JPH09316381A - Oil-base ball point pen ink - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain an oil-base ball point pen ink minimized in a problem of dripping a blob of ink when used for writing by mixing an organic solvent with a colorant, a resin and a neopentylpolyol fatty acid ester. SOLUTION: An organic solvent is mixed with a colorant, a resin and a neopentylpolyol fatty acid ester. It is desirable that the amount of the ester added be 1-10% and that the number of carbon atoms of the fatty acid be 4-17. The ester has good compatibility with and a good affinity for the organic solvent, the dye, the pigment and the oil-soluble polymer used in the ink. It has therefore an effect of lubricating the metal being the material of which the tip or ball of a ball point pen is made, causes the ink to show lowered surface tension and improved wetting properties, to stick weakly around the rotating ball and to form a thinned ink layer on the ball. As a result, it can give oil-based ball point pen ink markedly reduced in the tendency to drip a blob of ink.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、油性ボールペン用
インキ、更に詳しくは筆記に伴うインキのぼた落ち現象
（以下、インキボテとする）を極力抑制してなる油性ボ
ールペン用インキに関するものである。尚、インキボテ
とは、筆記中にボールペンのペン先で、紙面に転写しき
らずにペン先にだんだんと溜まってくるインキ玉が、あ
る程度の大きさまでなったところで、紙面に転写される
現象のことを言う。一般的にその現象が起きると筆記線
に対して美観を損ね、筆記者に対しても、不快感を与え
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an oil-based ballpoint pen ink, and more particularly to an oil-based ballpoint pen ink in which ink dripping phenomenon (hereinafter referred to as ink blobbing) accompanying writing is suppressed as much as possible. Note that the ink bot is the phenomenon that an ink ball that gradually accumulates on the pen tip without being completely transferred to the paper surface during writing with the pen tip of a ballpoint pen reaches a certain size and is transferred to the paper surface. To tell. In general, when such a phenomenon occurs, the aesthetic appearance of the writing line is impaired, and the writer also feels uncomfortable.

【０００２】[0002]

【従来の技術】従来の油性インキを内蔵したボールペン
には、一般的に有機溶剤を主溶剤とし、増粘させるため
に油溶性高分子を添加したり、筆跡を濃くするために高
濃度の染料を使用して、７０００〜１５０００ｃｐｓ程
度の比較的粘調性の高いインキが使用されていた。ま
た、油溶性高分子をポリビニルピロリドン等を使用して
インキに曳糸性を与えることによってインキの紙面への
転写をし易くすることなどが行われていた。2. Description of the Related Art In conventional ballpoint pens containing oil-based ink, an organic solvent is generally used as a main solvent, an oil-soluble polymer is added to increase the viscosity, and a high-concentration dye is added to increase the handwriting. And a relatively viscous ink having a viscosity of about 7,000 to 15,000 cps was used. Further, it has been carried out to make the transfer of the ink to the paper surface easy by imparting spinnability to the ink using polyvinylpyrrolidone or the like as an oil-soluble polymer.

【０００３】上述のような粘稠性及び曳糸性を有するイ
ンキを使用した場合、インキは回転する物体に対して巻
き付こうとする現象であるワイセンベルク効果を示す。
ワイセンベルク効果を示すことによって、筆記部材とし
てのボールの回転に対してインキがまとわりついてしま
い、かえってボール上のインキの一部又は全部が紙面に
転写しにくくなる現象が発生することがあった。すると
回転するボール上にインキが厚く堆積し、ボールペンチ
ップの先端開口部に溜まってしまい、ある程度溜った段
階で紙面に落ちてインキボテとなる。このインキボテの
現象は筆跡の美観を損ない、またインキボテにより紙面
に付着したインキは、他の筆跡部分に比べて著しく乾燥
しにくいため、接触した他のものを汚してしまうという
問題を引き起こすという問題があった。When the ink having the above-mentioned viscosity and spinnability is used, the ink exhibits the Weissenberg effect, which is a phenomenon in which the ink tends to wind around a rotating object.
When the Weissenberg effect is exhibited, the ink clings to the rotation of the ball as a writing member, which may cause a phenomenon in which some or all of the ink on the ball is difficult to transfer to the paper surface. Then, the ink is thickly deposited on the rotating ball and is accumulated in the opening of the tip of the ballpoint pen tip. This phenomenon of ink botching impairs the aesthetics of handwriting, and the ink adhered to the paper surface by ink botting is much less likely to dry than other handwriting parts, which causes the problem of staining other things that come into contact. there were.

