JPH0970809A - Form made of composite molded article and its manufacture - Google Patents
Form made of composite molded article and its manufactureInfo
- Publication number
- JPH0970809A JPH0970809A JP7228037A JP22803795A JPH0970809A JP H0970809 A JPH0970809 A JP H0970809A JP 7228037 A JP7228037 A JP 7228037A JP 22803795 A JP22803795 A JP 22803795A JP H0970809 A JPH0970809 A JP H0970809A
- Authority
- JP
- Japan
- Prior art keywords
- mold
- particles
- resin
- plate
- formwork
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】Detailed Description of the Invention
【０００１】[0001]
【発明の属する技術分野】本発明は、新規な型枠に関す
るものである。さらに詳細には、繊維強化樹脂からなる
スキン層とシンタクチックフォームコアからなる多孔質
コア層から構成されるサンドイッチ構造の複合成形品か
らなる、軽量かつ高剛性を有する型枠であって、従来の
木製型枠に比較して転用回数を格段と向上させた新規な
型枠に関するものである。TECHNICAL FIELD The present invention relates to a new form. More specifically, there is provided a lightweight and highly rigid mold frame composed of a composite molded article having a sandwich structure composed of a skin layer made of a fiber reinforced resin and a porous core layer made of a syntactic foam core. The present invention relates to a new formwork in which the number of diversions is remarkably improved as compared with a wooden formwork.
【０００２】[0002]
【従来技術】従来、サイディングボードと称されるコン
クリート板を成形する際や、あるいは建築現場などでコ
ンクリートを打設する際の型枠として最も一般的に使用
されているものは木製型枠である。しかしながら、これ
ら木製型枠は、材料となる木材が、地球規模での熱帯雨
林保護の動きもあり、最近では入手が困難になり始めて
いる。しかも、自然保護の見地から、政府もしくは自治
体がその使用を制限する動きが出ており、将来の材料供
給が懸念されている。さらに、木製の型枠は２〜３回か
ら１０回の使用で表面状態が悪化し、使い捨てられてい
るのが現状である。しかも、木製の型枠は、吸水によっ
て寸法変化（膨脹）や重量増大が生じるため作業性にも
問題がある。2. Description of the Related Art Conventionally, a wooden formwork is most commonly used as a formwork for forming a concrete plate called a siding board or for placing concrete at a construction site. . However, these wooden forms have recently become difficult to obtain because of the movement of protecting the tropical rainforest on a global scale. Moreover, from the standpoint of nature conservation, the government or local governments have started to restrict their use, and there is concern about future material supply. Furthermore, the wooden formwork has deteriorated in surface condition after being used 2-3 times to 10 times, and is currently in a disposable state. In addition, the wooden formwork has a problem in workability because dimensional change (expansion) and weight increase occur due to water absorption.
【０００３】このように、資源問題のみならず、型枠を
使用する建築現場での作業効率化および経済性改善の一
環としても、木製型枠に代わる新規な型枠材料が強く望
まれている。As described above, a new form material that replaces the wooden form is strongly desired not only as a resource problem but also as a part of improving work efficiency and improving economical efficiency at a construction site where the form is used. .
【０００４】このため、木材に代わる新たな材料からな
る型枠の提案がなされつつある。たとえば、特公平７−
２４８２１号には、アルミニウム板をベースとし表層に
熱可塑性樹脂層を貼り合わせた型枠が提案されている。
しかしながら、この提案による型枠は、多層構造にする
ための工程が多いため、高価につくばかりでなく、軽量
化も達成されていない。For this reason, proposals for a mold made of a new material replacing wood are being made. For example,
No. 24821 proposes a mold having an aluminum plate as a base and a thermoplastic resin layer bonded to the surface layer.
However, since the formwork proposed by this proposal has many steps for forming a multi-layer structure, not only is it expensive but also weight reduction has not been achieved.
【０００５】一方、軽量化を狙っての発泡ポリウレタン
や発泡ポリプロピレン等の使用も提案されている。たと
えば、特公平６−３４４３２２号には、ポリプロピレン
等の熱可塑性発泡体を芯材にしてその両面に表面材を貼
り合わせた型枠が示されている。しかしながら、ここに
示されている熱可塑性ポリマーの発泡体は、型枠使用状
態での荷重下での剛性および強度が不足し、挫屈や破壊
を起こし易いという欠点をもっている。On the other hand, it has been proposed to use foamed polyurethane or polypropylene for the purpose of weight reduction. For example, Japanese Examined Patent Publication No. 6-344322 discloses a mold in which a thermoplastic foam such as polypropylene is used as a core material and surface materials are attached to both surfaces thereof. However, the thermoplastic polymer foams shown here have the drawbacks that they lack rigidity and strength under load in the state of use of the mold, and are apt to buckle or break.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、従来の木製
型枠を代替しつつ、経済性に優れ、使用に際しては極め
て軽量でかつ剛性や強度に優れ、しかも、何回もの繰り
返し使用に耐え得る新規な型枠を提供することを目的と
するものである。DISCLOSURE OF THE INVENTION The present invention is an alternative to the conventional wooden formwork, is economical, is extremely lightweight in use, has excellent rigidity and strength, and can withstand repeated use many times. It is intended to provide a new form to be obtained.
【０００７】[0007]
【課題を解決するための手段】本発明者らは、上記の課
題を解決すべく鋭意研究の結果、上下の繊維強化樹脂
（ＦＲＰ）からなる緻密なスキン層の間に中空の軽量粒
子を含むシンタクチックフォームからなる多孔質コア層
を挟み込んだサンドイッチ構造に一体成形された複合成
形品（たとえば、特公平７−１２６１３号等に記載のも
の）からなる型枠は、従来の木製や合成樹脂製の型枠に
見られた諸問題を解消することができ、極めて有用性が
大きい型枠を提供することを見い出だし、本発明に到達
した。As a result of intensive studies to solve the above problems, the inventors of the present invention include hollow lightweight particles between the upper and lower dense skin layers of fiber reinforced resin (FRP). A mold made of a composite molded product integrally formed in a sandwich structure in which a porous core layer made of syntactic foam is sandwiched (for example, described in Japanese Patent Publication No. 7-12613) is made of conventional wood or synthetic resin. The inventors have found that the problems found in the molds can be solved and that the molds are extremely useful, and have reached the present invention.
【０００８】すなわち、本発明に係る型枠は、少なくと
も板状部は、上下の繊維強化樹脂からなる緻密なスキン
層の間に軽量充填粒子と硬化樹脂とからなる多孔質コア
層を有するサンドイッチ構造体であって、かつ、型枠全
体が一体化した複合成形品で構成されていることを特徴
とするものであり、さらには、少なくとも板状部は、上
下の繊維強化樹脂からなる緻密なスキン層、軽量充填粒
子と硬化樹脂とからなる多孔質コア層およびこれら各層
の間に配置された分離膜で構成されたサンドイッチ構造
体であって、かつ型枠全体が一体化した複合成形品で構
成されていることを特徴とするものである。That is, in the mold according to the present invention, at least the plate-like portion has a sandwich structure having a porous core layer made of light weight filling particles and a cured resin between upper and lower dense skin layers made of fiber reinforced resin. It is characterized in that it is a body and is composed of a composite molded product in which the entire form is integrated, and further, at least the plate-like portion is a dense skin made of upper and lower fiber reinforced resin. A sandwich structure composed of a layer, a porous core layer composed of lightweight filling particles and a cured resin, and a separation membrane arranged between these layers, and composed of a composite molded article in which the entire formwork is integrated. It is characterized by being.
【０００９】本発明の型枠は、上述のごとく、実質的に
その全部または大部分を占める平坦な板状部が、強化用
繊維質シートと硬化樹脂からなる繊維強化樹脂（ＦＲ
Ｐ）の緻密なスキン層の間に、必要に応じ分離膜を介し
て、軽量充填粒子と硬化樹脂とからなる多孔質コア（シ
ンタクチックフォーム・コア）層を挟み込むよう一体成
形したサンドイッチ構造体であることを最大の特徴とす
る。As described above, the mold of the present invention has a fiber-reinforced resin (FR) in which the flat plate-like portion occupying substantially all or most of the frame is composed of a reinforcing fibrous sheet and a cured resin.
A sandwich structure in which a porous core (syntactic foam core) layer composed of lightweight filling particles and a cured resin is sandwiched between the dense skin layers of P) via a separation membrane if necessary. The greatest feature is that there is.
【００１０】そして、かかる本発明の型枠は、その用途
に応じ、上記板状部の周囲に、肉厚部を設けてもよく、
裏面に補強用のリブを設けてもよく、また、多孔質内に
局所的に補強材を配置してもよい。In the mold of the present invention, a thick portion may be provided around the plate-like portion depending on its use,
A reinforcing rib may be provided on the back surface, or a reinforcing material may be locally arranged in the porous material.
【００１１】このような構造の本発明の型枠は、基本的
に、（ａ）硬化性樹脂と平均粒径が０．０１〜２ｍｍの
軽量充填粒子（および／またはその前駆体粒子）とを混
合して、含粒子樹脂組成物を調製し、（ｂ）２つの強化
用繊維質シートの間に上記含粒子樹脂組成物を供給し
て、積層体とし、（ｃ）次いで、上記積層体を、型枠を
成形するための型内で加熱し、硬化性樹脂を硬化せしめ
て、複合成形品からなる型枠を得る方法により製造され
る。The mold of the present invention having such a structure basically comprises (a) a curable resin and lightweight filling particles (and / or precursor particles thereof) having an average particle diameter of 0.01 to 2 mm. By mixing, a particle-containing resin composition is prepared, (b) the particle-containing resin composition is supplied between two reinforcing fibrous sheets to form a laminate, and (c) the laminate is then formed. The mold is manufactured by heating in a mold for molding the mold to cure the curable resin to obtain a mold composed of a composite molded product.
【００１２】本発明の型枠において、スキン層に使用さ
れる強化用繊維質シート素材の具体例としては、ガラス
繊維、炭素繊維、シリコンカーバイド繊維、金属繊維、
アラミド繊維、ポリアリレート繊維、高強度ポリエチレ
ン繊維またはこれらの２種以上の混合物をあげることが
できる。また、これらの繊維の他に、ポリエステル繊
維、ポリビニルアルコール繊維、レーヨン繊維、アセテ
ート繊維、天然繊維あるいは鉱物繊維等も使用すること
ができる。なかでも、ガラス繊維、炭素繊維、パラ系ア
ラミド繊維等のような高強力、高剛性（高モジュラス）
繊維を用いることが好ましい。In the formwork of the present invention, specific examples of the reinforcing fibrous sheet material used for the skin layer are glass fiber, carbon fiber, silicon carbide fiber, metal fiber,
Examples include aramid fiber, polyarylate fiber, high-strength polyethylene fiber, or a mixture of two or more thereof. In addition to these fibers, polyester fibers, polyvinyl alcohol fibers, rayon fibers, acetate fibers, natural fibers or mineral fibers can also be used. Among them, high strength and high rigidity (high modulus) such as glass fiber, carbon fiber, para-aramid fiber, etc.
It is preferable to use fibers.
【００１３】強化用繊維質シートの形態としては、各種
織物（平織、綾織、スダレ織等）、編物、不織布、マッ
ト、紙、一方向に引き揃え層状に集合させたロービング
等のシート状物にしたものが使用される。これらは単独
で用いてもよいし、２種以上のシート物を重ねて用いて
もよい。Examples of the form of the reinforcing fibrous sheet include various woven fabrics (plain weave, twill weave, woven weave, etc.), knitted fabrics, non-woven fabrics, mats, papers, and sheet-like products such as rovings gathered in one direction in layers. The one used is used. These may be used alone or in combination of two or more kinds of sheet materials.
