ・Ｄ８８２−６１Ｔ）
１０％以上とし、好ましくは３００％以上とする。な
お、伸長性基材シート２としては、フィラー等の粒子が
添加されているものも使用することができるが、この場
合には、フィラー等の粒子を含むシートの伸び率が、上
述の範囲となるようにすることが好ましい。As specific numerical values of the elongation percentage of the extensible base material sheet 2, the elongation at break (ASTM D882-61T)
10% or more, preferably 300% or more. In addition, as the extensible base sheet 2, a sheet to which particles such as fillers are added can be used. In this case, the elongation percentage of the sheet containing the particles such as fillers falls within the above range. Preferably.

【００２２】本発明において好ましく使用することので
きる伸長性基材シートの例としては、例えば、セルロー
ストリアセテート（破断伸び率約４０％）、エチレンビ
ニルアセテートコポリマー（ＥＶＡ）（破断伸び率約６
５０〜９００％）、二軸延伸ポリプロピレン（破断伸び
率約１００％）、高密度ポリエチレン（破断伸び率約１
０〜７０％）等をあげることができる。Examples of the extensible base sheet that can be preferably used in the present invention include, for example, cellulose triacetate (elongation at break: about 40%), ethylene vinyl acetate copolymer (EVA) (elongation at break: about 6%).
50-900%), biaxially oriented polypropylene (elongation at break about 100%), high density polyethylene (elongation at break about 1%)
0-70%).

【００２３】伸長性基材シート２の厚さは、被着体に貼
着させやすく、かつ開封防止テープ１の引き剥がし時に
該伸長性基材シート２を引っ張ったときに導電パターン
４が容易に断線するように、５〜３０μｍ程度とするこ
とが好ましい。The thickness of the extensible base sheet 2 is such that the conductive pattern 4 can be easily adhered to an adherend, and the conductive pattern 4 can be easily formed when the extensible base sheet 2 is pulled when the opening prevention tape 1 is peeled off. It is preferable that the thickness be about 5 to 30 μm so as to cause disconnection.

【００２４】なお、伸長性基材シート２上には、図示し
たように、貼着時の作業性の点から、必要に応じてアプ
リケーションテープ８を設けることができる。このよう
なアプリケーションテープ８としては、例えば、紙、プ
ラスチックシート等を使用することができる。As shown, an application tape 8 can be provided on the extensible base sheet 2 as required, from the viewpoint of workability at the time of sticking. As such an application tape 8, for example, paper, a plastic sheet, or the like can be used.

【００２５】プライマー層３は、本発明において、伸長
性基材シート２と導電パターン４との密着が十分でない
場合に、それらの密着性を向上させるため、必要に応じ
て設けられる層である。プライマー層３の形成により、
被着体に貼着された開封防止テープ１が引き剥がされる
ときに、伸長性基材シート２が導電パターン４から剥離
して単独で剥がれることを防止でき、導電パターン４と
共に剥がれるようになるので、導電パターン４が確実に
断線する。In the present invention, the primer layer 3 is a layer provided as needed to improve the adhesion between the extensible base sheet 2 and the conductive pattern 4 when the adhesion is not sufficient. By forming the primer layer 3,
When the anti-opening tape 1 attached to the adherend is peeled off, the extensible base sheet 2 can be prevented from being separated from the conductive pattern 4 and peeled off alone, and can be peeled off together with the conductive pattern 4. Then, the conductive pattern 4 is surely disconnected.

【００２６】プライマー層３の構成材料としては、伸長
性基材シート２、導電パターン４、接着剤層６の構成材
料等に応じて適宜選択することができるが、例えば、ポ
リエステル系、ゴム系、アクリル系、ウレタン系等の透
明又は着色塗料を使用することができる。The constituent material of the primer layer 3 can be appropriately selected according to the constituent materials of the extensible base sheet 2, the conductive pattern 4, the adhesive layer 6, and the like. A transparent or colored paint such as an acrylic or urethane paint can be used.