【０００４】インキボテを抑制するために、油溶性高分
子の種類や添加量によって曳糸性の度合いを調節した
り、界面活性剤等を種々組み合わせるなどして添加し、
インキの弾性変形特性と流動変形特性の調整等のインキ
のレオロジー特性の改善を行い、回転するボールからイ
ンキが紙面により多く転写しやすくしたものは知られて
いる。具体的には、ポリビニルピロリドン、ロジン、ロ
ジン変性マレイン酸樹脂等の油溶性高分子やオレイン
酸、ポリオキシエチレンアルキルエーテル類、ソルビタ
ン脂肪酸エステル等の界面活性剤を添加したものであ
る。In order to suppress ink bloating, the degree of spinnability is adjusted by the type and amount of the oil-soluble polymer added, and various additives such as surfactants are added in combination.
It is known that the rheological properties of the ink are improved by adjusting the elastic deformation property and the flow deformation property of the ink so that the ink can be more easily transferred from the rotating ball to the paper surface. Specifically, it is obtained by adding an oil-soluble polymer such as polyvinylpyrrolidone, rosin, or rosin-modified maleic acid resin, or a surfactant such as oleic acid, polyoxyethylene alkyl ethers, sorbitan fatty acid ester.

【０００５】[0005]

【発明が解決しようとする課題】しかし、上述の油溶性
高分子、界面活性剤等を種々組み合わせるなどして添加
したインキも、ボールへのインキのまとわりつきは十分
に抑制されず、インキボテの防止は十分とはいえなかっ
た。ＪＩＳ（Ｓ ６０３９）によれば、筆跡幅が正常な
筆跡（インキボテのない場合の筆跡）の３〜４倍程度に
なっているものをインキボテの大きさの限度見本として
おり、具体的には資料中の図より、０．３ｍｍ幅の筆跡
の一部分が５．５ｃｍにわたって最大幅０．８ｍｍとな
っているものが示されている。従来のインキを使用した
ものに筆記試験を実施した場合、１０００ｍ筆記中ＪＩ
Ｓで図示された大きさのインキボテが２個程度発生する
ものであり、満足できるものではなかった。本発明は、
インキボテが極端に少ない油性ボールペン用インキを得
ることを目的とする。However, even with the inks added by various combinations of the above-described oil-soluble polymers, surfactants, etc., the clinging of the ink to the ball is not sufficiently suppressed, and the prevention of ink sticking is not achieved. It was not enough. According to JIS (S 6039), the width of the handwriting is about 3 to 4 times that of a normal handwriting (handwriting without ink drips) as the limit sample for the size of the ink lips. The figure in the middle shows that a part of the 0.3 mm wide handwriting has a maximum width of 0.8 mm over 5.5 cm. When a writing test was carried out on the ink using the conventional ink, JI
About two ink spots of the size shown by S are generated, which is not satisfactory. The present invention
The purpose is to obtain an ink for oil-based ballpoint pens that has extremely little ink bloating.

【０００６】[0006]

【課題を解決するための手段】即ち、本発明は、有機溶
剤と着色剤と樹脂とネオペンチルポリオール脂肪酸エス
テルとから少なくともなり、該ネオペンチルポリオール
の添加量は１〜１０％、脂肪酸の炭素数は４〜１７であ
ることを特徴とする油性ボールペン用インキを要旨とす
る。That is, the present invention comprises at least an organic solvent, a colorant, a resin, and a neopentyl polyol fatty acid ester, and the addition amount of the neopentyl polyol is 1 to 10% and the number of carbon atoms in the fatty acid. Is 4 to 17, and the gist is an oil-based ballpoint pen ink.

【０００７】以下、本発明を詳細に説明する。本発明に
おいて、有機溶剤は従来油性ボールペンに使用されるも
のなら特に限定なく使用でき、例えばエチレングリコー
ルモノフェニルエーテル、ベンジルアルコール、プロピ
レングリコール、ジプロピレングリコール、１，３−ブ
チレングリコール、へキシレングリコール、テトラリ
ン、プロピレングリコールモノフェニルエーテル、ジプ
ロピレングリコールモノメチルエーテル、ジプロピレン
グリコールモノエチルエーテル、ジプロピレングリコー
ルモノブチルエーテル、ジプロピレングリコールモノメ
チルエーテルアセテート、トリプロピレングリコールモ
ノメチルエーテル、Ｎ−メチル−２−ピロリドン等があ
り、これらを適宜選択して単独あるいは組み合わせて使
用でき、その使用量はインキ全量に対し３０〜７０重量
％が好ましい。Hereinafter, the present invention will be described in detail. In the present invention, the organic solvent can be used without particular limitation as long as it is conventionally used for oil-based ballpoint pens, for example, ethylene glycol monophenyl ether, benzyl alcohol, propylene glycol, dipropylene glycol, 1,3-butylene glycol, hexylene glycol, There are tetralin, propylene glycol monophenyl ether, dipropylene glycol monomethyl ether, dipropylene glycol monoethyl ether, dipropylene glycol monobutyl ether, dipropylene glycol monomethyl ether acetate, tripropylene glycol monomethyl ether, N-methyl-2-pyrrolidone, etc. , Which can be used alone or in combination by selecting them appropriately, and the amount thereof is preferably 30 to 70% by weight based on the total amount of the ink. .

