JPH0961643A - Wide band plastic clad optical fiber and optical fiber cord with connector - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a plastic clad optical fiber of a step index type which has excellent handling quality, workability, easy connector connectability (press bondability), inexpensiveness and coupling property and has a transmission band as wide as 10 to 50MHz.km or above. SOLUTION: This wide band plastic clad optical fiber consists of a core consisting of quartz and a clad composed of a polymer disposed in tight contact with the outer periphery of this core. The refractive index (nc1 ) of the clad and the refractive index (nco ) of the core satisfy 0.25<=(nco <2> -nc1 <2> )<1/2> <=0.34. The clad consists of a fluorine (meth)acrylate resin which has Shore hardness of >=D60 and a coefft. of thermal expansion of 1.0×10<-4> to 2.0×10<-4> at ordinary temp. and is cured by UV rays.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、中距離、短距離範
囲内における高速で大容量のデータリンク等のＬＡＮ
（ローカルエリアネットワーク）を構築するために好適
な広帯域プラスチッククラッド光ファイバに関するもの
である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a LAN such as a high-speed and large-capacity data link in a medium-range or short-range range.
The present invention relates to a broadband plastic clad optical fiber suitable for constructing (local area network).

【０００２】[0002]

【従来の技術】芯（コア）が石英から成り、鞘（クラッ
ド）がプラスチックから成るステップインデックス型プ
ラスチッククラッド光ファイバ（以後、ＰＣＦと称す
る）は、比較的安価で、プラスチック光ファイバと比較
して透光性に優れ、受発光素子との結合性が良好（開口
数０．３７〜０．４０の高開口数）で、しかも取扱性に
優れていることから、中・短距離伝送用光ファイバやラ
イトガイドとして使用されている。2. Description of the Related Art A step index type plastic clad optical fiber (hereinafter referred to as PCF) whose core is made of quartz and whose sheath (clad) is made of plastic is relatively inexpensive and has a relatively low cost. An optical fiber for medium / short-distance transmission because it has excellent translucency, good coupling with a light emitting / receiving element (high numerical aperture of 0.37 to 0.40), and excellent handleability. It is also used as a light guide.

【０００３】例えば、特開平５−２７１３５０号公報に
記載された、コアが純粋石英、クラッドが紫外線硬化型
フッ素樹脂からなるＰＣＦは、機器内、機器間、移動体
通信やビル内通信等に使用が可能である。さらに、この
ＰＣＦにおいては硬度の高いフッ素系樹脂がクラッド材
として使用され、圧着コネクタの使用を可能ならしめ、
コネクタ接続を含む現場施工性にも優れている。For example, a PCF having a core made of pure quartz and a clad made of an ultraviolet-curable fluororesin described in Japanese Patent Application Laid-Open No. 5-271350 is used for communication in equipment, between equipment, mobile communication, and building communication. Is possible. Further, in this PCF, a fluorine resin with high hardness is used as a clad material, which enables the use of a crimp connector,
Excellent workability on site including connector connection.

【０００４】[0004]

【発明が解決しようとする課題】しかしながら、これら
従来のＰＣＦは、ハンドリング性、加工性、簡易コネク
タ接続（圧着）、低価格性及び結合性に優れているもの
の、開口数（ＮＡ）が０．３７〜０．４０のように高い
ので伝送帯域が狭く、その結果、広帯域の情報伝送方式
であるＡＴＭ−ＬＡＮや高速イーサネットなどには十分
に適用できないという問題があった。However, although these conventional PCFs are excellent in handleability, workability, simple connector connection (crimping), low cost and bondability, they have a numerical aperture (NA) of 0. Since it is as high as 37 to 0.40, the transmission band is narrow, and as a result, there is a problem that it cannot be sufficiently applied to the broadband information transmission system such as ATM-LAN and high-speed Ethernet.

【０００５】また、高速伝送用として、従来より知られ
ている石英系屈折率分布型やシングルモード型の光ファ
イバは、加工性、コネクタ接続作業が面倒で、価格にお
いても満足できないものであった。Further, conventionally known silica-based graded index or single mode type optical fibers for high-speed transmission are unsatisfactory in terms of workability and connector connection work, and cost. .

【０００６】そこで、本発明は、さらに圧着コネクタ取
り付け及び加工に伴うコネクタ部での長期信頼性を付与
した広帯域ＰＣＦを提供することを目的とする。Therefore, it is an object of the present invention to provide a broadband PCF having long-term reliability in the connector portion accompanying the crimping connector mounting and processing.

【０００７】[0007]

【課題を解決するための手段】この目的を達成するた
め、本発明のＰＣＦは、石英からなるコア、該コアの外
周に密着して設けられたポリマで構成されるクラッドか
らなるプラスチッククラッド光ファイバであって、前記
クラッドの屈折率（ｎ_cl）と前記コアの屈折率（ｎ_co）
とが、 ０．２５≦（ｎ_co ² −ｎ_cl ² ）^1/2 ≦０．３４ を満足し、かつ、前記クラッドがショア硬度Ｄ６０以
上、及び、常温での線膨脹係数１．０×１０^-4〜２．０
×１０^-4を有する紫外線硬化された弗素系（メタ）アク
リレート系樹脂からなることを特徴とする。In order to achieve this object, the PCF of the present invention is a plastic clad optical fiber comprising a core made of quartz and a clad made of a polymer closely attached to the outer periphery of the core. And the refractive index of the clad (n _cl ) and the refractive index of the core (n _co ).
And 0.25 ≦ (n _co ² −n _cl ² ) ^1/2 ≦ 0.34, and the cladding has a Shore hardness of D60 or more and a linear expansion coefficient of 1.0 × 10 at room temperature. ^{-4 to} 2.0
It is characterized in that it is made of an ultraviolet-cured fluorine-based (meth) acrylate resin having × 10 ⁻⁴ .

【０００８】さらに、そのクラッドは、３０〜４５ｋｇ
／ｍｍ² のヤング率を有することが好ましく、また、そ
のクラッドの厚みは５〜３０μｍであることが好まし
い。Further, the clad has a weight of 30 to 45 kg.
/ Mm ² Young's modulus is preferable, and the thickness of the clad is preferably 5 to 30 μm.

【０００９】そして、本発明の光ファイバは、４００ｋ
ｇ／ｍｍ² 以上のワイブル平均破断強度を有する。The optical fiber of the present invention is 400 k
It has a Weibull average breaking strength of g / mm ² or more.

