JPH0990858A - Biodecomposable hologram brittle seal - Google Patents
Biodecomposable hologram brittle sealInfo
- Publication number
- JPH0990858A JPH0990858A JP7245937A JP24593795A JPH0990858A JP H0990858 A JPH0990858 A JP H0990858A JP 7245937 A JP7245937 A JP 7245937A JP 24593795 A JP24593795 A JP 24593795A JP H0990858 A JPH0990858 A JP H0990858A
- Authority
- JP
- Japan
- Prior art keywords
- hologram
- layer
- biodegradable
- thin film
- brittle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、鮮明な画像ができ
る生分解性を有するプラスチックフィルムを支持体とし
たホログラムに係わり、ホログラムの貼り換えなどによ
る偽造、若しくは改ざんを困難にする脆性ホログラムを
形成するホログラムシールに関し、特に本発明のホログ
ラム脆性シールは真偽判別シールとして高いセキュリテ
ィ性を有するとともに、使用済の廃棄処理が容易であっ
て、廃棄処理による公害の心配がなく、自然環境に悪影
響のない環境に優しい生分解性ホログラム脆性シールに
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a hologram using a biodegradable plastic film capable of forming a clear image as a support, and forming a brittle hologram which makes it difficult to forge or falsify the hologram by replacing it. With regard to the hologram seal, in particular, the hologram brittle seal of the present invention has high security as a genuine / counterfeit discrimination seal, and is easy to dispose of after use, and there is no concern of pollution due to the disposal process, which may adversely affect the natural environment. Not related to eco-friendly biodegradable hologram brittle seal.
【０００２】[0002]
【従来の技術】近年、立体画像を再生し得る光の干渉を
利用したホログラム画像の開発が進められ、このホログ
ラムは高度な製造技術を要するとともに、様々な形態、
例えばラベル・シール、箔状に形成可能なことから、こ
れを応用し偽造防止手段としてビデオカセット、コンパ
クトディスク、スポーツ用品、ブランド品、ＲＯＭボー
ド（フロッピーディスクなど電子信号情報記録体）等の
一部に貼着して使用され、さらには各種のパッケージの
封印シールとして使用されている。2. Description of the Related Art In recent years, the development of hologram images utilizing the interference of light capable of reproducing a stereoscopic image has been advanced, and this hologram requires a high manufacturing technology and various forms.
For example, since it can be formed into a label, a seal, or a foil, it can be applied as a counterfeit prevention means for video cassettes, compact discs, sports equipment, brand products, ROM boards (electronic signal information recording bodies such as floppy disks), etc. It is used by sticking it on and used as a seal for various packages.
【０００３】このホログラムは、一見して本物か偽造で
あるかが判定でき、しかも製造困難なことから偽造防止
用として、またセキュリティ性の付与のために広く利用
されている。This hologram can be judged at a glance whether it is genuine or counterfeit, and since it is difficult to manufacture, it is widely used for the purpose of preventing forgery and for imparting security.
【０００４】また、各ホログラム製品は、立体的な画像
が得られ、高級感もあるので一般の商品に広く使われて
いる。Further, each hologram product is widely used as a general product because a three-dimensional image can be obtained and a sense of quality can be obtained.
【０００５】これらのホログラム製品、特にラベル・シ
ール等として使用されているホログラム製品の支持体材
料は、殆ど透明なプラスチックフィルム（またはシー
ト）から製造されたもので、例えば、透明なポリエチレ
ンテレフタレートフィルム、ポリ塩化ビニル、ポリエス
テル、ポリカーボネート、ポリメタクリル酸メチル、ポ
リスチレン、ポリプロピレン等の合成樹脂、天然樹脂が
使用されている。The support material for these hologram products, particularly hologram products used as labels and seals, is produced from an almost transparent plastic film (or sheet), for example, a transparent polyethylene terephthalate film, Synthetic and natural resins such as polyvinyl chloride, polyester, polycarbonate, polymethylmethacrylate, polystyrene and polypropylene are used.
【０００６】上記のような支持体材料を用いたホログラ
ムシールが、物品に貼付された後に剥がされ、悪用され
ることがないように支持体とホログラム層、或いはこれ
らの間に設けられた剥離層と支持体、又はホログラム層
で剥離するようにし、被着体から故意に剥離させた場合
にホログラム全体が破壊されるものがあり、また実公平
５−４８２１０号公報に開示されるホログラム脆性シー
ルのように、支持体とホログラム形成層との間にパター
ン状の剥離層を形成しておき、被着後ホログラムを端部
から剥がそうとすると、支持体とホログラム形成層とが
剥離するものがある。The hologram seal using the support material as described above is peeled off after being attached to an article so as not to be misused, or the release layer provided between the support and the hologram layer. And a support or a hologram layer, the entire hologram is destroyed when it is intentionally peeled off from an adherend, and the hologram brittle seal disclosed in Japanese Utility Model Publication No. 5-48210. As described above, when a patterned release layer is formed between the support and the hologram forming layer and the hologram is tried to be peeled off from the end portion after the attachment, there is a case where the support and the hologram forming layer are separated from each other. .
【０００７】[0007]
【発明が解決しようとする課題】しかしながら、前者の
全面破壊型のホログラム脆性シールは、剥がし方によっ
てはホログラム層及び反射性薄膜層を破壊することな
く、ホログラムシール全体を完全に剥離させてしまう可
能性がある。そのため、ホログラム層及び反射性薄膜層
自体を破壊する方法として後者の方法があるが、この方
法ではホログラム脆性シールを貼着した状態で見ると、
ホログラム形成層及び反射性薄膜層の上にパターン状の
剥離層が設けられているため、そのパターンの存在を目
視により判別でき、ホログラムの再生画像のよう見え方
に影響を与えるだけでなく、偽造防止策の存在が明らか
に成ってしまうという問題を有する。However, according to the former method, the hologram fragile seal of total destruction type can completely peel the hologram seal without destroying the hologram layer and the reflective thin film layer depending on the peeling method. There is a nature. Therefore, there is the latter method as a method of destroying the hologram layer and the reflective thin film layer itself, but in this method, when viewed with the hologram brittle seal attached,
Since the patterned peeling layer is provided on the hologram forming layer and the reflective thin film layer, the presence of the pattern can be visually discerned, not only affecting the appearance of the reproduced image of the hologram, but also the forgery. There is a problem that the existence of preventive measures is clearly established.