【００２７】また、プライマー層３は、コーターを用い
てあるいは印刷により伸長性基材シート２上に任意の柄
に形成することができる。この場合、プライマー層３の
柄としてはベタにしてもよいが、伸長性基材シート２と
導電パターン４との接着力に強弱の分布をもたせ、被着
体に貼着された開封防止テープ１が引き剥がされるとき
に導電パターン４が断線しやすい箇所を形成するため、
ベタ以外の柄に形成することが好ましく、通常、開封防
止テープの長手方向に非連続パターンとなるように形成
することが好ましい。The primer layer 3 can be formed in an arbitrary pattern on the extensible base sheet 2 using a coater or by printing. In this case, the pattern of the primer layer 3 may be solid, but the adhesive force between the extensible base sheet 2 and the conductive pattern 4 has a strong and weak distribution, and the unsealing prevention tape 1 adhered to the adherend. To form a portion where the conductive pattern 4 is easily broken when
It is preferably formed in a pattern other than solid, and it is usually preferable to form the pattern in a non-continuous pattern in the longitudinal direction of the unsealing prevention tape.

【００２８】プライマー層３を形成する最適な柄は、当
該プライマー層３と導電パターン４との密着力、伸長性
基材シート２と導電パターン４との密着力等に応じて異
なるが、例えば図示したように縞柄とする場合には、一
般に幅１ｍｍ以上、間隔１ｍｍ以上の縞柄とすることが
好ましい。この他プライマー層３を形成する柄として
は、ゼブラ状、Ｗ、Ｘ、∞、≧等の学術記号や、※、＊
等の一般記号、！、：等の記述記号、制御記号、カッコ
記号等を使用することができる。また、プライマー層３
の柄としては、開封防止テープ１の不正開封者に対し、
開封防止テープ１を引っ張ったときの導電パターン４の
断線箇所が予測されないようにするため、複雑な柄とす
ることが好ましい。The optimum pattern for forming the primer layer 3 differs according to the adhesion between the primer layer 3 and the conductive pattern 4 and the adhesion between the extensible base sheet 2 and the conductive pattern 4. In the case of a striped pattern as described above, it is generally preferable to use a striped pattern having a width of 1 mm or more and an interval of 1 mm or more. In addition, as a pattern for forming the primer layer 3, a scientific symbol such as zebra, W, X, ≧, ≧, *, *
General symbols such as! ,:, Etc., control symbols, parentheses, etc. can be used. In addition, the primer layer 3
As for the handle, against the unauthorized opening of the opening prevention tape 1,
It is preferable that the conductive pattern 4 has a complicated pattern in order to prevent the breakage of the conductive pattern 4 when the opening prevention tape 1 is pulled.

【００２９】プライマー層３の伸長性基材シート２に対
する面積率は、プライマー層３と導電パターン４との重
なり合いの点から５〜９０％とすることが好ましい。５
％未満であると、プライマー層３の図柄によってはプラ
イマー層３と導電パターン４とが重なり合わないおそれ
がある。反対に９０％を超えると、導電パターン４と伸
長性基材シート２との直接的な接着領域が少なくなり過
ぎ、プライマー層３の形成により導電パターン４と伸長
性基材シート２との接着力に強弱の分布をもたせること
が困難になる。The area ratio of the primer layer 3 to the extensible base sheet 2 is preferably 5 to 90% from the viewpoint of the overlap between the primer layer 3 and the conductive pattern 4. 5
%, The primer layer 3 and the conductive pattern 4 may not overlap depending on the design of the primer layer 3. On the other hand, if it exceeds 90%, the direct bonding area between the conductive pattern 4 and the extensible base sheet 2 is too small, and the adhesion between the conductive pattern 4 and the extensible base sheet 2 due to the formation of the primer layer 3. It is difficult to have a strong and weak distribution.