【００１０】また、本発明のコネクタ付き光ファイコー
ドは、上記した本発明のＰＣＦの外周にポリマ被覆層を
設けてなる光ファイバコード、及び、その片端または両
端に前記ポリマ被覆層を剥しかしめ圧着により取付けら
れたコネクタからなることを特徴とし、そのコネクタ内
部のフェルールからの光ファイバ引き抜き力が２ｋｇ以
上であり、かつ、１．０ｋｇ×１分間の引き抜き力で引
き抜き時のコア・クラッド間のピストニング量が１０μ
ｍ以下とすることができる。The optical fiber cord with a connector of the present invention is an optical fiber cord having a polymer coating layer on the outer periphery of the PCF of the present invention, and the polymer coating layer is peeled off at one or both ends thereof. It is characterized by consisting of a connector attached by crimping, the pulling force of the optical fiber from the ferrule inside the connector is 2 kg or more, and the pulling force of 1.0 kg × 1 minute causes the gap between the core and the clad to be pulled out. Pistoning amount is 10μ
m or less.

【００１１】プラスチッククラッド光ファイバ（ＰＣ
Ｆ）の広帯域化を実現するためには、クラッドの屈折率
（ｎ_cl）と前記コアの屈折率（ｎ_co）とが、 ０．２５≦（ｎ_co ² −ｎ_cl ² ）^1/2 （ｎ_cl）≦０．３４ を満足する水準まで、光ファイバの開口数（ＮＡ）を低
くすることが必要である。 即ち、広帯域の情報伝送方
式における光ファイバとして使用するためには、少なく
ともその帯域が２０〜５０ＭＨｚ・ｋｍであることが必
要であって、従来のステップインデックス型ＰＣＦでは
この帯域水準を満足できないが、開口数（ＮＡ）を前記
水準まで低くすれば、少なくとも２０〜５０ＭＨｚ・ｋ
ｍの帯域水準を満足できる。Plastic clad optical fiber (PC
In order to realize the wide band of F), the refractive index (n _cl ) of the cladding and the refractive index (n _co ) of the core are 0.25 ≦ (n _co ² −n _cl ² ) ^1/2 ( It is necessary to reduce the numerical aperture (NA) of the optical fiber to a level that satisfies n _cl ) ≦ 0.34. That is, in order to use as an optical fiber in a broadband information transmission system, at least the band must be 20 to 50 MHz · km, and the conventional step index type PCF cannot satisfy this band level. If the numerical aperture (NA) is lowered to the above level, at least 20 to 50 MHz · k
The band level of m can be satisfied.

【００１２】そのためには、例えば、石英コアの屈折率
が１．４５８の場合、クラッドの屈折率が１．４１８〜
１．４３６となるように、従来と比べ比較的高屈折率の
ポリマをクラッドに使用すればよい。To this end, for example, when the refractive index of the quartz core is 1.458, the refractive index of the cladding is 1.418 to.
A polymer having a relatively high refractive index as compared with the conventional one may be used for the clad so that it becomes 1.436.

【００１３】一般に、帯域を広げるためには開口数（Ｎ
Ａ）は低いほど好適であるが、逆に、開口数を低くする
と光ファイバを曲げた時の透光損失増加が大きくなるの
で、曲げた時の透光損失水準を許容範囲内に抑えるため
に、開口数（ＮＡ）は０．２５以上とすることが必要で
ある。即ち、実用上の曲げ損失値（入射ＮＡが０．２
５、フルモード励振条件の光源から３ｍ長の光ファイバ
に光を入射させて測定した曲げ損失値）を０．１ｄＢ以
下の許容範囲内とするためには、０．２５以上のＮＡが
必要である。Generally, the numerical aperture (N
The lower A) is more preferable, but conversely, the lower the numerical aperture, the larger the increase in light transmission loss when the optical fiber is bent. Therefore, in order to keep the light transmission loss level when the fiber is bent within the allowable range. The numerical aperture (NA) needs to be 0.25 or more. That is, a practical bending loss value (incident NA is 0.2
5. A NA of 0.25 or more is required to keep the bending loss value (measured by injecting light into a 3 m long optical fiber from a light source under full mode excitation conditions) within an allowable range of 0.1 dB or less. is there.

【００１４】さらに、本発明の広帯域プラスチッククラ
ッド光ファイバのクラッドポリマは、ショア硬度Ｄ法
（ＡＳＴＭ−Ｄ２２４０）にて６０以上の高硬度を有す
ることが必要である 光ファイバ側面をコネクタフェルールを介して直接かし
めて圧着コネクタを取付ける際に、光ファイバの破断や
クラックによる疲労破断を起こさないためには、クラッ
ドとして、硬度が比較的低い（例えば、ショア硬度Ｄが
５０〜５５程度あるいはそれ以下）ポリマを使用するこ
とが好ましいが、逆に、光ファイバとフェルールのかし
め固着力を十分に高めることができない。Further, the clad polymer of the broadband plastic clad optical fiber of the present invention is required to have a high hardness of 60 or more by the Shore hardness D method (ASTM-D2240). When the crimping connector is directly crimped to mount the optical fiber, a polymer having a relatively low hardness (for example, Shore hardness D of about 50 to 55 or less) is used as a clad so as not to cause a fracture of the optical fiber or a fatigue fracture due to a crack. However, conversely, it is not possible to sufficiently increase the caulking fixing force between the optical fiber and the ferrule.

【００１５】しかし、ショア硬度Ｄが６０以上と高硬度
のポリマをクラッドに使用すると、かしめ応力をポリマ
クラッド部にて十分に受け止めることができるので、強
く固着することができ、しかも光ファイバの破断や疲労
破断に至ることもない。さらに、クラッドポリマのショ
ア硬度Ｄが６０以上であると、光ファイバを切断する際
に、光ファイバに押し当てた切断刃の衝撃伝播がコアま
で到達し石英コアを鏡面を呈した状態でもって切断でき
るという利点があり、光ファイバ切断後の光ファイバ断
面を非常に平滑にでき、研磨工程なしでの接続をも可能
とすることができる。However, when a polymer having a high Shore hardness D of 60 or more is used for the clad, the caulking stress can be sufficiently received by the polymer clad portion, so that the polymer clad can be strongly fixed and the optical fiber can be broken. It does not lead to fatigue fracture. Furthermore, when the shore hardness D of the clad polymer is 60 or more, when the optical fiber is cut, the shock propagation of the cutting blade pressed against the optical fiber reaches the core and cuts the quartz core in a mirror-like state. This has the advantage that the optical fiber cross section after cutting the optical fiber can be made very smooth, and connection without the polishing step is possible.