【０００８】着色剤としては、従来ボールペンインキ組
成物に用いられている染料が主として用いられるが、調
色、筆跡特性改良のため顔料の併用も可能である。その
具体例を挙げると染料としては、ローダミンＢベース
（Ｃ．Ｉ．４５１７０Ｂ）、ソルダンレッド３Ｒ（Ｃ．
Ｉ．２１２６０）、メチルバイオレット２Ｂベース
（Ｃ．Ｉ．４２５３５Ｂ）、ビクトリアブルーＦ４Ｒ
（Ｃ．Ｉ．４２５６３Ｂ）、ニグロシンベースＬＫ
（Ｃ．Ｉ．５０４１５）、オリエント化学工業（株）製
の油性染料として、バリファーストイエロー＃３１０４
（Ｃ．Ｉ．１３９００Ａ）、バリファーストイエロー＃
３１０５（Ｃ．Ｉ．１８６９０）、オリエント スピリ
ットブラックＡＢ（Ｃ．Ｉ．５０４１５）、バリファー
ストブラック＃３８０４（Ｃ．Ｉ．１２１９５）、バリ
ファーストイエロー＃１１０９、バリファーストオレン
ジ＃２２１０、バリファーストレッド＃１３２０、バリ
ファーストブルー＃１６０５、バリファーストバイオレ
ット＃１７０１、保土谷化学工業（株）製の油性染料と
して、スピロンブラック ＧＭＨスペシャル、スピロン
イエローＣ−２ＧＨ、スピロンレッドＣ−ＧＨ、スピロ
ンレッドＣ−ＢＨ、スピロンブルーＢＰＮＨ、スピロン
ブルーＣ−ＲＨ、スピロンバイオレットＣ−ＲＨ、Ｓ．
Ｐ．Ｔ．オレンジ６、Ｓ．Ｐ．Ｔ．ブルー−１１１など
が例示できる。As the colorant, a dye conventionally used in a ballpoint pen ink composition is mainly used, but a pigment can be used in combination for the purpose of improving the color matching and handwriting characteristics. Specific examples thereof include dyes such as Rhodamine B base (C.I. 45170B) and Sordan Red 3R (C.I.
I. 21260), Methyl Violet 2B Base (C.I. 42535B), Victoria Blue F4R
(C.I. 42563B), Nigrosine base LK
(CI.50415), an oily dye manufactured by Orient Chemical Industry Co., Ltd., which is Varifast Yellow # 3104.
(C.I. 13900A), Varifast Yellow #
3105 (C.I. 18690), Orient Spirit Black AB (C.I. 50415), Bali First Black # 3804 (C.I. 12195), Bali First Yellow # 1109, Bali First Orange # 2210, Bali First Red #. 1320, Bali First Blue # 1605, Bali First Violet # 1701, Hodogaya Chemical Co., Ltd. oil dyes, Spiron Black GMH Special, Spiron Yellow C-2GH, Spiron Red C-GH, Spiron Red C-BH, Spyron Blue BPNH, Spyron Blue C-RH, Spyron Violet C-RH, S.I.
P. T. Orange 6, S.I. P. T. Blue-111 can be exemplified.