【０００８】また、従来のプラスチックホログラムシー
ルは、各種用品に貼着して使用された後は、適宜剥がさ
れ、或いは剥がされずに用品と一緒にそのまま廃棄され
ている。現在のところ、廃棄処理は焼却又は埋め立てな
どの処理によって廃棄されているが、特にプラスチック
の廃棄処理は、焼却における焼却温度の高熱化が起こ
り、そのため焼却炉の耐久性の問題や、燃焼ガスなどに
よる公害問題があり、また埋め立て処理における土壌中
に分解せず原型のまま存在する問題などがあるため、半
永久的に廃棄物として土壌中に残留して自然環境に放置
されたままになると、美観上の問題に加えて、生体系へ
の影響も深刻になる。[0008] Further, the conventional plastic hologram seal is used after being attached to various products, and is appropriately peeled, or is not peeled and is discarded as it is together with the products. At present, waste treatment is discarded by treatment such as incineration or landfill, but especially in the waste treatment of plastics, the incineration temperature rises during incineration, which causes the problem of durability of incinerator and combustion gas. There is a problem of pollution caused by wastewater, and there is a problem that it remains in its original form without being decomposed in the soil during landfill processing, so if it remains semi-permanently as waste in the soil and is left in the natural environment, it will not be beautiful. In addition to the above problems, the impact on biological systems becomes serious.
【０００９】そこで本発明は、上記の問題点を解決すべ
くなされたものであって、不正な剥離行為によるホログ
ラムシールの貼り替えを防止することが可能なホログラ
ム脆性シールで、とくに部分的に脆性破壊する層の存在
を発見しにくく、剥離により完全に再生不可能となり、
しかも廃棄処理が容易な生分解性ホログラム脆性シール
を提供することを目的とする。Therefore, the present invention has been made to solve the above-mentioned problems, and is a hologram brittle seal capable of preventing replacement of the hologram seal due to an illegal peeling action, and is particularly partially brittle. It is difficult to find the existence of the layer to be destroyed, and peeling makes it completely impossible to reproduce,
Moreover, it is an object to provide a biodegradable hologram brittle seal that can be easily disposed of.
【００１０】[0010]
【課題を解決するための手段】目的を達成するため本発
明の第１の発明によれば、透明で生分解性を有する（数
平均分子量が、10,000〜100,000 であるポリ乳酸とオキ
シカルボン酸のコポリマーを主成分とする) フィルム
（支持体）１上に、少なくとも剥離層２、ホログラムパ
ターン３を有する透明なホログラム形成層４と反射性薄
膜層５と、前記反射性薄膜層の少なくとも一部を覆う脆
性剥離層６、接着層７とを順次設けたことを特徴とする
生分解性ホログラム脆性シールである。According to the first aspect of the present invention for achieving the object, it is transparent and biodegradable (of polylactic acid and oxycarboxylic acid having a number average molecular weight of 10,000 to 100,000). Copolymer as main component) On a film (support) 1, at least a peeling layer 2, a transparent hologram forming layer 4 having a hologram pattern 3, a reflective thin film layer 5, and at least a part of the reflective thin film layer. The biodegradable hologram brittle seal is characterized in that a brittle peeling layer 6 for covering and an adhesive layer 7 are sequentially provided.
【００１１】第２の発明によれば、一方の面に、ホログ
ラムパターン３を成形してなる透明な生分解性を有する
ポリ乳酸フィルム（支持体）１上に、反射性薄膜層５
と、前記反射性薄膜層の少なくとも一部を覆う脆性剥離
層６、接着層７とを設けたことを特徴とする生分解性ホ
ログラム脆性シールである。According to the second invention, the reflective thin film layer 5 is formed on the transparent biodegradable polylactic acid film (support) 1 formed by molding the hologram pattern 3 on one surface.
And a brittle peeling layer 6 and an adhesive layer 7 which cover at least a part of the reflective thin film layer, and a biodegradable hologram brittle seal.
【００１２】第１の発明に係わる発明は、前記ホログラ
ムパターン３を有する透明なホログラム形成層４は、溶
剤可溶性生分解性樹脂からなることを特徴とする。The invention according to the first aspect is characterized in that the transparent hologram forming layer 4 having the hologram pattern 3 is made of a solvent-soluble biodegradable resin.
【００１３】第１又は第２の発明に係わる発明は、前記
透明で生分解性を有するポリ乳酸フィルム１のいずれか
一方の面に、印刷層８を設けたことを特徴とする。The invention according to the first or second invention is characterized in that a printing layer 8 is provided on either surface of the transparent and biodegradable polylactic acid film 1.
【００１４】第１の発明に係わる発明は、前記ホログラ
ム形成層４のいずれか一方の面に、印刷層８を設けたこ
とを特徴とする。The invention according to the first aspect is characterized in that a printing layer 8 is provided on either surface of the hologram forming layer 4.
【００１５】また、第１又は第２の発明に係わる発明
は、前記反射性薄膜層５が、光不透過性薄膜であること
を特徴とする。The invention according to the first or second invention is characterized in that the reflective thin film layer 5 is a light-impermeable thin film.
【００１６】第１の発明に係わる発明は、前記反射性薄
膜層が、前記ホログラム形成層４と異なる屈折率を有す
る光透過性薄膜であることを特徴とする。The invention according to the first aspect is characterized in that the reflective thin film layer is a light transmissive thin film having a refractive index different from that of the hologram forming layer 4.
【００１７】第２の発明に係わる発明は、前記反射性薄
膜層５が、前記生分解性を有するプラスチックフィルム
１と異なる屈折率を有する光透過性薄膜であることを特
徴とする。The invention according to the second aspect is characterized in that the reflective thin film layer 5 is a light transmissive thin film having a refractive index different from that of the biodegradable plastic film 1.