【００１６】さらに、本発明の光ファイバでは、クラッ
ドポリマの線膨脹係数が常温で１．０×１０^-4〜２．０
×１０^-4であることが必要である。１．０×１０^-4未満
であるとポリマが脆過ぎるので、コアとクラッドの密着
性が良好であっても、熱的ショックや曲げ等による機械
的刺激によってクラッドが剥離し易く、不適当である。
逆に、２．０×１０^-4を越えると、ｄｎ_cl／ｄＴ（クラ
ッドの屈折率の温度係数）がｄρ／ｄＴ（線膨脹係数）
に比例するために、低温域において、クラッドの屈折率
が大きくなって光ファイバのＮＡが大きく低下し、この
結果、低温下での透光損失が極めて大きくなるので、不
適当である。Furthermore, in the optical fiber of the present invention, the coefficient of linear expansion of the cladding polymer is 1.0 × 10 ^{−4 to} 2.0 at room temperature.
It needs to be × 10 ^-4 . If it is less than 1.0 × 10 ⁻⁴ , the polymer is too brittle, so even if the adhesion between the core and the clad is good, the clad is likely to peel off due to mechanical irritation due to thermal shock, bending, etc. is there.
On the other hand, when it exceeds 2.0 × 10 ⁻⁴ , dn _cl / dT (temperature coefficient of refractive index of cladding) is dρ / dT (coefficient of linear expansion).
In the low temperature region, the refractive index of the cladding is large and the NA of the optical fiber is greatly reduced, resulting in an extremely large light transmission loss at low temperatures, which is not suitable.

【００１７】従って、開口数（ＮＡ）を前記した低水準
としても、機械特性と低温特性との両方を満足するＰＣ
Ｆとするためには、クラッドの線膨脹係数を１．０×１
０^-4〜２．０×１０^-4とすることが必要である。Therefore, even if the numerical aperture (NA) is set to the above-mentioned low level, the PC satisfies both the mechanical characteristics and the low temperature characteristics.
To obtain F, the coefficient of linear expansion of the clad is 1.0 × 1
It is necessary to set it to 0 ^{−4 to} 2.0 × 10 ⁻⁴ .

【００１８】また、クラッドポリマは、そのヤング率が
２３℃で３０〜４５ｋｇ／ｍｍ² であることが望まし
い。一般的にクラッド等に使用される紫外線硬化された
弗素系（メタ）アクリレート系樹脂では、硬度が高くな
るほどヤング率が高くなる傾向にある。しかし、高ヤン
グ率の樹脂は伸びにくいので光ファイバを切断する際な
どに欠けが生じ易く、光ファイバ接続時の損失悪化の一
要因となる。従って、上述したようにかしめ特性を良好
とするために高硬度としてもそのヤング率は低い方が好
ましく、接続特性良好な光ファイバを得るためには、ヤ
ング率（２３℃）を３０〜４５ｋｇ／ｍｍ² の水準とす
ることが好ましい。The Young's modulus of the clad polymer is preferably 30 to 45 kg / mm ² at 23 ° C. Generally, in a UV-cured fluorine-based (meth) acrylate-based resin used for a clad or the like, the Young's modulus tends to increase as the hardness increases. However, since a resin having a high Young's modulus is difficult to stretch, it is likely to be chipped when the optical fiber is cut, which is one of the causes of deterioration of loss when connecting the optical fiber. Therefore, as described above, it is preferable that the Young's modulus is low even if the hardness is high in order to improve the crimping property. In order to obtain an optical fiber with good connection properties, the Young's modulus (23 ° C.) is 30 to 45 kg / The level of mm ² is preferable.

【００１９】さらにまた、石英コアの表面に塗布又は含
浸させた後、紫外線を照射することにより重合硬化せし
めてなるクラッドには、屈折率等を所望の値に制御し易
い点等から弗素系（メタ）アクリレート系樹脂を使用す
ればよい。Furthermore, the clad formed by coating or impregnating the surface of the quartz core and then polymerizing and curing by irradiating with ultraviolet rays has a fluorine-based (from the viewpoint that it is easy to control the refractive index etc. to a desired value). A (meth) acrylate resin may be used.

【００２０】又、クラッド層の厚みは５〜３０μｍであ
ることが好ましい。クラッド厚みが５μｍ未満である場
合は、石英コア中を伝播する光がクラッドから外に漏れ
出し易くなるので透光性能が不十分となり易い。逆に３
０μｍを越えると、低温放置した場合のクラッドの収縮
に起因する石英コアのマイクロベンド損が大きくなる等
の問題が生じ易い。The thickness of the clad layer is preferably 5 to 30 μm. If the clad thickness is less than 5 μm, the light propagating in the quartz core is likely to leak out of the clad, so that the light transmitting performance is likely to be insufficient. Conversely 3
If it exceeds 0 μm, problems such as an increase in microbend loss of the quartz core due to shrinkage of the clad when left at a low temperature are likely to occur.

【００２１】[0021]

【発明の実施の形態】本発明において、クラッドをなす
ポリマとして使用される紫外線硬化性の弗素系（メタ）
アクリレート系樹脂としては、例えば、米国特許第４５
１１２０９号明細書に記載されたクラッドポリマ用組成
物の技術を応用し、弗素化アルキル基含有の弗素系（メ
タ）アクリレートの主モノマとアルキル基含有の（メ
タ）アクリレート系の多官能モノマとの組み合わせ及び
それらの混合比率を適正化することによって所望物性と
したポリマが挙げられる。それらのモノマとしては以下
に例示する物が使用できる。BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, a UV-curable fluorine-based (meth) polymer used as a polymer forming a clad.
Examples of acrylate resins include, for example, US Pat. No. 45.
By applying the technique of the composition for clad polymer described in the specification of No. 11209, a main monomer of a fluorinated (meth) acrylate containing a fluorinated alkyl group and a (meth) acrylate-based multifunctional monomer containing an alkyl group are used. A polymer having desired physical properties by optimizing the combination and the mixing ratio thereof can be mentioned. As those monomers, those exemplified below can be used.

