JPH09323473A - Decorative material and its manufacture - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a decorative material having a woodgrain style and a flame retardant woodgrain pattern without allergy and a method for manufacturing it. SOLUTION: A substrate treatment layer 7 made of a urethane resin is provided on an inorganic base material 9 made of a calcium silicate plate. A print layer 5 having a woodgrain pattern 50 is provided on the treatment layer. A sealer layer made of a mixture of one or both of a wood flour and a colorant and a sealer resin is preferably provided between the treatment layer and the print layer. The sealer layer made of the colorant and the sealer resin is preferably transparent. The treatment layer preferably contains a wood flour. A clear layer 3 is formed on the print layer, and a lubricant clear layer containing a lubricant is preferably provided on the uppermost surface of the decorative material.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【技術分野】本発明は，木目模様を有する化粧材及びそ
の製造方法に関する。TECHNICAL FIELD The present invention relates to a decorative material having a wood grain pattern and a method for manufacturing the same.

【０００２】[0002]

【従来技術】従来，木目模様を有する化粧材としては，
基材として合板を用いた化粧材，合板又は無機質材
からなる基材に塩化ビニールシートを接着した化粧材，
無機質基材に，天然木材を０．２〜３ｍｍ程度にスラ
イスした突板を接着剤で接着した化粧材，基材とし
て，木材，ベニヤ合板，中質繊維ボード，パーティクル
ボード，ランバーコア合板，ペーパーコアサンドイッチ
合板，ボードコアー合板，塩化ビニール等のプラスチッ
ク板を用いた化粧材がある。2. Description of the Related Art Conventionally, as a decorative material having a wood grain pattern,
A decorative material using plywood as a base material, a decorative material in which a vinyl chloride sheet is bonded to a base material made of plywood or an inorganic material,
A decorative material in which a veneer sliced from natural wood into slices of 0.2 to 3 mm is adhered to an inorganic base material with an adhesive. As a base material, wood, plywood, medium fiber board, particle board, lumber core plywood, paper core sandwich There are decorative materials that use plywood, board core plywood, and plastic plates such as vinyl chloride.

【０００３】[0003]

【解決しようとする課題】しかしながら，上記従来の化
粧材においては，以下の問題がある。の化粧材におい
ては，合板製造時に使用するメラミン系接着剤の残留成
分（ホルマリン）が，アレルギー（アトピー）性皮膚
炎，ぜんそくの原因となるおそれがある。の化粧材に
おいては，接着剤に含まれる成分が，アレルギーの原因
となるおそれがある。また，塩化ビニールシートの可塑
剤成分には，ジブチルフタレート，ジオクチルフタレー
トなどが含まれるが，これらの成分は，アレルギーの原
因，火災時には塩素ガスが発生して窒息の原因となるお
それがある。However, the above-mentioned conventional decorative materials have the following problems. In the cosmetic material, the residual component (formalin) of the melamine-based adhesive used during plywood production may cause allergic (atopic) dermatitis and asthma. In the cosmetic material, the components contained in the adhesive may cause allergies. Further, the plasticizer components of the vinyl chloride sheet include dibutyl phthalate, dioctyl phthalate, etc., but these components may cause allergies and chlorine gas during a fire to cause suffocation.

【０００４】の化粧材においては，接着剤に含まれる
成分が，アレルギーの原因となるおそれがある。また，
世界的な木材資源の減少により将来木材の入手，及び良
質材の安定供給が困難となるおそれがある。の化粧材
においては，木材，各種ボード又は合板は可燃性であ
り，また，プラスチック材は有毒ガスを発生させて燃え
るため，火災時には安全性に問題が生じるおそれがあ
る。In the above cosmetic material, the components contained in the adhesive may cause allergies. Also,
Due to the decrease in global timber resources, it may be difficult to obtain timber and to stably supply high-quality timber in the future. In the decorative material, wood, various boards or plywood is flammable, and the plastic material burns by generating toxic gas, which may cause a safety problem in case of fire.

【０００５】本発明はかかる従来の問題点に鑑み，アレ
ルギーの発生がなく，木目調で，かつ難燃性の，木目模
様を有する化粧材及びその製造方法を提供しようとする
ものである。In view of such conventional problems, the present invention is to provide a decorative material having a wood grain pattern, which is free from allergies, has a wood grain tone, and is flame retardant, and a method for producing the same.

【０００６】[0006]

【課題の解決手段】請求項１の発明は，無機質基材の上
に下地処理層を設け，該下地処理層の上に木目模様の印
刷層を設けてなることを特徴とする化粧材である。According to a first aspect of the present invention, there is provided a cosmetic material comprising an inorganic base material, a base treatment layer provided on the inorganic base material, and a wood grain pattern printed layer provided on the base treatment layer. .

【０００７】本発明の化粧材においては，無機質基材の
表面に下地処理層を設けている。下地処理層は，無機質
基材及び印刷層の双方に対して密着性が高い。そのた
め，下地処理層は，無機質基材と印刷層との間を接着す
る接着層としての役割を果たす。それ故，接着剤を用い
ることなく，化粧材を得ることができる。従って，接着
剤に含まれるアレルギーの原因物質が，化粧材に混入す
るおそれはなく，アレルギー（アトピー）性皮膚炎，ぜ
んそく等の発生のおそれはない。In the decorative material of the present invention, an undercoat layer is provided on the surface of the inorganic base material. The undercoat layer has high adhesion to both the inorganic substrate and the printed layer. Therefore, the base treatment layer serves as an adhesive layer for adhering between the inorganic base material and the print layer. Therefore, a decorative material can be obtained without using an adhesive. Therefore, the allergenic substance contained in the adhesive is not likely to be mixed into the cosmetic material, and there is no possibility of allergic (atopic) dermatitis, asthma, or the like.