【００１４】一方、多孔質コア層に含まれる軽量充填粒
子は、（ア）成形時に熱膨脹させた樹脂粒子、（イ）圧
縮性軽量粒子、および（ウ）剛性軽量粒子からなる群か
ら選ばれた少なくとも１種の粒子であり、好ましくは、
比重が０．０５〜０．７０で平均粒径が０．０１〜２ｍ
ｍ（ただし、上記（ア）の樹脂粒子の場合は膨脹後の
値）であるモノセルまたはマルチセルの中空粒子が使用
される。On the other hand, the lightweight filler particles contained in the porous core layer are selected from the group consisting of (a) resin particles thermally expanded during molding, (a) compressible lightweight particles, and (c) rigid lightweight particles. At least one kind of particles, preferably
Specific gravity is 0.05-0.70 and average particle size is 0.01-2m
m (however, in the case of the resin particles of the above (a), a value after expansion) mono-cell or multi-cell hollow particles are used.
【００１５】この軽量充填粒子として、上記（ア）の樹
脂粒子や（イ）の圧縮性粒子を用いるときは、軽量充填
粒子の５０重量％以上が剛性軽量粒子となるよう、剛性
軽量粒子を配合することが強靭な型枠を形成する上で好
ましい。When the resin particles of (a) or the compressible particles of (ii) are used as the light weight filling particles, the rigid light weight particles are blended so that 50% by weight or more of the light weight filling particles become the rigid light weight particles. It is preferable to do so in order to form a strong mold.
【００１６】上記（ア）の熱膨脹した発泡樹脂粒子は、
成形前には加熱により体積膨脹する物質を内包する熱膨
脹性樹脂粒子であって未だ軽量性を有するものではない
が、成形段階で硬化性樹脂と混合した状態で加熱される
と大幅な体積膨脹を起こして軽量な中空粒子となり、引
き続いて起こる硬化性樹脂の硬化によって、軽量な多孔
質構造を有するシンタクチックフォーム構造を形成する
特性を持つ。このような体積膨脹の倍率は、加熱条件は
もとより、該樹脂粒子を構成するポリマー素材の種類や
粒子の膜厚、該粒子に内包されて加熱により著しい体積
変化を生じる物質にも依存するが、成形時の加熱によっ
て少なくとも約１０％以上、好ましくは約２０％以上、
通常は２０％〜７０倍の体積膨脹を起こすものである。
かかる熱膨脹性樹脂粒子の大きさは、体積膨脹前の平均
粒径が約０．００１〜２ｍｍの範囲が好適である。The heat-expanded expanded resin particles of (a) above are
It is a heat-expandable resin particle that contains a substance that expands in volume by heating before molding, and does not yet have light weight, but when heated in the state of being mixed with a curable resin during the molding stage, it undergoes a significant volume expansion. It has a property of forming a lightweight hollow particle and subsequently forming a lightweight syntactic foam structure having a porous structure by curing of the curable resin. Such a volume expansion ratio depends not only on heating conditions, but also on the type of polymer material constituting the resin particles, the film thickness of the particles, and the substance contained in the particles and causing a remarkable volume change by heating, At least about 10% or more, preferably about 20% or more by heating during molding,
Usually, it causes a volume expansion of 20% to 70 times.
The size of such heat-expandable resin particles is preferably such that the average particle size before volume expansion is about 0.001 to 2 mm.
【００１７】上記熱膨脹性樹脂粒子の例としては、ポリ
アクリロニトリル系共重合体、ポリメタクリロニトリル
系共重合体、ポリ塩化ビニリデン系共重合体、ポリスチ
レンまたはポリスチレン系共重合体、ポリオレフィン、
ポリフェニレンオキサイド系共重合体等からなる粒子
で、その内部に熱膨脹性物質を含有する微小な樹脂粒子
があげられ、とくに加熱により気体なって体積膨脹する
低沸点炭化水素類を内包するものが好ましい。かかる熱
膨脹性樹脂粒子の具体例としては、松本油脂製薬（株）
製「マツモトマイクロスフェアー」、ノーベル社製「エ
クスパンセル」、積水化学工業（株）製「エスレンビー
ズ」等をあげることができる。Examples of the heat-expandable resin particles include polyacrylonitrile-based copolymers, polymethacrylonitrile-based copolymers, polyvinylidene chloride-based copolymers, polystyrene or polystyrene-based copolymers, polyolefins,
Particles made of a polyphenylene oxide-based copolymer and the like include fine resin particles containing a heat-expandable substance therein, and particularly preferably those containing low-boiling point hydrocarbons which become a gas and expand in volume by heating. Specific examples of such heat-expandable resin particles include Matsumoto Yushi-Seiyaku Co., Ltd.
Examples include "Matsumoto Microsphere" manufactured by Nobel, "Expansel" manufactured by Nobel, "Eslen beads" manufactured by Sekisui Chemical Co., Ltd., and the like.
【００１８】また、上記（ロ）の圧縮性粒子は、加圧す
ることにより圧縮変形（弾性変形または塑性変形）して
体積の約１〜７０％（好ましくは５〜５０％程度）減少
する低比重の微小中空粒子であって、その代表例は、上
記熱膨脹性樹脂粒子を予め空気中または不活性ガス中で
加熱、膨脹させた中空軽量粒子、その既膨脹中空粒子の
表面に炭酸カルシウムや酸化チタンのような剛性成分を
薄く被覆した中空軽量粒子、あるいは多孔質ポリプロピ
レン粒子等である。Further, the compressive particles (b) mentioned above have a low specific gravity which is reduced by about 1 to 70% (preferably about 5 to 50%) of the volume by being compressed and deformed (elastically or plastically deformed) by applying pressure. The hollow hollow particles are, for example, hollow lightweight particles obtained by previously heating and expanding the heat-expandable resin particles in air or an inert gas, and calcium carbonate or titanium oxide on the surface of the already expanded hollow particles. Hollow light weight particles thinly coated with such a rigid component, or porous polypropylene particles.
【００１９】これらの圧縮性粒子は、再加熱しても、実
質的には体積膨脹しない非膨脹性粒子の１種であるが、
成形時の加圧により圧縮変形する点において従来のシン
タクチックフォーム構造に使用されているガラスバルー
ンとは異なる。These compressible particles are one kind of non-expandable particles that do not substantially expand in volume even when reheated.
It is different from the glass balloon used in the conventional syntactic foam structure in that it is compressed and deformed by the pressure applied during molding.
【００２０】かかる圧縮性粒子の具体例としては、たと
えば、上記の松本油脂製薬（株）製「マツモトマイクロ
スフェアー」、ノーベル社製「エクスパンセル」、積水
化学工業（株）製「エスレンビーズ」等の熱膨脹性粒子
を、蒸気加熱あるいは空気中または不活性ガス中で加熱
して膨脹させたものがあげられる。これらの圧縮性粒子
の大きさは、平均粒径で０．０１〜２ｍｍ、好ましくは
０．０５〜２ｍｍの範囲であることが好適である。Specific examples of such compressible particles include, for example, "Matsumoto Microsphere" manufactured by Matsumoto Yushi-Seiyaku Co., Ltd., "Expansel" manufactured by Nobel, and "Eslen beads" manufactured by Sekisui Chemical Co., Ltd. Heat-expandable particles such as those obtained by heating with steam or heating in air or an inert gas to be expanded. It is suitable that the size of these compressible particles is in the range of 0.01 to 2 mm, preferably 0.05 to 2 mm in terms of average particle size.
【００２１】上記（ハ）の剛性軽量粒子は、加圧状態で
も実質的に変形し難い高剛性の微小中空粒子であり、そ
の代表例は、ガラスバルーン、シラスバルーン、シリカ
バルーン等の名称で知られる無機中空微粒子である。か
かる剛性粒子の大きさは、平均粒径で０．０１〜２ｍ
ｍ、とくに０．０５〜２ｍｍの範囲のものが好適に使用
される。The rigid lightweight particles of the above (c) are minute hollow particles of high rigidity which are substantially hard to be deformed even under pressure, and typical examples thereof are known by the names such as glass balloons, shirasu balloons and silica balloons. These are inorganic hollow fine particles. The size of the rigid particles is 0.01 to 2 m in average particle size.
m, particularly in the range of 0.05 to 2 mm is preferably used.
【００２２】本発明において型枠を構成する複合成形品
のスキン層およびコア層に含まれ、かつこれらの層を形
成する樹脂は、硬化性樹脂であり、該樹脂は成形時の硬
化によってスキン層およびコア層を一体に形成する。In the present invention, the resin contained in the skin layer and core layer of the composite molded article constituting the mold and forming these layers is a curable resin, and the resin is a skin layer formed by curing during molding. And the core layer is integrally formed.
【００２３】ここで使用する硬化性樹脂は、通常の複合
材料の成形に用いられる熱硬化性樹脂であり、通常は常
温で液状のものが好ましく用いられるが、該硬化性樹脂
またはその混合物が、成形に際しての加熱状態において
液状となるものであれば、常温で固体状あるいは半固体
状であっても使用することができる。かかる硬化性樹脂
の具体例としては、エポキシ樹脂、不飽和ポリエステル
樹脂、ビニルエステル樹脂、アクリルウレタン樹脂、フ
ェノール樹脂、ポリウレタン樹脂、アクリル樹脂、ジシ
クロペンタジエン樹脂、石油樹脂等をあげることができ
る。なかでも、エポキシ樹脂、不飽和ポリエステル樹
脂、ビニルエステル樹脂、フェノール樹脂等が好ましい
硬化性樹脂である。この硬化性樹脂は、通常、それぞれ
必要な硬化剤または開始剤、硬化促進剤、稀釈剤等と共
に使用される。The curable resin used here is a thermosetting resin which is usually used for molding composite materials. Usually, a liquid resin at room temperature is preferably used. The curable resin or a mixture thereof is preferably used. It can be used even if it is in a solid state or a semi-solid state at room temperature as long as it is in a liquid state in a heated state during molding. Specific examples of such curable resin include epoxy resin, unsaturated polyester resin, vinyl ester resin, acrylic urethane resin, phenol resin, polyurethane resin, acrylic resin, dicyclopentadiene resin, petroleum resin and the like. Among them, epoxy resin, unsaturated polyester resin, vinyl ester resin, phenol resin and the like are preferable curable resins. This curable resin is usually used together with a necessary curing agent or initiator, curing accelerator, diluent and the like.
【００２４】本発明においては、上述のように多孔質コ
ア（シンッタクチックフォーム・コア）層の構成成分と
して微小な軽量充填粒子を使用するため、成形の途中段
階でこの軽量充填粒子が硬化性樹脂と共にスキン層を形
成する強化用繊維質シート中に浸透し、該強化用繊維質
シートの目開きが大きい場合には（とくに熱膨脹性粒子
を用いる場合には）、軽量充填粒子が成形品の表面にま
で滲出することもあり得る。このような場合には、上下
の強化用繊維質シートの内側に、それぞれ、含粒子樹脂
組成物の層と接するごとく分離膜を配置することが好ま
しい。In the present invention, as described above, fine light weight filler particles are used as a constituent component of the porous core (syntactic foam core) layer, and therefore, the light weight filler particles are cured during the molding process. When the reinforcing fibrous sheet that forms a skin layer together with the heat-resistant resin penetrates and the opening of the reinforcing fibrous sheet is large (particularly when heat-expandable particles are used), the light weight filling particles are molded articles. It can also exude to the surface of. In such a case, it is preferable to dispose separation membranes inside the upper and lower reinforcing fibrous sheets so as to contact the layers of the particle-containing resin composition, respectively.
