JPH09324154A - Moistureproof adhesive tape - Google Patents
Moistureproof adhesive tapeInfo
- Publication number
- JPH09324154A JPH09324154A JP14194996A JP14194996A JPH09324154A JP H09324154 A JPH09324154 A JP H09324154A JP 14194996 A JP14194996 A JP 14194996A JP 14194996 A JP14194996 A JP 14194996A JP H09324154 A JPH09324154 A JP H09324154A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- moisture
- pressure
- adhesive layer
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、基材の片面に粘着
剤層を設けてなる防湿粘着テープに関し、より詳細に
は、例えば建築物の内外の温度差による結露の水分を断
熱材に浸透させないために用いられる住宅建材用防湿粘
着テープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a moisture-proof pressure-sensitive adhesive tape having a pressure-sensitive adhesive layer provided on one surface of a base material, and more specifically, for example, moisture of dew condensation due to temperature difference between inside and outside of a building penetrates into a heat insulating material. The present invention relates to a moisture-proof pressure-sensitive adhesive tape for a house building material, which is used to prevent it.
【０００２】[0002]
【従来の技術】住宅では、断熱機能を持たせるために合
成樹脂発泡体やグラスウールなどからなる断熱材が壁の
内部に配置されている。すなわち、図１に略図的斜視図
で示すように、木枠１に囲まれた空間に合成樹脂発泡体
やグラスウールなどからなる断熱材２が配置されてい
る。また、上記木枠１内に収納された断熱材２は、図２
に断面図で示すように、別の木枠３，４で挟持され、外
壁材５に固定されている。この場合、木枠３，４の外表
面側には、それぞれ、防湿フィルム６及び透湿性もしく
は防湿性フィルム７が貼り付けられている。2. Description of the Related Art In a house, a heat insulating material made of synthetic resin foam, glass wool or the like is arranged inside a wall so as to have a heat insulating function. That is, as shown in a schematic perspective view in FIG. 1, a heat insulating material 2 made of synthetic resin foam or glass wool is arranged in a space surrounded by a wooden frame 1. In addition, the heat insulating material 2 housed in the wooden frame 1 is shown in FIG.
As shown in the sectional view, it is sandwiched between the other wooden frames 3 and 4 and fixed to the outer wall member 5. In this case, the moisture-proof film 6 and the moisture-permeable or moisture-proof film 7 are attached to the outer surface sides of the wooden frames 3 and 4, respectively.
【０００３】断熱材２は、建物内部の室温を保つために
用いられているものであるが、水分を含むとその断熱効
果が極端に低下することが知られている。従って、防湿
フィルム６により、断熱材２への水分の侵入を抑制して
いた。もっとも、外壁材５側においては、外壁材自身で
外部の雨などに起因する水分が遮断されるためさほど問
題とはならない。The heat insulating material 2 is used for keeping the room temperature inside the building, but it is known that the heat insulating effect is extremely lowered when it contains water. Therefore, the moisture-proof film 6 suppresses the entry of moisture into the heat insulating material 2. However, on the side of the outer wall material 5, since the outer wall material itself blocks moisture due to external rain or the like, this is not a serious problem.
【０００４】しかしながら、建物内部と外部との温度差
により、室内側の壁面には結露が生じることがある。結
露が生じると、結露の水分が断熱材２に侵入し、断熱効
果を低下させる。そこで、上記防湿フィルム６が建物の
内壁に貼り合わされている。However, the temperature difference between the inside and the outside of the building may cause dew condensation on the wall surface on the indoor side. When dew condensation occurs, moisture in the dew enters the heat insulating material 2 and reduces the heat insulating effect. Therefore, the moisture-proof film 6 is attached to the inner wall of the building.
【０００５】なお、外壁材５側においては、内部に滞っ
た湿気を外部に逃がすために、フィルム７は透湿性を有
するように構成されることもある。なお、図１及び図２
に示した断熱材２を有する壁面の構造は、あくまでも一
例に過ぎず、従来より種々の方法で断熱材が壁面内に配
置されている。On the side of the outer wall member 5, the film 7 may be constructed to have moisture permeability in order to allow moisture that has accumulated inside to escape to the outside. 1 and 2
The structure of the wall surface having the heat insulating material 2 shown in 1 above is merely an example, and the heat insulating material is arranged in the wall surface by various methods from the related art.
【０００６】ところで、従来、上記防湿フィルム６は、
断熱材２を施工した後に取り付けられていた。しかしな
がら、例えば図２に示した壁面を施工するに際し、断熱
材２及び木枠３，４を施工した後に、防湿フィルム６を
取り付ける場合、防湿フィルム６の施工作業が余分に必
要となり、工程が煩雑であるという問題があった。そこ
で、断熱材２と内側に配置される防湿材とを一体化し、
防湿材を断熱材２と同時に施工する方法が提案されてい
る（特開昭５６−１２２４５２号公報、特開昭６３−２
１２５４３号公報など）。By the way, conventionally, the moisture-proof film 6 is
It was attached after constructing the heat insulating material 2. However, for example, when the moisture barrier film 6 is attached after the heat insulating material 2 and the wooden frames 3 and 4 have been constructed in constructing the wall surface shown in FIG. 2, extra work for constructing the moisture barrier film 6 is required, and the process is complicated. There was a problem that was. Therefore, the heat insulating material 2 and the moistureproof material arranged inside are integrated,
A method of applying a moisture-proof material at the same time as the heat insulating material 2 has been proposed (JP-A-56-122452, JP-A-63-2).
No. 12543).
【０００７】例えば、特開昭５６−１２２４５２号公報
には、断熱材をその両面から合成樹脂フィルムで被覆
し、２枚の合成樹脂フィルムの端縁部分を貼り合わせた
り、ステープルで断熱材にフィルムを固定したりし、少
なくとも一方の合成樹脂フィルムを防湿性とする方法が
開示されている。この方法では、少なくとも片面の合成
樹脂フィルムが防湿性を有するため、上記２枚の合成樹
脂フィルムが断熱材と一体化された構成を、少なくとも
防湿性を有する面を内面となるように施工することによ
り、断熱材と防湿材とを１度の工程で施工することが可
能とされている。For example, in Japanese Unexamined Patent Publication No. 56-122452, a heat insulating material is covered from both sides with a synthetic resin film, and two edges of the synthetic resin film are stuck together, or a film is formed on the heat insulating material by stapling. Is disclosed, and at least one of the synthetic resin films is made moisture-proof. In this method, since the synthetic resin film on at least one surface has moisture resistance, the construction in which the two synthetic resin films are integrated with the heat insulating material is applied so that at least the surface having moisture resistance is the inner surface. As a result, it is possible to apply the heat insulating material and the moistureproof material in a single process.