【０００８】また，無機質基材と印刷層との間に下地処
理層を設けているため，無機質基材の機械的強度の向上
とアルカリ成分の流出を防止できる。また，天然木が本
来持つ断熱効果と同様の効果を発揮することができる。
また，基材として無機質基材を設けており，無機質基材
は難燃性を有する。そのため，本発明にかかる化粧材は
燃えにくい。Further, since the undercoating layer is provided between the inorganic base material and the printing layer, the mechanical strength of the inorganic base material can be improved and the alkaline component can be prevented from flowing out. In addition, it is possible to exert the same effect as the natural heat insulation effect of natural wood.
Also, an inorganic base material is provided as a base material, and the inorganic base material has flame retardancy. Therefore, the decorative material according to the present invention is difficult to burn.

【０００９】更に，無機質基材の上には，下地処理層を
介在させて，その表面に木目模様を有する印刷層を設け
ている。そのため，表面の木目模様が，内部の下地処理
層及び無機質基材の材質の模様又は色彩と干渉し合っ
て，天然木と同様の材質感，風合いを醸し出す。従っ
て，本発明の化粧材は，天然木風の材質感，風合いがあ
り，表面化粧用の材料として優れている。以上のごと
く，本発明によれば，アレルギーの発生がなく，木目調
で，かつ難燃性の化粧材を提供することができる。Further, a print layer having a grain pattern is provided on the surface of the inorganic base material with an undercoat layer interposed. Therefore, the wood grain pattern on the surface interferes with the pattern or color of the material of the internal base treatment layer and the inorganic base material, and gives the same texture and texture as natural wood. Therefore, the decorative material of the present invention has a natural woody appearance and texture and is excellent as a surface cosmetic material. As described above, according to the present invention, it is possible to provide a flame-retardant cosmetic material that does not cause allergies, has a wood grain tone.

【００１０】次に，請求項２の発明のように，上記無機
質基材は，ケイ酸カルシウム板，パルプセメント板，し
っくいドロマイトプラスター，プレキャストコンクリー
トパネル，セメントモルタル，石膏プラスター，石膏ボ
ード，ＡＬＣパネル（軽量気泡コンクリートパネルを意
味する。），石綿スレート板，ガラス繊維強化コンクリ
ート，石綿セメントケイカル板，木毛・木片セメント
板，及び石綿セメント押出成形板のグループから選ばれ
る１種又は２種以上であることが好ましい。Next, as in the invention of claim 2, the inorganic base material is calcium silicate board, pulp cement board, stucco dolomite plaster, precast concrete panel, cement mortar, gypsum plaster, gypsum board, ALC panel ( Light-weight cellular concrete panel), asbestos slate board, glass fiber reinforced concrete, asbestos cement silica board, wood wool / wood chip cement board, and asbestos cement extruded board. It is preferable.

【００１１】無機質基材は，印刷層及び下地処理層を透
かして，外部から見える。そのため，上記の材質からな
る無機質基材を用いることにより，天然木の持つ材質感
を最も効果的に発揮させることができる。The inorganic substrate is visible from the outside through the printed layer and the undercoat layer. Therefore, by using the inorganic base material made of the above material, the texture of natural wood can be most effectively exhibited.

【００１２】次に，請求項３の発明のように，上記下地
処理層は，ウレタン樹脂，エポキシ樹脂，アクリル樹
脂，アルキッド樹脂，セルロース樹脂，ポリビニールア
ルコール樹脂，及び水性ガラスのグループから選ばれる
１種又は２種以上であることが好ましい。これにより，
天然木が本来持つ断熱効果と同様の断熱効果を，一層効
果的に付与することができる。Next, as in the invention of claim 3, the undercoat layer is selected from the group consisting of urethane resin, epoxy resin, acrylic resin, alkyd resin, cellulose resin, polyvinyl alcohol resin, and water-based glass. It is preferable that there are two or more species. By this,
It is possible to more effectively give the same heat insulating effect as that of natural wood.

【００１３】次に，請求項４の発明のように，上記下地
処理層と印刷層との間には，木粉又は着色剤の一方又は
双方とシーラー用樹脂との混合物よりなるシーラー層を
有することが好ましい。シーラー層は，下地処理層を透
かして，外部から見えることがある。そのため，上記シ
ーラー層を設けることにより，シーラー層の木粉，模
様，色彩等が，下地処理層及び印刷層と相まって，上記
の天然木風の材質感，風合いを更に高めることができ
る。Next, as in the invention of claim 4, a sealer layer made of a mixture of one or both of wood powder and a colorant and a sealer resin is provided between the undercoating layer and the printing layer. It is preferable. The sealer layer may be visible from the outside through the undercoat layer. Therefore, by providing the sealer layer, wood powder, patterns, colors, etc. of the sealer layer, in combination with the base treatment layer and the printing layer, can further enhance the texture and texture of the natural wood look.