【００３０】一方、本発明において、導電パターン４は
導電粒子とバインダーからなる導電性塗料から形成した
ものとする。これにより、開封防止テープ１が引き剥が
されるときに伸長性基材シート２が引き伸ばされると、
導電パターンを構成している導電粒子相互に非接触の部
分が生じ、導電パターン４を断線状態にすることができ
る。このような導電性塗料としては、導電粒子から形成
されている限り特に制限はなく、例えば、銀ペースト、
カーボンペースト等を使用することができる。On the other hand, in the present invention, the conductive pattern 4 is formed from a conductive paint composed of conductive particles and a binder. Thereby, when the extensible base sheet 2 is stretched when the opening prevention tape 1 is peeled off,
Non-contact portions are generated between the conductive particles constituting the conductive pattern, and the conductive pattern 4 can be disconnected. Such a conductive paint is not particularly limited as long as it is formed from conductive particles. For example, a silver paste,
Carbon paste or the like can be used.

【００３１】また、導電パターン４のパターン形状は、
開封防止テープ１が引き剥がされるときに確実に断線す
るように、開封防止テープ１が引き剥がされるときに伸
長性基材シート２が引き伸ばされる方向に細長く伸びた
パターンとすることが好ましく、例えば、開封防止テー
プ１の長手方向に伸びた帯状パターンをもつようにす
る。The pattern shape of the conductive pattern 4 is as follows:
In order to surely break the wire when the opening prevention tape 1 is peeled off, it is preferable to form a pattern that is elongated in the direction in which the extensible base sheet 2 is stretched when the opening prevention tape 1 is peeled off. The opening prevention tape 1 has a belt-like pattern extending in the longitudinal direction.

【００３２】導電パターン４を所期のパターンに形成す
る方法には特に制限はなく、コーターを用いた導電性塗
料の塗布、印刷等により行うことができる。The method for forming the conductive pattern 4 into the desired pattern is not particularly limited, and it can be performed by applying a conductive paint using a coater, printing, or the like.

【００３３】導電パターン４には、その断線により作動
する任意の警報装置、監視システム、開封日時の記録装
置等を接続することができるが、これら機器との接続の
便宜上、導電パターン４の端部には必要に応じて、図示
したように端子用金属片５を接続することができる。The conductive pattern 4 can be connected to any alarm device, a monitoring system, a recording device for opening date and time, etc. which are activated by the disconnection. For convenience of connection with these devices, the end of the conductive pattern 4 can be connected. The terminal metal piece 5 can be connected as shown in FIG.

【００３４】開封防止テープ１を被着体に貼着させると
きの密着面となる接着剤層６は、開封防止テープ１を使
用する被着体と密着する限り、任意の接着剤から構成す
ることができる。例えば、被着体がスチロール樹脂、ポ
リカーボネート等のプラスチック製ボックス、鉄、銅等
の金属製ボックス等からなる場合、接着剤層６はアクリ
ル系や合成ゴム系接着剤から形成することができる。The adhesive layer 6 serving as a contact surface when the opening prevention tape 1 is adhered to an adherend is made of an arbitrary adhesive as long as the adhesive layer 6 adheres to the adherend using the opening prevention tape 1. Can be. For example, when the adherend is made of a plastic box such as styrene resin or polycarbonate, or a metal box such as iron or copper, the adhesive layer 6 can be formed of an acrylic or synthetic rubber adhesive.

【００３５】また、開封防止テープ１の保管、搬送、使
用上の便宜の点から、必要に応じて、接着剤層６上に
は、開封防止テープ１を被着体に貼着させるときに容易
に剥がしとることのできる剥離層あるいは保護層７を設
けておいてもよい。このような剥離層あるいは保護層７
としては、例えば、シリコーンコート紙、ポリエチレン
シート等をあげることができる。Further, in view of the convenience of storage, transportation and use of the opening prevention tape 1, if necessary, the opening prevention tape 1 can be easily attached to the adherend on the adhesive layer 6. A peelable layer or a protective layer 7 that can be peeled off may be provided. Such release layer or protective layer 7
Examples thereof include silicone-coated paper and polyethylene sheet.