【００２２】弗素化アルキル基含有の弗素系（メタ）ア
クリレートとしては、 ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＦ₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＦ₂ ＣＦ₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＦＨＣＦ₃ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ₂ ＣＦＨＣＦ₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＨ₂ ＣＦ₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＦ₂ ＣＦＨＣＦ₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＦ（ＣＦ₃ ）ＣＦ₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ（ＣＦ₃ ）₂ ＣＨ₂ ＝Ｃ（Ｆ）ＣＯＯＣＨ（ＣＦ₃ ）₂ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ（ＣＦ₃ ）₂ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ （ＣＦ₂ ＣＦ₂ ）₃ Ｈ ＣＨ₂ ＝Ｃ（Ｆ）ＣＯＯＣＨ₂ （ＣＦ₂ ＣＦ₂ ）₂ Ｈ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ₂ （ＣＦ₂ ＣＦ₂ ）₂
Ｈ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＦ₂ ＣＦ₂ ＣＦＨＣＦ₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＦ₂ ＣＦ₂ Ｈ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ₂ ＣＦ₂ ＣＦ₂ Ｈ ＣＨ₂ ＝Ｃ（Ｆ）ＣＯＯＣＨ₂ ＣＦ₂ ＣＦ₂ Ｈ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＨ₂ Ｃ₈ Ｆ₁₇ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ₂ ＣＨ₂ Ｃ₈ Ｆ₁₇ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＨ₂ Ｃ₁₂Ｆ₂₅ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ₂ ＣＨ₂ Ｃ₁₂Ｆ₂₅ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＨ₂ Ｃ₁₀Ｆ₂₁ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ₂ ＣＨ₂ Ｃ₁₀Ｆ₂₁ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＨ₂ Ｃ₈ Ｆ₁₃ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ₂ ＣＨ₂ Ｃ₆ Ｆ₁₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＨ₂ Ｃ₄ Ｆ₉ ＣＨ₂ ＝ＣＦＣＯＯＣＨ₂ ＣＨ₂ Ｃ₆ Ｆ₁₃ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ （ＣＨ₂ ）₆ ＣＦ（ＣＦ₃ ）
₂ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ （ＣＨ₂ ）₆ Ｈ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣＨ₂ （ＣＨ₂ ）₈ Ｈ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ （ＣＨ₂ ）₁₀Ｈ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ （ＣＨ₂ ）₁₂Ｈ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ Ｃ（ＯＨ）ＨＣＨ₂ Ｃ₈ Ｆ₁₇ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＨ₂ Ｎ（Ｃ₃ Ｈ₇ ）ＳＯ₂
Ｃ₈ Ｆ₁₇ ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ ＣＨ₂ Ｎ（Ｃ₂ Ｈ₅ ）ＣＯＣ
₇ Ｆ₁₅ ＣＨ₂ ＝ＣＨＣＯＯ（ＣＨ₂ ）₂ （ＣＦ₂ ）₈ ＣＦ（Ｃ
Ｆ₃ ）₂ ＣＨ₂ ＝Ｃ（ＣＨ₂ ＣＨ₂ Ｃ₈ Ｆ₁₇）ＣＯＯＣＨ₂ ＣＨ
₂ Ｃ₈ Ｆ₁₇ が挙げられ、これら弗素系（メタ）アクリレートは、構
造が異なる２種類以上の化合物を混合して使用してもよ
い。Examples of the fluorine-containing (meth) acrylate containing a fluorinated alkyl group include CH ₂ ═CHCOOCH ₂ CF ₃ CH ₂ ═CHCOOCH ₂ CF ₂ CF ₃ CH ₂ ═CHCOOCH ₂ CFHCF ₃ CH ₂ ═C (CH ₃ ) COOCH _{2 CFHCF 3 CH 2 = CHCOOCH 2} CH 2 CF 3 CH 2 = CHCOOCH 2 CF 2 CFHCF 3 CH 2 = CHCOOCH 2 CF (CF 3) CF 3 CH 2 = CHCOOCH (CF 3) 2 CH 2 = C (F) COOCH _{(CF 3) 2 CH 2 =} C (CH 3) COOCH (CF 3) 2 CH 2 = CHCOOCH 2 (CF 2 CF 2) 3 H CH 2 = C (F) COOCH 2 (CF 2 CF 2) 2 H CH ₂ = C (CH ₃ ) COOCH ₂ (CF ₂ CF ₂ ) _{2
H CH 2 = CHCOOCH 2 CF 2} CF 2 CFHCF 3 CH 2 = CHCOOCH 2 CF 2 CF 2 H CH 2 = C (CH 3) COOCH 2 CF 2 CF 2 H CH 2 = C (F) COOCH 2 CF 2 CF 2 _{H CH 2 = CHCOOCH 2 CH 2} C 8 F 17 CH 2 = C (CH 3) COOCH 2 CH 2 C 8 F 17 CH 2 = CHCOOCH 2 CH 2 C 12 F 25 CH 2 = C (CH 3) COOCH 2 CH _{2 C 12 F 25 CH 2 =} CHCOOCH 2 CH 2 C 10 F 21 CH 2 = C (CH 3) COOCH 2 CH 2 C 10 F 21 CH 2 = CHCOOCH 2 CH 2 C 8 F 13 CH 2 = C (CH 3 ) COOCH ₂ CH ₂ C ₆ F ₁₃ CH ₂ ＣＨCHCOOCH ₂ CH ₂ C ₄ F ₉ CH ₂ ＣＦCFCOOCH ₂ CH ₂ C ₆ F ₁₃ CH ₂ ＣＨCHCOOCH ₂ (CH ₂ ) ₆ CF (CF ₃ )
_{2 CH 2 = CHCOOCH 2 (CH} 2) 6 H CH 2 = C (CH 3) COOCH 2 (CH 2) 8 H CH 2 = CHCOOCH 2 (CH 2) 10 H CH 2 = CHCOOCH 2 (CH 2) 12 H _{CH 2 = CHCOOCH 2 C (OH} ) HCH 2 C 8 F 17 CH 2 = CHCOOCH 2 CH 2 N (C 3 H 7) SO 2
_{C 8 F 17 CH 2 = CHCOOCH} 2 CH 2 N (C 2 H 5) COC
₇ F ₁₅ CH ₂ ＣＨCHCOO (CH ₂ ) ₂ (CF ₂ ) ₈ CF (C
_{F 3) 2 CH 2 = C} (CH 2 CH 2 C 8 F 17) COOCH 2 CH
₂ C ₈ F _17. These fluorine-based (meth) acrylates may be used as a mixture of two or more compounds having different structures.