【０００８】また、断熱材に防湿フィルムを予め接着剤
で貼り合わせておき、防湿フィルムと断熱材とを１度の
工程で施工する方法も用いられている。さらに、特開平
７−２６２１７号公報に開示されているように、断熱材
に合成樹脂フィルムを熱融着させることにより一体化さ
せる方法も提案されている。Further, there is also used a method in which a moisture-proof film is previously attached to the heat insulating material with an adhesive and the moisture-proof film and the heat insulating material are applied in one step. Further, as disclosed in Japanese Patent Application Laid-Open No. 7-26217, there has been proposed a method in which a synthetic resin film is heat-sealed to a heat insulating material so as to be integrated.
【０００９】しかしながら、特開昭５６−１２２４５２
号公報や特開昭６３−２１２５４３号公報に記載の方法
では、２枚の合成樹脂フィルムを端縁部分において貼り
合わせたり、ステープルを用いて固定したりする必要が
あるため、防湿フィルムと断熱材とを一体化する工程が
煩雑であった。However, JP-A-56-122452
In the method disclosed in Japanese Patent Laid-Open No. 63-212543 or Japanese Patent Laid-Open No. 63-212543, it is necessary to bond two synthetic resin films at their edge portions or fix them with staples. The process of integrating and was complicated.
【００１０】また、接着剤を用いて防湿フィルムを断熱
材に貼り合わせる方法では、接着剤に用いられている溶
剤の揮散により、作業環境が悪化し、かつ接着剤が反応
するまでに比較的長い時間を必要とする。Further, in the method of bonding the moisture-proof film to the heat insulating material using the adhesive, the working environment is deteriorated due to the volatilization of the solvent used in the adhesive, and the adhesive takes a relatively long time to react. Need time.
【００１１】さらに、特開平７−２６２１７号公報に記
載のように、断熱材に防湿フィルムを熱融着する方法で
は、熱融着のための装置が必要であり、かつ夏場と冬場
との気温の差などにより条件を一部変更しなければなら
ないなどの問題があった。加えて、熱融着時あるいは運
搬時の衝撃等により、防湿フィルムにピンホールが発生
し、防湿性が低下することもあった。Further, as described in Japanese Patent Application Laid-Open No. 7-26217, the method of heat-sealing the moisture-proof film to the heat insulating material requires a device for heat-sealing and the temperature in summer and winter. There was a problem that some conditions had to be changed due to differences in In addition, a pinhole may be generated in the moisture-proof film due to an impact during heat-sealing or during transportation, and the moisture-proof property may be deteriorated.
【００１２】そこで、従来の防湿フィルムと断熱材とを
一体化する種々の方法の欠点を解消するために、防湿材
として、防湿性フィルム基材の一面に粘着剤層を設けて
なる粘着テープ型のものを用いる方法も提案されてい
る。この場合、フィルム基材を防湿性を有する材料で構
成することにより防湿機能を果たし得るだけでなく、粘
着剤層の粘着力により断熱材を木枠などの外枠に仮固定
する機能も持たせることができる。Therefore, in order to solve the drawbacks of various methods of integrating a conventional moisture-proof film and a heat insulating material, a pressure-sensitive adhesive tape type having a moisture-proof film substrate provided with an adhesive layer on one surface thereof as a moisture-proof material. A method using the above is also proposed. In this case, not only can the film substrate be made of a moisture-proof material to achieve the moisture-proof function, but also the function of temporarily fixing the heat insulating material to the outer frame such as a wooden frame by the adhesive force of the adhesive layer. be able to.
【００１３】しかしながら、上記のように断熱材を外枠
に仮固定する機能をも持たせた場合、防湿性フィルム基
材に粘着剤層を設けてなる粘着テープでは、粘着剤層が
断熱材と直接接着するだけでなく、外枠とも接着するこ
とになる。However, in the case where the heat insulating material also has a function of temporarily fixing it to the outer frame as described above, in a pressure-sensitive adhesive tape having a pressure-sensitive adhesive layer on the moisture-proof film base material, the pressure-sensitive adhesive layer serves as the heat insulating material. Not only will it adhere directly, but it will also adhere to the outer frame.
【００１４】ところが、一般に、外枠は木材で構成され
ていることが多く、その被着面にはかなりの凹凸がある
のが普通である。また、住宅資材のコストダウンによ
り、外枠は、極限まで細くされていることがあり、この
ような場合、外枠の被着面積は非常に小さくなる。従っ
て、これらの種々の要因が相まって、従来の防湿粘着テ
ープでは、外枠に接着するのに十分な接着性を得ること
ができず、次工程まで断熱材を外枠に仮固定する性能を
発揮し得ない場合もあった。However, in general, the outer frame is often made of wood, and the surface to which it is attached usually has considerable irregularities. Further, due to cost reduction of housing materials, the outer frame may be made as thin as possible, and in such a case, the adhered area of the outer frame becomes very small. Therefore, due to these various factors, the conventional moisture-proof pressure-sensitive adhesive tape cannot obtain sufficient adhesiveness to adhere to the outer frame, and exhibits the performance of temporarily fixing the heat insulating material to the outer frame until the next step. In some cases it couldn't be done.
【００１５】[0015]
【発明が解決しようとする課題】本発明の目的は、被着
面にかなりの凹凸が存在したり、あるいは十分な被着面
積を確保し得ないような状況にあっても、防湿性と接着
性の双方の機能を十分に果たし得る防湿粘着テープを提
供することにある。SUMMARY OF THE INVENTION It is an object of the present invention to provide moisture resistance and adhesion even in a situation where there is considerable unevenness on the surface to be adhered or sufficient adhesion area cannot be secured. It is intended to provide a moisture-proof pressure-sensitive adhesive tape that can sufficiently fulfill both functions of sex.