【００１８】[0018]
【発明の実施の形態】本発明は、透明で生分解性を有す
る（数平均分子量が、10,000〜100,000 であるポリ乳酸
とオキシカルボン酸のコポリマーを主成分とする) フィ
ルム（支持体）１上に、少なくとも剥離層２、ホログラ
ムパターン３を有する透明なホログラム形成層４と反射
性薄膜層５と、前記反射性薄膜層の少なくとも一部を覆
う脆性剥離層６、接着層７とを順次設けたことを特徴と
する生分解性ホログラム脆性シールである。BEST MODE FOR CARRYING OUT THE INVENTION The present invention comprises a film (support) 1 which is transparent and biodegradable (based on a copolymer of polylactic acid and oxycarboxylic acid having a number average molecular weight of 10,000 to 100,000). At least a peeling layer 2, a transparent hologram forming layer 4 having a hologram pattern 3, a reflective thin film layer 5, a brittle peeling layer 6 covering at least a part of the reflective thin film layer, and an adhesive layer 7 were sequentially provided. A biodegradable hologram brittle seal characterized by the above.
【００１９】[0019]
【作用】本発明によれば、反射性薄膜層の下面に脆性剥
離層を形成することにより、シール貼着後の外部からそ
の存在認識が困難であり、かつ故意による剥離に対して
ホログラムに部分的な脆性破壊を生じる。また、ホログ
ラム再生画像が脆性剥離層の存在による影響を受けるこ
とがなく、偽造防止性及び改ざん防止性を向上させるこ
とができる。According to the present invention, since the brittle peeling layer is formed on the lower surface of the reflective thin film layer, it is difficult to recognize its presence from the outside after the sticking of the seal, and the hologram is partially peeled off by intentional peeling. Brittle fracture occurs. Further, the reproduced hologram image is not affected by the presence of the brittle peeling layer, and the forgery prevention property and the tampering prevention property can be improved.
【００２０】また、印刷層の形成は、装飾性を高める効
果があるのに加えて、剥離によりホログラムと同様に部
分的に破壊されるため、偽造防止性、改ざん防止性を向
上させることができる。Further, in addition to the effect of enhancing the decorative property, the formation of the printing layer can be partially destroyed by peeling like the hologram, so that the forgery prevention property and the tampering prevention property can be improved. .
【００２１】また、反射性薄膜層をホログラム形成層と
は異なる屈折率を有する光透過性薄膜層とすることによ
って、被貼着体の下地のデザイン、模様、文字等の画像
や色などを損なうことなく、一層装飾性の向上を図るこ
とができるとともに、偽造防止性、改ざん防止性も高
い。特に、本発明の生分解性ホログラム脆性シールは、
透明な生分解性を有するフィルムと生分解性を有するホ
ログラム形成層で構成したので、普通の環境下にて偽造
防止や改ざん防止及び一般の目的（シールとしての通常
用途）に使用する際は、従来の生分解性ではないプラス
チック材料を用いたホログラムシールと同じに、外部か
らの衝撃や水濡れ等に対する耐久性や耐水性、及び耐薬
品性などを有し、かつ、偽造防止や改ざん防止等のセキ
ュリティ性が、従来のホログラムシールより向上すると
ともに、使用後の廃棄処理においては、土壌中に埋め立
て廃棄処理、或いはコンポストでの廃棄処理をすると、
微生物の作用により支持体とホログラム形成層が分解す
ることでシール全体が破壊して、最終的に水、炭酸ガ
ス、メタンガスなどにまで分解される。Further, by making the reflective thin film layer a light transmissive thin film layer having a refractive index different from that of the hologram forming layer, the image and color of the underlying substrate design, pattern, characters, etc. are impaired. It is possible to further improve the decorative property without having to do so, and it is also highly resistant to forgery and tampering. In particular, the biodegradable hologram brittle seal of the present invention,
Since it is composed of a transparent biodegradable film and a biodegradable hologram-forming layer, when used for normal purposes in anti-counterfeiting and tampering prevention and for general purposes (usual use as a seal), Same as a conventional hologram seal using a non-biodegradable plastic material, it has durability against external impact and water wetting, water resistance, chemical resistance, etc., and forgery prevention and tampering prevention etc. Is more secure than the conventional hologram sticker, and in the disposal after use, if it is landfilled in the soil or disposed of by compost,
When the support and the hologram-forming layer are decomposed by the action of microorganisms, the entire seal is destroyed, and finally, water, carbon dioxide gas, methane gas or the like is decomposed.
【００２２】また、印刷層の形成は、装飾性を高める効
果があるのに加えて、製造困難のため偽造防止性、改ざ
ん防止性を向上させることができる。In addition to the effect of enhancing the decorative property, the formation of the printing layer can improve the forgery prevention property and the tampering prevention property due to manufacturing difficulty.
【００２３】また、本発明の生分解性ホログラム脆性シ
ールは、土壌中への埋め立て処理による生分解処理と、
燃焼炉による焼却処理とを併用することができ、焼却処
理する場合には低カロリーの燃焼熱で焼却処理すること
ができる。The biodegradable hologram brittle seal of the present invention comprises a biodegradation treatment by landfill treatment in soil,
It can be used in combination with incineration treatment by a combustion furnace, and when incineration treatment can be performed with low calorie combustion heat.
【００２４】[0024]
【実施例】以下、本発明の生分解性ホログラム脆性シー
ルを、図面に従って詳細に説明する。The biodegradable hologram brittle seal of the present invention will be described in detail below with reference to the drawings.
【００２５】図１は、本発明の一実施例における生分解
性ホログラム脆性シールの構成を示す断面図であり、透
明で生分解性を有するプラスチックフィルム（支持体）
１の下面に、脆性シールを剥離し易くするため剥離層２
が形成されている。FIG. 1 is a cross-sectional view showing the structure of a biodegradable hologram brittle seal according to an embodiment of the present invention, which is a transparent and biodegradable plastic film (support).
A peeling layer 2 is formed on the lower surface of 1 to facilitate peeling of the brittle seal.
Are formed.
【００２６】また、前記剥離層２の下に、透明ホログラ
ム形成層４が形成されている。A transparent hologram forming layer 4 is formed under the peeling layer 2.
【００２７】さらに、前記ホログラム形成層４は、前記
生分解性ポリ乳酸フィルム（支持体）１とは反対側のホ
ログラム形成層４面に、ホログラムパターン３を備え
る。Further, the hologram forming layer 4 is provided with a hologram pattern 3 on the surface of the hologram forming layer 4 opposite to the biodegradable polylactic acid film (support) 1.
