JPH092866A - 液晶バックライト用低損失フェライト - Google Patents
液晶バックライト用低損失フェライトInfo
- Publication number
- JPH092866A JPH092866A JP7157334A JP15733495A JPH092866A JP H092866 A JPH092866 A JP H092866A JP 7157334 A JP7157334 A JP 7157334A JP 15733495 A JP15733495 A JP 15733495A JP H092866 A JPH092866 A JP H092866A
- Authority
- JP
- Japan
- Prior art keywords
- power loss
- liquid crystal
- electric power
- ferrite
- crystal backlight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
低損失な液晶バックライト用低損失フェライトを得る。 【構成】Fe2O3 53.0〜54.5モル%、ZnO
6〜12モル%、残部MnOからなる主成分と、副成
分として、CaO 200〜1000ppm、SiO2
0〜300ppm(但し0ppmを含まない)、Co
O 100〜4000ppm含有し、更にNb2O5、T
a2O5の少なくとも1種を50〜500ppm含有し、
100kHz、200mTでの電力損失が400kW/
m3以下で、その電力損失の最小値を得る温度が20〜
60℃である。
Description
ンバータートランス磁心等に好適な低損失フェライトに
関するものである。
用材料として、Mn―Zn系フェライトが使用されてい
る。このトランス用材料としては、低損失であることが
求められている。従来の低損失フェライトとしては、種
々の組成のものが既に提案されている。例えば、特開平
3―248405号には、Fe2O3、MnO、ZnOを
主成分とし、副成分として、CaO 200〜1000
ppm、SiO2 500ppm以下(0を含まず)、
Nb2O5 1500ppm以下(0を含まず)、Ta2
O51500ppm以下(0を含まず)を複合添加した
電源用低損失フェライトが開示されている。この低損失
フェライトでは、100kHz、200mTで電力損失
が300程度の材料が得られている。
ランスの動作温度は、70℃前後であり、上記従来材の
電力損失が最小となる温度は、トランスの発熱防止のた
め、100℃前後に設計されている。しかしながら、近
年では、例えば液晶バックライト用トランスに使用され
る用途では、動作温度が室温付近と低いため、その電力
損失が最小となる温度、所謂ボトム温度を60℃以下に
する要求がある。本発明は、上記のことを鑑みて、電力
損失のボトム温度が20〜60℃であり、低損失な液晶
バックライト用低損失フェライトを提供することを目的
とする。
3.0〜54.5モル%、ZnO 6〜12モル%、残
部MnOからなる主成分と、副成分として、CaO 2
00〜1000ppm、SiO2 0〜300ppm
(但し0ppmを含まない)、CoO 100〜400
0ppm含有し、更にNb2O5、Ta2O5の少なくとも
1種を50〜500ppm含有し、100kHz、20
0mTでの電力損失が400kW/m3以下で、その電
力損失の最小値を得る温度が20〜60℃であることを
特徴とする液晶バックライト用低損失フェライトであ
る。また本発明は、その液晶バックライト用低損失フェ
ライトにおいて、平均結晶粒径が5〜15μmであるこ
とを特徴とするものである。
下のとおりである。主成分は、Fe2O3が53.0モル
%未満、またはZnOが6モル%未満であると、電力損
失の最小値を得る温度が60℃以上となり、これに伴い
20〜60℃における電力損失が増大し、400kW/
m3を越える。また、Fe2O3が54.5モル%を超
過、またはZnOが12モル%を超過すると、電力損失
の最小値を得る温度が20℃以下となり、これに伴い2
0〜60℃における電力損失が増大し、400kW/m
3を越える。副成分は、CaO、SiO2の添加量が範囲
に満たないと、20〜60℃における損失が400kW
/m3を越え、またCaOが範囲を越えると粒界応力の
増加に伴い、電力損失が増大し、SiO2が範囲を越え
ると、異常粒成長が発生して、損失が増大するためであ
る。CoOは、添加量が100ppm未満では、電力損
失の低減効果が少なく、環境温度の変動に対する電力損
失の変化が大きくなる。一方、添加量が4000ppm
を超過すると、電力損失の温度変化は少ないが、電力損
失の最小値を得る温度が大幅に低下し、20℃以下とな
る。Nb2O5、Ta2O5は、範囲に満たない場合では電
力損失の低減効果が少なく、範囲を越えると異常粒成長
が発生して、電力損失が増大する。また、このNb
2O5、Ta2O5は、総量で、500ppm以下であるこ
とが望ましい。また、平均結晶粒径は、5〜15μmが
適当であり、好ましくは、6〜12μmである。
損失フェライトの実施例を説明する。まず、Fe2O3、
MnO、ZnOを所定量秤量し、900℃で仮焼し、副
成分としてCaO(CaCO3で添加)、SiO2、Co
O、Nb2O5、Ta2O5を所定量添加し、ボールミルで
12時間粉砕し、バインダーを1wt%添加してスプレ
ー造粒した。これを成形し、保持温度1300℃で5時
間焼成し、外径25mm、内径15mm、高さ5mmの
リング形コア(試料)を製造した。この各試料の成分を
表1に示す。又、各試料の電力損失の最小値とそのとき
の温度(ボトム温度)、初透磁率、焼結密度及び平均結
晶粒径を表2に示す。
には、試料の番号に*印を付けた。試料番号20では、
Fe2O3が54.8モル%と多く、ボトム温度が0℃と
なり、又試料番号17では、Fe2O3が52.8モル%
と少ないと、ボトム温度が80℃となっている。更に、
試料番号16では、CoOが8000ppmと多く、ボ
トム温度が0℃となり、又試料番号12では、CoOが
0ppmと含有されてなく、ボトム温度が70℃となっ
ている。このように、Fe2O3が53.0〜54.5モ
ル%で、CoOが100〜4000ppmであると、ボ
トム温度が20〜60℃となっている。本発明の実施例
によれば、電力損失の最小値が400kW/m3以下
で、しかもその最小値となる温度(ボトム温度)が20
〜60℃となっている。
00kW/m3以下で、その電力損失の最小値を得る温
度が20〜60℃の電源用低損失フェライトを得ること
が出来、例えば、液晶バックライト用トランスなどの用
途に極めて有効である。
Claims (2)
- 【請求項1】 Fe2O3 53.0〜54.5モル%、
ZnO 6〜12モル%、残部MnOからなる主成分
と、副成分として、CaO 200〜1000ppm、
SiO2 0〜300ppm(但し0ppmを含まな
い)、CoO 100〜4000ppm含有し、更にN
b2O5、Ta2O5の少なくとも1種を50〜500pp
m含有し、100kHz、200mTでの電力損失が4
00kW/m3以下で、その電力損失の最小値を得る温
度が20〜60℃であることを特徴とする液晶バックラ
イト用低損失フェライト。 - 【請求項2】 請求項1において、平均結晶粒径が5〜
15μmであることを特徴とする液晶バックライト用低
損失フェライト。