【００１６】[0016]
【課題を解決するための手段】本発明に係る防湿粘着テ
ープは、透湿度が３０ｇ／ｍ2 ・２４時間以下のポリオ
レフィン基材の片面に粘着剤層を設けてなり、少なくと
も幅方向両端近傍において前記粘着剤層の木材に対する
粘着力が０℃で２Ｎ／５０ｍｍ以上であることを特徴と
し、それによって上記課題を達成するものである。A moisture-proof pressure-sensitive adhesive tape according to the present invention comprises a polyolefin base material having a moisture permeability of 30 g / m 2 · 24 hours or less, and an adhesive layer provided on one side thereof, and at least in the vicinity of both ends in the width direction. The adhesive force of the pressure-sensitive adhesive layer with respect to wood is 2 N / 50 mm or more at 0 ° C., thereby achieving the above object.
【００１７】なお、本明細書において、防湿粘着テープ
の幅方向両端近傍の領域とは、対象となる木枠の形状や
寸法によっても異なるが、通常、幅方向端部から内側に
向かって１０〜１００ｍｍの範囲の領域である。In the present specification, the area near both ends in the width direction of the moisture-proof pressure-sensitive adhesive tape varies depending on the shape and size of the target wooden frame, but usually 10 to 10 from the width direction end toward the inside. The area is 100 mm.
【００１８】以下、本発明の詳細を説明する。本発明に
係る防湿粘着テープでは、テープ基材として上記特定の
透湿度を有するポリオレフィン基材が用いられる。この
ポリオレフィン基材としては、ポリプロピレン、ポリエ
チレンなどの適宜のポリオレフィンからなるものを用い
ることができるが、長期間にわたり、結露による水分の
侵入を防止するには、その透湿度は３０ｇ／ｍ2 ・２４
時間以下、好ましくは、１０ｇ／ｍ2 ・２４時間以下と
される。透湿度が３０ｇ／ｍ2 ・２４時間を超えると、
住宅の立地条件にもよるが、５年〜１０年で結露による
水分の吸湿が大きくなり、断熱材の防湿に用いた場合、
断熱材側に水分が侵入し、断熱効果が低下する。Hereinafter, the present invention will be described in detail. In the moisture-proof pressure-sensitive adhesive tape according to the present invention, the polyolefin base material having the above specific moisture permeability is used as the tape base material. As this polyolefin base material, one made of an appropriate polyolefin such as polypropylene or polyethylene can be used, but its moisture permeability is 30 g / m 2 · 24 in order to prevent moisture from entering due to dew condensation over a long period of time.
The time is not more than 10 hours, preferably not more than 10 g / m 2 · 24 hours. When the moisture vapor transmission rate exceeds 30 g / m 2 · 24 hours,
Depending on the location conditions of the house, moisture absorption due to dew condensation increases in 5 to 10 years, and when used as a moisture barrier for heat insulation materials,
Moisture penetrates into the heat insulating material, reducing the heat insulating effect.
【００１９】また、粘着テープは機械を用いて貼付され
るため、長尺状のものであることが好ましい。さらに、
粘着テープの巻重体の幅は、住宅部材とほぼ同じである
ため、ポリオレフィン基材の厚みが厚くなり過ぎると重
量が増加し、専用の運搬機や取付け治具が必要となるこ
とがある。他方、ポリオレフィン基材の厚みが薄くなり
過ぎると、防湿粘着テープを製造するに際し、あるいは
貼付時に基材にシワが生じ易くなったり、加工適性が低
下したりする。従って、ポリオレフィン基材の厚みは、
好ましくは、２０〜８０μｍ程度とされる。Further, since the adhesive tape is attached by using a machine, it is preferable that it is a long tape. further,
Since the width of the roll of the adhesive tape is almost the same as that of the housing member, if the thickness of the polyolefin base material becomes too thick, the weight may increase, and a dedicated carrier or a mounting jig may be required. On the other hand, if the thickness of the polyolefin base material is too thin, wrinkles are likely to occur on the base material during the production or attachment of the moisture-proof pressure-sensitive adhesive tape, or the processability is deteriorated. Therefore, the thickness of the polyolefin substrate is
The thickness is preferably about 20 to 80 μm.
【００２０】なお、上述したように、被着体の表面がか
なりの凹凸を有する木材であることが多いため、ポリオ
レフィン基材としては、腰が弱く、変形に対する追従性
が高いものが好ましいが、上述した透湿度を満たす範囲
で、コストと上記変形に対する追随性の双方を考慮して
ポリオレフィン基材の材質及び厚みを選定することが望
ましい。As described above, since the surface of the adherend is often wood having considerable unevenness, it is preferable that the polyolefin base material has a low rigidity and high followability to deformation. It is desirable to select the material and the thickness of the polyolefin base material in consideration of both the cost and the conformability to the above deformation within a range satisfying the moisture permeability described above.
【００２１】なお、本発明における上記粘着テープ基材
としてのポリオレフィン基材には、必要に応じて、表面
に金属を蒸着したりすることにより、機械的強度向上等
を図ってもよい。The polyolefin base material as the pressure-sensitive adhesive tape base material in the present invention may be improved in mechanical strength by vapor-depositing a metal on the surface, if necessary.
【００２２】本発明に係る防湿粘着テープでは、上記ポ
リオレフィン基材の片面に粘着剤層が設けられている
が、この粘着剤層を構成する粘着剤自体は、特に限定さ
れるものではない。もっとも、被着体が表面に凹凸を有
する木材であることが多いため、木材に接する幅方向両
端近傍部分は、前述したように、０℃において２Ｎ／５
０ｍｍ以上の粘着力を有することが必要である。幅方向
両端部分近傍において、粘着力が２Ｎ／５０ｍｍ未満と
なると、冬期には、防湿粘着テープを貼付するラインを
用いたとしても、木材からなる被着体に十分接着し難く
なり、防湿粘着テープの幅方向端部において浮きが発生
し易くなる。このような浮きが発生すると、次工程のラ
インを停止しなければならないことになり、施工性が大
幅に低下する。In the moisture-proof pressure-sensitive adhesive tape according to the present invention, a pressure-sensitive adhesive layer is provided on one surface of the above-mentioned polyolefin substrate, but the pressure-sensitive adhesive itself constituting this pressure-sensitive adhesive layer is not particularly limited. However, since the adherend is often wood having irregularities on its surface, the portions near both ends in the width direction in contact with the wood are 2 N / 5 at 0 ° C. as described above.