【００２８】前記ホログラム形成面には、前記ホログラ
ムパターン３面上より反射性薄膜層５が、真空蒸着、ス
パッタリング等により形成されている。なお、前記ホロ
グラム形成面は、レリーフ型ホログラムを構成する微細
な凹凸パターンが形成されたニッケル製のプレス版をホ
ログラム形成層４上に加熱押圧することにより形成可能
である。また、このようにホログラム形成層４表面にホ
ログラムパターンを有する場合は、例えばレインボーホ
ログラムや二光束干渉もしくは電子ビーム（ＥＢ）によ
る回折格子（グレーティング）により微細凹凸形状を有
するようにしたグレーティングホログラム等が適用可能
である。On the hologram forming surface, a reflective thin film layer 5 is formed on the surface of the hologram pattern 3 by vacuum vapor deposition, sputtering or the like. The hologram forming surface can be formed by heating and pressing a press plate made of nickel on which a fine relief pattern forming a relief hologram is formed on the hologram forming layer 4. When the surface of the hologram forming layer 4 has a hologram pattern, for example, a rainbow hologram or a grating hologram having a fine concavo-convex shape by a two-beam interference or a diffraction grating (grating) by an electron beam (EB) is used. Applicable.
【００２９】前記反射性薄膜層５には、少なくとも一部
を覆うように形成した脆性剥離層６が設けられている。
その上に接着層７が形成され、この接着層７には、図示
はしないが、紙等の基材シート上にシリコン樹脂などの
離型性樹脂をコーティングした離型シートが剥離可能に
仮貼着されている。The reflective thin film layer 5 is provided with a brittle peeling layer 6 formed so as to cover at least a part thereof.
An adhesive layer 7 is formed on the adhesive layer 7, and although not shown, a release sheet obtained by coating a base sheet such as paper with a release resin such as silicone resin is detachably temporarily attached to the adhesive layer 7. It is worn.
【００３０】本発明の生分解性ホログラム脆性シールの
支持体１材料は、ポリ乳酸樹脂（島津製作所（株）製、
商品名「ラクティ」）を用いて、Ｔダイ溶融押出しによ
りシートを成形してなる二軸延伸されたフィルムであ
り、フィルムの透明性が優れ、厚さ４０μｍのフィルム
の光透過率が９４％以上である。The support 1 material of the biodegradable hologram brittle seal of the present invention is a polylactic acid resin (manufactured by Shimadzu Corporation,
It is a biaxially stretched film obtained by molding a sheet by T-die melt extrusion using the product name “Lacty”), and the film has excellent transparency, and the light transmittance of a film having a thickness of 40 μm is 94% or more. Is.
【００３１】上記生分解性を有するポリ乳酸フィルムに
おいて、フィルムの透明性が影響しなければ、各種フィ
ラーを添加することができる。また、各種添加剤やポリ
マー等の非分解性の物質を添加することは可能である。
しかしながら、非分解性の物質を１０％以上添加するこ
とは、分解性と物性が著しく低下し、加工上の問題が生
じ、透明性が低下するため、好ましくない。In the biodegradable polylactic acid film, various fillers can be added as long as the transparency of the film does not influence. Further, it is possible to add various additives and non-degradable substances such as polymers.
However, it is not preferable to add a non-decomposable substance in an amount of 10% or more, because the decomposability and the physical properties are remarkably deteriorated, processing problems occur, and the transparency is deteriorated.
【００３２】生分解性フィルムによる支持体１は、厚さ
１０〜１００μｍの透明なフィルムが使用可能である
が、厚さは２０〜７０μｍが最適である。As the support 1 made of a biodegradable film, a transparent film having a thickness of 10 to 100 μm can be used, and the optimum thickness is 20 to 70 μm.
【００３３】また、剥離層２は、ホログラム形成層及び
反射性薄膜層の剥離を便利にするために設けられた層で
ある。この剥離層の接着力が強すぎる、或いは弱すぎる
と剥離に支障をきたすので、剥離層の組成及び膜厚のコ
ントロールが非常に重要である。本発明の場合は、以下
の配合比からなる組成物を、マイクログラビアコーティ
ングにより、乾燥温度１１０℃、厚さ０．２〜１μｍで
形成されている。 剥離層の組成 アクリル樹脂（三菱レイヨン（株）製，ダイヤナルBR80）１５部 メチルエチルケトン（東洋インキ製造（株）製） ５５部 トルエン （東洋インキ製造（株）製） ３０部The peeling layer 2 is a layer provided to facilitate peeling of the hologram forming layer and the reflective thin film layer. If the adhesive strength of the release layer is too strong or too weak, peeling will be hindered, so control of the composition and film thickness of the release layer is very important. In the case of the present invention, a composition having the following blending ratio is formed by microgravure coating at a drying temperature of 110 ° C. and a thickness of 0.2 to 1 μm. Composition of release layer Acrylic resin (Mitsubishi Rayon Co., Ltd., Dianal BR80) 15 parts Methyl ethyl ketone (Toyo Ink Mfg. Co., Ltd.) 55 parts Toluene (Toyo Ink Mfg. Co., Ltd.) 30 parts
【００３４】ホログラム形成層４は、例えばレリーフ型
ホログラムの場合はエンボス成形性が良好で、プレスむ
らが生じ難く、明るい再生画像が得られ、かつ、生分解
性プラスチックフィルム１とホログラム形成層４及び反
射性薄膜層５との接着性が良好な樹脂が要求され、以下
の配合比からなる組成物がグラビア法により、乾燥温度
１１０℃、厚さ１．０μｍで形成されている。 ホログラム形成層の組成 ポリ乳酸樹脂 （東洋紡（株）製） ２５部 メチルエチルケトン（東洋インキ製造（株）製） ２０部 トルエン （東洋インキ製造（株）製） ２５部 また、ホログラム形成面は、このような組成物のホログ
ラム形成層４に対し、プレス版の版面温度を１２０〜１
５０℃として押圧により形成される。In the case of a relief type hologram, for example, the hologram forming layer 4 has good embossing moldability, is less likely to cause press unevenness, and produces a bright reproduced image, and the biodegradable plastic film 1 and the hologram forming layer 4 and A resin having good adhesiveness to the reflective thin film layer 5 is required, and a composition having the following compounding ratio is formed by a gravure method at a drying temperature of 110 ° C. and a thickness of 1.0 μm. Composition of hologram-forming layer Polylactic acid resin (manufactured by Toyobo Co., Ltd.) 25 parts Methyl ethyl ketone (manufactured by Toyo Ink Mfg. Co., Ltd.) 20 parts Toluene (manufactured by Toyo Ink Mfg. Co., Ltd.) 25 parts The plate surface temperature of the press plate is 120 to 1 for the hologram forming layer 4 of various compositions.