【００２５】該分離膜は、硬化性樹脂は通すが軽量充填
粒子の通過は阻止する性質をもつ薄いシート状物であ
り、この分離膜を強化用繊維質シートと含粒子樹脂組成
物層との間に介在させて成形することにより、成形の際
における上述のような軽量充填粒子の表面層への滲出を
防ぐことができる。The separation membrane is a thin sheet having the property of allowing the curable resin to pass through but preventing the lightweight filling particles from passing through. The separation membrane is composed of a reinforcing fibrous sheet and a particle-containing resin composition layer. By interposing between them, it is possible to prevent the above-mentioned lightweight filler particles from leaching to the surface layer during the molding.
【００２６】かかる分離膜としては、目開きの小さい繊
維質シートおよび／または多孔質シートが使用される。
分離膜用の繊維質シートとしては、たとえば、各種の天
然繊維、合成繊維、無機繊維等からなる織物、編物、組
物、不織布、紙等が使用される。多孔質シートとは、連
通気孔を有するシートまたはフィルムであって、ポリウ
レタン、ポリプロピレン、ポリスチレン等のフォームシ
ートや延伸、抽出または凝固法等によって製造されるポ
リエチレン、ポリプロピレンあるいはポリスルホン等の
多孔膜が用いられる。As the separation membrane, a fibrous sheet and / or a porous sheet having a small opening is used.
As the fibrous sheet for the separation membrane, for example, woven fabrics, knitted fabrics, braids, non-woven fabrics, papers and the like made of various natural fibers, synthetic fibers, inorganic fibers and the like are used. The porous sheet is a sheet or film having continuous ventilation holes, and a foam sheet of polyurethane, polypropylene, polystyrene or the like, or a porous membrane such as polyethylene, polypropylene or polysulfone produced by a stretching, extraction or coagulation method or the like is used. .
【００２７】これら分離膜の目開きは、軽量充填粒子の
大きさに応じて適宜選択される。また、分離膜の材料と
しては、容易に成形品の形状に合わせ得るように伸縮性
を有するものを選択することもできる。分離膜は、その
一部が硬化性樹脂を通さない材料で構成されているもの
であってもよい。たとえば、分離機能を有する材料から
なる部分とそれとは異なった機能を有する材料からなる
部分とを繋ぎ合わせたもの、分離機能を有するシート状
物の一部を予め樹脂等でその目開きを封止処理したも
の、繊維質シートがポリプロピレン繊維シートであって
その融着可能な部分が加熱処理によって部分的に融着し
て一部の目開きを潰したもの、分離機能を有する材料の
一部に非多孔性フィルムを貼りつけたもの等でもよい。The openings of these separation membranes are appropriately selected according to the size of the lightweight filling particles. Further, as the material of the separation membrane, a material having elasticity can be selected so that it can be easily matched with the shape of the molded product. A part of the separation membrane may be made of a material that does not pass the curable resin. For example, one in which a part made of a material having a separating function and a part made of a material having a different function are connected to each other, or a part of a sheet material having a separating function is sealed in advance with a resin or the like to open its openings. Treated product, fibrous sheet is polypropylene fiber sheet and its fusible part is partially fused by heat treatment to crush some of the openings, and part of the material with separation function It may be a non-porous film attached.
【００２８】なお、分離膜として、それ自体が強化材と
しての機能を有する、ガラス繊維、炭素繊維、アラミド
繊維等からなる目開きの小さい繊維質シートを用いるこ
ともできる。この場合には、この繊維質シートで強化用
繊維質シートと分離膜とを兼用することができる。As the separation membrane, it is also possible to use a fibrous sheet having a small opening made of glass fiber, carbon fiber, aramid fiber or the like, which itself has a function as a reinforcing material. In this case, this fibrous sheet can serve as both the reinforcing fibrous sheet and the separation membrane.
【００２９】ただし、強化用繊維質シートと分離膜とを
別個に配置した方が、強化用繊維質シートの目開きを自
由に選択することができ、たとえば、一方向繊維配列プ
リプレグや三次元織編物のプリフォーム等も使用するこ
とができ、型枠表面に要求される外観、特性に応じた材
料を任意に選ぶことができるので好ましい。However, when the reinforcing fibrous sheet and the separation membrane are separately arranged, the openings of the reinforcing fibrous sheet can be freely selected. For example, a unidirectional fiber array prepreg or a three-dimensional weave is available. A knit preform or the like can also be used, and a material suitable for the appearance and characteristics required for the surface of the mold can be arbitrarily selected, which is preferable.
【００３０】本発明者らの研究によれば、たとえば「ユ
ニセル」等の商品名で市販されている目開きの小さい長
繊維不織布が分離機能や取扱い性等多くの面で優れてお
り、分離膜としてとくに好適であることが認められた。According to the research conducted by the present inventors, for example, a long-fiber nonwoven fabric having a small opening, which is marketed under the trade name of “UNICEL”, is excellent in many aspects such as separation function and handleability. Was found to be particularly suitable as
【００３１】さらに、型枠の外観や意匠性あるいは離型
性等、表面機能の向上、改善を目的として、たとえば表
面機能付与用のフィルム、金属箔、織物、不織布、紙、
人工皮革等のシート状物を、スキン層の表面または内部
に配置し、一体化した状態で成形することが可能であ
る。Further, for the purpose of improving and improving the surface function such as the appearance, designability or releasability of the mold, for example, a film for imparting a surface function, a metal foil, a woven fabric, a non-woven fabric, a paper,
It is possible to arrange a sheet-like material such as artificial leather on the surface or inside of the skin layer and mold it in an integrated state.
【００３２】一方、本発明の型枠の製造において使用す
る軽量充填粒子（および／またはその前駆体粒子）は、
上述のように、熱膨脹性樹脂粒子、圧縮性粒子および剛
性軽量粒子からなる群より選ばれた少なくとも１種の粒
子である。すなわち、これらの粒子はそれぞれ単独で使
用してもよく、熱膨脹性樹脂粒子と剛性軽量粒子との混
合物あるいは圧縮性粒子と剛性軽量粒子との混合物の形
で使用することもできるが、すでに述べたように、コア
層に剛性軽量粒子が存在するのが好ましく、該粒子単独
または剛性軽量粒子５０重量％以上の混合粒子の使用が
好ましい。On the other hand, the lightweight filler particles (and / or their precursor particles) used in the production of the mold of the present invention are:
As described above, it is at least one kind of particles selected from the group consisting of heat-expandable resin particles, compressible particles and rigid lightweight particles. That is, these particles may be used alone, or may be used in the form of a mixture of heat-expandable resin particles and rigid lightweight particles or a mixture of compressible particles and rigid lightweight particles. Thus, it is preferable that rigid lightweight particles are present in the core layer, and it is preferable to use the particles alone or mixed particles of 50% by weight or more of rigid lightweight particles.
【００３３】本発明の型枠の製造における軽量充填粒子
の使用量は、複合成形品である型枠のコア層における該
軽量充填粒子（熱膨脹性樹脂粒子の場合は膨脹後）の合
計量が、該コア層における硬化性樹脂と軽量充填粒子の
合計量との和に対して、２０〜８０体積％の範囲となる
量使用することが好適である。軽量充填粒子の使用量が
２０体積％より少ないと、本発明による型枠の比重を軽
くする効果が小さくなり、好ましくない。一方、８０体
積％を越える場合は、より軽量化が達成されるものの、
コア層における硬化性樹脂の充填状況が良好でなくな
り、亀裂を起こす等の問題が生じ、型枠としての剛性や
強度の低下を招くことがあるので好ましくない。好適な
特性の型枠を得るための軽量充填粒子のより好ましい使
用量は３０〜７０体積％の範囲である。The amount of the lightweight filling particles used in the production of the mold of the present invention is the total amount of the lightweight filling particles (after expansion in the case of heat-expandable resin particles) in the core layer of the mold which is a composite molded article, It is preferable to use an amount in the range of 20 to 80% by volume with respect to the sum of the curable resin in the core layer and the total amount of the lightweight filling particles. If the amount of the lightweight filling particles used is less than 20% by volume, the effect of reducing the specific gravity of the mold according to the present invention becomes small, which is not preferable. On the other hand, when the content exceeds 80% by volume, the weight reduction is achieved, but
The curable resin in the core layer may not be filled well, causing problems such as cracking, which may lead to a decrease in rigidity and strength of the mold, which is not preferable. A more preferable use amount of the lightweight filling particles for obtaining a mold having suitable properties is in the range of 30 to 70% by volume.
【００３４】本発明の型枠の製造においては、上記の軽
量充填粒子および硬化性樹脂とともに、成形品の機械的
特性、難燃性、耐熱性あるいは成形性を向上させるた
め、必要に応じ、各種添加剤を併用することも可能であ
る。これらの添加剤の例としては、ミルドガラス、クレ
イ、カオリン、マイカ、炭酸カルシウム、硫酸カルシウ
ム、シリカ、アルミナ、水酸化アルミニウム水和物、各
種難燃剤、各種顔料、紫外線吸収剤、内部離型剤等があ
げられる。また、これら添加剤の他の例として、使用済
みの樹脂成形品やＦＲＰからの微粉砕物をあげることが
できる。In the production of the mold of the present invention, in addition to the above-mentioned light weight filling particles and the curable resin, various kinds are added as necessary in order to improve the mechanical properties, flame retardancy, heat resistance or moldability of the molded product. It is also possible to use additives in combination. Examples of these additives include milled glass, clay, kaolin, mica, calcium carbonate, calcium sulfate, silica, alumina, aluminum hydroxide hydrate, various flame retardants, various pigments, ultraviolet absorbers, internal release agents. Etc. Other examples of these additives include used resin moldings and finely pulverized products from FRP.
【００３５】このような材料を用いて、本発明の複合成
形品からなる型枠を製造する第１の方法は、軽量充填粒
子としてその前駆体粒子である熱膨脹性粒子（またはこ
れと剛性軽量粒子との混合物）を使用する方法であり、
（ａ）硬化性樹脂と上記粒子とを混合して含粒子樹脂組
成物を調製し、（ｂ）所定の寸法にカットされた上下２
つの強化用繊維質シート（および必要に応じて２つの分
離膜）を配置し、この間に上記含粒子樹脂組成をほぼ均
一な厚みの層状になるように供給して、強化用繊維質シ
ート／（分離膜）／含粒子樹脂組成物／（分離膜）／強
化用繊維質シートからなる積層体を形成し、（ｃ）この
積層体を所定の型枠成形用の型内にセットし、（ｄ）型
を閉じた後、加熱して上記含粒子樹脂組成物中の熱膨脹
性粒子を膨脹させ、それにより型内に生じる圧力を利用
して硬化性樹脂を上下の強化用繊維質シートへ浸透さ
せ、その一部を表面まで至らしめ、（ｅ）加熱および／
または樹脂の反応熱によって型内に存在する硬化性樹脂
を硬化させ、固化を完了させることにより、繊維強化樹
脂からなる緻密なスキン層とシンタクチックフォームか
らなる多孔質コア層とが一体化した複合成形品となし、
目的とする軽量かつ高剛性の型枠を製造する方法であ
る。The first method for producing a mold made of the composite molded article of the present invention using such a material is the heat-expandable particles (or rigid lightweight particles thereof) which are the precursor particles of the light-weight filling particles. A mixture of) and
(A) A curable resin and the above particles are mixed to prepare a particle-containing resin composition, and (b) upper and lower parts 2 cut into predetermined dimensions.
One reinforcing fibrous sheet (and, if necessary, two separation membranes) are arranged, and the particle-containing resin composition is fed between them to form a layer having a substantially uniform thickness. A laminated body composed of (separation membrane) / particulate-containing resin composition / (separation membrane) / fibrous sheet for reinforcement is formed, and (c) this laminated body is set in a predetermined mold for frame molding, and (d) ) After closing the mold, heat is applied to expand the heat-expandable particles in the particle-containing resin composition, and the pressure generated in the mold thereby causes the curable resin to penetrate into the upper and lower reinforcing fibrous sheets. , Part of it reaches the surface, and (e) heating and / or
Alternatively, by curing the curable resin present in the mold by the reaction heat of the resin and completing the solidification, a dense skin layer made of fiber reinforced resin and a porous core layer made of syntactic foam are integrated. No molded article,
This is a method for manufacturing a target lightweight and highly rigid mold.