It is necessary to have an adhesive force of 0 mm or more. If the adhesive strength is less than 2 N / 50 mm in the vicinity of both ends in the width direction, it will be difficult to sufficiently adhere to the adherend made of wood even in the winter, even if a line for attaching the moisture-proof adhesive tape is used. Floats are likely to occur at the widthwise end portions of the. When such floating occurs, the line of the next process must be stopped, and the workability is significantly reduced.
【００２３】また、粘着剤を発泡させることが好まし
く、気泡を有する粘着剤層を構成した場合、木材表面の
ような凹凸を有する面に対する接着面積を増大させるこ
とができ、凹凸を有する被着面により確実に接着させる
ことができる。Further, it is preferable to foam the pressure-sensitive adhesive, and when the pressure-sensitive adhesive layer having bubbles is formed, the adhesion area to a surface having unevenness such as a wood surface can be increased, and an adherend surface having unevenness can be obtained. Can be surely adhered.
【００２４】また、本発明に係る防湿粘着テープは、木
枠などの外枠に接着されるだけでなく、断熱材を仮固定
する機能も果たすものであることが望ましい。従って、
好ましくは、幅方向両端だけでなく、粘着剤層はポリオ
レフィン基材の幅方向全領域にわたって設けられている
ことが望ましい。It is desirable that the moisture-proof pressure-sensitive adhesive tape according to the present invention not only adheres to an outer frame such as a wooden frame but also has a function of temporarily fixing a heat insulating material. Therefore,
It is preferable that the pressure-sensitive adhesive layer is provided not only on both ends in the width direction but also over the entire area in the width direction of the polyolefin substrate.
【００２５】もっとも、本発明の防湿粘着テープにおい
て、粘着剤層を設ける領域や粘着剤層の構造については
種々変形し得る。これを、図３〜図５を参照して説明す
る。図３は、ポリオレフィン基材１１の片面の全面に粘
着剤層１２を設けた例を示し、この場合には、粘着剤層
１２が、０℃で２Ｎ／５０ｍｍ以上の粘着力を有するよ
うに構成される。However, in the moisture-proof pressure-sensitive adhesive tape of the present invention, the region where the pressure-sensitive adhesive layer is provided and the structure of the pressure-sensitive adhesive layer can be variously modified. This will be described with reference to FIGS. FIG. 3 shows an example in which the pressure-sensitive adhesive layer 12 is provided on the entire surface of one side of the polyolefin base material 11. In this case, the pressure-sensitive adhesive layer 12 has a pressure-sensitive adhesive force of 2 N / 50 mm or more at 0 ° C. To be done.
【００２６】図４は、本発明に係る防湿粘着テープの他
の例を示す断面図である。ここでは、ポリオレフィン基
材１１の片面に、全面に粘着剤層１３が形成されてお
り、該粘着剤層１３上に、さらに幅方向両端近傍の領域
において粘着剤層１４，１５が形成されている。この場
合、粘着剤層１４，１５が、０℃で２Ｎ／５０ｍｍ以上
の粘着力を有するように構成されることが必要である。
粘着剤層１３の粘着力については、上記粘着力と同等で
あってもよく、あるいは該粘着力よりも低くとも高くと
もよい。FIG. 4 is a sectional view showing another example of the moisture-proof adhesive tape according to the present invention. Here, the pressure-sensitive adhesive layer 13 is formed on the entire surface of one side of the polyolefin substrate 11, and the pressure-sensitive adhesive layers 14 and 15 are further formed on the pressure-sensitive adhesive layer 13 in regions near both ends in the width direction. . In this case, it is necessary that the pressure-sensitive adhesive layers 14 and 15 are configured to have a pressure-sensitive adhesive force of 2 N / 50 mm or more at 0 ° C.
The adhesive force of the adhesive layer 13 may be equal to the above adhesive force, or may be lower or higher than the adhesive force.
【００２７】図５は、本発明に係る防湿粘着テープのさ
らに他の例を示す横断面図である。ここでは、基材１１
の片面に、幅方向全領域に至るように粘着剤層１６が形
成されており、さらに、粘着剤層１６上に複数の粘着剤
層１７，１８，１９，２０が形成されている。粘着剤層
１７〜２０のうち、粘着剤層１７及び粘着剤層２０は、
防湿粘着テープの幅方向両端近傍の領域に形成されてお
り、従って、０℃で２Ｎ／５０ｍｍ以上の粘着力を有す
るように構成される。他の粘着剤層１６，１８，１９に
ついては、粘着剤層１７，２０と同等の粘着力を有する
ように構成してもよく、あるいは粘着剤層１７，２０と
粘着力が異なるように構成されていてもよい。もっと
も、好ましくは、粘着剤層１８，１９は、粘着剤層１
７，２０と同一の粘着剤で構成することにより、粘着剤
層１７〜２０を形成する作業を容易に行うことができ
る。FIG. 5 is a cross-sectional view showing still another example of the moisture-proof pressure-sensitive adhesive tape according to the present invention. Here, the base material 11
The pressure-sensitive adhesive layer 16 is formed on one surface so as to reach the entire region in the width direction, and a plurality of pressure-sensitive adhesive layers 17, 18, 19, 20 are further formed on the pressure-sensitive adhesive layer 16. Of the adhesive layers 17 to 20, the adhesive layer 17 and the adhesive layer 20 are
It is formed in a region near both ends in the width direction of the moisture-proof pressure-sensitive adhesive tape, and thus has a pressure-sensitive adhesive force of 2 N / 50 mm or more at 0 ° C. The other adhesive layers 16, 18 and 19 may be configured to have the same adhesive force as the adhesive layers 17 and 20, or may be configured to have an adhesive force different from that of the adhesive layers 17 and 20. May be. However, preferably, the adhesive layers 18 and 19 are the adhesive layer 1
By using the same pressure-sensitive adhesive as 7 and 20, the work of forming the pressure-sensitive adhesive layers 17 to 20 can be easily performed.