【００２３】また、多官能モノマとしては、 エチレングリコールジ（メタ）アクリレート ジエチレングリコールジ（メタ）アクリレート トリエチレングリコールジ（メタ）アクリレート ポリエチレングリコールジ（メタ）アクリレート（数平
均分子量２００〜１０００） プロピレングリコールジ（メタ）アクリレート ジプロピレングリコールジ（メタ）アクリレート トリプロピレングリコールジ（メタ）アクリレート ポリプロピレングリコールジ（メタ）アクリレート（数
平均分子量２００〜１０００） ネオペンチルグリコールジ（メタ）アクリレート １，３−ブタンジオールジ（メタ）アクリレート １，４−ブタンジオールジ（メタ）アクリレート １，６−ヘキサンジオールジ（メタ）アクリレート ヒドロキシピバリン酸エステルネオペンチルグリコール
ジ（メタ）アクリレート ビスフェノールＡジ（メタ）アクリレート ペンタエリスリトールトリ（メタ）アクリレート ジペンタエリスリトールヘキサ（メタ）アクリレート ペンタエリスリトールテトラ（メタ）アクリレート トリメチロールプロパンジ（メタ）アクリレート ペンタエリスリトールモノヒドロキシペンタ（メタ）ア
クリレート ＣＨ₂ ＝ＣＨＣＯＯＣＨ₂ （Ｃ₂ Ｆ₄ ）₂ ＣＨ₂ ＯＣＯ
ＣＨ＝ＣＨ₂ ＣＨ₂ ＝ＣＨＣＯＯＣ₂ Ｈ₄ （Ｃ₂ Ｆ₄ ）₃ Ｃ₂ Ｈ₄ Ｏ
ＣＯＣＨ＝ＣＨ₂ ＣＨ₂ ＝Ｃ（ＣＨ₃ ）ＣＯＯＣ₂ Ｈ₄ （Ｃ₂ Ｆ₄ ）₃ Ｃ
₂ Ｈ₄ ＯＣＯＣ（ＣＨ₃）＝ＣＨ₂ が挙げられる。As the polyfunctional monomer, ethylene glycol di (meth) acrylate diethylene glycol di (meth) acrylate triethylene glycol di (meth) acrylate polyethylene glycol di (meth) acrylate (number average molecular weight 200 to 1000) propylene glycol di (Meth) acrylate dipropylene glycol di (meth) acrylate tripropylene glycol di (meth) acrylate polypropylene glycol di (meth) acrylate (number average molecular weight 200 to 1000) neopentyl glycol di (meth) acrylate 1,3-butanediol di (Meth) acrylate 1,4-butanediol di (meth) acrylate 1,6-hexanediol di (meth) acrylate hydroxypivalate ester Neopentyl glycol di (meth) acrylate Bisphenol A di (meth) acrylate pentaerythritol tri (meth) acrylate dipentaerythritol hexa (meth) acrylate pentaerythritol tetra (meth) acrylate trimethylolpropane di (meth) acrylate pentaerythritol monohydroxypenta (meth) acrylate _{CH 2 = CHCOOCH 2 (C 2} F 4) 2 CH 2 OCO
CH = CH ₂ CH ₂ = CHCOOC ₂ H ₄ (C ₂ F ₄ ) ₃ C ₂ H ₄ O
_{COCH = CH 2 CH 2 = C} (CH 3) COOC 2 H 4 (C 2 F 4) 3 C
_{2 H 4 OCOC (CH 3)} = CH 2 and the like.

【００２４】本発明で用いるクラッドポリマ用のモノマ
組成物は、石英コアへの表面コーティングの点から、１
０〜２０００ｃｐｓ程度であることが望ましく、常温塗
布の場合には特に１５〜２００ｃｐｓが望ましい。ま
た、そのモノマ組成物は加熱及び冷却によって粘度調整
しながら、石英コアにコーティングしてもよい。The monomer composition for the clad polymer used in the present invention is 1 in terms of surface coating on the quartz core.
It is preferably about 0 to 2000 cps, and particularly preferably 15 to 200 cps when applied at room temperature. Further, the monomer composition may be coated on the quartz core while the viscosity is adjusted by heating and cooling.

【００２５】このモノマ組成物は、前記した弗素アルキ
ル基含有弗素系（メタ）アクリレートの主モノマ、及び
アルキル基含有（メタ）アクリレート系の多官能モノマ
の外に、硬化条件や相溶性等の点で許容される範囲内で
あれば必要に応じて各種の添加剤を含有してもよい。In addition to the above-mentioned main monomer of fluorine-containing (meth) acrylate containing a fluorine alkyl group and polyfunctional monomer containing a (meth) acrylate containing an alkyl group, the monomer composition is characterized in terms of curing conditions and compatibility. If necessary, various additives may be contained as long as they are within the range allowed by.

【００２６】例えば、ヒンダードフェノール系等の抗酸
化剤、耐光性向上剤、石英コアとの密着性及び結合性を
向上させるためのシランカップリング剤、石英コアへの
均一塗布のための消泡剤、レベリング剤、界面活性剤な
ど適宜混合することができる。For example, an antioxidant such as a hindered phenol type, a light resistance improver, a silane coupling agent for improving adhesion and bondability with the quartz core, and defoaming for uniform application to the quartz core. Agents, leveling agents, surfactants and the like can be appropriately mixed.

【００２７】特に、γ−メルカプトトリメトキシシラン
を添加することが望ましい。なぜなら、クラッドのショ
ア硬度をＤ６０以上とすることに加えて、コアとクラッ
ドの密着性を良好にすることができるので、ワイブル平
均破断強度の値を４００ｋｇ／ｍｍ² 以上と高くするこ
とが可能であり、高い強度信頼性が得られるからであ
る。Particularly, it is desirable to add γ-mercaptotrimethoxysilane. This is because the Shore hardness of the clad can be D60 or more and the adhesion between the core and the clad can be improved, so that the Weibull average breaking strength value can be increased to 400 kg / mm ² or more. This is because high strength reliability can be obtained.