【００３６】また、第２の方法は、軽量充填粒子として
非熱膨脹性の圧縮性粒子を使用する方法である。この圧
縮性粒子は、すでに膨脹した状態の中空粒子であって加
熱により膨脹は起こさず、加圧することによって体積が
減少して圧縮された状態になるものである。この方法に
よれば、（ａ）硬化性樹脂と圧縮性粒子とを混合して含
粒子樹脂組成物を調製し、（ｂ）所定の寸法にカットさ
れた上下２つの強化用繊維質シート（および必要に応じ
て２つの分離膜）を配置し、この間に上記含粒子樹脂組
成物をほぼ均一な厚みの層状になるように供給して、強
化用繊維質シート／（分離膜）／含粒子樹脂組成物／
（分離膜）／強化用繊維質シートからなる積層体とな
し、（ｃ）この積層体を所定の型枠成形用の型内にセッ
トし、（ｄ）型を閉じて圧縮状態として、含粒子樹脂組
成物中の硬化性樹脂を上下の強化用繊維質シートへ浸透
させ、その一部を表面まで至らしめ、（ｅ）加熱および
／または樹脂の反応熱によって型内の硬化性樹脂を硬化
させ、固化を完了させることにより、繊維強化樹脂から
なる緻密なスキン層とシンタクチックフォームからなる
多孔質コア層とが一体化した複合成形品となし、目的と
する軽量かつ高剛性の型枠を製造する方法である。The second method is to use non-heat-expandable compressible particles as the lightweight filling particles. The compressible particles are hollow particles that have already expanded, and do not expand due to heating, and the compressed particles have a reduced volume and become compressed. According to this method, (a) a curable resin and compressible particles are mixed to prepare a particle-containing resin composition, and (b) two upper and lower reinforcing fibrous sheets (and If necessary, two separation membranes are arranged, and the particle-containing resin composition is supplied between them so as to form a layer having a substantially uniform thickness, and a reinforcing fibrous sheet / (separation membrane) / particle-containing resin is provided. Composition/
(Separation membrane) / a reinforcing fibrous sheet laminated body, (c) this laminated body is set in a predetermined mold for frame molding, and (d) the mold is closed to obtain a compressed state. The curable resin in the resin composition is infiltrated into the upper and lower reinforcing fibrous sheets, part of it is brought to the surface, and (e) the curable resin in the mold is cured by heating and / or reaction heat of the resin. By completing the solidification, it becomes a composite molded product in which a dense skin layer made of fiber reinforced resin and a porous core layer made of syntactic foam are integrated to produce the desired lightweight and highly rigid formwork. Is the way to do it.
【００３７】さらに、第３の製造方法は、軽量充填粒子
として剛性軽量粒子を使用する方法である。この剛性軽
量粒子は、すでに述べた如く、加熱あるいは加圧に際し
て、本質的に体積変化を起こさない剛性の高い中空粒子
であって、通常用いられるガラスバルーンやシラスバル
ーンのような無機中空粒子が好ましく使用される。Further, the third manufacturing method is a method of using rigid lightweight particles as the lightweight filling particles. As described above, the rigid lightweight particles are hollow particles having high rigidity that do not substantially change in volume upon heating or pressurization, and inorganic hollow particles such as commonly used glass balloons and shirasu balloons are preferable. used.
【００３８】この場合、加圧によって本質的に体積の変
化（圧縮および回復）を起こさないことを除けば、上述
の圧縮性粒子を使用する方法にほぼ準じて型枠を製造す
ることができる。In this case, the mold can be manufactured in almost the same manner as the above-mentioned method using the compressible particles, except that the change in volume (compression and recovery) is not caused essentially by pressurization.
【００３９】上記３通りの製造方法は、典型的な例を示
すものであって、これら各種の軽量充填粒子の２種類以
上を混合した状態で、含粒子樹脂組成物を調製し、上述
のようなサンドイッチ構造の複合成形品からなる型枠を
製造することも勿論可能であり、とくに、膨脹性粒子と
剛性軽量粒子とを併用すること、圧縮性粒子と剛性軽量
粒子とを併用することは、得られる型枠の物性を最大に
発揮させる上で、極めて有効な方法である。The above-mentioned three production methods are typical examples, and a particle-containing resin composition is prepared by mixing two or more kinds of these various kinds of lightweight filling particles, and as described above. It is of course possible to produce a mold made of a composite molded article having a sandwich structure, in particular, the use of expandable particles and rigid lightweight particles in combination, the use of compressible particles and rigid lightweight particles in combination, This is an extremely effective method for maximizing the physical properties of the obtained mold.
【００４０】[0040]
【発明の実施の形態】かかる本発明の型枠は、多孔質コ
ア層を有するサンドイッチ構造の板状部のみで構成され
てもよいが、その用途によっては、該板状部の周囲（周
辺）の一部または全部に、スキン層と同種の樹脂を含む
繊維強化樹脂からなる厚み調整用の肉厚部を設けたり、
補強リブを設けることが好ましい。BEST MODE FOR CARRYING OUT THE INVENTION The formwork of the present invention may be composed only of a plate-like portion having a sandwich structure having a porous core layer, but depending on the application, the periphery (periphery) of the plate-like portion may be used. Part or all of the, or a thick portion for thickness adjustment made of fiber reinforced resin containing the same type of resin as the skin layer,
It is preferable to provide reinforcing ribs.
【００４１】なお、板状部の厚みは、通常４〜２０ｍｍ
が適当であり、該板状部を構成するサンドイッチ構造体
における多孔質コア層の厚みがスキン層の厚みの合計に
対して１／２〜５０／１の範囲内にあるにあること、そ
して、該板状部における多孔質コア層の比重が０．３〜
０．７の範囲内にあること、さらには、該板状部の比重
が０．５〜０．９でかつ型枠全体の比重が０．５〜１．
２の範囲内にあることが、軽量性、強靭性、取扱性等の
バランスが取れた型枠とする上で好ましい。板状部の寸
法は、たとえば、サイディングボード用型枠の場合は、
縦方向の長さが１０００〜６０００ｍｍで、横方向の長
さが縦方向の長さの１／６〜１／２であり、かつ厚みが
４〜２０ｍｍとするのが適当であるが、型枠の用途に応
じて適宜変更することは差支えない。The thickness of the plate portion is usually 4 to 20 mm.
Is suitable, and the thickness of the porous core layer in the sandwich structure constituting the plate-like portion is in the range of 1/2 to 50/1 with respect to the total thickness of the skin layers, and The specific gravity of the porous core layer in the plate portion is 0.3 to
Within the range of 0.7, the specific gravity of the plate-shaped portion is 0.5 to 0.9, and the specific gravity of the entire mold is 0.5 to 1.
It is preferable that it is within the range of 2 in order to obtain a mold having a balance of lightness, toughness, handleability and the like. The size of the plate-shaped part is, for example, in the case of a siding board formwork,
It is suitable that the length in the vertical direction is 1000 to 6000 mm, the length in the horizontal direction is 1/6 to 1/2 of the length in the vertical direction, and the thickness is 4 to 20 mm. There is no problem in making appropriate changes according to the application.
【００４２】また、該板状部のコア部には、局所的に補
強材を内在させ、曲げに耐する抵抗性を向上させること
もできる。かかる補強材としてはガラス繊維製組み紐が
好ましく、通常、該組み紐が適当な間隔で配置される。
また、これと共にまたはこれとは別に、板状部の表面ま
たは裏面に、畝状の補強用リブを少なくとも１個、凸設
してもよい。A reinforcing material may be locally incorporated in the core portion of the plate-like portion to improve resistance to bending. As the reinforcing material, glass fiber braids are preferable, and the braids are usually arranged at appropriate intervals.
In addition to or separately from this, at least one ridge-shaped reinforcing rib may be provided on the front surface or the back surface of the plate-shaped portion in a protruding manner.
【００４３】一方、必要に応じて板状部の周囲に一体に
設置される肉厚部は、本型枠で成型すべき製品の厚み調
製のために設けられるもので、板状部の樹脂と同種の樹
脂を含む繊維強化樹脂で構成されるが、この肉厚部には
必ずしも上記の多孔質コア層を含む必要はなく、また、
該肉厚部に含まれる強化材も繊維質シートである必要は
なく、例えば、ガラス繊維パウダー等でもよい。この厚
み調整用の厚肉部は、サイディングボード用の型枠の場
合、板状部に対して６〜３５ｍｍの高さおよび５〜３０
ｍｍの幅を有し、かつ該厚肉部に２か所以上の水抜き用
の切り込み部を設けるのが好ましい。On the other hand, if necessary, the thick portion integrally provided around the plate-like portion is provided for adjusting the thickness of the product to be molded by the main frame, and is made of resin of the plate-like portion. Although it is composed of a fiber-reinforced resin containing the same kind of resin, it is not always necessary to include the porous core layer in the thick portion,
The reinforcing material contained in the thick portion does not have to be a fibrous sheet, and may be, for example, glass fiber powder. In the case of a mold for a siding board, the thick part for adjusting the thickness has a height of 6 to 35 mm and 5 to 30 mm with respect to the plate part.
It is preferable to have a width of mm and to provide two or more notches for draining water in the thick portion.
【００４４】なお、多孔質コア層が型枠の端面に露出し
ていると剥離強度等の問題が懸念される場合は、型枠の
端面を繊維強化樹脂または樹脂のみで構成するのがよ
い。When the porous core layer is exposed on the end face of the mold, problems such as peel strength may occur. Therefore, the end face of the mold should be made of fiber reinforced resin or only resin.
【００４５】本発明の型枠では、繊維強化樹脂からなる
スキン層の少なくとも片面に合成樹脂フィルムを積層一
体化してもよく、たとえば、コンクリートに対する安定
性、離型性等に優れたポリオレフィンのフィルムを積層
して一体に成形することにより上記の特性を改善したも
のでもよい。In the mold of the present invention, a synthetic resin film may be laminated and integrated on at least one surface of a skin layer made of a fiber reinforced resin. For example, a polyolefin film excellent in stability against concrete and mold releasability is used. It may be one in which the above characteristics are improved by laminating and integrally molding.
【００４６】また、本発明の型枠では、型枠の表面機能
の改善あるいは意匠性の向上のために、型枠の表面側す
なわちサイディングボード用では厚み調整用の厚肉部を
設けた側の板状部表面に所望の模様をつけることも可能
である。すなわち、複合成形品型枠の成形時に、対応す
る金型面に凹凸をつけるか、模様を施した部材を貼り付
けることによって、該模様が型枠表面に効果的に転写さ
れる。上記の模様を施した部材としては、一般に、有機
または無機ポリマーが使用され、望ましくはポリウレタ
ンシート等が使用される。これにより、表面に模様が施
された型枠が容易にしかも効率的に製造される。Further, in the mold of the present invention, in order to improve the surface function or design of the mold, the surface of the mold, that is, on the side provided with a thick portion for adjusting the thickness in the case of a siding board. It is also possible to provide a desired pattern on the surface of the plate-shaped portion. That is, at the time of molding a composite molded product frame, the pattern is effectively transferred to the surface of the mold by providing irregularities on the corresponding mold surface or by attaching a patterned member. An organic or inorganic polymer is generally used as the member having the above pattern, and a polyurethane sheet or the like is preferably used. As a result, a mold having a pattern on its surface can be manufactured easily and efficiently.
【００４７】次に、本発明に係る型枠の構造例について
図面により説明する。Next, a structural example of the mold according to the present invention will be described with reference to the drawings.