【００１４】次に，請求項５の発明のように，上記シー
ラー層は，１〜９０重量％の木粉と，９９〜１０重量％
のシーラー用樹脂とよりなることが好ましい。木粉が１
重量％未満の場合，又はシーラー用樹脂が９９重量％を
越える場合には，天然木の持つ材質感，風合いを損なう
おそれがある。逆に，木粉が９０重量％を越える場合，
又はシーラー用樹脂が１０重量％未満の場合には，無機
質基材と下地処理層との接着性が低下するおそれがあ
る。Next, according to the invention of claim 5, the sealer layer comprises 1 to 90% by weight of wood powder and 99 to 10% by weight.
It is preferable that the resin for a sealer is used. 1 wood flour
If it is less than wt% or if the sealer resin exceeds 99 wt%, the texture and texture of natural wood may be impaired. Conversely, if the wood powder exceeds 90% by weight,
Alternatively, if the sealer resin is less than 10% by weight, the adhesiveness between the inorganic base material and the undercoat layer may be deteriorated.

【００１５】次に，請求項６の発明のように，上記木粉
の粒径は１〜５００μｍであることが好ましい。粒径が
１μｍ未満の場合には，木粉の工場生産が困難となり，
製造コストが高くなるおそれがある。逆に，粒径が５０
０μｍを越える場合には，化粧材が粗くなり，天然木風
の風合いを損なうおそれがある。Next, as in the invention of claim 6, it is preferable that the grain size of the wood flour is 1 to 500 μm. If the particle size is less than 1 μm, it will be difficult to produce wood flour at the factory.
Manufacturing costs may increase. Conversely, if the particle size is 50
If it exceeds 0 μm, the decorative material becomes rough and the texture of natural wood may be impaired.

【００１６】次に，請求項７の発明のように，上記着色
剤とシーラー用樹脂とよりなるシーラー層は，透明であ
ることが好ましい。これにより，下地処理層の上に透明
シーラー層が形成され，下地処理層を透かして，無機質
基材の模様又は色彩と干渉し合って天然木と同様な材質
感，風合いを持つという効果が発揮される。なお，上記
着色剤としては，例えば，顔料又は塗料を用いる。Next, as in the invention of claim 7, it is preferable that the sealer layer comprising the colorant and the sealer resin is transparent. As a result, a transparent sealer layer is formed on the undercoat layer, and through the undercoat layer, the effect of interfering with the pattern or color of the inorganic base material and having the same texture and texture as natural wood is exhibited. To be done. As the colorant, for example, a pigment or paint is used.

【００１７】次に，請求項８の発明のように，上記下地
処理層は，木粉を含有していることが好ましい。これに
より，化粧材の天然木風の風合いを更に高めることがで
きる。特に，上記の請求項７の発明のように上記下地処
理層が透明である場合に，下地処理層に木粉を含有させ
ると，天然木風の風合いを最も効果的に高めることがで
きる。Next, as in the eighth aspect of the present invention, it is preferable that the undercoat layer contains wood powder. This can further enhance the natural woody feel of the decorative material. In particular, when the undercoating layer is transparent as in the case of the invention of claim 7, the wood-like texture can be most effectively enhanced by adding wood powder to the undercoating layer.

【００１８】次に，請求項９の発明のように，上記印刷
層の上には，クリヤー層を設けてなることが好ましい。
これにより，印刷層の表面を保護して，化粧材の天然木
風の風合いを長期間維持させることができる。また，ク
リヤー層は無色透明でもよいが，有色透明でもよい。有
色透明の場合は，印刷層の木目模様に更に天然木風の風
合いを付与することができる。Next, as in the ninth aspect of the invention, it is preferable that a clear layer is provided on the printed layer.
As a result, the surface of the printed layer can be protected and the natural woody texture of the decorative material can be maintained for a long time. The clear layer may be colorless and transparent, or colored and transparent. When it is colored and transparent, a natural wood-like texture can be added to the wood grain pattern of the printed layer.

【００１９】次に，請求項１０の発明のように，上記化
粧材の最表面には，減摩剤を含有する減摩クリヤー層を
有することが好ましい。これにより，化粧材の最表面の
摩耗を抑制でき，化粧材の木目模様を長期間維持させる
ことができる。ここに，上記化粧材の最表面とは，印刷
層の上にクリヤー層を形成した場合にはクリヤー層の表
面を，またクリヤー層を形成しない場合には印刷層の表
面をいう。また，印刷層の表面に上記クリヤー層以外の
被覆層を形成した場合には，該被覆層をいう。Next, as in the tenth aspect of the invention, it is preferable that the outermost surface of the decorative material has an antifriction clear layer containing an antifriction agent. As a result, abrasion of the outermost surface of the decorative material can be suppressed and the grain pattern of the decorative material can be maintained for a long time. Here, the outermost surface of the decorative material means the surface of the clear layer when the clear layer is formed on the print layer, and the surface of the print layer when the clear layer is not formed. Further, when a coating layer other than the above-mentioned clear layer is formed on the surface of the printed layer, it means the coating layer.

【００２０】次に，化粧材を製造する方法としては，例
えば，請求項１１の発明のように，無機質基材の表面に
シーラー用樹脂を塗布し，硬化させて下地処理層を形成
し，その後，該下地処理層の上に木目模様の印刷層を印
刷することを特徴とする化粧材の製造方法がある。Next, as a method for producing a decorative material, for example, as in the invention of claim 11, a sealer resin is applied to the surface of an inorganic base material and cured to form a base treatment layer, and thereafter, There is a method for manufacturing a decorative material, which comprises printing a print layer having a wood pattern on the base treatment layer.