【００２８】このワイブル平均破断強度（ワイブル破断
強度の平均値）は次の方法で求められる値である。９ｍ
長の光ファイバサンプルの引っ張り強力（ｋｇ）をｎ＝
１００で測定し、この引っ張り強力をコア断面積で除し
て引っ張り破断強度（ｋｇ／ｍｍ² ）を求める。この引
っ張り破断強度のワイブル分布をとり、このワイブル分
布から６３．２％における累積破断確率を求め、ワイブ
ル平均破断強度（ｋｇ／ｍｍ² ）とする。This Weibull breaking strength (average value of Weibull breaking strength) is a value obtained by the following method. 9m
The tensile strength (kg) of a long optical fiber sample is n =
The tensile strength at 100 is measured, and the tensile strength is divided by the core cross-sectional area to obtain the tensile strength at break (kg / mm ² ). The Weibull distribution of this tensile rupture strength is taken, and the cumulative rupture probability at 63.2% is calculated from this Weibull distribution to obtain the Weibull average rupture strength (kg / mm ² ).

【００２９】また、本発明のＰＣＦをボビンに巻取る際
の張力は２０ｇ以下と低く抑えることが、良好な透光損
失を保持するために望ましい。Further, it is desirable that the tension when the PCF of the present invention is wound on a bobbin is kept as low as 20 g or less in order to maintain good light transmission loss.

【００３０】さらに、本発明のＰＣＦは、その外周にポ
リマ被覆層を設けてなる光ファイバコードとし、このコ
ードの片端または両端におけるポリマ被覆層を剥してか
しめ圧着型コネクタを取り付けることによってコネクタ
付き光ファイコードとすればよい。Further, the PCF of the present invention is an optical fiber cord provided with a polymer coating layer on the outer periphery thereof, and the polymer coating layer at one or both ends of the cord is peeled off and a crimp type connector is attached to the optical fiber cord with a connector. It should be a phicode.

【００３１】本発明によると、このようなコネクタ付き
光ファイコードとしても、コネクタ内部のフェルールか
らの光ファイバ引き抜き力を２ｋｇ以上と高くし、か
つ、１．０ｋｇ×１分間の引き抜き力で引き抜いた時の
コア・クラッド間のピストニング量を１０μｍ以下と小
さくすることができる。According to the present invention, even with such an optical fiber cord with a connector, the pulling force of the optical fiber from the ferrule inside the connector is increased to 2 kg or more and the pulling force is 1.0 kg × 1 minute. At this time, the amount of pistoning between the core and the cladding can be reduced to 10 μm or less.

【００３２】このコネクタ内部のフェルールからの光フ
ァイバ引き抜き力はＪＩＳ・Ｆ０５型のかしめ圧着コネ
クタを光ファイバコードに取り付け、そのコネクタ内部
のフェルールから光ファイバを引き抜く際に要する力を
測定した値であり、フェルール引き抜き力が２ｋｇ未満
であると機器間配線等の施工時にコネクタから光ファイ
バが脱落してしまう危険性があり好ましくない。The pulling force of the optical fiber from the ferrule inside the connector is a value obtained by measuring the force required to pull out the optical fiber from the ferrule inside the connector by attaching a JIS F05 type crimp crimp connector to the optical fiber cord. If the ferrule pulling-out force is less than 2 kg, there is a risk that the optical fiber may drop out from the connector during the wiring between devices, which is not preferable.

【００３３】また、ピストニング量とは、フェルールの
引き抜き力を１．０ｋｇ×１分間とした際の石英コアと
クラッドポリマとの間で生じるピストニング量のことで
あり、ピストニング量が１０μｍ以下であることによっ
てコネクタ接続した際の出射光量すなわち接続効率の高
い光ファイバを得ることがで、本発明の光ファイバの施
工性において、高い長期信頼性が実現できる。The amount of pistening is the amount of pistening generated between the quartz core and the clad polymer when the pulling force of the ferrule is 1.0 kg × 1 minute, and the amount of pistening is 10 μm or less. With this, it is possible to obtain an optical fiber having a high amount of emitted light when the connector is connected, that is, a high connection efficiency, and it is possible to realize high long-term reliability in the workability of the optical fiber of the present invention.

【００３４】本発明の光ファイバにおいて、石英コアの
径は２００μが代表的であるが、これに限定されるもの
ではない。In the optical fiber of the present invention, the diameter of the quartz core is typically 200 μ, but the diameter is not limited to this.

【００３５】かかる光ファイバは、通常の方法によって
製造することができる。つまり、コア材用の石英母材を
火炎研磨もしくはフッ化水素酸により前処理した後、高
周波加熱炉、電気抵抗カーボン炉、もしくは酸水素炎に
て溶融細化し、光ファイバ基体とする。続いて、この光
ファイバ基体を液状のクラッド用モノマ組成物を連続的
に供給するクラッドコーティングダイを通してその組成
物を表面に連続塗布し、必要に応じて溶剤を除去した
後、紫外線を照射して、クラッド層を形成する方法等に
より行なえば良い。Such an optical fiber can be manufactured by a usual method. That is, after the quartz base material for the core material is pre-treated by flame polishing or hydrofluoric acid, it is melted and thinned in a high-frequency heating furnace, an electric resistance carbon furnace, or an oxyhydrogen flame to obtain an optical fiber substrate. Then, the optical fiber substrate is continuously applied to the surface of the optical fiber substrate through a clad coating die for continuously supplying a liquid clad monomer composition, and the solvent is removed if necessary, followed by irradiation with ultraviolet rays. It may be performed by a method of forming a clad layer or the like.

【００３６】本発明の光ファイバクラッド用硬化性組成
物を紫外線照射炉により重合硬化させる際の光源は、例
えば、カーボンアーク、キセノンランプ、中圧水銀
灯、、超高圧水銀灯、無電極ランプ、メタルハライドラ
ンプ等通常市販されている光源を用いればよい。また、
重合の効率を高める点からすると、窒素ガス等の不活性
ガス雰囲気下で照射を行なうことが好ましい。When the curable composition for optical fiber cladding of the present invention is polymerized and cured by an ultraviolet irradiation furnace, the light source is, for example, carbon arc, xenon lamp, medium pressure mercury lamp, ultra high pressure mercury lamp, electrodeless lamp, metal halide lamp. For example, a commercially available light source may be used. Also,
From the viewpoint of increasing the efficiency of polymerization, it is preferable to perform irradiation in an atmosphere of an inert gas such as nitrogen gas.