【００４８】図１は、サイディングボード用型枠の１例
を示す。Ａは斜視図、ＢはＸ−Ｘ方向における横断面
図、ＣはＹ−Ｙ方向における横断面図、ＤはＺ−Ｚ方向
における横断面図である。図１において、型枠１は、主
体となる長方形の平坦な板状部２とその周囲に設けた厚
み調整用の厚肉部３から構成される。板状部２の厚みｃ
は、型枠の大きさ（図１では縦方向の長さａ、横方向の
長さｂに相当）や成形すべきサイディングボードの厚み
（図１ではｆに相当）等により決められるが、通常４〜
２０ｍｍが好適であり、とくに８〜１５ｍｍの範囲が好
ましい。FIG. 1 shows an example of a mold for a siding board. A is a perspective view, B is a transverse sectional view in the XX direction, C is a transverse sectional view in the YY direction, and D is a transverse sectional view in the ZZ direction. In FIG. 1, a mold 1 is composed of a rectangular flat plate-like portion 2 serving as a main body and a thick portion 3 provided around the flat plate-like portion 2 for thickness adjustment. Thickness c of plate-like portion 2
Is determined by the size of the mold (corresponding to the length a in the vertical direction and the length b in the horizontal direction in FIG. 1) and the thickness of the siding board to be molded (corresponding to f in FIG. 1). 4-
20 mm is preferable, and a range of 8 to 15 mm is particularly preferable.
【００４９】本発明の型枠を用いてサイディングボード
を製造する際に、該型枠を多数枚重ね合わせて、同時に
多数の製品（セメント硬化物からなるサイディングボー
ド）を作ることが多く、したがって、図１で示される板
状部２の厚みｃは、作業空間上薄い方が望ましい。一
方、型枠により製造する製品の厚みを一定に保持するた
めには、製品原料の重量による板状部２の撓みを小さく
する必要があり、結果として厚みｃを大きく設計する傾
向になる。この相矛盾する問題を解決するために剛性の
大きい材料を使用することが望ましい。とくに、平面性
が重要な製品の場合はリブ補強等の対策がとれないの
で、型枠材料自身の剛性の高いもの、したがって材料の
弾性率が高いものを採用する必要がある。このような要
求に対して、本発明の型枠を構成する繊維強化樹脂から
なるスキン層とシンタクチックフォームからなる多孔質
コア層とから構成されるサンドイッチ構造の複合成形品
は、十分に高い剛性と著しい軽量性とを併有し、きわめ
て好適なサイディングボード用型枠を提供することが判
明した。When a siding board is manufactured using the mold of the present invention, it is often the case that a large number of the molds are overlapped with each other to simultaneously manufacture a large number of products (a siding board made of a hardened cement product). It is desirable that the thickness c of the plate-shaped portion 2 shown in FIG. 1 be thin in view of the working space. On the other hand, in order to keep the thickness of the product manufactured by the mold constant, it is necessary to reduce the bending of the plate-shaped portion 2 due to the weight of the raw material of the product, and as a result, the thickness c tends to be designed large. It is desirable to use highly rigid materials to solve this conflicting problem. In particular, in the case of a product in which flatness is important, measures such as rib reinforcement cannot be taken, so it is necessary to adopt a material having a high rigidity of the mold material itself, that is, a material having a high elastic modulus. In response to such a demand, a composite molded article having a sandwich structure composed of a skin layer made of a fiber reinforced resin constituting the mold of the present invention and a porous core layer made of syntactic foam has sufficiently high rigidity. It has been found to provide a very suitable formwork for a siding board, which has both excellent and light weight.
【００５０】厚肉部３には、図１の如く、セメント硬化
の過程で生ずる水を除去するため、切り込みを入れるこ
とが好ましい。この水抜き用切り込み部４の形状、大き
さについてはとくに制約はないが、切り込み部の深さは
板状部２の面と合わせることが好ましく、製品の大きさ
に応じて４箇所以上とすることが好ましい。なお、厚み
調整用の厚肉部３は、長さ方向の幅ｄと横方向の幅ｅは
必ずしも同じ大きさである必要はない。As shown in FIG. 1, it is preferable to make a cut in the thick portion 3 in order to remove water generated in the process of hardening the cement. There are no particular restrictions on the shape and size of the drainage notch 4, but the depth of the notch is preferably matched with the surface of the plate-like portion 2, and there are four or more locations depending on the size of the product. It is preferable. In the thick portion 3 for adjusting the thickness, the width d in the length direction and the width e in the lateral direction do not necessarily have to be the same size.
【００５１】図２は、コンクリート打設用の型枠の１例
を示す。Ａは斜視図、ＢはＸ−Ｘ方向における横断面
図、ＣはＹ−Ｙ方向における横断面図である。FIG. 2 shows an example of a formwork for placing concrete. A is a perspective view, B is a transverse sectional view in the XX direction, and C is a transverse sectional view in the YY direction.
【００５２】図２において、型枠２１はフラットの面
（図２では下面）を表とし、長方形の周囲（裏面に相
当）に形状保持用の枠２３および裏面補強リブ部２４を
３個有する構造である。この裏面補強リブ部２４は、長
さ方向（ａ）に連続した畝状になっており、幅方向
（ｂ）に関して等間隔にほぼ平行に配置されている。
（図２では幅ｂ＝６００ｍｍに対し１５０ｍｍ間隔で３
本の補強リブ部を配置。）In FIG. 2, the mold 21 has a flat surface (lower surface in FIG. 2) as a table, and has a shape-retaining frame 23 and three back reinforcing ribs 24 around the rectangle (corresponding to the back). Is. The back surface reinforcing rib portions 24 are in the form of ridges that are continuous in the length direction (a), and are arranged substantially parallel at equal intervals in the width direction (b).
(In FIG. 2, the width b = 600 mm is 3 at 150 mm intervals.
Arranged the reinforcing ribs of the book. )
【００５３】図２の型枠の使用に当っては、施工時のコ
ンクリートの面圧に対応した剛性が必要であるが、本発
明に係る型枠は、主要部となる板状部が繊維強化樹脂か
らなる緻密なスキン層とシンタクチックフォームからな
る多孔質コア層とが一体化されたサンドイッチ構造であ
ることにより、十分な強度および剛性を有し、かつ、周
囲部の枠２３（この枠部分は隣り合わせの型枠との位置
合わせおよび固定にも使用される）および裏面補強リブ
部２４を設置することにより、さらに大きな強度と剛性
を示し、きわめて有用性の高いコンクリート打設用の型
枠となる。In using the formwork of FIG. 2, it is necessary to have rigidity corresponding to the surface pressure of concrete during construction, but in the formwork according to the present invention, the plate-like part which is the main part is fiber reinforced. Due to the sandwich structure in which the dense skin layer made of resin and the porous core layer made of syntactic foam are integrated, sufficient strength and rigidity are obtained, and the frame 23 (this frame portion Is also used for aligning and fixing with adjacent formwork) and by providing the back reinforcing rib portion 24, the formwork for concrete pouring exhibiting extremely high strength and rigidity and being extremely useful. Become.
【００５４】図３は、サイディングボード用型枠の他の
例を示す。Ａは斜視図、ＢはＸ−Ｘ方向における横断面
図、ＣはＹ−Ｙ方向における横断面図である。図３にお
いても、上述の図１と同様に、型枠１は、主体となる長
方形の平坦な板状部２と該板状部の両側に設けた厚み調
整用の厚肉部３からなり、この厚肉部３には水抜き用切
り込み部４が設けられている。FIG. 3 shows another example of the siding board form. A is a perspective view, B is a transverse sectional view in the XX direction, and C is a transverse sectional view in the YY direction. Also in FIG. 3, as in the above-described FIG. 1, the mold 1 is composed of a rectangular flat plate-shaped portion 2 serving as a main body and thick-walled portions 3 provided on both sides of the plate-shaped portion for thickness adjustment. A cutout 4 for draining water is provided in the thick portion 3.
【００５５】図２および図３の型枠では、厚肉部３は、
内部に多孔質コアが存在せず、繊維強化樹脂のみで構成
されるが、図１のように、多孔質コアが厚肉部３にまで
入り込んだ構造にすることもできる。In the molds of FIGS. 2 and 3, the thick portion 3 is
Although the porous core does not exist inside and is composed only of the fiber-reinforced resin, it is also possible to adopt a structure in which the porous core is embedded in the thick portion 3 as shown in FIG.
【００５６】ただし、いずれの場合も多孔質コアが型枠
の端面に露出しない方が剥離強度等の観点から好まし
く、したがって、端面付近は繊維強化樹脂または樹脂で
構成し多孔質コアのない状態にするのが適当である。However, in any case, it is preferable that the porous core is not exposed to the end surface of the mold from the viewpoint of peeling strength and the like. Therefore, the vicinity of the end surface is made of fiber reinforced resin or resin and has no porous core. It is appropriate to do.
【００５７】このような、少なくとも主要部（板状部）
を繊維強化樹脂の緻密なスキン層とシンタクチックフォ
ームの多孔質コア層とからなるサンドイッチ構造の一体
成形品で構成した本発明の型枠は、軽量でかつ剛性、強
度の高い型枠という要求に対して、十分に応え得る高い
性能を有しており、広範な分野できわめて有用な型枠で
ある。このため、かかる本発明の型枠は、上述したサイ
ディングボード成形用の型枠やコンクリート打設用の型
枠のほか、各種コンクリートパネル、屋根瓦等の成形用
型枠や溝の工事用型枠等としても有効に利用することが
できる。At least the main part (plate-shaped part) as described above
The mold of the present invention, which is composed of an integrally molded product having a sandwich structure composed of a dense skin layer of fiber-reinforced resin and a porous core layer of syntactic foam, is required to be a lightweight, rigid, and high-strength mold. On the other hand, it has a high performance that can be sufficiently satisfied, and is a very useful formwork in a wide range of fields. Therefore, the formwork of the present invention includes, in addition to the formwork for forming the siding board and the formwork for placing concrete, the formwork for forming various concrete panels, roof tiles and the like, and the formwork for construction of grooves. It can also be effectively used as such.
【００５８】なお、型枠の用途によっては、該型枠の表
面に離型剤を塗布したり、スキン層内部に含有させるこ
とによって、コンクリート製品などの離型性をより向上
させることもできる。Depending on the use of the mold, a mold release agent may be applied to the surface of the mold or contained in the skin layer to further improve the mold releasability of concrete products and the like.
【００５９】[0059]
【実施例】以下に実施例をあげて本発明をより具体的に
説明する。ただし、これらの実施例は、本発明の理解を
助けるためのものであって、これらの記載によって本発
明の範囲が限定されるものではない。なお、実施例にお
ける「部」はとくに断らない限り重量部を表わす。EXAMPLES The present invention will be described more concretely with reference to the following examples. However, these examples are for helping understanding of the present invention, and the scope of the present invention is not limited by these descriptions. In the examples, "parts" means parts by weight unless otherwise specified.
【００６０】［実施例１］ （１）成形用金型の準備 サイディングボード用型枠の成形用金型として、図１に
示す形状の複合成形品が得られるキャビティーを有する
鋳造アルミニウムの金型を準備した。なお、本実施例に
より作製した型枠の寸法は次の通りである。Example 1 (1) Preparation of Mold for Molding As a mold for molding a mold for a siding board, a mold of cast aluminum having a cavity for obtaining a composite molded article having a shape shown in FIG. Prepared. The dimensions of the formwork produced in this example are as follows.