【０００９】顔料としてはＰＲＩＮＴＥＸ ９５、同７
５、同４５、同Ｐ、同ＸＥ２、（以上、デグサ・ジャパ
ン（株）製）、＃２４００Ｂ、＃１０００、＃ＭＣＦ８
８、ＭＡ１００、ＭＡ７、ＭＡ１１、＃５０、＃４０、
＃３０、ＣＦ９、＃２０Ｂ、（以上、三菱化成工業
（株）製）、ＲＡＶＥＮ７０００、同２０００、同１２
００、同１０００、同５００、同４１０、同１４（以
上、コロンビアカーボン日本（株）製）等のカーボンブ
ラック、Ｐ２５（日本アエロジル（株）製）等の酸化チ
タン、黒色酸化鉄、黄色酸化鉄、赤色酸化鉄、群青、コ
バルトブルー、クロムグリーン、酸化クロム等の無機顔
料、ハンザイエロー１０Ｇ、同５Ｇ、同３Ｇ、同４、同
ＧＲ、同Ａ、ベンジジンイエロー、パーマネントイエロ
ーＮＣＧ、タートラジンレーキ、キノリンイエロー、ス
ダーン１、パーマネントオレンジ、インダスレンブリリ
アントオレンジＧＮ、パーマネントブラウンＦＧ、パラ
ブラウン、パーマネントレッド４Ｒ、ファイヤーレッ
ド、ブリリアントカーミン６Ｂ、ボルドー５Ｂ、チオイ
ンジゴレッド、ファーストバイオレットＢ、ジオキサン
バイオレット、アルカリブルーレーキ、フタロシアニン
ブルー、インジゴ、アシッドグリーンレーキ、フタロシ
アニングリーン等の有機顔料が挙げられる。前記した着
色剤は、単独或いは、他との組合せにより使用でき、そ
の使用量は色調等によっても異なるが、油性ボールペン
インキ組成物全量に対して１０〜４５重量％が好まし
い。また、染料、顔料は混合して使用することもでき
る。As pigments, PRINTEX 95, PRINTEX 7
5, the same 45, the same P, the same XE2 (manufactured by Degussa Japan KK), # 2400B, # 1000, # MCF8.
8, MA100, MA7, MA11, # 50, # 40,
# 30, CF9, # 20B (Mitsubishi Kasei Kogyo Co., Ltd.), RAVEN7000, 2000, 12
Carbon blacks such as 00, 1000, 500, 410, and 14 (all manufactured by Columbia Carbon Japan Co., Ltd.), titanium oxides such as P25 (manufactured by Nippon Aerosil Co., Ltd.), black iron oxide, and yellow iron oxide Inorganic pigments such as red iron oxide, ultramarine blue, cobalt blue, chrome green, and chromium oxide, Hansa Yellow 10G, 5G, 3G, 4, GR, A, Benzidine Yellow, Permanent Yellow NCG, Tartrazine Lake, Quinoline Yellow, Sudan 1, Permanent Orange, Indus Ren Brilliant Orange GN, Permanent Brown FG, Para Brown, Permanent Red 4R, Fire Red, Brilliant Carmine 6B, Bordeaux 5B, Thioindigo Red, First Violet B, Dioxane Violet, Arca Blue Lake, phthalocyanine blue, indigo, acid green lake, and organic pigments such as phthalocyanine green. The above-mentioned coloring agents can be used alone or in combination with others, and the amount thereof is preferably 10 to 45% by weight with respect to the total amount of the oil-based ballpoint pen ink composition, although it varies depending on the color tone and the like. Dyes and pigments can also be used as a mixture.

【００１０】インキ粘度を上昇させたり、筆跡の定着性
を良くするために添加する樹脂としては、油性ボールペ
ンインキに使用されているものなら特に限定なく使用で
きる。一例を挙げると、ケトン樹脂、キシレン樹脂、ポ
リエチレンオキサイド、ロジン樹脂、テルペン系樹脂、
クマロンーインデン樹脂、ポリビニルブチラール、ポリ
ビニルピロリドン、ビニルピロリドン−酢酸ビニル共重
合物、ポリメタクリル酸エステル、ポリアクリル酸ポリ
メタクリル酸共重合物等が挙げられる。Any resin used for oil-based ballpoint pen inks can be used without particular limitation as the resin added to increase the ink viscosity or improve the fixability of handwriting. To give an example, ketone resin, xylene resin, polyethylene oxide, rosin resin, terpene resin,
Examples thereof include coumarone-indene resin, polyvinyl butyral, polyvinylpyrrolidone, vinylpyrrolidone-vinyl acetate copolymer, polymethacrylic acid ester, polyacrylic acid polymethacrylic acid copolymer and the like.