【００３６】以上の図１の開封防止テープは、安全管
理、品質保証を図る種々の容器や箱等の封緘に使用する
ことができるが、例えば、パチンコやパチスロの出玉の
確率を決めるＲＯＭを収容したプラスチックケースの封
緘に好ましく使用することができる。The above-described opening prevention tape shown in FIG. 1 can be used for sealing various containers and boxes for safety management and quality assurance. For example, a ROM for determining the probability of a pachinko or pachislot ball coming out can be used. It can be preferably used for sealing a plastic case housed therein.

【００３７】[0037]

【実施例】以下、本発明を実施例に基づいて具体的に説
明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be specifically described below based on embodiments.

【００３８】実施例１ 実施例の開封防止テープを次のようにして製造した。こ
の場合の製造工程を図２に示す。Example 1 The opening prevention tape of the example was manufactured as follows. FIG. 2 shows a manufacturing process in this case.

【００３９】伸長性基材シート２として、剥離紙部２ａ
と両面接着部２ｂからなる接着テープ（ソニーケミカル
社製、ＮＰ６０８）を用意した。この接着テープは、Ｅ
ＶＡ系の熱接着性のドライタイプノンサポート両面接着
テープであり、テープの厚みは５０〜６０μｍである。
また破断伸び率（ＡＳＴＭ・Ｄ８８２−６１Ｔ）は、約
４００％であった。As the extensible base sheet 2, a release paper portion 2a
And an adhesive tape (NP608, manufactured by Sony Chemical Co., Ltd.) comprising the double-sided adhesive portion 2b. This adhesive tape is E
It is a VA type heat-adhesive dry type non-supported double-sided adhesive tape, and the thickness of the tape is 50 to 60 μm.
The breaking elongation (ASTM.D882-61T) was about 400%.

【００４０】次に、接着テープ（伸長性基材シート）２
の接着部２ｂ上に、ユニチカ（株）製のポリエステル３
５００からなる透明インキをシルクスクリーン印刷し、
開封防止テープの全幅にわたる長さ２０ｍｍに縞が伸び
ている縞柄のプライマー層３を形成した（乾燥膜厚５〜
１０μｍ）（図２（ａ））。Next, an adhesive tape (extensible base sheet) 2
Of polyester 3 made by Unitika Ltd.
Silk screen printing of 500 transparent inks,
A primer layer 3 having a stripe pattern having a stripe extending to a length of 20 mm over the entire width of the opening prevention tape was formed.
10 μm) (FIG. 2 (a)).

【００４１】次に、プライマー層３を形成した接着テー
プ２の接着部２ｂ上に、導電性ペースト（藤倉化成
（株）製、ＦＡ３０３）を印刷し、図１（ａ）に示した
導電パターンと同様のパターンであって、幅１．５ｍｍ
の導通ラインが開封防止テープのテープの長手方向に伸
びかつ長さ１５５ｍｍごとに複数回折り返され、開封防
止テープの幅２０ｍｍの範囲内で縞様柄をなしている導
電パターン４（乾燥膜厚５〜１０μｍ）を形成した（図
２（ｂ））。Next, a conductive paste (FA303, manufactured by Fujikura Kasei Co., Ltd.) was printed on the adhesive portion 2b of the adhesive tape 2 on which the primer layer 3 was formed, and the conductive pattern shown in FIG. A similar pattern with a width of 1.5 mm
The conductive line of the opening prevention tape extends in the longitudinal direction of the tape of the opening prevention tape, is bent plural times every 155 mm, and has a striped pattern within a width of 20 mm of the opening prevention tape. To 10 μm) (FIG. 2B).