【００６１】板状部２： 縦方向の長さ（ａ）＝１９００ｍｍ 横方向の長さ（ｂ）＝５００ｍｍ 板状部（平面部）２の厚さ（ｃ）＝１３ｍｍ 板状体の周囲の厚み調整用厚肉部３： 縦方向の幅（ｄ）＝５０ｍｍ 横方向の幅（ｅ）＝４５ｍｍ 厚肉部の厚さ（ｆ）＝１２ｍｍ 水抜き用切り込み部４： 切り込み部の上幅（ｇ）＝３０ｍｍ 切り込み角度（θ）＝４５度Plate-shaped part 2: Length in the vertical direction (a) = 1900 mm Length in the horizontal direction (b) = 500 mm Thickness of plate-shaped part (planar part) 2 (c) = 13 mm Thickness adjusting thick part 3: Vertical width (d) = 50 mm Horizontal width (e) = 45 mm Thick part thickness (f) = 12 mm Draining notch 4: Upper width of notch ( g) = 30 mm Cutting angle (θ) = 45 degrees
【００６２】（２）強化用繊維質シートおよび分離膜の
準備 強化用繊維質シートとしてガラス繊維チョップドストラ
ンドマット（旭ファイバーグラス製「グラスロンＣＭ４
５０」、目付け４５０ｇ／ｍ2 ）を、分離膜としてポリ
エステル系不織布（ユニセル製「ユニセルＢＴ０８０７
Ｗ」、目付け４０ｇ／ｍ2 ）を、それぞれ２枚準備し
た。また、周囲の厚肉部強化用の繊維質シートとしてガ
ラス繊維チョップドストランドマット（旭ファイバーグ
ラス製「グラスロンＣＭ６００」）を所定の幅に切り出
したものを用意した。(2) Preparation of Reinforcing Fiber Sheet and Separation Membrane As a reinforcing fiber sheet, glass fiber chopped strand mat (“Glaslon CM4 manufactured by Asahi Fiber Glass”
50 ", basis weight 450 g / m 2 ) as a separation membrane using a polyester non-woven fabric (" Unicel BT0807 "manufactured by Unicell).
W "and basis weight 40 g / m 2 ) were prepared for each of two sheets. Further, a glass fiber chopped strand mat (“Glaslon CM600” manufactured by Asahi Fiber Glass) cut into a predetermined width was prepared as a fibrous sheet for strengthening the surrounding thick portion.
【００６３】（３）含粒子樹脂組成物の調製 硬化性樹脂としてエポキシ樹脂（大日本インキ化学製
「エピクロン８５０」）と硬化剤としてのイソホロンジ
アミンおよびＢＦ3 ＭＥＡ（三フッ化ホウ素モノエチル
アミン錯体）の１００／２４／１（重量比）の混合物を
使用し、また、軽量充填粒子として熱膨脹（発泡）性の
樹脂粒子（松本油脂製薬製「マツモトマイクロスフェア
ーＴＥＭ−８」）および剛性軽量粒子であるガラスバル
ーン（住友３Ｍ製「グラス「グラスバブルズＫ−１」）
の混合系（重量比で６０／４０）を使用した。上記硬化
性樹脂と軽量充填粒子混合物とを、重量比で８０／２０
の割合で混合して、スラリー状の含粒子樹脂組成物を調
製した。(3) Preparation of particle-containing resin composition Epoxy resin (“Epiclone 850” manufactured by Dainippon Ink and Chemicals) as a curable resin, isophoronediamine as a curing agent and BF 3 MEA (boron trifluoride monoethylamine complex) Of 100/24/1 (weight ratio), and as heat-expandable (foaming) resin particles (“Matsumoto Microspheres TEM-8” manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.) as lightweight filling particles and rigid lightweight particles. A glass balloon ("Glass Bubbles K-1" made by Sumitomo 3M)
The mixed system (60/40 in weight ratio) was used. 80/20 by weight ratio of the curable resin and the mixture of lightweight filling particles
Were mixed at a ratio of 1 to prepare a slurry-like particle-containing resin composition.
【００６４】なお、上記熱膨張性樹脂粒子の熱膨張前の
比重は１．０６であるが、成形時のエポキシ樹脂の硬化
反応により体積比で約１０倍膨脹し、成形後の比重は約
０．１となる。一方、上記剛性軽量粒子の比重は０．１
２５である。The specific gravity of the heat-expandable resin particles before thermal expansion is 1.06, but the epoxy resin undergoes a curing reaction during molding to expand by about 10 times in volume ratio, and the specific gravity after molding is about 0. It will be 1. On the other hand, the specific gravity of the rigid lightweight particles is 0.1
25.
【００６５】（４）型枠の成形 上記のアルミニウム金型に、強化用繊維質シート（チョ
ップドストランドマット）および分離膜（ポリエステル
系不織布）をセットし、その上に上記含粒子樹脂組成物
を金型の平面部全体に拡げるように供給し、その上にも
う１枚の分離膜を重ねた後、さらにもう１枚の強化用繊
維質シート（チョップドストランドマット）および厚肉
部補強用のカットしたチョップドストランドマットをセ
ットして平坦な状態とし、型を閉じた。(4) Mold Forming A reinforcing fibrous sheet (chopped strand mat) and a separation membrane (polyester non-woven fabric) are set in the above-mentioned aluminum mold, and the particle-containing resin composition is placed on the metal mold. It was supplied so that it spreads over the entire flat surface of the mold, and another separation membrane was placed on top of it, and then another fibrous sheet for reinforcement (chopped strand mat) and a cut for reinforcing the thick wall portion. The chopped strand mat was set to a flat state and the mold was closed.
【００６６】この状態で一旦金型のキャビティー内を真
空に引いて、不要のガスを排気した後、金型を１３０℃
に加熱した。加熱とともに、金型内の熱膨脹性樹脂粒子
の体積膨脹が起こり、次いで硬化性樹脂の硬化反応が進
行して、型枠の成形を終了した。In this state, the inside of the mold cavity was once evacuated to evacuate unnecessary gas, and then the mold was heated to 130 ° C.
Heated. With heating, volume expansion of the heat-expandable resin particles in the mold occurred, and then the curing reaction of the curable resin proceeded to complete the molding of the mold.
【００６７】得られた複合成形品からなる型枠は、板状
部（平面部）の厚み（ｃ）が１３．０ｍｍ、スキン層
（片側）の厚みは０．４５ｍｍであった。また、板状部
（平面部）のコア層の比重は０．４０、スキン層の比重
は１．７であり、板状部（平面部）全体の比重は０．４
９であって、軽量性に優れたものであった。In the mold made of the obtained composite molded product, the thickness (c) of the plate portion (flat portion) was 13.0 mm, and the thickness of the skin layer (one side) was 0.45 mm. The specific gravity of the core layer of the plate-shaped portion (flat portion) is 0.40, the specific gravity of the skin layer is 1.7, and the specific gravity of the entire plate-shaped portion (flat portion) is 0.4.
It was 9 and was excellent in lightness.
【００６８】（５）型枠としての評価 以上のようにして得られた図１に示す形状の複合成形品
からなる型枠に、セメント混合液および木枠を入れ、こ
れを３０枚重ね圧縮力を加えて、サイディングボードを
製造した。得られたサイディングボードボードには成形
欠陥が認められなかった。セメント硬化後、型枠を容易
に剥がすことができ、セメント硬化物表面の変色や硬化
不良も認められず、また３０回繰り返し使用しても支障
はなかった。さらに、このものは、一体化タイプの型枠
であるため、取扱い易く、きわめて軽量かつ耐久性もあ
り、良好な型枠であることが確認された。(5) Evaluation as Formwork A cement mixture and a wooden frame were put into the formwork made of the composite molded article having the shape shown in FIG. Was added to produce a siding board. No molding defects were found in the obtained siding board. After the cement was hardened, the mold could be easily peeled off, neither discoloration nor poor hardening of the surface of the hardened cement was observed, and there was no problem even after repeated use 30 times. Further, it was confirmed that this is a good form because it is an integrated type form, easy to handle, extremely lightweight and durable.
【００６９】［実施例２］ （１）成形用金型の準備 図２に示す形状の多孔質コア含有複合成形品が得られる
キャビティーを有する鋳造アルミニウムの金型を準備し
た。なお、本実施例で製作した型枠の寸法は次の通りで
ある。Example 2 (1) Preparation of Mold for Molding A mold of cast aluminum having a cavity to obtain a composite molded article containing a porous core having the shape shown in FIG. 2 was prepared. The dimensions of the formwork produced in this example are as follows.
【００７０】板状部２２： 縦方向の長さ（ａ）＝１５００ｍｍ 横方向の長さ（ｂ）＝６００ｍｍ 板状部（平面部）２２の厚さ（ｃ）＝１２ｍｍ 周囲の枠部分２３： 縦方向の幅（ｄ）＝１０ｍｍ 横方向の幅（ｅ）＝１０ｍｍ 枠部分の高さ（ｆ）＝６０ｍｍ 裏面補強リブ部２４： 補強リブ部の上部幅（ｈ）＝２０ｍｍ 補強リブ部の下部幅（ｉ）＝３０ｍｍ 補強リブ部の高さ（ｊ）＝１０ｍｍ 補強リブ部の本数＝３Plate-shaped portion 22: Length in the vertical direction (a) = 1500 mm Length in the horizontal direction (b) = 600 mm Thickness of plate-shaped portion (flat surface portion) 22 (c) = 12 mm Surrounding frame portion 23: Width in vertical direction (d) = 10 mm Width in lateral direction (e) = 10 mm Height of frame part (f) = 60 mm Back reinforcement rib part 24: Upper width of reinforcement rib part (h) = 20 mm Lower part of reinforcement rib part Width (i) = 30 mm Height of reinforcing ribs (j) = 10 mm Number of reinforcing ribs = 3
【００７１】（２）強化用繊維質シートおよび分離膜の
準備 強化用繊維質シートとしてガラス繊維チョップドストラ
ンドマット（旭ファイバーグラス製「グラスロンＣＭ６
００」、目付け６００ｇ／ｍ2 ）を、分離膜としてポリ
プロピレン系不織布を準備した。また、周囲の枠部分の
強化用繊維質シートとして上記「グラスロンＣＭ６０
０」を使用し、裏面補強部用繊維シートとして、上記
「グラスロンＣＭ６００」をカットして使用した。(2) Preparation of Fiber Sheet for Reinforcement and Separation Membrane As a fiber sheet for reinforcement, glass fiber chopped strand mat (“Glaslon CM6 manufactured by Asahi Fiber Glass”
00 ", and a basis weight of 600 g / m 2 ) were used as a separation membrane to prepare a polypropylene-based nonwoven fabric. In addition, as a reinforcing fiber sheet for the surrounding frame portion, the above-mentioned "Glaslon CM60
0 "was used, and the above-mentioned" Glaslon CM600 "was cut and used as the fiber sheet for the back reinforcing portion.
【００７２】（３）含粒子樹脂組成物の調製 硬化性樹脂として不飽和ポリエステル樹脂（大日本イン
キ化学製「ポリライトＦＧ１０４Ｎ」）と開始剤として
のベンゾイルパーオキサイド／クメンハイドロパーオキ
サイドおよび促進剤としてのジメチルアニリンとを、重
量比で、１００／１．０／０．４／０．６を良く混合し
て、樹脂混合物とした。軽量充填粒子として圧縮性粒子
（松本油脂製薬製「マツモトマイクロスフェアーＭＦＬ
１００ＣＡ」；比重０．１３）と剛性軽量粒子（住友３
Ｍ製「グラスバブルズＫ−１」；比重０．１２５）との
混合系（重量比で４２／５８）を準備した。そして、上
記硬化性樹脂と軽量粒子混合物とを、重量比８５／１５
の割合で混合して、含粒子樹脂組成物を調製した。(3) Preparation of Particle-Containing Resin Composition An unsaturated polyester resin (“Polylite FG104N” manufactured by Dainippon Ink and Chemicals) as a curable resin, benzoyl peroxide / cumene hydroperoxide as an initiator, and an accelerator. Dimethylaniline was mixed well in a weight ratio of 100 / 1.0 / 0.4 / 0.6 to obtain a resin mixture. Compressible particles as lightweight filling particles (“Matsumoto Microspheres MFL” manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.