【００１１】ネオペンチルポリオール脂肪酸エステルは
あらかじめインキ溶剤と混合し使用しても、インキの他
の組成物を混合した後から添加する方法で用いても良
い。その添加量はインキの溶剤の種類や着色剤、樹脂、
界面活性剤の種類によって影響されるので一義的ではな
いが、１重量％以下の添加ではその他の配合物によって
効果を希釈されてしまい、１０重量％以上の添加ではイ
ンキ成分が金属に対して親和性を持ちすぎ、紙面に対し
て転写性を落とすと考えられる為のボテ発生を招くこと
になるので通常１〜１０重量％の添加が好ましい。ネオ
ペンチルポリオール脂肪酸エステルの一例として、ネオ
ペンチルグリコールのモノ、ジ脂肪酸エステル、トリメ
チロールプロパンのモノ、ジ、トリ脂肪酸エステル、ペ
ンタエリスリトールのモノ、ジ、トリ、テトラ脂肪酸エ
ステルなどが挙げられる。最適な脂肪酸炭素数はインキ
の溶剤の種類や着色剤、樹脂、界面活性剤の種類によっ
て影響されるので一義的ではないが、１８以上ではネオ
ペンチルポリオールの金属への親和性が強すぎてしまい
ボテを発生させやすくなり、３以下ではインキ組成物中
に含まれる染料、樹脂によって生まれる粘性がボール回
転によってまとわりつくワイセンベルク性に対してイン
キを紙へ転写させようとする効果をなさず、すなわち添
加する意味をなさずにボテを発生を招くことになるの
で、通常４〜１７の炭素数であることが好ましい。ま
た、ネオペンチルポリオール脂肪酸エステルはインキの
他成分との混合性、相溶性などにより単一もしくは混合
物として適宜用いることができる。The neopentyl polyol fatty acid ester may be used by mixing it with the ink solvent in advance, or may be used by adding it after mixing other composition of the ink. The amount of addition depends on the type of ink solvent, colorant, resin,
It is not unique because it is affected by the type of surfactant, but the addition of 1 wt% or less dilutes the effect with other compounds, and the addition of 10 wt% or more causes the ink component to have an affinity for metals. Therefore, the addition of 1 to 10% by weight is usually preferable because it causes the occurrence of burrs which is considered to have too much property and deteriorates the transferability to the paper surface. Examples of neopentyl polyol fatty acid ester include mono-, di-fatty acid ester of neopentyl glycol, mono-, di-, tri-fatty acid ester of trimethylolpropane, mono-, di-, tri-, tetra-fatty acid ester of pentaerythritol and the like. The optimum fatty acid carbon number is not unique because it is affected by the type of ink solvent, colorant, resin, and surfactant, but if it is 18 or more, the affinity of neopentylpolyol for metal is too strong. If it is 3 or less, the viscosity produced by the dye and resin contained in the ink composition does not have the effect of attempting to transfer the ink to the paper against the Weissenberg property of clinging by ball rotation. It is preferable that the number of carbon atoms is usually 4 to 17 because it will cause occurrence of burrs without meaning. Further, the neopentyl polyol fatty acid ester can be appropriately used alone or as a mixture depending on the compatibility and compatibility with other components of the ink.

【００１２】本発明の油性ボールペンインキ組成物には
必要に応じて上記成分以外に、各種添加剤、界面活性剤
が使用できる。一例を挙げると、酸化防止剤、紫外線吸
収剤、防錆剤の他、筆記性、運筆性改良等に用いられる
各種界面活性剤、例えば、脂肪酸塩類、高級アルコール
硫酸エステル塩類、脂肪酸硫酸エステル塩類、アルキル
アリルスルホン酸塩類等の陰イオン界面活性剤、デカグ
リセリン脂肪酸エステル、ヘキサグリセリン脂肪酸エス
テル、ポリオキシエチレンアルキルエーテル類、ソルビ
タン脂肪酸エステル、ポリオキシエチレンソルビタン脂
肪酸エステル、ポリオキシエチレングリセリン脂肪酸エ
ステル、ポリオキシエチレンポリオキシプロピレンアル
キルエ−テル、ポリオキシエチレンアルキルフェニルエ
−テル、ポリオキシエチレン硬化ヒマシ油などの非イオ
ン系界面活性剤等が挙げられる。In addition to the above components, various additives and surfactants can be used in the oil-based ballpoint pen ink composition of the present invention, if necessary. As one example, antioxidants, ultraviolet absorbers, rust preventives, as well as writability, various surfactants used for improving writing performance, for example, fatty acid salts, higher alcohol sulfate ester salts, fatty acid sulfate ester salts, Anionic surfactants such as alkylallyl sulfonates, decaglycerin fatty acid ester, hexaglycerin fatty acid ester, polyoxyethylene alkyl ethers, sorbitan fatty acid ester, polyoxyethylene sorbitan fatty acid ester, polyoxyethylene glycerin fatty acid ester, polyoxy Examples include nonionic surfactants such as ethylene polyoxypropylene alkyl ether, polyoxyethylene alkylphenyl ether, and polyoxyethylene hydrogenated castor oil.