【００４２】次に、上記の導電パターン４が含まれるよ
うにテープをカットし、幅２２ｍｍ、長さ１６０ｍｍの
開封防止テープの外形を得た。そしてシートの導電パタ
ーン４の両端部にそれぞれハンダ付け用端子（端子用金
属片）５として、ソニーケミカル社製、ＣＵ７６３５Ｒ
を接続した（図２（ｃ））。このＣＵ７６３５Ｒは、圧
延法で製造した３５μｍ厚の銅箔に導電性接着剤が４５
〜５５μｍ塗布されているものである。Next, the tape was cut so as to include the above-mentioned conductive pattern 4 to obtain an outer shape of an opening prevention tape having a width of 22 mm and a length of 160 mm. Solder terminals (metal pieces for terminals) 5 are provided on both ends of the conductive pattern 4 of the sheet as CU7635R manufactured by Sony Chemical Corporation.
(FIG. 2 (c)). This CU7635R is made of a copper foil having a thickness of 35 μm manufactured by a rolling method and a conductive adhesive of 45 μm.
５５55 μm.

【００４３】次に、被着体に対する接着剤層６及びその
上の剥離層７として、ソニーケミカル社製、ＮＰ２０３
をラミネートした（図２（ｄ））。このＮＰ２０３はア
クリル系ドライタイプノンサポート両面接着テープ（テ
ープ厚４０〜５０μｍ）であり、剥離層としてシリコー
ンコート紙が一体になっているものである。Next, as the adhesive layer 6 to the adherend and the release layer 7 thereon, NP203 manufactured by Sony Chemical Co., Ltd.
Was laminated (FIG. 2D). This NP203 is an acrylic dry type non-supported double-sided adhesive tape (tape thickness: 40 to 50 μm), in which a silicone-coated paper is integrated as a release layer.

【００４４】得られた開封防止テープ１の導電パターン
４の端子間電気抵抗は、１０〜２５Ω／ｃｍであった。The electrical resistance between the terminals of the conductive pattern 4 of the obtained opening prevention tape 1 was 10 to 25 Ω / cm.

【００４５】また、この開封防止テープ１を、その接着
剤層６を貼着面としてスチロール製の箱に貼着した。そ
して、導電パターン４の端子間抵抗を測定しつつこの開
封防止テープ１を剥がそうとした。その結果、開封防止
テープ１を約５ｍｍ剥がした時点で、伸長性基材シート
２の伸びにより、導電パターン４が端子５から３ｍｍ以
内の部分で破断した。The opening prevention tape 1 was attached to a styrene box with the adhesive layer 6 as an attachment surface. Then, the user tried to peel off the opening prevention tape 1 while measuring the inter-terminal resistance of the conductive pattern 4. As a result, when the opening prevention tape 1 was peeled off by about 5 mm, the conductive pattern 4 was broken at a portion within 3 mm from the terminal 5 due to the extension of the extensible base sheet 2.

【００４６】[0046]

【発明の効果】本発明によれば、伸び率が高い基材シー
トに、導電性塗料からなる導電パターンを形成したの
で、この開封防止テープを被着体に貼着し、その後これ
を剥がそうとすると、基材シートが伸び、それにより導
電パターンを構成している導電粒子相互の接触が失わ
れ、導電パターンが確実に断線状態となる。したがっ
て、導電パターンを警報装置、監視システム、記録装置
等と接続することにより、開封防止テープを貼着した被
着体の不正開封に対して、不正開封の行為時に対処する
ことが可能となり、また不正開封の日時を記録すること
も可能となる。According to the present invention, since a conductive pattern made of a conductive paint is formed on a base sheet having a high elongation, this anti-opening tape is adhered to an adherend, and then this is peeled off. Then, the base sheet elongates, whereby the contact between the conductive particles constituting the conductive pattern is lost, and the conductive pattern surely becomes disconnected. Therefore, by connecting the conductive pattern to an alarm device, a monitoring system, a recording device, and the like, it becomes possible to cope with an unauthorized opening of the adherend to which the anti-opening tape is attached, in the event of an unauthorized opening, It is also possible to record the date and time of unauthorized opening.