100CA ”; specific gravity 0.13) and rigid lightweight particles (Sumitomo 3
A mixed system (42/58 in weight ratio) with "Glass Bubbles K-1" manufactured by M; specific gravity 0.125) was prepared. Then, the curable resin and the lightweight particle mixture are mixed in a weight ratio of 85/15.
And a particle-containing resin composition was prepared.
【００７３】（４）型枠の成形 上記のアルミニウム金型に、強化用繊維質シートおよび
分離膜をセットし、その上に上記含粒子樹脂組成物を金
型の平面部全体に拡げるように供給し、さらに分離膜を
重ねた後、周囲の枠部分用および裏面補強部用にカット
した強化用繊維質シートをそれぞれ配置した。そして、
後者の繊維質シートに、上記硬化性樹脂混合物を追加
し、型を閉じて加圧状態にして、硬化性樹脂の含浸を行
なった。(4) Mold Forming A reinforcing fibrous sheet and a separation film are set in the above-mentioned aluminum mold, and the particle-containing resin composition is supplied thereon so as to spread over the entire flat surface of the mold. Then, after further stacking the separation membranes, the reinforcing fibrous sheets cut for the surrounding frame portion and the back surface reinforcing portion were arranged. And
The curable resin mixture was added to the latter fibrous sheet, and the mold was closed to bring it into a pressurized state for impregnation with the curable resin.
【００７４】この状態で、金型を１００℃に昇温し、硬
化性樹脂の反応熱がピークに達してから５分間保持し、
その後型を冷却し、金型から複合成形品を取り出した。In this state, the mold is heated to 100 ° C. and held for 5 minutes after the reaction heat of the curable resin reaches its peak,
After that, the mold was cooled, and the composite molded article was taken out from the mold.
【００７５】この複合成形品からなる型枠は、板状部
（平面部）の厚み（ｃ）が１２．０ｍｍ、スキン層（片
側）の厚みは０．６ｍｍであった。また、板状部（平面
部）のコア層の比重は０．６３、スキン層の比重は１．
７であり、板状部（平面部）全体の比重は０．７４であ
って、十分な軽量性を有するものであった。In the mold made of this composite molded product, the thickness (c) of the plate portion (flat portion) was 12.0 mm, and the thickness of the skin layer (one side) was 0.6 mm. The specific gravity of the core layer of the plate-shaped portion (planar portion) is 0.63, and the specific gravity of the skin layer is 1.
7 and the specific gravity of the entire plate-shaped portion (planar portion) was 0.74, which was sufficient lightness.
【００７６】（５）型枠としての評価 以上のようにして得られた図２に示す形状の複合成形品
からなる型枠を堰板として用いて、コンクリート壁の打
設を行なった。本実施例で得られた型枠は、セメントの
硬化に伴う発熱および打設の応力に対してもほとんど変
形せず、型枠としての優れた機能を有する事実が認めら
れ、また、繰り返し使用にも耐え、しかも極めて軽量で
あるため現場施工での作業性に優れていることが確認さ
れた。(5) Evaluation as Formwork A concrete wall was cast using the formwork made of the composite molded product having the shape shown in FIG. 2 obtained as described above as a dam plate. The mold obtained in this example is hardly deformed against the heat generated by the hardening of cement and the stress of placing, and the fact that it has an excellent function as a mold is recognized, and it can be repeatedly used. It has been confirmed that it excels in workability in on-site construction because it withstands even the most and is extremely lightweight.
【００７７】［実施例３］ （１）成形用金型の準備 サイディングボード用型枠の成形用金型として、図３に
示す形状の複合成形品が得られるキャビティーを有する
鋳造アルミニウムの金型を使用した。なお、本実施例で
製造した型枠の寸法は次の通りであった。Example 3 (1) Preparation of Mold for Molding As a mold for molding a frame for a siding board, a mold of cast aluminum having a cavity for obtaining a composite molded article having a shape shown in FIG. It was used. The dimensions of the formwork manufactured in this example were as follows.
【００７８】板状部２： 縦方向の長さ（ａ）＝１９００ｍｍ 横方向の長さ（ｂ）＝９９０ｍｍ 板状部（平面部）２の厚さ（ｃ）＝１２ｍｍ 板状体の長さ方向の厚み調整用厚肉部３： 縦方向の幅（ｄ）＝５５ｍｍ 厚肉部の厚さ（ｆ）＝１０ｍｍ 水抜き用切り込み部４： 縦方向の長さ部に片側３箇所、両方で６箇所設けた。 切り込み部の上幅（ｇ）＝２３ｍｍ 切り込み角度（θ）＝４５度Plate-shaped part 2: Length in the vertical direction (a) = 1900 mm Length in the horizontal direction (b) = 990 mm Thickness of plate-shaped part (planar part) 2 (c) = 12 mm Length of plate-shaped body Direction thickness adjustment thick part 3: Vertical width (d) = 55 mm Thick part thickness (f) = 10 mm Drainage notch 4: Vertical length part 3 at one side, both We provided 6 places. Upper width of cut part (g) = 23 mm Cut angle (θ) = 45 degrees
【００７９】（２）強化用繊維質シートおよび分離膜の
準備 それぞれ、実施例１で使用したものと同じ材料を準備し
た。(2) Preparation of Reinforcing Fiber Sheet and Separation Membrane The same materials as those used in Example 1 were prepared.
【００８０】（３）含粒子樹脂組成物の調製 硬化性樹脂として不飽和ポリエステル樹脂（大日本イン
キ化学製「ポリライトＦＧ１０４Ｎ」）と開始剤として
のベンゾイルパーオキサイド／クメンハイドロパーオキ
サイドおよび促進剤としてのジメチルアニリンとを、１
００／１．０／０．４／０．６の重量比で良く混合し、
樹脂混合物とした。一方、軽量充填粒子として圧縮性粒
子（松本油脂製薬製「マツモトマイクロスフェアーＭＦ
Ｌ１００ＣＡ」、比重０．１３）と剛性粒子（住友３Ｍ
製「グラスバブルズＫ−１」、比重０．１２５）とを、
重量比で４２／５８の混合系を使用した。そして、上記
樹脂混合物と軽量充填粒子とを、重量比で８５／１５の
割合で混合し、含粒子樹脂組成を調製した。(3) Preparation of Particle-Containing Resin Composition Unsaturated polyester resin (“Polylite FG104N” manufactured by Dainippon Ink and Chemicals) as a curable resin, benzoyl peroxide / cumene hydroperoxide as an initiator and an accelerator 1 with dimethylaniline
Mix well at a weight ratio of 00 / 1.0 / 0.4 / 0.6,
This was a resin mixture. On the other hand, as lightweight filling particles, compressible particles (“Matsumoto Microsphere MF” manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.
L100CA ", specific gravity 0.13) and rigid particles (Sumitomo 3M
"Glass Bubbles K-1", specific gravity 0.125),
A mixed system of 42/58 by weight was used. Then, the resin mixture and the lightweight filling particles were mixed at a weight ratio of 85/15 to prepare a particle-containing resin composition.
【００８１】（４）型枠の成形 上記のアルミニウム金型に、上記の強化用繊維質シート
および分離膜をセットし、その上に含粒子樹脂組成物を
金型の平面部全体に均一に拡げながら供給し、さらに分
離膜を重ねた後、その上にチョップドストランドマット
および両端の厚み調整用の厚肉部用にカットしたチョッ
プドストランドマットを配置した。さらに、厚肉部に相
当するチョップドストランドの上に上記脂混合物を追加
して含浸させた後、型を閉じて加圧状態にし、硬化性樹
脂の均一含浸と圧縮性粒子の圧縮を行った。(4) Mold Forming The above-mentioned reinforcing fibrous sheet and separation membrane were set in the above-mentioned aluminum mold, and the particle-containing resin composition was spread evenly over the entire flat surface of the mold. While being fed while further separating the membranes, a chopped strand mat and a chopped strand mat cut for the thick portions for adjusting the thickness of both ends were arranged on the separation membrane. Further, after the above fat mixture was additionally impregnated onto the chopped strand corresponding to the thick portion, the mold was closed to bring it into a pressurized state, and the curable resin was uniformly impregnated and the compressible particles were compressed.
【００８２】この状態で、金型を１００℃に昇温し、硬
化性樹脂の硬化反応熱がピークに達してから５分間保持
して成形を終了した。その後、金型を冷却し、複合成形
品を取り出した。板状部の厚み関係は実施例２と同様
で、コア層の比重は０．６２、スキン層の比重は１．７
であり、板状部（平面部）全体の比重は０．７３であっ
て、十分な軽量性を有するものであった。In this state, the mold was heated to 100 ° C., and after the curing reaction heat of the curable resin reached its peak, it was held for 5 minutes to complete the molding. Then, the mold was cooled and the composite molded product was taken out. The thickness relationship of the plate-like portion is the same as in Example 2, the specific gravity of the core layer is 0.62, and the specific gravity of the skin layer is 1.7.
The specific gravity of the entire plate-shaped portion (flat surface portion) was 0.73, which was sufficient lightness.
【００８３】（５）型枠としての評価 以上のようにして得られた図３に示す形状の型枠の内側
平面部に、模様入りポリウレタンシートを貼りつけた。
その状態で、セメント混合液を入れ、これを３０枚重ね
て圧縮力を加えた状態で静置して、サイディングボード
を製造した。(5) Evaluation as Formwork A patterned polyurethane sheet was attached to the inner flat surface of the formwork having the shape shown in FIG. 3 obtained as described above.
In this state, a cement mixed solution was added, 30 sheets of this were stacked, and the mixture was allowed to stand with a compressive force applied, to produce a siding board.
【００８４】セメント硬化後、型枠を容易に剥がすこと
ができ、表面に模様の入った、変色や欠陥のないボード
を得ることができた。After the cement was hardened, the mold could be easily peeled off, and a board with a pattern on the surface and without discoloration or defects could be obtained.
【００８５】[0085]
【発明の効果】本発明の型枠は、緻密な繊維強化樹脂ス
キン層と多孔質コア層のサンドイッチ構造を有する軽量
かつ高剛性の強靭な複合材料からなり、従来使用される
ことのなかった材質からなる新規な型枠である。したが
って、木材を始めとする従来の型枠に比べて、天然資源
の保護、繰り返し使用性の向上、軽量化による作業性お
よび経済性の改善など、市場からの要望に応えるきわめ
て優れた型枠である。The mold of the present invention is made of a lightweight, highly rigid and tough composite material having a sandwich structure of a dense fiber reinforced resin skin layer and a porous core layer, which has never been used before. It is a new formwork consisting of. Therefore, compared with conventional formwork such as wood, it is an extremely superior formwork that responds to market demands, such as protection of natural resources, improvement of reusability, improvement of workability and economy by weight reduction. is there.
【００８６】また、本発明の型枠は、上述した軽量性、
剛性、強靭性、耐久性などの利点に加えて、（１）一体
成形品なので、釘打ちなどによって組み立てる手間が省
け、かつ破壊し難く、隙間からの漏れが無い、（２）コ
ア部が多孔質のため、衝撃が加わった時や持ち運び時の
揺れや振動が少ないので（ダンピング効果）、作業性に
優れる、（３）表面が平滑で緻密な構造のため木製合板
などに比べて本質的に離型性が良好である、（４）吸湿
性・吸水性が無いので、水に濡れても寸法、重量等の変
化がない、という効果も期待できる。The mold of the present invention has the above-mentioned lightweight property,
In addition to the advantages of rigidity, toughness, durability, etc. (1) Since it is an integrally molded product, it is easy to assemble by nailing, it is difficult to break, there is no leakage from the gap, (2) Core part is porous Because of its quality, there is little shaking and vibration when shocked or carried (damping effect), and it has excellent workability. (3) Due to its smooth surface and dense structure, compared to wooden plywood, etc. Good releasability, and (4) no hygroscopicity / water absorption, and therefore, the effect that the dimensions, weight, etc. do not change even when wet with water can be expected.