【００２８】また、図４及び図５に示したように、幅方
向両端近傍の領域において、複数層の粘着剤層を形成し
た場合には、粘着剤層の全体としての厚みを厚くするこ
とができ、それによって木材などの凹凸の大きな被着面
に対する接着性を効果的に高め得る。Further, as shown in FIGS. 4 and 5, when a plurality of pressure-sensitive adhesive layers are formed in the regions near both ends in the width direction, the thickness of the pressure-sensitive adhesive layers as a whole may be increased. Therefore, it is possible to effectively enhance the adhesiveness to the adherend surface having large unevenness such as wood.
【００２９】また、図４及び図５に示したように、全面
に形成された粘着剤層１３，１６上に、部分的に粘着剤
層１４，１５，１７〜２０を形成した場合には、粘着テ
ープの幅方向全領域にわたって粘着剤層の厚みは厚くす
る必要はない。従って、コストを低減することができ、
しかも、凹凸の大きな被着面に接着される部分において
は十分な厚みの粘着剤層が形成されているため、木材等
の凹凸の大きな被着面に確実に接着し得る。すなわち、
必要な部分のみ粘着剤層の厚みが厚くされているため、
木材などの凹凸の大きな被着面に対する接着力を低下さ
せることなくコストを低減することができる。Further, as shown in FIGS. 4 and 5, when the pressure-sensitive adhesive layers 14, 15, 17 to 20 are partially formed on the pressure-sensitive adhesive layers 13, 16 formed on the entire surface, It is not necessary to increase the thickness of the pressure-sensitive adhesive layer over the entire widthwise region of the pressure-sensitive adhesive tape. Therefore, the cost can be reduced,
Moreover, since the pressure-sensitive adhesive layer having a sufficient thickness is formed in the portion to be adhered to the large-unevenness adhered surface, it can be surely adhered to the large-unevenly adhered surface such as wood. That is,
Since the thickness of the adhesive layer is increased only in the necessary parts,
The cost can be reduced without lowering the adhesive force with respect to the adherend surface having large irregularities such as wood.
【００３０】また、粘着剤層の厚みについては、上述し
たポリオレフィン基材の厚みとも関連するが、全体とし
て２０〜８０μｍ程度であることが好ましい。粘着剤層
の厚みが２０μｍ未満の場合には、凹凸を有する被着面
に対する十分な接着力を得ることができないことがあ
り、８０μｍを超えると、コストが高くなるだけでなく
全体の厚みバランスがとれなくなり、凹部でシワ入り等
が発生することがあるからである。Further, the thickness of the pressure-sensitive adhesive layer is related to the thickness of the above-mentioned polyolefin base material, but is preferably about 20 to 80 μm as a whole. If the thickness of the pressure-sensitive adhesive layer is less than 20 μm, it may not be possible to obtain sufficient adhesive force to the adherend surface having irregularities, and if it exceeds 80 μm, not only the cost increases but also the overall thickness balance is increased. This is because it may not be removed and wrinkles may occur in the recess.
【００３１】上述したように、本発明に係る防湿粘着テ
ープの粘着剤層を構成する粘着剤については、特に限定
されるものではないが、例えば、スチレン−イソプレン
−スチレンブロック共重合体系の粘着剤が基材に対する
粘着力を確保し易く、上記特定の粘着力を実現し得る配
合の一例を配合例１として示すと以下の通りである。As described above, the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer of the moisture-proof pressure-sensitive adhesive tape according to the present invention is not particularly limited, but for example, a pressure-sensitive adhesive of styrene-isoprene-styrene block copolymer system. The following is an example of a compounding example in which it is easy to secure the adhesive force to the base material and the specific adhesive force can be realized as the compounding example 1.
【００３２】配合例１…スチレン−イソプレン−スチレ
ンブロック共重合体（シェル化学社製、商品名：カリフ
レックスＴＲ１１０７）１００重量部に、石油系粘着付
与樹脂（日本ゼオン社製、商品名：クイントンＡ−１０
０）１００重量部、プロセスオイル（シェル化学社製、
商品名：シェルフレックス３７１Ｎ）８０重量部及び老
化防止剤（チバガイギー社製、商品名：イルガノックス
１０１０）２重量部を配合したもの。Formulation Example 1 100 parts by weight of a styrene-isoprene-styrene block copolymer (manufactured by Shell Chemical Co., trade name: Califlex TR1107) and 100 parts by weight of a petroleum-based tackifying resin (manufactured by Nippon Zeon Co., Ltd., trade name: Quinton A). -10
0) 100 parts by weight, process oil (manufactured by Shell Chemical Co.,
Product name: Shelf Rex 371N) 80 parts by weight and an antioxidant (manufactured by Ciba-Geigy, product name: Irganox 1010) 2 parts by weight.
【００３３】また、図４及び図５に示したように、２Ｎ
／５０ｍｍ以上の粘着力を有する粘着剤層１４，１５，
１７，２０の下地として形成される粘着剤層１３，１６
については、例えば、下記の配合例２，３のような配合
により構成することができる。Further, as shown in FIGS. 4 and 5, 2N
/ Adhesive layers 14, 15 having an adhesive force of 50 mm or more,
Adhesive layer 13, 16 formed as a base of 17, 20
With respect to, for example, it can be constituted by the following formulation examples 2 and 3.
【００３４】配合例２…天然ゴム１００重量部に、石油
系粘着付与樹脂（日本ゼオン社製、商品名：クイントン
Ａ−１００）８０重量部、プロセスオイル（シェル化学
社製、商品名：シェルフレックス３７１Ｎ）１０重量部
及び老化防止剤（チバガイギー社製、商品名：イルガノ
ックス１０１０）２重量部を配合したもの。Blending Example 2 ... 100 parts by weight of natural rubber, 80 parts by weight of a petroleum-based tackifying resin (manufactured by Zeon Corporation, trade name: Quinton A-100), process oil (manufactured by Shell Chemical Co., trade name: Shelf Rex). 371N) 10 parts by weight and 2 parts by weight of an antioxidant (manufactured by Ciba Geigy, trade name: Irganox 1010).