【００２１】これにより，天然木自身が持つ材質感，風
合いと同様の風合いを持つ化粧材を得ることができる。
また，下地処理層は，無機質基材と印刷層との間を接着
する接着層としての役割を果たすため，接着剤を用いる
必要はない。それ故，得られた化粧材は，接着剤に起因
するアレルギーの発生はない。また，基材として無機質
基材を用いているため，難燃性である。As a result, it is possible to obtain a decorative material having a texture and texture similar to that of natural wood itself.
Further, since the base treatment layer serves as an adhesive layer for adhering the inorganic base material and the print layer, it is not necessary to use an adhesive. Therefore, the obtained cosmetic material does not cause allergy due to the adhesive. Moreover, since an inorganic base material is used as the base material, it is flame-retardant.

【００２２】次に，請求項１２の発明のように，上記無
機質基材は，ケイ酸カルシウム板，パルプセメント板，
しっくいドロマイトプラスター，プレキャストコンクリ
ートパネル，セメントモルタル，石膏プラスター，石膏
ボード，ＡＬＣパネル，石綿スレート板，ガラス繊維強
化コンクリート，石綿セメントケイカル板，木毛・木片
セメント板，及び石綿セメント押出成形板のグループか
ら選ばれる１種又は２種以上であることが好ましい。そ
の理由は，請求項２の発明と同様である。Next, as in the invention of claim 12, the inorganic substrate is a calcium silicate board, a pulp cement board,
From the group of stucco dolomite plaster, precast concrete panel, cement mortar, gypsum plaster, gypsum board, ALC panel, asbestos slate board, glass fiber reinforced concrete, asbestos cement calical board, wood wool / wood chip cement board, and asbestos cement extrusion board It is preferable to be one or more selected. The reason is the same as the invention of claim 2.

【００２３】また，請求項１３の発明のように，上記下
地処理層は，ウレタン樹脂，エポキシ樹脂，アクリル樹
脂，アルキッド樹脂，セルロース樹脂，ポリビニールア
ルコール樹脂，及び水性ガラスのグループから選ばれる
１種又は２種以上であることが好ましい。その理由は，
請求項３の発明と同様である。According to the thirteenth aspect of the present invention, the undercoat layer is one selected from the group consisting of urethane resin, epoxy resin, acrylic resin, alkyd resin, cellulose resin, polyvinyl alcohol resin, and aqueous glass. Alternatively, it is preferable that there are two or more kinds. The reason is,
This is similar to the invention of claim 3.

【００２４】また，請求項１４の発明のように，上記下
地処理層を形成した後には，木粉又は着色剤の一方又は
双方とシーラー用樹脂との混合物よりなるシーラー層を
形成し，その後，該シーラー層の表面に上記印刷層を印
刷することが好ましい。その理由は，請求項４の発明と
同様に，更に天然木風の材質感，風合いを化粧材に付与
することができる。Further, as in the invention of claim 14, after forming the undercoat layer, a sealer layer made of a mixture of one or both of wood powder and a coloring agent and a sealer resin is formed, and thereafter, The printing layer is preferably printed on the surface of the sealer layer. The reason is that, similar to the invention of claim 4, the texture and texture of natural wood can be further imparted to the decorative material.

【００２５】次に，請求項１５の発明のように，上記印
刷層の上には，クリヤー層を形成することが好ましい。
これにより，請求項９の発明と同様に，化粧材の天然木
風の風合いを長期間維持させることができる。Next, as in the fifteenth aspect of the invention, it is preferable to form a clear layer on the printed layer.
As a result, similar to the ninth aspect of the invention, the natural woody texture of the decorative material can be maintained for a long period of time.

【００２６】[0026]

【発明の実施の形態】BEST MODE FOR CARRYING OUT THE INVENTION

実施形態例１ 本発明の実施形態例にかかる化粧材について，図１，図
２を用いて説明する。本例の化粧材１１は，図１，図２
に示すごとく，無機質基材９の上に下地処理層７を設け
ている。下地処理層７の上には，木目模様５０を有する
印刷層５を設けている。また，化粧材１１の最表面は，
クリヤー層３により被覆されている。本例において，上
記無機質基材９は厚み３ｍｍの石綿スレート板を，下地
処理層７はウレタン樹脂を用いる。また，クリヤー層３
は，有色透明層である。Embodiment 1 A decorative material according to an embodiment of the present invention will be described with reference to FIGS. 1 and 2. The decorative material 11 of this example is shown in FIGS.
As shown in FIG. 3, the base treatment layer 7 is provided on the inorganic base material 9. A print layer 5 having a grain pattern 50 is provided on the base treatment layer 7. The outermost surface of the decorative material 11 is
It is covered with a clear layer 3. In this example, the inorganic base material 9 is an asbestos slate plate having a thickness of 3 mm, and the base treatment layer 7 is a urethane resin. Also, clear layer 3
Is a colored transparent layer.

【００２７】次に，上記化粧材の製造方法について説明
する。まず，厚み３ｍｍの石綿スレート板を準備し，こ
れを無機質基材９とした。次いで，無機質基材９の表面
に，一液型湿気硬化型ポリウレタン樹脂塗料を塗布し，
硬化させた。これにより，無機質基材９の表面に下地処
理層７を形成した。次に，下地処理層７の表面に，ロー
ラ式の印刷機により，目的の樹種の木目模様を印刷し
て，木目模様５０を有する印刷層５を形成した。Next, a method of manufacturing the above decorative material will be described. First, an asbestos slate plate having a thickness of 3 mm was prepared and used as the inorganic base material 9. Then, a one-component moisture-curing polyurethane resin coating is applied to the surface of the inorganic base material 9,
Cured. Thus, the base treatment layer 7 was formed on the surface of the inorganic base material 9. Next, the grain pattern of the target tree species was printed on the surface of the base treatment layer 7 by a roller type printing machine to form the printed layer 5 having the grain pattern 50.