It is formed by pressing at 50 ° C.
【００３５】なお、ホログラム形成層４としては、ポリ
乳酸樹脂以外、ポリカプラクトン（ＰＣＬ）樹脂等の生
分解性を有する樹脂が使用でき、また、生分解性を有し
ない樹脂、ポリカーボネート樹脂、ポリスチレン樹脂、
ポリ塩化ビニル樹脂などの熱可塑性樹脂、不飽和ポリエ
ステル樹脂、メラミン樹脂、エポキシ樹脂、ウレタン
（メタ）アクリレート、ポリエステル（メタ）アクリレ
ート、エポキシ（メタ）アクリレート、ポリオール（メ
タ）アクリレート、メラミン（メタ）アクリレート、ト
リアジン（メタ）アクリレートなどの熱硬化性樹脂、或
いはこれらの混合物、さらにはラジカル重合性不飽和基
を有する熱成形性材料などが、生分解性樹脂とブレンド
して使用可能であり、また、上記以外のものでも、ホロ
グラム画像を形成可能な安定性を有する材料であれば使
用可能である。As the hologram forming layer 4, a resin having biodegradability such as polycaplacton (PCL) resin can be used in addition to the polylactic acid resin, and a resin having no biodegradability, a polycarbonate resin, or a polystyrene resin can be used. resin,
Thermoplastic resin such as polyvinyl chloride resin, unsaturated polyester resin, melamine resin, epoxy resin, urethane (meth) acrylate, polyester (meth) acrylate, epoxy (meth) acrylate, polyol (meth) acrylate, melamine (meth) acrylate , A thermosetting resin such as triazine (meth) acrylate, or a mixture thereof, or a thermoformable material having a radically polymerizable unsaturated group, and the like can be used by blending with a biodegradable resin, and Materials other than those described above can be used as long as they are stable materials that can form a hologram image.
【００３６】反射性薄膜層５は入射光線を反射する層で
あって、厚さ１００ｎｍのアルミニウムが真空蒸着法に
より形成されている。なお、反射性薄膜層５としては、
他に銀、金、錫、窒化チタン（ＴｉＮｘ）が使用可能で
ある。この場合、後述する脆性剥離層６が薄膜層の下に
存在することを認識するのが非常に困難なため偽造防止
性を向上させることができる。The reflective thin film layer 5 is a layer that reflects incident light and is made of aluminum having a thickness of 100 nm formed by a vacuum deposition method. In addition, as the reflective thin film layer 5,
Besides, silver, gold, tin, and titanium nitride (TiNx) can be used. In this case, since it is very difficult to recognize that the brittle peeling layer 6 described below exists under the thin film layer, it is possible to improve the forgery prevention property.
【００３７】反射性薄膜層５の少なくとも一部を覆うよ
うに形成した脆性剥離層６は、ホログラム脆性シールの
貼着後、ホログラム脆性シールを剥離した場合に、脆性
剥離層６と反射性薄膜層５の界面が剥離するか、若しく
は脆性剥離層６が接着層７を弾くようにするために設け
られたものであり、グラビア印刷法の他に、オフセット
印刷法又はスクリーン印刷法等により形成される。この
脆性剥離層６は、反射性薄膜層５の一部に設けられ、文
字・マーク等のメッセージを表すように設けることも可
能で、その形状は任意であるが、ホログラムを不正に剥
離した状態であることが明確に判別できるようにするこ
とが必要である。The brittle peeling layer 6 formed so as to cover at least a part of the reflective thin film layer 5 is the brittle peeling layer 6 and the reflective thin film layer when the hologram brittle seal is peeled after the hologram brittle seal is attached. 5 is peeled off or the brittle peeling layer 6 is provided so as to repel the adhesive layer 7, and is formed by an offset printing method, a screen printing method or the like in addition to the gravure printing method. . The brittle peeling layer 6 may be provided on a part of the reflective thin film layer 5 so as to show a message such as characters and marks. The shape is arbitrary, but the hologram is peeled off illegally. It is necessary to be able to clearly determine that
【００３８】脆性剥離層６は、例えば以下の配合比から
なる組成物をグラビア法により、乾燥温度１１０℃、厚
さ０．５μｍで形成されている。 脆性剥離層の組成 アクリル樹脂（三菱レイヨン（株）製，ダイヤナルBR80） ３０部 メチルエチルケトン（東洋インキ製造（株）製） ４０部 トルエン （東洋インキ製造（株）製） ４０部 メチルイソブチルケトン（東洋インキ製造（株）製） ２０部The brittle peeling layer 6 is formed, for example, by a gravure method using a composition having the following composition ratio at a drying temperature of 110 ° C. and a thickness of 0.5 μm. Composition of brittle release layer Acrylic resin (Mitsubishi Rayon Co., Ltd., Dianal BR80) 30 parts Methyl ethyl ketone (Toyo Ink Mfg. Co., Ltd.) 40 parts Toluene (Toyo Ink Mfg. Co., Ltd.) 40 parts Methyl isobutyl ketone (Toyo Ink Co., Ltd.) Manufacturing Co., Ltd. 20 parts
【００３９】接着層７としては、以下の配合比からなる
組成物がグラビア法により、乾燥温度１１０℃、厚さ２
０μｍで形成されている。 接着層の組成 アクリル系粘着剤（東洋インキ製造（株）製，オリバイン）３０部 メチルエチルケトン（東洋インキ製造（株）製） ５０部 トルエン （東洋インキ製造（株）製） ５０部 なお、接着層７としては、他にも反射性薄膜層５及び脆
性剥離層６を変質させたり、冒すものでなければ通常用
いられるものでよく、接着成分としては、ブチルゴム
系、天然ゴム系、シリコン系、ポリイソブチル系が挙げ
られるが、その限りではない。また、アルキルメタクリ
レート、ビニルエステル、アクリルニトリル、スチレ
ン、ビニルモノマー等が挙げられる凝集成分、不飽和カ
ルボン酸、ヒドロキシル基含有モノマー、アクリルニト
リル等に代表される改質成分や重合開始剤、可塑剤、硬
化剤、硬化促進剤、酸化防止剤等の添加剤を必要に応じ
て添加することができる。As the adhesive layer 7, a composition having the following compounding ratio was used by a gravure method to obtain a drying temperature of 110 ° C. and a thickness of 2
It is formed at 0 μm. Composition of adhesive layer Acrylic adhesive (manufactured by Toyo Ink Mfg. Co., Ltd., Olivine) 30 parts Methyl ethyl ketone (manufactured by Toyo Ink Mfg. Co., Ltd.) 50 parts Toluene (manufactured by Toyo Ink Mfg. Co., Ltd.) 50 parts Adhesive layer 7 Other than the above, it may be a commonly used one as long as it does not alter or affect the reflective thin film layer 5 and the brittle peeling layer 6, and the adhesive component may be a butyl rubber type, a natural rubber type, a silicone type, polyisobutyl. The system is mentioned, but not limited thereto. Further, alkyl methacrylate, vinyl ester, acrylonitrile, styrene, aggregating components such as vinyl monomers, unsaturated carboxylic acids, hydroxyl group-containing monomers, modifying components typified by acrylonitrile and polymerization initiators, plasticizers, Additives such as a curing agent, a curing accelerator and an antioxidant can be added as necessary.