【図１】本発明に係る複合成形品からなるサイディング
ボード用型枠の１例を示す図であり、Ａは斜視図、Ｂは
Ｘ−Ｘ断面図、ＣはＹ−Ｙ断面図、ＤはＺ−Ｚ断面図を
示す。FIG. 1 is a view showing an example of a siding board form frame made of a composite molded article according to the present invention, where A is a perspective view, B is an XX sectional view, C is a YY sectional view, and D is The ZZ sectional view is shown.
【図２】本発明に係る複合成形品からなるコンクリート
打設用型枠の１例を示す図であり、Ａは斜視図、ＢはＸ
−Ｘ断面図、ＣはＹ−Ｙ断面図を示す。FIG. 2 is a view showing an example of a concrete placing form made of a composite molded article according to the present invention, where A is a perspective view and B is X.
-X sectional view, C shows YY sectional view.
【図３】本発明に係る複合成形品からなるサイディング
ボード用型枠の他の例を示す図であり、Ａは斜視図、Ｂ
はＸ−Ｘ断面図、ＣはＹ−Ｙ断面図を示す。FIG. 3 is a view showing another example of the siding board frame made of the composite molded article according to the present invention, in which A is a perspective view and B is a perspective view.
Shows an X-X sectional view, and C shows an YY sectional view.
１：サイディングボード用型枠 ２：板状部 ３：厚み調整用の厚肉部 ４：水抜き用切り込み部 ５：スキン層 ６：多孔質コア層 ７：スキン層 ２１：コンクリート打設用型枠 ２２：板状部 ２３：周囲の枠部分 ２４：裏面補強リブ部 ２５：スキン層 ２６：多孔質コア層 ２７：スキン層 1: Form for siding board 2: Plate-like part 3: Thick part for thickness adjustment 4: Notch for draining water 5: Skin layer 6: Porous core layer 7: Skin layer 21: Concrete pouring formwork 22: Plate-like part 23: Surrounding frame part 24: Back surface reinforcing rib part 25: Skin layer 26: Porous core layer 27: Skin layer
Claims (20)
脂からなる緻密なスキン層の間に軽量充填粒子と硬化樹
脂とからなる多孔質コア層を有するサンドイッチ構造体
であり、かつ型枠全体が一体化した複合成形品で構成さ
れていることを特徴とする型枠。1. At least the plate-like portion is a sandwich structure having a porous core layer made of lightweight filling particles and a cured resin between upper and lower dense skin layers made of fiber reinforced resin, and the entire formwork. A formwork characterized in that it is composed of a composite molded product that is integrated.
脂からなる緻密なスキン層、軽量充填粒子と硬化樹脂と
からなる多孔質コア層およびこれらの各層間に配置され
た分離膜で構成されたサンドイッチ構造体であり、かつ
型枠全体が一体化した複合成形品で構成されていること
を特徴とする型枠。2. At least the plate-shaped portion is composed of a dense skin layer composed of upper and lower fiber-reinforced resin, a porous core layer composed of lightweight filling particles and a cured resin, and a separation membrane arranged between these layers. A formwork which is a sandwich structure and is composed of a composite molded product in which the entire formwork is integrated.
ン層と同じ樹脂を含む繊維強化樹脂からなる肉厚部を設
けたことを特徴とする請求項１または請求項２に記載の
型枠。3. The thick portion made of a fiber-reinforced resin containing the same resin as the skin layer is provided at a part or the whole of the periphery of the plate-like portion, according to claim 1 or 2. Formwork.
を少なくとも１個設けたことを特徴とする請求項１、請
求項２または請求項３に記載の型枠。4. The mold according to claim 1, wherein at least one reinforcing rib is provided on the front surface or the back surface of the plate-shaped portion.
コア部に、局所的に補強材を内在させたことを特徴とす
る請求項１〜請求項４のいずれかに記載の型枠。5. The mold according to any one of claims 1 to 4, wherein a reinforcing material is locally incorporated in the core portion of the sandwich structure forming the plate-shaped portion.
とも片面に合成樹脂フィルムを積層一体化した請求項１
〜請求項５のいずれかに記載の型枠。6. A synthetic resin film is laminated and integrated on at least one surface of a skin layer made of fiber reinforced resin.
~ The mold according to claim 5.
あり、該板状部を構成するサンドイッチ構造体における
多孔質コア層の厚みがスキン層の厚みの合計に対して１
／２〜５０／１の範囲内にあることを特徴とする請求項
１〜請求項６のいずれかに記載の型枠。7. The thickness of the plate-like portion is in the range of 4 to 20 mm, and the thickness of the porous core layer in the sandwich structure constituting the plate-like portion is 1 with respect to the total thickness of the skin layers.
It exists in the range of / 2-50 / 1, The formwork in any one of the Claims 1-6 characterized by the above-mentioned.
における多孔質コア層の比重が０．３〜０．７の範囲内
にあることを特徴とする請求項１〜請求項７のいずれか
に記載の型枠。8. The specific gravity of the porous core layer in the sandwich structure constituting the plate-like portion is in the range of 0.3 to 0.7, according to any one of claims 1 to 7. Formwork described in.
り、かつ型枠全体の比重が０．５〜１．２の範囲内にあ
ることを特徴とする請求項１〜請求項８のいずれかに記
載の型枠。9. The plate-shaped portion has a specific gravity of 0.5 to 0.9, and the entire mold has a specific gravity of 0.5 to 1.2. The mold according to claim 8.
が、（ア）成形時に熱膨脹させた樹脂粒子、（イ）圧縮
性軽量粒子、および（ウ）剛性軽量粒子からなる群から
選ばれた少なくとも１種の粒子であることを特徴とする
請求項１〜請求項９のいずれかに記載の型枠。10. The lightweight filler particles contained in the porous core layer are selected from the group consisting of (a) resin particles thermally expanded during molding, (a) compressible lightweight particles, and (c) rigid lightweight particles. The mold according to any one of claims 1 to 9, which is at least one kind of particles.
軽量粒子であることを特徴とする請求項１〜１０のいず
れかに記載の型枠。11. The mold according to claim 1, wherein 50% by weight or more of the lightweight filling particles are rigid lightweight particles.
０．７で、かつ平均粒径が０．０１〜２ｍｍの中空粒子
であることを特徴とする請求項１〜請求項１１のいずれ
かに記載の型枠。12. The light weight filler particles have a specific gravity of 0.05 to.
The mold according to any one of claims 1 to 11, which is a hollow particle having a particle size of 0.7 and an average particle size of 0.01 to 2 mm.
含有させたことを特徴とする請求項１〜請求項１２のい
ずれかに記載の型枠。13. The mold according to claim 1, wherein a release agent is applied to or contained in the skin layer.
枠であることを特徴とする請求項１〜請求項１３のいず
れかに記載の型枠。14. The mold according to any one of claims 1 to 13, wherein the mold is a mold for molding a siding board.
ｍで、横方向の長さが縦方向の長さの１／６〜１／２で
あり、かつ厚さが４〜２０ｍｍである板状部の片面の周
囲の少なくとも一部に、厚み調整用の厚肉部を設けたこ
とを特徴とする請求項１４記載の型枠。15. The vertical length is 1000 to 6000 m.
m, the length in the horizontal direction is 1/6 to 1/2 of the length in the vertical direction, and the thickness is adjusted to at least a part of one side of the plate-like portion having a thickness of 4 to 20 mm. 15. The mold according to claim 14, wherein the thick wall portion is provided.
６〜３５ｍｍの高さおよび５〜３０ｍｍの幅を有し、か
つ該厚肉部に２か所以上の水抜き用の切り込み部を設け
たことを請求項１５記載の型枠。16. The thickness adjusting thick portion has a height of 6 to 35 mm and a width of 5 to 30 mm with respect to the plate portion, and the thick portion is used for draining water at two or more locations. The mold according to claim 15, wherein a notch is provided.
ることを特徴とする請求項１〜請求項１３のいずれかに
記載の型枠。17. The formwork according to claim 1, wherein the formwork is a formwork for concrete pouring.
のいずれかに記載の複合成形品からなる型枠を製造する
に際し、（ａ）硬化性樹脂および平均粒径が０．０１〜
２ｍｍの軽量充填粒子および／またはその前駆体粒子を
混合して含粒子樹脂組成物を調製し、（ｂ）上下の強化
用繊維質シートの間に上記含粒子樹脂組成物を層状に供
給して、強化用繊維質シート／含粒子樹脂組成物／強化
用繊維質シートからなる積層体となし、（ｃ）次いで、
上記積層体を、加圧した後または加圧することなく、型
枠成形用の型内にセットし、（ｄ）型内で加熱し、硬化
性樹脂を強化用繊維質シートに浸透させた状態で硬化せ
しめて、複合成形品からなる型枠とする、ことを特徴と
する型枠の製造方法。18. The method according to claim 1 or claims 3 to 16.
(A) The curable resin and the average particle size are 0.01-.
A particle-containing resin composition is prepared by mixing 2 mm lightweight filling particles and / or its precursor particles, and (b) the particle-containing resin composition is supplied in layers between upper and lower reinforcing fibrous sheets. A reinforcing fiber sheet / particle-containing resin composition / reinforcing fiber sheet, (c)
The laminated body is set in a mold for forming a mold after or without being pressed, and (d) is heated in the mold to allow the curable resin to penetrate into the reinforcing fibrous sheet. A method for producing a mold, which comprises curing and forming a mold made of a composite molded product.
載の複合成形品からなる型枠を製造するに際し、（ａ）
硬化性樹脂および平均粒径が０．０１〜２ｍｍの軽量充
填粒子および／またはその前駆体粒子を混合して含粒子
樹脂組成物を調製し、（ｂ）２つの強化用繊維質シート
および２つの分離膜を配置し、その分離膜の内側に上記
含粒子樹脂組成物を層状に供給して、強化用繊維質シー
ト／分離膜／含粒子樹脂組成物／分離膜／強化用繊維質
シートからなる積層体となし、（ｃ）次いで、上記積層
体を、加圧した後または加圧することなく、型枠成形用
の型内にセットし、（ｄ）型内で加熱し、硬化性樹脂を
強化用繊維質シートに浸透させた状態で硬化せしめて、
複合成形品からなる型枠とする、ことを特徴とする型枠
の製造方法。19. When manufacturing a mold made of the composite molded article according to any one of claims 2 to 16, (a)
A curable resin and lightweight filled particles having an average particle size of 0.01 to 2 mm and / or precursor particles thereof are mixed to prepare a particle-containing resin composition, and (b) two reinforcing fibrous sheets and two A separation membrane is arranged, and the above particle-containing resin composition is supplied in layers inside the separation membrane to form a reinforcing fibrous sheet / separation membrane / particle-containing resin composition / separation membrane / reinforcing fibrous sheet. No laminate, (c) then, the laminate is set in a mold for molding a mold after or without being pressed, and (d) is heated in the mold to strengthen the curable resin. Cure in a state that it has penetrated into the fibrous sheet for
A method of manufacturing a mold, comprising: a mold made of a composite molded product.
化用繊維質シートの表面に局所的に強化材含有硬化性樹
脂を配置して肉厚部を有する複合成形品を成形する請求
項１８または請求項１９に記載の型枠の製造方法。20. A composite molded article having a thick portion is formed by locally disposing a reinforcing material-containing curable resin on the surface of at least one reinforcing fibrous sheet constituting the plate-shaped portion. A method for manufacturing a mold according to claim 19.