【００２８】次に，印刷層５の表面に，チーク色，オー
ク色，オールナット色，赤色，青色，黄色，茶色等の顔
料又は染料で着色されたウレタン系，ラッカー系，ポリ
エステル系，エポキシ系，紫外線硬化塗料等を塗布し
て，種々の色調のクリヤー層３を形成した。以上によ
り，上記化粧材が得られた。得られた化粧材は，いずれ
も木目模様を有し，かつ天然木の持つ材質感，風合いを
持った雅趣に富んでいた。また，アレルギーの発生はな
かった。天然木に比べて，燃えにくかった。Next, on the surface of the printed layer 5, urethane type, lacquer type, polyester type, epoxy type colored with a cheek color, oak color, all nut color, red color, blue color, yellow color, brown color or the like is used. Then, a UV curable paint or the like was applied to form the clear layer 3 having various color tones. As described above, the above decorative material was obtained. All of the obtained decorative materials had a wood grain pattern and were rich in elegance with the texture and texture of natural wood. Also, no allergies occurred. It was harder to burn than natural wood.

【００２９】実施形態例２ 本例の化粧材は，図３に示すごとく，下地処理層７と印
刷層５との間に，木粉６１０とシーラー用樹脂との混合
物よりなるシーラー層６１を有している。また，無機質
基材９としては，厚み１２ｍｍのケイ酸カルシウム板を
用いる。その他は，実施形態例１と同様である。Embodiment 2 As shown in FIG. 3, the decorative material of this embodiment has a sealer layer 61 made of a mixture of wood powder 610 and a sealer resin between the undercoating layer 7 and the printing layer 5. are doing. As the inorganic base material 9, a calcium silicate plate having a thickness of 12 mm is used. Others are the same as those in the first embodiment.

【００３０】本例の化粧材１２の製造方法について説明
する。まず，厚み１２ｍｍのケイ酸カルシウム板を準備
し，これを無機質基材９とした。次いで，無機質基材９
の表面に実施形態例１と同様に一液型湿気硬化型ポリウ
レタン樹脂塗料からなる下地処理層７を形成した。A method of manufacturing the decorative material 12 of this example will be described. First, a calcium silicate plate having a thickness of 12 mm was prepared and used as the inorganic base material 9. Then, the inorganic base material 9
A surface treatment layer 7 made of a one-pack type moisture-curable polyurethane resin paint was formed on the surface of the same as in the first embodiment.

【００３１】次いで，杉，米栂，檜等の淡色の木屑を粉
砕して，粒径５〜５０μｍの木粉を得る。次いで，粉砕
した木粉を２０重量％とシーラー用樹脂を８０重量％と
を混合した。この混合物を上記下地処理層７の表面に塗
布し，硬化させた。シーラー用樹脂としては，ポリウレ
タン系樹脂を用いた。これにより，図３に示すごとく，
下地処理層７の表面に，木粉６１０を含有するシーラー
層６１を形成した。その後，シーラー層６１の表面に，
実施形態例１と同様に木目模様の印刷層５およびクリヤ
ー層３を形成して，上記化粧材１２を得た。Next, light-colored wood chips such as cedar, rice stalks, and cypress are crushed to obtain wood powder having a particle size of 5 to 50 μm. Then, 20% by weight of the crushed wood powder and 80% by weight of the resin for sealer were mixed. This mixture was applied to the surface of the undercoat layer 7 and cured. A polyurethane resin was used as the sealer resin. As a result, as shown in FIG.
A sealer layer 61 containing wood powder 610 was formed on the surface of the base treatment layer 7. After that, on the surface of the sealer layer 61,
The printed layer 5 and the clear layer 3 having a wood grain pattern were formed in the same manner as in Example 1 to obtain the decorative material 12.

【００３２】本例の化粧材は，実施形態例１の化粧材よ
りも，更に天然木の持つ材質感，風合いが高かった。こ
れは，印刷層５と下地処理層７との間に，木粉６１０を
含有するシーラー層６１を設けたため，この木粉６１０
が表面の印刷層５の木目模様５０と干渉し合って，天然
木風の風合いに酷似した風合いを醸しだしているためで
あると考えられる。また，実施形態例１と同様の効果を
有する。The decorative material of this example had a higher texture and texture of natural wood than the decorative material of the first embodiment. This is because the sealer layer 61 containing the wood flour 610 was provided between the printing layer 5 and the base treatment layer 7, and thus the wood flour 610
It is thought that this is because the interference with the wood pattern 50 of the printed layer 5 on the surface creates a texture very similar to that of natural wood. Further, it has the same effect as that of the first embodiment.