【００４７】また、本発明の開封防止テープによれば、
導電パターンを上下で挟む一対の粘着材の導電パターン
に対する粘着力の大小を、隣接する領域ごとに逆転させ
るという構成が不要であり、容易に作製すること可能と
なる。According to the opening prevention tape of the present invention,
A configuration in which the magnitude of the adhesive force of the pair of adhesives sandwiching the conductive pattern at the top and bottom with respect to the conductive pattern is not required to be reversed for each adjacent region is possible, and the device can be easily manufactured.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の開封防止テープの平面図（同図
（ａ））及び断面図（同図（ｂ））である。FIG. 1 is a plan view (FIG. 1A) and a cross-sectional view (FIG. 1B) of an opening prevention tape of the present invention.

【図２】実施例の開封防止テープの製造工程の説明図で
ある。FIG. 2 is an explanatory diagram of a manufacturing process of the unsealing prevention tape of the example.

【図３】従来の開封防止テープの断面図である。FIG. 3 is a sectional view of a conventional opening prevention tape.

【図４】従来の開封防止テープの断面図である。FIG. 4 is a sectional view of a conventional opening prevention tape.

【図５】従来の開封防止テープの断面図である。FIG. 5 is a cross-sectional view of a conventional opening prevention tape.

【図６】従来の開封防止テープの断面図（同図（ａ））
及びその開封時の説明図（同図（ｂ））である。FIG. 6 is a sectional view of a conventional opening prevention tape (FIG. 6A).
And an explanatory diagram at the time of opening the same (FIG. (B)).

【符号の説明】[Explanation of symbols]

１…開封防止テープ、 ２…伸長性基材シート、 ３…
プライマー層、 ４…導電パターン、 ５…端子用金属
片、 ６…接着剤層1 ... opening prevention tape, 2 ... extensible base sheet, 3 ...
Primer layer, 4: conductive pattern, 5: metal piece for terminal, 6: adhesive layer

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 破断伸び率が１０％以上の伸長性基材シ
ート、導電性塗料から形成された導電パターン及び接着
剤層からなる積層構造を有することを特徴とする開封防
止テープ。1. An anti-opening tape having a laminated structure comprising an extensible base sheet having an elongation at break of 10% or more, a conductive pattern formed from a conductive paint, and an adhesive layer. 【請求項２】 伸長性基材シートの破断伸び率が３００
％以上である請求項１記載の開封防止テープ。2. The extensible base sheet has a breaking elongation of 300.
%. 【請求項３】 伸長性基材シートと導電パターンとの間
にこれらの接着力を高めるプライマー層が形成されてい
る請求項１記載の開封防止テープ。3. The anti-sealing tape according to claim 1, wherein a primer layer for increasing the adhesive strength between the extensible base sheet and the conductive pattern is formed. 【請求項４】 プライマー層が、開封防止テープの長手
方向に非連続パターンに形成されている請求項３記載の
開封防止テープ。4. The anti-opening tape according to claim 3, wherein the primer layer is formed in a discontinuous pattern in the longitudinal direction of the anti-opening tape. 【請求項５】 プライマー層の伸長性基材シートに対す
る面積率が、５〜９０％である請求項３又は４記載の開
封防止テープ。5. The anti-opening tape according to claim 3, wherein the area ratio of the primer layer to the extensible base sheet is 5 to 90%. 【請求項６】 導電パターンが、開封防止テープの長手
方向に伸びた帯状に形成されている請求項１〜５のいず
れかに記載の開封防止テープ。6. The anti-opening tape according to claim 1, wherein the conductive pattern is formed in a belt shape extending in the longitudinal direction of the anti-opening tape. 【請求項７】 導電パターンの端部に端子用金属片が接
続されている請求項１〜６のいずれかに記載の開封防止
テープ。7. The unsealing prevention tape according to claim 1, wherein a terminal metal piece is connected to an end of the conductive pattern.