【００４０】図２は、第２の発明に係わる生分解性ホロ
グラム脆性シールの構成を示す断面図であり、透明な生
分解性を有するフィルム（支持体）１の下面に、ホログ
ラムパターン３を備える。すなわち生分解性プラスチッ
クフィルムに直接エンボスしてホログラムを形成するこ
とが特徴である。FIG. 2 is a cross-sectional view showing the structure of the biodegradable hologram brittle seal according to the second invention, in which a hologram pattern 3 is provided on the lower surface of a transparent biodegradable film (support) 1. . That is, the feature is that the hologram is formed by directly embossing the biodegradable plastic film.
【００４１】生分解性ホログラム脆性シールは、生分解
性を有するプラスチックフィルム１の片面にホログラム
パターン３が形成されている。このホログラムパターン
の下に反射性薄膜層５が真空蒸着、スパッタリング等に
より形成されている。なお、このホログラムパターン３
の形成については、レリーフ型ホログラムを構成する微
細な凹凸パターンが形成されたニッケル製のプレス板
を、前記フィルムに加熱押圧することにより形成するこ
とができる。また、このホログラムパターン３表面にホ
ログラムパターンを有する場合は、例えばレインボーホ
ログラムや二光束干渉若しくは電子ビーム（ＥＢ）によ
る回折格子（グレーティング）により微細凹凸形状を有
するようにしたグレーティングホログラム等が適用可能
である。また、生分解性プラスチックフィルム１を押出
し成形する際に、直接エボスすることもできる。The biodegradable hologram brittle seal has a hologram pattern 3 formed on one surface of a biodegradable plastic film 1. A reflective thin film layer 5 is formed under the hologram pattern by vacuum deposition, sputtering or the like. In addition, this hologram pattern 3
The film can be formed by heating and pressing a nickel press plate on which a fine relief pattern forming a relief hologram is formed on the film. Further, when the hologram pattern 3 has a hologram pattern on its surface, for example, a rainbow hologram or a grating hologram having a fine concavo-convex shape by a two-beam interference or a diffraction grating (grating) by an electron beam (EB) can be applied. is there. Further, when the biodegradable plastic film 1 is extruded, it is possible to directly emboss it.
【００４２】図３は、第１及び第２の発明に係わり、印
刷層を設けた生分解性ホログラム脆性シールの一例を示
す断面図である。本発明の生分解性ホログラム脆性シー
ルは、生分解性を有するプラスチックフィルム（支持
体）１の下にホログラム形成層４、前記ホログラム形成
層の下に印刷層８、反射性薄膜層５、脆性剥離層６、接
着層７の順に形成されている。印刷層８は、文字やマー
ク等の図柄を印刷したものである。印刷方式としては、
グラビア印刷の他に、オフセット印刷やスクリーン印刷
等の方法がある。印刷層は、例えば以下の配合比からな
るインキ組成がグラビア印刷法により、乾燥温度１００
℃、厚さ１．０μｍで形成されている。 印刷層のインキ組成 ポリエステル樹脂（東洋紡（株）製，バイロン200 ） ２５部 カーボンブラック ８部 メチルエチルケトン（東洋インキ製造（株）製） ７０部 トルエン （東洋インキ製造（株）製） ３０部FIG. 3 is a cross-sectional view showing an example of a biodegradable hologram brittle seal provided with a printing layer according to the first and second inventions. The biodegradable hologram brittle seal of the present invention comprises a hologram forming layer 4 under a biodegradable plastic film (support) 1, a printing layer 8 under the hologram forming layer, a reflective thin film layer 5, and a brittle peeling. The layer 6 and the adhesive layer 7 are formed in this order. The print layer 8 is a pattern printed with characters and marks. As a printing method,
Besides gravure printing, there are methods such as offset printing and screen printing. The printing layer has a drying temperature of 100, for example, by an gravure printing method using an ink composition having the following composition ratio.
It is formed at a temperature of 1.0 ° C. and a thickness of 1.0 μm. Ink composition of printing layer Polyester resin (Toyobo Co., Ltd., Byron 200) 25 parts Carbon black 8 parts Methyl ethyl ketone (Toyo Ink Mfg. Co., Ltd.) 70 parts Toluene (Toyo Ink Mfg. Co., Ltd.) 30 parts
【００４３】本発明の生分解性ホログラム脆性シールに
おける反射性薄膜層５は、入射光線を反射する層であっ
て、厚さ１０〜１００ｎｍ、若しくはそれ以上のアルミ
ニウムが真空蒸着法により形成されている。なお、反射
性薄膜層としては、他に銀、金、硫化亜鉛、錫等の金属
又は金属化合物を使用することができる。The reflective thin film layer 5 in the biodegradable hologram brittle seal of the present invention is a layer for reflecting an incident light ray, and aluminum having a thickness of 10 to 100 nm or more is formed by a vacuum deposition method. . In addition, as the reflective thin film layer, a metal such as silver, gold, zinc sulfide, tin, or a metal compound can be used.