【００３３】実施形態例３ 本例の化粧材は，図４に示すごとく，シーラー層６２と
して，着色剤６２０をシーラー用樹脂に混合した混合物
を用いた例である。シーラー層６２は，有色透明層であ
る。着色剤６２０は，赤，黄，黒，白，茶等を一色又は
二色以上用いて，木粉と類似した色に配合した特殊顔料
である。シーラー用樹脂はウレタン系樹脂である。その
他は，実施形態例２と同様である。Embodiment 3 As shown in FIG. 4, the decorative material of this embodiment is an example in which a mixture of a colorant 620 and a sealer resin is used as the sealer layer 62. The sealer layer 62 is a colored transparent layer. The colorant 620 is a special pigment in which one color or two or more colors of red, yellow, black, white, brown and the like are used and mixed in a color similar to wood flour. The resin for the sealer is a urethane resin. Others are the same as the second embodiment.

【００３４】本例の化粧材１３の製造方法について説明
する。まず，厚み６ｍｍのケイ酸カルシウム板を準備
し，これを無機質基材９とした。次いで，無機質基材９
の表面に，実施形態例１と同様に一液型湿気硬化型ポリ
ウレタン樹脂塗料を塗布し，硬化させた。A method of manufacturing the decorative material 13 of this example will be described. First, a calcium silicate plate having a thickness of 6 mm was prepared and used as the inorganic base material 9. Then, the inorganic base material 9
The one-component moisture-curable polyurethane resin coating material was applied to the surface of No. 1 and cured in the same manner as in the first embodiment.

【００３５】次いで，特殊顔料１０重量％と，ウレタン
系のシーラー用樹脂９０重量％とを混合した。この混合
物を上記下地処理層７の表面に塗布し，硬化させた。こ
れにより，下地処理層７の表面に，着色剤６２０を含有
するシーラー層６２を形成した。その後，シーラー層６
２の表面に，実施形態例１と同様にして印刷層５及びク
リヤー層３を形成した。これにより，上記化粧材１３を
得た。Next, 10% by weight of the special pigment and 90% by weight of the urethane type sealer resin were mixed. This mixture was applied to the surface of the undercoat layer 7 and cured. As a result, the sealer layer 62 containing the colorant 620 was formed on the surface of the base treatment layer 7. After that, the sealer layer 6
The printing layer 5 and the clear layer 3 were formed on the surface of No. 2 in the same manner as in the first embodiment. As a result, the above decorative material 13 was obtained.

【００３６】得られた化粧材は，実施形態例２と同様に
天然木の持つ材質感，風合いを有していた。これは，着
色剤６２０が実施形態例２の木粉と色が近似しているた
め，実施形態例２と同様の天然木風の風合いを化粧材に
与えることができたためであると考えられる。また，実
施形態例１と同様の効果を得ることができる。The obtained decorative material had the texture and texture of natural wood as in the second embodiment. It is considered that this is because the colorant 620 has a color similar to that of the wood powder of the second embodiment, and thus the natural wood-like texture similar to that of the second embodiment can be given to the decorative material. Further, the same effect as that of the first embodiment can be obtained.

【００３７】実施形態例４ 本例の化粧材は，図５に示すごとく，下地処理層７１が
木粉７１０を含んでいる点が，上記実施形態例１と相違
する。その他は，実施形態例１と同様である。本例の化
粧材は，実施形態例１で用いた一液型湿気硬化型ポリウ
レタン樹脂塗料の中に，木粉を２０重量％含むようにし
て加え，混合する。次いで，この混合物を，無機質基材
９の表面に塗布し，硬化させて，下地処理層７１を形成
する。その後，下地処理層７１の表面に，実施形態例１
と同様にして印刷層５及びクリヤー層３を形成する。こ
れにより，上記化粧材１４を得る。Embodiment 4 The decorative material of this embodiment is different from Embodiment 1 described above in that the undercoating layer 71 contains wood powder 710, as shown in FIG. Others are the same as those in the first embodiment. The decorative material of this example is added to and mixed with the one-pack type moisture-curable polyurethane resin coating used in the first embodiment so as to contain 20% by weight of wood powder. Next, this mixture is applied to the surface of the inorganic base material 9 and cured to form the base treatment layer 71. After that, the first embodiment is formed on the surface of the base treatment layer 71.
The printing layer 5 and the clear layer 3 are formed in the same manner as. Thereby, the decorative material 14 is obtained.

【００３８】得られた化粧材は，実施形態例１の化粧材
と同様の効果を得ることができる。また，下地処理層７
１は木粉７１０を含有しているため，実施形態例２と同
様に印刷層５と下地処理層７１との間に木粉を含有する
シーラー層を設けた場合と同様に，木粉７１０が印刷層
５の木目模様と干渉しあい，天然木風の風合いを更に高
めている。The obtained decorative material can obtain the same effect as the decorative material of the first embodiment. In addition, the base treatment layer 7
Since No. 1 contains wood powder 710, the wood powder 710 is similar to the case where the sealer layer containing wood powder is provided between the printing layer 5 and the base treatment layer 71 as in the second embodiment. Interference with the grain pattern of the printed layer 5 enhances the texture of natural wood.

【００３９】また，実施形態例２のようにシーラー層を
設けなくても，実施形態例２と同様に優れた天然木風の
風合いを有する化粧材を製造できる。従って，本例の化
粧材１４は，実施形態例２よりも製造容易で，かつ，優
れた天然木風の風合いを有している。Even if the sealer layer is not provided as in the second embodiment, it is possible to manufacture a decorative material having an excellent natural wood-like texture as in the second embodiment. Therefore, the decorative material 14 of this example is easier to manufacture than the second embodiment and has an excellent natural wood-like texture.