【００３５】配合例３…スチレン−イソプレン−スチレ
ン共重合体（シェル化学社製、商品名：カリフレックス
ＴＲ１１０７）１００重量部に対し、石油系粘着付与樹
脂（日本ゼオン社製、商品名：クイントンＡ−１００）
１３０重量部、プロセスオイル（シェル化学社製、商品
名：シェルフレックス３７１Ｎ）５０重量部及び老化防
止剤（チバガイギー社製、商品名：イルガノックス１０
１０）２重量部を配合したもの。Blending Example 3 ... 100 parts by weight of a styrene-isoprene-styrene copolymer (manufactured by Shell Chemical Co., trade name: Califlex TR1107) to a petroleum-based tackifying resin (manufactured by Nippon Zeon Co., trade name: Quinton A). -100)
130 parts by weight, process oil (manufactured by Shell Chemical Co., Ltd., trade name: Shelf Rex 371N) 50 parts by weight, and antioxidant (manufactured by Ciba-Geigy Co., Ltd., trade name: Irganox 10)
10) Compounding 2 parts by weight.
【００３６】また、上述したように、粘着剤層は発泡さ
れていることが好ましいが、この場合、粘着剤層を発泡
させるには、適宜の方法を採用することができ、熱分解
型発泡剤を用いる方法を好適に用いることができる。す
なわち、熱分解型発泡剤は、加熱により、窒素、二酸化
炭素、水蒸気などの分解ガスを生じ気泡を形成するもの
であるが、粘着剤組成に上記熱分解型発泡剤を混練して
おき加熱することにより、容易に所望の気泡を形成する
ことができる。この場合、気泡は、粘着剤中の総体積の
うち１０〜４０体積％を占めるように形成することが望
ましい。１０体積％未満では、粗面に対する粘着力が低
下することがあり、４０体積％以上では、全体としての
接着力が低下することがある。発泡剤を含有した粘着剤
の組成の一例を、以下に配合例４として挙げる。As described above, it is preferable that the pressure-sensitive adhesive layer is foamed. In this case, an appropriate method can be adopted for foaming the pressure-sensitive adhesive layer. The method using is preferably used. That is, the thermal decomposition type foaming agent is to generate a decomposition gas such as nitrogen, carbon dioxide and water vapor to form bubbles when heated, and the adhesive composition is kneaded and heated. As a result, desired bubbles can be easily formed. In this case, the bubbles are preferably formed so as to occupy 10 to 40% by volume of the total volume of the adhesive. If it is less than 10% by volume, the adhesive force to the rough surface may decrease, and if it is 40% by volume or more, the adhesive force as a whole may decrease. An example of the composition of the pressure-sensitive adhesive containing the foaming agent is given below as Formulation Example 4.
【００３７】配合例４…スチレン−イソプレン−スチレ
ン共重合体１００重量部に、石油系粘着付与樹脂１２０
重量部、石油系オイル６０重量部、老化防止剤２重量部
及び熱分解型発泡剤として、例えば大塚化学社製、商品
名：ユニフォームＡＺ−Ｌを０．５重量部配合したも
の。Blending Example 4 ... 100 parts by weight of styrene-isoprene-styrene copolymer and 120 parts of petroleum-based tackifying resin.
By weight, 60 parts by weight of petroleum-based oil, 2 parts by weight of an anti-aging agent, and 0.5 parts by weight of Uniform Decomposition Agent AZ-L manufactured by Otsuka Chemical Co., Ltd. as a thermal decomposition type foaming agent.
【００３８】用途 本発明に係る防湿粘着テープは、幅方向両端において粗
面に対する接着力が十分な粘着剤層が設けられているた
め、前述した住宅における断熱材を施工する際に防湿粘
着テープとして好適に用い得るものであるが、車両内層
材において断熱材の内面側における結露を防止するため
の用途にも用いることができる。 Applications The moisture-proof pressure-sensitive adhesive tape according to the present invention is provided with a pressure-sensitive adhesive layer having a sufficient adhesive force to a rough surface at both ends in the width direction. Although it can be preferably used, it can also be used for the purpose of preventing dew condensation on the inner surface side of the heat insulating material in the vehicle inner layer material.
【００３９】作用 本発明に係る防湿粘着テープでは、透湿度が３０ｇ／ｍ
2 ・２４時間以下のポリオレフィン基材を用いて構成さ
れているため、内外の温度差による結露からの水分の透
過を確実に防止することができ、しかも、幅方向両端近
傍の領域において、０℃で２Ｎ／５０ｍｍ以上の粘着力
を有するように構成されているため、例えば木枠のよう
に比較的凹凸の大きな被着面に対して確実に接着し得
る。 Action The moisture-proof pressure-sensitive adhesive tape according to the present invention has a moisture permeability of 30 g / m.
Since it is composed of a polyolefin base material for 2 to 24 hours or less, it is possible to reliably prevent the permeation of water due to the dew condensation due to the temperature difference between the inside and the outside, and at 0 ° C in the regions near both ends in the width direction. Since it has a pressure-sensitive adhesive force of 2 N / 50 mm or more, it can be reliably bonded to an adherend having a relatively large unevenness such as a wooden frame.
【００４０】[0040]
【実施例】以下、本発明の非限定的な実施例及び比較例
を挙げることにより、本発明を明らかにする。The present invention will be clarified by the following non-limiting examples and comparative examples.
【００４１】（実施例１）幅９００ｍｍ、厚さ４０μｍ
の延伸ポリプロピレンフィルムを基材として用い、該基
材の全面に下記の配合の粘着剤を４０μｍの厚みとなる
ように塗工し、実施例１の防湿粘着テープを作製した。Example 1 Width 900 mm, Thickness 40 μm
Using the stretched polypropylene film of 1. as a base material, a pressure-sensitive adhesive having the following composition was coated on the entire surface of the base material so as to have a thickness of 40 μm, to prepare a moisture-proof pressure-sensitive adhesive tape of Example 1.
【００４２】粘着剤の配合…スチレン−イソプレン−ス
チレン共重合体１００重量部、石油系粘着付与樹脂１０
０重量部、石油系オイル８０重量部及び老化防止剤２重
量部。Blending of pressure sensitive adhesive: 100 parts by weight of styrene-isoprene-styrene copolymer, petroleum-based tackifying resin 10
0 parts by weight, 80 parts by weight of petroleum oil and 2 parts by weight of antioxidant.