【００１３】[0013]

【作用】本発明の油性ボールペンインキ組成物により、
筆記に伴うインキボテが極端に少ない油性ボールペンが
得られる理由は次のように考えられる。ネオペンチルポ
リオール脂肪酸エステルは、一般に油性ボールペンイン
キに使用される有機溶剤や染料、顔料、油溶性高分子に
対して相溶性、親和性が良好であり、ボールペンチップ
やボールの材料である金属に対して潤滑性をもたらす効
果がある。つまり、ネオペンチルポリオール脂肪酸エス
テルを溶有する事でインキの表面張力が低下し、インキ
は金属ボールへのインキの濡れ性が向上する。そして染
料や油溶性高分子に粘性を高められたインキが持つワイ
ゼンベルク効果を弱め、すなわちボールの回転によるイ
ンキのまとわりつきが弱くなり、ボール上のインキ層が
薄くなる。よって紙面に転写されなかった僅かなインキ
はボール上に堆積しにくい。また、インキは金属ボール
と親和しているため、ボールペンチップのインキの吐出
する隙間を容易に通ることができる。その結果、ボール
ペンチップの先端開口部のインキの吐出する隙間に入り
きれないインキが溜まりにくくなりインキボテが極端に
少ない油性ボールペンが得られると思われる。By the oil-based ballpoint pen ink composition of the present invention,
The reason why an oil-based ballpoint pen with extremely few ink blobbing associated with writing can be obtained is considered as follows. Neopentyl polyol fatty acid ester has good compatibility and affinity with organic solvents, dyes, pigments, and oil-soluble polymers generally used for oil-based ballpoint pen inks, and with respect to metals that are materials for ballpoint pen tips and balls. Has the effect of providing lubricity. That is, since the neopentyl polyol fatty acid ester is dissolved, the surface tension of the ink is lowered, and the ink has improved wettability of the ink to the metal balls. Then, the Weisenberg effect of the ink whose viscosity is increased by the dye or the oil-soluble polymer is weakened, that is, the cling of the ink due to the rotation of the ball is weakened, and the ink layer on the ball becomes thin. Therefore, the slight amount of ink that has not been transferred to the paper surface is unlikely to deposit on the balls. Further, since the ink is compatible with the metal ball, it can easily pass through the gap of the ballpoint pen tip where the ink is ejected. As a result, it is thought that the oil-based ball-point pen having extremely few ink blemishes can be obtained because the ink that does not fit in the ink discharge gap at the tip opening of the ball-point pen tip is less likely to accumulate.

【００１４】以下、本発明を実施例によって詳細に説明
するが、単に「部」とあるのは、重量部を示す。Hereinafter, the present invention will be described in detail with reference to Examples, but "parts" means "parts by weight".

【００１５】実施例１ フェニルセロソルブ（溶剤、エチレングリコールモノフェニルエーテル） ３８．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン（染料溶解助剤） １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０（染料、オリエント化学工業（株）製） ２０．０部 バリファーストバイオレット１７０１（染料、オリエント化学工業（株）製） １０．０部 ペンタエリスリトールテトラブチレート ４．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 1 Phenyl cellosolve (solvent, ethylene glycol monophenyl ether) 38.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine (dye dissolution aid) 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10 0.0 parts Varifast Black 3820 (dye, manufactured by Orient Chemical Industry Co., Ltd.) 20.0 parts Balifast Violet 1701 (dye, manufactured by Orient Chemical Industry Co., Ltd.) 10.0 parts Pentaerythritol tetrabutyrate 4.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００１６】実施例２ フェニルセロソルブ ３８．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 ペンタエリスリトールテトラヘキサノエート ４．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 2 Phenyl cellosolve 38.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts Pentaerythritol tetrahexanoate 4.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００１７】実施例３ フェニルセロソルブ ３８．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 ペンタエリスリトールテトラオクタノエート ４．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 3 Phenyl cellosolve 38.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts Pentaerythritol tetraoctanoate 4.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００１８】実施例４ フェニルセロソルブ ３８．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 ペンタエリスリトールテトララウレート ４．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 4 Phenyl cellosolve 38.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts Pentaerythritol tetralaurate 4.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００１９】実施例５ フェニルセロソルブ ３８．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 ペンタエリスリトールテトラミリスチレート ４．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 5 Phenyl cellosolve 38.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts Pentaerythritol tetramyristyrate 4.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００２０】実施例６ フェニルセロソルブ ３８．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 トリメチロールプロパンジオクタノエート ４．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 6 Phenylcellosolve 38.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts Trimethylolpropane dioctanoate 4.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００２１】実施例７ フェニルセロソルブ ４０．５部 ベンジルアルコール １５．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０（染料、オリエント化学工業（株）製） ２０．０部 バリファーストバイオレット１７０１ １０．０部 ペンタエリスリトールテトラオクタノエート １．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 7 Phenyl cellosolve 40.5 parts Benzyl alcohol 15.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Varifast Black 3820 (Dye, Orient Chemical Industry Co., Ltd. )) 20.0 parts Varifast Violet 1701 10.0 parts Pentaerythritol tetraoctanoate 1.0 part The above ingredients were stirred at 80 ° C for 5 hours to obtain a black ink.