【００４０】実施形態例５ 本例の化粧材は，図６に示すごとく，クリヤー層３の表
面に減摩剤３１０を含む減摩クリヤー層３１を被覆して
いる。その他は，実施形態例２と同様である。Embodiment 5 In the decorative material of this example, as shown in FIG. 6, the surface of the clear layer 3 is coated with an anti-friction clear layer 31 containing an anti-friction agent 310. Others are the same as the second embodiment.

【００４１】上記化粧材１５を製造するに当たっては，
実施形態例２と同様にして無機質基材９の表面に，下地
処理層７，シーラー層６１，印刷層５，及びクリヤー層
３を形成する。 次いで，アルミナ系減摩剤を１〜５０
重量％混入したウレタン系のトップコート剤を準備す
る。このトップコート剤を，上記クリヤー層３の表面に
塗布して，減摩クリヤー層３１を形成する。これによ
り，上記化粧材１５が得られる。In manufacturing the above decorative material 15,
In the same manner as in the second embodiment, the base treatment layer 7, the sealer layer 61, the printing layer 5, and the clear layer 3 are formed on the surface of the inorganic base material 9. Then, 1-50 alumina lubricant
Prepare a urethane-based top coat agent mixed with wt%. The top coat agent is applied to the surface of the clear layer 3 to form the anti-friction clear layer 31. As a result, the decorative material 15 is obtained.

【００４２】得られた化粧材１５は，耐摩耗性が著しく
高かった。特に，減摩クリヤー層３１が上記減摩剤を１
０重量％以上含む場合には，ＪＡＳ（日本農林規格）耐
摩耗Ａ試験に合格した。また，本例の化粧材は，実施形
態例１の化粧材と同様の効果を得ることができる。The obtained decorative material 15 had extremely high wear resistance. In particular, the anti-friction clear layer 31 contains one of the above-mentioned anti-friction agents.
When the content was 0% by weight or more, it passed the JAS (Japan Agricultural Standards) abrasion resistance A test. Further, the decorative material of this example can obtain the same effect as the decorative material of the first embodiment.

【００４３】[0043]

【発明の効果】本発明によれば，アレルギーの発生がな
く，木目調で，かつ難燃性の，木目模様を有する化粧材
及びその製造方法を提供することができる。According to the present invention, it is possible to provide a decorative material which does not cause allergies, has a wood grain tone, and is flame retardant and has a wood grain pattern, and a method for producing the same.

【図面の簡単な説明】[Brief description of drawings]

【図１】実施形態例１の化粧材の斜視図。FIG. 1 is a perspective view of a decorative material according to a first embodiment.

【図２】実施形態例１の化粧材の断面説明図。FIG. 2 is an explanatory cross-sectional view of the decorative material according to the first embodiment.

【図３】実施形態例２の化粧材の断面説明図。FIG. 3 is an explanatory cross-sectional view of a decorative material according to the second embodiment.

【図４】実施形態例３の化粧材の断面説明図。FIG. 4 is an explanatory cross-sectional view of a decorative material according to the third embodiment.

【図５】実施形態例４の化粧材の断面説明図。FIG. 5 is an explanatory cross-sectional view of the decorative material according to the fourth embodiment.

【図６】実施形態例５の化粧材の断面説明図。FIG. 6 is an explanatory cross-sectional view of a decorative material according to the fifth embodiment.

【符号の説明】[Explanation of symbols]

１１，１２，１３，１４，１５．．．化粧材， ３．．．クリヤー層， ３１．．．減摩クリヤー層， ５．．．印刷層， ５０．．．木目模様， ６１，６２．．．シーラー層， ７，７１．．．下地処理層， ９．．．無機質基材， 11, 12, 13, 14, 15. . . Decorative material, 3. . . Clear layer, 31. . . Anti-friction clear layer, 5. . . Printing layer, 50. . . Wood pattern, 61, 62. . . Sealer layer, 7, 71. . . Base treatment layer, 9. . . Inorganic base material,

Claims (15)