【００４４】また、反射性薄膜層５に、透明性を有する
反射性薄膜として、ホログラム形成層とは異なる屈折率
を有する透過性薄膜層を設けることが可能である。この
透過性薄膜層は、光透過性を示すとともにホログラム形
成層との屈折率差から界面での光反射を生じ、ホログラ
ム形成面のホログラム画像の再生に利用されている。例
えば、厚さ５０ｎｍのＺｎＳからなる薄膜層として真空
蒸着法等の蒸着により形成したものである。これによれ
ば、ホログラムの再生が被着体の下地のデザイン、模
様、文字等の画像や色等とともに目視することができ、
一層の装飾性の向上を図ることができる。なお、透過性
薄膜層としては、ホログラム形成層４（屈折率ｎ＝１．
３〜１．６）よりも屈折率の高いことが、装飾性の向上
に好ましい。Further, the reflective thin film layer 5 can be provided with a transparent thin film layer having a refractive index different from that of the hologram forming layer as a transparent reflective thin film. This transparent thin film layer exhibits optical transparency and causes light reflection at the interface due to the difference in refractive index from the hologram forming layer, and is used for reproducing a hologram image on the hologram forming surface. For example, a thin film layer made of ZnS having a thickness of 50 nm is formed by vapor deposition such as a vacuum vapor deposition method. According to this, the reproduction of the hologram can be visually checked along with the image, color, etc. of the design, pattern, characters, etc. of the substrate of the adherend,
The decorativeness can be further improved. As the transparent thin film layer, the hologram forming layer 4 (refractive index n = 1.
It is preferable that the refractive index is higher than 3 to 1.6) to improve the decorative property.
【００４５】このような透過性薄膜層を形成する方法と
しては、真空蒸着法の他にスパッタリング法、イオンプ
レーティング法等の成膜手段が適用可能であり、膜厚と
しては１０〜１０００ｎｍの範囲にあることが好まし
い。As a method of forming such a transparent thin film layer, a film forming means such as a sputtering method or an ion plating method can be applied in addition to the vacuum vapor deposition method, and the film thickness is in the range of 10 to 1000 nm. Is preferred.
【００４６】図４は、本発明の生分解性ホログラム脆性
シールの、応用例を示す断面図である。図４には、塩化
ビニル、アクリル、ポリカーボネート、ＡＢＳ等の基材
からなるプラスチックカードの表面に、ホログラム脆性
シールを貼着した後、強制的に剥離したときにホログラ
ム脆性シールが破壊されるようすを示したもので、これ
によれば脆性剥離層６の部分から剥離し、剥離面に剥離
されたホログラムの一部分が残り、再生不可能な状態に
なる。FIG. 4 is a sectional view showing an application example of the biodegradable hologram brittle seal of the present invention. FIG. 4 shows that the hologram brittle seal is destroyed when it is forcibly peeled off after the hologram brittle seal is adhered to the surface of a plastic card made of a substrate such as vinyl chloride, acrylic, polycarbonate, and ABS. According to this, according to this, it is peeled from the brittle peeling layer 6, and a part of the peeled hologram remains on the peeled surface, which makes it impossible to reproduce.
【００４７】＜分解テスト１＞以上の方法で製作した生
分解性ホログラム脆性シールを、電動式ゴミ処理機（日
立製作所製）に入れ定期的に分解状態を観察したとこ
ろ、３ヵ月後にシールが白濁し、形状は保持しているも
のの部分的な分解が見られた。６ヵ月経過後は、ほぼ完
全に分解し、形状の確認ができない状態になった。<Disassembly test 1> The biodegradable hologram brittle seal produced by the above method was put in an electric waste treatment machine (manufactured by Hitachi, Ltd.) and the disassembly state was observed periodically. The seal became cloudy after 3 months. However, although the shape was retained, partial decomposition was observed. After 6 months, it was almost completely decomposed and the shape could not be confirmed.
【００４８】＜分解テスト２＞比較例として、プラスチ
ックフィルム（ＰＥＴ）（東レ（株）製，「商品名ルミ
ラー」）を用いたホログラムシールは、実施例と同様の
方法で電動式ゴミ処理機に入れ、定期的に分解状態を観
察したところ、６ヵ月経過後、プラスチック基材は、多
少黄色に変色していたが形状は保持され、分解されてい
ないことが確認された。<Disassembly test 2> As a comparative example, a hologram sticker using a plastic film (PET) ("Lumirror", trade name, manufactured by Toray Industries, Inc.) was used in an electric waste treatment machine in the same manner as in the example. After putting it in and periodically observing the decomposition state, after 6 months, it was confirmed that the plastic base material was slightly discolored to yellow, but the shape was retained and not decomposed.
【００４９】＜評価＞比較例のホログラムシールと本発
明の生分解性ホログラム脆性シールとの比較結果によ
り、本発明の生分解性ホログラム脆性シールは優れた生
分解性持っていることが判明した。<Evaluation> As a result of comparison between the hologram seal of the comparative example and the biodegradable hologram brittle seal of the present invention, it was found that the biodegradable hologram brittle seal of the present invention has excellent biodegradability.