【００３７】このようにして、コアの外周にクラッド層
が形成されてなる光ファイバは、速度制御されたローラ
を介して引き取られ、必要に応じて保護層機能を有する
樹脂組成物等で被覆された後、巻き取られる。In this way, the optical fiber having the clad layer formed on the outer circumference of the core is taken out through the roller whose speed is controlled, and if necessary, coated with a resin composition having a protective layer function or the like. Then, it is rolled up.

【００３８】[0038]

【実施例】以下の実施例において光ファイバ特性は以下
の方法に基づいて測定した。EXAMPLES Optical fiber characteristics in the following examples were measured by the following methods.

【００３９】曲げ損失（ｄＢ）： ３ｍ長の光ファイバ
に、入射ＮＡが０．２５、フルモード励振条件の光源か
ら光を入射させ、シリコンフォトマル受光素子とを用い
てその透過光量を測定し、初期光量とする。次いで試料
を半径１０ｍｍのマンドレルに１０回巻き付けて透過光
量を測定し、初期光量との差を曲げ損失とする。Bending loss (dB): Light was made incident on a 3 m long optical fiber from a light source having an incident NA of 0.25 and a full mode excitation condition, and the amount of transmitted light was measured using a silicon photomal light receiving element. , And the initial amount of light. Then, the sample is wound 10 times around a mandrel having a radius of 10 mm, the amount of transmitted light is measured, and the difference from the initial amount of light is taken as the bending loss.

【００４０】フェルールかしめ損失（ｄＢ）： 無接
着、無かしめでコネクタを取り付けた試料長３ｍの光フ
ァイバの８５０ｎｍＬＥＤでの透過光量を初期光量とす
る。ついで片端にコネクタをかしめによって取り付け、
その際の透過光量を測定し、初期光量との差をフェルー
ルかしめ損失とする。Ferrule caulking loss (dB): The amount of light transmitted through an 850 nm LED of an optical fiber with a sample length of 3 m, which is attached without adhesion and without caulking, is the initial amount of light. Then attach the connector to one end by caulking,
The amount of transmitted light at that time is measured, and the difference from the initial amount of light is taken as the ferrule caulking loss.

【００４１】低温損失（ｄＢ／ｋｍ）： 長さ１ｋｍの
光ファイバを２５℃、５０％ＲＨの環境下で透過光量を
測定し、次に−６０℃の低温下に放置した時の透過光量
の差から、−６０℃の低温下での透過損失とする。Low temperature loss (dB / km): The amount of transmitted light when an optical fiber having a length of 1 km was measured under the environment of 25 ° C. and 50% RH and then left at a low temperature of −60 ° C. From the difference, the transmission loss at a low temperature of −60 ° C. is used.

【００４２】［実施例１］プラズマ法により合成された
合成石英母材を、酸水素炎による火炎研磨の前処理をし
た後、２２００℃の高純度炭素抵抗発熱型加熱炉に連続
的に供給し、コア径が２００μｍとなるように溶融細化
させ、光ファイバ基体とした。この基体を、トリハイド
ロパーフルオロウンデシルアクリレート、トリメチロー
ルプロパントリアクリレート、γ−メルカプトトリメト
キシシラン及び光増感剤からなるクラッドポリマ用モノ
マ組成物（１８ｃｐｓ）が０．１μｍのフィルタで濾過
して供給されているクラッドコートダイの中を通して、
その組成物を基体の表面に連続的に塗布した後、３６０
ｎｍに中心波長を有する３００Ｗ／インチの無電極ラン
プからの光を照射して硬化させ、ローラで引っ張り、ク
ラッド外径が２２７μｍの光ファイバとして巻き取っ
た。コア・クラッド偏心率は４．０％，また石英コア及
びポリマクラッドの非円率はそれぞれ０．５％、０．８
％と極めて真円度の高い光ファイバであった。またポリ
マクラッドのショアＤ硬度、ヤング率（２３℃）及び線
膨脹係数は、それぞれ、Ｄ６８、３９ｋｇ／ｍｍ² 、
１．９×１０^-4であった。Example 1 A synthetic quartz base material synthesized by a plasma method was pretreated by flame polishing with an oxyhydrogen flame, and then continuously supplied to a high-purity carbon resistance heating furnace at 2200 ° C. Then, the optical fiber substrate was obtained by melting and thinning so that the core diameter was 200 μm. The substrate was filtered with a 0.1 μm filter of a monomer composition (18 cps) for a cladding polymer, which consisted of trihydroperfluoroundecyl acrylate, trimethylolpropane triacrylate, γ-mercaptotrimethoxysilane and a photosensitizer. Through the supplied clad coat die,
After continuously applying the composition to the surface of the substrate, 360
It was irradiated with light from a 300 W / inch electrodeless lamp having a central wavelength of nm to be cured, pulled by a roller, and wound as an optical fiber having a clad outer diameter of 227 μm. The core / clad eccentricity is 4.0%, and the non-circularity of the quartz core and polymer clad is 0.5% and 0.8, respectively.
The optical fiber had a very high circularity of 100%. The Shore D hardness, Young's modulus (23 ° C.) and linear expansion coefficient of the polymer clad are D68, 39 kg / mm ² , respectively.
It was 1.9 × 10 ⁻⁴ .

【００４３】得られた光ファイバの屈折率を測定したと
ころ、石英コア及びポリマクラッドの屈折率がそれぞれ
１．４５８、１．４３０であり、ＮＡ（開口数）は０．
２８であった。また、透光損失（８５０ｎｍ）は３．９
ｄＢ／ｋｍと低く、帯域は３０ＭＨｚ・ｋｍと高く光学
的特性において非常に優れたものであった。When the refractive index of the obtained optical fiber was measured, the refractive indexes of the quartz core and the polymer clad were 1.458 and 1.430, respectively, and the NA (numerical aperture) was 0.
28. The light transmission loss (850 nm) is 3.9.
It was as low as dB / km and the band was as high as 30 MHz · km, which was very excellent in optical characteristics.

【００４４】得られた光ファイバにエチレン・テトラフ
ルオロエチレン共重合体からなるポリマを溶融被覆して
コア・クラッド及び１次被覆層からなる構造のプラスチ
ッククラッド光ファイバを得た。その特性は表１に示す
通りであり、光学特性及び端末加工性、取扱性が極めて
優れていた。The obtained optical fiber was melt-coated with a polymer composed of ethylene / tetrafluoroethylene copolymer to obtain a plastic clad optical fiber having a structure composed of a core / clad and a primary coating layer. The characteristics are as shown in Table 1, and the optical characteristics, terminal processability, and handleability were extremely excellent.