【特許請求の範囲】[Claims] 【請求項１】 無機質基材の上に下地処理層を設け，該
下地処理層の上に木目模様の印刷層を設けてなることを
特徴とする化粧材。1. A decorative material comprising an inorganic base material, a base treatment layer provided on the inorganic base material, and a wood grain pattern printed layer provided on the base treatment layer. 【請求項２】 請求項１において，上記無機質基材は，
ケイ酸カルシウム板，パルプセメント板，しっくいドロ
マイトプラスター，プレキャストコンクリートパネル，
セメントモルタル，石膏プラスター，石膏ボード，ＡＬ
Ｃパネル，石綿スレート板，ガラス繊維強化コンクリー
ト，石綿セメントケイカル板，木毛・木片セメント板，
及び石綿セメント押出成形板のグループから選ばれる１
種又は２種以上であることを特徴とする化粧材。2. The inorganic base material according to claim 1, wherein:
Calcium silicate board, pulp cement board, plaster dolomite plaster, precast concrete panel,
Cement mortar, plaster plaster, plasterboard, AL
C panel, asbestos slate board, glass fiber reinforced concrete, asbestos cement silica board, wood wool / wood chip cement board,
And asbestos-cement extruded board group 1
One or two or more kinds of decorative materials. 【請求項３】 請求項１又は２において，上記下地処理
層は，ウレタン樹脂，エポキシ樹脂，アクリル樹脂，ア
ルキッド樹脂，セルロース樹脂，ポリビニールアルコー
ル樹脂，及び水性ガラスのグループから選ばれる１種又
は２種以上であることを特徴とする化粧材。3. The surface treatment layer according to claim 1, wherein the undercoat layer is one or two selected from the group consisting of urethane resin, epoxy resin, acrylic resin, alkyd resin, cellulose resin, polyvinyl alcohol resin, and aqueous glass. A cosmetic material characterized by being more than one kind. 【請求項４】 請求項１〜３のいずれか一項において，
上記下地処理層と印刷層との間には，木粉又は着色剤の
一方又は双方とシーラー用樹脂との混合物よりなるシー
ラー層を有することを特徴とする化粧材。4. The method according to claim 1, wherein
A decorative material comprising a sealer layer made of a mixture of one or both of wood powder and a colorant and a sealer resin, between the base treatment layer and the printing layer. 【請求項５】 請求項４において，上記シーラー層は，
１〜９０重量％の木粉と，９９〜１０重量％のシーラー
用樹脂とよりなることを特徴とする化粧材。5. The sealer layer according to claim 4, wherein:
A decorative material comprising 1 to 90% by weight of wood flour and 99 to 10% by weight of a resin for a sealer. 【請求項６】 請求項４又は５において，上記木粉の粒
径は，１〜５００μｍであることを特徴とする化粧材。6. The decorative material according to claim 4, wherein the wood powder has a particle size of 1 to 500 μm. 【請求項７】 請求項４〜６のいずれか一項において，
上記着色剤とシーラー用樹脂とよりなるシーラー層は，
透明であることを特徴とする化粧材。7. The method according to claim 4, wherein
The sealer layer consisting of the colorant and the resin for sealer is
A cosmetic material characterized by being transparent. 【請求項８】 請求項１〜７のいずれか一項において，
上記下地処理層は，木粉を含有していることを特徴とす
る化粧材。8. The method according to any one of claims 1 to 7,
The above-mentioned base treatment layer contains wood powder, which is a decorative material. 【請求項９】 請求項１〜８のいずれか一項において，
上記印刷層の上には，クリヤー層を設けてなることを特
徴とする化粧材。9. The method according to claim 1, wherein:
A decorative material characterized in that a clear layer is provided on the printed layer. 【請求項１０】 請求項１〜９のいずれか一項におい
て，上記化粧材の最表面には，減摩剤を含有する減摩ク
リヤー層を有することを特徴とする化粧材。10. The decorative material according to claim 1, wherein the outermost surface of the decorative material has an antifriction clear layer containing an antifriction agent. 【請求項１１】 無機質基材の表面にシーラー用樹脂を
塗布し，硬化させて下地処理層を形成し，その後，該下
地処理層の上に木目模様の印刷層を印刷することを特徴
とする化粧材の製造方法。11. A sealer resin is applied to the surface of an inorganic base material and cured to form a base treatment layer, and then a wood grain pattern printing layer is printed on the base treatment layer. A method for manufacturing a decorative material. 【請求項１２】 請求項１１において，上記無機質基材
は，ケイ酸カルシウム板，パルプセメント板，しっくい
ドロマイトプラスター，プレキャストコンクリートパネ
ル，セメントモルタル，石膏プラスター，石膏ボード，
ＡＬＣパネル，石綿スレート板，ガラス繊維強化コンク
リート，石綿セメントケイカル板，木毛・木片セメント
板，及び石綿セメント押出成形板のグループから選ばれ
る１種又は２種以上であることを特徴とする化粧材の製
造方法。12. The inorganic base material according to claim 11, wherein the calcium silicate board, pulp cement board, stucco dolomite plaster, precast concrete panel, cement mortar, gypsum plaster, gypsum board,
A cosmetic material characterized by being one or more selected from the group consisting of ALC panels, asbestos slate boards, glass fiber reinforced concrete, asbestos cement silica boards, wood wool / wood chip cement boards, and asbestos cement extrusion boards. Manufacturing method. 【請求項１３】 請求項１１又は１２において，上記下
地処理層は，ウレタン樹脂，エポキシ樹脂，アクリル樹
脂，アルキッド樹脂，セルロース樹脂，ポリビニールア
ルコール樹脂，及び水性ガラスのグループから選ばれる
１種又は２種以上であることを特徴とする化粧材の製造
方法。13. The surface treatment layer according to claim 11, wherein the undercoat layer is one or two selected from the group consisting of urethane resin, epoxy resin, acrylic resin, alkyd resin, cellulose resin, polyvinyl alcohol resin, and aqueous glass. A method for producing a decorative material, characterized in that the number of kinds is at least one. 【請求項１４】 請求項１１〜１３のいずれか一項にお
いて，上記下地処理層を形成した後には，木粉又は着色
剤の一方又は双方とシーラー用樹脂との混合物よりなる
シーラー層を形成し，その後，該シーラー層の表面に上
記印刷層を印刷することを特徴とする化粧材の製造方
法。14. The sealer layer according to any one of claims 11 to 13, after forming the base treatment layer, a sealer layer made of a mixture of one or both of wood powder and a colorant and a sealer resin is formed. Then, a method for producing a decorative material, characterized by printing the printing layer on the surface of the sealer layer. 【請求項１５】 請求項１１〜１４のいずれか一項にお
いて，上記印刷層の上には，クリヤー層を形成すること
を特徴とする化粧材の製造方法。15. The method for manufacturing a decorative material according to claim 11, wherein a clear layer is formed on the printed layer.