【００４３】（実施例２）幅９００ｍｍ、厚さ４０μｍ
の延伸ポリプロピレンフィルムをポリオレフィン基材と
して用い、この基材の片面の全面に下記の配合の粘着剤
Ａを２０μｍの厚みに塗工した後、幅方向両端からそれ
ぞれ、８０ｍｍの領域に、下記の配合の発泡剤含有粘着
剤Ｂを３０μｍの厚みにさらに塗設し、実施例２の防湿
粘着テープを得た。Example 2 Width 900 mm, Thickness 40 μm
After using the stretched polypropylene film as a polyolefin base material and applying a pressure-sensitive adhesive A having the following composition to a thickness of 20 μm on the entire surface of one side of the base material, the following composition is applied to 80 mm regions from both ends in the width direction. The foaming agent-containing pressure-sensitive adhesive B of Example 1 was further applied to a thickness of 30 μm to obtain a moisture-proof pressure-sensitive adhesive tape of Example 2.
【００４４】粘着剤Ａの配合…天然ゴム１００重量
部、石油系粘着付与樹脂８０重量部、石油系オイル１０
重量部及び老化防止剤２重量部。 粘着剤Ｂの配合…スチレン−イソプレン−スチレン共
重合体１００重量部、石油系粘着付与樹脂１２０重量
部、石油系オイル６０重量部、老化防止剤２重量部及び
発泡剤（大塚化学社製、商品名：ユニフォームＡＺ−
Ｌ）０．３重量部。Blending of Adhesive A: 100 parts by weight of natural rubber, 80 parts by weight of petroleum-based tackifying resin, 10 of petroleum-based oil
Parts by weight and 2 parts by weight of anti-aging agent. Blending of Adhesive B ... 100 parts by weight of styrene-isoprene-styrene copolymer, 120 parts by weight of petroleum-based tackifying resin, 60 parts by weight of petroleum-based oil, 2 parts by weight of antioxidant and foaming agent (manufactured by Otsuka Chemical Co., Ltd., product Name: Uniform AZ-
L) 0.3 parts by weight.
【００４５】（実施例３）幅９００ｍｍ、厚さ２５μｍ
のポリエチレンテレフタレートフィルムを基材として用
い、実施例１で用いたのと同一の粘着剤を厚み２５μｍ
となるように塗工し、実施例３の防湿粘着テープを作製
した。Example 3 Width 900 mm, Thickness 25 μm
Using the same polyethylene terephthalate film as the substrate, the same pressure-sensitive adhesive as used in Example 1 was formed to a thickness of 25 μm.
Was coated so that the moisture-proof pressure-sensitive adhesive tape of Example 3 was produced.
【００４６】（比較例１）幅９００ｍｍ、厚さ５０μｍ
のスチレンフィルムを基材として用い、実施例１で用い
たのと同じ粘着剤を厚さ４０μｍとなるように塗工し、
比較例１の防湿粘着テープを得た。Comparative Example 1 Width 900 mm, Thickness 50 μm
Using the styrene film of No. 1 as a base material, the same adhesive as that used in Example 1 was applied to a thickness of 40 μm,
A moisture-proof pressure-sensitive adhesive tape of Comparative Example 1 was obtained.
【００４７】（比較例２）幅９００ｍｍ、厚さ４０μｍ
の延伸ポリプロピレンフィルムを基材として用い、実施
例２で用いた粘着剤Ｂを全面に厚さ４０μｍとなるよう
に塗工し、比較例２の防湿粘着テープを得た。(Comparative Example 2) width 900 mm, thickness 40 μm
Using the stretched polypropylene film of No. 2 as a base material, the pressure-sensitive adhesive B used in Example 2 was coated on the entire surface so as to have a thickness of 40 μm to obtain a moisture-proof pressure-sensitive adhesive tape of Comparative Example 2.
【００４８】（評価方法） 対木材（ベニヤ板裏面）粘着力の測定…試料片として
平面形状が６０×１５０ｍｍの矩形のベニヤ板と、５０
ｍｍ幅にスリットした防湿粘着テープを０℃の環境で４
時間以上放置する。次に、上記ベニヤ板の裏面に上記防
湿粘着テープを０℃において貼付し、裏面から２ｋｇの
ゴムローラーを１往復させ圧着する。その他の条件につ
いては、ＪＩＳ−Ｚ−０２３７に基づき、１８０度粘着
力を測定した。この対木材粘着力が２Ｎ／５０ｍｍ未満
であると、粘着テープが剥がれ易く、両端の浮きが発生
し、防湿性だけでなく工程のトラブルを引き起こす。(Evaluation method) Adhesive strength measurement against wood (back surface of veneer plate) ... A rectangular veneer plate having a planar shape of 60 × 150 mm as a sample piece, 50
The moisture-proof pressure-sensitive adhesive tape slit to the width of mm is 4
Leave for more than an hour. Next, the moisture-proof pressure-sensitive adhesive tape is attached to the back surface of the veneer plate at 0 ° C., and a 2 kg rubber roller is reciprocated once from the back surface to perform pressure bonding. About other conditions, 180 degree adhesive force was measured based on JIS-Z-0237. When the adhesive force to wood is less than 2 N / 50 mm, the adhesive tape is easily peeled off and the both ends are floated, causing not only moisture resistance but also process troubles.
【００４９】透湿度…ＪＩＳ−Ｚ−０２０８の防湿包
装材料の透湿度試験法（カップ法）に準じて測定する。
一方の空気を相対湿度９０％、他方を相対湿度３０％と
した境界に試料としての基材を配置し、２４時間経過後
に境界を通過する水蒸気の質量（ｇ）を、その試料１ｍ
2 当たりに換算した値を示す。透湿度試験は２５℃及び
４０℃の何れかで行われるが、実施例及び比較例では４
０℃にて透湿度を測定した。Moisture Permeability: Measured according to the moisture permeability test method (cup method) for moisture-proof packaging materials according to JIS-Z-0208.
A base material as a sample is placed at a boundary where one air has a relative humidity of 90% and the other has a relative humidity of 30%, and the mass (g) of water vapor passing through the boundary after 24 hours has passed is 1 m of the sample.
The value converted per 2 is shown. The moisture vapor permeability test is conducted at either 25 ° C. or 40 ° C., but in the examples and comparative examples, it is 4
The moisture permeability was measured at 0 ° C.