【００４５】［実施例２〜３、比較例１〜４］表１に示
す条件変更を行った以外は、実施例１と同じ条件で広帯
域プラスチッククラッド光ファイバを得て、同様に測定
した。その特性は表１の通りであった。[Examples 2 to 3 and Comparative Examples 1 to 4] Broadband plastic clad optical fibers were obtained under the same conditions as in Example 1 except that the conditions shown in Table 1 were changed, and the same measurements were performed. The characteristics are shown in Table 1.

【００４６】[0046]

【表１】 [Table 1]

【００４７】表１の結果からわかるように、ＮＡを小さ
くすることによって伝送帯域を高めることができるが、
低くし過ぎると曲げ損失が大きくなり過ぎて実用上不適
当となるので、本発明で特定したＮＡの範囲とすること
が必要である。As can be seen from the results of Table 1, the transmission band can be increased by reducing the NA,
If it is set too low, the bending loss becomes too large and it becomes unsuitable for practical use. Therefore, it is necessary to set the range of NA specified in the present invention.

【００４８】また、低温特性、切断端面欠け防止及びか
しめ特性等の点から、１．０×１０^-4〜２．０×１０^-4
の線膨脹係数及びショアＤ硬度６０以上のクラッドポリ
マが必要である。Further, from the viewpoint of low temperature characteristics, prevention of cut end face chipping and crimping characteristics, etc., 1.0 × 10 ^{−4 to} 2.0 × 10 ^−4.
A clad polymer having a linear expansion coefficient and a Shore D hardness of 60 or more is required.

【００４９】[0049]

【発明の効果】伝送帯域を２０〜５０ＭＨｚ・ｋｍある
いはそれ以上のように広くすることができ、中距離、短
距離の光伝送媒体として高速、大容量の光伝送が可能な
ステップインデックス型プラスチッククラッド光ファイ
バが得られる。しかも、コネクタフェルールの引き抜き
力が高く、フェルールかしめ損失が小さく、石英とプラ
スチッククラッドとのピストニング量が小さく、現場施
工性が良好で長期信頼性の良いという優れた特性も兼備
できる。Industrial Applicability The step index type plastic clad capable of widening the transmission band of 20 to 50 MHz · km or more and capable of high-speed and large-capacity optical transmission as an optical transmission medium for medium and short distances. An optical fiber is obtained. Moreover, the connector ferrule has a high pull-out force, a small ferrule caulking loss, a small pistening amount between the quartz and the plastic clad, good on-site workability, and good long-term reliability.

Claims (6)

【特許請求の範囲】[Claims] 【請求項１】 石英からなるコア、及び、該コアの外
周に密着して設けられたポリマで構成されるクラッドか
らなるプラスチッククラッド光ファイバにおいて、前記
クラッドの屈折率（ｎ_cl）と前記コアの屈折率（ｎ_co）
とが、 ０．２５≦（ｎ_co ² −ｎ_cl ² ）^1/2 ≦０．３４ を満足し、かつ、前記クラッドがショア硬度Ｄ６０以
上、及び、常温での線膨脹係数１．０×１０^-4〜２．０
×１０^-4を有する紫外線硬化された弗素系（メタ）アク
リレート系樹脂からなることを特徴とする広帯域プラス
チッククラッド光ファイバ。1. A plastic clad optical fiber comprising a core made of quartz and a clad made of a polymer provided in close contact with the outer periphery of the core, wherein the refractive index (n _cl ) of the clad and the core Refractive index (n _co )
And 0.25 ≦ (n _co ² −n _cl ² ) ^1/2 ≦ 0.34, and the cladding has a Shore hardness of D60 or more and a linear expansion coefficient of 1.0 × 10 at room temperature. ^{-4 to} 2.0
A broadband plastic clad optical fiber comprising an ultraviolet-cured fluorine-based (meth) acrylate-based resin having × 10 ⁻⁴ . 【請求項２】 前記クラッドをなす樹脂の２３℃での
ヤング率が３０〜４５ｋｇ／ｍｍ² であることを特徴と
する請求項１記載の広帯域プラスチッククラッド光ファ
イバ。2. The broadband plastic clad optical fiber according to claim 1, wherein the resin forming the clad has a Young's modulus at 23 ° C. of 30 to 45 kg / mm ² . 【請求項３】 前記クラッドの厚みが５〜３０μｍで
あることを特徴とする請求項１記載の広帯域プラスチッ
ククラッド光ファイバ。3. The broadband plastic clad optical fiber according to claim 1, wherein the clad has a thickness of 5 to 30 μm. 【請求項４】 光ファイバのワイブル平均破断強度が
４００ｋｇ／ｍｍ²以上であることを特徴とする請求項
１記載の広帯域プラスチッククラッド光ファイバ。4. The broadband plastic clad optical fiber according to claim 1, wherein the Weibull average breaking strength of the optical fiber is 400 kg / mm ² or more. 【請求項５】 請求項１記載の広帯域プラスチックク
ラッド光ファイバの外周にポリマ被覆層を設けてなる光
ファイバコード、及び、その片端または両端の前記ポリ
マ被覆層を剥しかしめ圧着により取付けられたコネクタ
からなることを特徴とするコネクタ付き光ファイコー
ド。5. An optical fiber cord in which a polymer coating layer is provided on the outer periphery of the broadband plastic clad optical fiber according to claim 1, and a connector attached by peeling the polymer coating layer at one end or both ends and crimping the polymer coating layer. An optical fiber cord with a connector, which consists of 【請求項６】 コネクタ内部のフェルールからの光フ
ァイバ引き抜き力が２ｋｇ以上であり、かつ、１．０ｋ
ｇ×１分間の引き抜き力で引き抜いた時のコア・クラッ
ド間のピストニング量が１０μｍ以下であることを特徴
とする請求項５記載のコネクタ付き光ファイバコード。6. The pulling force of the optical fiber from the ferrule inside the connector is 2 kg or more, and 1.0 k
6. The optical fiber cord with a connector according to claim 5, wherein the pistening amount between the core and the clad when pulled out with a pulling force of g × 1 minute is 10 μm or less.