【００５０】[0050]
【発明の効果】以上に述べたように、本発明によれば生
分解性プラスチックを使用することにより、従来のホロ
グラムシールの偽造防止性、美観、高級性を有しなが
ら、シール使用後の廃棄処理が簡単にでき、地球環境に
悪影響を与えない優れたホログラム脆性シールを提供す
る。すなわち、生分解性ホログラム脆性シールの貼着
後、シールの表面から見ても部分的な脆性効果をもたら
す層を反射性薄膜層の下に設けることによって、その存
在の確認を非常に困難とすることができ、偽造防止性を
向上させることができる。また、反射性薄膜層をホログ
ラム形成層とは異なる屈折率を有する透過性薄膜層とす
ることにより、被着体の下地デザイン、模様、文字等の
画像や色等を損なうことなく、一層、装飾性の向上を図
ることができる。また、印刷層を設けることにより装飾
性を高めることができ、かつ剥離行為に対して、ホログ
ラムと同じく部分的に破壊されることにより、より一層
の偽造防止性、改ざん防止性を向上させることができ
る。また、本発明の生分解性ホログラム脆性シールは、
優れた透明性を有するフィルムを使用しているので、従
来品よりさらに鮮明な画像を見ることができる。As described above, according to the present invention, by using the biodegradable plastic, the conventional hologram seal has the anti-counterfeiting property, aesthetics, and high quality, but is discarded after the seal is used. (EN) Provided is an excellent hologram brittle seal which can be easily treated and does not adversely affect the global environment. That is, after sticking the biodegradable hologram brittle seal, by providing a layer below the reflective thin film layer that causes a partial brittle effect even when viewed from the surface of the seal, it becomes very difficult to confirm its existence. It is possible to improve the anti-counterfeit property. In addition, the reflective thin film layer is a transmissive thin film layer having a refractive index different from that of the hologram forming layer, so that the decorative layer can be further decorated without impairing the underlying design, pattern, characters and other images and colors of the adherend. It is possible to improve the sex. Further, by providing the printing layer, the decorative property can be enhanced, and the peeling action can be partially destroyed like the hologram, so that the anti-counterfeiting property and the tampering preventive property can be further improved. it can. Further, the biodegradable hologram brittle seal of the present invention,
Since a film having excellent transparency is used, a clearer image can be seen than conventional products.
【図１】本発明の一実施例を示す、生分解性ホログラム
脆性シールの断面図である。FIG. 1 is a cross-sectional view of a biodegradable hologram brittle seal showing an embodiment of the present invention.
【図２】本発明の他の実施例を示す生分解性ホログラム
脆性シールの断面図である。FIG. 2 is a sectional view of a biodegradable hologram brittle seal showing another embodiment of the present invention.
【図３】本発明の他の実施例を示す生分解性ホログラム
脆性シールの断面図である。FIG. 3 is a cross-sectional view of a biodegradable hologram brittle seal showing another embodiment of the present invention.
【図４】本発明の生分解性ホログラム脆性シールの、応
用例を示す断面図である。FIG. 4 is a cross-sectional view showing an application example of the biodegradable hologram brittle seal of the present invention.
１ …生分解性プラスチック ２ …剥離層 ３ …ホログラムパターン ４ …ホログラム形成層 ５ …反射性薄膜層（光透過性薄膜層） ６ …脆性剥離層 ７ …接着層 ８ …印刷層 1 ... Biodegradable plastic 2 ... Release layer 3 ... Hologram pattern 4 ... Hologram forming layer 5 ... Reflective thin film layer (light transmissive thin film layer) 6 ... Brittle release layer 7 ... Adhesive layer 8 ... Printing layer
Claims (8)
が、10,000〜100,000 であるポリ乳酸とオキシカルボン
酸のコポリマーを主成分とする) フィルム（支持体）１
上に、少なくとも剥離層２、ホログラムパターン３を有
する透明なホログラム形成層４と反射性薄膜層５と、前
記反射性薄膜層の少なくとも一部を覆う脆性剥離層６、
接着層７とを順次設けたことを特徴とする生分解性ホロ
グラム脆性シール。1. A film (support) 1 which is transparent and biodegradable (having a polylactic acid / oxycarboxylic acid copolymer having a number average molecular weight of 10,000 to 100,000 as a main component).
A transparent hologram forming layer 4 having at least a peeling layer 2, a hologram pattern 3, a reflective thin film layer 5, and a brittle peeling layer 6 covering at least a part of the reflective thin film layer,
A biodegradable hologram brittle seal, which is provided with an adhesive layer 7 in order.
してなる透明で生分解性を有するポリ乳酸フィルム（支
持体）１上に、反射性薄膜層５と、前記反射性薄膜層の
少なくとも一部を覆う脆性剥離層６、接着層７とを設け
たことを特徴とする生分解性ホログラム脆性シール。2. A reflective thin film layer 5 and at least the reflective thin film layer on a transparent and biodegradable polylactic acid film (support) 1 formed by forming a hologram pattern 3 on one surface. A biodegradable hologram brittle seal comprising a brittle peeling layer 6 and an adhesive layer 7 which cover a part of the biodegradable hologram brittle seal.
ホログラム形成層４は、溶剤可溶性生分解性樹脂からな
ることを特徴とする請求項１に記載の生分解性ホログラ
ム脆性シール。3. The biodegradable hologram brittle seal according to claim 1, wherein the transparent hologram forming layer 4 having the hologram pattern 3 is made of a solvent-soluble biodegradable resin.
ルム１のいずれか一方の面に、印刷層８を設けたことを
特徴とする請求項１又は請求項２に記載の生分解性ホロ
グラム脆性シール。4. The biodegradable hologram according to claim 1 or 2, wherein a printing layer 8 is provided on one surface of the transparent polylactic acid film 1 having biodegradability. Brittle seal.
面に、印刷層８を設けたことを特徴とする請求項１に記
載の生分解性ホログラム脆性シール。5. The biodegradable hologram brittle seal according to claim 1, wherein a printing layer 8 is provided on one surface of the hologram forming layer 4.
あることを特徴とする請求項１又は請求項２に記載の生
分解性ホログラム脆性シール。6. The biodegradable hologram brittle seal according to claim 1 or 2, wherein the reflective thin film layer 5 is a light impermeable thin film.
成層４と異なる屈折率を有する光透過性薄膜であること
を特徴とする請求項１に記載の生分解性ホログラム脆性
シール。7. The biodegradable hologram brittle seal according to claim 1, wherein the reflective thin film layer 5 is a light transmissive thin film having a refractive index different from that of the hologram forming layer 4.
するプラスチックフィルム（支持体）１と異なる屈折率
を有する光透過性薄膜であることを特徴とする請求項２
に記載の生分解性ホログラム脆性シール。8. The reflective thin film layer 5 is a light transmissive thin film having a refractive index different from that of the biodegradable plastic film (support) 1.
The biodegradable hologram brittle seal described in.