【００５０】工程内における端部剥がれトラブル…上
述したように、防湿粘着テープを用い、断熱材及び木枠
に接着する工程を実施し、幅方向両端近傍における粘着
不良によるトラブルの有無を確認した。下記の表１に示
す○印及び×印は、それぞれ、○…良好、×…端部剥が
れトラブルが発生したことを意味する。Edge peeling trouble in the process: As described above, the process of adhering to the heat insulating material and the wooden frame using the moisture-proof pressure-sensitive adhesive tape was carried out, and it was confirmed whether or not there was a trouble due to poor adhesion in the vicinity of both ends in the width direction. The ◯ mark and the X mark shown in Table 1 below mean that ◯ ... Good and X ... Edge peeling troubles occurred, respectively.
【００５１】[0051]
【表１】 [Table 1]
【００５２】表１から明らかなように、比較例１では、
対木材粘着力に優れ、実際の工程における端部剥がれト
ラブルも発生しなかったが、透湿度が１２０ｇ／ｍ2 ・
２４時間と高く、従って十分な防湿機能を果たし得ない
ことがわかる。As is clear from Table 1, in Comparative Example 1,
It has excellent adhesion to wood and did not cause problems such as edge peeling in the actual process, but its water vapor transmission rate is 120 g / m 2 ·
It is as high as 24 hours, and therefore it can be seen that the sufficient moistureproof function cannot be achieved.
【００５３】また、比較例２では、透湿度が５ｇ／ｍ2
・２４時間と低く、十分な防湿機能を有するが、対木材
粘着力が１．５Ｎ／５０ｍｍと低く、従って実際の工程
に用いた場合、防湿粘着テープの幅方向両端近傍で剥が
れが発生し、ステープルを用いて打ち付けないと木枠に
固定することができなかった。従って、生産ラインを停
止しなければならなかった。In Comparative Example 2, the water vapor permeability is 5 g / m 2
-It has a low moisture resistance of 24 hours and has a sufficient moisture-proof function, but has a low adhesive strength to wood of 1.5 N / 50 mm. Therefore, when used in an actual process, peeling occurs near both ends in the width direction of the moisture-proof adhesive tape, It could not be fixed to the crate unless it was struck with staples. Therefore, the production line had to be stopped.
【００５４】これに対して、実施例１〜３では、ポリオ
レフィン基材の透湿度が２５ｇ／ｍ 2 ・２４時間以下と
低く十分な防湿機能を果たすことがわかる。加えて、対
木材粘着力も２．５Ｎ／５０ｍｍ以上と高く、従って実
際に上記工程試験を行ったところ端部剥がれトラブルは
発生しなかった。On the other hand, in Examples 1 to 3, polio was used.
Water vapor permeability of the reffin base material is 25g / m Two・ With 24 hours or less
It can be seen that it has a low and sufficient moisture-proof function. In addition,
The adhesive strength of wood is as high as 2.5N / 50mm or more, so
When the above process test was performed, the edge peeling trouble
Did not occur.
【００５５】[0055]
【発明の効果】以上のように、本発明に係る防湿粘着テ
ープでは、透湿度が３０ｇ／ｍ2 ・２４時間以下のポリ
オレフィン基材の片面に粘着剤層を設けてなり、少なく
とも幅方向両端近傍の領域において対木材粘着力が０℃
で２Ｎ／５０ｍｍ以上とされているので、十分な防湿性
を有するだけでなく、木材に対する十分な粘着性能を有
する。As described above, in the moisture-proof pressure-sensitive adhesive tape according to the present invention, the pressure-sensitive adhesive layer is provided on one side of the polyolefin base material having a moisture permeability of 30 g / m 2 · 24 hours or less, and at least in the vicinity of both ends in the width direction. Adhesion to wood is 0 ℃ in the area of
2N / 50 mm or more, it not only has sufficient moisture resistance but also has sufficient adhesiveness to wood.
【００５６】従って、例えば、住宅における断熱材の結
露による断熱機能の低下を防止するために断熱材の内面
に貼り合わせるのに好適な防湿粘着テープを提供するこ
とができ、本発明に係る防湿粘着テープをこのような用
途に用いることにより、住宅の生産性向上に大きく寄与
することができる。Therefore, for example, it is possible to provide a moisture-proof pressure-sensitive adhesive tape suitable for being attached to the inner surface of the heat insulating material in order to prevent deterioration of the heat insulating function due to dew condensation of the heat insulating material in a house. By using the tape for such an application, it is possible to greatly contribute to the improvement of the productivity of the house.
【図１】従来の住宅建材における断熱材と木枠との関係
を示す略図的斜視図。FIG. 1 is a schematic perspective view showing a relationship between a heat insulating material and a wooden frame in a conventional housing building material.
【図２】従来の住宅における壁面の構造を略図的に示す
断面図。FIG. 2 is a sectional view schematically showing a structure of a wall surface in a conventional house.
【図３】本発明の防湿粘着テープの一例を示す横断面
図。FIG. 3 is a cross-sectional view showing an example of the moisture-proof pressure-sensitive adhesive tape of the present invention.
【図４】本発明に係る防湿粘着テープの他の例を示す横
断面図。FIG. 4 is a cross-sectional view showing another example of the moisture-proof pressure-sensitive adhesive tape according to the present invention.
【図５】本発明の防湿粘着テープのさらに他の例を示す
横断面図。FIG. 5 is a cross-sectional view showing still another example of the moisture-proof pressure-sensitive adhesive tape of the present invention.
１１…ポリオレフィン基材 １２〜２０…粘着剤層 11 ... Polyolefin substrate 12-20 ... Adhesive layer
Claims (1)
ポリオレフィン基材の片面に粘着剤層を設けてなり、少
なくとも幅方向両端近傍において前記粘着剤層の木材に
対する粘着力が０℃で２Ｎ／５０ｍｍ以上であることを
特徴とする防湿粘着テープ。1. A pressure-sensitive adhesive layer is provided on one side of a polyolefin base material having a water vapor permeability of 30 g / m 2 · 24 hours or less, and the pressure-sensitive adhesive force of the pressure-sensitive adhesive layer to wood is 0 ° C. at least near both ends in the width direction. A moisture-proof pressure-sensitive adhesive tape having a thickness of 2 N / 50 mm or more.