【００２２】実施例８ フェニルセロソルブ ３４．５部 ベンジルアルコール １２．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 ペンタエリスリトールテトラオクタノエート １０．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 8 Phenyl cellosolve 34.5 parts Benzyl alcohol 12.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts Pentaerythritol tetraoctanoate 10.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００２３】実施例９ フェニルセロソルブ ３８．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １３．０部 バリファーストブルー１６０７（染料、オリエント化学工業（株）製） ２６．０部 ペンタエリスリトールテトラヘキサノエート ４．０部 上記配合成分を８０℃５時間攪拌して青色インキを得
た。Example 9 Phenyl cellosolve 38.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 13.0 parts Varifast Blue 1607 (dye, Orient Chemical Industry Co., Ltd. )) 26.0 parts Pentaerythritol tetrahexanoate 4.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a blue ink.

【００２４】実施例１０ フェニルセロソルブ ３８．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １３．０部 スピロンレッドＣ−ＧＨ（染料、オリエント化学工業（株）製） １２．０部 スピロンオレンジ（染料、オリエント化学工業（株）製） １５．０部 ペンタエリスリトールテトラヘキサノエート ４．０部 上記配合成分を８０℃５時間攪拌して赤色インキを得
た。Example 10 Phenyl cellosolve 38.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 13.0 parts Spyron Red C-GH (dye, Orient Chemical Industry Co., Ltd. ) 12.0 parts Spyron Orange (dye, manufactured by Orient Chemical Industry Co., Ltd.) 15.0 parts Pentaerythritol tetrahexanoate 4.0 parts The above ingredients are stirred at 80 ° C. for 5 hours to obtain a red ink. It was

【００２５】実施例１１ フェニルセロソルブ ４０．５部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １３．０部 カーボンブラック １８．０部 オレイン酸 ５．０部 ペンタエリスリトールテトラヘキサノエート ４．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Example 11 Phenylcellosolve 40.5 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 13.0 parts Carbon black 18.0 parts Oleic acid 5.0 parts Pentaerythritol tetrahexanoate 4.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００２６】比較例１ 実施例１においてペンタエリスリトールテトラブチレー
トを除いた替わりにペンタエリスリトールテトラプロピ
レートを同量加えた以外は同様にして黒色インキを得
た。Comparative Example 1 A black ink was obtained in the same manner as in Example 1 except that pentaerythritol tetrabutyrate was added in place of pentaerythritol tetrabutyrate.

【００２７】比較例２ 実施例１においてペンタエリスリトールテトラブチレー
トを除いた替わりにペンタエリスリトールジオレエート
を同量加えた以外は同様にして黒色インキを得た。Comparative Example 2 A black ink was obtained in the same manner as in Example 1 except that pentaerythritol tetrabutyrate was omitted and pentaerythritol dioleate was added in the same amount.

【００２８】比較例３ フェニルセロソルブ ４２．０部 ベンジルアルコール １４．０部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 ペンタエリスリトールテトラオクタノエート ０．５部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Comparative Example 3 Phenyl cellosolve 42.0 parts Benzyl alcohol 14.0 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts Pentaerythritol tetraoctanoate 0.5 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００２９】比較例４ フェニルセロソルブ ３３．０部 ベンジルアルコール １１．５部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 ペンタエリスリトールテトラオクタノエート １２．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Comparative Example 4 Phenylcellosolve 33.0 parts Benzyl alcohol 11.5 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts Pentaerythritol tetraoctanoate 12.0 parts The above ingredients were stirred at 80 ° C for 5 hours to obtain a black ink.

【００３０】比較例５ フェニルセロソルブ ４２．０部 ベンジルアルコール １４．５部 オキシエチレンドデシルアミン １．０部 ポリビニルピロリドン ２．５部 ケトン樹脂 １０．０部 バリファーストブラック３８２０ ２０．０部 バリファーストバイオレット１７０１ １０．０部 上記配合成分を８０℃５時間攪拌して黒色インキを得
た。Comparative Example 5 Phenyl cellosolve 42.0 parts Benzyl alcohol 14.5 parts Oxyethylene dodecylamine 1.0 part Polyvinylpyrrolidone 2.5 parts Ketone resin 10.0 parts Balifast black 3820 20.0 parts Balifirst violet 1701 10.0 parts The above ingredients were stirred at 80 ° C. for 5 hours to obtain a black ink.

【００３１】[0031]

【発明の効果】実施例１〜１１及び比較例１〜５のボー
ルペン用油性インキを市販の油性ボールペン本体ＢＫ１
００（ぺんてる（株）製）に各０．２５ｇ充填し、イン
キボテ及び初筆カスレ性について試験を行った。The oil-based inks for ballpoint pens of Examples 1 to 11 and Comparative Examples 1 to 5 are commercially available oil-based ballpoint pen bodies BK1.
00 (manufactured by Pentel Co., Ltd.) was filled with 0.25 g of each, and the tests were performed for ink swelling and first-stroke smearing property.

【００３２】インキボテ数計測試験；筆記加重２００
ｇ、筆記角度７０度、筆記速度７ｃｍ／ｓｅｃで初筆上
質紙に螺旋を１０００ｍ描いた後、筆跡をＳｃａｌｅ
Ｌｕｐｅ（東海産業（株）製）で観察し、螺旋筆跡上に
あるインキボテの個数を計測した。尚、値は４本のサン
プルの平均値とした。Ink-butter count measurement test; writing weight 200
g, writing angle 70 degrees, writing speed 7 cm / sec, draw a spiral for 1000 m on high-quality first writing paper, and then scale the handwriting.
It was observed with Lupe (manufactured by Tokai Sangyo Co., Ltd.) and the number of ink spots on the spiral handwriting was counted. The value was the average value of four samples.

【００３３】インキボテは、試験を行うボールペンの正
常な筆跡幅のおよそ１．５倍程度のものを０．２５個、
それ以上３倍程度のものを０．５０個、ＪＩＳで規定さ
れたインキボテと同等のものを１．００個として計測
し、合計したものをインキボテ数とした。0.25 ink bots are about 1.5 times the normal handwriting width of the ballpoint pen to be tested.
About 0.5 times more than that, and 1.00 equivalent to the ink knives specified by JIS were measured, and the total was taken as the number of ink knives.

【００３４】初筆カスレ計測試験；試験品が筆記可能か
を確認の上、２４時間、横向き、室温経時後、筆記加重
２００ｇ、筆記角度７０度、筆記速度３０ｃｍ／ｓｅｃ
で上質紙に直線を描いた後、筆跡をＳｃａｌｅ Ｌｕｐ
ｅ（東海産業（株）製）で観察し、初筆カスレ長さを計
測した。尚、値は１０本のサンプルの平均値とした。各
結果を表１、表２に示す。First brush scraping measurement test: After confirming whether the test product is writable, the test piece is turned sideways for 24 hours, and after room temperature passage, a writing load of 200 g, a writing angle of 70 degrees, and a writing speed of 30 cm / sec.
After drawing a straight line on high-quality paper with, the handwriting is Scale Lup
e (manufactured by Tokai Sangyo Co., Ltd.), and the length of the first brush stroke was measured. The value was an average value of 10 samples. The results are shown in Tables 1 and 2.

【００３５】[0035]

【表１】 [Table 1]

【００３５】[0035]

【表２】 [Table 2]

【００３６】以上のように、本発明のボールペン用油性
インキは、インキボテが比較的少ない良好なものであ
る。As described above, the oil-based ink for ballpoint pens of the present invention is a good ink with relatively few ink bloats.

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 有機溶剤と着色剤と樹脂とネオペンチル
ポリオール脂肪酸エステルとから少なくともなり、該ネ
オペンチルポリオールの添加量は１〜１０％、脂肪酸の
炭素数は４〜１７であることを特徴とする油性ボールペ
ン用インキ。1. A method comprising at least an organic solvent, a colorant, a resin and a neopentyl polyol fatty acid ester, wherein the addition amount of the neopentyl polyol is 1 to 10% and the fatty acid has 4 to 17 carbon atoms. Ink for oil-based ballpoint pens.